AU750513B2 - Nylon compositions for golf ball constructions and method of making same - Google Patents

Description

AUSTRALIA

Patents Act COMPLETE SPECIFICATION

(ORIGINAL)

Class Int. Class Application Number: Lodged: Complete Specification Lodged: Accepted: Published: Priority Related Art: Name of Applicant: Spalding Sports Worldwide, Inc.

Actual Inventor(s): Michelle A Bellinger, Michael J Sullivan Address for Service: i PHILLIPS ORMONDE FITZPATRICK Patent and Trade Mark Attorneys 367 Collins Street Melbourne 3000 AUSTRALIA Invention Title: NYLON COMPOSITIONS FOR GOLF BALL CONSTRUCTIONS AND METHOD OF MAKING

SAME

Our Ref: 634695 POF Code: 346866/346866 The following statement is a full description of this invention, including the best method of performing it known to applicant(s): la NYLON COMPOSITIONS FOR GOLF BALL CONSTRUCTIONS AND METHOD OF MAKING SAME This application is a divisional application of Australian Patent Application 41882/97, the entire disclosure of which is incorporated herein by reference.

Field of the Invention The present invention relates to compositions suitable for golf ball constructions, and to golf balls which employ those compositions.

Background of the Invention The discussion of the background to the invention herein is included to explain the context of the invention. This is not to be taken as an admission that any of the material referred to was published, known or part of the common general knowledge in Australia as at the priority date of any of the claims.

W:\mary\MMHNODEL\Div41882-97.doc lb Modern golf balls typically employ ionomeric resins as cover materials. lonomeric resins, as a result of their toughness, durability, and wide range of hardness values have become materials of choice for golf ball covers over traditional rubbers. Ionomeric resins generally comprise an a-olefin and an a, (3 ethylenically unsaturated mono- or dicarboxylic acid neutralized with metal ions to the extent desired.

Olefins which have been employed to prepare ionomeric resins include ethylene, propylene, butene-l and the like. Unsaturated carboxylic acids which have been employed to prepare ionomeric resins include acrylic, methacrylic, ethacrylic, o-chloroacrylic, crotonic, maleic, fumaric, itaconic and the like. lonomeric resins include copolymers of ethylene with acrylic acid such as those sold by Exxon Corporation under the trademark "IOTEK", as well as copolymers of ethylene with methacrylic acid such as those sold by E.I. DuPont Nemours Company under the trademark "SURLYN". In some instances, a softening comonomer such as an acrylate ester has been included such that the ionomeric copolymer is an ionomeric terpolymer. Although various compositions have been employed to provide golf balls of varying playability characteristics, a need continues for compositions and covers which can be employed to provide golf balls which exhibit good playability and durability.

There are no commercially available golf balls which are generally known to contain nylon. Nylon alone would be too brittle for use in a golf ball cover. When efforts have been made in other fields to blend nylon with softer materials some degree of incompatibility often has *oooo W:\mary\MMHNODEL\Div41882-97.doc 2 resulted, rendering the blends susceptible to cracking and premature failure.

USP 4,690,981, the contents of which are incorporated herein by reference, shows soft terpolymer ionomers of ethylene/unsaturated carboxylic acid/softening comonomer which are useful in injection-molded items such as ski boots, ice skate shells, as coatings for fabrics, and as a replacement for balata in golf balls. The unsaturated carboxylic acid may be, for example, acrylic acid and methacrylic acid. The softening comonomer is, for example, an alkyl acrylate such as n-butyl acrylate. The '981 patent briefly mentions that the ionomers can be blended with other materials such as nylon, polypropylene, propylene-ethylene copolymers, linear polyethylene, and ethylene/unsaturated carboxylic acid copolymers. However, there is no indication that blends can be used for golf balls.

Summary of the Invention An object of the invention is to overcome or at least alleviate one or more of the difficulties present in the prior art.

An advantage of the invention is the provision of a highly durable golf ball.

Another advantage of the invention is the provision of a golf ball with a cover layer containing reduced quantities of ionomer.

A further advantage of the invention is the provision of a golf ball having a high coefficient of restitution.

Another advantage of the invention is the provision of a durable golf ball with a low spin rate.

25 Yet another advantage of the invention is the provision of a golf ball having a hard cover layer which is resistant to cracking.

Another advantage of the invention is the provision of a method of making a golf ball with a cover layer of the type described above.

Other advantages of the invention will be in part obvious and in part 30 pointed out more in detail hereinafter.

The invention in a preferred form is a golf ball having a cover layer with a S: resin composition comprising a combination of a polyamide component and an ionomeric component, the content of the polyamide component being at least 23 wt% of the resin composition, the golf ball W:\mary\MMHNODEL\Div41882.97.doc having a coefficient of restjtutiorn of at least 0.750. The polyamide component preferably includes at least one member selected from the group consisting of a polyamide homopolymer and a polyamide copolymer. In one preferred form of the invention, at least a portion of the polyamide component and at least a portion of the ionomeric component are part of the same copolymer. In another form of the invention, the polyamide component is present in a mixture with the ionomeric component. The combination preferably has 23 85 wt% polyamide component and at least 15 77 wt% ionomeric component.

In one particularly preferred form of the invention, the combination further includes an ester component. The ester component can be, for example, an olefin ester component. At least a portion of each of the polyamide component, ionomeric component and ester component preferably are part of the same copolymer. The composition of this embodiment optionally further comprises a carboxylic acid-containing copolymer which includes at least one member selected from the group consisting of ionomeric copolymers and non-ionomeric terpolymers and which is mixed with the copolymer of polyamide, ionomer and ester components.

In another particularly preferred form of the invention, the ionomeric component includes an acrylate ester. The polyamide component preferably is in a mixture with the ionomeric component.

In yet another embodiment of the invention, the combination of a polyamide component and ionomeric component is mixed with a nonpolyamide-containing copolymer.

Some examples of the invention include a graft copolymer or blend of a polyamide homopolymer with one or both of an ionomeric terpolymer and an ionomeric copolymer with two types of monomers.

SC Preferred polyamides for use according to the invention are polymers of caprolactam such as polyepsiloncaprolactam (nylon 6), polyhexamethyleneadipamide (nylon 66), and copolymers of nylon 6 and nylon 66. The ionomeric component of the invention preferably is a copolymer formed from an a-olefin having 2 to 8 carbon atoms and an acid which is selected from the group consisting of a, I-ethylenically unsaturated mono- or dicarboxylic acids and is neutralized with cations which include at least one member selected from the group consisting of zinc, lithium, sodium, manganese, calcium, chromium, nickel, aluminum, potassium, barium, tin, copper, and magnesium ions.

Preferred cations are zinc, sodium and lithium, and combinations thereof. In one preferred embodiment, the copolymer is further formed from an unsaturated monomer of the acrylate ester class having from 1 to 21 carbon atoms. The golf ball preferably has a Durability Rating of at least 2.

Another preferred form of the invention is a golf ball having a cover layer with a composition comprising a graft copolymer of at least one of a polyamide homopolymer and a polyamide copolymer and a first ionomeric copolymer which is formed from an a-olefin and a carboxylic acid. The golf ball has a Durability Rating of at least 2. The cover layer has a Shore D hardness of at least Yet another preferred form of the invention is a golf ball having a cover layer with a composition comprising a nylon backbone with ionomer grafted thereto, the golf ball having a coefficient of restitution of at least 0.750.

Another preferred form of the invention is a golf ball having a cover layer with a composition comprising a combination of a polyamide and a non-ionomeric acid copolymer which is formed from an a-olefin, an ester, and a carboxylic acid. The golf ball preferably has a Durability 'i Rating of at least 2.

A further preferred form of the invention is a golf ball having a cover layer comprising at least 10 wt% of a graft copolymer of polyepsiloncaprolactam and ionomer, the graft copolymer having a yield tensile strength of about 54 MPa (ASTM D-638), a flexural modulus of about 1585 MPa (ASTM D-790), and a drop weight impact at -400F of about 200 J (ASTM D-3029). In a particularly preferred form of the

S

S.

invention, the cover layer comprises at least 80 wt% of the graft copolymer.

Yet another preferred form of the invention is a method of making a golf ball. The method comprises steps of obtaining a golf ball core, and forming a cover layer over the core, the cover layer having a resin composition comprising a combination of a polyamide component and an ionomeric component, the content of the polyamide component being at least 23 wt% of the resin composition, the golf ball having a coefficient of restitution of at least 0.750.

The invention comprises the several steps in the relation of one or more such steps with respect to each of the others, and the article possessing the features, properties and the relation of elements exemplified in the following detailed disclosure.

Brief Description of the Drawings Fig. 1 schematically shows the durability test apparatus used to determine the durability of the golf balls of the invention.

Fig. 2 is a partial side view of a portion of an insert plate in the durability test apparatus which has grooves intended to simulate a golf club face.

Detailed Description of the Invention According to the present invention, there is provided a golf ball having a cover layer with a composition including a graft copolymer of at least one of a polyamide homopolymer and a polyamide copolymer and a first ionomeric copolymer which is formed from an a-olefin and a carboxylic acid, the cover layer having a Shore D hardness of at least 30, the golf ball having a Durability Rating of at least 2.

The present invention also provides a golf ball having a cover layer with a composition including a nylon backbone with ionomer, formed from an a-olefin and a carboxylic acid, grafted thereto, the golf ball having a coefficient of restitution of at least 0.750, the cover layer having a Shore D hardness of at least 30, the golf ball having a Durability Rating of at least 2.

The present invention further provides a golf ball having a cover layer with a composition including a combination of at least one of a polyamide homopolymer and a polyamide copolymer with an ionomeric acid copolymer formed from an a-olefin, an ester, and a carboxylic acid, the cover layer having W:\mary\MMHNODEL\Div41882- 9 7 .do c L ^ooye n oymd ooymrwt ninmrcai ooye Sld a Shore D hardness of at least 30, the golf ball having a Durability Rating of at least 2.

The present invention still further provides a golf ball having a cover layer with a resin composition including at least 10 wt% of a graft copolymer of polyepsiloncaprolactam and ionomer, formed from an a-olefin and a carboxylic acid, the graft copolymer having a yield tensile strength of about 54 MPa (ASTM D-638), a flexural modulus of about 1585 MPa (ASTM D-790), and a drop weight impact at -40'F of about 200 J (ASTM D-3029), the cover layer having a Shore D hardness of at least 30, the golf ball having a Durability Rating of at least 2.

Also disclosed herein is a golf ball having a cover layer with a resin composition including a combination of a polyamide component, an ester component and an ionomeric component, the content of the polyamide component being at least 23 wt% of the resin composition, the golf ball having a "15 coefficient of restitution of at least 0.750.

Further disclosed herein is a method of making a golf ball, including the steps of: obtaining a golf ball core, and forming a cover layer over the core, the cover layer having a resin 20 composition including a combination of a polyamide component, an ester component and an ionomeric component, the content of the polyamide component being at least 23 wt% of the resin composition, the golf ball having a coefficient of restitution of at least 0.750.

The present invention relates to golf balls which employ polyamide containing constructions, preferably as inner and/or outer cover compositions of golf balls having a core and one, two, or more cover layers formed thereon.

Some non-limiting examples of compositions according to the invention are as follows: the reaction product of a 3-part reactive mixture of polyamide, ionomeric copolymer, and ester, RP and at least one non-ionomeric terpolymer, RP with at least one ionomeric copolymer, W:\maryWMMHNODELkDiv41882-97.dOC a polyamide homppolymer and/or copolymer combined with at least one ionomeric copolymer, and a polyamide homopolymer and/or copolymer combined with at least one non-ionomeric carboxylic acid-containing terpolymer.

