CA1338530C - Means for constraining a rumen drug delivery device in a rolled configuration - Google Patents

Abstract

Improved means for constraining a rumen drug delivery device in a rolled configuration, said means comprising a laminate, which may be perforated, comprising a water-permeable material having a low friction surface in the presence of water, said material being bonded by means of a water-dispersible pressure sensitive adhesive to a repulpable tape, said tape having said water-dispersible pressure sensitive adhesive on both its surfaces; a laminate comprising a flexible, water-permeable polymeric material bonded between the low friction surface material and the repulpable tape; and devices constrained by said means.

Description

~ 338530 -IMPROVED MEANS FOR CONSTRAINING A RUMEN DRUG
DELIVERY DEVICE IN A ROLLED CONFIGURATION
This invention relates to improved means for constraining rumen drug delivery devices in a rolled configuration. More particularly, it relates to laminates comprising water permeable material having a low friction surface in the presence of water, said material being bonded to a repulpable tape having a water-dispersible adhesive on both surfaces; to laminates comprising a flexible, water-permeable polymeric material bonded between the low friction surface material and the repulpable tape; and to devices so constrained.
U.S. Patents 4,228,149, 4,601,893 and 4,861,596 and European Patent Publication No. 0334516 refer to rumen drug delivery devices constrained in a rolled-up configuration by appropriate constraining means.
In has been observed that the prior art devices described above are sometimes expelled by the ruminant because of untimely removal of the constraining means within the rumen.
Additionally, difficulty is often encountered upon oral administration of the constrained devices to young ruminants.
Premature removal of the constraining means and subsequent unrolling of the constrained device or slow transit of the constrained device can lead to dosing problems. Thus, the need for improved constraining means for rumen drug delivery devices which will facilitate dosing of ruminants therewith and enable timely change of configuration in the rumen and eliminate expulsion of the device by the ruminant.

~ -2- 1 338530 The constraining means of the present invention provide a low friction surface to facilitate dosing of the device, afford timely change in geometry of the rolled-up device within the rumen, avoid premature unrolling of the devices on dosing, are stable and non-toxic.
The improved constraining means of the present invention is a laminate which comprises a water-permeable material having a low friction surface in the presence of water, said material being bonded by means of a water-dispersible pressure sensitive adhesive to a repulpable tape which is coated on both surfaces with said adhesive. In one embodiment of the present invention, the above-described laminate comprises a flexible, water-permeable polymeric material bonded between the low friction surface material and the repulpable tape. A still further embodiment comprises a laminate comprising a flexible, water-permeable polymeric material sandwiched between two sheets of a water-permeable material having a low friction surface in the presence of water, one surface of which is bonded by means of a water-dispersible pressure sensitive adhesive to a repulpable tape which is coated on both surfaces (doubly coated) with said adhesive. Also included in this invention are rolled-up rumen drug delivery devices constrained by the herein-described improved constraining means.
Water-dispersible pressure sensitive tapes and repulpable tapes coated with said water-dispersible pressure sensitive adhesives are described in U.S.
patents 3,865,770; 3,441,430; 4,413,080; and 4,569,960.
Such tapes find extensive use in the paper-making industry.

~3~ 1 338530 The favored water-permeable material having a low friction surface in the presence of water is nitro-cellulose. As the outermost, or top layer, of the laminates described herein, the nitrocellulose facilitates oral administration of the constrained devices in view of the low-friction surface which it acquires in the presence of the saliva in the ruminant's esophageal passage.
In one form of the herein described constraining means, the nitrocellulose film is bonded directly to one surface of the doubly adhesive coated repulpable tape. The other adhesive coated surface, of the tape is, of course, bonded to the rolled-up drug delivery device so as to constrain it in said configuration.
This form of constraining means may, if increased flow of environmental fluid to the water dispersible adhesive is desired, be perforated, especially with macroholes ranging from about 0.5-5 mm in diameter, prior to its being applied to the rolled-up device.
The holes are normally circular but could be any shape such as, for example, ovals, triangles, squares, hexagons, etc. The perforations tend to accelerate removal of the constraining means.
In a modified, and favored, form of the improved constraining means of this invention, a flexible, water-permeable polymeric material, preferably cellophane, is bonded between the low friction surface material and the repulpable tape. The cellophane serves to enhance removal of the constraining means and unrolling of the rolled-up device. In addition to cellophane other water-permeable polymers, such as polyvinyl acetate, polymethylmethacrylate, polyethyl-methacrylate, polyvinylchloride, cellulose acetate and polydimethylsiloxane, can be used.

