CA1090545A - Terminal connectors and method of making same - Google Patents

Abstract

CHANNEL TYPE TERMINAL CONNECTORS AND METHOD OF MAKING

Abstract of the Disclosure Forming of wire contacting jaws for a channel type electrical terminal of conductive sheet metal is disclosed, without diminishing the length of the terminal, by first obtaining a stretching of the conductive metal into a preliminary displaced configuration in a first die. Then reverse forming and coining the metal into a jaw formation deeper and narrower than the first configuration. Then in a third die substantially removing the reverse curvature, with added coining and stretching of the metal, into a final jaw formation which is deeper and narrower than that obtained in the second die, without rupture of the metal. Slight reverse curvature is retained adjacent the juncture of the sides of the jaw with the body of the terminal.

Description

1~9054S

This invention relates to wire termination systems in which a wire to be held in a terminal may be held between a pair of jaws or within sets of jaws. More especially it relates to a method of forming generally U-shaped jaws in a terminal without shortening the original terminal blank and without rupturing the metal used therefor.
Terminal connectors of the type presently involved are formed of highly conductive metal which typically is shaped to provide an elongated channel. Insulation piercing jaws are provided within and along the edges of the channel, as disclosed more specifically in McKee and Witte Canadian application Serial No. 214,478, filed November 22, 1974, and McKee Canadian Patent 1,027,199, issued February 28, 1978. In use, an insulated wire is forced into the channel so that the jaws penetrate the insulation and forcibly contact the conductor of the wire.
Terminals of the type here involved typically are used where space is at a premium and miniturization is im-portant, as in molded, insulating receptacles designed to contain a large number of terminals. A primary examine is in connectors for 50-wire telephone cables. In such recep-tables the tolerances are close, frequently on the order of just a few thousandths of an inch. In order to accommodate such tolerances it has been recognized that the terminals must be of precise uniform dimensions.
The dimensional accuracy is important to insure proper configurations and spacings for very high reliability of forming good electrical contact of the jaws with the 109~545 conductor of the inserted wire. High compressive strength of the jaws also is important to maintaining the spacing tolerances under the compressive stresses imposed by forcibly inserting a wire when forming a termination, i.e., to avoid compressive yielding or failure of the jaws. The compressive stresses may be of a high order, as in relying upon a camming or wedging action between the wire and the jaws to effect an intimate gas-tight contact therebetween, and which may involve forcible displacement or distortion of the material of the wire conductor by that action. It is also desirable to maintain the side and bottom walls integral with one another, and to avoid deformation of the bottom wall which would increase the required overall depth of the terminal.
All of the foregoing problems and requirements are exacerbated by the small size of the terminals involved. Thus there is very little material available for forming the necessary configurations or to lend mechanical strength.
These factors require close adherence to designs providing high stress capabilities relative to the inherent strength ~0 of the material available, including the geometry of the designs. Finally, highly conductive materials must be used in such terminals to maximize conductivity. However, practical and economical materials meeting these parameters usually are of low ductility and more particularly have a low to medium elongation capability, e.g., 5% to 10%. This means that the materials will not accommodate significant tensile stretching without tensile cracking and failure.
It is an object OL this invention to provide methods for forming terminals of the aforementioned type, and which methods overcome the noted problems and meet the related desirable parameters.

-2-Accordingly, there is provided: the method of forming a wire contacting jaw in an electrical wire terminal comprising: disposing a flat sheet of current conductive metal upon a first ribbed die face and impressing a portion of the sheet upon said face, forming thereby a first depression in said sheet portion, moving the first depression onto a second die face having ribbing therein of deeper dimension than the first die face and impressing the first depression deeper than the depth thereof formed on the first die face, moving the first depression onto a third die face having ribbing therein of deeper dimension than the second die face and impressing the first depression deeper than the depth thereof formed on the second die face, and folding the sheet into an elongated wire receiving body having a bottom and facing sides defining a wire receiving channel wherein the first depression is disposed from one of said facing sides.
Brief Description of the Drawings For a complete understanding of this invention reference should be made to the accompanying drawings in which:
Fig. 1 is a top plan view of a section of a blank of a flat metal sheet for use on a progressive die and showing a series of terminals in various stages of formation, Fig. 2 is a cross-sectional view of a portion of the blank shown in Fig. 1, taken along the line 2-2 in Fig. 1, disposed between a first ribbed die and a first mating die, lQ90545 Fig. 3 is a perspective view of a broken away portion of the blank shown in Fig. 1, at approximately the cross-sectional portion shown in Fig. 2, but showing the full width of a terminal blank as indicated at bracket 3 in Fig. l;
Fig. 4 is a cross-sectional view of a portion of the blank shown in Fig. 1, taken along the line 4-4 in Fig. 1, disposed between a second ribbed die and a second mating die;
Fig. 5 is a perspective view of a broken away portion of the blank shown in Fig. 1, at approximately the cross-sectional portion shown in Fig. 4, but showing the full widthof a terminal blank as indicated at bracket 5 in Fig. l;
Fig. 6 is a cross-sectional view of a portion of the blank shown in Fig. 1, taken along the line 6-6 in Fig. 1, disposed between a third ribbed die and a third mating die;
Fig. 7 is a perspective view of a broken away portion of the blank shown in Fig. 1, at approximately the cross-sectional portion shown in Fig. 6, but showing the full width of a terminal blank as indicated at bracket 7 in Fig. l;
Fig. 8 is a perspective view of a completely formed terminal separated from the blank shown in Fig. l;
Fig. 9 is a perspective cross-sectional view of a plurality of terminals identical to that shown in Fig. 8, mounted in a receptacle body frequently referred to as an insulating high density connector body;
Fig. 10 is a cross-sectional and elevational view of a pair of terminals ldentical to the terminal shown in Fig. 8 taken along the line 10-10 in Fig. 9 and including a pair of insulated conductor wires, not shown in Fig. 9, disposed for insertion into the terminals; and Fig. 11 is a cross-sectional and elevational view of the pair of terminals shown in Fig. 10 illustrating insertion of the wiresinto the terminals.
DETAILED DESCRIPTION O~ THE PREFERRED EM~ODIMENT
Considering first Figs. 1-7, the improved method of making a terminal for use in a wire termination system is illustrat-ed by showing successive steps in the formation of the terminal.Such terminals are especially useful as solderless terminations in high density connectors, particularly those used in miniturized electrical and electronic components. It will be recognized that the metal used in the formation of such terminals, particularly those of the present invention, is quite thin but only slightly ductile. One especially suitable metal is cadmium bronze alloy 961 in 0.006 inch sheets. Ordinarily the tensile strength of this material is on the order of 73,000 psi., and it has an elongation capability of about 6-8%, preferably with a minimum of 7%.

