AU733427B2 - Golf ball with ionomeric cover and method of making same - Google Patents

Description

1 0

AUSTRALIA

Patents Act COMPLETE SPECIFICATION

(ORIGINAL)

Class Int. Class Application Number: Lodged: Complete Specification Lodged: Accepted: Published: Priority Related Art: .0 0 0 0 o o 6 o eo .:00 0.0.

0 0 0 Name of Applicant: Spalding Sports Worldwide, Inc.

Actual Inventor(s): MICHAEL J SULLIVAN Address for Service: PHILLIPS ORMONDE FITZPATRICK Patent and Trade Mark Attorneys 367 Collins Street Melbourne 3000 AUSTRALIA Invention Title: GOLF BALL WITH IONOMERIC COVER AND METHOD OF MAKING SAME Our Ref 622299 POF Code: 346866/346866 The following statement is a full description of this invention, including the best method of performing it known to applicant(s): -1ft SI la GOLF BALL WITH IONOMERIC COVER AND METHOD OF MAKING SAME The present application is a divisional application from Australian patent application number 722705 (formerly 10148/97).

Background of the Invention The present invention relates to golf balls having ionomeric covers, and more particularly to golf balls having covers formed from acrylate ester-containing ionic copolymers.

lonomeric resins are polymers containing interchain ionic bonding.

As a result of their toughness, durability, and flight characteristics, various ionomeric resins sold by E.I. DuPont deNemours Company under the trademark "Surlyn®" and by the Exxon Corporation (see U.S.

Pat. No. 4,911,451) under the trademark "Escore" and the tradename o 15 "lotek", have become the materials of choice for the construction of *15 golf ball covers over the traditional "balata" (trans polyisoprene, natural or synthetic) rubbers. The softer balata covers, although exhibiting enhanced playability properties, lack the durability necessary for repetitive play.

Ionomeric resins are ionic copolymers of an olefin such as ethylene and a metal salt of an unsaturated carboxylic acid, such as acrylic acid, methacrylic acid, or maleic acid. Metal ions, such as sodium or zinc, are used to neutralize some portion of the acidic groups in the copolymer resulting in a thermoplastic elastomer exhibiting enhanced properties, i.e. improved durability, etc., for golf ball cover 25 construction over balata. However, the advantages gained in increased durability have been offset to some degree by the decreases produced in playability. This is because the durable ionomeric resins tend to be very hard when utilized for golf ball cover construction, and thus lack the degree of softness required to impart the spin necessary to control the ball in flight.

-As a result, while there are currently more than fifty commercial grades of ionomers available from DuPont and Exxon with a wide range W:tatryMMHNODELO148.97.DOC of properties which vary according to the type and amount of metal cations, molecular weight, composition of the base resin relative content of ethylene and methacrylic and/or acrylic acid groups) and additive ingredients such as reinforcements, etc., a great deal of research continues in order to develop golf ball cover compositions exhibiting not only the improved impact resistance and carrying distance properties produced by the "hard" ionomeric resins, but also the playability "spin") characteristics previously associated with the "soft" balata covers, properties which are still desired by the more skilled golfer.

In various attempts to produce a durable, high spin ionomeric golf ball, the golfing industry has blended the hard ionomeric resins with a number of softer ionomeric resins. U.S. Patents Nos. 4,884,814 and 5,120,791 are directed to cover compositions containing blends of hard and soft ionomeric resins. The hard copolymers typically are made from an olefin and an unsaturated carboxylic acid.

The soft copolymers are generally made from an olefin, an unsaturated carboxylic 15 acid, and an acrylate ester. It has been found that golf balls covers formed from S: hard-soft ionomer blends tend to become scuffed more readily than covers made of hard ionomer alone. It would be useful to develop a golf ball having a combination of softness and durability which is better than the softness-durability combination of a golf ball cover made from a hard-soft ionomer blend.

20 It is an object of the present invention to provide a golf ball which overcomes or at least alleviates, one or more disadvantages of the prior art. It is also an object to provide a method for making that golf ball.