~ 338533 A preferred modification of the improved constraining means of this invention comprises a laminate comprising a flexible, water-permeable polymeric material, such as is described above, sandwiched between two sheets of a water-permeable material (e.g. nitrocellulose) having a low friction surface in the presence of water, one surface of which is bonded to a repulpable tape doubly coated with a water-dispersible pressure sensitive adhesive. The thickness of~6~d coated/ee~13phanc can range from about 0.3 to 3.0 mils (0.0076 to 0.076 mm.). Cellophane~
coated on both surfaces with nitrocellulose, i.e., sandwiched between nitrocellulose, is commercially available from BCL America, Inc. of Malvern, PA. 19355, product grade 345 PS-41. It has a thickness of about 0.9 mil (0.023 mm.).
Each of the forms of the constraining means described herein may optionally have macroperforations made in them, especially at that portion thereof where the said means abut or overlap when placed about the rolled-up delivery device to enhance unrolling of the device in the use environment.
The laminates of this invention are conveniently constructed by contacting the individual layers of the lamina, e.g., nitrocellulose, or cellophane coated on both sides with nitrocellulose, with the repulpable tape doubly coated with a water-dispersible pressure sensitive adhesive. Suitable water-dispersible pressure sensitive adhesives are well known in the art.
Representa~ive water-dispersible pressure sensitive adhesives are those comprising a copolymer of ~raC~e -f~av~ ~

monomeric acrylic acid esters and vinyl carboxylic acid monomer, said copolymer being partially neutralized with a secondary or tertiary alkanolamine, or an alkali metal hydroxide. Oily plasticizing compounds such as water-soluble polyoxyethylenes; and tackifiers such as reaction products of acid rosins and alkanolamines are added thereto. Such adhesives and their use to make repulpable tapes are described in U.S. patents 3,865,770; 4,413,080, 4,569,960.
Illustrative of such adhesives described in said patents are those comprising:
(I) (a) a copolymer of monomers consisting essentially of (1) about 90-20 parts by weight monomeric acrylic acid ester of non-tertiary alkyl alcohol the molecules of which have 1 to 4 carbon atoms; and

