CA1296495C - Process for producing stretch blow-molded bottle with a handle - Google Patents
Process for producing stretch blow-molded bottle with a handleInfo
- Publication number
- CA1296495C CA1296495C CA 569651 CA569651A CA1296495C CA 1296495 C CA1296495 C CA 1296495C CA 569651 CA569651 CA 569651 CA 569651 A CA569651 A CA 569651A CA 1296495 C CA1296495 C CA 1296495C
- Authority
- CA
- Canada
- Prior art keywords
- preform
- blow
- handle
- mold
- bottle
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
ABSTRACT OF THE DISCLOSURE
A process for producing a stretch blow-molded bottle with a handle, by the steps of (a) stretching an injection-molded or blow-molded preform formed of a thermoplastic resin within a blow-mold by axial stretching with a stretch pin and transverse stretch with blown air at a temperature at least equal to the glass transition point of the resin but below its molding temperature; (b) pressing and holding an area of the stretched preform between a pair of opposed movable projecting members provided within the blow mold after the preform is expanded to substantially fill the inner volume of the blow mold and before the preform is cooled to a temperature below the glass transition point;
and (c) cooling the expanded preform by contact with the inner walls of the blow mold to form a stretch blow-molded bottle having opposing depressions defining a handle. In another aspect, the invention relates to a process for pro-ducing a stretch blow-molded bottle by the further step of thermally fusing the peripheral edges of the opposing depression and removing the resin inside the peripheral edges to form a hand hole surrounded by the stretch blow-molded bottle.
A process for producing a stretch blow-molded bottle with a handle, by the steps of (a) stretching an injection-molded or blow-molded preform formed of a thermoplastic resin within a blow-mold by axial stretching with a stretch pin and transverse stretch with blown air at a temperature at least equal to the glass transition point of the resin but below its molding temperature; (b) pressing and holding an area of the stretched preform between a pair of opposed movable projecting members provided within the blow mold after the preform is expanded to substantially fill the inner volume of the blow mold and before the preform is cooled to a temperature below the glass transition point;
and (c) cooling the expanded preform by contact with the inner walls of the blow mold to form a stretch blow-molded bottle having opposing depressions defining a handle. In another aspect, the invention relates to a process for pro-ducing a stretch blow-molded bottle by the further step of thermally fusing the peripheral edges of the opposing depression and removing the resin inside the peripheral edges to form a hand hole surrounded by the stretch blow-molded bottle.
Description
129649~
PROCESS FOR PRODUCING
STRETCH BLOW-MOLDED BOTTLE WITH A HANDLE
FIELD OF THE INVENTI~N
The present invention relates to a process for pro-ducing a stretch blow-molded bottle with a handle from a thermoplastic resin.
Modern plastic bottles with large inner capacities are usually furnished with a handle that render them easy to carry.
A common process for producing a plastic bottle with 10a handle by blow molding requires the following basic steps:
extruding a hollow parison from an extruder; fitting the parison with a bottom; blowing air into the bottomed parison so that it expands to a preblown article; holding the pre-blown article between a pair of split mold halves having 15handle forming projections; and blowing air so that the article is expanded to conform to the shape of the molds.
In this process, the area of the preblown article where a handle-defining hole is to be made is closed with the pro-jections on the molds so as to form a bottle where the 20peripheral edges of said hole are used, and the fused edges (i.e., burrs) are then removed by boring. A method for making pinched-shut, non-blown portions of a blown plastic jug with a blow mold projection is disclosed in U.S. Patent - 1 - ~
æ96495 3,983,199.
This conventional process for making a handle on a bottle by holding a preblown article between projections on molds has the following major disadvantage: the handle is usually situated in the neighborhood of the shoulder of the bottle, so the area around the top opening of the preblown article inevitably becomes large but since the neck required for the blow-molded bottle is small, burrs are unavoidably formed around the neck of the bottle. The formation of burrs is extensive in large bottles. See, e.g., Szajna, "The Plastic Bottle-i~krketing/ Engineering and Economics: A
Supplement to 1980 ANTEC Paper 'Functions vs. Economics vs.
Aesthetics'," SocietY of Plastics En~ineers Annual Technical Conference 40 (1982), page 707. Another problem is that the formation of burrs on tbe bottom is too extensive to neglect in the conventional process.
While direct blow molding has been the most common of the conventional blow molding techniques, it has recently become possible to produce blow-molded articles that are better than the direct blow-molded products in such aspects as mechanical strength, clarity and gas barrier properties.
Such superior products can be obtained by a new technique called stretch blow molding, which is already in commercial use. In the stretch blow-molding technique, air is injected into a parison emerging from an extruder ~preblowing step), 1 and the resulting preform (or an injection-molded preform) is transferred to a blow mold, where it is stretched bi-directionally at an optimum stretching temperature not lower than the glass transition point of the resin but less than its molding temperature, with a stretch pin being inserted to effect axial stretching and air being blown to cause transverse stretching. This bidrectional stretching causes molecular orientation of the polymer chains in the thermo-plastic resin of which the preform is made, thereby yielding 1~ blow molded articles having the improved properties de-scribed above. See, Szajna, "The Plastic Bottle - Market-ing, Engineering and Economics," supra, at pages 705-706;
U.S. Patent Re. 29,045.