Summary of the Invention 25 According to the present invention, there is provided a golf ball including a core and a cover including an ionomeric resin having at least 95 wt of one or more terpolymers which are formed from ethylene, at least one acid selected from the group consisting of acrylic, maleic, itaconic, fumaric and methacrylic acid, and half esters of maleic, fumaric and itaconic acids and at least one comonomer selected from the group consisting of methyl, ethyl, n-propyl, n-butyl, n-octyl, 2ethylhexyl, and 2-methoxyethyl-l-acrylates, said one or more terpolymers having an overall Shore D hardness of about 40 64.

W:\mary\MMHNODEL\10148-97.DOC 3 The present invention further provides a method of making golf ball having a core and a cover, including the steps of: obtaining a golf ball core, forming a cover over the core, the cover including at least 95 wt of one or more terpolymers of ethylene, an acrylate ester, and an acid selected from the group consisting of acrylic acid and methacrylic acid, the acid being neutralized with cations, the cover having a hardness of 40 64.

Also disclosed herein is a golf ball including a core and a cover including an ionomeric resin having at least 95 wt of one or more terpolymers which are formed from ethylene, at least one acid selected from the group consisting of acrylic, maleic, itaconic, fumaric and methacrylic acid, and half esters of maleic, fumaric and itaconic acids and at least one comonomer selected from the group consisting of methyl, ethyl, n-propyl, n-butyl, n-octyl, 2-ethylhexyl, and 2methoxyethyl-1-acrylates, said one or more terpolymers having an overall Shore 15 D hardness of about 40 64.

Further disclosed herein is a method of making golf ball having a core and a cover, including the steps of: obtaining a golf ball core, forming a cover over the core, the cover including at least 95 wt of one 20 or more terpolymers of ethylene, an acrylate ester, and an acid selected from the group consisting of acrylic acid and methacrylic acid, the acid being neutralized with cations, the cover having a hardness of 40 64.

An advantage of the invention is the provision of a golf ball with a soft cover which has good scuff resistance.

*.O

S 25 Yet another advantage of the invention is the provision of a golf ball having a favorable combination of spin rate and durability.

A further advantage of the invention is the provision of a golf ball having a soft cover made from a cover material which is blended with minimal mixing difficulties.

Another advantage of the invention is the provision of a method of making a golf ball which has a soft cover with good scuff resistance and cut resistance.

Yet another advantage of the invention is the provision of a method of making a durable golf ball with a relatively high spin rate.

W:\mary\MMHNODEL\10148-97.DOC 3a Other advantages will be in part obvious and in part pointed out more in details hereafter.

The invention in a preferred form is a golf ball comprising a core and a scuff-resistant cover. The cover comprises an ionomeric resin having more than 90 weight of one or more acrylate ester-containing ionic copolymers. The one or more acrylate ester-containing ionic copolymers are each formed from an olefin having 2 to 8 carbon atoms, an unsaturated monomer of the acrylate ester class having from 1 to 21 carbon atoms, and an acid which includes at least one member selected from the group consisting of a, p-ethylenically unsaturated mono- or dicarboxylic acids with a portion of the acid groups being neutralized with cations. The one or more acrylate ester-containing ionic copolymers have an overall Shore D hardness of 40 64. The resulting golf ball has a coefficient of restitution of at least 0.770.

The one or more acrylate ester-containing ionic copolymers preferably are 15 terpolymers. In each copolymer, the olefin preferably is an alpha olefin, and the acid preferably is acrylic acid. The overall cover preferably has a Shore D hardness of no more than about 64.

The one or more acrylate ester-containing ionic copolymers typically have a degree of neutralization of the acid groups in the range of about 10 100%. In a preferred form of the invention, the covers e W:\mary\MMHNODEL\10148-97.DOC have a scuff resistance rating of 3.0 or better when subjected to the Golf Ball Cover Scuff Test which is described below.