The low spin golf balls of the invention preferably have a coefficient of restitution of at least 0.780 and more preferably at least 0.800. The Shore D hardness of a hard nylon-containing cover layer generally is at least 65 (measured generally in accordance with ASTM D-2240, but measured on the curved surface of the ball). The PGA compression of the hard cover layer generally is 85 117, more preferably 90 105, and most preferably 90 97. The high spin, softer golf balls of the invention preferably have a COR of at least 0.775 and more preferably at least 0.790, a Shore D hardness of 30 60, and a PGA compression of 70 100, more preferably 75 95 and most preferably 75 85. Both hard and soft nylon-containing covers preferably have a melt index of 0.5 20 g/10 min., more preferably 8 g/10 min., and most preferably 1 4 g/10 mins.

An "ionomeric copolymer" as this term is used herein is a copolymer of an a-olefin and an a, (-ethylenically unsaturated mono- or 20 dicarboxylic acid with at least 3% of the carboxylic acid groups being neutralized with metal ions. The a-olefin preferably has 2 8 carbon atoms, the carboxylic acid preferably is acrylic acid, methacrylic acid, maleic acid, or the like and the metal ions include at least one cation selected from the group consisting of ions of zinc, magnesium, lithium, S 25 barium, potassium, calcium, manganese, nickel, chromium, tin, aluminum, sodium, copper, or the like. Preferably the cation is zinc, sodium or lithium or a combination thereof. The term "copolymer" includes copolymers having two types of monomers which are polymerized together, terpolymers (which are formed by the 30 polymerization of three types of monomers), and copolymers which are formed by the polymerization of more than three types of monomers.

7 A "polyamide component" as used herein is a polyamide homopolymer, a polyamide copolymer containing two or more types of amide units, e.g. nylon 6, 12, or a combination of both a polyamide homopolymer and a polyamide copolymer. The polyamide component preferably is a long chain polymer, not an oligomer, which typically is a short chain polymer of 2 10 units. An "ionomeric component" is a non-polyamide-containing ionomeric copolymer which is capable of being mixed or blended with the polyamide component, (b) the ionomeric portion of a polyamide-containing ionomeric copolymer, or a combination of both and If the polyamide component and ionomeric component are bonded to one another, the acid portion of the ionomeric component preferably is neutralized before the reaction of the polyamide and a ionomeric components, but most probably could also be neutralized after the reaction of the polyamide and ionomeric components.

:As used herein, the term "nylon backbone" refers to the polyamide portion of the polyamide/ionomer composition.

The details of interaction between a polyamide and an ionomeric copolymer are not fully understood. A polyamide and an ionomer could, for example, be intimately mixed without any bonding but with specific intermolecular interactions. Furthermore, it is possible, in combining a specific :i 20 quantity of polyamide with a specific quantity of ionomeric copolymer that portions of the overall quantities of the polyamide component and ionomeric component could be bonded to each other, as in a graft reaction, while other portions of the polyamide component and ionomeric component could form a blend which may have specific intermolecular interactions. Thus, this application is not intended to be limited by the degree of bonding versus intermolecular interaction of the polyamide component and ionomeric component unless specifically indicated.

In a first embodiment, golf balls of the invention employ, preferably as a '0 cover, a composition that is the reaction product of a reactive mixture-of polyamide, ionomeric copolymer, and an ester. The RP preferably is formed from a reactive mixture of at least one of W:\maryMMHNODELDiv41882-97.dOC polyepsiloncaprolactam (Nylon 6) and polyhexamethyleneadipamide (Nylon 66), zinc neutralized ethylene/methacrylic acid ionomer copolymer, and ethylene (meth)acrylate. As used herein, the term "(meth)acrylate" includes both acrylates and,methacrylates. The polyamide preferably is about 50 wt to about 90 wt of the reactive mixture, the ionic copolymer is about 5 50 wt of the reactive mixture, and the copolymer is about 1 20 wt of the reactive mixture. More preferably, the polyamide is about 60 72 wt of the reactive mixture, the ionic copolymer is about 26 34 wt of the reactive mixture, and the ester copolymer, preferably olefin ester copolymer, is about 2 6 wt of the reactive mixture.

Commercially available products which are the reaction products of reactive mixtures of polyamide, ionic copolymer, and olefin ester copolymer include CAPRON 8351, available from Allied Signal. This reactive mixture, and the processing thereof, is believed to be described in USP 4,404,325, the teachings of which are incorporated herein by reference in their entirety. As described therein, the preferred polyamide is polyepsiloncaprolactam or polyhexamethyleneadipamide, most preferably polyespiloncaprolactam. The preferred olefin ester 20 copolymer is ethylene/ethyl acrylate. The preferred ionic copolymer is a Zn neutralized copolymer of ethylene/methacrylic acid available from DuPont under the trade name SURLYN 9721 (1801). According to claim 7 of USP 4,404,325, the polyamide is present in the reactive mixture in an amount of about 60 72 wt the ionomeric copolymer 25 is present in an amount of about 26 wt to about 34 wt and the olefin ester copolymer is present in an amount of about 2 to about 6 wt based on the total weight of the reactive mixture. It is believed that CAPRON 8351 has a nylon backbone with ionomer grafted thereto.

Allied Signal states that CAPRON 8351 is a graft copolymer which has 30 the properties shown in Table 1 below.

9 Table 1 Property Test Method Value

(ASTM)

Specific Gravity D-792 1.07 Yield Tensile Strength, psi (MPa) D-638 7800 (54) Ultimate Elongation D-638 200 Flexural Strength, psi (MPa) D-790 9500 Flexural Modulus, psi (MPa) D-790 230,000 (1585) Notched Izod Imoact ft-lbs/in D-256 No break Drop weight Impact ft-lbs D-3029 150 (200) Drop weight Impact -40F, ft-lbs D-3029 150 (200) Heat Deflection temp. 264 psi, °C D-648 Melting Point, oC D-789 215 CAPRON 8351 is the most preferred RP for use in the invention.

Variations of CAPRON 8351 also may be used. For example, variations of CAPRON 8351 which may be used include those which employ polyepsiloncaprolactam or polyhexamethyleneadipamide with olefin 5 ester copolymers such as ethylene/methyl acrylate, ethylene/ethyl methacrylate, and ethylene/methyl methacrylate. Ionic copolymers which may be used in variations of CAPRON 8351 include ionic copolymers of an alpha olefin of the formula RCH CH 2 where R is H or alkyl radicals having 1-8 carbons, and an a, I1 ethylenically unsaturated 10 carboxylic acid having from 3-8 carbons. The ionic copolymer has at least about 10 wt of the COOH groups neutralized with metal cations, preferably Zn. Examples of these ionic copolymers include Zn neutralized ethylene/methacrylic acid. In variations of CAPRON 8351, the reactive mixture neutralized to produce such variations may include 15 about 50 wt to about 90 wt polyamide, about 5 wt to 50 wt ionic copolymer, and about 1 wt to 20 wt olefin ester copolymer, all percents based on the weight of the reactive mixture.

In another embodiment, golf balls of the invention employ preferably as a cover, a composition that includes RP and at least one terpolymer. Terpolymers which may be employed include olefin/alkyl (meth)acrylate/carboxylic acid terpolymers. These terpolymers typically have about 50 98 wt olefin, about 1 30 wt alkyl acrylate, and about 1 20 wt carboxylic acid. The olefin may be any of ethylene, propylene, butene-l, hexene-l and the like, preferably ethylene. The alkyl (meth)acrylate may be any of methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, butyl vinyl ether, methyl vinyl ether, and the like, preferably methyl acrylate. The carboxylic acid may be any one of acrylic acid, methacrylic acid, maleic acid, and fumaric acid.

Monoesters of diacids such as methyl hydrogen maleate, methyl hydrogen furmarate, ethyl hydrogen fumarate, and maleic anhydride which is considered to be a carboxylic acid may also be used.

Preferably, the carboxylic acid is acrylic acid. Useful ethylene/methyl acrylate/acrylic acid terpolymers may comprise about 98 50 wt preferably about 65 85 wt most preferably about 76 wt ethylene, about 1 30 wt preferably 15 20 wt most preferably 20 about 18 wt methyl acrylate, and about 1 20 wt preferably about 4 10 wt most preferably about 6 wt acrylic acid.

Olefin/alkyl (meth)acrylate/carboxylic acid terpolymers which are preferred for use in the compositions employed in the invention are ethylene/methyl acrylate/acrylic acid terpolymers such as those 25 marketed by Exxon Chemical Co. under the name ESCOR. Examples of these terpolymers include ESCOR ATX 320 and ESCOR ATX 325. The i properties of ESCOR ATX 320 and ESCOR ATX 325 as provided by Exxon are presented in Table 2.

11 Table 2 Property/Resin ESCOR

ESCOR

ATX-320 ATX-325 Melt Index' 5.0g/10 min 20.0g/10 min Density'1 0.950 glcc 0.950 glcc Melting Point' 69 C 670C Crystallization Temperature' 51 C 50 C Vicat Softening Temperature 200g 2 66 C 60 C Tensile Strength yield 3 1 2 MPa j 7.8 MPa Hardness 4 34 Elongation break 3 800% >800% Exxon Method 3 ASTM 638 2 ASTM D 1525 4 Shore D Other olefin/alkyl (meth)acrylate/carboxyic acid terpolymers which may be employed with RP in the compositions employed in the invention include but are not limited to: ethylene/n-butyl acrylate/acrylic acid, ethyl ene/n-butyl acrylatelmethacrylic acid, ethyl ene/2-ethoxyethyl acrylate/acrylic acid, ethylene/2-ethoxyethyl acylate/methacrylic acid, ethylene/n-pentyl acrylatelacrylic acid, ethylene/n-pentyl acrylate/meth acrylic acid, ethylene/n-octyl acrylate/acrylic acid, ethylene/2-ethyhexyl acrylate/acrylic acid, ethyl ene/n-pro pyl acrylate/acrylic acid, ethyl ene/n-pro pyl acrylate/methacrylic acid,.

ethylene/n-heptyl acrylate/acrylic acid, ethyl e ne/2-meth oxylethyl acrylate/acrylic acid, ethylene/3-methoxypropyl acrylate/acrylic acid, ethylene/3-ethoxypropyl acrylate/acrylic acid, and **to.

0 a.

0 0 0..

ethylene/acryjate/acylic acid.

Compositions which may be employed to provide golf balls according to this embodiment of the invention include about 1 to about 90 wt preferably about 1 to about 30 wt most preferably about wt RP and about 99 wt to about 10 wt terpolymer, preferably about 99 wt% to about 70 wt most preferably about wt terpolymer.

In another embodiment, golf balls of the invention employ, preferably as a cover, compositions which include RP and an olefin/alkyl acrylate/carboxylic acid terpolymer ionomer. Typically, the carboxylic acid groups of the terpolymer ionomer are partially approximately 80 percent) neutralized by metal ions such as Li, Na, Zn, Mn, Ni, Ba, Sn, Ca, Mg, Cu and the like, preferably Zn, Na or Li or a combination thereof, most preferably Zn or Li or a combination thereof. These terpolymer ionomers usually have a relatively high molecular weight, a melt index of about 0.1 to 1000 g/10 min., and/or a weight average molecular weight of 5000 up to one million. The ethylene/methyl acrylate/acrylic acid terpolymer ionomer may comprise about 50 98 wt preferably about 76 75. wt most preferably 20 about 76 wt ethylene, about 1 30 wt preferably about 15 wt most preferably about 18 wt methyl acrylate, and about 1 20 wt preferably about 4 10 wt most preferably about 6 wt acrylic acid. Useful terpolymer ionomers include, for example, ethylene/methyl acrylate/acrylic acid terpolymer ionomers sold by Exxon 25 Chemical Co. under the designation "IOTEK". Preferred terpolymer ionomers for use in the invention include Zn neutralized ethylene/methyl acrylate/acrylic acid terpolymer ionomers such as IOTEK 7520 and IOTEK 7510, and Li neutralized ionomers such as ESCOR ATX-320-Li- 30 ESCOR ATX 320 Li-80 is produced by utilizing a 6.0 wt acrylic acid/18.0 wt methyl acrylate/76 wt ethylene terpolymer produced by Exxon Chemical Co. under the designation ESCOR ATX 320. The 13 acid groups present in the trpolymer then are neutralized to 80 mol by Li using lithium hydroxymonohydrate. Neutralization is performed by adding lithium hydroxymonohydrate and ESCOR ATX 320 terpolymer to an intensive mixer (Banbury® type). The Li salt solubilizes in the ATX 320 terpolymer above the melting temperature of the terpolymer, and a vigorous reaction occurs with foaming as the Li cation reacts with the acid groups of the terpolymer, and volatile byproducts are evaporated. The reaction is continued until foaming ceases about 45 minutes at 250 350 F) and the batch is removed from the Banbury mixer. Mixing continues on a hot two-roll mill (175 F 250 F) to complete the neutralization reaction.