There has been a need in the packaging industry to l~ apply the stretch blow molding technique to the manufacture of plastic bottles with handles. However, in the stretch blow molding method, the preform is heated in the mold at a temperature not lower than the glass transition point of the thermoplastic resin being molded and which is less than the 2n molding temperature of the resin. If a polyvinyl chloride bottle is to be made, the preform is typically heated at a temperature from about 90C to 140C, preferably from 100C
to 120C. In this regard, the glass transition point of polyvinyl chloride is from about 70C to 80C and the 2~ molding temperature is from about 160C to 220C.
~2964~S
l Therefore, even if the method of using a pair of split mold halves having projections for forming a handle-defining hole is applied to the air and pin stretched preblown article with a veiw to forming both the handle and the bottle body 5 from a single preform, the neck portion cannot be fused and the area left after deburring cannot be sealed to provide a commercially acceptable bottle.
When the handle portion of the thermoplastic resin is heated at a temperature higher than the molding tempera-1~ ture of the resin using a mold equipped with a heater so asto avoid the above problem, the effect due to stretching is lost at the heated portion of the resin so that the mechani-cal strength markedly decreases~ Particularly, use of crys-talline resins such as polyethylene terephthalate suffers, 1~ in addition, other problems, e.g., the resin becomes white as crystallization proceeds by heat, and the molded resin is easily broken due to distortion generated by the difference in crystallinity between the handle portion and other por-tions.
~n As described above, the method commonly employed in the conventional blow molding technique (i.e., direct blow molding) cannot be satisfactorily applied to the stretch blow molding technique, and therefore, various other methods have been proposed for producing blow-molding bottles with a handle by the stretch blow molding technique. A method which is typical of these proposals is described in Japanese ~296~95 Patent Pubiication No. 11218/88 and consists of furnishing a stretch blow-molded bottle body with a separately fabricated handle by a suitable method such as tight fitting.
However, the bottle fabricated by this process is not a unitary assembly prepared from a single preform con-sisting of the bottle body and a handle, so it lacks secure attachment of the handle to the bottle body. In addition, the fabrication process involves complicated steps.
SUMMARY OF THE INVF~NTION
An object, therefore, of the present invention is to provide an improved process for producing a bottle with a handle by the stretch blow molding technique.
As a result of studies conducted in order to attain this and other objects of the present invention, the present inventors have now found that a stretch blow-molded bottle with a handle can be readily produced if, in the process of stretch blow-molding a preform at a temperature not lower than its glass transition point but below its molding tem-perature, a blow mold furnished with a pair of opposed mova-ble projectlng parts, is used and if the projections arepushed into the preform after it has expanded to the stage where the formation of a handle portion becomes possible (i.e., the preform has expanded to at least about 80% of the inner capacity of the blow mold) and before the preform cools to a temperature below the glass transition point, 1 2964~5 preferably before the preform expands completely (until its volume becomes equal to the inner capacity of the blow mold) and cools upon contact with the inside walls of the blow mold, thereby pressing and holding the area where a handle-defining hole is to be formed until cavities in a shapecorresponding to the handle-defining hole form.
If desired, the peripheral edges of the thus-formed cavities may be fused with heat, followed by boring the resin in the cavities to form a handle-defining portion.
Accordingly, in one aspect the present invention relates to a process for producing a stretch blow-molded bottle with a handle, by the steps of (a) stretching an injection-molded or blow-molded thermoplastic resin preform within a blow mold by axial stretching with a stretch pin and transverse stretching with blown air at a temperature at least equal to the glass transition point of the resin but below its molding temperature, (b) pressing and holding an area of the stretched preform between a pair of opposed movable projecting members provided within the blow mold, after the preform is expanded to substantially fill the volume blow mold and before the preform is cooled to a tem-perature below the glass transition point of the resin; and (c) cooling the expanded preform by contact with the inner walls of the blow mold to form a stretch blow-molded bottle having opposing depressions defining a handle.
In another-aspect, the present invention relates to a process for producing a stretch blow-molded bottle by the further step of thermally fusing the peripheral edges of the opposing depressions and removing the resin inside the peripheral edges to form a handle hole surrounded by the stretch blow-molded bottle.
BRIEF DESCRIPTION OF THE DR WINGS
Fig. 1 is a longitudinal section of a mold with a pair of movable projecting parts 2 in which a preform 1 is placed in position;
Fig. 2 is a cross section taken on line A-A' of Fig.
1 and which shows the state where the projecting parts 2 are pushed into the preform 1 that has been expanded by stretch-ing with air blown through a bl~w pin 5 and by axial move-ment of a stretch pin 4;
Fig. 3A is a front view of a stretch blow-molded bottle 7 with cavities 6;
Fig. 3B is a longitudinal section of the same bot-tle; and Fig. 4 shows schematically how the peripheral edges of the cavities 6 in the bottle 7 are fused under pressure with a high-frequency dielectric heater.