In a particularly preferred form of the invention, the cover comprises an ionomeric resin having at least 95 weight of one or more acrylate ester-containing ionic copolymers. The cover preferably contains at least 90 weight ionomeric resin. Each of the acrylate ester-containing copolymers preferably comprises ethylene, at least one acid selected from the group consisting of acrylic acid, maleic acid, fumaric acid, itaconic acid, methacrylic acid, and half-esters of maleic, fumaric and itaconic acids, and at least one comonomer selected from the group consisting of methyl, ethyl, n-propyl, n-butyl, n-octyl, 2ethylhexyl, and 2-methoxyethyl-1-acrylates.

Another preferred form of the invention is a method of making a golf ball. The method comprises the steps of obtaining a golf ball core 15 and forming a scuff-resistant cover over the core. The cover comprises an ionomeric resin having more than 90 weight of one or more acrylate ester-containing ionic copolymers formed from an olefin having 2 to 8 carbon atoms, an unsaturated monomer of the acrylate ester class having from 1 to 21 carbon atoms, and an acid which is 20 selected from the group consisting of alpha, beta-ethylenically unsaturated mono- or dicarboxylic acids with a portion of the acid groups being neutralized with cations. The one or more acrylate estercontaining ionic copolymers preferably have a Shore D hardness of about 40 64.

The invention accordingly comprises the several steps and the relation of one or more of such steps with respect to each of the others and the article possessing the features, properties, and the relation of elements exemplified in the following detailed disclosure.

Detailed Description of the Invention The present invention overcomes mixing difficulties associated with the preparation of soft-covered ionomeric golf balls by forming the cover of soft ionomeric golf balls from a cover composition in which the ionomer has more than 90 weight of an acrylate ester-containing ionic copolymer or blend of acrylate ester-containing ionic copolymers.

Furthermore, the invention provides golf ball covers having a favorable combination of durability and spin rate.

The one or more acrylate ester-containing ionic copolymers to be used in forming the cover of the inventive golf ball each contain an olefin, an acrylate ester, and an acid. In a blend of two or more acrylate ester-containing ionic copolymers, each copolymer may contain the same or a different olefin, acrylate ester and acid than are contained in the other copolymers. Preferably, the acrylate ester-containing ionic 15 copolymer or copolymers are terpolymers, but additional monomers can be combined into the copolymers if the monomers do not substantially reduce the scuff resistance or other good playability properties of the cover.

For a given copolymer, the olefin is selected from the group consisting of olefins having 2 to 8 carbon atoms, including, as nonlimiting examples, ethylene, propylene, butene-1, hexene-1 and the like.

Preferably the olefin is ethylene.

The acrylate ester is an unsaturated monomer having from 1 to S* 21 carbon atoms which serves as a softening comonomer. The acrylate ester preferably is methyl, ethyl, n-propyl, n-butyl, n-octyl, 2-ethylhexyl, or 2-methoxyethyl 1-acrylate, and most preferably is methyl acrylate or n-butyl acrylate. Another suitable type of softening comonomer is an alkyl vinyl ether selected from the group consisting of n-butyl, n-hexyl, 2-ethylhexyl, and 2-methoxyethyl vinyl ethers.

The acid is a mono- or dicarboxylic acid and preferably is selected from the arouo consisting of methacrylic, acrylic, ethacrylic, a- 6 chloroacrylic, crotonic, maleic, fumaric, and itaconic acid, or the like, and half esters of maleic, fumaric and itaconic acid, or the like. The acid group of the copolymer is 10 100% neutralized with any suitable cation, for example, zinc, sodium, magnesium, lithium, potassium, calcium, manganese, nickel, chromium, tin, aluminum, or the like. It has been found that particularly good results are obtained when the neutralization level is about 50 100%.

The one or more acrylate ester-containing ionic copolymers each has an Individual Shore D hardness of about 5 64. The overall Shore D hardness of the acrylate ester-containing ionic copolymer or blend of acrylate ester-containing ionic copolymers is 40 64. It is preferred that the overall Shore D hardness of the acrylate ester-containing ionic copolymer or blend is in the range of 50 64 in order to impart particularly good playability characteristics to the ball. It has been 15 found that excellent results can be obtained when the Shore D hardness of the acrylate ester-containing ionic copolymer or acrylate estercontaining ionic copolymer blend is in the range of 52 54 for a soft covered golf ball or 62 64 for a somewhat harder ball.