10~0545 ~ ig. 1 shows a series of terminal blanks of con-ductive metal on which successivc steps of formation have been carricd out in accordance with the present invention. A pro-gressive die blank 2 is stamped to form foldable configurations such as the configuration 4 which are ultimately folded into terminals such as terminal 6. Sheet 2 may be as long as necessary to fit both the stamping operation and the terminal forming dies to be described later. Stems such as those shown at 8 and 10 maintain the foldable and folded configurations evenly disposed througl-out the length of the metal blank. The stems 8 may be finally severed, as at stem end 12, from a strip 14 at the outer edge of blank 2, and the stems 10 may similarly be severed from a strip 16 in the center of blank 2. A completely finishea and separated ter~inal 6 is shown as 6A in Fig. 8.
As shown in Fig. 1, the center strip 16 of the metal blank 2 includes a plurality of regularly spaced apertures 18 which function as an indexing means for moving blank 2, including the foldable configurations 4, between terminal forming prosressive die faces. It should be understood that although the foldable configurations 4 are illustrated in Fig. 1 in individual and successively more finished form from left to right, it is possible to shape those configurations in groups having the same form so that groups of the configurations 4 would bé
shaped identically. In that event the blank would be adYancea more rapidly in accordance with the spacings of the groups.
; Also, it will be noted that Fig. 1 illustrates forming the foldable configurations 4 on both sides of the center strip 16 in blank 2. As viewed in Fig. 1, the configurations 4 below .

, ~ _ ~ _ the strip 16 are ex~ctly identical to those located immediately ab~ve them. Since~ the resulting terminals are used in large numbcrs (a 2-1/8 inch long connector may contain as many as fifty terminals, for cxample), it is desirable to obtain high production rates. By duplicating the configura-tions, and the steps involvcd in making them, on each side of the metal blan~ 2, a number of terminals can be made very rapidly with a minimum number of movements of the metal blank and a correspondingly lesser unit cost.
hlhether the apertures 18 or other indexing means are located along the center portion of blank 2 or along one edge thereof, it is important that the metal blank 2 remain the same width throughout as the blank progresses through the equipment for forming the terminals. ~niform width and lack of distortion of the blanl; in this respect insures that the shearing of the edge strips 14 and center strip 16 from the stems 12 and 10 will result in finished terminals of uniform dimensions. Such uniformity can be achieved notwithstanding the formation of several impressed undulations in the sides of the terminals, shortly to be described. Formation of such undulations would be expected to rupture the material or to cause deformation of parallel connected flat portions of the blank. The former of course is unacceptable and the latter would pull the outer edge portions 14 of the blank closer together, or distort the uniform linear configuration of the center strip 16, and not only create a substantial number of variations in the width of the blank but also distrub the uniform oricntation of the components of the terminals themselves.
The imprcssion of the undulations just referred to, and to which the present invontion is directed, is particularly illustratod at Figs. 2-7, ~u~ is best perceived with reference .
B ~ `