DETAILED DESCRIPTION OF THE INVENTION
The present invention is hereinafter described in detail with reference to the accompanying drawings.
As shown in Fig. 1, a preform l of a thermoplastic resin kept at an optimum stretching temperature is placed in position in a mold 3 having a pair of projecting parts 2 that are moved by suitable means such as hydraulic or 5pnematic pressure, the mold being preferably cooled with a refrigerant such as water. Then, a stretch pin 4 is pushed downward to press the bottom of the preform 1. Simultane-ously or immediately thereafter, air is injected through a blow pin 5 to expand the preform l toward the inside walls lOof the mold 3. After the preform 1 has expanded to the stage where the formation of a handle portion becomes possi-ble ~i.e., the preform has expanded to at least about 80% of the inner capacity of the m~ld 3) and before the preform cools at a temperature below the glass transition point of the resin, 15preferably before the preform expands completely (until its volume becomes equal to the inner capacity of the mold 3) and cools upon contact with the inside walls of the mold 3, the projecting parts 2 are pushed into the preform as shown in Fig. 2 which is a cross section taken on line A-A' of 20Fig. 1. As a result, a bottle 7 having the shape shown in Fig. 3 is formed in the mold 3 (this bottle is hereinafter referred to as an intermediate bottle).
If, in the process described above, the projecting parts 2 are pushed into the preform 1 before it has expanded ; 25to ~he stage where the formation of a handle portion becomes possible (i.e., the volume of the preform is less than about 80% of the inner capacity of the mold 3), cavities 6 corre-sponding to a handle-defining hole will not be formed in a desired shape. When the preform 1 has expanded completely S (until its volume becomes equal to the inner capacity of the mold 3) and cools to a temperature below the glass transi-tion point upon contact with the inside walls of the mold 3, the subsequent pressing and holding cannot be performed. If the projecting parts 2 are pushed into the preform l at this stage, the preform l may break or the thickness of the walls between the cavities 6 may become uneven.
The projecting parts 2 are preferably pushed into the preform 1 at a time that is as close as possible to the time when the latter has expanded completely (until its volume becomes equal to the inner capacity of the mold 3) and cools upon contact with the inside walls of the mold 3.
If this condition is satisfied, better characteristics are provided for the blow-molded bottle obtained.
The portion corresponding to the cavities 6 is preferably curved concavely toward the center of the blow-molded bottle in view of the strength against deformation and for gripping the bottle formed. For this pùrpose, the projecting parts 2 preferably have smoothly and convexly curved surfaces.
The so produced intermediate bottle 7 can be direct-~ 296495 ly used as a final bottle with a handle. If a large bottle having an inner capacity of at least 1,000 ml is to be pro-duced, the cavities 6 are preferably bored through. As will be stated below, the peri~heral edges of the cavities 6 can be readily fused with heat, so by boring the inside of the cavities after thermally fusing their peripheral edges, a bottle with a handle that is easier to carry can be pro-duced.
The depressions or cavities 6 in the intermediate bottle 7 are defined by a pair of opposed plastic walls spaced apart by a small gap. Since the palr of oppo ~ plastic wall are formed by pressing the pair of projecting parts 2 in the accordance with the present invention, the gap between the two plastic walls can be made as small as 0.1 mm and below or even substantially zero if desired, so the peripheral edges of the cavities 6 can be readily fused with heat.
The method for thermally fusing the peripheral edges of the cavities 6 in the intermediate bottle 7 is described ; 20 in greater detail below.
Typical methods of thermal fusion that can be employed in the present invention include high-frequency dielectric heating, ultrasonic bonding, heat sealing and impulse sealing. An appropriate method can easily be selected in accordance with the type of thermoplastic resin '~. ', 1296~5 of which the bottle is to be made. For example, if the bottle is made of polyvinyl chloride, high-frequency dielec-tric bonding is preferably used; if the bottle is made of polyethylene terephthalate or polypropylene, ultrasonic bonding or i~pulse sealing is preferably used; and if the bottle is made of polyacrylonitrile, a preferred method is high-frequency bonding, heat sealing or impulse sealing.
Thermal fusion of the peripheral edges of the cavi-ties 6 is described hereinafter more specifically with reference to the case where the intermediate bottle 7 is made of polyvinyl chloride and thermal fusion is effected by high-frequency dielectric heating, but the present invention is not to be construed as being limited thereto.
The electrodes, or heating terminals, on the high-frequency dielectric bonding apparatus are preferably madeof brass. The periphery of the working faces of the heating terminals is preferably slightly smaller than the periphery of each cavity 6. As shown in Fig. 4, the heating terminals 8 preferably have protruding working faces 8a of about 0.2 to about 2 mm in width provided at their periphery so that the cavities 6 are thermally fused throughout the periphery thereof. The width of the protruding working faces 8a is particularly preferably from about 0.2 to about 0.4 mm, whereby the cavities 6 after thermal fusion can be removed more easily and with less burr and moreover the cavities 6 ..
