BE1029746A1 - PLA coating of fertilizers - Google Patents

PLA coating of fertilizers Download PDF

Info

Publication number
BE1029746A1
BE1029746A1 BE20215705A BE202105705A BE1029746A1 BE 1029746 A1 BE1029746 A1 BE 1029746A1 BE 20215705 A BE20215705 A BE 20215705A BE 202105705 A BE202105705 A BE 202105705A BE 1029746 A1 BE1029746 A1 BE 1029746A1
Authority
BE
Belgium
Prior art keywords
weight
polylactic acid
monomer units
proportion
lactic acid
Prior art date
Application number
BE20215705A
Other languages
German (de)
Other versions
BE1029746B1 (en
Inventor
Yevgeny Makhynya
Original Assignee
Thyssenkrupp Ag
Thyssenkrupp Ind Solutions Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Thyssenkrupp Ag, Thyssenkrupp Ind Solutions Ag filed Critical Thyssenkrupp Ag
Priority to BE20215705A priority Critical patent/BE1029746B1/en
Priority to PCT/EP2022/075033 priority patent/WO2023036893A1/en
Publication of BE1029746A1 publication Critical patent/BE1029746A1/en
Application granted granted Critical
Publication of BE1029746B1 publication Critical patent/BE1029746B1/en

Abstract

Die vorliegende Erfindung betrifft ein partikuläres Düngemittel, wobei das partikuläre Düngemittel eine Beschichtung aufweist, wobei die Beschichtung Polymilchsäuremasse enthält, dadurch gekennzeichnet, dass die Polymilchsäuremasse einen Anteil von 70 % bis 99 % L-Milchsäure-Monomereinheiten und 1 % bis 30 % D-Milchsäure-Monomereinheiten aufweist.The present invention relates to a particulate fertilizer, the particulate fertilizer having a coating, the coating containing polylactic acid mass, characterized in that the polylactic acid mass has a proportion of 70% to 99% L-lactic acid monomer units and 1% to 30% D-lactic acid -Has monomer units.

Description

PLA-Beschichtung von DüngemittelnPLA coating of fertilizers

Die Erfindung betrifft ein partikuläres Düngemittel mit einer PLA-Beschichtung, derThe invention relates to a particulate fertilizer with a PLA coating

Verwendung einer geeigneten PLA-Masse, einer Lösung mit PLA zur Beschichtung, derUse of a suitable PLA mass, a solution with PLA for coating, the

Verwendung einer entsprechenden Lösung sowie eines Verfahrens zur Beschichtung partikulärer Düngemittel.Use of a corresponding solution and a method for coating particulate fertilizers.

Die Patentschrift EP 1 890 985 B1 beschreibt ein beschichtetes Düngemittel mit kontrollierter Wirkstofffreisetzung. Die Offenlegungsschrift DE 196 03 739 A1 beschreibt Mischungen aus Düngemittelgranulaten. Die OffenlegungsschriftPatent specification EP 1 890 985 B1 describes a coated fertilizer with a controlled release of active ingredient. The published application DE 196 03 739 A1 describes mixtures of fertilizer granules. The disclosure document

EP 0 763 510 A1 beschreibt eine mittels Wirbelschicht-Granulation aufgesprühteEP 0 763 510 A1 describes one sprayed on by means of fluidized bed granulation

Polymer-Schicht. Die Patentschrift US 9,266,787 B2 beschreibt Düngemittel mit einerpolymer layer. The patent US 9,266,787 B2 describes fertilizers with a

Polymer-Schicht mit spezifischer Dicke.Polymer layer with specific thickness.

Aus der WO 2006 133 893 A2 ist ein beschichtetes Düngemittel mit kontrollierterWO 2006 133 893 A2 discloses a coated fertilizer with a controlled

Wirkstofffreisetzung bekannt.Drug release known.

Aus der JP 07309689 A ist ein PLA aufweisendes Düngemittel bekannt.From JP 07309689 A a fertilizer containing PLA is known.

Aus der JP 11092304 A ist ein Sprühverfahren für ein biologisch abbaubares Polymer bekannt.JP 11092304 A discloses a spraying method for a biodegradable polymer.

Aus der JP 07033577 A ist ein PLA beschichtetes Düngemittel bekannt.A PLA-coated fertilizer is known from JP 07033577 A.

Aus der DE 10 2017 217 498 A1 ist ein Verfahren zur Herstellung PLA-beschichteter partikulärer Düngemittel bekannt.A method for producing PLA-coated particulate fertilizers is known from DE 10 2017 217 498 A1.

Es hat sich jedoch gezeigt, dass handelsübliche PLA-Massen nur eine begrenzteHowever, it has been shown that commercially available PLA masses only have a limited

Löslichkeit in geeigneten Lösemitteln aufweisen. Zwar weist PLA in vielen chloriertenHave solubility in suitable solvents. True, PLA has chlorinated in many

Lôsemitteln gute Löslichkeiten auf, chlorierte Lösemittel sind jedoch für dieSolvents have good solubilities, but chlorinated solvents are for the

Beschichtungen aus Ökologischen Gesichtspunkten nicht geeignet. Daher ist eine qualitativ gute Beschichtung sowie eine einfache und schnelle Herstellung derCoatings not suitable from an ecological point of view. Therefore, a qualitatively good coating as well as a simple and quick production of the

Beschichtung schwierig.coating difficult.

Aufgabe der Erfindung ist es, ein PLA zu finden, welches einfacher eine qualitativ guteThe object of the invention is to find a PLA which simply has a good quality

Beschichtung ermöglicht.coating allows.

