CA2005899C - Solid electrolyte tube for sodium sulfur cells and surface finishing process thereof - Google Patents
Solid electrolyte tube for sodium sulfur cells and surface finishing process thereofInfo
- Publication number
- CA2005899C CA2005899C CA002005899A CA2005899A CA2005899C CA 2005899 C CA2005899 C CA 2005899C CA 002005899 A CA002005899 A CA 002005899A CA 2005899 A CA2005899 A CA 2005899A CA 2005899 C CA2005899 C CA 2005899C
- Authority
- CA
- Canada
- Prior art keywords
- solid electrolyte
- electrolyte tube
- firing
- bisque
- tube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
SOLID ELECTROLYTE TUBE FOR SODIUM SULFUR
CELLS AND SURFACE FINISHING PROCESS THEREOF
Abstract of the Disclosure A solid electrolyte tube for sodium sulfur cells, having an outer surface of a roughness defined by an arithmetical mean deviation of the profile (Ra) of not exceeding 2.0 µm and a maximum height of the profile (Rmax) of not exceeding 15 µm, is produced by leveling the outer surface of the solid electrolyte tube in a state of green body, bisque fired and calcined body, or fired body, by means of a finishing apparatus such as a centerless grinding machine, external cylindrical grinding machine, lathe, or the like. The solid electrolyte tube having a smooth and even surface can be prevented from crack formation due to local concentration of Na ion, S, sodium polysulfide and thermal stress thereon, so that it can improve durability and reliability.
CELLS AND SURFACE FINISHING PROCESS THEREOF
Abstract of the Disclosure A solid electrolyte tube for sodium sulfur cells, having an outer surface of a roughness defined by an arithmetical mean deviation of the profile (Ra) of not exceeding 2.0 µm and a maximum height of the profile (Rmax) of not exceeding 15 µm, is produced by leveling the outer surface of the solid electrolyte tube in a state of green body, bisque fired and calcined body, or fired body, by means of a finishing apparatus such as a centerless grinding machine, external cylindrical grinding machine, lathe, or the like. The solid electrolyte tube having a smooth and even surface can be prevented from crack formation due to local concentration of Na ion, S, sodium polysulfide and thermal stress thereon, so that it can improve durability and reliability.
Description
;~0()~
SOLlD ELECTROLYTE TUBE FOR SODIUM SULFUR
CE LS_AND SURFACE FINISHING PROCESS THEREOF
The present invention relates to a solid electrolyte tube for sodium sulfur cells and a process for finishing the surface thereof, particularly, to a solid electrolyte tube having improved durability and reliability and a surface finishing process for producing the same.
Recently, research and development have been conducted of high temperature type sodium sulfur cells which function at 300-350C and are excellent, from both functional and economi-cal points of view, in application to electric vehicles or night electric power storage, as a secondary battery.
Fig. 1 is a sectional elevation along the longitu-dinal axis of a solid electrolyte tube according to an embodi-ment of the present invention;
Fig. 2 is an enlarged view of the part A of Fig. l;
Fig. 3 is a sectional elevation along the longitu-dinal axis of a sodium sulfur cell;
Fig. 4 is a sectional elevation for illustrating a molding process of a solid electrolyte tube;
Fig. 5 is an enlarged view of the part B of Fig. 4;
and Fig. 6 is an enlarged sectional elevation of a part of surfaces of a solid electrolyte tube.
Hitherto known sodium sulfur cells, as shown in Fig.
3, comprise: a cylindrical anode container 1 accommodating ~()o~
6~8~]-345 an electroconductive material M for anode, such as carbon mat or the like, impregnated with molten sulfur S i.e. an anode active material; a cathode container 3 containing molten metallic sodium Na and being connected with the top end portion of the anode container 1 via an insulator ring 2 of ~-alumina interposed therebetween; and a solid electrolyte tube 4 made of polycrystalline ~"-alumina in the form of cylindrical test tube-shaped ceramics with a closed end tube ;~t)O'~ '3 ~4881-345 extending downward from its open top end fixed to an inner peripheral portion of said insulator ring 2, which solid electrolyte tube functions to allow sodium ion Na+, a cathode active material, to permeate selectively.
Further, a long and slender cathode tube 5 extending through the cathode container 3 down to near the bottom portion o the solid electrolyte tube 4 penetrates and is supported on the central portion of the upper lid of the cathode container 3.
u During discharging, the sodium ion permeates the solid electrolyte tube 4 and reacts with the sulfur S in the anode container 1 to form sodium polysulfide, according to the following reaction.
2Na + XS - Na2Sx Alternatively, during char~ing, a reaction reverse to the above takes place to produce sodium, Na, and sulfur, S.
