CA1285723C - Sliding part formed by monomer casting and method for producing the same - Google Patents
Sliding part formed by monomer casting and method for producing the sameInfo
- Publication number
- CA1285723C CA1285723C CA000518884A CA518884A CA1285723C CA 1285723 C CA1285723 C CA 1285723C CA 000518884 A CA000518884 A CA 000518884A CA 518884 A CA518884 A CA 518884A CA 1285723 C CA1285723 C CA 1285723C
- Authority
- CA
- Canada
- Prior art keywords
- bearing
- shaft
- resin
- monomer
- sliding part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
ABSTRACT OF THE DISCLOSURE
A sliding part produced by monomer casting. The sliding part consists of a bearing, a shaft which is rotatably or reciprocatably supported by and fitting into the bearing, and a resin lining formed on the bearing surf ace of the bearing. The resin lining is formed by pouring a low-viscosity monomer or prepolymer into the clearance between the bearing surface and the shaft and permitting the monomer or prepolymer to polymerize or cure in situ. The shaft is slidable on the resin lining.
A sliding part produced by monomer casting. The sliding part consists of a bearing, a shaft which is rotatably or reciprocatably supported by and fitting into the bearing, and a resin lining formed on the bearing surf ace of the bearing. The resin lining is formed by pouring a low-viscosity monomer or prepolymer into the clearance between the bearing surface and the shaft and permitting the monomer or prepolymer to polymerize or cure in situ. The shaft is slidable on the resin lining.
Description
~2~8~72~ 1 BACKGROUND OF_HE INVENTION
1. Field of the Invention The present invention relates to a sliding part ana a method for producing the same, said sliding part consisting of a shaft and a bearing, the former fitting into the latter, such as a com-bination of a journal and a ~ournal bearing and a combination of a spline shaft (internal spline) and a hub (external spline).
More particularly, the present invention relates to a sliding part in which a resin lining is formed on the bearing surface of the hearing by monomer casting, and it also relates to a method for producing the sliding part.
1. Field of the Invention The present invention relates to a sliding part ana a method for producing the same, said sliding part consisting of a shaft and a bearing, the former fitting into the latter, such as a com-bination of a journal and a ~ournal bearing and a combination of a spline shaft (internal spline) and a hub (external spline).
More particularly, the present invention relates to a sliding part in which a resin lining is formed on the bearing surface of the hearing by monomer casting, and it also relates to a method for producing the sliding part.
2. Description of the Prior ~rt Sliding parts with a resin lining have been in general use in automobiles and many other machines. ~he conventional sliding parts fall under two broad categories: (A) There are sliding parts constructed of a shaft, a bearing and a bushing interposed between them, said bushing being formed by coating a flat, metal plate ~ith a resin, cutting the coated plate to proper size, curling the cut plate, and fitting the curled plate into the bearing surface of the bearing, as in the case of a Teflon CT~
resin-coated bushing. (B) There are sliding parts constructed of a bearing with the bearing surface thereof directly coated with a resin and a shaft machined to fit into the bearing.
The sliding parts belonging to category (A) have the follow-ing disadvantages: (1) Both the lining and the shaft should have a considerably high dimensional accuracy, which sometimes ~8~3 needs the selective fitting of accurately matching parts. (~) Depending on the shape of the bearing surface, it may be diffi-cult to fit the lining (3) The production cost of the lining is high. On the other hand, the sliding parts belonging to cate-gory (B) have the following disadvantages. (1) The machining of the shaft is indispensable, which adds to the cost of the sliding part. (2) The machining of the shaft should be performed with high accuracy and selective fitting may be necessary in some in-stances.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide a sliding part having a highly accurate clearance at sliding interfaces and outstanding sliding performance.
It is another object of the present invention to provide a method for producing with ease and certainty a sliding part of high accuracy and high performance regardless of the dimensional accuracy of the shaft and bearing.
The present invention is based on the so-called monomer casting in which a molded item is produced by castiny a monomer, followed by polymerization and curing, as employed in the case of nylon monomer casting.
The sliding part of this invention comprises a bearing, a shaft which is rotably or reciprocatably supported by and fitting into the bearing, and a lining of resin formed on the bearing surface of the bearing. The resin lining is formed by pouring a low-viscosity monomer or prepolymer into a clearance between the .