to the fol~able configuration of the blan~ :a in ~ig. 1 and the completely finished terminal 6A in Fig. 8. Confi~ur~-tion 4a includc.s notches 20 and i5 flat except for impres-sions and protuberances 22 and 24 which are not directly in-volved in the present invention. Configuration 4a is formedas the result of preceding stampin~ steps perforned upon the flat m~tal blan.t; 2. ~lso included in configuration 4a are slots 26 (which alternatively may be sheared slits, ~ithout removing material) and which are prc-ferably formed in pairs opposite the notches 20, so that each notch is disposed along the edge of the foldable configuration pointing at approxi-mately the midpoint of a cor,panion severance 26. The por-tions of each blank 4 comprising the sections between the slots 26 and the respective blank edges together with ad-joining sections at each end of those sections are formedinto jaws in accordance with this invention.
The end result of the desired shaping of configura-tion 4a is shown in Fig. 8, a completed terminal 6A ready for installation in a receptacle body such as an insulating hih Bensity connector body. The stem ends 10 and 12 have been appropriately severed, as by shearing, from the metal blank 2. Side or panel portions 28 and 30 of the terminal have been folded into upright parallel positions, at approximately right angles to a terminal body base panel 32, thus forming a narrow channel bod5~ 34 extending longitudinally of the terminal. The notches 20, which have been beveled, are disposed along the top edges of the sides 28 and 30, and slots 26 are disposed at the bottom edges at the junctions of the ~ides with the terminal body base 32. The jaws 36 extend into the channel for contacting the electrical conductor B -~-of a wire to be disposed wi~hin the channel. Shoulders 38a are provided at the junctures of the outer edges of the jaws 36 with nominally planar portions 40a of the sides, and shoulders 38b are forme~ at the junctures of the inner edges of the j~ws with yoke portions 40b of the sides inter-mediate the jaws.
By way of a more specific illustration, in a terminal 6A for use in telephone wire connectors and in the production of which this inventlon is particularly advantageous, the channel body is about 0.050" wide (outside dimension), about 0.058" high and about 0.40"
long from the outside of tab 174d to the near end as seen in Fig. 8. Such terminals are formed of the afore-mentioned 0.006" cadmium bronze alloy sheets and are used lS in a solderless ribbon-type miniature connector made and sold by TR~ Inc., Elk Grove Village, Illinois. Two pairs of opposed jaws 36 are provided on 0.080" centers in each terminal, with each jaw being about 0.022" deep from the out-side surface of the respective channel side. Each jaw is about 0.007" outside radius at the inner nose, and about 0.030" wide between the centers of curvature of the junctions between its legs and the respective side panel, which curves are of about 0.006" radius. Each jaw is beveled at the top and tapers inward slishtly therebelow, as seen in Figs. 8, 10 and 11. Each slot 26 is 0.040" long and separates the respective jaw from the base panel 32.
The forming of the jaws 36 is accomplished in steps which result in succes~ive forms of the jaw-forming portions of the blanks as shown by the blanks 4b-4d in B

Fig. 1 and illustrated cross-sectionally and in perspective in Figs. 2-7. In Fig. 2 a portion of the side 28 of fold-able configuration 4b from which a pair of jaws 36 is to be formed is shown between a first ribbed die face 42 of a die 48 and a first mating die face 44 of a die 46. Both die faces are of configurations to include a plurality of ribs and valleys.
When the dies are moved together (as in Fig. 2 as by raising or lowering the first die 46, depending upon orientation of the die faces) the intervening two jaw-forming portions of the blank are formed into two broad shallow depression or wave configurations 50a and 50b by first ribs 52 on the die face 44 and first valleys 54 in the die face 42. In this initial step the mating dies are not closed on the blank completely or "bottomed". The first depressions 50 are shaped such that the metal configuration 4b is not ruptured despite the fact that the material may have very limited elongation capabilities. One of the prime objectives of the first step is to form each depression 50 as the beginning of a jaw by causing the metal to flow and stretch over the longest available length of material by a minimum degree of stretch in any one section without rupture of the material.
The initial shaping of the jaw portions of the blanks, in the manner just described, results in a blank with the shallow wave formation 56 of two depressions 50a and 50b as shown in Fig. 3 (see also the left side of con-figuration 4b in Fig. 1). These depressions extend the full width of the jaw-forming portions, and are raised or otherwise displaced from the plane of configuration 4b, distorting one edge 58 of each of slots 26 while leaving the B lo ~K--10905~5 other edges 60 generally co-planar with the terminal body base 32 which remains flat. The zenith or peak of each depression 50 is indicated by a dashed line 62 and is perpendicular to a vertical plane containing the principal longitudinal axis of the terminal body base 32. These peaks also coincide with the edges of the notches 20 at their deepest and closest penetration toward the distorted edges 58 of slots 26.
For the specific example given above, the shallow wave forms created in the preliminary shaping of the jaws may be obtained by using a die 46 having rigs 52 spaced on 0.080 centers, with outer ends of 0.015" radius and which protrude 0.20" from the otherwise generally flat face of the die.
Corresponding valleys 54 may be 0.042" wide and 1/32" deep, with 0.019" radius shoulders at each side. It has been found by using dies having such dimensions and the cadmium bronze alloy metal to form a terminal, that there is some spring-back of the metal depressions 50 when the ribbed die and the mating die faces are separated. The depressions 50 are pressed to a depth such that, after being released from the dies, their inner depth is on the order of 0.010"
i.e., 0.016" to 0.018 outer height measured vertically from the outer surface of their peaks to the opposite flat surface of the side panel.
By approaching the formation of jaws 36 (see Figs. 7 and 8) gradually and over a maximum length, that is, by separately performing the first step of making shallow wave forms in the otherwise flat sides of the terminal blank in the manner just described, the side portions 28 of terminal 6A tFig. 8) permit the creation of the wave forms therein as demonstrated in Figs. 2-3 without distortion or shortening of either base 32 or of B ~/

the remai~der o~ ~he sides 28 ~nd 30 despit~ th~ fact that the sides and base are integrally connected. Primarily, the wave forms (such as depressions 50) are obtained by dispersed stretching and in~low of metal from portions of the configura-tion 4b adjacent but beyond the ends of the sections bet~7eenthe notches 2p and slots 26, as well as by dispersed stretch-ing within those sections. Some displacement of the por-tions of the blan~ intermediate the wave forms and the notches 61 (Fig. 1, and which portions are about 0.020"
wide), apparently occurs as there is a change in the angle of the adjacent edge of this notch as the depressions 50 are formed, compare blanks 4b-4d with blank 4a. However, the same displacement is not available between the waves or at the opposite end, where all of the blank remains integral and the elongation must occur by stretching. The stretching is not concentrated and is relatively uniform throughout the metal being worked.
In examining the second step of crea~ing jaws 36, attention should be given to Figs. 4 and 5 as well as to confi5uration 4c in Fig. 1. The jaw-forming portions of the blank, after having undergone the initial forming step shown and described with respect to configuration 4b in ~igs. 2 and 3, are placed between a second ribbed die face 64 of a die 68 and a second mating die face 66 of a die 70. The blanks are located with the previously-formed depressions 50 centered on ribs and valleys of these die faces to be described. Preferably these dies are then fully closed (~bottomed") against the blank to reform and modify the pre-liminary shapina of the terminal side panel in the areas in-cluding the deprcssions 50, as shown for example in Fig. 4.Thereby, a number of significant modifications are made to reform the depressions toward their ultimate jaw form.

