CA1049344A - System and method for rigid enclosures - Google Patents
System and method for rigid enclosuresInfo
- Publication number
- CA1049344A CA1049344A CA163,045A CA163045A CA1049344A CA 1049344 A CA1049344 A CA 1049344A CA 163045 A CA163045 A CA 163045A CA 1049344 A CA1049344 A CA 1049344A
- Authority
- CA
- Canada
- Prior art keywords
- resin
- activated
- fabric
- impregnated
- amine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
ABSTRACT
An improved system and method for pro-ducing lightweight and strong rigid enclosures formed by enclosing or wrapping the article in a dry peroxide catalyst-impregnated fabric and applying thereto an activated thermosetting vinyl type resin.
An improved system and method for pro-ducing lightweight and strong rigid enclosures formed by enclosing or wrapping the article in a dry peroxide catalyst-impregnated fabric and applying thereto an activated thermosetting vinyl type resin.
Description
10493~
This invention relates to an improved system and method for preparing enclosed bodies, moldings and casts.
BACKGROUND OF THE INVENTION
Several attempts have been made to adopt modern plastic technology to the production of rigid enclosures for such segments as a living body, human or animal. The use of rigid body and body member casts are important to assist in the healing of tissues and in knitting of fractures of the bone.
Such methods have incorporated systems, which have been disadvantageous for one of many reasons. For example, one method is dependent upon a closed plastic bag which is ~rapped around the member and a plastic foam is allowed to develope in the bag. This system of encasement is slow, diffiCult to apply and very hot and uncomfortable for the wearer. The system does not allow air to enter or leave the appliance.
The conventional plaster of Paris systems have many ~
d~ssatisfactory properties. Particularly, the casts formed ~ ;
therewith are heavy, X-ray impervious, absorb excessive mois-ture which thereby destroys the mechanical property, soil rapidly, are difficult to clean, poor shock resistance, lack elasticity, slow to reach ultimate strength, poor abrasive resistance and receptive to bacterial and fungal growth.
It also has been proposed to soften sheets of plastic materials and apply them to the part of the body to be immobi-lized so as to set upon cooling to a desired position. Un-fortunately, the temperature to which such thermoplastic materials must be raised to make them moldable is too high to ~e endured b~ a patient unless an însulat~ng intermediate material is first applied. ;~
This invention relates to an improved system and method for preparing enclosed bodies, moldings and casts.
BACKGROUND OF THE INVENTION
Several attempts have been made to adopt modern plastic technology to the production of rigid enclosures for such segments as a living body, human or animal. The use of rigid body and body member casts are important to assist in the healing of tissues and in knitting of fractures of the bone.
Such methods have incorporated systems, which have been disadvantageous for one of many reasons. For example, one method is dependent upon a closed plastic bag which is ~rapped around the member and a plastic foam is allowed to develope in the bag. This system of encasement is slow, diffiCult to apply and very hot and uncomfortable for the wearer. The system does not allow air to enter or leave the appliance.
The conventional plaster of Paris systems have many ~
d~ssatisfactory properties. Particularly, the casts formed ~ ;
therewith are heavy, X-ray impervious, absorb excessive mois-ture which thereby destroys the mechanical property, soil rapidly, are difficult to clean, poor shock resistance, lack elasticity, slow to reach ultimate strength, poor abrasive resistance and receptive to bacterial and fungal growth.
It also has been proposed to soften sheets of plastic materials and apply them to the part of the body to be immobi-lized so as to set upon cooling to a desired position. Un-fortunately, the temperature to which such thermoplastic materials must be raised to make them moldable is too high to ~e endured b~ a patient unless an însulat~ng intermediate material is first applied. ;~
-2-.... . . . . . .
~o49;~44 Certain systems and methods of casting have been proposed which util-~ze polymerizing systems and polymerizing bandages. However, these systems employ large amounts of liquid volatile and non-volatile diluents to replace part of the monomer as liquid extenders or wetting material. The presence of such volatile liquids are unsatisfactory. The presence of non-volatile viscous diluents do not cause vapor cells and form weak casts due to inadequate wetting of the solid filter or inability to satisfactorily dissolve the lQ polymer formed and the like. Various catalyzed and accelerated mixtures of monomeric solvents within the prior diluent systems attempt to overcome the disadvantages thereof by addition of non-polymerizable polyalcohol esters. The problem of noxious volatile fumes remains. This is highly undesirable when such a system is used in a confined area. Further, the method for body use requires the coating of the body member with petrolatum or other protectant, this prevents air from reaching the injured member.
The prior art, U.S. Patent 3,089,486, discloses a 2Q methacrylate polymer impregnant which is imbued into a bandage.
T~e bandage in this form can be stored, however, this requires constant monitoring to insure a usable material. Further, the system described therein requires applying a barrier to the body membex prior to applying the monomer component. This presents the disadvantage of placing an air impervious barrier which allows moisture to collect under the barrier from body prespiration, thereby inducing skin irritation.
Means, in U.S. Patent 2,576,027, describes impreg-nating a cloth such as surgical gauze or the like, with a chem~cal that acts as a catalyst with reference to a solution of a`synthetic resin. The solution of synthetic resin is applied to the gauze to form a rigid solid. The catalyst and ~3~
synthetic resin relates to a specific urea-formaldehyde system.