For the purpose of determining the weight percent of neutralization of the acrylic acid groups in the terpolymer ionomer after reacting with the Li salt, it is assumed that one mol of Li neutralizes one mol of acrylic acid. The calculations of neutralization are based upon an acrylic acid molecular weight of 72 g/mol, giving 0.067 mols of Li per 100 grams of the terpolymer.

Although ESCOR ATX 320 terpolymer can be 80 mol neutralized by Li, it is to be understood that other degrees of 20 neutralization with Li, ranging from about 3 mol to about 90 mol may be employed to provide useful ionomers. Thus, for example, ATX 320 that is 20 mol neutralized by Li, hereinafter referred to as ATX 320-Li-20 may be employed. In addition, various cation salts such as salts of Na, K, Mg, Mn, Ca and Ni may be employed in a manner similar to Li salts to provide various other ESCOR ATX 320 type terpolymer ionomers.

Other terpolymer ionomers which may be used in the 2* 'compositions employed in this embodiment of the invention include ethylene/alkyl ester/methacrylic acid terpolymer ionomers such as those 0 30 disclosed in USP 4,690,981, the teachings of which are incorporated by reference in its entirety herein, and which are available from DuPont Corp. under the trade name SURLYN. Properties of five SURLYN 14 terpolymer ionomers whichmay be used in the invention are set forth in Table 3. The terpolymer ionomer may be about 1 wt to about 99 wt preferably about 50 wt to about 99 wt most preferably about 85 wt all amounts based on the total weight of the RPterpolymer ionomer composition. RP may be about 1 wt to about 99 wt preferably about 1 wt to about 50 wt most preferably about 15 wt all amounts based on the total weight of the composition.

to to 8*0 4: 0* 00 0 6 5 0 a .04 0 of* 0 C C Table 3 ASTMV Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Surlyn Resin/ 7930 7940 80201 8528 8550 8660 8120' 8320' 90201 9320' 9520 9650 9720 9730 9910 9950 PropertyII I Cation Li Li Na Na Na Na Na Na Zn Zn Zn Zn Zn Zn Zn Zn Melt Flow D- 1.8 2.6 1 1.3 3.9 10 0.9 0.9 1.1 0.6 1.1 5 1 1.6 0.7 Index 1238 (g/1 Ominl Density 0-792 0.94 0.94 0.95 0.94 0.94 0.94 0.94 0.94 0.96 0.94 0.95 0.96 0.96 0.95 0.97 0.96 Notched D-256 NB' NB' NB' 11.4 16 NB 2 10.1 14.5 NB' NB' 6.8 NB' Izod Tensile 0- 140 220 630 550 795 345 235 213 610 570 460 600 590 485 485 Impact 1 822S (23C~ft- 49. 1 1 -I Q 1 Flexural Mod (23C)kpsi D-790 49.1 14 2.2 D-638 1I 2.8* 2.2 2.2 _II I 4 770 510 440 4~U Elongation 0 -638 120 285.

530 419 770 510 440 490 0, Hardness, D- 68 68 56 60 60 62 38 25 55 140 60 63 61 63 64 62 Shore D 2240 vicat 0- 62 63 61 73 78 71 51 48 57 454 74 71 71 73 62 66 Temp. 1525- Ra te 'Terpolymer ionomers N ra No Break 16 In another embodiment, golf balls of the invention employ, preferably as a cover, compositions of olefin/carboxylic acid copolymer ionomers made from two types of monomers and RP.

Olefin/carboxylic acid copolymer ionomers which may be employed with RP include those wherein the carboxylic acid groups of the copolymer ionomer are partially approximately 5 80 percent) neutralized by metal ions such as but not limited to Li, Na, Zn and Mg, preferably Zn, Na. Ionic copolymers may be zinc neutralized ethylene/methacrylic acid ionomer copolymer, Na neutralized ethylene/acrylic acid copolymer ionomers, and mixtures thereof. The Zn neutralized ethylene/acrylic acid copolymer ionomer can be the reaction product of Zn neutralization of an ethylene/acrylic acid copolymer having about 15 20 wt acrylic acid and a melt index of about 37 to about 100. These copolymer ionomers usually have a relatively high molecular weight, a melt index of about 0.1 to 1000 g/ 0 min., and/or a weight average molecular weight of 5000 up to one million. Useful copolymer ionomers include, for example, ethylene/acrylic acid copolymer ionomers sold by Exxon Chemical Co. under the designation "IOTEK" such as IOTEK 7030, IOTEK 7020, IOTEK 7010, IOTEK 8030, IOTEK 8020, and IOTEK 8000.

Non-limiting examples of preferred IOTEK copolymer ionomers for use in the invention include IOTEK 7010, IOTEK 7030 and IOTEK 8000. Properties of various IOTEK copolymer ionomers are shown in Tables 4 o° S ooo 0 @0 S 0 0 0 0 @00 000 0 0 00 S 0 00 S S. 0 000 0 5 00 S 0 0 0 @0 0 @00 0 0 00050 @0 0 @00 0 00 0 0 00 00 @00 @000 0 0 000 0 050 0 00 0 00 17 Table 4 Resin/Property ASTM IOTEK IOTEK IOTEK IOTEK IOTEK IOTEK IOTEK IOTEK IOTEK IOTEK IOTEK Method 4000 4010 7010 7020 7030 8000 8020 8030 7520 7510 3110 Cation Zn Zn Zn Zn Zn Na Na Na Zn Zn Na Melt Flow Index g/10 min D-1 238 2.5 1.5 0.8 11.5 2.5 0.8 1.6 2.8 2 0.8 1.3 Density k g/rn 3 D-792 964 966 968 966 964 957 0.956 956 962 970 939 Melting Point, C D-2240 85 84 83.5 84 85 83 84 87 67 67 Crystallization Point, C D-638 58 56 55 56 58 45 47 49 39 38 58 Vicat Softening Point, C D-638 60 60 60 160 60 54 54.5 55.5 40 40 Flexural Mod, MPa Tensile Impact at 23C, Kj/m 2 (Type S Dumbbell. 2mm Thick Compression Plaques) D-790 155 175 355 .4ou D__1822_ 480 j520j550 520 480 570 550 50 780 950 I 580 Plaque Properties (2mm thick compression molding) Tensile Strength at Break MPa Yield Point MPa Elongation at Break 1% Secant Modulus MVPa Shore D Hardness Terpolymer ionomer 18 Table Another embodiment, of the invention is golf balls which employ, preferably as a cover, compositions of nylon homopolymer and/or copolymer and one or more olefin/alkyl acrylate/carboxylic acid terpolymer ionomers. Terpolymer ionomers which may be used with the nylon homopolymers preferably are ethylene/methyl acrylate/acrylic acid terpolymer ionomers. Nylon homopolymers for use in any of the compositions employed in the invention include but are not limited to nylon 6, nylon 66, and mixtures or copolymers thereof. Other nylons such as nylon 11, nylon 12, nylon 612, nylon 66/6 and nylon 46 also can be used as long as sufficient durability is achieved. In the case of nylon 6, a polyamide chain of about 140 222 repeating units is typically useful, but lower and higher molecular weight material may be employed. CAPRON 8202, a nylon 6 type polymer available from Allied Signal, is preferred.

According to Allied Signal, CAPRON 8202 has the properties set forth in Table 6.

Table 6 Prope Test Method Value Property

(ASTM)

-792 1.13 Specific Gravity D-792 1.1 20 Yield Tensile Strength, psi (MPa) D-638 11500 Ultimate Elongation D-638 Flexural Strength, psi (MPa) D-790 15700 (110) Flexural Modulus, psi (MPa) D-790 410,000 (2825) Notched Izod Impact, ft-lbs/in D-256 1.0 I^ Tm-r^ (0 964 osi. oC D-648 Terpolymer ionomers which may be employed include but are not limited to those having 50 98 wt preferably about 76 wt most preferably about 76 wt ethylene, about 1 30 wt preferably about 15 20 wt most preferably about 18 wt methyl acrylate, about 1 20 wt preferably about 4 10 wt most preferably about 6 wt acrylic acid, wherein the acrylic acid has been neutralized by Zn, Li or Na or combinations thereof.

Preferred terpolymer ionomers include IOTEK 7520, IOTEK 7510, ESCOR ATX 320-Li-80, or a mixture thereof. The nylon homopolymer may be present in the compositions an amount of about I wt to about 99 wt preferably about 1 wt to 50 wt most preferably about 15 wt of the composition. The terpolymer ionomer may be about 99 wt to about 1 wt preferably about 1 wt to 50 wt most preferably about 85 wt all amounts based on total weight of the composition.

ZYTEL 408 is a nylon 66 modified molding compound containing ionomer. It is believed that ZYTEL 408 is an intimate mixture of polyamide and an ionomeric terpolymer of an a-olefin, an acrylate ester, and an a, /-ethylenically unsaturated mono- or dicarboxylic acid with a portion of the carboxylic acid groups being neutralized with metal ions. It is unknown to the present inventors whether ZYTEL 408 is a graft copolymer or a blend; however, ZYTEL 408 is believed to be a blend of nylon 66 and an ethylene alkylmethacrylate methacrylic acid terpolymer ionomer neutralized 25 with Zn. The properties of ZYTEL 408, as provided by DuPont, are shown in Table 7.

STable 7 Property Test Method Value 1

(ASTM)

Specific Gravity D-792 1.09 Tensile Strength (-40 0 F) D-638 15100 psi Tensile Strength (-400C) D-638 104.1 MPa Flexural Modulus (-40 0 F) D-790 410,000 psi Flexural Modulus (-400C) D-790 2827 MPa Izod Impact Strength at -400F D-256 1.3 ft.lb./in.

Izod Impact Strength at -400C D-256 69 J/m Gardner Impact at -30F D-3029 >320 ft.lbs.

Heat Deflection temp. 1.8-106 Pa D-648 750C Melting Point D-789 2550C 1 Dry as molded, with about 0.2% water A further embodiment of the invention is golf balls which employ, preferably as a cover, compositions of polyamide homopolymers or copolymers, and olefin/carboxylic acid copolymer ionomers made from two types of monomers such as IOTEK. The 5 polyamides which can be used in the compositions employed in the invention include but are not limited to nylon 6, nylon 66, nylon 11, nylon 12, nylon 612, nylon 66/6, nylon 46 and mixtures thereof, as long as sufficient durability is achieved. Preferably, the nylon polymer is any of nylon 6 and nylon 66, most preferably nylon 6.