The cover of the invention is formed over a core to result in a golf ball having a coefficient of restitution of at least 0.770, more preferably .at least 0.780, and most preferably at least 0.790. The coefficient of restitution of the ball will depend upon the properties of both the core and the cover. The cover of the present invention is adapted for use with any type of golf ball core.

The acrylate ester-containing ionic copolymer or copolymers used in the golf ball of the invention can be obtained by neutralizing commercially available acrylate ester-containing acid copolymers such as polyethylene-methyl acrylate-acrylic acid terpolymers, including ESCOR ATX (Exxon Chemical Company) or poly (ethylene-butyl acrylate-methacrylic acid) terpolymers, including NUCREL (DuPont Chemical Company), Particularly preferred commercially available materials include ATX 320, ATX 325, ATX 310, ATX 350, and blends of these materials with NUCREL 010 and NUCREL 035. The acid groups of these materials and blends are neutralized with one or more of various cation salts including zinc, sodium, magnesium, lithium, potassium, calcium, manganese, nickel, etc. The degree of neutralization ranges from 10 100%. Generally, a higher degree of neutralization results in a harder and tougher cover material. The properties of non-limiting examples of commercially available unneutralized acid terpolymers which can be used to form the golf ball covers of the invention are provided below in Table 1.

Table 1 Trade Name Melt Index Acid No. Flex modulus Hardnes dg/min KOH/g MPA (Shore C ASTM D1238 (ASTM D790) ATX 310 6 45 80 44 ATX 320 5 45 50 34 ATX 325 20 45 9 ATX 350 6 15 20 28 Nucrel 010 11 60 40 Nucrel 035 35 60 59 The ionomer resins used to form the golf balls of the invention 20 are produced by reacting the acrylate ester-containing acid copolymer with various amounts of the metal cation salts at a temperature above the crystalline melting point of the copolymer, such as a temperature from about 200 0 F to about 500 0 F, preferably from about 250 0 F to about 3500F, under high shear conditions at a pressure of from about 100 psi to 10,000 psi. Other well known blending techniques may also be used. The amount of metal cation salt utilized to produce the neutralized ionic copolymers is the quantity which provides a sufficient amount of the metal cations to neutralize the desired percentage of the carboxylic acid groups in the high acid copolymer. When two or more different copolymers are to be used, the copolymers can be blended before or after neutralization. Generally, it is preferable to blend the copolymers before they are neutralized to provide for optimal mixing.

The compatibility of the acrylate ester-containing copolymers with each other in a copolymer blend produces a golf ball having a surprisingly good scuff resistance for a given cover hardness. The golf ball according to the invention has a scuff resistance of no higher than It is preferred that the golf ball has a scuff resistance of no higher than about 2.5 to ensure that the golf ball is scuff resistant when used in conjunction with a variety of types of clubs, including sharp-grooved i* irons, which are particularly inclined to result in scuffing of golf ball 15 covers. The best results according to the invention are obtained when S. ~the cover has a scuff resistance of no more than about 2.0. The scuff resistance test is described in detail below.

The golf ball of the invention has a spin rate of 7,500 or more.

It is particularly preferred that the golf ball of the invention have a spin rate of 8,000 or more in order to provide experienced players with excellent spin characteristics. In a particularly preferred form of the invention, the golf ball has a spin rate of at least 8,500. These spin rates are surprisingly high given the good scuff and cut resistance ratings of the ionomeric cover material. The test for spin rate is described below.

Additional materials may also be added to the ionic cover compositions of the present invention as long as they do not substantially reduce the playability properties of the ball. Such materials include dyes (for example, Ultramarine Blue sold by Whitaker, Clark, and Daniels of South Plainsfield, (see U.S. Pat. No. 4,679,795), pigments such as titanium dioxide, zinc oxide, barium sulfate and zinc sulfate; UV absorbers; antioxidants; antistatic agents; and stabilizers.

Moreover, the cover compositions of the present invention may also contain softening agents such as those disclosed in U.S. Patent Nos.