Gelöst wird diese Aufgabe durch ein partikuläres Düngemittel mit den in Anspruch 1 angegebenen Merkmalen, eine Verwendung von Polymilchsäuremasse mit den inThis object is achieved by a particulate fertilizer with the features specified in claim 1, a use of polylactic acid mass with the

Anspruch 9 angegebenen Merkmalen einer Lösung mit den in Anspruch 12 angegebenen Merkmalen, einer Verwendung der Lösung mit den in Anspruch 16 angegebenen Merkmalen sowie durch ein Verfahren zur Beschichtung mit den inClaim 9 specified features of a solution with the features specified in claim 12, use of the solution with the features specified in claim 16 and by a method for coating with the in

Anspruch 17 angegebenen Merkmalen. Vorteilhafte Weiterbildungen ergeben sich aus den Unteransprüchen und der nachfolgenden Beschreibung.Claim 17 specified features. Advantageous developments result from the dependent claims and the following description.

Das erfindungsgemäße partikuläre Düngemittel weist eine Beschichtung auf wobei dieThe particulate fertilizer according to the invention has a coating on which the

Beschichtung Polymilchsäuremasse enthält. Erfindungswesentlich weist dieCoating contains polylactic acid mass. Essential to the invention has the

Polymilchsäuremasse einen Anteil von 70 % bis 99 %, bevorzugt von 90 % bis 99 %, L-Polylactic acid mass has a proportion of 70% to 99%, preferably 90% to 99%, L-

Milchsäure-Monomereinheiten und 1% bis 30 %, bevorzugt von 1% bis 10%, D-lactic acid monomer units and 1% to 30%, preferably from 1% to 10%, D-

Milchsäure-Monomereinheiten auf.lactic acid monomer units.

Eine Polymilchsäuremasse im Sinne der Erfindung weist wenigstens eine ersteA polylactic acid composition according to the invention has at least one first

Polymilchsäure auf, kann aber auch ein Blend aus zwei oder mehr verschiedenenPolylactic acid, but can also be a blend of two or more different ones

Polymilchsäuren sein. Daneben können Dimere oder Oligomere der Milchsäure enthalten sein, vorzugsweise mit weniger als 5 Gew.-%. Zusätzlich kann diebe polylactic acids. In addition, dimers or oligomers of lactic acid can be present, preferably with less than 5% by weight. In addition, the

Polymilchsäure bis zu 5 Gew.-% andere Komponenten enthalten, beispielsweisePolylactic acid up to 5 wt .-% contain other components, for example

Farbstoffe zu Einfärbung des Produkts.Dyes to color the product.

Polymilchsäure (Polylactide, polylactic acid, PLA) werden oftmals über ringöffnendePolylactic acid (polylactide, polylactic acid, PLA) are often used via ring-opening

Polyaddition von Lactid, einem ringförmigen Ester aus zwei Milchsäure-Polyaddition of lactide, a cyclic ester of two lactic acid

Monomereinheiten, hergestellt. Da Milchsäure ein stereogenes Zentrum aufweist gibt es drei mögliche Lactide. Das erste besteht aus zwei L-Milchsäure-Monomereinheiten und wird entsprechend L-Lactid genannt. Ein zweites besteht aus zwei D-Milchsäure-monomer units produced. Since lactic acid has a stereogenic center, there are three possible lactides. The first consists of two L-lactic acid monomer units and is accordingly named L-lactide. A second consists of two D-lactic acid

Monomereinheiten und wird entsprechend D-Lactid genannt. Ein drittes besteht aus einer L-Milchsäure-Monomereinheit und einer D-Milchsäure-Monomereinheit und wird als meso-Lactid bezeichnet. Vor der ringöffnenden Polyaddition werden die Lactide getrennt, wobei für die meisten Anwendungen reines L-Lactid verwendet wird. Das entstehende Polymer, auch PLLA genannt, weist eine vergleichsweise hoheMonomer units and is accordingly called D-lactide. A third consists of an L-lactic acid monomeric unit and a D-lactic acid monomeric unit and is referred to as meso-lactide. Before the ring-opening polyaddition, the lactides are separated, using pure L-lactide for most applications. The resulting polymer, also called PLLA, has a comparatively high

Kristallinität auf und einen Schmelzpunkt von bis über 175 °C. Steigt der Anteil an D-crystallinity and a melting point of up to over 175 °C. If the proportion of D-

Milchsäure-Monomereinheiten in der Polymilchsäure, so ist ab einem Anteil von etwa 6% an D-Milchsäure-Monomereinheiten das erhaltene Polymer amorph und weist einen geringeren Schmelzpunkt auf, welcher unter 130 °C liegen kann.lactic acid monomer units in the polylactic acid, the polymer obtained is amorphous from a proportion of about 6% of D-lactic acid monomer units and has a lower melting point, which can be below 130.degree.

Reines PLLA weist eine extrem hohe Kristallinität auf und einen hohen Schmelzpunkt.Pure PLLA has extremely high crystallinity and a high melting point.

Mit steigendem Anteil an D-Milchsäure-Monomereinheiten nehmen Kristllinität undWith increasing proportion of D-lactic acid monomer units, crystallinity and

Schmelzpunkt ab. Es hat sich herausgestellt, dass entsprechender Anteil an D-melting point. It has been found that the corresponding proportion of D-

Milchsäure-Monomereinheiten die Eignung für die Beschichtung von partikulärenLactic acid monomer units suitability for coating particulate

Düngemitteln besonders gut geeignet ist.Fertilizers is particularly well suited.