The catalyst system described ~y Means i5 not effective incuring vinyl-type monomers and cannot be used with the instant invention.
The prior art, U.S. Patents 3,421,501 and 3,613,675, describe bandages which contain an activated resin. The bandages are cured by exposure to ultraviolet light.
SUMMARY OF THE INVENTION
The present invention possesses definite advanta~es over the above-described systems. Primarily, it requires neither a pail of plaster of Paris, nor the soaking of a pre-pared plaster gauze material. Further, there is no need for actinic radiation to catalyze the system into a rigid form.
The requirement of ultraviolet irradiation includes the distinct advantage that such a system must be necessarily employed near a source of electrical power. Further, such systems produce a slower cured resin enclosure. It is inherently difficult to irradiate certain areas such as in a cast utility, as under the arm or crouch ~urther advantages of the present invention are ~a~t curing and the presence of no volatile solvents. The cured system is light in weight and possesses an open con- -figuration which allows good air exchange with the underlying ~ember. The physical properties of the system are not greatly affected by exposure to water allowing for the possibility of washing the encased or immobilized member. .
~rhe present invention relates to a fully usable system which functions without further reference to any other system. It is understood that to be usable, a catalyzed fabric and a resin must be used in combination~ Therefore, the improved operable system of this invention relates to the use of wrapping material treated and impregnated with a free radical catalyst, such as peroxides, then applying by a suitable means a resin con-1049.~44 taining active unsaturated radicals, as found in polyesters and acrylics, and contaîning tertiary aromatic amine accelerator.
The instant invention is contemplated for resin structures and enclosures for a wide variety of uses, e.g., models, toys, linings, shaped articles generally. Porous surgical dressings, orthopedic supports, and like objects, can be readily prepared. Further, for easily prepared plastic shells the present system is easily applicable as well as for repairs and maintenance of such items, ie.g., fiber glass bodies on cars and boats. Without the requirement of heat or special preparation, the instant system is especially useful.
Accordingly, it is a principal object of this inven-tion to provide for the application of orthopedic casts of b~ody members or enclosures of other articles which comprise enclosing said member in a peroxide catalyst impregnated, woven or non-woven fabric and applying to said enclosed member a thermo-setting polyester or thermosetting acrylic monomer of the dimethacrylate type, containing a tertiary aromatic amine accelerator to form a hard, lightweight, rigid physiologically 2Q inert intergral enclosure or case.
A further object of this invention is to provide for the application of orthopedic casts or enclosures for articles formed of lightweight plastic wherein the hardening or setting of the plastic is accomplished by a peroxide catalyst impreg-nated in the enclosing fabric.
DETAILED DESCRIPTION OF THE INVENTION
As a general definition, the group of resins include the members defined as thermosetting polyesters and thermosetting acrylics, also known as Yinyl resins, those members having active therminal ethylene unsaturation or poly functional un-saturated ester moieties. Representative of this group is the following list:
j~ ~c , . : . .
. . . .
~049344 ethylene glycol dimethacrylate diethylene glycol dimethacrylate triethylene glycol dimethacrylate hexamethylene glycol dimethacrylate 2,2-bis(2-methacrylatoethoxyphenyl)propane 2,2-bis(3-methacrylato-2-hydroxypropoxyphenyl)propane phthalic-maleic-propylene glycol polyester Resin blends comprising two or more ther~osetting acrylic monomers are also contemplated. Resin blends comprising at least one thermosetting acrylic monomer and one or more thermo-setting polyester resins are within the resins defined herein.
In some instances, these blends constitute a preferred resin composition for the method of the instant invention, in that they produce the least amount of heat during the curing (i.e., polymerization) of the resin, The cast material can contain a blend of resins of up to about 90 per cent, preferably about 65 to 75 per cent, of acrylic resin and from about 5 to 35 per cent polyester resin, preferably about 25 to 35 per cent. -These percentages are based upon the total weight of the blended ~-2Q resîn. ~
The monomer or resin-forming component is preferably ~-advanced to an activated state. The activation develops in the resin when the system is combined with an accelerator and in which condition the activated monomer thus prepared retains a ` reasonable shelf-life. In order to arrive at this activated state in the resin, it is preferred to employ, as an accelera-tor, a tertiary aromatic amine, which is particularly useful in the instant invention. Examples of members of the class tertiary aromatic amine include N~3-tolyl-diethanol amine and N-4-tolyl-diet~anol amine. ~hen the activated resin is employed, appli-cation to the catalyst-impregnated fabric causes a very rapid curing to a desirable rigid structure. The monomer or resin is ,. ~ , : . .. .. .
generally used in an amount of from about one-half the weight of fabric to two times the weight of fabric. The amount of tertiary aromatic amine as accelerator in the resin is about 0,1 to about 2.0 phr (parts per hundred of resin).