~2~3S'7~
bearing surface and the shaft and permitting the monomer or prepolvmer to polymeriæe or cure in situ. The shaft slides on the resin lining.
The shaft may constit~te an internal spline and the bearing an external spline. Either the external spline or the internal spline may be provided with a groove constituting a well for receiving resin poured into the clearance between the external and internal splines. The resin lining may be a thin film of polyamide resin, urethane resin, epoxy resin or polyester resin The method of this invention for producing the sliding part by monomer casting is accomplished by pouring a low-viscosity monomer or prepolymer into a clearance between a shaft and the bearing surface of a bearing. ~he shaft is fitted into the bearing and is rotatably or reciprocatably supported by the bearing and specifically the bearing surface. After polymeriza-tion and curing, the monomer forms a resin lining on the bearing surface of the bearing, and the shaft slides on the resin lining.
BRIEF DESCRIPTION OF THE DRAWINGS
Fig. 1 is a graph showing the relation between the thickness and the compression strength of the resin lining of the present invention;
Fig. 2 is a sectional view of the sliding part of Example 1 of this invention;
Fig. 3 is a plan view of the sliding part as shown in Fig.
~;
"'' ' ' ~' ' '' .
. ~2~'7~3 Fig. 4 is a sectional view of the sliding part of Example 2 of this invention;
Fig. 5 is a sectional view of the sliding part of ~xample 3 of this invention;
Fig. 6 is an enlarged sectional view taken along the line VI-VI of Fig. 5;
Fig. 7 is an enlarged sectional view taken along the line VII-VII of Fig. 5;
Fig. 8 is a sectional view of the sliding part of Example 4 of this invention;
Fig. 9 is an enlarged sectional view taken along the line IX-IX of Fiy. 8; and Fig. 10 is an enlarged sectional view taken along the line X-X of Fig. 8.
The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and, together with the description, serve to ex-plain the principles of the invention.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
The sliding part of this invention is produced in the fol-lowing manner. At first, a shaft is fitted into a bearing and rotatably or reciprocatably supported by the bearing, primarily in the ,axial direction. The bearing may be separate and indepen-dent or integral with the machine proper. Next, a monomer or a low-viscosity prepolymer of a suitable resin, such as polyamide resin, urethane resin, epoxy resin or pPlyester resin, which may ~Z8S~Z3 be incorporated with a polymerization initiator according to need, is poured into the clearance between the shaft and the bearing surface of the bearing. The monomer or prepolymer is polymerized or cured by heating or irradiation. A resin lining is thus formed on the bearing surface in the existing clearance between the shaft and the bearing surface of the bearing. Prior to the pouring of a monomer, the bearing should be provided with proper masking excluding the bearing surface, because it is dif-ficult to remove the unnecessary resin lining after polymeriza-tion. For the uniform, smooth polymerization of the monomer, it may be desirable to preheat the shaft and bearing to a tempera-ture suitable for polymerization prior to the pouring of the monomer. In addition, it is also desirable to apply a proper primer to the bearing surface of the bearing and a proper mold release to the shaft. The primer ensures the firm adherence of the resin lining to the bearing surface of the bearing. The polymerization initiator shoulcl be properly selected according to the monomer used. For example, Eor caprolactam (monomer or nylon-6), lactam anion and acyl lactam are recommended.
The polymerization of the monomer is usually accompanied by a certain degree of molding shrinkage. This molding shrinkage gives rise to a very small amount of clearance between the shaft and the resin lining when the resin lining is formed. The amount of clearance is as Eollows in the case where the resin lining is made of nylon-6. The molding shrinkage of nylon-6 is 14 to 16%
(by volume) and it corresponds to a linear shrinkage of 4 to 5%
1~2~35~
across the thickness or cross-section when nylon-6 is used as a thin film. If the clearance between the shaft and the bearing surface is about 0.2 mm and the resin lining of nylon-6 is formed in the clearance, the shrinkage of nylon-6 is about 8 to ~0 um.