In einer weiteren Ausführungsform der Erfindung weist die Polymilchsäuremasse einenIn a further embodiment of the invention, the polylactic acid mass has a

Anteil von 95% bis 98% L-Milchsäure-Monomereinheiten und 2% bis 5% D-Proportion of 95% to 98% L-lactic acid monomer units and 2% to 5% D-

Milchsäure-Monomereinheiten auf.lactic acid monomer units.

In einer weiteren Ausführungsform der Erfindung weist die Polymilchsäuremasse wenigstens eine erste Polymilchsäure auf, wobei die erste Polymilchsäure einen Anteil von 50 % bis 67 % L-Milchsäure-Monomereinheiten und 33 % bis 50 % D-Milchsäure-In a further embodiment of the invention, the polylactic acid composition has at least one first polylactic acid, the first polylactic acid having a proportion of 50% to 67% L-lactic acid monomer units and 33% to 50% D-lactic acid

Monomereinheiten aufweist.Has monomer units.

Verwendet man meso-Lactid zur ringöffnenden Polyaddition, so erhält man im Idealfall ein ataktisches Polymer mit 50 % L-Milchsäure-Monomereinheiten und 50% D-If meso-lactide is used for the ring-opening polyaddition, an atactic polymer with 50% L-lactic acid monomer units and 50% D-

Milchsäure-Monomereinheiten, da die Ringöffnung üblicherweise nicht stereoselektiv erfolgt. Die erhaltene Polymilchsäure wird auch m-PLA oder PDLLA genannt. Für die meisten Anwendungen erfolgt jedoch keine vollständige Aufreinigung des meso-Lactic acid monomer units since ring opening is not usually stereoselective. The polylactic acid obtained is also called m-PLA or PDLLA. For most applications, however, the meso-

Lactids, sodass sich bei einem üblicherweise vorhandenen Überschuss der natürlichenLactids, so that when there is usually an excess of the natural

L-Milchsäure-Monomereinheit ein Verhältnis von 2:1 bis 1:1 für L:D ergibt. Auch wenn einige Eigenschaften des PDLLA sich als für viele Anwendungen ungünstiger herausgestellt haben, so hat sich jedoch gerade für die Beschichtung von Düngemittel gezeigt, dass PDLLA wenigstens zwei positive Eigenschaften aufweist. Zum einen ist die Löslichkeit in geeigneten (nicht umweltschädlichen) Lösemitteln, beispielsweiseL-lactic acid monomer unit gives a ratio of 2:1 to 1:1 for L:D. Even if some properties of PDLLA have turned out to be unfavorable for many applications, it has been shown that PDLLA has at least two positive properties, especially for the coating of fertilizers. On the one hand, the solubility in suitable (non-polluting) solvents, for example

Aceton (Propanon) deutlich höher, zum anderen ist auch die biologische Abbaubarkeit erleichtert beziehungsweise beschleunigt. Die erste Eigenschaft erleichtert dieacetone (propanone) is significantly higher, and on the other hand the biodegradability is also facilitated or accelerated. The first property facilitates that

Beschichtung, die zweite Eigenschaft erleichtert die Freisetzung des Düngemittels auf dem Feld und den anschließenden schnellen, vollständigen und rückstandsfreienCoating, the second property, facilitates the release of the fertilizer on the field and the subsequent rapid, complete and residue-free

Abbau. Dadurch wurde festgestellt, dass gerade Beschichtungen, welche wenigstens eine erste Polymilchsäure aufweisen, wobei die erste Polymilchsäure einen Anteil von 50 % bis 67 % L-Milchsäure-Monomereinheiten und 33 % bis 50 % D-Milchsäure-degradation. It was thereby found that straight coatings which have at least one first polylactic acid, the first polylactic acid having a proportion of 50% to 67% L-lactic acid monomer units and 33% to 50% D-lactic acid

Monomereinheiten auf, für die Beschichtung von partikulären Düngemitteln überraschend gut geeignet sind. Reines PDLLA ist für eine Beschichtung weniger geeignet, da bei den üblichen Verarbeitungstemperaturen bereits zu einer Erweichung kommt. Damit kann es dann bei dem Beschichtungsprozess zu Verklebungen kommen.Monomer units that are surprisingly well suited for the coating of particulate fertilizers. Pure PDLLA is less suitable for a coating, since softening already occurs at the usual processing temperatures. This can then lead to sticking during the coating process.

Damit ist die Verarbeitbarkeit von reinem PDLLA nicht optimal, auch wenn dieThus, the processability of pure PDLLA is not optimal, even if the

Löslichkeit für die Beschichtung vorteilhaft wäre.Solubility for the coating would be advantageous.

In einer weiteren Ausführungsform der Erfindung weist die Beschichtung wenigstens eine zweite Polymilchsäure auf, wobei die zweite Polymilchsäure einen Anteil von 95 % bis 100% L-Milchsäure-Monomereinheiten und 0% bis 5% D-Milchsäure-In a further embodiment of the invention, the coating has at least one second polylactic acid, the second polylactic acid having a proportion of 95% to 100% L-lactic acid monomer units and 0% to 5% D-lactic acid

Monomereinheiten aufweist. Die zweite Polymilchsäure ist somit bevorzugt PLLA und damit kristallin.Has monomer units. The second polylactic acid is thus preferably PLLA and is therefore crystalline.

