BR112018001193A2 - ferro fundido ferrítico com grafita esférica - Google Patents
ferro fundido ferrítico com grafita esféricaInfo
- Publication number
- BR112018001193A2 BR112018001193A2 BR112018001193A BR112018001193A BR112018001193A2 BR 112018001193 A2 BR112018001193 A2 BR 112018001193A2 BR 112018001193 A BR112018001193 A BR 112018001193A BR 112018001193 A BR112018001193 A BR 112018001193A BR 112018001193 A2 BR112018001193 A2 BR 112018001193A2
- Authority
- BR
- Brazil
- Prior art keywords
- cast iron
- spherical graphite
- maximum
- ferritic cast
- ferritic
- Prior art date
Abstract
a presente invenção refere-se a ferro fundido ferrítico com grafita esférica, que contém em % em massa: 3,4 a 3,8% de carbono (c), 1,5 a 2,1% de silício (si), no máximo, 0,25% de manganês (mn), no máximo 0,05% de enxofre (s), no máximo, 0,6% de elementos acessórios usuais, restante ferro (fe). para obter em um ferro fundido ferrítico com grafita esférica desse tipo uma resistência ao impacto de entalhe de pelo menos 20j, a uma temperatura de -10°c, a invenção propõe que os elementos acessórios cromo (cr), vanádio (v), nióbio (nb) e titânio (ti) estejam limitados, na soma, a 0,05% em massa. desse modo, resulta nesse ferro fundido um número de esferas grafíticas que é menor ou igual a 160/mm2. além disso, a invenção refere-se ao uso de um ferro fundido desse tipo para componentes sensíveis ao frio, particularmente, em navios ou centrais elétricas eólicas.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
DE102015111915.3A DE102015111915A1 (de) | 2015-07-22 | 2015-07-22 | Ferritisches Gusseisen mit Kugelgraphit |
PCT/EP2016/067271 WO2017013165A1 (de) | 2015-07-22 | 2016-07-20 | Ferritisches gusseisen mit kugelgraphit |
Publications (1)
Publication Number | Publication Date |
---|---|
BR112018001193A2 true BR112018001193A2 (pt) | 2018-09-11 |
Family
ID=56683892
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
BR112018001193A BR112018001193A2 (pt) | 2015-07-22 | 2016-07-20 | ferro fundido ferrítico com grafita esférica |
Country Status (9)
Country | Link |
---|---|
US (1) | US20180209020A1 (pt) |
EP (1) | EP3325682A1 (pt) |
JP (1) | JP2018527470A (pt) |
KR (1) | KR20180031703A (pt) |
CN (1) | CN107949649A (pt) |
BR (1) | BR112018001193A2 (pt) |
DE (1) | DE102015111915A1 (pt) |
MX (1) | MX2018000935A (pt) |
WO (1) | WO2017013165A1 (pt) |
Families Citing this family (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN108588545B (zh) * | 2018-03-19 | 2019-09-13 | 河北硕凯铸造有限公司 | 一种ggg70l球墨铸铁及其制备方法 |
CN110819885A (zh) * | 2019-12-17 | 2020-02-21 | 湘电风能有限公司 | 一种风电机组用高强度高韧性低温球墨铸铁 |
CN111560560A (zh) * | 2020-06-30 | 2020-08-21 | 河南中原吉凯恩气缸套有限公司 | 一种离心铸造高强度球墨铸铁气缸套的方法 |
CN112410654A (zh) * | 2020-10-30 | 2021-02-26 | 江苏华龙铸铁型材有限公司 | 一种柱状球墨铸铁材料及其垂直连铸法铸造工艺 |
Family Cites Families (13)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS6030735B2 (ja) * | 1979-10-30 | 1985-07-18 | 日立金属株式会社 | 球状黒鉛鋳鉄およびその製造方法 |
FR2486100A1 (fr) * | 1980-07-01 | 1982-01-08 | Creusot Loire | Pieces massives en fonte a graphite spheroidal |
GB2203448B (en) * | 1987-03-09 | 1991-05-22 | Hitachi Metals Ltd | Nodular cast iron |
JPS6439322A (en) * | 1987-08-06 | 1989-02-09 | Kawasaki Steel Co | Production of thick-walled ductile cast iron having excellent ductility and toughness |
US4990194A (en) * | 1988-09-09 | 1991-02-05 | Hitachi Metals, Ltd. | Thin high-strength article of spheroidal graphite cast iron and method of producing same |
JPH09125190A (ja) * | 1995-10-31 | 1997-05-13 | Hitachi Metals Ltd | 高耐力、高延性球状黒鉛鋳鉄 |
US6126713A (en) * | 1996-10-24 | 2000-10-03 | Hitachi Metals, Ltd. | Additive for use in producing spheroidal graphite cast iron |
CN104024450B (zh) * | 2011-12-28 | 2017-03-29 | 日立金属株式会社 | 强度和韧性优异的球状石墨铸铁及其制造方法 |
CN103898396B (zh) * | 2012-12-26 | 2016-02-24 | 江苏吉鑫风能科技股份有限公司 | 兆瓦级风电高强高韧-30℃低温球墨铸铁件的制备方法 |
JP5506973B1 (ja) * | 2013-03-29 | 2014-05-28 | 日立造船株式会社 | 球状黒鉛鋳鉄およびその製造方法 |
CN103205624A (zh) * | 2013-04-16 | 2013-07-17 | 常熟建华模具科技股份有限公司 | 铁素体基体的石墨铸铁玻璃模具及其制备方法 |
JP5655115B1 (ja) * | 2013-06-28 | 2015-01-14 | 株式会社リケン | 球状黒鉛鋳鉄 |