B ~

- 10905~5 Referring to the die surfaces adjacent the de-pression 50a, as shown in Fi~. 4, the die face 64 includes a second valley 72. The sides 74 and 76 of the second valley 72 converge toward each other as they extend into the body of die G8. At their outermost extrem;ties, ad-jaoent the face 64 of the second ribbed die, these sides are closer together than the sides 78 and 80 of each valley 54 a~ viewed in Fig. 2. At each of those extremities first shoulder ribs 82 and 84 are formed upon the second ribbed die face 64, extending outwardly beyond the generally flat plane of that die face. These ribs provide surfaces which cooperate with first shoulder recciving grooves 86 and 88 in the second mating die face 66 for forming shoulder impressions 90 and 92 in the blanX 4c. Similarly, a rib 94 between the grooves 86 and 88 matès with the valley 72 for reforming the center segment of the depression 50a. The second valley 72 and rib 94 are so dimensioned that the depression 50a may be further deepened within valley ?2 from the preliminary depth of that depression achieved between the first ribbed die face 42 and the first mating die face 44.
In order to insure the reverse curvature (from the curvature formed at the depth of depression 50a) for the formation of shoulder impressions 90 and 92, the face 64 of the second ribbed die 68 may be provided with a shoulder return face portion 96 adjacent the outer extremity of rib 84. A similar shoulder return face portion 98 may be provided adjacent the outer extremity of shoulder 82. The shoulder return face portions 96 and 98 in die face 64, and cooperative shoulders 100 and 102 of the face 66, serve to return lC~ /3 D

~090545 the adjacent portions of thc respcctive side pancl to its normal pla~e relative to the jaw deformations.
The described ribs, shoulders and valleys of die faces 64 and 66 are duplicated for reforming 5 of the depression 50b in the same manner as described for depression 50a, as indicated by the parts identified by the same numerals with a subscript a. I~owever, when it is desired to provide a plurality of jaws 36 in a side panel, as shown, the formation of the shoulder face portions 98 and 102 will be slightly varied from those of the face portions 96 and 100. As shown in Fig. 4, adjacent shoulder return face portions 98 and 98a in the face 64 of die 68 merge with an intervenins arcuate section 104 intermediate shoulders 82 and 82a.
~he center of this section is substantially co-planar with the major face surface of die face 64. Such a section 104 in cooperation with a corresponding portion 105 of the die face 66 which merges with surfaces 102 and 102a provides for a wa~e formation 106 in the side panel between depressions 50a and 50b (which are to be finally ~ formed into jaws 36). The center of this wave is maintained co-planar with the main body of the respective side panel.
The second mating die faces 64 and 66, as above de-scribed, preferably are adapted to be bottomed against the por-tions of blank 4c between those two die faces. Such bottominginsures proper formation of the various depressions and shoulders of the blank, which occurs by reforming the blank to the new configuration while coining and further stretching the metal in the work area, as described further below. At the same time, the remainder of the blank 4c is retained in a flat undistorted form between other flat portions of the dies.

B ~ `

The rcsult of utilizing such co;nplementar~ die faces as described with respect to Fiq. 4 is shown in Pig. 5, albeit Fig. S, likc ~i~. 3, illustrates the use of four sets of die faces rather than two sc's. Since Fig. 5 shows merely a further step in the formation of terminal 6~ (see Fiq. 8), which step is a further ~evelopment of the depressions shown in the frag-mentary portion of the terminal illustrated in Fig. 3, it is only necessary to identify the particular char,ges which have occurred. Portions of each of the original depressions 50 have been xeformed as shoulders 90 and 92, extending on the opposi,e side of the blank 2 from the central segments of depressions. The two sides of each depression 50 have been formed much closer together and the depressions themselves have been narrowed and deepened, with considerable reduction in the included angle defined between these sides.
Of primary importance is the fact that the terminal body base 32 has not been distorted or shortened in any manner. The length of slots 2~ has remained unchanged but despite the increased length of the metal necessary for forming the depressions and adjacent shoulders, the metal has remained unruptured.
The manipulation of the metal in the jaw-forming portions to form the depressions and the shoulders in the step of Fig. 4 includes reforming or reshaping of the stretched wave form of Fig. 3. In addition, and simulta-neously, controlled coining, that is, gradual, measured, compressive forming of the metal is effected in the areas comprising the shoulders 90, 90a, 92 and 92a as those shoulders are formed, along with some additional stretching of the metal throughout the portion being formed. The ,~ _ ~; _ 10905~5 coining is effected in and adjacent the center portions or bends of the arcuate end configurations of the impressions 90, 90a, 92 and 92a, between the outer end of each rib 82, 82a, 84 and 84a and the respective opposed groove 36, 86a, 88 or 88a. The metal is caused to flow into the convolu-tions on the die faces under the influence of pressure exerted through the die faces thus providing reshaping of the metal and avoiding rupture of the metal during the necessary lengthening and bending of the respective portion of the blank to form the described configuration. Any substantial concentrated or uneven tensile stretching of the metal is avoided in order to obviate the possibility of tensile fracture or failure, particularly at the tips of the several bends created in the shoulder and depression curved portions.
The above-described second step achieves quite minute dimensions, especially in obtaining the reverse curvatures provided by the shoulders in each side of each initial depression 50. Whereas, in forming the depressions 50 initially (see Fig. 2), the first rib 52 on the first mating die face 46 may impress each depression 50 into a valley 54 which measures 0.042" wide even at its deepest point, in the second, coining step (see Fig. 4), each de-pression 50 may be impressed into a valley 72 which may measure only about 0.025" where left and right sides 74 and 76 join shoulders 82 and 84, respectively.
Depressions 50a and 50b, as viewed in Fig. 5, include convex curvatures having their peaks along zenith line 62. Looking at the same face of sides 28 and B ~