In einer weiteren Ausführungsform der Erfindung weist die Beschichtung einen Anteil der ersten Polymilchsäure von 0,1 Gew.-% bis 50 Gew.-% und einen Anteil der zweitenIn a further embodiment of the invention, the coating has a proportion of the first polylactic acid of 0.1% by weight to 50% by weight and a proportion of the second

Polymilchsäure von 50 Gew.-% bis 99,9 Gew.-% auf.polylactic acid from 50% to 99.9% by weight.

In einer weiteren Ausführungsform der Erfindung weist die Beschichtung einen Anteil der ersten Polymilchsäure von 5 Gew.-% bis 50 Gew.-%, bevorzugt 7,5 Gew.-% bisIn a further embodiment of the invention, the coating has a proportion of the first polylactic acid of 5% by weight to 50% by weight, preferably 7.5% by weight to

Gew.-%, besonders bevorzugt von 10 Gew.-% bis 20 Gew.-% und einen Anteil der 25 zweiten Polymilchsäure von 50 Gew.-% bis 95 Gew.-%, bevorzugt 75 Gew.-% bis 92,5 Gew.-%, besonders bevorzugt von 80 Gew.-% bis 90 Gew.-%, auf. In dieser% by weight, particularly preferably from 10% by weight to 20% by weight and a proportion of the second polylactic acid from 50% by weight to 95% by weight, preferably 75% by weight to 92.5% by weight %, more preferably from 80% to 90% by weight. In this

Ausführungsform ist somit der größte Anteil der Polymilchsäuremasse ein kristallinesEmbodiment is thus the largest portion of the polylactic acid mass is a crystalline

PLLA und nur eine gewisse Beimischung aus einem PDLLA. Auf diese Weise kann einePLLA and only some admixture of a PDLLA. In this way one can

Beschichtung erhalten werden, die eine vergleichsweise ähnliche Eigenschaft hinsichtlich mechanischer Belastbarkeit und Freisetzungsdynamik aufweist wie eine reine PLLA-Beschichtung, aufgrund des Anteils an PDLLA jedoch eine höhereCoating are obtained, which has a comparatively similar property in terms of mechanical strength and release dynamics as a pure PLLA coating, but due to the proportion of PDLLA higher

Löslichkeit und damit eine einfachere Herstellung ermôglichst.solubility and thus easier production.

In einer weiteren Ausführungsform der Erfindung weist das partikuläre Düngemittel einen Kern auf, wobei der Kern zu wenigstens 80 Gew.-% aus Harnstoff besteht.In a further embodiment of the invention, the particulate fertilizer has a core, the core consisting of at least 80% by weight of urea.

Harnstoff ist derzeit der wichtigste Stickstoffdünger. 5 In einer weiteren Ausführungsform der Erfindung weist das partikuläre Düngemittel einen Kern auf, wobei der Kern zu wenigstens 80 Gew.-% aus Kalkammonsalpeter (Calciumammoniumnitrat) besteht.Urea is currently the most important nitrogen fertilizer. In a further embodiment of the invention, the particulate fertilizer has a core, the core consisting of at least 80% by weight of calcium ammonium nitrate (calcium ammonium nitrate).

In einer weiteren Ausführungsform der Erfindung weist das partikuläre Düngemittel einen Kern auf, wobei der Kern zu wenigstens 80 Gew.-% aus PK; einem komplexenIn a further embodiment of the invention, the particulate fertilizer has a core, wherein the core consists of at least 80% by weight of PK; a complex one

Mischdünger, bestehend aus 2 Hauptnährstoffen für die Pflanzen (Phosphor in Form von Phosphate, in der Regel mono- und di-Ammoniumphosphat, Kalium in Form vonMixed fertilizer consisting of 2 main nutrients for the plants (phosphorus in the form of phosphates, usually mono- and di-ammonium phosphate, potassium in the form of

Kaliumsalzen) besteht.potassium salts).

In einer weiteren Ausführungsform der Erfindung weist das partikuläre Düngemittel einen Kern auf, wobei der Kern zu wenigstens 80 Gew.-% aus NPK; einem komplexenIn a further embodiment of the invention, the particulate fertilizer has a core, wherein the core consists of at least 80% by weight of NPK; a complex one

Mischdünger, bestehend aus 3 Hauptnährstoffen für die Pflanzen (Stickstoff in Form von Nitrate und/oder Harnstoff, Phosphor in Form von Phosphate, in der Regel mono- und di-Ammoniumphosphat, Kalium in Form von Kaliumsalzen) besteht.Mixed fertilizer consisting of 3 main nutrients for plants (nitrogen in the form of nitrates and/or urea, phosphorus in the form of phosphates, usually mono- and di-ammonium phosphate, potassium in the form of potassium salts).

In einem weiteren Aspekt betrifft die Erfindung die Verwendung einerIn a further aspect, the invention relates to the use of a

Polymilchsäuremasse zur Beschichtung von Düngemitteln. Erfindungsgemäß weist diePolylactic acid compound for coating fertilizers. According to the invention

Polymilchsäuremasse einen Anteil von 70 % bis 99 %, bevorzugt von 90 % bis 99 %, L-Polylactic acid mass has a proportion of 70% to 99%, preferably 90% to 99%, L-

Milchsäure-Monomereinheiten und 1% bis 30%, bevorzugt 1% bis 10%, D-lactic acid monomer units and 1% to 30%, preferably 1% to 10%, D-

Milchsäure-Monomereinheiten auf.lactic acid monomer units.