(2) about 10-80 parts by weight vinyl carboxylic acid monomer copolymerizable with said 20 acrylic acid ester, at least a number of the carboxyl groups in said acid monomers sufficient to constitute about 3-22% the weight of said copolymer, having been neutralized by reaction with a secondary or tertiary alkanolamine containing at least 4 carbon atoms; and (b) 0-400 parts by weight of at least one water-dispersible tack-promoting material selected from the class consisting of the oily plasticizing water-soluble polyoxyethylene compounds and the tackifying reaction products of acid rosins and alkanolamines; or i 338530 (II) the blended reaction product of (a) 100 parts by weight of a copolymer of monomers consisting essentially of (1) about 75-85 weight percent of at least one monomeric acrylic acid ester of nontertiary alkyl alcohol, and correspondingly, (2) about 25-15 weight percent of vinyl carboxylic acid, (b) about 35-100 parts by weight of acidic rosin or rosin derivative, (c) sufficient potassium hydroxide to neutralize about 30-45~ of the combined carboxyl groups of the copolymer and rosin or rosin derivative, (d) sufficient sodium hydroxide, lithium hydroxide, or a combination of sodium and lithium hydroxide to neutralize about 20-45~ of said carboxyl groups, and (e) about 100-225 parts by weight of oily plasticizing water-soluble polyoxyethylene compound; or (III) the blended reaction product of (a) 100 parts by weight of a copolymer of monomers consisting essentially of (1) about 60-85 weight percent of at least one monomeric acrylic acid ester of nontertiary alkyl alcohol having 4-14 carbon atoms, and correspondingly, (2) about 40-15 weight percent of vinyl carboxylic acid, (b) about 50 to 250 parts by weight of ethoxylated plasticizing components, sufficient to impart adhesion values such as to cause the adhesive to delaminate kraft paper when tested as described herein, consisting essentially of at least one of the following:
(1) up to about 125 parts by weight, but not so much as to cause adhesive separation, of one or more OH-functional ethoxylated plasticizers and (2) one or more electrolyte-tolerant complex and acidic esters of phosphoric acid and an ethoxylated nonionic surfactant, and (c) alkaline hydroxide consisting essentially of (1) sodium hydroxide, lithium hydroxide, or both sodium hydroxide and lithium hydroxide, in an amount sufficient to enhance shear strength and minimize bleeding but insufficient to cause separation of any OH-functional ethoxylated plasticizer present, not exceeding about 0.07 hydroxyl equivalent if OH-functional ethoxylated plasticizer is the only plasticizing component present, and (2) potassium hydroxide in an amount sufficient to promote water solubility.
The constraining means of this invention should not substantially increase the overall diameter of the constrained device at the point of constrainment to a thickness that would give rise to dosing problems when the constrained device is administered to a rumen.
This relationship between the thickness (diameter) of the rolled-up device and that of the constraining means will be recognized by those skilled in the art. Said individuals will appreciate the need to maintain the thickness of the constraining means to a minimum thickness consistent with acceptable times of removal - of the constraining means in the use environment. In general, constraining means of this invention having a thickness of from about 1.3 to 10.0 mils (0.0013 to 0.010 inch; or 0.033 to 0.254 ml.) afford acceptable release times.
Using the improved constraining means of this invention, it is easy to prepare a device for the controlled and prolonged release of veterinary medicaments, for example, anthelminthics, for the treatment of animals. The device comprises a resilient and flexible ethylene-vinyl acetate copolymer core which is sandwiched between a pair of coextensive resilient films of the copolymer. The core sheet can contain from about 10~ to about 75~ by weight of a water-soluble morantel salt (e.g., morantel tartrate) which is dispersed within the core sheet. The device can have one or a plurality of circular macroperforations of about 0.5 to about 10 mm in diameter. These macroperforations are distributed symmetrically across the face of the device and extend through the resilient films and the core sheet. The diameter and arrangement of the macroperforations in relation to the thickness of the core sheet are selected to expose sufficient interior edge area of the core sheet. Exposing sufficient edge area would 1 33853û
provide the desired morantel salt release rate. The device is constrained in a rolled configuration by a constraining means which is releasable in the rumen of an animal. Suitable constraining means include the laminate of the present invention.
The point of greatest tension in the constraining means occurs at that segment of the roll where the constraining means bridges the gap formed by its contact with the terminal edge of the outer layer of the rolled-up device and the surface of the layer upon said outer layer ends. The effect of this tension can be minimized by doubling the thickness of the overall length of the constraining means used. Alternatively, the effect can be minimized by placing a reinforcing strip of said constraining means having the thickness disclosed above over said segment.
As will be appreciated the constraining means used can be of sufficient length as to completely wrap about the rolled-up device, the ends thereof forming a butt joint. Alternatively, the constraining means can be of such a length that the ends thereof overlap to a lesser or greater extent when said means is placed about a rolled-up device. The extent of overlap should, for economic reasons, be less than that which would result in a double thickness of constraining means. Still further, the constraining means need not entirely wrap about the rolled-up device. It should, at the least, be in contact with the terminal end of the outer layer of the rolled-up device and the surface of the layer upon which said outer layer ends. The favored length of constraining means is that required to completely wrap about the rolled-up device.