In the case of nylon 6, a polyamide chain of about 140-222 repeating units is typically useful, but lower and higher molecular weight material may be employed. A preferred polyamide homopolymer is CAPRON 8202 available from Allied Signal. Useful copolymer ionomers include copolymer ionomers having about 99 wt to 70 wt preferably about 90 wt to 80 wt most preferably 85 wt ethylene, about 1 wt to about 30 wt preferably about 10 wt to about 20 wt most preferably 15 wt acrylic acid. A preferred ethylene/acrylic acid copolymer ionomer is IOTEK 7010 from Exxon Chemical Co. The copolymer ionomer may be present in the composition an amount of about 99 wt to about 1 wt preferably about 95 wt to about 70 wt most preferably about 80 wt of the composition. The polyamide homopolymer may be about 1 wt to about 99 wt preferably about 5 wt to about 30 wt most preferably about 20 wt wherein all amounts are based on the total weight of the composition.

Two or more copolymer ionomers may be preblended prior to blending with polyamide homopolymers and/or RP to provide compositions which may be used in the invention. Thus, preblends of hard and soft copolymer ionomers, as well as preblends of high carboxylic acid copolymer ionomers and low carboxylic acid copolymer ionomers may be utilized to provide compositions for use in the invention. An Example of such a preblend is a mixture of IOTEK 8000 and IOTEK 7010.

20 Another embodiment of the invention is golf balls which employ, preferably as a cover, compositions of polyamide homopolymers or copolymers, and olefin/alkyl acrylate/carboxylic acid terpolymers. Useful terpolymers include terpolymers having about 50 98 wt preferably about 76 75 wt most preferably 25 about 76 wt olefin, preferably ethylene, about 1 30 wt preferably about 15 20 wt most preferably about 18 wt alkyl acrylate, preferably methyl acrylate, and about 1 20 wt preferably about 4 10 wt most preferably about 6 wt carboxylic acid, preferably acrylic acid. The terpolymer may be present in the composition an amount of about 1 wt to about 99 wt preferably about 50 wt to about 99 wt most preferably about 85 wt of the composition. The polyamide homopolymer may be about 1 wt to about 99 wt preferably about 1 wt to about 50 wt most preferably about 15 wt wherein all amounts are based on the total weight of the composition. Useful polyamides may be of polyepsiloncaprolactam and polyhexamethyleneadipamide, more preferably nylon 6, nylon 66, nylon 11, nylon 12, nylon 612, nylon 66/6, nylon 46 and mixtures thereof. Preferably, the nylon polymer is any of nylon 6 and nylon 66, still more preferably nylon 6, most preferably the nylon homopolymer sold by Allied Signal under the trade name CAPRON 8202. A preferred ethylene/methyl acrylate/acrylic acid terpolymer is ESCOR ATX 320 from Exxon Chemical Co.

Two or more terpolymers may be preblended prior to blending with any of RP or the polyamide homopolymers to provide compositions which may be used in the invention. Thus, preblends of hard and soft terpolymers, as well as preblends of high carboxylic acid terpolymers and low carboxylic acid terpolymers may be utilized to provide compositions for use in the invention.

Although the compositions employed in the invention may be used in golf ball construction such as solid cores, one-piece balls 20 and covers, these compositions are preferably employed as covers.

Golf ball covers can be produced by injection molding or compression molding the nylon containing compositions employed herein over a wound or solid molded core, or a liquid core to produce a golf ball having a diameter of about 1.680 inches and weighing 25 about 1.620 ounces. The core itself may be of a uniform composition, or may have two or more layers. The standards for :both the diameter and weight for golf balls are established by the United States Golf Association Although the compositions employed in the invention can be used in solid core, two-piece and wound balls, solid and two-piece balls are preferred over wound balls due to their lower cost and superior performance.

The term "solid cores" as used herein refers not only to one piece cores but also to multi-layer cores.

Golf balls of the invention may be produced by forming covers which include compositions of the invention around cores by conventional molding processes. The cover material is mixed in a rigorous mixing procedure, preferably using a twin screw extruder or the like and an extrusion temperature of 200 250 0 C. The cover compositions may be injection molded directly around the core while the core is positioned in the center of a golf ball mold at temp of about 350F to about 450F. In compression molding, the cover composition is first injection molded at about 380F to about 450F to provide smooth surfaced hemispherical shells. The shells are then positioned around the core in a dimpled golf ball mold and compression molded at about 230-300F for about 2 minutes to about 10 minutes at a pressure sufficient to retain the mold in a closed position. Thereafter, the mold is cooled at about 50F to about 70F for about 2 minutes to about 10 minutes to fuse the shells together to form a unitary ball. After molding, the resulting golf balls may undergo various further processing steps such as 20 buffing, painting and marking.

~The present invention is further illustrated by the following non-limiting examples set forth below. In Tables 8 17 which °°ooo include data for the examples, the compositions are injection molded at 420 480 0 F (depending upon nylon content) around identical solid cores which have a finished diameter of 1.545" to produce golf balls about 1.680" in diameter having nominal cover thickness of 0.0675 inches. Each example represents the average data for one S.i dozen balls produced according to the invention. The properties for °oooo° the balls listed in the examples are measured according to the following procedures: The resilience or coefficient of restitution (COR) of a golf ball is the constant which is the ratio of the relative velocity of an elastic sphere after direct impact to that before impact. As a result, the COR can vary from 0 to 1, with 1 being equivalent to a perfectly or completely elastic collision and 0 being equivalent to a perfectly or completely inelastic collision.

COR, along with additional factors such as club head speed, club head mass, ball weight, ball size and density, spin rate, angle of trajectory and surface configuration dimple pattern and area of dimple coverage) as well as environmental conditions (e.g.

temperature, moisture, atmospheric pressure, wind, etc.) generally determine the distance a ball will travel when hit. Along thris line, the distance a golf ball will travel under controlled environmental conditions is a function of the speed and mass of the club and size, density and resilience (COR) of the ball and other factors. The initial velocity of the club, the mass of the club and the angle of the ball's departure are essentially provided by the golfer upon striking. Since club head, club head mass, the angle of trajectory and environmental conditions are not determinants controllable by golf ball producers and the ball size and weight are set by the these are not factors of concern among golf ball manufacturers. The factors or 20 determinants of interest with respect to improved distance are generally the coefficient of restitution (COR) and the surface configuration (dimple pattern, ratio of land area to dimple area, etc.) o of the ball.

The COR in solid core balls is a function of the composition of 25 the molded core and of the cover. The molded core and/or cover may be comprised of one or more layers such as in multi-layered balls. In balls containing a wound core balls comprising a liquid or solid center, elastic windings, and a cover), the coefficient of restitution is a function of not only the composition of the center and cover, but also the composition and tension of the elastomeric windings. As'in the solid core balls, the center and cover of a wound core ball may also consist of one or more layers.

The coefficient of restitution is the ratio of the outgoing velocity to the incoming velocity. In the examples of this application, the coefficient of restitution of a golf ball was measured by propelling a ball horizontally at a speed of 125+ 5 feet per second (fps) and corrected to 125 fps against a generally vertical, hard, flat steel plate and measuring the ball's incoming and outgoing velocity electronically. Speeds were measured with a pair of Oehler Mark 55 ballistic screens available from Oehler Research, Inc., P.O.

Box 9135, Austin, TX, which provide a timing pulse when an object passes through them. The screens were separated by 36" and are located 25.25" and 61.25" from the rebound wall. The ball speed was measured by timing the pulses from screen 1 to screen 2 on the way into the rebound wall (as the average speed of the ball over and then the exit speed was timed from screen 2 to screen 1 over the same distance. The rebound wall was tilted 2 degrees from a vertical plane to allow the ball to rebound slightly downward in order to miss the edge of the cannon that fired it. The rebound wall is solid steel 0.2 inches thick.

As indicated above, the incoming speed should be 125 20 fps but corrected to 125 fps. The correlation between COR and emese forward or incoming speed has been studied and a correction has been made over the 5 fps range so that the COR is reported as if the ball had an incoming speed of exactly 125.0 fps.

The coefficient of restitution must be carefully controlled in all 25 commercial golf balls if the ball is to be within the specifications regulated by the United States Golf Association As mentioned to some degree above, the U.S.G.A. standards indicate that a "regulation" ball cannot have an initial velocity exceeding 255 feet per second in an atmosphere of 75 0 F. when tested on a U.S.G.A. machine. Since the coefficient of restitution of a ball is related to the ball's initial velocity, it is highly desirable to produce a ball having sufficiently high coefficient of restitution to closely approach the U.S.G.A. limit.on initial velocity, while having an ample degree of softness hardness) to produce enhanced playability spin, etc.).

Cold cracking resistance is measured by firing a ball, having been previously stored at 10OF for 24 hours, at a velocity of 165 ft/sec from an air cannon against a steel plate positioned 12 feet from the muzzle of the cannon. The ball is fired 5 times against the plate. After allowing the ball to equilibrate to room temperature, the ball is visually inspected to identify cracks in the cover. One or more cracks, no matter how small, constitute failure.

The term "compression" utilized in the golf ball trade generally defines the overall deflection that a golf ball undergoes when subjected to a compressive load. For example, PGA compression indicates the amount of change in golf ball's shape upon striking.

The development of solid core technology in two-piece balls has allowed for much more precise control of compression in comparison to thread wound three-piece balls. This is because in the •"-manufacture of solid core balls, the amount of deflection or deformation is precisely controlled by the chemical formula used in making the cores. This differs from wound three-piece balls wherein •o compression is controlled in part by the winding process of the elastic thread. Thus, two-piece and multilayer solid core balls exhibit much more consistent compression readings than balls having wound cores such as the thread wound three-piece balls.

In the past, PGA compression related to a scale of from 0 to *200 given to a golf ball. The lower the PGA compression value, the softer the feel of the ball upon striking. In practice, tournament quality balls have compression ratings around 70 1 10, preferably around 80 to 100.

In determining PGA compression using the 0 200 scale, a standard force is applied to the external surface of the ball. A ball which exhibits no deflection (0.0 inches in deflection) is rated 200 28 and a ball which deflects 2' 10th of an inch (0.2 inches) is rated 0.

Every change of .001 of an inch in deflection represents a 1 point drop in compression. Consequently, a ball which deflects O. 1 inches (100 x .001 inches) has a PGA compression value of 100 200 100) and a ball which deflects 0. 110 inches (110 x .001 inches) has a PGA compression of 90 200 110).

In order to assist in the determination of compression, several devices have been employed by the industry. For example, PGA compression is determined by an apparatus fashioned in the form of a small press with an upper and lower anvil. The upper anvil is at rest against a 200-pound die spring, and the lower anvil is movable through 0.300 inches by means of a crank mechanism. In its open position the gap between the anvils is 1.780 inches allowing a clearance of 0.100 inches for insertion of the ball. As the lower anvil is raised by the crank, it compresses the ball against the upper anvil, such compression occurring during the last 0.200 inches of stroke of the lower anvil, the ball then loading the upper anvil which "in turn loads the spring. The equilibrium point of the upper anvil is o*°S* measured by a dial micrometer if the anvil is deflected by the ball 20 more than 0.100 inches (less deflection is simply regarded as zero compression) and the reading on the micrometer dial is referred to as the compression of the ball. In practice, tournament quality balls have compression ratings around 80 to 100 which means that the upper anvil was deflected a total of 0.120 to 0.100 inches.

25 An example to determine PGA compression can be shown by utilizing a golf ball compression tester produced by Atti Engineering Corporation of Newark, N.J. The value obtained by this tester relates to an arbitrary value expressed by a number which may range from 0 to 100, although a value of 200 can be measured as indicated by two revolutions of the dial indicator on the apparatus.

The value obtained defines the deflection that a golf ball undergoes when subjected to compressive loading. The Atti test apparatus consists of a lower movable'platform and an upper movable springloaded anvil. The dial indicator is mounted such that it measures the upward movement of the springloaded anvil. The golf ball to be tested is placed in the lower platform, which is then raised a fixed distance. The upper portion of the golf ball comes in contact with and exerts a pressure on the springloaded anvil. Depending upon the distance of the golf ball to be compressed, the upper anvil is forced upward against the spring.