` ~296495 can be removed simultaneously upon thermal fusion. The heating terminals preferably have a built-in heater that maintains a temperature of about 45 to 80C during use.
A pair of the heating terminals 8 described above are held against the peripheral edges of the cavities 6 in the intermediate bottle 7 as shown in Fig. 4 and an electric current is applied to the heating terminals so that the entire portion of the peripheral edges is thermally fused over a width ranging from about 0.2 to 2 mm. The high-fre-quency dielectric bonding apparatus typically generates afrequency of the order to 40.46 MHz. The preferred heating time varies with the wall thickness of the bottle to be produced but sat$sfactory results are usually attained by heating for a period of 1 to 4 seconds.
The peripheral edges of the cavities 6 in the bottle 7 may be thermally fused by high-frequency dielectric heat-ing in the manner described above after the bottle 7 is removed from the blow mold. Alternatively, thermal fusion may be conducted within the mold 3 if it is furnished with movable plugs incorporating in its tips the heating termi-nals of-the high-frequency dielectric bonding apparatus.
After thermally fusing the peripheral edges of the area of the intermediate bottle 7 where the handle-defining hole is to be formed, the inside of the cavities 7 may be 2~ bored through by the following method.
, .
~296495 If thermal fusion of the peripheral edges of the cavities 6 is performed by high-frequency dielectric heat-ing, the inside of the cavities 6 can be readily bored through the pushing one of the two heating terminals into the fixed bottle 7 while pulling the other heating terminal away from the bottle immediately after the thermal fusion, or at the time when the bonded areas are still in the molten state. Another method that can be employed to bore the inside of the cavities 6 is to use a punching machine.
Thermoplastic resins from which a bottle with a han-dle can be produced in the present invention include those which are capable of undergoing orientation of the polymer chains upon stretch blow molding~ Suitable examples include polyvinyl chloride, polypropylene, polyethylene terephthal-ate, polyacrylonitrile and polyethylene. From the view-points of moldability and mechanical strength of the bottle produced, polyvinyl chloride having a degree of polymeriza-tion in the range of about 600 to 1100 and polyethylene terephthalate are preferred, and polyvinyl chloride which can be stretched within a wide range of temperature and be thermally fused by the high-frequency dielectric bonding method is particularly suitable for the process of the present invention.
One embodiment of the process of the present inven-tion is illustrated in greater detail with reference to the ~649~;
following example, which is not to be construed as limiting the scope of the present invention.
EXAMPLE
A stretch blow-molded bottle with a handle was pro-duced with a biaxial stretching blow-molding machine (BM04, manufactured by Bekumu Co.) using a commercially available PVC compound for blow-molding, mainly composed of PVC (de-gree of polymerization 700) stabilized with octyl-tin-mercato octyl (Aron Compound BL 2H-8VIP, produced by Toa Gosei Chemical Industry Co., Ltd.).
The PVC compound was molded into a cylindrical pari-son by an extruder wherein the temperature of the cylinder, adapter and die portions were controlled to 170 to 180C.
The parison was then put into a preform mold of beryllium-copper alloy kept at 10 to 70C with a heat-control jacket capable of controlling temperatures in seven divided por-tions independently and the parison was cut at the top of the mold through which a blow pin was inserted, followed by blowing compressed air thereto to obtain a preform which was then properly cooled to 100 to 120C with the thermally controlled mold, to produce a molded preform having a dia-meter of 45 mm, a height of 250 mm and a round bottom.
The thus obtained preform which was thermally con-trolled at 100 to 120C was placed in a finish mold ~for a bottle of 1,800 ml) provided with a pair of movable project-lZ96495 ing parts for forming a handle and was stretched downward to the bottom of the mold with a stretch pin while blowing air from the upper portion of the preform. When the volume of the preform was almost the same as that of the mold, the preform was pressed with the pair of projecting parts to form the handle, and then the air-blowing was completed to fill the mold with the molded product.
After removing the molded product from the mold, it was then subjected to thermal fusion at the peripheral edge of the pressed portions with a pair of heating terminals having protruding working faces of high-frequency welder (3kw) in conformity with the periphery of the pressed por-tions to fuse the opposing pressed portions at their edges, and then one of the heating terminals was pushed into the fused pressed portion of the bottle while withdrawing the other terminal, whereby the pressed portion was removed with burr and the thus formed handle was smoothed with the side of the heating terminal inserted.
In accordance with the present invention, a bottle with a handle can be easily stretch blow-molded from a single preform as a unitary assembly of the handle and the bottle body. The molded bottle has good aesthetic appeal because of its high clarity. In addition, it has sufficient gas barrier properties to ensure prolonged storage of the contents. As a further advantage, the bottle can be pro-duced from a small charge of resin without sacrificing its mechanical strength.
Whlle the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.
PROCESS FOR PRODUCING
STRETCH BLOW-MOLDED BOTTLE WITH A HANDLE
FIELD OF THE INVENTI~N
The present invention relates to a process for pro-ducing a stretch blow-molded bottle with a handle from a thermoplastic resin.
Modern plastic bottles with large inner capacities are usually furnished with a handle that render them easy to carry.