Für die Verwendung gilt das für die Beschichtung des partikulären DüngemittelsFor use, this applies to the coating of the particulate fertilizer

Gesagte analog. Dieses gilt auch für die weiteren Ausführungsformen.Said analogue. This also applies to the other embodiments.

In einer weiteren Ausführungsform der Erfindung weist die Polymilchsäuremasse wenigstens eine erste Polymilchsäure auf, wobei die erste Polymilchsäure einen Anteil von 50 % bis 67 % L-Milchsäure-Monomereinheiten und 33 % bis 50 % D-Milchsäure-In a further embodiment of the invention, the polylactic acid composition has at least one first polylactic acid, the first polylactic acid having a proportion of 50% to 67% L-lactic acid monomer units and 33% to 50% D-lactic acid

Monomereinheiten aufweist.Has monomer units.

In einer weiteren Ausführungsform der Erfindung weist die Polymilchsäuremasse wenigstens eine zweite Polymilchsäure auf, wobei die zweite Polymilchsäure einenIn a further embodiment of the invention, the polylactic acid composition has at least one second polylactic acid, the second polylactic acid having a

Anteil von 95% bis 100 % L-Milchsäure-Monomereinheiten und 0% bis 5% D-Proportion of 95% to 100% L-lactic acid monomer units and 0% to 5% D-

Milchsäure-Monomereinheiten aufweist.Has lactic acid monomer units.

In einer weiteren Ausführungsform der Erfindung weist die Polymilchsäuremasse wenigstens eine erste Polymilchsäure auf, wobei die erste Polymilchsäure einen Anteil von 50 % bis 67 % L-Milchsäure-Monomereinheiten und 33 % bis 50 % D-Milchsäure-In a further embodiment of the invention, the polylactic acid composition has at least one first polylactic acid, the first polylactic acid having a proportion of 50% to 67% L-lactic acid monomer units and 33% to 50% D-lactic acid

Monomereinheiten aufweist. Zusätzlich weist die Polymilchsäuremasse weiter auch wenigstens eine zweite Polymilchsäure auf, wobei die zweite Polymilchsäure einenHas monomer units. In addition, the polylactic acid composition also has at least one second polylactic acid, the second polylactic acid having a

Anteil von 95% bis 100 % L-Milchsäure-Monomereinheiten und 0% bis 5% D-Proportion of 95% to 100% L-lactic acid monomer units and 0% to 5% D-

Milchsäure-Monomereinheiten aufweist.Has lactic acid monomer units.

In einer weiteren Ausführungsform der Erfindung weist die Polymilchsäuremasse einenIn a further embodiment of the invention, the polylactic acid mass has a

Anteil der ersten Polymilchsäure von 5 Gew.-% bis 50 Gew.-%, bevorzugt von 7,5 Gew.-% bis 25 Gew.-%, besonders bevorzugt von 10 Gew.-% bis 20 Gew.-%, und einen Anteil der zweiten Polymilchsäure von 50 Gew.-% bis 95 Gew.-%, bevorzugt von 75 Gew.-% bis 92,5 Gew.-%, besonders bevorzugt von 80 Gew.-% bis 90 Gew.-%, auf.Proportion of the first polylactic acid from 5% by weight to 50% by weight, preferably from 7.5% by weight to 25% by weight, particularly preferably from 10% by weight to 20% by weight, and one Proportion of the second polylactic acid from 50% by weight to 95% by weight, preferably from 75% by weight to 92.5% by weight, particularly preferably from 80% by weight to 90% by weight.

In einem weiteren Aspekt betrifft die Erfindung eine Lösung zur Beschichtung von partikulären Düngemitteln, wobei die Lösung als Lösemittel Aceton oder einIn a further aspect, the invention relates to a solution for coating particulate fertilizers, the solution being acetone or a solvent

Lösemittelgemisch mit wenigstens 90 Gew.-% Aceton aufweist.Solvent mixture with at least 90% by weight of acetone.

Erfindungsgemäß sind in dem Lösemittel + Gew.-% bis 25 Gew.-%, bevorzugt 4 Gew.- % bis 17 Gew.-%, einer Polymilchsäuremasse gelöst. Die Polymilchsäuremasse weist von 70 % bis 99 %, bevorzugt von 90 % bis 99 %, L-Milchsäure-Monomereinheiten und 1 % bis 30 %, bevorzugt 1 % bis 10 %, D-Milchsäure-Monomereinheiten auf.According to the invention, +% by weight to 25% by weight, preferably 4% by weight to 17% by weight, of a polylactic acid composition are dissolved in the solvent. The polylactic acid mass has from 70% to 99%, preferably from 90% to 99%, L-lactic acid monomer units and 1% to 30%, preferably 1% to 10%, D-lactic acid monomer units.

Für die Lösung gilt das für die Beschichtung des partikulären Düngemittels Gesagte analog. Dieses gilt auch für die weiteren Ausführungsformen.What was said for the coating of the particulate fertilizer applies analogously to the solution. This also applies to the other embodiments.

In einer weiteren Ausführungsform der Erfindung wenigstens eine erste Polymilchsäure auf, wobei die erste Polymilchsäure einen Anteil von 50 % bis 67 % L-Milchsäure-In a further embodiment of the invention, at least one first polylactic acid, the first polylactic acid having a proportion of 50% to 67% L-lactic acid

Monomereinheiten und 33 % bis 50 % D-Milchsäure-Monomereinheiten aufweist.monomer units and 33% to 50% D-lactic acid monomer units.