The solid electrolyte tube 4 of sodium sulfur cells composed as described above, since the material of 2(~ the tube to be press-molded is a powder containing polycrystalline B"-alumina, is required to be molded by the so-called "rubber-press molding process", wherein the above powder containing polycrystalline B"-alumina is charged into the gap between an inner rigid mold 11 and an outer rubber mold 12, as shown in Fig. 4, constituting a rubber-press moldin~ apparatus (an ~ ~ 6488l-345 isostatic press) which are then introduced into a high pressure vessel to isostatically press the external peripheral surface of the outer rubber mold 12 at a predetermined pressure P. Thus the pressure acts evenly 05 on and over the whole body of the solid electrolyte tube 4 so that it makes the density uniform throu~hout the molded body.
The solid electrolyte tube 4 obtained by the above described rubber-press molding process, since the inner surface 4b is high-pressure molded with the rigid inner mold 11, has a rather smooth and even inner surface 4b densified with compressed powder ~articles 6 as shown in the left hand side of Fig. 5 t Therefore, during electric discharge, sodium ions permeate uniformly the solid electrolyte tube 4 so that the inner surface 4b presents little problem. However, the outer surface 4a of the solid electrolyte tube 4 is molded with the nonrigid rubber mold 12, so that its surface condition is not always smooth and even, as shown on the .~() right hand side of Fig. 5. With respect to the surface roughness, the outer surface 4a shows a very high arithmetical mean deviation of the profile Ra as well as a large maximum height of the profile RmaX~ as compared with the inner surface 4b. Consequently, in the use condition of the solid electrolyte tube 4, sodium ion Na~, sulfur S and sodium polysulfide Na2Sx which contact ;~005a~9 64881-3q5 with the surface of the solid electrolyte tube are apt to gather in valley portions 8 rather than in peak portions 7, as shown in Fig. 6. Therefore, electric current concentrates in the valley portions 8 so that the valley portions 8 are liable to deteriorate. Alternatively, when the sodium sulfur cells are heated or chilled, thermal stresses are apt to con-centrate on the valley portions 8. Therefore, cracks are liable to be formed in the valley portions 8, so that there arise problems such that the life of the solid electrolyte tube 4 is shortened and the reliability as a battery is lowered.
An aspect of the invention provides a solid electro-lyte tube for sodium sulfur cells, which has an outer surface of a roughness defined by an arithmetical mean deviation of the profile Ra of not exceeding 2.0 ~m, preferably about 0.2 to 0.8 ~m, and a maximum height of the profile RmaX of not exceeding 15 ~m, preferably about 2 to ll ~m.
Through the specification and appended claims of this invention, the arithmetical mean deviation of the profile Ra and the maximum height of the profile RmaX are understood to be as defined in accordance with ISO R 468 (Definitions and Designation of Surface Roughness).
Another aspect of the invention provides a process for finishing an outer surface of a solid electrolyte tube for sodium sulfur cells. The process comprises leveling the outer surface in a certain stage of its production using a finishing apparatus or device so that the above-defined surface ~00~ 9 648~1-345 smoothness is achieved.
In a first embodiment of this process, the outer surface of the solid electrolyte tube in a state of as-molded unfired and non-bisque fired green body is leveled by means of the finishing apparatus.
In a second embodiment of the surface finishing process, the outer surface of the solid electrolyte tube in a state of bisque fired and calcined molded body, is leveled by means of the finishing apparatus.
In a third embodiment of the surface finishing process, the outer surface of the solid electrolyte tube in a state of bisque fired and fired molded body is leveled by means of the finishing apparatus.
A further aspect of the present invention provides a process for producing the solid electrolyte tube. This process comprises molding a powder material containing ~-alumina by a rubber~ress molding process using an isostatic press, thereby obtaining an unfired and non-bIsque fired green body having a test tube shape; and either (a) bisque-firing the green body at a bisque-firing temperature and then firing the bisque-fired body at a final firing temperature, thereby converting the ~-alumina to poly-crystalline ~"-alumina, or (b) firing the green body at a final firing tempera-ture, thereby converting the ~-alumina to polycrystalline ~"-alumina;
;~o() :;~9~
wherein the outer surface of the tube body is leveled at any stage selected from the group consisting of (i) after molding the green body and before the bisque-firing in process variant (a), (ii) after the bisque-firing and before the final firing in process variant (a), and (iii) after molding the green body and before the final firing in process variant (b).
The present invention will be explained in more de-tail hereinafter by way of example with reference to the appended drawinqs.