A common process for producing a plastic bottle with 10a handle by blow molding requires the following basic steps:
extruding a hollow parison from an extruder; fitting the parison with a bottom; blowing air into the bottomed parison so that it expands to a preblown article; holding the pre-blown article between a pair of split mold halves having 15handle forming projections; and blowing air so that the article is expanded to conform to the shape of the molds.
In this process, the area of the preblown article where a handle-defining hole is to be made is closed with the pro-jections on the molds so as to form a bottle where the 20peripheral edges of said hole are used, and the fused edges (i.e., burrs) are then removed by boring. A method for making pinched-shut, non-blown portions of a blown plastic jug with a blow mold projection is disclosed in U.S. Patent - 1 - ~
æ96495 3,983,199.
This conventional process for making a handle on a bottle by holding a preblown article between projections on molds has the following major disadvantage: the handle is usually situated in the neighborhood of the shoulder of the bottle, so the area around the top opening of the preblown article inevitably becomes large but since the neck required for the blow-molded bottle is small, burrs are unavoidably formed around the neck of the bottle. The formation of burrs is extensive in large bottles. See, e.g., Szajna, "The Plastic Bottle-i~krketing/ Engineering and Economics: A
Supplement to 1980 ANTEC Paper 'Functions vs. Economics vs.
Aesthetics'," SocietY of Plastics En~ineers Annual Technical Conference 40 (1982), page 707. Another problem is that the formation of burrs on tbe bottom is too extensive to neglect in the conventional process.
While direct blow molding has been the most common of the conventional blow molding techniques, it has recently become possible to produce blow-molded articles that are better than the direct blow-molded products in such aspects as mechanical strength, clarity and gas barrier properties.
Such superior products can be obtained by a new technique called stretch blow molding, which is already in commercial use. In the stretch blow-molding technique, air is injected into a parison emerging from an extruder ~preblowing step), 1 and the resulting preform (or an injection-molded preform) is transferred to a blow mold, where it is stretched bi-directionally at an optimum stretching temperature not lower than the glass transition point of the resin but less than its molding temperature, with a stretch pin being inserted to effect axial stretching and air being blown to cause transverse stretching. This bidrectional stretching causes molecular orientation of the polymer chains in the thermo-plastic resin of which the preform is made, thereby yielding 1~ blow molded articles having the improved properties de-scribed above. See, Szajna, "The Plastic Bottle - Market-ing, Engineering and Economics," supra, at pages 705-706;
U.S. Patent Re. 29,045.
There has been a need in the packaging industry to l~ apply the stretch blow molding technique to the manufacture of plastic bottles with handles. However, in the stretch blow molding method, the preform is heated in the mold at a temperature not lower than the glass transition point of the thermoplastic resin being molded and which is less than the 2n molding temperature of the resin. If a polyvinyl chloride bottle is to be made, the preform is typically heated at a temperature from about 90C to 140C, preferably from 100C
to 120C. In this regard, the glass transition point of polyvinyl chloride is from about 70C to 80C and the 2~ molding temperature is from about 160C to 220C.
~2964~S
l Therefore, even if the method of using a pair of split mold halves having projections for forming a handle-defining hole is applied to the air and pin stretched preblown article with a veiw to forming both the handle and the bottle body 5 from a single preform, the neck portion cannot be fused and the area left after deburring cannot be sealed to provide a commercially acceptable bottle.
When the handle portion of the thermoplastic resin is heated at a temperature higher than the molding tempera-1~ ture of the resin using a mold equipped with a heater so asto avoid the above problem, the effect due to stretching is lost at the heated portion of the resin so that the mechani-cal strength markedly decreases~ Particularly, use of crys-talline resins such as polyethylene terephthalate suffers, 1~ in addition, other problems, e.g., the resin becomes white as crystallization proceeds by heat, and the molded resin is easily broken due to distortion generated by the difference in crystallinity between the handle portion and other por-tions.
~n As described above, the method commonly employed in the conventional blow molding technique (i.e., direct blow molding) cannot be satisfactorily applied to the stretch blow molding technique, and therefore, various other methods have been proposed for producing blow-molding bottles with a handle by the stretch blow molding technique. A method which is typical of these proposals is described in Japanese ~296~95 Patent Pubiication No. 11218/88 and consists of furnishing a stretch blow-molded bottle body with a separately fabricated handle by a suitable method such as tight fitting.
However, the bottle fabricated by this process is not a unitary assembly prepared from a single preform con-sisting of the bottle body and a handle, so it lacks secure attachment of the handle to the bottle body. In addition, the fabrication process involves complicated steps.
SUMMARY OF THE INVF~NTION
An object, therefore, of the present invention is to provide an improved process for producing a bottle with a handle by the stretch blow molding technique.