30, reverse, or concave, curvatures are formed at the shoulders 90, 92, 90a and 92a which extend from the outside edgcs of the jaw-forming portions 50a and 50b to the slots 26. The nadirs of these shoulders are approximately ali~ned with the ends of the slots 26, as illustrated by dashed lines 112 and 114. A dashed line 116 designates the zenith of the arcuate t-ave formation 106 intermediate the shoulders 92 and 92a, which zenith extends perpendicularly toward an imaginary line 118 aligned with the inside edges of slots 26.
The section 106 extends between an imaginary line 120 approximately at the outside edges of slots 26 to the outer edge of the panels and is shaped to present a convex surface on the same face of side 28 as the convex surfaces of depressions 50, with the outer edges leading downward to the shoulder ribs 92-92a. Creases at 122 accommodate the offset of the outer portions of shoulders 90, 90a, 92 and 92a.
The die faces 64 and 66 are of configurations and dimensions to extend the overall height of the jaw-forming port~ons to slightly greater than 0.018" ~-hen $n the dies as in Fig. 4, as measured from the peaks of portions 50 to the opposite peaks of shoulders 90 and 92.
Due to springback of the material, this height is about 0.018" in the blank 4c of Fig. 5.
In addition to dimensions already noted, a set of specific dimensions for die faces 64 and 66 for the spe-cific example referred to above includes locating the valleys 72-72a and ribs 94-94a on 0.080" centers.

B ~-The valleys 72 and 72a may be of a 0.0135" radii with their uppcrmost surfaces 0.007" above the major flat surface (die line) of die face 64, and each shoulder or rib ~2, 82a, ~4 and 84a may be of 0.0076"
radius with its pea~ 0.007" below the die line. The shoulders 96, 96a, 98, 98a and intervening surface 104 all may be of 0.025" radii, and are tangent at their upper edges with the major flat surface (die line) of die face 64. The centers of curvature of shoulders 82-84 and 82a and 84a are spaced 0.020" on the respective sides of the centerlines of valleys 72 and 72a. Surface 104 is a continuation of the curvature of shoulders 98 and 98a and has its centerline midway between the centerlines of the valleys. These various arcuate surfaces merge directly tlith one another at common tangent lines on the side of each rib, shoulder and valley. Referring to die 'ace 66, each rib 94-94a may be of 0.0076" radius with its outermost peak 0.007"
above the major plane of the respective die face. The valleys 86, 86a, 88 and 88a may be of 0;0135" radii, each having its center of curvature spaced 0.020" on the respective side of the centerline of the related rib and each extending 0.005" below the plane of the die face 66. Shoulders 100 and lOOa are of 0.019" radii and surface 105 is of 0.024" radius including shoulder surfaces 102 and 102a, with each of these surfaces extending tangent to the major plane of die face 66.
~hese various arcuate surfaces also merge directly with one another at co~mon tangent lines.