In einer weiteren Ausführungsform der Erfindung weist die Polymilchsäuremasse wenigstens eine zweite Polymilchsäure auf, wobei die zweite Polymilchsäure einenIn a further embodiment of the invention, the polylactic acid composition has at least one second polylactic acid, the second polylactic acid having a

Anteil von 95% bis 100 % L-Milchsäure-Monomereinheiten und 0% bis 5% D-Proportion of 95% to 100% L-lactic acid monomer units and 0% to 5% D-

Milchsäure-Monomereinheiten aufweist.Has lactic acid monomer units.

In einer weiteren Ausführungsform der Erfindung weist die Polymilchsäuremasse wenigstens eine erste Polymilchsäure auf, wobei die erste Polymilchsäure einen Anteil von 50 % bis 67 % L-Milchsäure-Monomereinheiten und 33 % bis 50 % D-Milchsäure-In a further embodiment of the invention, the polylactic acid composition has at least one first polylactic acid, the first polylactic acid having a proportion of 50% to 67% L-lactic acid monomer units and 33% to 50% D-lactic acid

Monomereinheiten aufweist. Zusätzlich weist die Polymilchsäuremasse wenigstens eine zweite Polymilchsäure auf, wobei die zweite Polymilchsäure einen Anteil von 95 % bis 100% L-Milchsäure-Monomereinheiten und 0% bis 5% D-Milchsäure-Has monomer units. In addition, the polylactic acid composition has at least one second polylactic acid, the second polylactic acid having a proportion of 95% to 100% L-lactic acid monomer units and 0% to 5% D-lactic acid

Monomereinheiten aufweist.Has monomer units.

In einer weiteren Ausführungsform der Erfindung weist die Polymilchsäuremasse einenIn a further embodiment of the invention, the polylactic acid mass has a

Anteil der ersten Polymilchsäure von 5 Gew.-% bis 50 Gew.-%, bevorzugt von 7,5 Gew.-% bis 25 Gew.-%, besonders bevorzugt von 10 Gew.-% bis 20 Gew.-%, und einen Anteil der zweiten Polymilchsäure von 50 Gew.-% bis 95 Gew.-%, bevorzugt von 75 Gew.-% bis 92,5 Gew.-%, besonders bevorzugt von 80 Gew.-% bis 90 Gew.-%, auf.Proportion of the first polylactic acid from 5% by weight to 50% by weight, preferably from 7.5% by weight to 25% by weight, particularly preferably from 10% by weight to 20% by weight, and one Proportion of the second polylactic acid from 50% by weight to 95% by weight, preferably from 75% by weight to 92.5% by weight, particularly preferably from 80% by weight to 90% by weight.

In einer weiteren Ausführungsform der Erfindung sind in dem Lösemittel 12 Gew.-% bis 18 Gew.-% einer Polymilchsäuremasse gelöst. Dieses übersteigt die Löslichkeit von kristallinem PLLA bei Normalbedingungen deutlich und wird durch den Zusatz anIn a further embodiment of the invention, 12% by weight to 18% by weight of a polylactic acid composition are dissolved in the solvent. This clearly exceeds the solubility of crystalline PLLA under normal conditions and is increased by the addition of

PDLLA erreicht.PDLLA reached.

In einem weiteren Aspekt betrifft die Erfindung eine Verwendung einer erfindungsgemäßen Lösung zur Beschichtung von partikulären Düngemitteln.In a further aspect, the invention relates to the use of a solution according to the invention for coating particulate fertilizers.

In einem weiteren Aspekt betrifft die Erfindung ein Verfahren zur Beschichtung eines partikulären Düngemittels, wobei ein unbeschichtetes partikuläres Düngemittel mit einer erfindungsgemäßen Lösung in einem Beschichter beschichtet wird. Bevorzugt wird dasIn a further aspect, the invention relates to a method for coating a particulate fertilizer, an uncoated particulate fertilizer being coated with a solution according to the invention in a coater. That is preferred

Verfahren in einem Wirbelschicht-Beschichter oder einem Trommel-Beschichter durchgeführt. Ein entsprechendes Verfahren ist dem Fachmann beispielsweise und insbesondere aus der DE 10 2017 217 498 A1. Das erfindungsgemäße Verfahren kann entsprechend der Offenbarung von Verfahrensschritten der DE 10 2017 217 498 A1 durch den Fachmann einfach ergänzt werden.Process carried out in a fluid bed coater or a drum coater. A corresponding method is known to the person skilled in the art, for example and in particular from DE 10 2017 217 498 A1. The method according to the invention can easily be supplemented by a person skilled in the art in accordance with the disclosure of method steps in DE 10 2017 217 498 A1.