It has been found that certain properties of the resins can be enhanced by the addition of suitable plasticizer to the system. A plasticizer is a material incorporated in a plastic to increase the workability and flexibility or dis-tensibility of the plastic product. Plasticizers may improve impact resistance of the final product. Organic plasticizers axe usually moderately high-molecular-weight liquids or occasionally low-melting solids. Most commonly, organic plasticizers are esters of carboxylic acids. Other types also ~nclude hydrocarbons, halogenated hydrocarbons, ethers, poly-glycols and sulfonamides. The choice of a specific plasticizer for a given use requires a compromise of desirable properties ~n each case. It is therefore a preferred embodiment of this invention that the resin system contain a plasticizer to enhance the properties as desired. More preferably, a plasticizer content of from about 10 per cent to about 50 per cent based on the total resin formulation including the plasticizer. By the term "resin" is meant resin blends comprising two or more thermosetting acrylic monomers; blends comprising at least one thermosetting acrylic monomer and one or more thermosetting polyester resin. The percentage composition of the blended resins include the above-mentioned percentages for acrylic resin and polyester resin.
Catalyst for the production of free radical initi-ators of polymerizat~on may be used to impregnate the fabric of th-ls ~nvention, but preferred is the peroxide type. The catalyst impregnated fabric should be stable at ambient temper-atures. Of the preferred catalyst peroxides which are within the class înclude for example:
2,4-dichlorobenzoyl peroxide caprylyl peroxide lauraoyl peroxide benzoyl peroxide acetyl peroxide Some mixed peroxides such as acetyl benzoyl peroxides are also suitable.
Prior to the application of the desired catalyst to the fabric, the catalyst may be dissolved in a suitable solvent. ~ `
For example, benzoyl peroxide in chloroform. Actually, any non-protonic organic solvent, such as methylene chloride, benzene, cyclohexane and the like, may be employed. The ~-solution of catalyst contains generally the amount from about 1 per cent to about 10 per cent of catalyst. The solution is ... .
applied to the fabric by a suitable means, so as to treat and impregnate the fabric. After application, the catalyst treated fabric is dried to remove the solvent. The fabric then is usable in the dry state. No special handling is required for the peroxide impregnated fabric. Storage should not expose the treated fabric to excessive heat. A variety of techniques may be employed to apply the catalyst, for example, dipping or spraying. The condition to be achieved within the fabric is a thorough intermingling with and in the surrounding area in relation to the threads or fibers of the fabric. It is not ; indicated that the catalyst is to any extent absorbed by the fibers themselves. It is preferred that for certain uses the `~ fabric have a relatively open, knit structure and the applied resin thereby able to flow in and around the ~ibers to become rigidly bonded to the f~bers and yet retain an open mesh appearance. The catalyst impregnated fabric is furnished in the dry state. The presence of a wet state would be undesirable .; - -: . . ':- ..
~)49344 to the advantages of the instant invention and would incorporate exposure to undesira~le solvents.
The fabric material which is impregnated with the preferred peroxide-type catalyst described above, may be in the form of a continuous sheet, or of short or long strips. The fabric base can comprise two or more layers folded on each other as in cotton gauze bandages. The material of construction may Be of woven or non-woven material, including felt-type materials, as an air-laid felt. The fabric itself is preferably made of cotton, synthetic fiber or fiberglass. However, the particular fabric selected will depend upon the particular application, and accordingly, this invention is not limited to any particular choice of fabric material. The amount of catalyst on the impregnated fabric will depend upon the nature of the fabric.
The amount of catalyst present will further depend upon the amount of catalyst retained from the application thereof, i.e., by spraying, dipping, brushincJ, rolling, or flow techniques.
The activated monomer with the selected accelerator is applied to the dry peroxide catalyst-impregnated fabric.
The method of application will vary with the specific use.
Contemplated within this invention is the application of the activated vinyl monomer of the polyester or acrylic type -~ described herein by spraying, painting, swabing and the like.
Upon contact with the catalyst-impregnated fabric, the activated resin begins to polymerize almost immediately, such that within a few minutes the composite system is rigid and servicable.
The cast or enclosure is light in weight, has an open con-figuration and conforms to the position and shape of the dry impregnated fabric prior to application of the activated resin.
Other layers of fabric can be over laid the initial form almost ;~mmediately to obtain a more closed configuration if desired.
~ - , . ..
Thus, within the skill of those qualified in the orthopedic sciences, the preparation and application of orthopedic casts for use in the treatment of bone fractures or other conditions requiring immobilization of body members may be advantageously formed from the materials and method of this invention. In applying the peroxide catalyst-impregnated fabric from a rolled up material to a body member, the strip of fabric is wrapped around the member in an advancing overlapping manner.
When the member has been completely wrapped in the impregnated fabric, an acti~ated vinyl monomer resin described herein is -applied, as by spraying, on the fabric. Within one to two minutes, the component system is rigid and usable. The resulting ; cast thickness will depend upon location of the body portion to be cast; upon the strength and rigidity required.
; The examples presented herein serve solely to illus-trate the composite system and method of this invention. Ac-cordingly, the examples should not be regarded as limiting the invention in any way. In the examples, the parts and percent-ages are by weight unless otherwise indicated.
EXAMPLE I
An activated resin was prepared by dissolving 1.0 g.
of N~3-tolyldiethanol amine in 100.0 g. of ethylene glycol di-methacrylate. This activate resin was sprayed onto a sample of each cotton, nylon and glass cloths which had been dipped into a chloroform solution containing 5 per cent benzoyl peroxide.