5,312,857 and 5,306,760, including plasticizers, metal stearates, processing acids, etc., and reinforcing materials such as glass fibers and inorganic fillers, as long as the desired properties produced by the golf ball covers of the invention are not impaired. Furthermore, nonionomeric cover materials such as metallocene catalyzed polyolefins, including EXACT materials available from EXXON, can be blended with the terpolymers as long as a favorable combination of S. scuff resistance, COR, compression and spin rate is obtained.

When a blend of two or more acrylate ester-containing ionic copolymers is to be used, the cover compositions of the present invention may be produced according to conventional melt blending 15 procedures. Generally, the copolymer resins are blended in a Banbury type mixer, two-roll mill, or extruder prior to neutralization. After blending, neutralization then occurs in the melt or molten state in the Banbury mixer. Mixing problems are minimal because preferably more than 91 wt and more preferably at least 95 wt of the ionic 20 copolymers in the mixture contain acrylate esters, and in this respect, most of the polymer chains in the mixture are similar to each other. The blended composition is then formed into slabs, pellets, etc., and maintained in such a state until molding is desired. If necessary, further additives such as inorganic fillers, antioxidants, stabilizers, processing aids, etc., may be added and uniformly mixed before initiation of the molding process. In one embodiment of the invention, a masterbatch of non-acrylate ester-containing ionomer with pigments and other additives incorporated therein is mixed with the acrylate estercontaining copolymers in a ratio of about 1 7 weight masterbatch and 93 99 weight acrylate ester-containing copolymer.

The golf balls of the present invention can be produced by molding processes which include but are not limited to those which are currently well known in the golf ball art. For example, the golf balls can be produced by injection molding or compression molding the novel cover compositions around a wound or solid molded core to produce a golf ball having a diameter of about 1.680 1.80 inches and typically but not necessarily weighing about 1.620 ounces. The standards for both the minimum diameter and maximum weight of the balls are established by the United States Golf Association The cores of the inventive golf balls typically have a coefficient of restitution of about 0.775 and a PGA compression of about 110.

The term "solid cores" as used herein refers not only to one piece cores but also to those cores having a separate solid layer beneath the cover and over the core. When the golf ball of the invention has a solid core, this core can be compression molded from a slug of uncured or lightly cured elastomer composition comprising a high cis content polybutadiene and a metal salt of an a, fP, ethylenically unsaturated carboxylic acid such as zinc mono- or diacrylate or methacrylate. To achieve higher coefficients of restitution and/or to increase hardness in 20 the core, the manufacturer may include a small amount of a metal oxide such as zinc oxide. In addition, larger amounts of metal oxide than are needed to achieve the desired coefficient may be included in order to increase the core weight so that the finished ball more closely approaches the U.S.G.A. upper weight limit of 1.620 ounces. Nonlimiting examples of other materials which may be used in the core composition including compatible rubbers or ionomers, and low molecular weight fatty acids such as stearic acid. Free radical initiator catalysts such as peroxides are admixed with the core composition so that on the application of heat and pressure, a curing or cross-linking reaction takes place.

11 Wound cores are generally produced by winding a very large elastic thread around a solid or liquid filled balloon center. The elastic thread is wound around the center to produce a finished core of about 1.4 to 1.6 inches in diameter, generally. Since the core material is not an integral part of the present invention, a detailed discussion concerning the specific types of core materials which may be utilized with the cover compositions of the invention are not specifically set forth herein.

As indicated, the golf balls of the present invention may be produced by forming covers consisting of the above-described compositions around cores by molding processes. For example, in compression molding, the cover composition is formed via injection at e.g. about 380 0 F to about 450 0 F into smooth surfaced hemispherical shells which are then positioned around the core in a dimpled golf ball 15 mold and subjected to compression molding at e.g. 2000 300 0 F for 2 10 minutes, followed by cooling at 500 70 0 F for 2 10 minutes, to fuse the shells together to form an unitary ball. In one type of injection molding process, the cover composition is injected directly around the core placed in the center of a golf ball mold for a period of time at a mold temperature of from 500 to about 100 0 F. After molding, the golf balls produced may undergo various further processing steps such as buffing, painting, and marking.