Where the solid electrolyte tube of the present invention is used in sodium sulfur cells, sodium ion, sulfur or sodium polysulfide contacting with ~ 9 9 G4881-345 the surface of the solid electrolyte tube does not concentrate locally on the surface of the solid electrolyte tube by virtue of its low surface roughness and, besides, when the sodium sulfur cells are heated and chilled, the concentration of the thermal stress on the surface of the solid electrolyte tube is relaxed, so that the solid electrolyte tube is restrained from deterioration.
Alternatively, the above first embodiment of the surface finishing process of solid electrolyte tubes according to the present invention has an outstanding merit of facilitating the surface leveling, as the solid electrolyte tubes in a state of unfired, green molded body have a soft surface as compared with fired bodies.
The above second embodiment of the surface finishing process of solid electrolyte tubes according to the present invention facilitates the surface leveling to decrease the surface roughness after molding, as the surface of the bisque fired and calcined solid electrolyte tube can be leveled under the condition close to the unfired, green molded bodies.
The above third embodiment of the surface finishing process of solid electrolyte tubes according to the present invention, since the surface of the fired solid electrolyte tube is leveled, has an outstanding merit such that the surface roughness can be made to be ~ 0 05 89 9 ~488l-345 further lowered, to an equal level of the polished roughness, and the solid electrolyte tube can be formed in a final desired dimension.
The invention will be explained in more detail u5 hereinafter by way of example.
Example 1 This example illustrates the first embodiment of the surface finishing process of solid electrolyte tubes for sodium sulfur cells according to the present l~ invention.
On the outset, -alumina, sodium carbonate and lithium oxalate compounded in a predetermined formulation are pulverized and mixed by means of wet grinding, for example, with a 100 e ball-mill.
Thereafter, the resulting mixture is granulated, preferably by a spray dryer, into a powder having a predetermined particle diameter (an average particle diameter of 40~120 ~m).
Then, using a rubber-press apparatus ~an 2~ isostatic press), a solid electrolyte tube 4 in the form of cul-de-sac as shown in Fig. 1, for example, having an outside diameter of 15 mm, a wall thickness of 1.0 mm and a length of 150 mm, is molded at a pressure of 2.5 ton/cm2.
Further, using a centerless grinding machine, the above molded solid electrolyte tube 4 in a state of ;~t)05~
648~3l-345 unfired and non-bisque fired green is ground-finished at its surface 4a with a diamond grinding wheel (#180).
Then, finishing the surface by a paper wiper or nylon mesh, the leveling of the outer surface of the 05 solid electrolyte tube is completed. Finally, after bisque firing at about l,000C for 2 hours and firing at about 1,600C for 10 minutes, a solid electrolyte tube made of ~"-alumina that is most suitable for sodium sulfur cells is obtained.
u The thus produced solid electrolyte tube 4 has a smooth and even surface 4a as shown in Fig. 2.
The surface 4a has an arithmetical mean deviation of the profile Ra of 0.5~0.8 ~m and a maximum height of the profile RmaX of 6~11 ~m, as shown in Table hereinbelow.
I5 Further, the solid electrolyte tube 4 so molded by the above rubber-press as to have an inner peripheral surface of a center-line mean roughness Ra of at most O.S ~m and a maximum height RmaX of at most 5.0 ~m, is particularly desirable for securing the smooth movement of the cathode active materials from inside to outside of the solid electrolyte tube 4.
Example 2 The solid electrolyte tube 4 in a state of unfired and non-bisque fired green mold, manufactured in the foregoing Example 1, is bisque fired at about l,OOODC for 2 hours. Using a centerless grinding _ 10 _ ;~)O'~ '3 ~81-,45 machine, the bisque fired and calcined solid electrolyte tube 4 is finished in dry at its surface with a diamond grinding wheel (#180).
Finally, firing at about 1,610C for 5 minutes, 05 a solid electrolyte tube 4 is obtained. The surface of this solid electrolyte tube 4 has an arithmetical mean deviation of the profile Ra of 0.2~0.4 ~m as shown in Table hereinbelow, which is much better than the arithmetical mean deviation of the profile Ra of the solid electrolyte tube obtained in Example 1.
Additionally, the maximum height of the profile RmaX is 2~6 ~m which is smoother than the solid electrolyte tube 4 of Example 1.
Exam~le 3 The solid electrolyte tube 4 in a state of unfired and non-bisque fired green mold, manufactured in the foregoing Example 1, is fired at about 1,590C for 15 minutes. Thereafter, using a centerless grinding machine, the solid electrolyte tube 4 in a sintered 2u state is finished in wet at its surface 4a with a diamond grinding wheel ~#1~0) and further finished in wet with a #1,200 diamond grinding wheel.
