BR8007714A - PROCESS FOR THE PRODUCTION OF A HIGH VOLTAGE COLD LAMINATED STEEL PLATE, OF TWO PHASES HAVING EXCELLENT PROCESSABILITY - Google Patents
PROCESS FOR THE PRODUCTION OF A HIGH VOLTAGE COLD LAMINATED STEEL PLATE, OF TWO PHASES HAVING EXCELLENT PROCESSABILITYInfo
- Publication number
- BR8007714A BR8007714A BR8007714A BR8007714A BR8007714A BR 8007714 A BR8007714 A BR 8007714A BR 8007714 A BR8007714 A BR 8007714A BR 8007714 A BR8007714 A BR 8007714A BR 8007714 A BR8007714 A BR 8007714A
- Authority
- BR
- Brazil
- Prior art keywords
- phases
- production
- high voltage
- steel plate
- laminated steel
- Prior art date
Links
- 229910000576 Laminated steel Inorganic materials 0.000 title 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
- C21D8/0473—Final recrystallisation annealing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
- C21D1/185—Hardening; Quenching with or without subsequent tempering from an intercritical temperature
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/56—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering characterised by the quenching agents
- C21D1/60—Aqueous agents
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Heat Treatment Of Sheet Steel (AREA)
- Heat Treatment Of Steel (AREA)
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP15339179A JPS5677329A (en) | 1979-11-27 | 1979-11-27 | Production of composite structure high tensile cold-rolled steel plate of superior workability |
Publications (1)
Publication Number | Publication Date |
---|---|
BR8007714A true BR8007714A (en) | 1981-06-09 |
Family
ID=15561454
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR8007714A BR8007714A (en) | 1979-11-27 | 1980-11-26 | PROCESS FOR THE PRODUCTION OF A HIGH VOLTAGE COLD LAMINATED STEEL PLATE, OF TWO PHASES HAVING EXCELLENT PROCESSABILITY |
Country Status (10)
Country | Link |
---|---|
JP (1) | JPS5677329A (en) |
BE (1) | BE886350A (en) |
BR (1) | BR8007714A (en) |
CA (1) | CA1142069A (en) |
DE (1) | DE3044339A1 (en) |
FR (1) | FR2470163A1 (en) |
GB (1) | GB2066852B (en) |
IT (1) | IT1134491B (en) |
NL (1) | NL184790C (en) |
SE (1) | SE441278C (en) |
Families Citing this family (8)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH0674487B2 (en) * | 1986-11-28 | 1994-09-21 | 新日本製鐵株式会社 | High toughness electric resistance welded steel pipe with excellent saw resistance |
JPS644429A (en) * | 1987-06-26 | 1989-01-09 | Nippon Steel Corp | Manufacture of high-strength cold-rolled steel sheet with high (r) value |
JP2531591Y2 (en) * | 1991-03-19 | 1997-04-02 | 株式会社ノダ | Fire door |
CN104388816A (en) * | 2014-10-29 | 2015-03-04 | 江苏沙钢集团有限公司 | Low-carbon steel plate with ultralow yield-strength ratio and manufacturing method thereof |
CN106480281A (en) * | 2015-08-24 | 2017-03-08 | 鞍钢股份有限公司 | A kind of production method of high magentic induction oriented electrical sheet |
CN106480282A (en) * | 2015-08-24 | 2017-03-08 | 鞍钢股份有限公司 | A kind of production method of the efficient electrical sheet of No yield point |
CN106480305A (en) * | 2015-08-24 | 2017-03-08 | 鞍钢股份有限公司 | A kind of production method improving cold rolling electric decarburization efficiency |
CN111826507B (en) * | 2020-06-19 | 2021-12-03 | 华菱安赛乐米塔尔汽车板有限公司 | Production process of steel with ultrahigh yield ratio |
Family Cites Families (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS5443453B2 (en) * | 1973-07-25 | 1979-12-20 | ||
JPS5619380B2 (en) * | 1973-08-11 | 1981-05-07 | ||
JPS5157623A (en) * | 1974-11-18 | 1976-05-20 | Nippon Kokan Kk | Takaitosoyakitsukekokaseitosugureta hijikoseiomotsukochoryokureienkohanno seizohoho |
US4033789A (en) * | 1976-03-19 | 1977-07-05 | Jones & Laughlin Steel Corporation | Method of producing a high strength steel having uniform elongation |
BE846024A (en) * | 1976-09-09 | 1977-03-09 | PROCESS FOR THE CONTINUOUS THERMAL TREATMENT OF SHEETS | |
JPS5827329B2 (en) * | 1978-04-05 | 1983-06-08 | 新日本製鐵株式会社 | Manufacturing method of low yield ratio high tensile strength hot rolled steel sheet with excellent ductility |
-
1979