It follows, therefore, that a very small amount of clearance (about 8 to 10 um) is formed between the shaft and the resin lin-ing. Such a small anmount of clearance will be possible only with with extremely accurate machining. According to the present invention, the high precision clearance can be obtained easily even though the shaft and the bearing are characterized by low dimensional accuracy. The sliding part of the present invention is formed in situ,and according to the method of the invention, it is not necessary to select a shaft and a bearing that mate with each other. In addition, it is not necesary to machine the shaft and the bearing to high accuracy to achieve a close fit.
In spite of the good sliding characteristics, resin linings have not been effectively utilized for sliding parts that gener-ate significant frictional heat resulting ~rom repeated sliding motion because of the following disadvantages. Resins undego a great amount of creep or deformation at high temperatures, and they exhibit low thermal conductivity, which is responsible for their low critical PV value. In this invention, these disadvan-tages are eliminated. The resin lining produced in accordance with this invention in the form of a thin film between the shaft and the bearing has a greatly increased compression strength resulting from the support provld~d by the bearing metal. In the ~35~7~3 case of resin lining made of nylon-6, the compression strength remarkabl~ increases if the lining is thinner than about 0.6 mm, as shown in Fig. 1. In addition, such a thin resin lining per-mits rapid heat dissipation and consequently provides an improved critical PV value. Thus the sliding part of this invention has high performance. That is the resin lining fully utilizes the sliding characteristics of the resin; the resin lining is greatly improved in compression strength and resistance to deformation;
and the resin lining permits rapid heat dissipation, providing an improved critical PV value. The sliding part of the invention is produced simply by pouring a monomer into the clearance between the sliding interfaces, which results in low production cost.
The sliding part of this invention may be advantageously applied to various functional parts where sliding motion frequently and repeatedly takes place, such as a crank shaft and crank journal bearing, cam shaft and cam-shaft journal bearing, and transmis-sion.
According to the method of this invention, the resin lining is formed in situ by monomer casting. Since the resin lining is in the form of a thin layer, a sliding part with high accuracy and high performance can be produced regardless of the dimensional accuracy of the associated shaft and bearing. In adidtion, the monomer casting can be accomplished without the application of pressure and heat, and consequently the sliding part can be produced easily and at a low cost.
~ 28S7~3 The invention is described with reference to a slide spline consisting of an internal spline and an external spline. Nylon monomer is poured into the clearance between the two components and cured therein so that a resin lining is formed on either of the two components. In the preferred slide spline, at least either the internal spline or external spline is provided with a groove to receive excess monomer so that no flash is formed. The absence of flash eliminates the need for fabrication operations, such as deflashing, which impairs the product precision and slide performance.
S PEC I F I C EXAMP LES
In Fi~s. 2 and 3, there is shown an external spline 1 and an internal spline 2 which is fitted into and reciprocatably sup-ported by the external spline. There is also shown a resin lin-ing 3 of nylon-6 formed on the inner surface 4 of the external spline 2. A centering pin 5 and centering hole 6 are provided at an end of the internal spline 2.
The sliding part in this example was produced as follows:
First, the external spline 1 was coated with a primer and the in-ternal spline 2 was coated with a release agent. The external spline 1 and the internal spline 2 were preheated to 130 to 160C
within which temperature range the monomer of nylon-6 poly-merizes. A proper amount of the monomer of nylon-6 containing the polymerization initiator (lactam anion and acyl lactam) was poured into the external spline 1, and then the internal spline 2 : . . . , . . . - . . .
85~723 was fitted into the external spline 1, whereby the clearance (t =
about 0.2 mm) between the external spline and the internal spiine was filled with the nylon monorner. The nylon monomer was poly-merized at a temperature of 130 to 160C. This resulted in the formation of a resin lining 3 on the surface 4 of the external spline 1. The sliding part thus produced allowed the internal spline 2 to slide on the resin lining 3 without any play.
In this example, the sliding part of the invention was applied in the prodiction of a manual transmission gear, as shown in Fig. 4. This gear has a bearing 7, a shaft 8 fitted into the bearing and rotatably supported by the bearing, and a resin lin-ing 3 of nylon-6 which is formed on the bearing surface 9 of the bearing 7 in the same manner as in Example 1. This sliding part exhibited outstanding sliding performance without any play.