-lO- 133~530 The improved constraining means of this invention are readily prepared by laminating the adhesive coated repulpable tape to the water-permeable polymeric material having a low friction surface in the presence A 5 of water, e.g., nitrocellulose; or to the nitro-C~ll o ~hq ~)~*cellulose coated/ccllophanc, by known methods, care being taken to avoid formation of bubbles or wrinkles.
The laminated tape is then cut to desired size.
Perforations may be conveniently made either before or after cutting of the laminated tape.
The removability of the constraining means of this invention in the use environment, e.g., the rumen of a ruminant, is determined by in vitro or in vivo methods.
The in vitro method comprises placing the constrained device in water, or more appropriately a synthetic rumen fluid, at 40C on an incubator shaker (ca.~0 excursions per minute~ and observing the time required for unrolling of the constrained device. The in vivo method comprises administering the constrained device to a fistulated ruminant and observing the time required for unrolling of the constrained device.
To further minimize dosing problems, the constrained devices desirably have plugs, e.g., polyethylene plugs, inserted into their open ends to convert the hollow tube to substantially a rod like device.

* rr ~

A morantel tartrate containing device prepared according to Example 1 of U.S. patent 4,601,893 was constrained in a rolled-up configuration with a constraining means of this invention comprising a 8.9 x A 7.6 cm wide laminate of 3M tape no. 900 and~c~ophan coated on both surfaces with nitrocellulose (product grade 345 PS-41). The ends of the tape when wrapped around the device overlapped 0.635 cm.
When placed in water at 40C as described above, the constraining means was removed in 40 minutes.
A similar device which had been stored at ambient temperature for 6 months required 57 minutes for removal of the constraining means when placed in 40C
water.

The constraining means of a constrained device prepared according to Example 1, when administered to a fistulated ruminant, was observed to be removed within 40 minutes, resulting in unrolling of the device.

The experiment of Example 1 was repeated but using a tape in which 50 perforations, each 2 mm in diameter, were made in the overlapping ends.
The constraining means was removed in 15 minutes when the constrained device was placed in 40C. water.

~ Ir~e- ~r ~

A device prepared according to Example 2 of U.S.
patent 4,228,149 is constrained in a rolled confi-guration by a 8.9 x 7.6 cm wide laminate of 3M tape no.
405 and ~c~lPophanc~coated on both surfaces with nitrocellulose. The laminate was sufficiently long so that the ends overlapped 0.635 cm.

The procedure of Example 3 is repeated but using doubly coated repulpable tapes prepared using the adhesives of Example 29 of U.S. patent 4,569,960 and of Example 7 of U.S. patent 4,413,080.

Ten devices are prepared according to the procedure of Example 1 except that, prior to being constrained, the devices are annealed at 50C for 24 hours. The devices are then tested at varying time levels for their ability to unroll. All devices, even those stored at ambient temperature for 6 months, unrolled; i.e., the constraining means is removed, from their original 2.5 cm cross-section diameter to a cross-section diameter within one hour sufficient to prevent their regurgitation by a ruminant.

Devices prepared according to Example l were administered to 100 young ruminants (approximately 100 kg in weight). No difficulty was experienced in dosing the animals and no devices were regurgitated by any of the animals.

'fQ~e- m ~ ~

-! 338530 Twenty devices prepared substantially according to Example 1 were divided into two equal groups. Group A
devices were placed in 40C water as described above and group B devices were administered to fistulated cattle, one device per animal. The times required for removal of the constraining means were recorded Average Range of Standard GroupRemoval Time Removal Time Deviation A - in vitro31 minutes 20-46 minutes 8 minutes B - in vivo51 minutes 30-63 minutes 9 minutes Nitrocellulose coated/a~ phanc (BCL 345 PS 41) was coated with (Fitchburg Coated Products Inc., Scranton, PA 18501) WASH-AWAY adhesive (a blend of polyvinyl methyl ether, maleic anhydride and a phosphate ester) to prepare a pressure sensitive constraining means with water soluble adhesive. A
device from Example 1 of U.S. 4,601,893 was constrained by the above-mentioned constraining means. The constrained device when immersed in water at 40C
underwent removal of the constraining means in 23 minutes.

*~rQd.~ f~a~^

Claims (16)

THE EMBODIMENTS OF THE INVENTION IN WHICH AN EXCLUSIVE
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:

1. A laminate adapted to act as a constraining device, comprising a water-permeable material having a low friction surface in the presence of water, the material being bonded by means of a water-dispersible pressure sensitive adhesive to a first surface of a repulpable tape, having first and second surfaces, the tape having the water-dispersable pressure sensitive adhesive on its second surface.