The surface of this solid electrolyte tube 4 has an arithmetical mean deviation of the profile Ra of 0.2~0.4 ~m, which is as good as the arithmetical mean deviation of the profile Ra of the solid electrolyte ;~0()5~
tube obtained in Example 2. Additionally, the maximum heiqht of the profile RmaX is also 2~6 um same as the solid electrolyte tube 4 of Example 2.
Note) Using solid electrolyte tubes 150 mm long, having an outside diameter of 15 mm and a wall thickness of 1.0 mm, prepared by molding and finishing processes shown in Examples 1~3, 10 each of sodium sulfur cells having a cell capacity of 60 ~h were manufactured which comprise an anode active material of graphite impregnated with sulfur and a cathode active material of molten sodium. A charge-dischar~e durability test was conducted by applying an electricity of 80 mA/cm2 current density at an operating temperature of 330C for totalling 40 cells including 10 cells wherein a conventional solid electrolyte tube was used.
Table 1 _ Durability (Cumulative breakage) Example Ra(~m) Rmax(~m) 500 1,000 1,500l2,000 _ cycles cycles cycles cycles Conventional 2.7~4.2 23~35 7/lo 10/10 _ 1 0.5~0.8 6~11 0/10 1/10 4/10 6/10 2 0.2~0.4 2~6 0/10 0/10 (ll/ol%o) (33/ol%) 3 0.2~0.4 2~6 0/10 0/10 2/10 4/10 ~00~
648~1-345 The breakage rates of the cells after passing every 500 cycles are shown in Table 1.
It is clear from Table 1 that the sodium sulfur cells wherein the solid electrolyte tube according to u5 the present invention is used is remarkably improved in durability as compared with the cells wherein the conventional solid electrolyte tube is used.
Further, the present invention can be embodied as follows.
o Although a centerless grinding machine equipped with a diamond grinding wheel was used as a finishing apparatus in the foregoing Examples, it is needless to say that, in this case, the surface roughness can be varied by changing the grit or grain size of the diamond grinding wheel. Namely, in the foregoing each Example, the arithmetical mean deviation of the profile can be further lowered by further decreasing the abrasive grain size of the diamond grinding wheel. Further, the present invention may be practiced or embodied in still other ways without departing from the spirit or essential character thereof. For example, the centerless grinding machine can be replaced by other devices such as a lathe, an external cylindrical grinding machine or the like, or the finishing may be performed by using abrasive grains.
The solid electrolyte tube of the present 20C)5~'~9 fi48~]-345 invention, since its surface has a low arithmetical mean deviation of the profile, has meritorious effects such that the surface strength is improved and, besides, when it is used in sodium sulfur cells, local concentration 05 of sodium ion, sulfur or sodium polysulfide as well as thermal stresses on the surface of the solid electrolyte tube is prevented, so that the solid electrolyte tube can be improved in durability.
Alternatively, the above surface finishing process of solid electrolyte tubes according to the present invention can readily level the surface of the solid electrolyte tubes in a state of unfired, green molded body and further can perform the surface leveling of the solid electrolyte tubes in a bisque fired and calcined state, as effectively as in the case of green mold, so that the surface roughness after firing can be further lowered. Moreover, when the surface of the solid electrolyte tubes of sintered body is leveled, the arithmetical mean deviation of the profile of the 2~ surface can be similarly decreased and the dimension of the solid electrolyte tubes can be accorded precisely with the desired dimension of the final products, yielding solid electrolyte tubes high in dimensional accuracy.
SOLlD ELECTROLYTE TUBE FOR SODIUM SULFUR
CE LS_AND SURFACE FINISHING PROCESS THEREOF
The present invention relates to a solid electrolyte tube for sodium sulfur cells and a process for finishing the surface thereof, particularly, to a solid electrolyte tube having improved durability and reliability and a surface finishing process for producing the same.
Recently, research and development have been conducted of high temperature type sodium sulfur cells which function at 300-350C and are excellent, from both functional and economi-cal points of view, in application to electric vehicles or night electric power storage, as a secondary battery.
Fig. 1 is a sectional elevation along the longitu-dinal axis of a solid electrolyte tube according to an embodi-ment of the present invention;
Fig. 2 is an enlarged view of the part A of Fig. l;
Fig. 3 is a sectional elevation along the longitu-dinal axis of a sodium sulfur cell;
Fig. 4 is a sectional elevation for illustrating a molding process of a solid electrolyte tube;
Fig. 5 is an enlarged view of the part B of Fig. 4;
and Fig. 6 is an enlarged sectional elevation of a part of surfaces of a solid electrolyte tube.
Hitherto known sodium sulfur cells, as shown in Fig.