Having generally described the invention, the following examples are included for purposes of illustration so that the invention may be more readily understood and are in no way intended to limit the scope of the invention unless otherwise specifically indicated.

Example 1 A set of golf balls was made with solid cores and a cover composition of 75 weight NUCREL 035, which is an acrylate estercontaining acid terpolymer, and 25 weight of a masterbatch containing 4.5 weight MgO in Surlyn® 1605 ("MgO Masterbatch").

The terpolymer was reacted with the masterbatch at a temperature of about 250°F under high shear conditions at a pressure of about 0 to 100 psi. The magnesium in the masterbatch neutralized acid groups of the terpolymer at a level of about 62% neutralization. The molded balls were finished with polyurethane primer and top coats. The PGA compression, coefficient of restitution, Shore C hardness, scuff resistance, spin rate and cold crack of the golf balls were determined.

The results are shown on Table 2 below.

To measure cold crack, the finished golf balls were stored at 10 0 F for at least 24 hours and were then subjected to 5 blows in a coefficient machine at 165 ft/sec. The balls were allowed to return to room temperature and were then visually inspected for cover cracking.

S: None of the golf balls experienced cracking.

Coefficient of restitution (COR) was measured by firing the resulting golf ball in an air cannon at a velocity of 125 feet per second against a steel plate which was positioned 12 feet from the muzzle of 'the cannon. The rebound velocity was then measured. The rebound velocity was divided by the forward velocity to give the coefficient of restitution. Shore hardness was determined in general accordance 20 with ASTM Test 2240, but was measured on the golf ball.

S: Comparative Example 1 A set of 12 golf balls was made according to the same procedure as that of Example 1 with the exception that NUCREL 925, a nonacrylate ester-containing acid copolymer was substituted for NUCREL 035. The resulting golf ball cover was too hard, resulting in four breaks during cold crack testing.

13 Comparative Example 2 The procedure of Example 1 was repeated with the exception that the MgO Masterbatch was replaced by pure Surlyn® 1605. All of the golf ball covers broke during cold crack testing.

Comparative Example 3 The procedure of Comparative Example 1 was repeated with the exception that the MgO masterbatch was replaced by pure Surlyn® 1605. The results are shown on Table 2. When subjected to cold crack testing, all of the golf ball covers broke.

10 As can be seen from the results of Example 1 and Comparative Examples 1 3, inferior golf balls are obtained when a hard, non- 1 acrylate ester-containing copolymer is used instead of a softer, acrylate ester-containing terpolymer, and when either an acrylate estercontaining acid terpolymer or a non-acrylate ester-containing acid copolymer is not neutralized with metal ions.

Example 2 An acrylate ester-containing terpolymer sold as ESCOR ATX 325 (Exxon Chemical Co.) was 57% neutralized with lithium cations. The ionomeric material, which also contained titanium dioxide, brightener, •20 etc. from a white masterbatch, was placed over a solid golf ball core and the golf ball was primed and top coated. The properties of the resulting golf ball are shown on Table 3. This procedure was repeated using different combinations of terpolymers with cations and cation blends at the degrees of neutralization which are shown on Table 3. In the cation blends, mole ratios were about 1:1:1. All of the ATX materials shown on Table 2 are ESCOR ATX materials available from Exxon Chemical Co. The Nucrel materials are available from DuPont Chemical Co. Primacor 3440 is available from Dow Chemical Co.

I C 14 The spin rate of the golf ball was measured by striking the resulting golf balls with a pitching wedge or 9-iron wherein the clubhead speed is about 80 feet per second and the ball was launched at an angle of 26 to 34 degrees with an initial velocity of 100 115 feet per second. The spin rate was measured by observing the rotation of the ball in flight using stop action Strobe photography or via the use of a high speed video system.