In this example, the sliding part of the invention was applied in the production of a slide spline 11 as shown in Figs.
5 to 7. This slide spline has an external spline 12 and an in-ternal spline 13 slidably fitted into the external spline 12.
The external spline 12 has a cylindrical shape with a bottom 12a.
The inner surface of the cylinder has spline serrations 14 extrending in the longitudinal direction. The spline serrations 14 are defined by squares 15 and trapezoids 16 projected and re-cessed alternatively at regular intervals on the periphery. The bottom 12a of the cylinder is connected to a rod 12b having an ~ 5~3 end attached to an additional component (not shown). A groove 17 as best shown in Fig. 5, is formed at the upper inside o~ the ex-ternal spline 12 and serves as a well for excess resin.
The internal spline 13 has a cylindrical shape with a base attached to an additional component (not shown) through the fix-ing member 18. The external surface of the cylinder has spline serrations 19 extending in the longitudinal direction. The spline serrations 19 are defined by squares 20 and trapezoids 21 projected and recessed alternately at regular intervals on the periphery.
The internal spline 13 is fitted into the external spline 12 so that a clearance 22 is formed between the spline serrations 14 and the spline serrations 19. This clearance is filled with nylon-6 forming the resin lining 23 to reduce frictional resis-tance. The resin lining is formed on either the spline ser~a-tions 14 of the external spline 12 or the spline serrations 19 of the internal spline 13.
Prior to the formation of the resin lining 23, a release agent is applied to either the spline serrations 14 of the exernal spline 12 or the spline serrations 19 of the internal spline 13, according to which side is to constitute the substrate for the resin lining. The clearance 22 bewtween the spline ser-rations 14 and the spline serrations 19 is then filled with the resin lining material, which is molten nylon. The molten nylon Eills the clearance completely and an excess 24 of the molten nylon stays in the groove 17, which serves as a well. This arrangement prevents formation of flash 30, as shown in Fig. 2.
.~
" ' "
~2~ 3 ,`.
The resin lining material in the clearance 22 adheres to either the spline serrations 19 or the spline serrations 14 depending upon which of these components is not coated with a re-lease agent. The resin lining material shri.nks during curing to form a very small gap that permits the mutual sliding motion of the two splines.
In this~example, the sliding part of the invention was applied in the production of a slide spline, as shown in Figs. 8 to 10. This slide spline is identical to that of Example 3, ex-cept that the groove 77 serving as a well for excess resin lining material is formed at the upper portion of the internal spline,
resin-coated bushing. (B) There are sliding parts constructed of a bearing with the bearing surface thereof directly coated with a resin and a shaft machined to fit into the bearing.
The sliding parts belonging to category (A) have the follow-ing disadvantages: (1) Both the lining and the shaft should have a considerably high dimensional accuracy, which sometimes ~8~3 needs the selective fitting of accurately matching parts. (~) Depending on the shape of the bearing surface, it may be diffi-cult to fit the lining (3) The production cost of the lining is high. On the other hand, the sliding parts belonging to cate-gory (B) have the following disadvantages. (1) The machining of the shaft is indispensable, which adds to the cost of the sliding part. (2) The machining of the shaft should be performed with high accuracy and selective fitting may be necessary in some in-stances.
SUMMARY OF THE INVENTION
It is an object of the present invention to provide a sliding part having a highly accurate clearance at sliding interfaces and outstanding sliding performance.
It is another object of the present invention to provide a method for producing with ease and certainty a sliding part of high accuracy and high performance regardless of the dimensional accuracy of the shaft and bearing.
The present invention is based on the so-called monomer casting in which a molded item is produced by castiny a monomer, followed by polymerization and curing, as employed in the case of nylon monomer casting.
The sliding part of this invention comprises a bearing, a shaft which is rotably or reciprocatably supported by and fitting into the bearing, and a lining of resin formed on the bearing surface of the bearing. The resin lining is formed by pouring a low-viscosity monomer or prepolymer into a clearance between the .
~2~3S'7~
bearing surface and the shaft and permitting the monomer or prepolvmer to polymeriæe or cure in situ. The shaft slides on the resin lining.