Alternative devices have also been employed to determine compression. For example, Applicant also utilizes a modified Riehle Compression Machine originally produced by Riehle Bros. Testing Machine Company, Phil., PA to evaluate compression of the various components cores, mantle cover balls, finished balls, etc.) of the golf balls. The Riehle compression device determines deformation in thousandths of an inch under a fixed initialized load of 200 pounds. Using such a device, a Riehle compression of 61 corresponds to a deflection under load of 0.061 inches.

Additionally, an approximate relationship between Riehle compression and PGA compression exists for balls of the same size.

It has been determined by Applicant that Riehle compression corresponds to PGA compression by the general formula PGA compression 160 Riehle compression. Consequently, 80 Riehle compression corresponds to 80 PGA compression, 70 Riehle compression corresponds to 90 PGA compression, and 60 Riehle 25 compression corresponds to 100 PGA compression. For reporting purposes, Applicant's compression values are usually measured as Riehle compression and converted to PGA compression.

Furthermore, additional compression devices may also be utilized to monitor golf ball compression so long as the correlation to PGA compression is know. These devices have been designed, such as a Whitney Tester, to correlate or correspond to PGA compression through a set relationship or formula.

Durability is determined by.firing a golf ball at 135 ft/sec (at 72°F) into 5-sided steel pentagonal container, the walls of which are steel plates. The container 10, which is shown schematically in Fig.

1, has a 19 1/2 inch long insert plate 12 mounted therein, the central portion 14 of which has horizontally extending square grooves on it which are intended to simulate a square grooved face of a golf club. The grooves, which are shown in an exaggerated form in Fig. 2, have a width 30 of 0.033 inches, a depth 32 of 0. 100 inches, and are spaced apart from one another by land areas 34 having a width of 0.130 inches. The five walls 16 of the pentagonal container each have a length of 14 1/2 inches. The inlet wall is vertical and the insert plate is mounted such that it inclines upward 600 relative to a horizontal plane away from opening 20 in container 10. The ball travels 15 1/2 15 3/4 inches horizontally from its point of entry into the container 10 until it hits the squaregrooved central portion- 14 of insert plate 12. The angle between the line of trajectory of the ball and the insertplate 12 is 300. The balls are subjected to 70 or more blows (firings) and are inspected at regular intervals for breakage any signs of cover cracking or 20 delamination). If a microcrack forms in a ball, its speed will change and the operator is alerted. The operator then visually inspects the ball. If the microcrack cannot yet be observed, the ball is returned to the test until a crack can be visually detected.

A ball is assigned a Durability Rating according to the following scale. A sample of twelve balls of the same type are obtained and are tested using the durability test apparatus described in the previous paragraph. If less than all of the balls in the sample survive 70 blows each without cracking, the ball is assigned a Durability Rating of 1. If all of the balls survive 70 blows and one or two of the twelve balls crack before 100 blows, the ball is assigned a Durability Rating of 2. If all twelve balls in the sample survive 100 blows each, but seven or more balls crack at less than 31 200 blows each, the ball is-assigned a Durability Rating of 3. If all twelve balls in the sample survive 100 blows and at least six out of the twelve balls in the sample also survive 200 blows, the ball is assigned a Durability Rating of 4.

The spin rate of the golf ball is measured by striking the ball with a 9-iron wherein the club-head speed is about 105 feet per second and the ball is launched at an angle of 26 to 34 degrees with an initial velocity of about 110-115 feet per second. The spin is measured by observing the rotation of the ball in flight using stop action strobe photography.

"Shore D hardness" of a cover is measured generally in accordance with ASTM D-2240, except the measurements are made on the curved surface of a molded cover, rather than on a plaque.

Furthermore, the Shore D hardness of the cover is measured while the cover remains over the core. When a hardness measurement is made on a dimpled cover, Shore D hardness is measured at a land area of the dimpled cover.

EXAMPLES 1-28: Use of Nylon-Containing lonomers in Golf Ball Covers 20 By blending the ingredients set forth in Tables 8 10 and 13, cover compositions were produced and injection molded around a core to yield a two piece ball,as described above. The balls were then evaluated. The results are shown below: Examples 1-3: 25 Examples 1-3 in Table 8 illustrate golf balls formed from compositions which include RP (CAPRON 8351) with ethylene/methyl acrylate/acrylic acid terpolymers (ESCOR ATX 325), and compositions formed from RP (CAPRON 8351) with Zn neutralized ethylene/methyl acrylate/acrylic acid terpolymer ionomers (IOTEK 7520, and IOTEK 7510). The cover material was blended in a single screw extruder. Cold cracking of Examples 1 and 2 may have been a result of molding problems.

Table 8 Example/component (grams) 1 2 3 IOTEK 7520 1500 IOTEK 7510 1500 CAPRON 8351 1500 1500 1500 ESCOR ATX 325 1500 Cold Crack Resistance 2 cracks 2 cracks at 2 blows at 3 blows 4 cracks at 3 cracks at 3 blows 5 blows Durability 300 hits No Failures No Failures Examples 4-9: Examples 4-9 in Table 9 show compositions of nylon homopolymers (CAPRON 8202) with ethylene/acrylic acid copolymer ionomers (IOTEK 7010 and IOTEK 8000), blends of ethylene/acrylic acid ionomers (IOTEK 7010 and IOTEK 8000), compositions of nylon homopolymers (CAPRON 8202) with terpolymers (ESCOR ATX 320) and terpolymer ionomers such as (ESCOR ATX-320-Li-80), and of nylon homopolymers (CAPRON 8202) and terpolymers (ESCOR ATX o oo 320) are shown. Blends A, B, C and D were each pre-extruded in a single screw extruder and were molded over cores having the same formulation, a Riehle compression in the range of 61 69 and I a COR in the range of 0.766 0.778. Example 5 was a control in which no nylon was used. Examples 4 and 6 9 show that Nylon 6 can be blended with ionomeric copolymers to make a durable golf ball if sufficient mixing occurs. It was surprising that the inclusion of 10% nylon (Example 4) produced a cover that had nearly the same durability as Control Lxample 5. In Example 6, a preextrusion of zinc ionomer (IOTEK 7010) with nylon, followed by dry blending with sodium ionomer unexpectedly resulted in better durability than the balls of Example 4 although the covers of Examples 4 and 6 had the same overall composition. While the covers of Examples 7 and 8 were expected to break as a result of incompatibility, it was instead found that terpolymer and terpolymer ionomer were compatible with nylon, and no cracking occurred in the 300-blow durability test.

o 9*99 9 6 C. S S 0

S

C

0O@ See

C

0 5 0 S C 0 5

C

S *S C S C S S S Ge.

:9 POP se 34 Table 9 Example/Component (grams) 4 5 (control) 6 7 8 9 Blend A' Blend B 2 2000. Blend C 3 2000---- Blend D 4 650 1000 OTEK 8000 1500 1350--..

IOTEK 7010 500---- Compression (Reihiel 59 60 59 74 75 Coefficient of Restitution 0.804 0.805 0.806 0.783 0.767 0.798 Durab ility 100 blows 12 12 12 12 12 12 200 blows 12 12 12 12 12 12 300 blows 7 8 9 12 125 Sample taken from mixture of 2025g IOTEK 8000, 675g IOTEK 7010, and 300g CAPRON 8202.

2 Sample taken from mixture of 2700g ESCOR ATX 320 and 300g CAPRON 8202..

3Sample taken from mixture of 1350g ESCOR ATX 320. 1350g ESCOR ATX 320-Li-8O. and 300g CAPRON 8202.

4Sample taken from mixture of 1350g IOTEK 7010 and 600g CAPRON 8202.

'Number of balls out of 12 which survived 100 blows. 200 blows and 300 blows Examples 10-14: Examples 10-14 in Table 10 illustrate compositions which employ one or more copolymer ionomers (IOTEK, SURLYN) with ZYTEL. These compositions were prepared and molded into golf balls according to the procedures above. The materials were blended using a single screw extruder. Example 11 produced the "best" ball of this set of Examples due to its high COR.

Table Example/ 10 11 12 13 14 Component IOTEK 4000 35 wt 42.5 wt IOTEK 8000 35 wt 42.5 wt SURLYN 9910 85 wt SURLYN 9320 75 wt 50 wt ZYTEL 408 30 wt 15 wt 15 wt 25 wt 50 wt COR 0.784 0.812 0.803 0.784 0.782 Compression 53 54 56 65 61 (Reihle) Hardness 70 70 67 50 62 Shore D 00 0e S @00 0 00 00 S

OSSO

00 0

S

0 Example Example 15 illustrates use of RP in the form of CAPRON 8351 as the cover of a golf ball. The core had a Riehle compression in the range of 85 95 and a COR in the range of 0.772 0.789 and was 5 the same type of core as was used in Examples 16 44. The performance of this ball is shown in Table 13. The resulting ball had low spin and high hardness, which would make it useful for a high handicap player.

5*

SS

S

36 Examples 16-20: RP (CAPRON 8351) was admixed with blend BX1 that included a Na neutralized ethylene/acrylic acid copolymer ionomer, a first Zn neutralized ethylene/acrylic acid copolymer ionomer, and a component mixture (masterbatch). The component mixture included a second Zn neutralized ethylene/acrylic acid copolymer ionomer. The second Zn neutralized ethylene/acrylic acid ionomer was different from the first Zn neutralized ethylene/acrylic acid copolymer ionomer.

More specifically, in examples 16 20, CAPRON 8351 was blended with blend BX1. In blend BX1, the first Na neutralized ethylene/acrylic acid copolymer ionomer was IOTEK 8000 in an amount of 70 wt of blend BX1. The first Zn neutralized ethylene/acrylic acid copolymer ionomer was IOTEK 7010 in an amount of 20 wt of blend BX1. The component mixture formed wt of blend BX1. The component mixture contained IOTEK 7030 as the second Zn neutralized ethylene/acrylic acid copolymer ionomer in an amount of 75 wt of the component mixture. The component mixture also included 24 wt of UV stabilizer, 0.26 wt 20 brightener, 0.46 wt dye and 0.04 wt antioxidant. Blend BX1 was produced by dry blending the Na and Zn copolymer ionomers with the component mixture. The component mixture employed in the blend BX1 was produced by melt extruding the ingredients of the component mixture at a temperature of about 380F. Mixing of RP and blend BX1 took place using a twin screw extruder designed for intensive mixing. The RP was melt mixed with blend BX1 at a temperature of about 450F. The resulting compositions then were molded into covers and balls as described above. The performance of balls according to examples 16 20 is shown in Table 13.

Stated more generally, when CAPRON 8351 and blend BX1 are used to form a golf ball cover, CAPRON 8351 is about 1 to 99 wt preferably about 20 wt to about 80 wt more preferably about 20 wt of the composition, and blend BX1 is about 1 to 99 wt preferably about 20 to about 80 wt of the composition, more preferably about 80 wt of the composition. In blend BX1, the first Zn neutralized ethylene/acrylic acid copolymer ionomer is about 1 to about 90 wt preferably about 20 wt of blend BX1, the Na neutralized ethylene/acrylic acid copolymer ionomer is about 1 to about 90 wt preferably about 70 wt of blend BX1, and the component mixture is about 1 to about 30 wt preferably about 10 wt of blend BX1. Preferably, the second Zn neutraeized ethylene/acrylic acid copolymer ionomer in the component mixture is about 75 wt of the component mixture, with the remainder being additives such as stabilizers for oxidative degradation, stabilizers for thermal degradation, stabilizers for ultraviolet light degradation, inhibitors for oxidative degradation, inhibitors for thermal degradation, inhibitors for ultraviolet light degradation, lubricants, plasticizers, dyes, pigments, fibrous fillers, particulate fillers, and reinforcement nucleating agents. In this embodiment, a variety of Na ionomers including but not limited to those listed 20 in Table 4, preferably IOTEK 8000 may be employed. The first Zn copolymer ionomer may be, for example, any of those listed in Table 4, preferably IOTEK 7010. The second Zn copolymer ionomer may be, for example, any of those listed in Table 4, preferably IOTEK 7030. The aforesaid component mixture preferably includes about 75 wt IOTEK 7030, remainder additives.