Claims (18)

Patentansprüchepatent claims 1. Partikuläres Düngemittel, wobei das partikuläre Düngemittel eine Beschichtung aufweist, wobei die Beschichtung Polymilchsäuremasse enthält, dadurch gekennzeichnet, dass die Polymilchsäuremasse einen Anteil von 70 % bis 99% L-Milchsäure-Monomereinheiten und 1% bis 30% D-Milchsäure- Monomereinheiten aufweist.1. Particulate fertilizer, wherein the particulate fertilizer has a coating, the coating containing polylactic acid composition, characterized in that the polylactic acid composition has a proportion of 70% to 99% L-lactic acid monomer units and 1% to 30% D-lactic acid monomer units . 2. Partikuläres Düngemittel nach Anspruch 1, dadurch gekennzeichnet, dass die Polymilchsäuremasse einen Anteil von 95% bis 98% L-Milchsäure- Monomereinheiten und 2 % bis 5 % D-Milchsäure-Monomereinheiten aufweist.2. Particulate fertilizer according to claim 1, characterized in that the polylactic acid mass has a proportion of 95% to 98% L-lactic acid monomer units and 2% to 5% D-lactic acid monomer units. 3. Partikuläres Düngemittel nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Polymilchsäuremasse wenigstens eine erste Polymilchsäure aufweist, wobei die erste Polymilchsäure einen Anteil von 50 % bis 67 % L-Milchsäure-Monomereinheiten und 33 % bis 50 % D-Milchsäure- Monomereinheiten aufweist.3. Particulate fertilizer according to one of the preceding claims, characterized in that the polylactic acid mass has at least one first polylactic acid, the first polylactic acid having a proportion of 50% to 67% L-lactic acid monomer units and 33% to 50% D-lactic acid monomer units having. 4. Partikuläres Düngemittel nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass die Polymilchsäuremasse wenigstens eine zweite Polymilchsäure aufweist, wobei die zweite Polymilchsäure einen Anteil von 95 % bis 100 % L-Milchsäure-Monomereinheiten und 0% bis 5% D-Milchsäure- Monomereinheiten aufweist.4. Particulate fertilizer according to one of the preceding claims, characterized in that the polylactic acid mass has at least one second polylactic acid, the second polylactic acid having a proportion of 95% to 100% L-lactic acid monomer units and 0% to 5% D-lactic acid monomer units having. 5. Partikuläres Düngemittel nach Anspruch 3 und 4, dadurch gekennzeichnet, dass die Polymilchsäuremasse einen Anteil der ersten Polymilchsäure von 5 Gew.-% bis 50 Gew.-% und einen Anteil der zweiten Polymilchsäure von 50 Gew.-% bis 95 Gew.-% aufweist.5. Particulate fertilizer according to claims 3 and 4, characterized in that the polylactic acid composition has a proportion of the first polylactic acid of 5% by weight to 50% by weight and a proportion of the second polylactic acid of 50% by weight to 95% by weight. % having. 6. Partikuläres Düngemittel nach Anspruch 5, dadurch gekennzeichnet, dass die Polymilchsäuremasse einen Anteil der ersten Polymilchsäure von 7,5 Gew.-% bis 25 Gew.-% und einen Anteil der zweiten Polymilchsäure von 75 Gew.-% bis 92,5 Gew.-% aufweist.6. Particulate fertilizer according to claim 5, characterized in that the polylactic acid composition has a proportion of the first polylactic acid of 7.5% by weight to 25% by weight and a proportion of the second polylactic acid of 75% by weight to 92.5% by weight .-% having. 7. Partikuläres Düngemittel nach Anspruch 6, dadurch gekennzeichnet, dass die Polymilchsäuremasse einen Anteil der ersten Polymilchsäure von 10 Gew.-% bis7. Particulate fertilizer according to claim 6, characterized in that the polylactic acid composition has a proportion of the first polylactic acid of 10% by weight to 20 Gew.-% und einen Anteil der zweiten Polymilchsäure von 80 Gew.-% bis 90 Gew.-% aufweist.20% by weight and a proportion of the second polylactic acid of 80% by weight to 90% by weight. 8. Partikuläres Düngemittel nach einem der vorstehenden Ansprüche, dadurch gekennzeichnet, dass das partikuläre Düngemittel einen Kern aufweist, wobei der Kern zu wenigstens 80 Gew.-% aus Harnstoff besteht.8. Particulate fertilizer according to one of the preceding claims, characterized in that the particulate fertilizer has a core, wherein the core consists of at least 80% by weight of urea. 9. Verwendung von Polymilchsäuremasse zur Beschichtung von Düngemitteln, dadurch gekennzeichnet, dass die Polymilchsäuremasse einen Anteil von 70 % bis 99 % L-Milchsäure-Monomereinheiten und 1 % bis 30 % D-Milchsäure- Monomereinheiten aufweist.9. Use of polylactic acid compound for coating fertilizers, characterized in that the polylactic acid compound has a proportion of 70% to 99% L-lactic acid monomer units and 1% to 30% D-lactic acid monomer units. 10. Verwendung der Polymilchsäuremasse nach Anspruch 9, dadurch gekennzeichnet, dass die Polymilchsäuremasse wenigstens eine erste Polymilchsäure aufweist, wobei die erste Polymilchsäure einen Anteil von 50 % bis 67 % L-Milchsäure-Monomereinheiten und 33 % bis 50 % D-Milchsäure- Monomereinheiten aufweist, wobei die Polymilchsäuremasse wenigstens eine zweite Polymilchsäure aufweist, wobei die zweite Polymilchsäure einen Anteil von 95% bis 100 % L-Milchsäure-Monomereinheiten und 0% bis 5% D- Milchsäure-Monomereinheiten aufweist.10. Use of the polylactic acid composition according to claim 9, characterized in that the polylactic acid composition has at least one first polylactic acid, the first polylactic acid having a proportion of 50% to 67% L-lactic acid monomer units and 33% to 50% D-lactic acid monomer units wherein the polylactic acid composition comprises at least a second polylactic acid, the second polylactic acid having a proportion of 95% to 100% L-lactic acid monomer units and 0% to 5% D-lactic acid monomer units. 