2. A laminate according to claim 1 wherein the water-dispersible pressure sensitive adhesive comprises:
(I) (a) a copolymer of monomers consisting essentially of (1) about 90-20 parts by weight monomeric acrylic acid ester of non-tertiary alkyl alcohol the molecules of which have 1 to 4 carbon atoms; and (2) about 10-80 parts by weight vinyl carboxylic acid monomer copolymerziable with said acrylic acid ester, at least a number of the carboxyl groups in said acid monomers sufficient to constitute about 3-22% the weight of said copolymer, having been neutralized by reaction with a secondary or tertiary alkanolamine containing at least 4 carbon atoms; and (b) 0-400 parts by weight of at least one water-dispersible tack-promoting material selected from oily plasticizing water-soluble polyoxyethylene compounds and tackifying reaction products of acid rosins and alkanolamines; or (II) the blended reaction product of (a) 100 parts by weight of a copolymer of monomers consisting essentially of (1) about 75-85 weight percent of at least one monomeric acrylic acid ester of nontertiary alkyl alcohol, and correspondingly, (2) about 25-15 weight percent of vinyl carboxylic acid, (b) about 35-100 parts by weight of acidic rosin or rosin derivative, (c) sufficient potassium hydroxide to neutralize about 30-45% of the combined carboxyl groups of the copolymer and rosin or rosin derivative, (d) sufficient sodium hydroxide, lithium hydroxide, or a combination of sodium and lithium hydroxide to neutralize about 20-45% of said carboxyl groups, and (e) about 100-225 parts by weight of oily plasticizing water-soluble polyoxyethylene compound; or (III) the blended reaction product of (a) 100 parts by weight of a copolymer of monomers consisting essentially of (1) about 60-85 weight percent of at least one monomeric acrylic acid ester of nontertiary alkyl alcohol having 4-14 carbon atoms, and correspondingly, (2) about 40-15 weight percent of vinyl carboxylic acid, (b) about 50 to 250 parts by weight of ethoxylated plasticizing components, sufficient to impart adhesion values such as to cause the adhesive to delaminate kraft paper when tested as described herein, consisting essentially of at least one of the following:
(1) up to about 125 parts by weight, but not so much as to cause adhesive separation, of one or more OH-functional ethoxylated plasticizers and (2) one or more electrolyte-tolerant complex and acidic esters of phosphoric acid and an ethoxylated nonionic surfactant, and (c) alkaline hydroxide consisting essentially of (1) sodium hydroxide, lithium hydroxide, or both sodium hydroxide and lithium hydroxide, in an amount sufficient to enhance shear strength and minimize bleeding but insufficient to cause separation of any OH-functional ethoxylated plasticizer present, not exceeding about 0.07 hydroxyl equivalent if OH-functional ethoxylated plasticizer is the only plasticizing component present, and (2) potassium hydroxide in an amount sufficient to promote water solubility.

3. A laminate according to claim 2 wherein the pressure sensitive adhesive is that of claim 2, part I.

4. A laminate according to any one of claims 1 to 3 wherein the low friction surface material is nitrocellulose.

5. A laminate according to any one of claims 1 to 3, the laminate having a flexible, water-permeable polymeric material bonded between the low friction surface material and the repulpable tape.

6. A laminate according to claim 5 wherein the flexible water-permeable polymeric material is a flexible cellulose.

7. A laminate according to any one of claims 1 to 3 wherein the water-permeable material contains a morantel salt.

8. A laminate according to claim 7, wherein the morantel salt is morantel tartrate.

9. A device for controlled and prolonged release of anthelmintic in a ruminant comprising a resilient and flexible ethylene-vinyl acetate copolymer core sheet sandwiched between a pair of coextensive resilient films of the copolymer, the core sheet containing from about 10 to 75%
by weight of a water-soluble morantel salt dispersed therein, the device having one or a plurality of circular macroperforations about 0.5 to 10 mm in diameter symmetrically distributed across the face of the device and extending through the films and the core sheet, the diameter and arrangement of the macroperforations in relation to the thickness of the core sheet being selected to expose sufficient interior edge area of the sheet to afford the desired morantel release rate, the device being constrained in rolled configuration by constraining means releasable in the rumen of an animal, the constraining means being a laminate according to any one of claims 1 through 3.