As shown by the results in Table 13, the addition of nylon increased the hardness and COR of the balls, increased distance slightly, and reduced spin. It is important to note that the mixture of CAPRON 8351 with ionomer resulted in a highly durable product except in Example 17, in which the balls broke early. The poor results of Example 17 may have been caused by inadequate molding.

Examples 21-24: RP (CAPRON 8351) and blend BX2 that includes a Na neutralized ethylene/acrylic acid copolymer ionomer, a Zn neutralized ethylene/acrylic acid copolymer ionomer, and the above described component mixture were employed in a golf ball as a golf ball cover.

Mixing of RP and blend BX2 took place using a twin screw extruder designed for intensive mixing.

In examples 21-24, the first Zn neutralized ethylene/acrylic acid copolymer ionomer was EX1003 in an amount of 45% of blend BX2, the Na neutralized ethylene/acrylic acid copolymer ionomer was EX1002 in an amount of 45 wt of blend BX2, and the component mixture was 10 wt of blend BX2. The second Zn neutralized ethylene/acrylic acid copolymer ionomer in the component mixture was IOTEK 7030 in an amount of 75 wt of the component mixture. The component mixture also included 24 wt UV stabilizer, 0.26 wt brightener, 0.46 wt dye and 0.04 wt antioxidant. The performance of balls with these covers is shown in examples 21-24 of Table 13.

Stated more generally, in this embodiment, CAPRON 8351 is 20 about 1 to about 99 wt preferably about 20 80 wt more preferably about 20 wt of the composition, and blend BX2 is about 1 to about 99 wt preferably about 20 80 wt more preferably about 80 wt of the composition. In blend BX2, the Na neutralized ethylene/acrylic acid copolymer ionomer is about 1 to about 90 wt preferably about 45 wt of blend BX2, the Zn neutralized ethylene/acrylic acid copolymer ionomer is about 1 to about 90 wt preferably about 45 wt of blend BX2, and the component mixture is about 1 to 30 wt preferably about 10 wt of blend BX2. In this embodiment, the preferred Na neutralized ionomer is EX1002 and the preferred Zn ionomer is EX1003.

EX1002 and EX1003 are provided by Exxon Chemical Co. and the properties of EX1002 and EX1003 are shown in Table 11 below.

39 Table 11 Resin/Property ASTM EX 1002 EX 1003 Method Na Zn Cation Melt Index (g/10 min) D-1235 1.6 1.1 Melting Point D-3417 83.7 82 Crystallization Point D-3417 43.2 51.5 Plaque Properties (2mm thick compression molding) Tensile Strength at D-638 31.7 24.8 Break MPa Yield Point MPa D-638 22.5 14.9 Elongation at Break D-638 348 387 1% Secant Modulus MPa D-638 418 145 1% Flexural Modulus MPa D-790 380 147 Shore D Hardness D-2240 62 54 Vicat Softening Point D-1525 51.5 56 EX1002 is made by neutralizing an ethylene/acrylic acid copolymer having about 18 wt acrylic acid and a melt index of about 28 with Na to achieve a Na neutralized ethylene/acrylic acid copolymer ionomer that has a melt index of about 1. EX1003 is made by 5 neutralizing an ethylene/acrylic acid copolymer having about 18 wt acrylic acid having a melt index of about 28 with Zn to yield a Zn neutralized ethylene/acrylic acid ionomer having a melt index of about 1. Blend BX2 is made in the manner employed to make blend ":BX1. CAPRON 8351 and blend BX2 then are blended together. The 10 resultant compositions then are formed into golf ball covers and golf balls as described above.

As was the case in Examples 16 20, Examples 21 24 also show that the addition of nylon increases the hardness and COR of o oo the golf balls, and increases distance slightly while reducing spin.

Examples 25-28: RP (CAPRON 8351) with blend BX3 that included a Na neutralized ethylene/acrylic acid copolymer ionomer, a Zn neutralized ethylene/acrylic acid copolymer ionomer, and the above described component mixture were employed in a golf ball as a golf ball cover.

Mixing of RP with blend BX3 was conducted using a twin screw extruder designed for intensive mixing. In examples 25 28, the first neutralized ethylene/acrylic acid copolymer ionomer was EX 990 in an amount of 45 wt of blend BX3, the Na neutralized ethylene/acrylic acid copolymer ionomer was EX 989 in an amount of 45 wt of blend BX3, and the component mixture was 10 wt of blend BX3. The second Zn neutralized ethylene/acrylic acid copolymer ionomer in the component mixture was IOTEK 7030 in an amount of 75 wt of the component mixture. The component mixture also included 24 wt UV stabilizer, 0.26 wt brightener, 0.46 wt dye and 0.04 wt antioxidant. The properties of EX 989 and EX 990, as provided by Exxon, are shown in Table 12. The performance of balls with covers of these compositions is shown in examples 25-28 of Table 13.

20 Stated more generally, in this embodiment, CAPRON 8351 is about 1 to about 99 wt preferably about 20 80 wt more preferably about 20 wt of the composition, and blend BX3 is about 1 to about 99 wt preferably about 20 80 wt more preferably about 80 wt of the composition. In blend BX3, the Na neutralized ethylene/acrylic acid copolymer ionomer is about 1 to about 90 wt preferably about 45 wt of blend BX3, the first Zn 00..0' neutralized ethylene/acrylic acid copolymer ionomer is about 1 to wt preferably about 45 wt of blend BX3, and the component mixture is about 1 to 30 wt preferably about 10 wt of blend BX3. In this embodiment, the preferred Na ionomer is EX 989. The preferred Zn copolymer ionomer is EX 990. EX 989 is made by neutralizing an ethylene/acrylic acid copolymer that has about 18 wt 41 acrylic acid and a melt index of about 100 with Na. EX 990 is made by neutralizing an ethylene/acrylic acid copolymer that has about 18 wt acrylic acid and a melt index of about 100 with Zn.

EX 989 and EX 990 are available from Exxon Chemical Co.

As indicated by the results on Table 13, CAPRON 8351 produces a golf ball with excellent durability, as well as a very high coefficient of restitution and good distance, when used in combination with BX3.

Examples 20, 21 and 25 were controls. In each set of Examples 16 20, 21 24 and 25 28, intermolecular interactions are believed to have caused, or at least contributed to, the reduction in melt index for the blends as compared to the pure materials.

Durability of the covers containing 20 wt% CAPRON 8351 is better than durability of covers containing 40 wt% CAPRON 8351.

However, the 40 wt% CAPRON 8351 covers met the durability standard for commercial golf balls and resulted in a harder cover.

*o* Table 12 Resin/Property EX 989 EX 990 Melt Index (g/10 min) 1.3 1.24 Cation type Na Zn Density (kg/m 3 959 977 Vicat Softening Temp. 52/5 55.0 Crystallization Temp. 40.1 54.4 Melting Point 92.6 81.0 Tensile at Yield (MPa) 23.8 16.5 Tensile at Break (MPa) 32.3 23.8 Elongation at Break 330 357 1% Secant Modulus (MPa) 389 205 Flexural Modulus (MPa) 340 183 Hardness (Shore D) 62 56 Zwick Rebound 61 48

S

S

8 8 8 8 88 8 8 8 8 8*8 88 8 88 8 8 8* *8 Table MOLD MI 2

SIZE

3

WT

4

COMP

5

COR

6

HARD

7

SPIN

8 DIST DUR 9 100'° 20011 30012 EX BX3 BX2 BX1 C8351 TEMP 1 blows blows blows 0 100 465 5.51 1.679 45.92 56 808 77 5514 251.3" 258 12 10 9 16 20 80 465 3.13 1.677 45.57 60 801 75 5984 248.1" 155 9 2 0 17 40 60 460 0.43 1.68 45.52 65 B 1 3 73 6891 235.0" 18 60 40 450 0.9 1.68 45.41 71 803 72 248.8"* 197 12 6 0 19 80 20 430 3.23 1.68 45.27 73 806 69 7777 249.6"** 278 12 12 4 100 0 430 9.49 1.68 45.13 75 807 67 8375 248.1" 335 12 12 8 21 100 0 430 17.5 1.679 45.22 68 821 72 7028 264.7. 171 12 0 0 22 80 20 430 7.5 1.68 45.3 66 818 73 6988 263.8* 239 12 5 23 60 40 450 1.45 1.681 45.6 65 815 74 6434 262.8* 139 9 1 0 24 40 60 460 0.62 1.678 45.56 61 781 75 6300 264.2' 3 100 0 430 15.8 1.68 45.26 68 819 72 6707 266.0* 157 12 1 0 26 80 20 430 8.08 1.68 45.32 67 819 73 6842 265.0' 253 12 7 4 27 60 40 430 2.8 1.679 45.38 66 816 75 6257 266.1 172 11 2 0 28 40 60 460 1.39 1.681 45.73 62 813 77 6013 261.7 55 1 0 0 •j l I Iirmntar n "Winht in arams SDegrees I- IvIel IIuevx--y/ lin Riehle Compression 6 Coefficient of Restitution 7 Hardness--Shore

D

8 revs. per min.

.4 4r~f~ 9 Durability--Average No. of hits to failure Number or balls out Ot iz wnicn surviveu ,u uuvo Number of balls out of 12 which survived 200 blows 12 Number of balls out of 12 which survived 300 blows 13 Bro Yards total distance after impact with Top Flight Tour metal wood having 10.5 Deg. loft at 157.96 ft/sec onto firm turf Yards total distance after impact with Top.Flight Tour metal wood having 12 Deg. loft at 163.3 ft/sec onto soft turf ke Examples 29-44: Use of Blends of Copolymer lonomer and Nylon in Golf Ball Covers Examples 29-34: CAPRON 8202 with the aforementioned blend BX1 was employed as a cover in a golf ball. The CAPRON 8202 and blend BX1 were mixed using a twin screw extruder designed for intensive mixing.

In examples 29 34, the Na neutralized ethylene/acrylic acid copolymer ionomer was IOTEK 8000 in an amount of 70 wt of blend BX1, the first Zn neutralized ethylene/acrylic acid copolymer ionomer was IOTEK 7010 in an amount of 20 wt of blend BX1, and the component mixture is 10 wt of blend BX1. The second Zn neutralized ethylene/acrylic acid copolymer ionomer in the component mixture was IOTEK 7030 in an amount of 75 wt of the component mixture. The component mixture also included 24 wt of UV stabilizer, 0.26 wt brightener, 0.46 wt dye and 0.04 wt antioxidant. The performance of balls which employ those covers is shown as examples 29 34 in Table 14 below.

Stated more generally, in this embodiment, CAPRON 8202 is 20 about 1 to about 50 wt preferably about 20 50 wt more preferably about 20 wt of the composition, and blend BX1 is about 50 to 99 wt preferably about 50 80 wt more preferably about 80 wt of the composition as long as a Durability Rating of at least 2 is obtained. The compositions are formed into 25 golf ball covers and golf balls as described above.

e i 8 Table 14 MOLD MI 2

SIZE

3

WT

4

COMP

5

COR

6

HARD

7

SPIN

8 DIST DUR 9 10010 20011 30012 EX BX3 BX2 BX1 C8202 TEMP' blows blows blows 29 0 100 465 14.38 1.68 46.3 43 B1 3 80 7412 20 80 465 15.9 1.68 46.02 50 B 13 78 13 31 40 60 460 5.32 1.68 45.76 57 B 3 75 13 32 60 40 450 1.73 1.68 45.54 67 808 72 7056 251.6** 69 1 0 0 33 80 20 430 5.68 1.68 45.4 71 809 70 7845 250.9* 178 12 2 0 34 100 0 430 9.49 1.68 45.13 75 807 67 8375 248.1"* 335 12 12 8 100 0 430 17.5 1.68 45.22 68 821 72 7028 264.7* 171 12 0 0: 36 80 20 430 6.23 1.68 45.44 66 821 73 6375 265.5* 103 11 0 0 37 60 40 450 2.21 1.68 45.33 63 821 75 5826 265.8* 93 9 0 0.