As a result of studies conducted in order to attain this and other objects of the present invention, the present inventors have now found that a stretch blow-molded bottle with a handle can be readily produced if, in the process of stretch blow-molding a preform at a temperature not lower than its glass transition point but below its molding tem-perature, a blow mold furnished with a pair of opposed mova-ble projectlng parts, is used and if the projections arepushed into the preform after it has expanded to the stage where the formation of a handle portion becomes possible (i.e., the preform has expanded to at least about 80% of the inner capacity of the blow mold) and before the preform cools to a temperature below the glass transition point, 1 2964~5 preferably before the preform expands completely (until its volume becomes equal to the inner capacity of the blow mold) and cools upon contact with the inside walls of the blow mold, thereby pressing and holding the area where a handle-defining hole is to be formed until cavities in a shapecorresponding to the handle-defining hole form.
If desired, the peripheral edges of the thus-formed cavities may be fused with heat, followed by boring the resin in the cavities to form a handle-defining portion.
Accordingly, in one aspect the present invention relates to a process for producing a stretch blow-molded bottle with a handle, by the steps of (a) stretching an injection-molded or blow-molded thermoplastic resin preform within a blow mold by axial stretching with a stretch pin and transverse stretching with blown air at a temperature at least equal to the glass transition point of the resin but below its molding temperature, (b) pressing and holding an area of the stretched preform between a pair of opposed movable projecting members provided within the blow mold, after the preform is expanded to substantially fill the volume blow mold and before the preform is cooled to a tem-perature below the glass transition point of the resin; and (c) cooling the expanded preform by contact with the inner walls of the blow mold to form a stretch blow-molded bottle having opposing depressions defining a handle.
In another-aspect, the present invention relates to a process for producing a stretch blow-molded bottle by the further step of thermally fusing the peripheral edges of the opposing depressions and removing the resin inside the peripheral edges to form a handle hole surrounded by the stretch blow-molded bottle.
BRIEF DESCRIPTION OF THE DR WINGS
Fig. 1 is a longitudinal section of a mold with a pair of movable projecting parts 2 in which a preform 1 is placed in position;
Fig. 2 is a cross section taken on line A-A' of Fig.
1 and which shows the state where the projecting parts 2 are pushed into the preform 1 that has been expanded by stretch-ing with air blown through a bl~w pin 5 and by axial move-ment of a stretch pin 4;
Fig. 3A is a front view of a stretch blow-molded bottle 7 with cavities 6;
Fig. 3B is a longitudinal section of the same bot-tle; and Fig. 4 shows schematically how the peripheral edges of the cavities 6 in the bottle 7 are fused under pressure with a high-frequency dielectric heater.
DETAILED DESCRIPTION OF THE INVENTION
The present invention is hereinafter described in detail with reference to the accompanying drawings.
As shown in Fig. 1, a preform l of a thermoplastic resin kept at an optimum stretching temperature is placed in position in a mold 3 having a pair of projecting parts 2 that are moved by suitable means such as hydraulic or 5pnematic pressure, the mold being preferably cooled with a refrigerant such as water. Then, a stretch pin 4 is pushed downward to press the bottom of the preform 1. Simultane-ously or immediately thereafter, air is injected through a blow pin 5 to expand the preform l toward the inside walls lOof the mold 3. After the preform 1 has expanded to the stage where the formation of a handle portion becomes possi-ble ~i.e., the preform has expanded to at least about 80% of the inner capacity of the m~ld 3) and before the preform cools at a temperature below the glass transition point of the resin, 15preferably before the preform expands completely (until its volume becomes equal to the inner capacity of the mold 3) and cools upon contact with the inside walls of the mold 3, the projecting parts 2 are pushed into the preform as shown in Fig. 2 which is a cross section taken on line A-A' of 20Fig. 1. As a result, a bottle 7 having the shape shown in Fig. 3 is formed in the mold 3 (this bottle is hereinafter referred to as an intermediate bottle).
If, in the process described above, the projecting parts 2 are pushed into the preform 1 before it has expanded ; 25to ~he stage where the formation of a handle portion becomes possible (i.e., the volume of the preform is less than about 80% of the inner capacity of the mold 3), cavities 6 corre-sponding to a handle-defining hole will not be formed in a desired shape. When the preform 1 has expanded completely S (until its volume becomes equal to the inner capacity of the mold 3) and cools to a temperature below the glass transi-tion point upon contact with the inside walls of the mold 3, the subsequent pressing and holding cannot be performed. If the projecting parts 2 are pushed into the preform l at this stage, the preform l may break or the thickness of the walls between the cavities 6 may become uneven.
The projecting parts 2 are preferably pushed into the preform 1 at a time that is as close as possible to the time when the latter has expanded completely (until its volume becomes equal to the inner capacity of the mold 3) and cools upon contact with the inside walls of the mold 3.
If this condition is satisfied, better characteristics are provided for the blow-molded bottle obtained.
The portion corresponding to the cavities 6 is preferably curved concavely toward the center of the blow-molded bottle in view of the strength against deformation and for gripping the bottle formed. For this pùrpose, the projecting parts 2 preferably have smoothly and convexly curved surfaces.
The so produced intermediate bottle 7 can be direct-~ 296495 ly used as a final bottle with a handle. If a large bottle having an inner capacity of at least 1,000 ml is to be pro-duced, the cavities 6 are preferably bored through. As will be stated below, the peri~heral edges of the cavities 6 can be readily fused with heat, so by boring the inside of the cavities after thermally fusing their peripheral edges, a bottle with a handle that is easier to carry can be pro-duced.