/~

~09054S
As outlined above, Figs. 2 and 3 illustrate a preferred initial step in the process of forming term~nals 6A, while Figs. 4 a~d 5 illustrate a preferred intermediate step in formi~g such terminals. Figs. 6 and 7 illustrate a preferred third step of terminal formation prior to folding the sides of a processed configuration 4 into a completed terminal 6~.
In Fig. 6 a third ribbed die face 124 of third ribbed die 12~ is opposed by a third m~ting die face 128 of third mating die 130. The processed portion of configuration 4c sho~m in Fig. 5 is positioned between the faces of the third dies and is further formed thereby as in Fig. 6 to produce the configuration 4d as shown in Pig. 7. Similarly to the first processing step illustrated in Fig. 2, but contrary to the intermediate processing step illustrated in Fig. 4, the dies 126 and 130 are not fully bottomed in the third processing step illustrated in Fig. 6.
The ribbed die face 124 includes a third valley 132 having oppcsite sides 134 and 136 which are generally parallel to each other. Curved second ~houlder ribs 138 and 140 connect the major planar portions of the die face 124 with the sides 134 and 136, reapectivelY, of the third valley. Otherwise the face 124 of the third ribbed die adjacent valley 132 lies almost entirely in the same horizontal plane. The valley 132, and more particularly the shoulders 133 and 140, is adapted to receive and further shape depres-sio~ 50a following the processing of such depression /~
B -~ -~090545 bet-leen di~ faces 68 and 70 as in Fig. 4. When it is desired to simultaneously process a plurality of adjacent depressions, such as depressions 50a and 50b, a further third valley 132a identical to valley 132 may be aisposed in the third ribb~d die face 124. Li~e third valley 132, third valley 132a includes opposite sides 134a and 136a which are parallel to each other. Curved second shoulder rihs 138a and 140a conn~ct portions of the die face 124 with the sides 134a and 136a, respectively, of third valley 132a.
The third mating die face 128 includes a third rib projection 142 which has a rounded but much more sharply pointed tip portion 144 than the end of rib 94 on the second matins die face 66, shown in Fig. 4. Rib projection 142 is adapte~
to press depression 50 (see Fig. 6) between the narrowly spaced apart second shoulder ribs 138 and 140 of the third ribbed die face 124, ~hereby those shoulders press and coin the sides of the depression against the sides of the rib 142.
The third rib projection 142 also extends much further ou'.~:ard-ly from third mating die face 128 than does rib 94 of the second mating die face. Accordingly, a depression 50 is further deepened, or elongated, between the third die faces 124 and 128. A similar rib projection 142a may be formed on mating die face 128, spaced apart fror.~ rib projection 142, when it is desired to process a plurality of depres-sions, such as 50a and 50b in configuration 4d (see Fig. 1).
Face 128 of the third mating die 130 further com-plements face 124 of the third ribbed die 126 in that the sides of the third rib projection 142, namely, right side 146 and ~0 B -~ -left side 148, as viewed in Fig. 6, are, for most of their length, closer together than the sides 134 and 136 of vallcy 132. This relationship is maintained even though sides 146 and 14 R are angled to~ard each other as they approach tip portion 144 of tlle third rib projection 142, while sides 134 and 136 of valley 132 are substantially parallel. Second shoulder receiving cur~atures 150 and 152 are situated at the extremities of the sides 146 and 148, respectively, of the third rib projection 142, and these second shoulder receiving curvatures merge with sides 146 and 148 at common tangent lines where rib 142 is narrower than the valley 132 by an amount exceeding tt~ice the thickness of the sheet material being formed, i.e., the total width of the rib 142 at this level plus a thickness of the material on each side would be less than the width of valley 132. The surfaces 150 and 152 curve outward from these merge areas and are tangent with th~ major planar surface of face 128 as illustrated.
When it is desired to process a plurality of depressions, such as 50a and 50b (see Fig. 6), the third rib projection 142a is formed with sides 146a and 148a, and second shoulder receiving curvatures 150a and 152a, disposed identically with respect to valley sides 134a and 136a and second shoulder ribs 138a and 140a, as the rib pro-jection sides and shoulder receiving curvatures of rib 142 are disposed relative to valley 132.
As suggested above in describing the third ribbed die face 124 as being almost entirely in the same horizontal ~/
B

plane, the face 128 of the third mating die 130 also lies almost entirely in a horizontal plane, thus further complementing the third ribbed die face 124 and the valleys and shoulders formed therein. The disposition of the third ribbed die face 124 and third mating die face 128 in horizontal planes may correlate two yo~e forming portions on these die faces, i.e., when a plurality of depressi~ns are to be formed, a planar yoke-forming face portion 154 on die face 124 joins the second shoulder rib 140 adjacent valley 132 with the further second shoulder rib 138a adjacent valley 132a, and an oppositely disposed planar yoke-receiving face portion 156 on the third mating die face 128 joins the second shoulder receiving curvature 152 adjacent rib projection 142 with the further second shoulder receiving curvature 150a adjacent rib projec-tion 142a.
Relative to the dimensions of the die faces set forth above with respect to the first ribbed and first mating dies 48 and 46 and with respect to the second mating dies 68 and 70, the faces of the third rib-bed die and the third mating die may be dimensioned as follows. The valleys 132 and 132a and the ribs 142 and 142a are spaced 0.080" on centers. Both of the valleys 132 and 132a extend inwardly into the third ribbed die face 1/32", and their sides 134 and 136 as well as 134a and 136a are parallel to one another and disposed 0.017" apart.
Each of the second shoulders 138, 140, 138a and 140a has o?~ ~
B -~ -1~9054S

a radius of 0.006". In a complementary manner, the third mating die face 128 is dimensioned so that each of the rib projectio~s 142 and 142a extends outwardly from die face 128 a di~tance of 0.016". The radius of each of the tip portions 144 and 144a is 0.002" and the sides 146 and 148 for projection 142 and 146a and 148a for projection 142 diverge inward from the lines of tangency with the rounded tip portion of each projection toward the horizontal plane of the face 128 of the die, defining an included angle of 40 bisected by a line normal to face 128. Each of the shoulder-receiving curvatures 150, 152, lSOa and 152a is of 0.010" radius, and the centers for each pair of these curvatures are s~metrically disposed about the centerline of the respecti~e rib and are spaced apart 0.029". Using such dimensions for the face of die 130, the yoke-receiving face portion is 0.051" between the centers of the shoulder-receivins curvatures 152 and 150a.
In the third step for further forming the jaws 36, die faces 124 and 128 are engaged with a configuration 4c i.e., ~ portion of side 28 previously processed as il-lustrated in Figs. 4 and 5 and subsequently positioned between die faces 124 and 128. These two die faces then are closed on the blank as in Fig. 6, but the dies preferably are not bottomed.
Since substantially the same forming action occurs in and around the second depression 50b, it is only necessary to specifically describe the third step in forr..ing of depression 50a. The primary stress B ~
~s `