10. A device adapted for administration to ruminants comprising a water soluble veterinary medicament dispersed in a resilient sheet of water insoluble ethylenevinyl acetate copolymer, said medicament being present in an amount corresponding to 30 to 75% by weight of said sheet, said copolymer sheet being of a size and composition such that it is capable of being constrained by constraining means in a rolled-up configuration which permits oral administration, said constraining means being operable to release said constrained sheet in the rumen environment, said constraining means being a laminate according to any one of claims 1 to 3.

11. A laminate according to any one of claims 1 through 3, which is adapted to act for constraining rumen drug delivery device in a rolled configuration.

12. A laminate according to claim 11 wherein the low friction surface material is nitrocellulose.

13. The laminate according to claim 12 wherein the water-dispersible pressure sensitive adhesive comprises:
(I) (a) A copolymer of monomers consisting essentially of (1) about 90-20 parts by weight monomeric acrylic acid ester of non-tertiary alkyl alcohol having 1 to 4 carbon atoms; and (2) about 10-80 parts by weight vinyl carboxylic acid monomer copolymerizable with the acrylic acid ester, at least a number of the carboxyl groups in the acid monomers being sufficient to constitute about 3-22% the weight of the copolymer having been neutralized by reaction with a secondary or tertiary alkanolamine containing at least 4 carbon atoms; and (b) 0-400 parts by weight of at least one water-dispersible tack-promoting material selected from the group consisting of oily plasticizing water-soluble polyoxyethylene compounds and tackifying reaction products of acid rosins and alkanolamines; or (II) the blended reaction product of:
(a) 100 parts by weight of a copolymer of monomers consisting essentially of:
(1) about 75-85 weight percent of at least one monomeric acrylic acid ester of a nontertiary alkyl alcohol, and correspondingly, (2) about 25-15 weight percent of vinyl carboxylic acid, (b) about 35-100 parts by weight of acidic rosin or rosin derivative;
(c) sufficient potassium hydroxide to neutralize about 30-45% of combined carboxyl groups of the copolymer and the rosin or rosin derivative, (d) sufficient sodium hydroxide, lithium hydroxide, or a combination of sodium and lithium hydroxides to neutralize about 20-45% of the carboxyl groups, and (e) about 100-225 parts by weight of oily plasticizing water-soluble polyoxyethylene compound; or (III) the blended reaction product of (a) 100 parts by weight of a copolymer of monomers consisting essentially of:
(1) about 60-85 weight percent of at least one monomeric acrylic acid ester of a nontertiary alkyl alcohol having 4-14 carbon atoms, and correspondingly, (2) about 40-15 weight percent of vinyl carboxylic acid, (b) about 50 to 250 parts by weight of ethoxylated plasticizing components, sufficient to impart adhesion values such as to cause the adhesive to delaminate kraft paper, consisting essentially of at lest one of the following:
(1) up to about 125 parts by weight, but not so much as to cause adhesive separation, of one or more OH-functional ethoxylated plasticizers and (2) one or more electrolyte-tolerant complex and acidic esters of phosphoric acids and an ethoxylated nonionic surfactant and (c) alkaline hydroxide consisting essentially of (1) sodium hydroxide, lithium hydroxide, or both sodium hydroxide and lithium hydroxide, in an amount sufficient to enhance shear strength and minimize bleeding but insufficient to cause separation of any OH-functional ethoxylated plasticizer present, not exceeding about 0.07 hydroxyl equivalent if OH-functional ethoxylated plasticizer is the only plasticizing component present, and (2) potassium hydroxide in an amount sufficient to promote water solubility.

14. The laminate according to claim 13 wherein the pressure sensitive adhesive is that of claim 13, part (I).

15. A laminate according to claim 14, having a flexible, water-permeable polymeric material bonded between the low friction surface material and the repulpable tape.

16. The laminate according to claim 15 wherein the low friction surface material is nitrocellulose and the flexible water-permeable polymeric material is a flexible Cellophane*.