The shaft may constit~te an internal spline and the bearing an external spline. Either the external spline or the internal spline may be provided with a groove constituting a well for receiving resin poured into the clearance between the external and internal splines. The resin lining may be a thin film of polyamide resin, urethane resin, epoxy resin or polyester resin The method of this invention for producing the sliding part by monomer casting is accomplished by pouring a low-viscosity monomer or prepolymer into a clearance between a shaft and the bearing surface of a bearing. ~he shaft is fitted into the bearing and is rotatably or reciprocatably supported by the bearing and specifically the bearing surface. After polymeriza-tion and curing, the monomer forms a resin lining on the bearing surface of the bearing, and the shaft slides on the resin lining.
BRIEF DESCRIPTION OF THE DRAWINGS
Fig. 1 is a graph showing the relation between the thickness and the compression strength of the resin lining of the present invention;
Fig. 2 is a sectional view of the sliding part of Example 1 of this invention;
Fig. 3 is a plan view of the sliding part as shown in Fig.
~;
"'' ' ' ~' ' '' .
. ~2~'7~3 Fig. 4 is a sectional view of the sliding part of Example 2 of this invention;
Fig. 5 is a sectional view of the sliding part of ~xample 3 of this invention;
Fig. 6 is an enlarged sectional view taken along the line VI-VI of Fig. 5;
Fig. 7 is an enlarged sectional view taken along the line VII-VII of Fig. 5;
Fig. 8 is a sectional view of the sliding part of Example 4 of this invention;
Fig. 9 is an enlarged sectional view taken along the line IX-IX of Fiy. 8; and Fig. 10 is an enlarged sectional view taken along the line X-X of Fig. 8.
The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and, together with the description, serve to ex-plain the principles of the invention.
DESCRIPTION OF THE PREFERRED EMBODIMENTS
The sliding part of this invention is produced in the fol-lowing manner. At first, a shaft is fitted into a bearing and rotatably or reciprocatably supported by the bearing, primarily in the ,axial direction. The bearing may be separate and indepen-dent or integral with the machine proper. Next, a monomer or a low-viscosity prepolymer of a suitable resin, such as polyamide resin, urethane resin, epoxy resin or pPlyester resin, which may ~Z8S~Z3 be incorporated with a polymerization initiator according to need, is poured into the clearance between the shaft and the bearing surface of the bearing. The monomer or prepolymer is polymerized or cured by heating or irradiation. A resin lining is thus formed on the bearing surface in the existing clearance between the shaft and the bearing surface of the bearing. Prior to the pouring of a monomer, the bearing should be provided with proper masking excluding the bearing surface, because it is dif-ficult to remove the unnecessary resin lining after polymeriza-tion. For the uniform, smooth polymerization of the monomer, it may be desirable to preheat the shaft and bearing to a tempera-ture suitable for polymerization prior to the pouring of the monomer. In addition, it is also desirable to apply a proper primer to the bearing surface of the bearing and a proper mold release to the shaft. The primer ensures the firm adherence of the resin lining to the bearing surface of the bearing. The polymerization initiator shoulcl be properly selected according to the monomer used. For example, Eor caprolactam (monomer or nylon-6), lactam anion and acyl lactam are recommended.
The polymerization of the monomer is usually accompanied by a certain degree of molding shrinkage. This molding shrinkage gives rise to a very small amount of clearance between the shaft and the resin lining when the resin lining is formed. The amount of clearance is as Eollows in the case where the resin lining is made of nylon-6. The molding shrinkage of nylon-6 is 14 to 16%
(by volume) and it corresponds to a linear shrinkage of 4 to 5%
1~2~35~
across the thickness or cross-section when nylon-6 is used as a thin film. If the clearance between the shaft and the bearing surface is about 0.2 mm and the resin lining of nylon-6 is formed in the clearance, the shrinkage of nylon-6 is about 8 to ~0 um.
It follows, therefore, that a very small amount of clearance (about 8 to 10 um) is formed between the shaft and the resin lin-ing. Such a small anmount of clearance will be possible only with with extremely accurate machining. According to the present invention, the high precision clearance can be obtained easily even though the shaft and the bearing are characterized by low dimensional accuracy. The sliding part of the present invention is formed in situ,and according to the method of the invention, it is not necessary to select a shaft and a bearing that mate with each other. In addition, it is not necesary to machine the shaft and the bearing to high accuracy to achieve a close fit.