Insos4s points arc in t}lC areas of cngagcment of the terminal blan~.
between the second shoulders 138 and 140 of ribbed die face 124 and the sc-cond shoulder-receiving curvatures 150 2nd 152 of th~ mating die face 128, as illustrated ~tith some exagycration ln Fig. 6, and in the engagement of tip 144 in the apex of th~ depression 50a. Coining of the metal takes place in the side shoulder stress areas, bet~;een the shoulders 138-140 and the curvatures 150-152, apparently alor.g with some further stretching of adjacent portions of the blank, to provide additional length in the jaw-forming portion for further deepenins and for narrowing of the depression 50a.
Moreover, these areas of coining are shifted slightly inward and upward of the shoulders 90 and 92 from the coining of the preceding step, and the stretching is distributed, to avoid tensile rupture of the metal. Simultar.eously there is further stretching and further forming of the metal over the nose 144 to further distribute the stretch-ing and further forming stresses, l.e., in extending the depression around tip portion 144 of the third rib projection 142. In the latter regard, it will be noted that the rib 142 is slightly higher (0.016") than the vertical dimension of the depression 50a of the blank 4c resulting from the preceding step. Allowing for some springback of the metal used, the depression 50a is lengthened to approximately 0.022" (outside height dimension) in the blank 4d.
Because die faces 124 and 128 are not completely bottomed, shoulders 90 and 92 of blank 4c are not completely eliminated in the further forming of blank 4d, but remain in part as slight residual shoulder ridges 158 B ~ `

1(190545 and lG0 (~i~s. G ana 7) o~ thc con~iguration of final should~r forms 3~a and 3~b ~Fig. 8). Correspondingly, neither are the shoulder return portions completely eliminated, since they are presscd into the modified, final forms 162 and 164 of side 28. When more than one depression in side 28 is desired, the wave formation 106 of blank 4c (Fig. 5) is substantially flattened to ~orm yo!~c 166 (Figs. 6 and 7) between the terminuses of shoulder return portion 164 and an adjacent shoulder return portion lG4A associated ~ith depression SOb. In the preferred form of the terminal formins process or method of the present invention, described above in terms of the dimensions of dies used in the specific illustrative process, the distance bet~7een the outermost surfaces o. the shoulders 158 and 160 and the corresponding outer face plane of yoke 166 and the remainder of side panel 28 will generall~ be only a few thousandths of an inch in the blank 4d (Fiss. 6 and 7) and in the ultimate folded form of terminal 6A (38a and 38b in Fig. 8).
It should be particularly noted that in the ~urther forming of blank 4d from blank 4c, as described with reference to Pig. 6, not only is each depression 50 deepened, but also its sides are brought closer together and straightened somewhat, more nearly approaching posi-tions normal to the plane of the respective side panel 28 or 30. Correspondingly, the shoulders at the base .of each depression 50 are formed closer together and their radii of curvature reduced, thereby minimizing the distance between their nadirs or support peaks, i.e., the B ~5 shouldcr ri~ge surfaccs opposite thc dashed lincs 170 and 172 in Fig. 7. The net result is to provide jaws 36 which are of a geometry to withstand large compressivc forces applied outwardly on their noses 176 and resisted by support forces occurring primarily at the ridge lines 170 and 172.
The ribs 142 also may be of appropriate configuration to provide a slight converging taper of the resulting jaw noses from the upper ends to the lower ends in the terminal 6A, as best seen in Figs. 10 and 11.
After the final formation of the depressions to form the jaws 36, as in blank 4d, the foldable configurations 4 may be shaped in other respects to arrive at the final terminal form of Fig. 8. Among such steps are coining of the angular top surfaces of the jaws (which have resulted from the notches 20) to provide a smooth beveled surface on each jaw for the wire-engaging functions, folding the sides 28 and 30 approximately perpendicularly to the terminal body base 32, folding tabs 174a, 174b, 174c and 174d (Fig. 8) into their proper positions, and severing stems 8 and 10 - from the metal blank 2. Stem 8 is bent to its bow form, and its distal end 8a lS bent into a U-shaped configuration, to form the completed terminal 6A.
Jaws 36, the completed result of the formative steps performed upon depressions 50, are accordingly disposed along at least one side, and preferably both sides 28 and 30, of the terminal 6A to extend inwardly over the terminal body base panel 32. In the form of the terminal , B -~ -~` 1090545 6A shown in Fig. 8, two pairs of jaws 36 are disposed in the sides 28 and 30 so that the jaws extend toward each other and the tip portions 176 are positioned in opposition to each other.
When the completely formed terminals 6A have been severed from the metal blank 2 and finally formed into their ultimate configurations they may be mounted in a molded, insulating receptacle 178, such as shown in Fig. 9. Without describing the receptable 178 in great detail, it may be noted that it includes a plurality of generally channel-shaped passages 180 into which the terminals 6A may be inserted.
The U-shaped distal end 8a of each terminal may be hooked about a rib 182 or 182a on one side of receptacle 178 as each of the terminals is inserted into a passage 180, and tabs 174c are bent up to the locking portion of Fig. 9.
Vertical passages 184 permit access to be had to each channel 34 running through the body of each terminal 64 in a passage 180. The sides 186 of each passage 180 are disposed so that the shoulders 38a and 38b of each terminal are closely fitted against them, and the shoulders may ~therefore provide the primary support force transfer from the jaws 36 to the sides 186 for supporting the jaws 36 against outward deformation of the jaws which might other-wise result from forcible insertion of wfres against the jaw noses 176. In order to obtain the close fitting engage-ment of the shoulders against the sides of the passages 180, it is important that the widths of the terminals and the widths of the passages be precisely dimensioned.