The benzoyl peroxide treated fabric cloths were allowed to dry before application of the activated resin. The resin on the cloth samples began to polymerize and becarne comfortably warm in 40 seconds. At the end of one minute, the composite system was rigid, hard and servicable.
.
lo -In a similar method as descrîbed in Example I, the following dimethacrylate resins each were used on cotton, nylon and glass cloths. The results in each case are comparable.
a) diethylene glycol dimethacrylate b~ triethylene glycol dimethacrylate c) hexamethylene glycol dimethacrylate d~ 2,2-bis~2-methacrylatoethoxyphenyl)propane EXAMPLE III
An activated resin blend was prepared by mixing 100 parts of ethylene glycol dimethacrylate, 100 parts of 2,2-bis (3-methacrylato-2-hydroxypropoxyphenyl)propane and 2 parts of N-3-tolyldiethanol amine. This resin system was sprayed on to benzoyl peroxide catalyzed cloths, prepared in the same manner as Example I. After 20 seconds, the applied resin began to gel and at 30 seconds, the composite system was rigid and servicable.
No undesirable heat evolution was detected during gelling of this system.
EXAMPLE IV
In a similar manner as Example III, an activated resin blend was prepared using triethylene glycol dimethacrylate instead of ethylene glycol dimethacrylate. Comparable results were obtained.
EXAMPLE V
An activated vinyl resin blend was prepared by mixing 60 parts triethylene glycol dimethacrylate, 1 part of N-3-tolyl-diethanol amine and 40 parts of polyester resin prepared from 2 moles of phthalic anhydride, 1 mole of maleic anhydride and
~o49;~44 Certain systems and methods of casting have been proposed which util-~ze polymerizing systems and polymerizing bandages. However, these systems employ large amounts of liquid volatile and non-volatile diluents to replace part of the monomer as liquid extenders or wetting material. The presence of such volatile liquids are unsatisfactory. The presence of non-volatile viscous diluents do not cause vapor cells and form weak casts due to inadequate wetting of the solid filter or inability to satisfactorily dissolve the lQ polymer formed and the like. Various catalyzed and accelerated mixtures of monomeric solvents within the prior diluent systems attempt to overcome the disadvantages thereof by addition of non-polymerizable polyalcohol esters. The problem of noxious volatile fumes remains. This is highly undesirable when such a system is used in a confined area. Further, the method for body use requires the coating of the body member with petrolatum or other protectant, this prevents air from reaching the injured member.
The prior art, U.S. Patent 3,089,486, discloses a 2Q methacrylate polymer impregnant which is imbued into a bandage.
T~e bandage in this form can be stored, however, this requires constant monitoring to insure a usable material. Further, the system described therein requires applying a barrier to the body membex prior to applying the monomer component. This presents the disadvantage of placing an air impervious barrier which allows moisture to collect under the barrier from body prespiration, thereby inducing skin irritation.
Means, in U.S. Patent 2,576,027, describes impreg-nating a cloth such as surgical gauze or the like, with a chem~cal that acts as a catalyst with reference to a solution of a`synthetic resin. The solution of synthetic resin is applied to the gauze to form a rigid solid. The catalyst and ~3~
synthetic resin relates to a specific urea-formaldehyde system.
The catalyst system described ~y Means i5 not effective incuring vinyl-type monomers and cannot be used with the instant invention.
The prior art, U.S. Patents 3,421,501 and 3,613,675, describe bandages which contain an activated resin. The bandages are cured by exposure to ultraviolet light.
SUMMARY OF THE INVENTION
The present invention possesses definite advanta~es over the above-described systems. Primarily, it requires neither a pail of plaster of Paris, nor the soaking of a pre-pared plaster gauze material. Further, there is no need for actinic radiation to catalyze the system into a rigid form.
The requirement of ultraviolet irradiation includes the distinct advantage that such a system must be necessarily employed near a source of electrical power. Further, such systems produce a slower cured resin enclosure. It is inherently difficult to irradiate certain areas such as in a cast utility, as under the arm or crouch ~urther advantages of the present invention are ~a~t curing and the presence of no volatile solvents. The cured system is light in weight and possesses an open con- -figuration which allows good air exchange with the underlying ~ember. The physical properties of the system are not greatly affected by exposure to water allowing for the possibility of washing the encased or immobilized member. .
~rhe present invention relates to a fully usable system which functions without further reference to any other system. It is understood that to be usable, a catalyzed fabric and a resin must be used in combination~ Therefore, the improved operable system of this invention relates to the use of wrapping material treated and impregnated with a free radical catalyst, such as peroxides, then applying by a suitable means a resin con-1049.~44 taining active unsaturated radicals, as found in polyesters and acrylics, and contaîning tertiary aromatic amine accelerator.
The instant invention is contemplated for resin structures and enclosures for a wide variety of uses, e.g., models, toys, linings, shaped articles generally. Porous surgical dressings, orthopedic supports, and like objects, can be readily prepared. Further, for easily prepared plastic shells the present system is easily applicable as well as for repairs and maintenance of such items, ie.g., fiber glass bodies on cars and boats. Without the requirement of heat or special preparation, the instant system is especially useful.