3, comprise: a cylindrical anode container 1 accommodating ~()o~
6~8~]-345 an electroconductive material M for anode, such as carbon mat or the like, impregnated with molten sulfur S i.e. an anode active material; a cathode container 3 containing molten metallic sodium Na and being connected with the top end portion of the anode container 1 via an insulator ring 2 of ~-alumina interposed therebetween; and a solid electrolyte tube 4 made of polycrystalline ~"-alumina in the form of cylindrical test tube-shaped ceramics with a closed end tube ;~t)O'~ '3 ~4881-345 extending downward from its open top end fixed to an inner peripheral portion of said insulator ring 2, which solid electrolyte tube functions to allow sodium ion Na+, a cathode active material, to permeate selectively.
Further, a long and slender cathode tube 5 extending through the cathode container 3 down to near the bottom portion o the solid electrolyte tube 4 penetrates and is supported on the central portion of the upper lid of the cathode container 3.
u During discharging, the sodium ion permeates the solid electrolyte tube 4 and reacts with the sulfur S in the anode container 1 to form sodium polysulfide, according to the following reaction.
2Na + XS - Na2Sx Alternatively, during char~ing, a reaction reverse to the above takes place to produce sodium, Na, and sulfur, S.
The solid electrolyte tube 4 of sodium sulfur cells composed as described above, since the material of 2(~ the tube to be press-molded is a powder containing polycrystalline B"-alumina, is required to be molded by the so-called "rubber-press molding process", wherein the above powder containing polycrystalline B"-alumina is charged into the gap between an inner rigid mold 11 and an outer rubber mold 12, as shown in Fig. 4, constituting a rubber-press moldin~ apparatus (an ~ ~ 6488l-345 isostatic press) which are then introduced into a high pressure vessel to isostatically press the external peripheral surface of the outer rubber mold 12 at a predetermined pressure P. Thus the pressure acts evenly 05 on and over the whole body of the solid electrolyte tube 4 so that it makes the density uniform throu~hout the molded body.
The solid electrolyte tube 4 obtained by the above described rubber-press molding process, since the inner surface 4b is high-pressure molded with the rigid inner mold 11, has a rather smooth and even inner surface 4b densified with compressed powder ~articles 6 as shown in the left hand side of Fig. 5 t Therefore, during electric discharge, sodium ions permeate uniformly the solid electrolyte tube 4 so that the inner surface 4b presents little problem. However, the outer surface 4a of the solid electrolyte tube 4 is molded with the nonrigid rubber mold 12, so that its surface condition is not always smooth and even, as shown on the .~() right hand side of Fig. 5. With respect to the surface roughness, the outer surface 4a shows a very high arithmetical mean deviation of the profile Ra as well as a large maximum height of the profile RmaX~ as compared with the inner surface 4b. Consequently, in the use condition of the solid electrolyte tube 4, sodium ion Na~, sulfur S and sodium polysulfide Na2Sx which contact ;~005a~9 64881-3q5 with the surface of the solid electrolyte tube are apt to gather in valley portions 8 rather than in peak portions 7, as shown in Fig. 6. Therefore, electric current concentrates in the valley portions 8 so that the valley portions 8 are liable to deteriorate. Alternatively, when the sodium sulfur cells are heated or chilled, thermal stresses are apt to con-centrate on the valley portions 8. Therefore, cracks are liable to be formed in the valley portions 8, so that there arise problems such that the life of the solid electrolyte tube 4 is shortened and the reliability as a battery is lowered.
An aspect of the invention provides a solid electro-lyte tube for sodium sulfur cells, which has an outer surface of a roughness defined by an arithmetical mean deviation of the profile Ra of not exceeding 2.0 ~m, preferably about 0.2 to 0.8 ~m, and a maximum height of the profile RmaX of not exceeding 15 ~m, preferably about 2 to ll ~m.
Through the specification and appended claims of this invention, the arithmetical mean deviation of the profile Ra and the maximum height of the profile RmaX are understood to be as defined in accordance with ISO R 468 (Definitions and Designation of Surface Roughness).
Another aspect of the invention provides a process for finishing an outer surface of a solid electrolyte tube for sodium sulfur cells. The process comprises leveling the outer surface in a certain stage of its production using a finishing apparatus or device so that the above-defined surface ~00~ 9 648~1-345 smoothness is achieved.
In a first embodiment of this process, the outer surface of the solid electrolyte tube in a state of as-molded unfired and non-bisque fired green body is leveled by means of the finishing apparatus.
In a second embodiment of the surface finishing process, the outer surface of the solid electrolyte tube in a state of bisque fired and calcined molded body, is leveled by means of the finishing apparatus.