B ~

10~054S

Ref~rring now particularl~ to Figs. 10 and 11, the inscrtion in~o the receptacle of wires to carry electrical currcnt, and fixing them there, normally is accomplish~d by forcing the wires 188, including a center conductor 189 and an insulation covering 190, laterally of their axes through the vertical passages 184 into the inclined surfaces defined by notches 20 of jaws 36 and between the noses 176. A tool blade 192 is shown above each wire and having an end surface to force each insulation-co~ered wire between a set of jaws 36. If a plurality of wires 188 are to be inserted substantially simultaneously, the tool may comprise a plurality of blade faces 194. As each ram face 194 is forced downwardly, it forces-one wire 188 between jaws 36 of one terminal, and in the course of so position-inq wire 188, the insulation 190 is stripped fro~ the wire and the conductor core 189 engages the noses 176 in order to obtain reliable electrical contact between the conductor and the terminal. Shoulders 38a and 38b by providing compressive support between the side walls of each terminal and the sides 186 of the passages 180 substantially in alignment with the side walls of each respective jaw 36, assist in assuring accurate and rigid positioning of the conductor engaging edges 176 to assure the desired engagement of the jaws with the conductor when a conductor is forced against the jaws.

B -~ -`~ 1090545 From the foregoing detailed description it may be ascertained that the present invention includes obtaining addi-tional lengths of metal in and ad~acent to, or between, a jaw or set of jaws disposed in at least one of the sides of an electrical terminal. Such additional lengths are produced by coining the metal used in making the terminal and by limiting the stretching of the metal to a gradual and dispersed stretching throughout a substantial portion of the side of the terminal. It may also be ascertained that the base width of the jaws is progressively narrowed to provide rigidity against outward collapse of each jaw under outward pressure exerted by disposing electrical wires in the terminal. The shoulders at each side of each jaw insure contact with the side walls of the receptacle passages very near positions of alignment with the jaw sides, thus enhancing the compression strength of the jaws upon the current-carrying wire.
Thus it will be seen that improvements have been provided in the formation of electrical terminals and which meet the aforestated objects.
While a particular embodiment of the present invention has been shown, it will be understood, of course, that the invention is not limited thereto since modifica-tions may be made by those skilled in the art, particularly in light of the foregoing teachings. It is, therefore, contemplated by the appended claims to cover any such modifications as incorporate those features which come within the true spirit and scope of the invention.

Claims (15)

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:

1. The method of forming a wire contacting jaw in an electrical wire terminal comprising:
disposing a flat sheet of current conductive metal upon a first ribbed die face and impressing a portion of the sheet upon said face, forming thereby a first depression in said sheet portion, moving the first depression onto a second die face having ribbing therein of deeper dimension than the first die face and impressing the first depression deeper than the depth thereof formed on the first die face, moving the first depression onto a third die face having ribbing therein of deeper dimension than the second die face and impressing the first depression deeper than the depth thereof formed on the second die face, and folding the sheet into an elongated wire receiving body having a bottom and facing sides defining a wire receiving channel wherein the first depression is disposed from one of said facing sides.

2. The method of claim 1 which further comprises forming a plurality of first depressions in said sheet upon said first die face and progressively deepening said first depressions upon said second and third die faces.

3. The method of claim 1 which further comprises including a plurality of ribs on the first die face, forming thereon a plurality of first depressions in said sheet and progressively deepening the first depressions upon said second and third die faces.

4. The method of claim 2 which further comprises forming a plurality of first depressions in the sheet upon said face of said first die, said first die face having a plurality of ribs of like dimensions with each other for forming the first depressions in opposite side portions of said sheet for opposition to each other on the facing sides of said wire receiving channel, and progressively deepening said first depressions upon faces of second and third dies which include, respectively, second and third sets of ribs of like dimensions within each set.

5. The method of claim 1 which further comprises impressing shoulders in the sheet at the junctures of each side of the first depression and the sheet.

6. The method of claim 5 which further comprises impressing said shoulders in the sheet while said sheet is disposed between the faces of the second die.

7. The method of claim 6 which further comprises impressing the shoulers in a raised position on the side of the sheet opposite the direction in which the first depression is extended.

8. The method of claim 5 which further comprises impressing a plurality of depressions and shoulders in the sheet, the said sheet forming an integral yoke between a first terminus of a shoulder adjacent one depression and a second terminus of a like shoulder adjacent a second depression formed in the sheet.

9. The method of claim 6 which further comprises disposing the shoulders in the sheet closer together than the mouth of the first depression formed in the face of the first die.

10. The method of claim 5 which further comprises disposing the shoulders in the sheet closer together between the faces of said third die than said shoulders are disposed between the faces of the second die.

11. The method of claim 1 which further comprises coining the sheet of metal on the second and third die faces.

12. The method of claim 8 which further comprises coining the sheet of metal on the second die face at said shoulders.

13. The method of claim 8 which further comprises coining the sheet of metal on the third die face at said shoulders.

14. The method of claim 8 which further comprises coining the sheet of metal on the second and third die faces at said shoulders.

15. The method of claim 1 which further comprises forming and stretching the sheet into a first depression on the first die face, forming and coining shoulders into the sheet at the junctures of the sides of said first depression and the sheet on the second die face, and coining and stretching said shoulders and stretching the deepest extremity of the first depression on the third die face.