- 1979-11-27 JP JP15339179A patent/JPS5677329A/en active Pending
-
1980
- 1980-11-24 NL NLAANVRAGE8006404,A patent/NL184790C/en not_active IP Right Cessation
- 1980-11-25 SE SE8008247A patent/SE441278C/en not_active IP Right Cessation
- 1980-11-25 DE DE19803044339 patent/DE3044339A1/en active Granted
- 1980-11-26 FR FR8025126A patent/FR2470163A1/en active Granted
- 1980-11-26 BR BR8007714A patent/BR8007714A/en not_active IP Right Cessation
- 1980-11-26 BE BE2/58877A patent/BE886350A/en not_active IP Right Cessation
- 1980-11-27 CA CA000365677A patent/CA1142069A/en not_active Expired
- 1980-11-27 IT IT26281/80A patent/IT1134491B/en active
- 1980-11-27 GB GB8037995A patent/GB2066852B/en not_active Expired
Also Published As
Publication number | Publication date |
---|---|
JPS5677329A (en) | 1981-06-25 |
SE441278B (en) | 1985-09-23 |
SE441278C (en) | 1987-05-04 |
FR2470163A1 (en) | 1981-05-29 |
DE3044339C2 (en) | 1987-01-08 |
IT1134491B (en) | 1986-08-13 |
GB2066852A (en) | 1981-07-15 |
NL184790C (en) | 1989-11-01 |
BE886350A (en) | 1981-03-16 |
CA1142069A (en) | 1983-03-01 |
IT8026281A0 (en) | 1980-11-27 |
GB2066852B (en) | 1983-03-23 |
NL184790B (en) | 1989-06-01 |
FR2470163B1 (en) | 1985-04-19 |
DE3044339A1 (en) | 1981-07-02 |
SE8008247L (en) | 1981-05-28 |
NL8006404A (en) | 1981-07-01 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR8707115A (en) | PROCESS FOR THE PRODUCTION OF A STEEL STEEL STRIP TO THE DUPLEX STRUCTURE CHROME, HAVING HIGH RESISTANCE AND STRETCHING AND ALSO REDUCED FLAT ANISOTROPY | |
BR7704835A (en) | ARMORED STEEL PIPES AND PROCESS FOR ITS PRODUCTION BY LAMINATION | |
BR8008153A (en) | PROCESS TO PRODUCE A TWO PHASE STEEL PLATE | |
BR8003776A (en) | PERFECT PROCESS TO PRODUCE A POLYMER OR COPOLYMER FROM AN OLEFINE | |
BR8605420A (en) | PROCESS FOR THE PRODUCTION OF A FOAMED POLYMERIC COMPOSITION, COMPOSITION SO PRODUCED AND LAMINATED | |
BR7603555A (en) | PROCESS AND INSTALLATION TO SWITCH AT LEAST ONE SERVICE INFORMATION | |
BR7507609A (en) | PROCESS FOR MANUFACTURING A COLD REDUCED STEEL PLATE THAT HAS HIGH RESISTANCE AND HIGH CAPACITY FOR THERMAL HARDENING, AND EXCELLENT NON-AGING PROPERTY | |
BR7605658A (en) | PROCESS FOR THE PRODUCTION OF LEAVES HAVING HIGH RESISTANCE TO WATER ABSORPTION | |
BR8700442A (en) | PROCESS TO IMPROVE THE MECHANICAL RESISTANCE OF A LEAF PLATE | |
BR7701980A (en) | PROCESS TO CRYOGENICALLY DEFORM A METAL PLATE | |
BR8600829A (en) | LUBRICANT COMPOSITION AND PROCESS FOR THE MANUFACTURE OF COLD LAMINATED STEEL SHEETS | |
BR8007714A (en) | PROCESS FOR THE PRODUCTION OF A HIGH VOLTAGE COLD LAMINATED STEEL PLATE, OF TWO PHASES HAVING EXCELLENT PROCESSABILITY | |
BR7701471A (en) | PERFECT PROCESS FOR THE PRODUCTION OF A FORMAMIDE | |
BR8600963A (en) | PROCESS FOR THE PRODUCTION OF A MOLDABLE FINE STEEL SHEET | |
IT1081185B (en) | PROCESS FOR THE PRODUCTION OF NON-DIRECTIONAL ELECTRIC STEEL SHEETS WITHOUT CRESTS | |
BR7902369A (en) | SEGMENT EXCHANGER APPLIANCE FOR A CONTINUOUS FOUNDATION INSTALLATION AND PROCESS FOR THE SAME OPERATION | |
BR7600624A (en) | PERFECT PROCESS TO MANUFACTURE AN ELECTROLYTICALLY CHROMED STEEL SHEET | |
BR7309085D0 (en) | PROCESS FOR THE PRODUCTION OF STEEL PLATES, COLD LAMINATED, HAVING NOT ONLY THE PROPERTY OF NON-AGING AS ALSO EXCELLENT CONFORMABILITY | |
BR8002340A (en) | STEEL MANUFACTURING PROCESS | |
BR8500856A (en) | PROCESS FOR THE POLYMERIZATION OF AN ALPHA-MONOOLEFINE | |
AR219499A1 (en) | NEW 1-BENZOIL-3- (2,2,4,4-TETRAFLUORO-1,3-BENZODIOXIN-6-IL) -UREAS, WITH INSECTICIDED PROPERTIES, PROCEDURES FOR THEIR PRODUCTION AND INSECTICIDED COMPOSITIONS BASED ON THE SAME | |
BR8004421A (en) | PROCESS FOR THE PRODUCTION OF LAMINATES WITH STRONG TOLERANCE | |
BR7705786A (en) | PROCESS FOR THE PRODUCTION OF ALUMINUM-SILICON ALLOYS | |
BR8007715A (en) | PROCESS FOR THE PRODUCTION OF A COLD LAMINATED STEEL SHEET, OF HIGH RESISTANCE, HAVING EXCELLENT PAINTING AND WELDING | |
BR7705337A (en) | NEW PROCESS FOR THE PREPARATION OF 5-AMINO-1,2,3-TIADIAZO |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
MK | Patent expired |
Effective date: 19951126 |