In a third embodiment of the surface finishing process, the outer surface of the solid electrolyte tube in a state of bisque fired and fired molded body is leveled by means of the finishing apparatus.
A further aspect of the present invention provides a process for producing the solid electrolyte tube. This process comprises molding a powder material containing ~-alumina by a rubber~ress molding process using an isostatic press, thereby obtaining an unfired and non-bIsque fired green body having a test tube shape; and either (a) bisque-firing the green body at a bisque-firing temperature and then firing the bisque-fired body at a final firing temperature, thereby converting the ~-alumina to poly-crystalline ~"-alumina, or (b) firing the green body at a final firing tempera-ture, thereby converting the ~-alumina to polycrystalline ~"-alumina;
;~o() :;~9~
wherein the outer surface of the tube body is leveled at any stage selected from the group consisting of (i) after molding the green body and before the bisque-firing in process variant (a), (ii) after the bisque-firing and before the final firing in process variant (a), and (iii) after molding the green body and before the final firing in process variant (b).
The present invention will be explained in more de-tail hereinafter by way of example with reference to the appended drawinqs.
Where the solid electrolyte tube of the present invention is used in sodium sulfur cells, sodium ion, sulfur or sodium polysulfide contacting with ~ 9 9 G4881-345 the surface of the solid electrolyte tube does not concentrate locally on the surface of the solid electrolyte tube by virtue of its low surface roughness and, besides, when the sodium sulfur cells are heated and chilled, the concentration of the thermal stress on the surface of the solid electrolyte tube is relaxed, so that the solid electrolyte tube is restrained from deterioration.
Alternatively, the above first embodiment of the surface finishing process of solid electrolyte tubes according to the present invention has an outstanding merit of facilitating the surface leveling, as the solid electrolyte tubes in a state of unfired, green molded body have a soft surface as compared with fired bodies.
The above second embodiment of the surface finishing process of solid electrolyte tubes according to the present invention facilitates the surface leveling to decrease the surface roughness after molding, as the surface of the bisque fired and calcined solid electrolyte tube can be leveled under the condition close to the unfired, green molded bodies.
The above third embodiment of the surface finishing process of solid electrolyte tubes according to the present invention, since the surface of the fired solid electrolyte tube is leveled, has an outstanding merit such that the surface roughness can be made to be ~ 0 05 89 9 ~488l-345 further lowered, to an equal level of the polished roughness, and the solid electrolyte tube can be formed in a final desired dimension.
The invention will be explained in more detail u5 hereinafter by way of example.
Example 1 This example illustrates the first embodiment of the surface finishing process of solid electrolyte tubes for sodium sulfur cells according to the present l~ invention.
On the outset, -alumina, sodium carbonate and lithium oxalate compounded in a predetermined formulation are pulverized and mixed by means of wet grinding, for example, with a 100 e ball-mill.
Thereafter, the resulting mixture is granulated, preferably by a spray dryer, into a powder having a predetermined particle diameter (an average particle diameter of 40~120 ~m).
Then, using a rubber-press apparatus ~an 2~ isostatic press), a solid electrolyte tube 4 in the form of cul-de-sac as shown in Fig. 1, for example, having an outside diameter of 15 mm, a wall thickness of 1.0 mm and a length of 150 mm, is molded at a pressure of 2.5 ton/cm2.
Further, using a centerless grinding machine, the above molded solid electrolyte tube 4 in a state of ;~t)05~
648~3l-345 unfired and non-bisque fired green is ground-finished at its surface 4a with a diamond grinding wheel (#180).
Then, finishing the surface by a paper wiper or nylon mesh, the leveling of the outer surface of the 05 solid electrolyte tube is completed. Finally, after bisque firing at about l,000C for 2 hours and firing at about 1,600C for 10 minutes, a solid electrolyte tube made of ~"-alumina that is most suitable for sodium sulfur cells is obtained.
u The thus produced solid electrolyte tube 4 has a smooth and even surface 4a as shown in Fig. 2.
The surface 4a has an arithmetical mean deviation of the profile Ra of 0.5~0.8 ~m and a maximum height of the profile RmaX of 6~11 ~m, as shown in Table hereinbelow.
I5 Further, the solid electrolyte tube 4 so molded by the above rubber-press as to have an inner peripheral surface of a center-line mean roughness Ra of at most O.S ~m and a maximum height RmaX of at most 5.0 ~m, is particularly desirable for securing the smooth movement of the cathode active materials from inside to outside of the solid electrolyte tube 4.