CN103436772B (zh) * | 2013-09-05 | 2016-03-30 | 常州华德机械有限公司 | -60℃低温韧性铁素体球墨铸铁及其制备方法 |
-
2015
- 2015-07-22 DE DE102015111915.3A patent/DE102015111915A1/de not_active Withdrawn
-
2016
- 2016-07-20 BR BR112018001193A patent/BR112018001193A2/pt not_active Application Discontinuation
- 2016-07-20 MX MX2018000935A patent/MX2018000935A/es unknown
- 2016-07-20 WO PCT/EP2016/067271 patent/WO2017013165A1/de active Application Filing
- 2016-07-20 US US15/746,146 patent/US20180209020A1/en not_active Abandoned
- 2016-07-20 EP EP16750638.5A patent/EP3325682A1/de not_active Withdrawn
- 2016-07-20 CN CN201680051021.3A patent/CN107949649A/zh active Pending
- 2016-07-20 JP JP2018522860A patent/JP2018527470A/ja active Pending
- 2016-07-20 KR KR1020187004086A patent/KR20180031703A/ko not_active Application Discontinuation
Also Published As
Publication number | Publication date |
---|---|
DE102015111915A1 (de) | 2017-01-26 |
EP3325682A1 (de) | 2018-05-30 |
JP2018527470A (ja) | 2018-09-20 |
US20180209020A1 (en) | 2018-07-26 |
MX2018000935A (es) | 2018-09-27 |
CN107949649A (zh) | 2018-04-20 |
KR20180031703A (ko) | 2018-03-28 |
WO2017013165A1 (de) | 2017-01-26 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
BR112018001193A2 (pt) | ferro fundido ferrítico com grafita esférica | |
BRPI0805832A2 (pt) | aço não-tratado termicamente para uso em forjamento a quente do tipo martensita e peça de aço não-tratada termicamente forjada a quente | |
BR112018072904A2 (pt) | barra de aço para membro de fundo de poço e membro de fundo de poço | |
BR112012028294A2 (pt) | "aço inoxidável austenítico de baixo teor de níquel e uso do referido aço" | |
BR112012014178A2 (pt) | aço para mola com alta resistência | |
BR112015005951A2 (pt) | placa de aço resistente à abrasão que tem excelente tenacidade à baixa temperatura e excelente resistência ao desgaste corrosivo | |
BR112019005395A2 (pt) | material de aço, tubo de aço de poço de petróleo e método para produzir material de aço | |
BR112012014801A2 (pt) | "uso combinado de proteínas cry1ca e cry1fa para controle de resistência a insetos" | |
BR112016011895A2 (pt) | Liga forjável de níquel-cromo-cobalto-titânio-alumínio endurecedora, e seus usos | |
BR112019007842A2 (pt) | cano inteiriço de aço inoxidável martensítico para cano de poço de petróleo e método para produzir cano inteiriço | |
BR112019000376A2 (pt) | aço martensítico resistente ao calor de alto teor de cromo com alta resistência à ruptura por fluência e resistência de oxidação combinadas | |
BR112016012102A2 (pt) | liga de níquel-cromo-titânio-alumínio, endurecedora, com boa resistência ao desgaste, resistência à fluência, resistência à corrosão e processabilidade | |
BR112018016547A2 (pt) | aços ferrítico-martensíticos, resistentes à radiação, de temperatura elevada | |
BR112018017095A2 (pt) | aço patinável | |
BR112015031072A2 (pt) | aço inoxidável duplex ferrítico austenítico | |
BR112012030817A2 (pt) | "aço de baixa liga com elevado limite de elasticidade e alta resistência à fissuração sob tensão por sulfufetos". | |
BR112017023673A2 (pt) | aço avançado de alta resistência de terceira geração e baixa liga | |
BR112012021177A2 (pt) | lâmina de aço elétrica não orientada | |
BR112015031596A2 (pt) | tubo de aço sem emendas para tubo em linha usado em ambientes acres | |
BR112018067359A2 (pt) | roda para ferrovia | |
BR112016024014A2 (pt) | metal de soldagem que apresenta força, dureza e resistência ao craqueamento sr excelentes | |
BR112021021482A2 (pt) | Chapa de aço laminada a frio e revestida, método de produção de uma chapa de aço laminada a frio e revestida, uso de uma chapa de aço e veículo | |
BR112017003652A2 (pt) | aço para parafuso de alta resistência, e parafuso de alta resistência | |
BR112019006254A2 (pt) | placa de aço | |
BR112019002593A2 (pt) | chapa de aço laminado a quente |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
B11A | Dismissal acc. art.33 of ipl - examination not requested within 36 months of filing | ||
B11Y | Definitive dismissal acc. article 33 of ipl - extension of time limit for request of examination expired |