In spite of the good sliding characteristics, resin linings have not been effectively utilized for sliding parts that gener-ate significant frictional heat resulting ~rom repeated sliding motion because of the following disadvantages. Resins undego a great amount of creep or deformation at high temperatures, and they exhibit low thermal conductivity, which is responsible for their low critical PV value. In this invention, these disadvan-tages are eliminated. The resin lining produced in accordance with this invention in the form of a thin film between the shaft and the bearing has a greatly increased compression strength resulting from the support provld~d by the bearing metal. In the ~35~7~3 case of resin lining made of nylon-6, the compression strength remarkabl~ increases if the lining is thinner than about 0.6 mm, as shown in Fig. 1. In addition, such a thin resin lining per-mits rapid heat dissipation and consequently provides an improved critical PV value. Thus the sliding part of this invention has high performance. That is the resin lining fully utilizes the sliding characteristics of the resin; the resin lining is greatly improved in compression strength and resistance to deformation;
and the resin lining permits rapid heat dissipation, providing an improved critical PV value. The sliding part of the invention is produced simply by pouring a monomer into the clearance between the sliding interfaces, which results in low production cost.
The sliding part of this invention may be advantageously applied to various functional parts where sliding motion frequently and repeatedly takes place, such as a crank shaft and crank journal bearing, cam shaft and cam-shaft journal bearing, and transmis-sion.
According to the method of this invention, the resin lining is formed in situ by monomer casting. Since the resin lining is in the form of a thin layer, a sliding part with high accuracy and high performance can be produced regardless of the dimensional accuracy of the associated shaft and bearing. In adidtion, the monomer casting can be accomplished without the application of pressure and heat, and consequently the sliding part can be produced easily and at a low cost.
~ 28S7~3 The invention is described with reference to a slide spline consisting of an internal spline and an external spline. Nylon monomer is poured into the clearance between the two components and cured therein so that a resin lining is formed on either of the two components. In the preferred slide spline, at least either the internal spline or external spline is provided with a groove to receive excess monomer so that no flash is formed. The absence of flash eliminates the need for fabrication operations, such as deflashing, which impairs the product precision and slide performance.
S PEC I F I C EXAMP LES
In Fi~s. 2 and 3, there is shown an external spline 1 and an internal spline 2 which is fitted into and reciprocatably sup-ported by the external spline. There is also shown a resin lin-ing 3 of nylon-6 formed on the inner surface 4 of the external spline 2. A centering pin 5 and centering hole 6 are provided at an end of the internal spline 2.
The sliding part in this example was produced as follows:
First, the external spline 1 was coated with a primer and the in-ternal spline 2 was coated with a release agent. The external spline 1 and the internal spline 2 were preheated to 130 to 160C
within which temperature range the monomer of nylon-6 poly-merizes. A proper amount of the monomer of nylon-6 containing the polymerization initiator (lactam anion and acyl lactam) was poured into the external spline 1, and then the internal spline 2 : . . . , . . . - . . .
85~723 was fitted into the external spline 1, whereby the clearance (t =
about 0.2 mm) between the external spline and the internal spiine was filled with the nylon monorner. The nylon monomer was poly-merized at a temperature of 130 to 160C. This resulted in the formation of a resin lining 3 on the surface 4 of the external spline 1. The sliding part thus produced allowed the internal spline 2 to slide on the resin lining 3 without any play.
In this example, the sliding part of the invention was applied in the prodiction of a manual transmission gear, as shown in Fig. 4. This gear has a bearing 7, a shaft 8 fitted into the bearing and rotatably supported by the bearing, and a resin lin-ing 3 of nylon-6 which is formed on the bearing surface 9 of the bearing 7 in the same manner as in Example 1. This sliding part exhibited outstanding sliding performance without any play.
In this example, the sliding part of the invention was applied in the production of a slide spline 11 as shown in Figs.
5 to 7. This slide spline has an external spline 12 and an in-ternal spline 13 slidably fitted into the external spline 12.
The external spline 12 has a cylindrical shape with a bottom 12a.