Accordingly, it is a principal object of this inven-tion to provide for the application of orthopedic casts of b~ody members or enclosures of other articles which comprise enclosing said member in a peroxide catalyst impregnated, woven or non-woven fabric and applying to said enclosed member a thermo-setting polyester or thermosetting acrylic monomer of the dimethacrylate type, containing a tertiary aromatic amine accelerator to form a hard, lightweight, rigid physiologically 2Q inert intergral enclosure or case.
A further object of this invention is to provide for the application of orthopedic casts or enclosures for articles formed of lightweight plastic wherein the hardening or setting of the plastic is accomplished by a peroxide catalyst impreg-nated in the enclosing fabric.
DETAILED DESCRIPTION OF THE INVENTION
As a general definition, the group of resins include the members defined as thermosetting polyesters and thermosetting acrylics, also known as Yinyl resins, those members having active therminal ethylene unsaturation or poly functional un-saturated ester moieties. Representative of this group is the following list:
j~ ~c , . : . .
. . . .
~049344 ethylene glycol dimethacrylate diethylene glycol dimethacrylate triethylene glycol dimethacrylate hexamethylene glycol dimethacrylate 2,2-bis(2-methacrylatoethoxyphenyl)propane 2,2-bis(3-methacrylato-2-hydroxypropoxyphenyl)propane phthalic-maleic-propylene glycol polyester Resin blends comprising two or more ther~osetting acrylic monomers are also contemplated. Resin blends comprising at least one thermosetting acrylic monomer and one or more thermo-setting polyester resins are within the resins defined herein.
In some instances, these blends constitute a preferred resin composition for the method of the instant invention, in that they produce the least amount of heat during the curing (i.e., polymerization) of the resin, The cast material can contain a blend of resins of up to about 90 per cent, preferably about 65 to 75 per cent, of acrylic resin and from about 5 to 35 per cent polyester resin, preferably about 25 to 35 per cent. -These percentages are based upon the total weight of the blended ~-2Q resîn. ~
The monomer or resin-forming component is preferably ~-advanced to an activated state. The activation develops in the resin when the system is combined with an accelerator and in which condition the activated monomer thus prepared retains a ` reasonable shelf-life. In order to arrive at this activated state in the resin, it is preferred to employ, as an accelera-tor, a tertiary aromatic amine, which is particularly useful in the instant invention. Examples of members of the class tertiary aromatic amine include N~3-tolyl-diethanol amine and N-4-tolyl-diet~anol amine. ~hen the activated resin is employed, appli-cation to the catalyst-impregnated fabric causes a very rapid curing to a desirable rigid structure. The monomer or resin is ,. ~ , : . .. .. .
generally used in an amount of from about one-half the weight of fabric to two times the weight of fabric. The amount of tertiary aromatic amine as accelerator in the resin is about 0,1 to about 2.0 phr (parts per hundred of resin).
It has been found that certain properties of the resins can be enhanced by the addition of suitable plasticizer to the system. A plasticizer is a material incorporated in a plastic to increase the workability and flexibility or dis-tensibility of the plastic product. Plasticizers may improve impact resistance of the final product. Organic plasticizers axe usually moderately high-molecular-weight liquids or occasionally low-melting solids. Most commonly, organic plasticizers are esters of carboxylic acids. Other types also ~nclude hydrocarbons, halogenated hydrocarbons, ethers, poly-glycols and sulfonamides. The choice of a specific plasticizer for a given use requires a compromise of desirable properties ~n each case. It is therefore a preferred embodiment of this invention that the resin system contain a plasticizer to enhance the properties as desired. More preferably, a plasticizer content of from about 10 per cent to about 50 per cent based on the total resin formulation including the plasticizer. By the term "resin" is meant resin blends comprising two or more thermosetting acrylic monomers; blends comprising at least one thermosetting acrylic monomer and one or more thermosetting polyester resin. The percentage composition of the blended resins include the above-mentioned percentages for acrylic resin and polyester resin.
Catalyst for the production of free radical initi-ators of polymerizat~on may be used to impregnate the fabric of th-ls ~nvention, but preferred is the peroxide type. The catalyst impregnated fabric should be stable at ambient temper-atures. Of the preferred catalyst peroxides which are within the class înclude for example:
2,4-dichlorobenzoyl peroxide caprylyl peroxide lauraoyl peroxide benzoyl peroxide acetyl peroxide Some mixed peroxides such as acetyl benzoyl peroxides are also suitable.
Prior to the application of the desired catalyst to the fabric, the catalyst may be dissolved in a suitable solvent. ~ `
For example, benzoyl peroxide in chloroform. Actually, any non-protonic organic solvent, such as methylene chloride, benzene, cyclohexane and the like, may be employed. The ~-solution of catalyst contains generally the amount from about 1 per cent to about 10 per cent of catalyst. The solution is ... .
applied to the fabric by a suitable means, so as to treat and impregnate the fabric. After application, the catalyst treated fabric is dried to remove the solvent. The fabric then is usable in the dry state. No special handling is required for the peroxide impregnated fabric. Storage should not expose the treated fabric to excessive heat. A variety of techniques may be employed to apply the catalyst, for example, dipping or spraying. The condition to be achieved within the fabric is a thorough intermingling with and in the surrounding area in relation to the threads or fibers of the fabric. It is not ; indicated that the catalyst is to any extent absorbed by the fibers themselves. It is preferred that for certain uses the `~ fabric have a relatively open, knit structure and the applied resin thereby able to flow in and around the ~ibers to become rigidly bonded to the f~bers and yet retain an open mesh appearance. The catalyst impregnated fabric is furnished in the dry state. The presence of a wet state would be undesirable .; - -: . . ':- ..