The depressions or cavities 6 in the intermediate bottle 7 are defined by a pair of opposed plastic walls spaced apart by a small gap. Since the palr of oppo ~ plastic wall are formed by pressing the pair of projecting parts 2 in the accordance with the present invention, the gap between the two plastic walls can be made as small as 0.1 mm and below or even substantially zero if desired, so the peripheral edges of the cavities 6 can be readily fused with heat.
The method for thermally fusing the peripheral edges of the cavities 6 in the intermediate bottle 7 is described ; 20 in greater detail below.
Typical methods of thermal fusion that can be employed in the present invention include high-frequency dielectric heating, ultrasonic bonding, heat sealing and impulse sealing. An appropriate method can easily be selected in accordance with the type of thermoplastic resin '~. ', 1296~5 of which the bottle is to be made. For example, if the bottle is made of polyvinyl chloride, high-frequency dielec-tric bonding is preferably used; if the bottle is made of polyethylene terephthalate or polypropylene, ultrasonic bonding or i~pulse sealing is preferably used; and if the bottle is made of polyacrylonitrile, a preferred method is high-frequency bonding, heat sealing or impulse sealing.
Thermal fusion of the peripheral edges of the cavi-ties 6 is described hereinafter more specifically with reference to the case where the intermediate bottle 7 is made of polyvinyl chloride and thermal fusion is effected by high-frequency dielectric heating, but the present invention is not to be construed as being limited thereto.
The electrodes, or heating terminals, on the high-frequency dielectric bonding apparatus are preferably madeof brass. The periphery of the working faces of the heating terminals is preferably slightly smaller than the periphery of each cavity 6. As shown in Fig. 4, the heating terminals 8 preferably have protruding working faces 8a of about 0.2 to about 2 mm in width provided at their periphery so that the cavities 6 are thermally fused throughout the periphery thereof. The width of the protruding working faces 8a is particularly preferably from about 0.2 to about 0.4 mm, whereby the cavities 6 after thermal fusion can be removed more easily and with less burr and moreover the cavities 6 ..
` ~296495 can be removed simultaneously upon thermal fusion. The heating terminals preferably have a built-in heater that maintains a temperature of about 45 to 80C during use.
A pair of the heating terminals 8 described above are held against the peripheral edges of the cavities 6 in the intermediate bottle 7 as shown in Fig. 4 and an electric current is applied to the heating terminals so that the entire portion of the peripheral edges is thermally fused over a width ranging from about 0.2 to 2 mm. The high-fre-quency dielectric bonding apparatus typically generates afrequency of the order to 40.46 MHz. The preferred heating time varies with the wall thickness of the bottle to be produced but sat$sfactory results are usually attained by heating for a period of 1 to 4 seconds.
The peripheral edges of the cavities 6 in the bottle 7 may be thermally fused by high-frequency dielectric heat-ing in the manner described above after the bottle 7 is removed from the blow mold. Alternatively, thermal fusion may be conducted within the mold 3 if it is furnished with movable plugs incorporating in its tips the heating termi-nals of-the high-frequency dielectric bonding apparatus.
After thermally fusing the peripheral edges of the area of the intermediate bottle 7 where the handle-defining hole is to be formed, the inside of the cavities 7 may be 2~ bored through by the following method.
, .
~296495 If thermal fusion of the peripheral edges of the cavities 6 is performed by high-frequency dielectric heat-ing, the inside of the cavities 6 can be readily bored through the pushing one of the two heating terminals into the fixed bottle 7 while pulling the other heating terminal away from the bottle immediately after the thermal fusion, or at the time when the bonded areas are still in the molten state. Another method that can be employed to bore the inside of the cavities 6 is to use a punching machine.
Thermoplastic resins from which a bottle with a han-dle can be produced in the present invention include those which are capable of undergoing orientation of the polymer chains upon stretch blow molding~ Suitable examples include polyvinyl chloride, polypropylene, polyethylene terephthal-ate, polyacrylonitrile and polyethylene. From the view-points of moldability and mechanical strength of the bottle produced, polyvinyl chloride having a degree of polymeriza-tion in the range of about 600 to 1100 and polyethylene terephthalate are preferred, and polyvinyl chloride which can be stretched within a wide range of temperature and be thermally fused by the high-frequency dielectric bonding method is particularly suitable for the process of the present invention.
One embodiment of the process of the present inven-tion is illustrated in greater detail with reference to the ~649~;
following example, which is not to be construed as limiting the scope of the present invention.
EXAMPLE
A stretch blow-molded bottle with a handle was pro-duced with a biaxial stretching blow-molding machine (BM04, manufactured by Bekumu Co.) using a commercially available PVC compound for blow-molding, mainly composed of PVC (de-gree of polymerization 700) stabilized with octyl-tin-mercato octyl (Aron Compound BL 2H-8VIP, produced by Toa Gosei Chemical Industry Co., Ltd.).