Example 2 The solid electrolyte tube 4 in a state of unfired and non-bisque fired green mold, manufactured in the foregoing Example 1, is bisque fired at about l,OOODC for 2 hours. Using a centerless grinding _ 10 _ ;~)O'~ '3 ~81-,45 machine, the bisque fired and calcined solid electrolyte tube 4 is finished in dry at its surface with a diamond grinding wheel (#180).
Finally, firing at about 1,610C for 5 minutes, 05 a solid electrolyte tube 4 is obtained. The surface of this solid electrolyte tube 4 has an arithmetical mean deviation of the profile Ra of 0.2~0.4 ~m as shown in Table hereinbelow, which is much better than the arithmetical mean deviation of the profile Ra of the solid electrolyte tube obtained in Example 1.
Additionally, the maximum height of the profile RmaX is 2~6 ~m which is smoother than the solid electrolyte tube 4 of Example 1.
Exam~le 3 The solid electrolyte tube 4 in a state of unfired and non-bisque fired green mold, manufactured in the foregoing Example 1, is fired at about 1,590C for 15 minutes. Thereafter, using a centerless grinding machine, the solid electrolyte tube 4 in a sintered 2u state is finished in wet at its surface 4a with a diamond grinding wheel ~#1~0) and further finished in wet with a #1,200 diamond grinding wheel.
The surface of this solid electrolyte tube 4 has an arithmetical mean deviation of the profile Ra of 0.2~0.4 ~m, which is as good as the arithmetical mean deviation of the profile Ra of the solid electrolyte ;~0()5~
tube obtained in Example 2. Additionally, the maximum heiqht of the profile RmaX is also 2~6 um same as the solid electrolyte tube 4 of Example 2.
Note) Using solid electrolyte tubes 150 mm long, having an outside diameter of 15 mm and a wall thickness of 1.0 mm, prepared by molding and finishing processes shown in Examples 1~3, 10 each of sodium sulfur cells having a cell capacity of 60 ~h were manufactured which comprise an anode active material of graphite impregnated with sulfur and a cathode active material of molten sodium. A charge-dischar~e durability test was conducted by applying an electricity of 80 mA/cm2 current density at an operating temperature of 330C for totalling 40 cells including 10 cells wherein a conventional solid electrolyte tube was used.
Table 1 _ Durability (Cumulative breakage) Example Ra(~m) Rmax(~m) 500 1,000 1,500l2,000 _ cycles cycles cycles cycles Conventional 2.7~4.2 23~35 7/lo 10/10 _ 1 0.5~0.8 6~11 0/10 1/10 4/10 6/10 2 0.2~0.4 2~6 0/10 0/10 (ll/ol%o) (33/ol%) 3 0.2~0.4 2~6 0/10 0/10 2/10 4/10 ~00~
648~1-345 The breakage rates of the cells after passing every 500 cycles are shown in Table 1.
It is clear from Table 1 that the sodium sulfur cells wherein the solid electrolyte tube according to u5 the present invention is used is remarkably improved in durability as compared with the cells wherein the conventional solid electrolyte tube is used.
Further, the present invention can be embodied as follows.
o Although a centerless grinding machine equipped with a diamond grinding wheel was used as a finishing apparatus in the foregoing Examples, it is needless to say that, in this case, the surface roughness can be varied by changing the grit or grain size of the diamond grinding wheel. Namely, in the foregoing each Example, the arithmetical mean deviation of the profile can be further lowered by further decreasing the abrasive grain size of the diamond grinding wheel. Further, the present invention may be practiced or embodied in still other ways without departing from the spirit or essential character thereof. For example, the centerless grinding machine can be replaced by other devices such as a lathe, an external cylindrical grinding machine or the like, or the finishing may be performed by using abrasive grains.
The solid electrolyte tube of the present 20C)5~'~9 fi48~]-345 invention, since its surface has a low arithmetical mean deviation of the profile, has meritorious effects such that the surface strength is improved and, besides, when it is used in sodium sulfur cells, local concentration 05 of sodium ion, sulfur or sodium polysulfide as well as thermal stresses on the surface of the solid electrolyte tube is prevented, so that the solid electrolyte tube can be improved in durability.
Alternatively, the above surface finishing process of solid electrolyte tubes according to the present invention can readily level the surface of the solid electrolyte tubes in a state of unfired, green molded body and further can perform the surface leveling of the solid electrolyte tubes in a bisque fired and calcined state, as effectively as in the case of green mold, so that the surface roughness after firing can be further lowered. Moreover, when the surface of the solid electrolyte tubes of sintered body is leveled, the arithmetical mean deviation of the profile of the 2~ surface can be similarly decreased and the dimension of the solid electrolyte tubes can be accorded precisely with the desired dimension of the final products, yielding solid electrolyte tubes high in dimensional accuracy.