38 40 60 460 7.49 1.68 45.96 54 B1 3 80 4708 13 39 0 100 465 14.38 1.68 46.3 43 B 13 80 7412 13 100 0 430 15.8 1.68 45.26 68 819 72 6707 266* 157 12 1 0 41 80 20 430 6.88 1.79 45.39 66 821 74 6607 266.5* 186 12 3 1 42 60 40 450 3.86 1.68 45.67 62 824 77 5656 267.1* 150 12 1 0 43 40 60 460 7.49 1.683 45.92 53 B 1 3 80 B' 3 13 13 463 4.B1.0.4 44 0 100 465 14.38 1.68 46.3 43 B' z 80 7412 Degrees F Melt Index--g/lOmin Diameter in inches Weight in grams Riehle Compression 6 Coefficient of Restitution 7 Hardness--Shore D 8 RPM 9 Durability--Average No. of hits to failure 10 Number of balls out of 12 which survived 100 blows "Number of balls out of 12 which survived 200 blows 12 Number of balls out of 12 which survived 300 blows 13 Broke Yards total distance after impact with Top Flight Tour metal wood having 10.5 Deg.loft at 157.96 ft/sec onto firm turf Yards total distance after impact with Top Flight Tour metal wood having 12 Deg. loft at 163.3 ft/sec onto soft turf 46 Examples 35-39: CAPRON 8202 with the aforementioned blend BX2 was employed as a cover in a golf ball. The CAPRON 8202 and blend BX2 were mixed using a twin screw extruder designed for intensive mixing.

In Examples 35-39, the Na neutralized ethylene/acrylic acid copolymer ionomer was EX 1002 in an amount of 45 wt of blend BX2, the first Zn neutralized ethylene/acrylic acid copolymer ionomer was EX 1003 in an amount of 45 wt of blend BX2, and the component mixture was 10 wt of blend BX2. The second Zn neutralized ethylene/acrylic acid copolymer ionomer in the component mixture was IOTEK 7030 in an amount of 75 wt of the component mixture. The component mixture also included 24 wt UV stabilizer, 0.26 wt brightener, 0.46 wt dye and 0.04 wt antioxidant. The performance of balls with those covers is shown in Examples 35-39 of Table 14 above.

Stated more generally, in this embodiment, CAPRON 8202 is about 1 to about 50 wt preferably about 20 50 wt more preferably about 20 wt of the composition, and blend BX2 is 20 about 50 to about 99 wt preferably about 50 80 wt more preferably about 80 wt of the composition as long as a minimal Durability Rating of 2 is obtained. The compositions are formed into golf ball covers and golf balls as described above.

Examples 40-44: 25 CAPRON 8202 with blend BX3 was employed as a golf ball cover of a golf ball. The CAPRON 8202 and blend BX3 were mixed using a twin screw extruder designed for intensive mixing. In Examples 40 44, the first Zn neutralized ethylene/acrylic acid copolymer ionomer was EX 990 in an amount of 45 wt of blend BX3, the Na neutralized ethylene/acrylic acid copolymer ionomer was EX 989 in an amount of 45 wt of blend BX3, and the 47 component mixture was 10 wt of blend BX3. The second Zn neutralized ethylene/acrylic acid copolymer ionomer in the component mixture was IOTEK 7030 in an amount of 75 wt of the component mixture. The component mixture also included 24 wt UV stabilizer, 0.26 wt brightener, 0.46 wt dye and 0.04 wt antioxidant. The performance of balls with those covers is shown in Examples 40 44 of Table 14 above.

Stated more generally, in this embodiment, CAPRON 8202 is about 1 to about 50 wt. preferably about 20 50 wt. more preferably about 20 wt. of the composition, and blend BX3 is about 50 to about 99 wt. preferably about 50 80 wt. more preferably 80 wt. of the composition as long as a minimal Durability Rating of 2 is obtained. The compositions are formed into golf ball covers and golf balls as described above.

Examples 45 59: Use of Blends of Terpolymer lonomer and Nylon in Golf Ball Covers CAPRON 8351 was blended in different amounts with four 20 different ionomeric or non-ionomeric terpolymers, namely SURLYN 9320, IOTEK 7520, ATX 320-Li-40 and DS3076 (Chevron Chemical DS3076 is an extrusion grade sodium ionomer resin with a melt index of 0.5 g/10 min (ASTM D-1238) and a flexural modulus of 34,400 psi (ASTM D-790-66). Blending took place in a twin 25 screw extruder designed for intensive mixing. The weight percentages of CAPRON 8351 and the terpolymer materials are shown on Table 15 below. The blend was employed as a cover of a golf ball. The covers were placed over cores having the same formulation, Riehle compression in the range of 82 92, and COR in the range of 0.785 0.805. The physical properties and 1. 48 performance of the resulting balls is shown on Table 15. The inclusion of nylon increased cover hardness and reduced ball spin.

On Table 15, scuff resistance measurements were determined as follows: A Top-Elite tour pitching wedge (1994) with box grooves was obtained and was mounted in a Miyamae driving machine. The club face was oriented for a square hit. The forward/backward tee position was adjusted so that the tee was four inches behind the point in the downswing where the club was vertical. The height of the tee and the toe-heel position of the club relative to the tee were adjusted in order that the center of the impact mark was about 3/4 of an inch above the sole and was centered toeto heel across the face. The machine was operated at a club head speed of 125 feet per second. A minimum of three samples of each ball were tested.

Each ball was hit three times.

After testing, the balls were rated according to the following table: Rating Type of damage 1 Little or no damage (groove markings or dents) 2 Small cuts and/or ripples in cover .3 Moderate amount of material lifted from ball surface but still attached "to ball 4 Material removed or barely attached 25 The balls that were tested were primed and top coated.

The addition of nylon caused a slight reduction in scuff resistance in Examples 45 48 and 49 52. However, Examples and 49 51 were found to have a scuff resistance that was better than a number of commercially available "soft" golf balls, which typically have a scuff resistance of about 1.0. The "best balls" in 49 this set of Examples were those of Examples 50 51 because they had a soft feel low Shore D and relatively high spin) in conjunction with good scuff resistance.

.o *C C 9 C

C

CS 0 I C C C C C *i.

C CC...

C C~ C C C .1 C CC C C SC ii C C C C C C C C C C *C Table MOD MI SIZE WT COMP CR HARD' SPIN DIST DIST CC' SCUFF' DUR6 EX 9320 7520 ATX DS3076 C8351 TEMP

D

2

P~

100 0 3.7 1.6790 45.35 80 781 71 10550 248 173 NF 0.5 NF 46 90 10 2.3 1.6790 45.55 81 781 74 10299 247 175 NF 1.5 NP 47 80 20 1.4 1.680 45.58 79 782 75 10086 248 175 NF 3.0 NIF 48 70 30 0.6 1.6790 45.68 78 782 80 9549 248 177 NF 2.0 N] 49 100 0 6.7 1.680 45.52 80 781 69 10622 242 172 NF 0.5 NF 90 10 5.1 1.681 45.63 80 781 70 10578 247 173 NF 1.0 NF 51 80 20 3.6 1.681 45.67 80 779 74 10468 248 174 NF 1.0 NIF 52 70 30 2.6 1.681 45.77 78 780 80 10245 248 175 107' 1.5 NF 53 100 0 3.1 1.679 45.37 80 782 74 10405 245 176 1e3 7 1.5 NIF 54 90 10 1.5 1.679 45.44 79 783 76 10318 247 177 NF 3.0 NIF 80 20 1.2 1.680 45.60 79 783 80 10147 250 176 NP 4.0 NP 56 70 30 0.8 1.6.80 45.65 78 783 84 9559 249 178 NF 4.5 NF 57 100 0 58 90 10 59 80 20 'Shore C hardness 2 yards. with driver 3yards, with 9-iron 4cold crack scuff resistance eNF 12/12 balls survived 20 blows in COR machine at 150 160 ft/sec.

7one break at third blow (most possibly due to molding) 51 Examples 45, 49, 53 and 57 were controls. As indicated by the results on Table 15, the golf balls of Examples 46 48, 50 51 and 54 56 possessed good cold crack resistance. Example 52 was believed to fail because of poor/inadequate molding. The formations of Examples 57 59 could not be molded due to difficulties during the extrusion process.

Examples 60 68: Use of Blends of Lithium lonomer and Nylon in Golf Ball Covers CAPRON 8202 and CAPRON 8351 were blended with various ionomers. In some of the Examples, all of the CAPRON and ionomers were pre-dried and co-extruded. In other Examples, the CAPRON was predried and preextruded with one ionomer and subsequently dry blended with another ionomer. A single screw extruder was used. The results are shown on Table 16.

As indicated by the results on Table 16, blends of nylon with lithium ionomers resulted in good durability. Example 63 shows a golf ball with particularly high durability. Core type A had a Riehle compression in the range of 68 76 and a COR in the range of 20 0.795 0.805. Core type B had a Riehle compression in the range "of 54 62 and a COR in the range of 0.789 0.797.

*f ft 'ft ft 52 Table 16 Pre-dried and Co-extruded Dry Blended- COMP COR CORE 100'S 2002 3003 OUR 4 EX 996 Li 996 Na 7010 BX1 8351 8202 7010 996 Li TYPE blows blows blows 50 33.3 16.7 59 826 A 12 7 3 257 61 50 16.7 33.3 58 826 A 12 10 3 273 62 33.3 16.7 50 59 826 A 12 11 5 261 63 50 33.3 16.7 59 824 A 12 12 8 300 64 100 60 822 A 12 12 11 300 50 33.3 16.7 49 810 B 12 11 10 300 66 100 50 806 B 12 12 11 300 67 50 16.7 33.3 157 825 A 12 8 6 258 68 E 50 33.3 16.7 59 824 A 12 1 3 24 Number of balls out of 12 which survived 100 blows 2 Number of balls out of 12 which survived 200 blows 3Number of balls out of 12 which survived 300 blows 4Durability average number of hits to failure Examples 69 96: Use of Small Quantities of Nylon in lonomeric Golf Ball Covers A number of blends were made using up to 30 wt% CAPRON 8351 or 10 wt% CAPRON 8202. The cores were of the same formulation as those of Examples 15 28. A twin screw extruder was used for blending. The results are shown on Table 17.

As shown on Table 17, all of the samples exhibited good durability and had good COR.