The PVC compound was molded into a cylindrical pari-son by an extruder wherein the temperature of the cylinder, adapter and die portions were controlled to 170 to 180C.
The parison was then put into a preform mold of beryllium-copper alloy kept at 10 to 70C with a heat-control jacket capable of controlling temperatures in seven divided por-tions independently and the parison was cut at the top of the mold through which a blow pin was inserted, followed by blowing compressed air thereto to obtain a preform which was then properly cooled to 100 to 120C with the thermally controlled mold, to produce a molded preform having a dia-meter of 45 mm, a height of 250 mm and a round bottom.
The thus obtained preform which was thermally con-trolled at 100 to 120C was placed in a finish mold ~for a bottle of 1,800 ml) provided with a pair of movable project-lZ96495 ing parts for forming a handle and was stretched downward to the bottom of the mold with a stretch pin while blowing air from the upper portion of the preform. When the volume of the preform was almost the same as that of the mold, the preform was pressed with the pair of projecting parts to form the handle, and then the air-blowing was completed to fill the mold with the molded product.
After removing the molded product from the mold, it was then subjected to thermal fusion at the peripheral edge of the pressed portions with a pair of heating terminals having protruding working faces of high-frequency welder (3kw) in conformity with the periphery of the pressed por-tions to fuse the opposing pressed portions at their edges, and then one of the heating terminals was pushed into the fused pressed portion of the bottle while withdrawing the other terminal, whereby the pressed portion was removed with burr and the thus formed handle was smoothed with the side of the heating terminal inserted.
In accordance with the present invention, a bottle with a handle can be easily stretch blow-molded from a single preform as a unitary assembly of the handle and the bottle body. The molded bottle has good aesthetic appeal because of its high clarity. In addition, it has sufficient gas barrier properties to ensure prolonged storage of the contents. As a further advantage, the bottle can be pro-duced from a small charge of resin without sacrificing its mechanical strength.
Whlle the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.
Claims (12)
1. A process for producing a stretch blow-molded bottle with a handle, comprising the steps of (a) stretching an injection-molded or blow-molded thermoplastic polyvinyl chloride resin preform within a blow mold by axial stretching with a stretch pin and transverse stretching with blown air at a temperature at least equal to the glass transition point of said resin but below its molding tem-perature of said resin;
(b) pressing and holding an area of the stretched preform between a pair of opposed movable projecting members provided within said blow mold, after the preform is expand-ed to substantially fill the inner cavity of the blow mold and before the preform is cooled to a temperature below the glass transition point of the resin;
(c) cooling said expanded preform by contact with the inner walls of the blow mold to form a stretch blow-molded bottle having opposing depressions defining a handle;
and (d) the step of thermally fusing the peripheral edges of said opposing depressions defining said handle and removing the resin inside the peripheral edges to form a handle hole surrounded by the stretch blow-molded bottle, wherein said thermally fusing is performed by high frequency dielectric heating.
(b) pressing and holding an area of the stretched preform between a pair of opposed movable projecting members provided within said blow mold, after the preform is expand-ed to substantially fill the inner cavity of the blow mold and before the preform is cooled to a temperature below the glass transition point of the resin;
(c) cooling said expanded preform by contact with the inner walls of the blow mold to form a stretch blow-molded bottle having opposing depressions defining a handle;
and (d) the step of thermally fusing the peripheral edges of said opposing depressions defining said handle and removing the resin inside the peripheral edges to form a handle hole surrounded by the stretch blow-molded bottle, wherein said thermally fusing is performed by high frequency dielectric heating.
2. The method as claimed in claim 1, wherein said pressing and holding in step (b) is performed after the preform is expanded to fill at least about 80% of the volume of the blow mold.
3. The method as claimed in claim 2, wherein said pressing and holding is performed before the preform is expanded to completely fill the blow mold, and the preform is then expanded to fill the blow mold prior to said cooling in step (c).
4. The method as claimed in claim 1, wherein said axial stretching and said transverse stretching in step (a) are performed simultaneously.
5. The method as claimed in claim 1, wherein said axial stretching is performed prior to said transverse stretching.
6. The method as claimed in claim 1, wherein said blown mold is cooled with a refrigerant.
7. The method as claimed in claim 6, wherein said refrigerant is water.
8. The method as claimed in claim 1, wherein said stretching in step (a) is performed at a temperature of from 100 to 120°C.
9. The method as claimed in claim 1, wherein said thermally fusing is performed by high-frequency dielectric heating.
10. The method as claimed in claim 1, wherein said thermally fusing in step (d) is performed using two heating terminals inserted into said opposing depressions, each said terminal having a raised peripheral area from about 0.2 to 2 mm in width adopted for fusing said peripheral edges to a width of from about 0.2 to 2 mm.
11. The method as claimed in claim 10 , wherein said removing the resin inside the peripheral edges in step (d) is performed by inserting one heating terminal through the handle hole while withdrawing the opposing heating terminal, while the peripheral edges are in a molten state.
12. The method as claimed in claim 1, wherein said stretching in step (a) is performed at a temperature of from 90 to 140°C.