The inner surface of the cylinder has spline serrations 14 extrending in the longitudinal direction. The spline serrations 14 are defined by squares 15 and trapezoids 16 projected and re-cessed alternatively at regular intervals on the periphery. The bottom 12a of the cylinder is connected to a rod 12b having an ~ 5~3 end attached to an additional component (not shown). A groove 17 as best shown in Fig. 5, is formed at the upper inside o~ the ex-ternal spline 12 and serves as a well for excess resin.
The internal spline 13 has a cylindrical shape with a base attached to an additional component (not shown) through the fix-ing member 18. The external surface of the cylinder has spline serrations 19 extending in the longitudinal direction. The spline serrations 19 are defined by squares 20 and trapezoids 21 projected and recessed alternately at regular intervals on the periphery.
The internal spline 13 is fitted into the external spline 12 so that a clearance 22 is formed between the spline serrations 14 and the spline serrations 19. This clearance is filled with nylon-6 forming the resin lining 23 to reduce frictional resis-tance. The resin lining is formed on either the spline ser~a-tions 14 of the external spline 12 or the spline serrations 19 of the internal spline 13.
Prior to the formation of the resin lining 23, a release agent is applied to either the spline serrations 14 of the exernal spline 12 or the spline serrations 19 of the internal spline 13, according to which side is to constitute the substrate for the resin lining. The clearance 22 bewtween the spline ser-rations 14 and the spline serrations 19 is then filled with the resin lining material, which is molten nylon. The molten nylon Eills the clearance completely and an excess 24 of the molten nylon stays in the groove 17, which serves as a well. This arrangement prevents formation of flash 30, as shown in Fig. 2.
.~
" ' "
~2~ 3 ,`.
The resin lining material in the clearance 22 adheres to either the spline serrations 19 or the spline serrations 14 depending upon which of these components is not coated with a re-lease agent. The resin lining material shri.nks during curing to form a very small gap that permits the mutual sliding motion of the two splines.
In this~example, the sliding part of the invention was applied in the production of a slide spline, as shown in Figs. 8 to 10. This slide spline is identical to that of Example 3, ex-cept that the groove 77 serving as a well for excess resin lining material is formed at the upper portion of the internal spline,
Claims (7)
1. A sliding part comprising a bearing, a shaft rotatably or reciprocatably supported by and machined to closely fit into the bearing, and a thin film of resin having a thickness of no more than 0.6 mm formed on a bearing surface of the bearing by pouring a low-viscosity monomer or prepolymer into a clearance between the bearing surface and the shaft and permitting the monomer or prepolymer to polymerize or cure in situ, said shaft being slidable on said thin resin film.
2. A sliding part as set forth in claim 1, wherein the shaft is an internal spline and the bearing is an external spline.
3. A sliding part as set forth in claim 2, wherein at least one of said external spline and said internal spline is provided with a groove constituting a well for receiving an excess of the resin poured into the clearance between the two splines.
4. A sliding part as set forth in claim 1, wherein the resin lining is a thin film formed by polymerization and curing of a monomer or prepolymer of a resin selected from the group consisting of polyamide resin, urethane resin, epoxy resin, and polyester resin.
5. The sliding part as set forth in claim 4, wherein said resin contains a polymerization initiator.
6. A method for producing a sliding part, comprising pouring a low-viscosity monomer or prepolymer into a clearance between a shaft and a bearing surface of a bearing, said shaft machined to closely fit into said bearing and being rotatably or reciprocatably supported by said bearing surface, polymerizing or curing the monomer or prepolymer to form a thin resin film having a thickness of no more than 0.6 mm on said bearing surface of said bearing for sliding of said shaft thereon.
7. A method for producing a sliding part, comprising pouring solely a low-viscosity monomer or prepolymer into a clearance between a shaft surface of a shaft and a bearing surface of a bearing with said shaft surface being masked from contact with said monomer or prepolymer, said shaft being fitted into said bearing and being rotatably or reciprocatably supported by said bearing surface, polymerizing or curing the monomer or prepolymer to form solely a resin lining on said bearing surface of said bearing for sliding of said shaft thereon and providing a groove adjacent to said shaft and bearing surfaces, said groove constituting a well for receiving an excess of the monomer or prepolymer poured into the clearance.