**too: .0 0 r .0 0 0 0 0 0 000 000 0 0 00 0 0 00 0 00 0 000 0 0 00 00.0 0 0 0 0 000 0 0 00000 00 0 000 0 00 0 0 *0 *0 0 000 0000 0 0 0 000 0 000 0 00 0 00 Table 17 part 1 lonomer Resin is a drybiend of 8000/7010 75/25 Ex. lonomer 8351 8202 COMP COR Shore D Cold Crack 100' blows 2002 blows 3003 blows MI 69 100 0 68 800 70 nb .12 12 7 5.3 90 10 66 801 71 nb 12 12 4 3.1 71 80 20 66 .801 72 nb 12 12 1 2.4 72 70 30 65 800 72 nb 1.2 8 0 7 3 90 10 65 802 73 nb 12 12 2 3.1 lonomer resin Ir COMP is a dryblend of 8000/7010 50/50 Shore D Cold Crack 66 803 71 nb 803 72 nb 64 803 74 nb 801 74 nb 66 803 73 nb lonomer resin is a dryblend of 1006/1007 50/50 Ex. lonomer 8351 8202 COMP COR Shore D Cold Crack 1001 blows 2002 blows 3003 blows Mt 79 100 0 68 802 71 nb 12 12 4 6.7 90 10 67 800 71 nb 12 12 3 5.2 81 80 20 66 801 73 nb 12 12 4 82 70 30 65 798 74 nb 12 11 1 2 83 90 10 67 802 75 nb 12 12 7 5.2 lonomer Resin is a dryblend of 1002/1003 50/50 Ex. lonomer 8351 8202 Reihle COR Shore D Cold Crack 1001 blows 2002 blows 3003 blows MI 84 100 0 65 805 71 nb 12 12 2 11.2 90 10 65 805 72 nb 12 11 3 7.4 86 80 20 64 804 73 nb 12_ 10 0 4.6 87 70 30 67 810 75 1 @5th blow 12 4 0 2.8 88 90 10 66 815 75 nb 12 12 0 lonomner resin is a dryblend of AD8195/AD8444 50/50 lonomer resin is a dryblend of AD8195/AD8181 50/50 Ex. lonomer 8351 Reihle C OR Shore D Cold Crack 100' blows 2002 blows 300' blows MI 93 100 0 66 815 73 nb 12 12 0 6.3 94 490 10 67 817 74 nb 12 9 0 4.3 80 20 66 814 74 nb 12 7 0 4.3 96 70 30 64 812 75 nb 12 4 0 2.3 Numnrot oais OU 01 I~WIUL A uvI~ AA,~ IOTEK 8000 IOTEK 7010 IOTEK 1006 IOTEK 1007 15%AA Na 15%AA Zn 15%AA Na 15%AA Zn Precursor 37MI Precursor 37Ml Precursor 20MI Precursor 20MI IOTEK 1002 18%AA Na Precursor 28MI IOTEK 1003 18%AA Zn Precursor 28MI AD 8195 Zn AD 8444 Na AD 8181 Li 2Number of balls out of 12 which survived 2Number of balls out of 12 which survived 00 blows 56 Examples 97 143: Tensile Data for lonomers and Nylon-lonomer Blends Tensile data was collected for a number of blends of ionomer and nylon. The results are shown on Table 18. The addition of nylon generally increased tensile modulus and energy to break.

e* *e 57 Tensile Data Table 18 Ex. lonomer Nylon Nylon Break Stress Strain Energy to Break Yield Stress Strain Modulus' Type PSI Break In-Lb PSI Yield PSI 97 8000/7010 (75/25) 0 3666 211.3 58.8 3203 20.7 26825 98 8351 10 3834 224.3 65.9 3314 21.4 27723 99 8351 20 3985 217.8 67 3483 22.1 28777 100 8351 30 4158 220 70.8 3659 24.9 30363 101 8202 10 3751 211.8 62 3412 21.6 27254 102 8000/7010 (50/50) 0 3496 232.5 62 3151 20.1 25930 103 8351 10 3635 241.6 67.3 3196 20.1 26196 104 8351 20 3869 265.1 76 3193 20.2 26920 105 8351 30 4075 257.5 77.8 3355 21.8 26928 106 8202 10 3684 248.2 69.1 3179 20.9 25584 107 1006/1007 (50/50) 0 3551 239.6 66.1 3162 19.9 26335 108 8351 10 3677 252.8 71.4 3125 20.4 26070 109 8351 20 3995 254.5 76.2 3320 20.7 27938 110 8351 30 4056 246.1 75.7 3389 22 29071 111 8202 10 3556 234.8 65.7 3207 19.8 27561 112 1002/1003(50/50) 0 3759 251.8 72.5 3586 18.1 30593 113 8351 10 4007 276.4 81.5 3530 18.4 30491 114 8351 20 4107 277.4 84 3551 18.8 30589 115 8351 30 4305 277.3 87.7 3683 18.1 30671 *5* 58 Table 1 8 part 2 Ex. lonomer Nylon Nylon Break Stress Strain Energy to Break Yield Stress Strain Modulus' Psi Break ln-Lb PSI Yield PSI 116 1002/1003 150150) 8202 10 4481 317.2 99.8 3675 17.8 32585 117 8351 100 8927 478.8 255.1 5085 25.8 56670 118 8351 100 8312 500.4 247.2 4785 27.5 42281 119 BX1 8351 40 5323 293 106.2 3606 20.6 30198 120 8X1 8351 20 4584 265 81.8 3293 19.5 28032 121 BX1 0 3907 216.9 62.8 3305 21.6 26094 122 8202 100 8434 422.4 248 7064 19.8 63744 123 BX1 8202 80 9223 518.9 288.8 5973 17.8 58195 124 BX1 8202 60 7920 484 238.3 5510 18.9 58424 125 8X1 8202 40 6072 397.6 158.5 4771 18.1 45577 126 BX1 8202 20 4538 281.4 96.4 4090 20.7 35404 127 BXI 0 3907 216.9 62.8 3305 21.6 26094 128 BX2 0 3489 217.2 61.8 3603 19.2 29755 129 BX2 8351 20 3732 245.8 71.3 3540 19.5 29814 130 OX2 8351 40 5465 352.6 125.2 3834 20.7 32862 131 BX2 8351 60 7449 459.7 212 4408 34.4 37181 132 BX2 0 3489 217.2 61.8 3603 19.2 29755 133 8X2 8202 20 4760 314.6 111.7 4462 18.3 37510 134 j X2 8202 40 68 2. 7. 911. a. a a a .a a a a a a a. a a a. a.

.a a a a *a 59 Ex. lonomer Nylon Nylon Break Stress Strain Energy to Break Yield Stress Strain Modulus' #Type Psi Break In-Lb PSI at Yield PSI 135 BX2 8202 60 7202 456.6 214.4 5288 21.3 49705 136 BX3 0 3647 184.2 55.3 3866 19.5 31580 137 8X3 8351 20 4010 231.7 72.2 3864 19.6 32011 138 BX3 8351 40 5342 327.2 118.2 4058 22.5 32499 139 BX3 8351 60 7266 454.5 211.2 4695 27.8 43427 140 BX3 0 3647 1 84.2 55.3 3866 19.5 31580 141 BX3 8202 20 4820 323.8 105.5 3768 18.2 32422 142 BX3 8202 40 6341 448.2 177.2 4236 17.4 40094 1L_43 8X3 8202 -L 60 7910 1 486.9 232.7. 5154. 20.1 50535 In any of the compositions employed in the invention, additional materials may be added to these compositions employed to provide desired properties. These materials include, for example, dyes such as Ultramarine sold by Witaker, Clark and Daniels of South Plainfield, NJ, titanium dioxide, UV absorbers and stabilizers. The compositions also may include softening agents such as plasticizers and reinforcing materials such as glass fibers and inorganic fillers. Antioxidants also may be included in the compositions of the invention, conventionally in amounts of about 1% by weight. Useful antioxidants include 4,4'-di (1,1,3,3-tetramethylbutyl) diphenylamine sold under the trade designation "Octamine Antioxidant" by Naugatuck Division of US Rubber. Also useful is the hydroperoxide decomposer antidegradant tetrakis 2 4 -ditertbutylphenyl)-4,4'-biphenylenediphosphonite sold under the trade designation "Sandostab P-EPQ" by Sandoz Colors Chemicals Co.

The compositions employed in the invention may be prepared by any conventional procedure that provides a substantially uniform admixture of the components. Preferably drying and melt blending procedures and equipment are used. For example, in preparation of compositions which employ nylon materials such as RP with one or more terpolymers and/or terpolymer ionomers, the terpolymer and/or terpolymer ionomer can be dry mixed with RP, typically at room temperature, and the resulting mixture melt blended in any conventional type blending equipment heated to about 200-250 0 C. The nylon material and the copolymer, terpolymer, terpolymer ionomer, and/or copolymer ionomer preferably are dried (either individually or together) *o before melt blending. Drying is done in desiccated air at a temperature and for a time suitable to reduce the moisture content to a point which it will not have any adverse effect on the subsequent use of the compositions or the properties of the resulting product. If additives such as those identified above have not previously been added to either the nylon material, the copolymer or copolymer ionomer during 61 processing of those individual components, before they are admixed with each other, the additives may be added during melt blending of those components. The uniform admixture resulting from the melt blending procedure then may be commuted by chopping, pelletizing or grinding into granules, pellets, chips, flakes or powders suitable for subsequent use, e.g. injection molding to provide a golf ball.

The invention has been described with reference to the preferred embodiments. Modification and alterations will occur to others upon reading and understanding the preceding detailed description. It is intended that the invention be construed as including allsuch alterations and modifications insofar as they come within the scope of the claims and the equivalents thereof.

gO o.eo oeoo.

Claims (12)

1. A golf ball having a cover layer with a composition including a graft copolymer of at least one of a polyamide homopolymer and a polyamide copolymer and a first ionomeric copolymer which is formed from an ca-olefin and a carboxylic acid, the cover layer having a Shore D hardness of at least the golf ball having a Durability Rating of at least 2.

2. A golf ball according to claim 1, wherein the cover layer further includes a second ionomeric copolymer which is blended with the graft copolymer.

3. A golf ball according to claim 1 or 2, wherein the cover layer has a Shore D hardness of 30 15 4. A golf ball according to claim 1 or 2, wherein the cover layer has a Shore .D hardness of at least A golf ball according to any one of claims 1 to 4, wherein the polyamide homopolymer includes at least one member selected from the group consisting 20 of polyepsiloncaprolactam and polyhexamethyleneadipamide.

6. A golf ball having a cover layer with a composition including a nylon backbone with ionomer, formed from an a-olefin and a carboxylic acid, grafted thereto, the golf ball having a coefficient of restitution of at least 0.750, the cover layer having a Shore D hardness of at least 30, the golf ball having a Durability Rating of at least 2.

7. A golf ball according to claim 6, wherein the cover layer has a Shore D hardness of 30

8. A golf ball according to claim 6, wherein the cover layer has a Shore D hardness of at least 63

9. A golf ball having a cover layer with a composition including a combination of at least one of a polyamide homopolymer and a polyamide copolymer with an ionomeric acid copolymer formed from an a-olefin, an ester, and a carboxylic acid, the cover layer having a Shore D hardness of at least 30, the golf ball having a Durability Rating of at least 2. A golf ball according to claim 9, wherein the cover layer has a Shore D hardness of 30-60.

11. A golf ball according to claim 9 or 10, wherein the polyamide homopolymer includes at least one member selected from the group consisting of polyepsiloncaprolactam and polyhexamethyleneadipamide.

12. A golf ball having a cover layer with a resin composition including at least 15 wt% of a graft copolymer of polyepsiloncaprolactam and ionomer, formed from an a-olefin and a carboxylic acid, the graft copolymer having a yield tensile strength of about 54 MPa (ASTM D-638), a flexural modulus of about 1585 MPa (ASTM D- 790), and a drop weight impact at -40"F of about 200 J (ASTM D-3029), the cover layer having a Shore D hardness of at least 30, the golf ball having a Durability Rating of at least 2.

13. A golf ball according to claim 12, wherein the resin composition includes an ionomeric terpolymer blended with the graft copolymer. 25 14. A golf ball according to claim 12 or 13, wherein the resin composition includes at least 80 wt% of the graft copolymer. A golf ball according to claim 1, substantially as herein described with reference to any one of the examples.

16. A golf ball according to claim 6, substantially as herein described with reference to any one of the examples. p S 17. A golf ball according to claim 9, substantially as herein described with 3ib 3 reference to any one of the examples. W:VmaryMMHNODEL\Div41882-97.doc 64

18. A golf ball according to claim 12, substantially as herein described with reference to any one of the examples. DATED: 22 April 2002 PHILLIPS ORMONDE FITZPATRICK Patent Attorneys for: SPALDING SPORTS WORLDWIDE, INC. W:mnry.MMHN0DELDv418B2.97.doC