Claims (11)
1. A solid electrolyte tube for sodium sulfur cells, which has an outer surface of a roughness defined by an arithmetical mean deviation of profiles (Ra) of not exceeding 2.0 µm and a maximum height of profiles (Rmax) of not exceeding 15 µm.
2. A surface finishing process of solid electrolyte tubes, wherein an outer surface of the solid electrolyte tube in any state of: green body as compression molded; bisque fired and calcined body; and fired body, is leveled by means of a finishing apparatus to a roughness defined by an arithmetical mean deviation of the profile (Ra) of not exceeding 2.0 µm and a maximum height of the profile (Rmax) of not exceeding 15 µm.
3. The solid electrolyte tube according to claim 1, which is made of polycrystalline .beta."-alumina; has generally a test tube shape; and comprises a closed lower end, an open top end and a main tube body connecting the top and lower ends, wherein the main tube body has an inner surface which, when in use in the sodium sulfur cell, is in contact with molten metallic sodium Na, and the said outer surface which, when in use in the sodium sulfur cell, is in contact with molten sul-fur S and the main tube body, when in use in the sodium sulfur cell, selectively allows sodium ion Na+ to permeate there-through.
4. The solid electrolyte tube according to claim 3, wherein the outer surface has a roughness defined by an arith-metical mean deviation of the profiles (Ra) of 0.2 to 0.8.
5. The solid electrolyte tube according to claim 3, wherein the outer surface has a roughness defined by a maxi-mum height of profiles (Rmax) of 2 to 11 µm.
6. A process for producing the solid electrolyte tube as defined in claim 3, which comprises:
molding a powder material containing .alpha.-alumina by a rubber-press molding process using an isostatic press, thereby obtaining an unfired and non-bisque fired green body having a test tube shape; and either (a) bisque-firing the green body at a bisque-firing temperature and then firing the bisque-fired body at a final firing temperature, thereby converting the .alpha.-alumina to polycrystalline .beta."-alumina, or (b) firing the green body at a final firing tempera-ture, thereby converting the .alpha.-alumina to polycrystalline .beta."-alumina;
wherein the outer surface of the tube body is leveled at any stage selected from the group consisting of (i) after molding the green body and before the bisque-firing in process variant (a), (ii) after the bisque-firing and before the final firing in process variant (a), and (iii) after molding the green body and before the final firing in process variant (b).
molding a powder material containing .alpha.-alumina by a rubber-press molding process using an isostatic press, thereby obtaining an unfired and non-bisque fired green body having a test tube shape; and either (a) bisque-firing the green body at a bisque-firing temperature and then firing the bisque-fired body at a final firing temperature, thereby converting the .alpha.-alumina to polycrystalline .beta."-alumina, or (b) firing the green body at a final firing tempera-ture, thereby converting the .alpha.-alumina to polycrystalline .beta."-alumina;
wherein the outer surface of the tube body is leveled at any stage selected from the group consisting of (i) after molding the green body and before the bisque-firing in process variant (a), (ii) after the bisque-firing and before the final firing in process variant (a), and (iii) after molding the green body and before the final firing in process variant (b).
7. The process according to claim 6, wherein the level-ing is carried out using a centerless grinding machine equipped with a diamond grinding wheel.
8. The process according to claim 6 or 7, wherein the outer surface is leveled after molding the green body and before the bisque-firing in process variant (a).
9. The process according to claim 6 or 7, wherein the outer surface is leveled after the bisque-firing and before the final firing in process variant (a).
10. The process according to claim 6 or 7, wherein the outer surface is leveled after molding the green body and before the final firing in process variant (b)
11. The solid electrolyte tube according to any one of claim 3,4 and 5, used in the sodium sulfur cell which comprises:
a cylindrical anode container for containing an electroconductive material for anode impregnated with molten sulfur, a cathode container for containing molten metallic sodium connected to a top end portion of the anode container via an insulator ring of .alpha.-alumina interposed therebetween, the said solid electrolyte tube with its open top end fixed to an inner peripheral portion of the insulator ring, and a long and slender cathode tube extending through the cathode container down to near the bottom of the solid electrolyte tube and being supported by a central portion of an upper lid of the cathode container.
a cylindrical anode container for containing an electroconductive material for anode impregnated with molten sulfur, a cathode container for containing molten metallic sodium connected to a top end portion of the anode container via an insulator ring of .alpha.-alumina interposed therebetween, the said solid electrolyte tube with its open top end fixed to an inner peripheral portion of the insulator ring, and a long and slender cathode tube extending through the cathode container down to near the bottom of the solid electrolyte tube and being supported by a central portion of an upper lid of the cathode container.