~)49344 to the advantages of the instant invention and would incorporate exposure to undesira~le solvents.
The fabric material which is impregnated with the preferred peroxide-type catalyst described above, may be in the form of a continuous sheet, or of short or long strips. The fabric base can comprise two or more layers folded on each other as in cotton gauze bandages. The material of construction may Be of woven or non-woven material, including felt-type materials, as an air-laid felt. The fabric itself is preferably made of cotton, synthetic fiber or fiberglass. However, the particular fabric selected will depend upon the particular application, and accordingly, this invention is not limited to any particular choice of fabric material. The amount of catalyst on the impregnated fabric will depend upon the nature of the fabric.
The amount of catalyst present will further depend upon the amount of catalyst retained from the application thereof, i.e., by spraying, dipping, brushincJ, rolling, or flow techniques.
The activated monomer with the selected accelerator is applied to the dry peroxide catalyst-impregnated fabric.
The method of application will vary with the specific use.
Contemplated within this invention is the application of the activated vinyl monomer of the polyester or acrylic type -~ described herein by spraying, painting, swabing and the like.
Upon contact with the catalyst-impregnated fabric, the activated resin begins to polymerize almost immediately, such that within a few minutes the composite system is rigid and servicable.
The cast or enclosure is light in weight, has an open con-figuration and conforms to the position and shape of the dry impregnated fabric prior to application of the activated resin.
Other layers of fabric can be over laid the initial form almost ;~mmediately to obtain a more closed configuration if desired.
~ - , . ..
Thus, within the skill of those qualified in the orthopedic sciences, the preparation and application of orthopedic casts for use in the treatment of bone fractures or other conditions requiring immobilization of body members may be advantageously formed from the materials and method of this invention. In applying the peroxide catalyst-impregnated fabric from a rolled up material to a body member, the strip of fabric is wrapped around the member in an advancing overlapping manner.
When the member has been completely wrapped in the impregnated fabric, an acti~ated vinyl monomer resin described herein is -applied, as by spraying, on the fabric. Within one to two minutes, the component system is rigid and usable. The resulting ; cast thickness will depend upon location of the body portion to be cast; upon the strength and rigidity required.
; The examples presented herein serve solely to illus-trate the composite system and method of this invention. Ac-cordingly, the examples should not be regarded as limiting the invention in any way. In the examples, the parts and percent-ages are by weight unless otherwise indicated.
EXAMPLE I
An activated resin was prepared by dissolving 1.0 g.
of N~3-tolyldiethanol amine in 100.0 g. of ethylene glycol di-methacrylate. This activate resin was sprayed onto a sample of each cotton, nylon and glass cloths which had been dipped into a chloroform solution containing 5 per cent benzoyl peroxide.
The benzoyl peroxide treated fabric cloths were allowed to dry before application of the activated resin. The resin on the cloth samples began to polymerize and becarne comfortably warm in 40 seconds. At the end of one minute, the composite system was rigid, hard and servicable.
.
lo -In a similar method as descrîbed in Example I, the following dimethacrylate resins each were used on cotton, nylon and glass cloths. The results in each case are comparable.
a) diethylene glycol dimethacrylate b~ triethylene glycol dimethacrylate c) hexamethylene glycol dimethacrylate d~ 2,2-bis~2-methacrylatoethoxyphenyl)propane EXAMPLE III
An activated resin blend was prepared by mixing 100 parts of ethylene glycol dimethacrylate, 100 parts of 2,2-bis (3-methacrylato-2-hydroxypropoxyphenyl)propane and 2 parts of N-3-tolyldiethanol amine. This resin system was sprayed on to benzoyl peroxide catalyzed cloths, prepared in the same manner as Example I. After 20 seconds, the applied resin began to gel and at 30 seconds, the composite system was rigid and servicable.
No undesirable heat evolution was detected during gelling of this system.
EXAMPLE IV
In a similar manner as Example III, an activated resin blend was prepared using triethylene glycol dimethacrylate instead of ethylene glycol dimethacrylate. Comparable results were obtained.
EXAMPLE V
An activated vinyl resin blend was prepared by mixing 60 parts triethylene glycol dimethacrylate, 1 part of N-3-tolyl-diethanol amine and 40 parts of polyester resin prepared from 2 moles of phthalic anhydride, 1 mole of maleic anhydride and
3 moles of propylene glycol. This resin ~ystem ~as sprayed on to benzoyl perox~de catal~zed cloths, prepared as in Example I.
The system gelled in about 2 minutes and became rigid in about 2~5 minutes. ~o appreciable heat was evolved during the curing 10493~4 of this system. The composite system was rigid and servicable.