11.Verwendung der Polymilchsäuremasse nach Anspruch 10, dadurch gekennzeichnet, dass die Polymilchsäuremasse einen Anteil der ersten Polymilchsäure von 5 Gew.-% bis 50 Gew.-%, bevorzugt von 7,5 Gew.-% bis 25 Gew.-%, besonders bevorzugt von 10 Gew.-% bis 20 Gew.-%, und einen Anteil der zweiten Polymilchsäure von 50 Gew.-% bis 95 Gew.-%, bevorzugt von 75 Gew.-% bis 92,5 Gew.-%, besonders bevorzugt von 80 Gew.-% bis 90 Gew.- %, aufweist.11. Use of the polylactic acid composition according to claim 10, characterized in that the polylactic acid composition has a proportion of the first polylactic acid of 5% by weight to 50% by weight, preferably 7.5% by weight to 25% by weight, particularly preferably from 10% to 20% by weight, and a proportion of the second polylactic acid from 50% to 95% by weight, preferably from 75% to 92.5% by weight, particularly preferably from 80% to 90% by weight. 12.Lösung zur Beschichtung von partikulären Düngemitteln, wobei die Lösung als Lösemittel Aceton oder ein Lôsemittelgemisch mit wenigstens 90 Gew.-% Aceton aufweist, wobei in dem Lösemittel 1 Gew.-% bis 25 Gew.-% einer Polymilchsäuremasse gelôst sind, wobei die Polymilchsäuremasse einen Anteil von 70% bis 99% L-Milchsäure-Monomereinheiten und 1% bis 30% D- Milchsäure-Monomereinheiten aufweist.12. Solution for coating particulate fertilizers, wherein the solution has acetone or a solvent mixture with at least 90% by weight acetone as solvent, wherein 1% by weight to 25% by weight of a polylactic acid composition is dissolved in the solvent, wherein the Polylactic acid composition has a proportion of 70% to 99% L-lactic acid monomer units and 1% to 30% D-lactic acid monomer units. 13.Lösung nach Anspruch 12, dadurch gekennzeichnet, dass die Polymilchsäuremasse wenigstens eine erste Polymilchsäure aufweist, wobei die erste Polymilchsäure einen Anteil von 50% bis 67% L-Milchsäure- Monomereinheiten und 33% bis 50% D-Milchsäure-Monomereinheiten aufweist, wobei die Polymilchsäuremasse wenigstens eine zweite Polymilchsäure aufweist, wobei die zweite Polymilchsäure einen Anteil von 95 % bis 100 % L-Milchsäure-Monomereinheiten und 0% bis 5% D-Milchsäure- Monomereinheiten aufweist.13.Solution according to claim 12, characterized in that the polylactic acid composition comprises at least one first polylactic acid, the first polylactic acid having a proportion of 50% to 67% L-lactic acid monomer units and 33% to 50% D-lactic acid monomer units, wherein the polylactic acid composition has at least one second polylactic acid, the second polylactic acid having a proportion of 95% to 100% L-lactic acid monomer units and 0% to 5% D-lactic acid monomer units. 14.Lösung nach Anspruch 13, dadurch gekennzeichnet, dass die Polymilchsäuremasse einen Anteil der ersten Polymilchsäure von 5 Gew.-% bis 50 Gew.-%, bevorzugt von 7,5 Gew.-% bis 25 Gew.-%, besonders bevorzugt von 10 Gew.-% bis 20 Gew.-%, und einen Anteil der zweiten Polymilchsäure von 50 Gew.-% bis 95 Gew.-%, bevorzugt von 75 Gew.-% bis 92,5 Gew.-%, besonders bevorzugt von 80 Gew.-% bis 90 Gew.-%, aufweist.14.Solution according to claim 13, characterized in that the polylactic acid mass has a proportion of the first polylactic acid of 5% by weight to 50% by weight, preferably from 7.5% by weight to 25% by weight, particularly preferably from 10% by weight to 20% by weight, and a proportion of the second polylactic acid from 50% by weight to 95% by weight, preferably from 75% by weight to 92.5% by weight, particularly preferably from 80% to 90% by weight. 15. Lösung nach einem der Ansprüche 12 bis 14, dadurch gekennzeichnet, dass in dem Lösemittel 12 Gew.-% bis 18 Gew.-% einer Polymilchsäuremasse gelöst sind.15. Solution according to one of Claims 12 to 14, characterized in that 12% by weight to 18% by weight of a polylactic acid mass are dissolved in the solvent. 16. Verwendung einer Lösung nach einem der Ansprüche 12 bis 15 zur Beschichtung von partikulären Düngemitteln.16. Use of a solution according to any one of claims 12 to 15 for coating particulate fertilizers. 17.Verfahren zur Beschichtung eines partikulären Düngemittels, wobei ein unbeschichtetes partikuläres Düngemittel mit einer Lösung nach einer der Ansprüche 12 bis 15 in einem Beschichter beschichtet wird.17. A method for coating a particulate fertilizer, wherein an uncoated particulate fertilizer is coated with a solution according to any one of claims 12 to 15 in a coater. 18. Verfahren nach Anspruch 17, dadurch gekennzeichnet, dass das Verfahren in einem Wirbelschicht-Beschichter oder einem Trommel-Beschichter durchgeführt wird.18. The method according to claim 17, characterized in that the method is carried out in a fluidized bed coater or a drum coater.
BE20215705A 2021-09-10 2021-09-10 PLA coating of fertilizers BE1029746B1 (en)