    PROCEDE   DE FABRICATION D'AGGLOMERE DE   COMBUSTIBLES   ET PRO- DOIT EN RESULTANT. 



   La présente invention a pour objet un nouveau procédé dE fabrication   d'agglomérés   de combustibles permettant d'utili- ser des combustibles pauvres et par suite de faible valeur: 
 EMI1.1 
 fine,poussiers,schlamms,t1rbes,etc)ans emploi comme liant de brai de goudron,qui,dans les circonstances actuel- les, est difficilement obtenable. 



   Conformément à l'invention,on utilise comme liant du ciment Portland, tel que celui employé habituellement pour la fabrication du béton.Il a été démontré   quJen   mélangeant ,dans des proportions déterminées, du ciment Portland à du pous- sier,à du schlamm,à de la tourbe,ou à un mélange de ces pro- duits, on obtient par agglomération un combustible économi- ' que de pouvoir calorifique relativement élevé et de manuten- tion aisée. 



   Suivant un mode opératoire particulièrement avantageux, 

 <Desc/Clms Page number 2> 

 le procédé de fabrication conforme à l'invention s'exécute de la manière suivante: 
On traite par exemple 75   kgs.de   poussier de charbon avec 75   kgs.de   schlamm et 8% de ciment Portland,soit 12   kgs.   



   On mélange d'abord à sec,très intimement,24- kgs de poussier avec les 12   kgs.de     ciment,puis   on agit de même avec le restant du   poussier,soit   51 kgs., et les 75 kgs.de schlamn Enfin on mélange les deux masses ci-dessus obtenues, et le tout est ensuite passé au broyeur avec addition d'une quan- tité d'eau,qui dépend du type de produit   dé siré.   Dans le cas de briquettes,par exemple,cette quantité d'eau devra être telle que le produit possède une compacité suffisante. 



  Finalement la pâte venant du broyeur est soumise à l'action 'd'une presse,qui l'agglomère sous forme de   briques,briquet-   tes,boulets,etc. 



   Il va de soi que les proportions indiquées ci-dessus peuvent être modifiées dans une certaine limite sans sortir du domaine de l'invention,et cela suivant les produits de base employés. On resterait également dans; le cadre de l' invention en ajoutant éventuellement,en cours de   fa.brica-   tion, aux   mélanges   spécifiés ci-dessus,ou à la pâte,d'autres substances agglomérantes ou non. 



    REVENDICATIONS.   



   I. Procédé de fabrication d'agglomérés de combusti- bles ,caractérisé en ce que l'on utilise comme liant, avec du poussier,du schlamm,de la tourbe, ou un mélange de ces produits, du ciment Portland.



   <Desc / Clms Page number 1>
 



    PROCESS FOR THE MANUFACTURE OF FUEL AGGLOMERATES AND RESULTS.



   The present invention relates to a new process for the manufacture of fuel agglomerates making it possible to use poor fuels and therefore of low value:
 EMI1.1
 fine, dust, slime, turf, etc.) used as a binder for tar pitch, which, under present circumstances, is difficult to obtain.



   In accordance with the invention, use is made as a binder of Portland cement, such as that usually employed for the manufacture of concrete. It has been demonstrated that by mixing, in determined proportions, Portland cement with dust, with slime, with peat or a mixture of these products, agglomeration results in an economical fuel of relatively high calorific value and easy to handle.



   According to a particularly advantageous procedure,

 <Desc / Clms Page number 2>

 the manufacturing process according to the invention is carried out as follows:
For example, 75 kgs of coal dust are treated with 75 kgs of schlamm and 8% of Portland cement, ie 12 kgs.



   24- kgs of dust are first mixed dry, very intimately with the 12 kgs of cement, then the same is done with the remainder of the dust, i.e. 51 kgs., And the 75 kgs of schlamn. the two above masses obtained, and the whole is then passed to the mill with the addition of a quantity of water, which depends on the type of product desired. In the case of briquettes, for example, this quantity of water should be such that the product has sufficient compactness.



  Finally, the pulp coming from the mill is subjected to the action of a press, which agglomerates it in the form of bricks, briquettes, balls, etc.



   It goes without saying that the proportions indicated above can be modified within a certain limit without departing from the scope of the invention, and this depending on the basic products used. We would also stay in; within the scope of the invention by optionally adding, during fa.brica- tion, to the mixtures specified above, or to the paste, other agglomerating substances or not.



    CLAIMS.



   I. Process for the manufacture of fuel agglomerates, characterized in that Portland cement is used as a binder with dust, slime, peat, or a mixture of these products.

Claims

2, A method according to claim I, characterized in that the proportion of cement added as a binder is about 8% of the weight of the dust, of the slurry, of the peat, or of the mixture of these products used.

3. Method according to claims I and 2, characterized in that it can be carried out as follows: 24 kgs of dust are intimately mixed with 12 kgs of Portland cement. <Desc / Clms Page number 3> dry, likewise separately 5 I kgs. of dust with 75 kgs. of schlamm, then the two above mixtures are combined, which are passed to the mill with the addition of a quantity of water depending on the final product to be obtained, finally the paste coming from the mill is subjected to pressure in a briquetting press or the like.

4. Agglomerated combustible product obtained by the above process and having the shape of brick, briquettes, ball, etc.