FXAMPLE VI
A 4 g. mixture containing 70 per cent 2,2-bis(3-methacrylato-2-hydroxypropoxyphenyl)propane and 30 per cent of polypropylene glycol (average molecular weight = 400) and 1 per cent N-3 tolyldiethanol amine was cured by adding, with mixing 12 drops (about 0.6 g.~ of a catalyst solution made from 10 g.
triethylene glycol dimethacrylate, 1 g. benzoyl peroxide, and 0.1 g. butylated hydroxytoluene. The system became a hard amber solid in 20 seconds. When a 50-50 per cent mixture of resin to polyglycol was used, a milky solid with much poorer physical properties was obtained. Both resin ratios cured when placed upon cloth which had been treated with benzoyl peroxide.
EXAMPLE VII
A resin system was prepared from 70 g. 2,2-bis(3-methacrylato-2-hydroxypropoxyphenyl)propane, 40 g. triethylene glycol dimethacrylate, 30 g. polypropylene glycol (average molecular weight = 400~ and 1 g. N-3-tolyldiethanol amine.
This system produced a tough amber colored composite solid 2Q when applied to cloth which had been treated with benzoyl peroxide.
ExAMæLE VIII
A resin blend was prepared from 25 g. 2,2-bis(3-methacrylato-2-hydroxypropoxyphenol)propane, 25 g. of triethylene glycol dimethacrylate, 25 g. of an isophthalate-maleic acid polyester resin, 25 g. polypropylene glycol (average molecular weight = 400) and 0.7 g. N-3-tolyldiethanol amine. This resin system was applied to glass cloth which had been treated with benzoyl peroxide. The resin began to gell in 20 seconds and was hard in 60 seconds. The composite system was rigid and servicable.
1~49344 It will readily be appreciated by those skilled in the art that the proportions of the various components of the system may vary widely depending upon the identity of the components and the conditions under which the system is to be applied and the hardened composite system is to be used. The best proportions in any particular instance can readily be determined on the basis of prior experience and by trial and error It is also within the scope of the invention to add to the mixture such modifying agents as therapeutic compounds, disinfectants, deodorants, and coloring agents, e.g., dyes and pigments. Proportions of such optional components as therapeutic compounds, deodorants, disinfectants, coloring materials, inactive fillers, and the like, are largely a matter of choice, it being understood of course that they should be present only in minor amounts sufficient to accomplish their ~ntended functions and not in quantities large enough to ~nterfere with the primary objectives of the system.
~13-
The system gelled in about 2 minutes and became rigid in about 2~5 minutes. ~o appreciable heat was evolved during the curing 10493~4 of this system. The composite system was rigid and servicable.
FXAMPLE VI
A 4 g. mixture containing 70 per cent 2,2-bis(3-methacrylato-2-hydroxypropoxyphenyl)propane and 30 per cent of polypropylene glycol (average molecular weight = 400) and 1 per cent N-3 tolyldiethanol amine was cured by adding, with mixing 12 drops (about 0.6 g.~ of a catalyst solution made from 10 g.
triethylene glycol dimethacrylate, 1 g. benzoyl peroxide, and 0.1 g. butylated hydroxytoluene. The system became a hard amber solid in 20 seconds. When a 50-50 per cent mixture of resin to polyglycol was used, a milky solid with much poorer physical properties was obtained. Both resin ratios cured when placed upon cloth which had been treated with benzoyl peroxide.
EXAMPLE VII
A resin system was prepared from 70 g. 2,2-bis(3-methacrylato-2-hydroxypropoxyphenyl)propane, 40 g. triethylene glycol dimethacrylate, 30 g. polypropylene glycol (average molecular weight = 400~ and 1 g. N-3-tolyldiethanol amine.
This system produced a tough amber colored composite solid 2Q when applied to cloth which had been treated with benzoyl peroxide.
ExAMæLE VIII
A resin blend was prepared from 25 g. 2,2-bis(3-methacrylato-2-hydroxypropoxyphenol)propane, 25 g. of triethylene glycol dimethacrylate, 25 g. of an isophthalate-maleic acid polyester resin, 25 g. polypropylene glycol (average molecular weight = 400) and 0.7 g. N-3-tolyldiethanol amine. This resin system was applied to glass cloth which had been treated with benzoyl peroxide. The resin began to gell in 20 seconds and was hard in 60 seconds. The composite system was rigid and servicable.
1~49344 It will readily be appreciated by those skilled in the art that the proportions of the various components of the system may vary widely depending upon the identity of the components and the conditions under which the system is to be applied and the hardened composite system is to be used. The best proportions in any particular instance can readily be determined on the basis of prior experience and by trial and error It is also within the scope of the invention to add to the mixture such modifying agents as therapeutic compounds, disinfectants, deodorants, and coloring agents, e.g., dyes and pigments. Proportions of such optional components as therapeutic compounds, deodorants, disinfectants, coloring materials, inactive fillers, and the like, are largely a matter of choice, it being understood of course that they should be present only in minor amounts sufficient to accomplish their ~ntended functions and not in quantities large enough to ~nterfere with the primary objectives of the system.
~13-
Claims (18)
1. A method for preparing a rigid enclosure comprising the steps:
(a) wrapping the object to be enclosed with a free radical organic peroxide catalyst-impregnated fabric;
(b) applying to said fabric an activated thermo-setting vinyl resin activated with a tertiary aromatic amine, said resin being selected from the group consisting of thermosetting polyester and thermosetting acrylic resins.
(a) wrapping the object to be enclosed with a free radical organic peroxide catalyst-impregnated fabric;
(b) applying to said fabric an activated thermo-setting vinyl resin activated with a tertiary aromatic amine, said resin being selected from the group consisting of thermosetting polyester and thermosetting acrylic resins.
2. The method of claim 1 in which the fabric is impregnated with benzoyl peroxide.
3. The method of claim 1 in which the fabric is impregnated with benzoyl peroxide and the resin is ethylene glycol dimethacrylate activated with N-3-tolyldiethanol amine.
4. The method of claim 1 in which the fabric is impregnated with benzoyl peroxide and the resin is diethylene glycol dimethacrylate activated with N-3-tolyldiethanol amine.
5. The method of claim 1 in which the fabric is impregnated with benzoyl peroxide and the resin is triethylene glycol dimethacrylate activated with N-3-tolyldiethanol amine.
6. The method of claim 1 in which the fabric is impregnated with benzoyl peroxide and the resin is hexamethylene glycol dimethacrylate activated with N-3-tolyldiethanol amine.
7. The method of claim 1 in which the fabric is impregnated with benzoyl peroxide and the resin is 2,2-bis(2-methacrylatoethoxyphenyl)propane activated with N-3-tolyldi-ethanol amine.
8. The method of claim 1 in which the fabric is impregnated with benzoyl peroxide and the resin is a blend of ethylene glycol dimethacrylate and 2,2-bis(3-methacrylato-2-hydroxypropoxyphenyl)propane activated with N-3-tolyldiethanol amine.
9. The method of claim 1 in which the fabric is impregnated with benzoyl peroxide and the resin is a blend of triethylene glycol dimethacrylate and 2,2-bis(3-methacrylato-2 hydroxypropoxyphenyl)propane activated with N-3-tolyldiethanol amine.
10. The method of claim 1 in which the fabric is impregnated with benzoyl peroxide and the resin is a blend of triethylene glycol dimethacrylate, activated with N-3-tolyldi-ethanol amine and a polyester resin comprising phthalic anhydride, maleic anhydride and propylene glycol.
11. A method for the application of an orthopedic case to a body member which comprises the steps:
(a) wrapping said member in free radical organic peroxide catalyst impregnated fabric;
(b) applying to said fabric an activated thermosetting vinyl resin activated with about 0.1 to about 2.0 parts per hundred of resin of a tertiary aromatic amine, said resin being selected from the group consisting of thermosetting polyester and thermosetting acrylic resins.
(a) wrapping said member in free radical organic peroxide catalyst impregnated fabric;
(b) applying to said fabric an activated thermosetting vinyl resin activated with about 0.1 to about 2.0 parts per hundred of resin of a tertiary aromatic amine, said resin being selected from the group consisting of thermosetting polyester and thermosetting acrylic resins.
12. The method of claim 11 in which the free radical catalyst is benzoyl peroxide, the vinyl resin is ethylene glycol dimethacrylate and the tertiary aromatic amine is N-3-tolyldi-ethanol amine.
13. The method of claim 11 in which the free radical catalyst is benzoyl peroxide, the vinyl resin is a blend of ethylene glycol dimethacrylate and 2,2-bis(3-methacrylato-2-hydroxypropoxyphenyl)propane and the tertiary aromatic amine is N-3-tolyldiethanol amine.
14. The method of claim 11 in which the free radical catalyst is benzoyl peroxide, the vinyl resin is a blend of triethylene glycol dimethacrylate, activated with N-3-tolyldi-ethanol amine and a polyester resin comprising phthalic anhydride, maleic anhydride and propylene glycol.
15. Orthopedic cast for use on a portion of the human or animal body comprising a cast material shaped to the contours of said body portion, said cast material comprising a free radical organic peroxide catalyst-impregnated fabric and an activated thermosetting vinyl resin activated with a tertiary aromatic amine, said resin being selected from the group consisting of thermosetting polyesters and thermosetting acrylic resins.
16. Orthopedic cast as claimed in claim 15 wherein said activated thermosetting vinyl resin activated with a tertiary aromatic amine contains from about 10 per cent to about 50 per cent plasticizer.
17. A method for preparing a rigid enclosure comprising the steps:
(a) wrapping the object to be enclosed with a free radical organic peroxide catalyst-impregnated fabric;
(b) applying to said fabric an activated thermosetting vinyl resin containing from about 10 per cent to about 50 per cent plasticizer and activated with a tertiary aromatic amine, said resin being selected from the group consisting of thermo-setting polyesters and thermosetting acrylic resins.
(a) wrapping the object to be enclosed with a free radical organic peroxide catalyst-impregnated fabric;
(b) applying to said fabric an activated thermosetting vinyl resin containing from about 10 per cent to about 50 per cent plasticizer and activated with a tertiary aromatic amine, said resin being selected from the group consisting of thermo-setting polyesters and thermosetting acrylic resins.
18. The method according to claim 17 wherein said activated thermosetting vinyl resin is a blend of up to about 90 per cent acrylic resin, from about 5 per cent to about 35 per cent polyester resin and from about 10 per cent to about 50 per cent plasticizer.