The scuff resistance test was conducted in the following manner: a Top-Flite tour pitching wedge (1994) with box grooves was obtained and was mounted in a Miyamae driving machine. The club face was oriented for a square hit. The forward/backward tee position was adjusted so that the tee was four inches behind the point in the downswing where the club was vertical. The height of the tee and the toe-heel position of the club relative to the tee were adjusted in order that the center of the impact mark was about 3/4 of an inch above the sole and was centered toe to heel across the face. The machine was operated at a club head speed of 125 feet per second. A minimum of three samples of each ball were tested. Each ball was hit three times.

After testing, the balls were rated according to the following table: Rating Type of damage 1 Little or no damage (groove markings or dents) 2 Small cuts and/or ripples in cover 3 Moderate amount of material lifted from ball surface but still attached to ball 4 Material removed or barely attached The balls that were tested were primed and top coated.

As shown on Table 3, many of the cover materials resulted in golf balls having a scuff resistance of 1.5 or less, and others had a scuff resistance rating of 1.5 St- 6 Comparative Example 4 A golf ball with a cover formed from a blend of a commercially available hard sodium ionomer and a commercially available soft acrylate ester-containing zinc ionomer in which the blend contains less than 60 wt soft ionomer was subjected to the same testing as the golf balls of Example 2. The results are shown on Table 3.

Example 3 The procedure of Example 2 was repeated with the exception that single cations of lithium, magnesium, sodium and potassium were 10 used in the cover material. The results are shown on Table 4.

As indicated on Table 4, the scuff resistance of the golf balls was 3.0 or better. The scuff resistance of the balls with covers made of an acrylic acid terpolymer was 1.0. For a given terpolymer, the scuff resistance did not change when different cations were used for 15 neutralization.

As will be apparent to persons skilled in the art, various modifications and adaptations of the structure above described will become readily apparent without departure from the spirit and scope of the invention, the scope of which is defined in the appended claims.

16 TABLE 2 Experiment No.

Cover Material Weight PGA COR Shore C Cold comp. IxlOOO) Hardness Crack Nuorel 036/ MgO MB In $urlyn 1605 45.2 104 .783 camp. 1 75% Nucrel 9261 Mg0 MB In Surlyn 1605 camp. 2 75% Nucrel 035! 25% Surlyn 1605 camp. 3 75% Nucrel 9251 25% Surlyn 1805 45.1 ill .798 45.1 99 .774 45. 2 106 .790 so No breaks 90 4 breaks 70 All broke 75 All broke 17 TABLE 3 o* 0 :periment Cover No. Material omp .4 hard-soft lonomer blend 1 (control) 2-1 ATX 325 2-2 ATX 325 2-3 ATX 320 2-4 ATX 320 Nucrel 010 2-6 Nucrel 0 10 2-7 Nucrel 035 2-8 Nucrel 035 2- 9 ATX 310 2-10 ATX 310 2-11 ATX 325 2-12 ATX 325 2-13 50% ATX 325-U

ATX

320-unneut.

2-14 75%ATX32O -LI/Zn/K 25%ATX32O -unneut.

2-15 60%ATX325 -U/Zn/K 3440-unnout.

2-16 ATX 320 2-17 ATX 325 2-18 ATX 326 2-19 ATX 325 2-20 ATX 325 2-21 ATX 325 2-22 ATX 325 Cation Zn/Na Li U/Zn/K

U

U/ZnIK

LI

U/Zn/K

LI

Li/Zn/K

LI

LI/Zn/K

LI

WlZnlK 11-i1 (U/Zn/K) (U/Zn/K) Unneut.

Unneut.

LI

U

U/Zn/K UIJZn/K LiJZn/K Neutralization 60% 57% 65% 57% 65% 53% 60% 57% 65% 28.5% 49% 39% 50% 30% 50% 30% 50% PGA COB Shore D Comp. ix 1000) Hardness 90 787 86 86

N.T.

87.

89 89 87 87 88 88 83 82 89 787 787

N.T.

790 803 802 801 798 802 801 797 796 777 58 51 50 66 5 65 66 62 62 62 63 63 54 54 42 46 48 47 10,430 10,464 10.299 10,35 7,644 7,710 8,931 8,915 8.892 8,244 Scuff Spin Rate Resist. Iron at 105 ftlsec) 4.0 9,859 87 -776 88 779 775 795 791 791 N .T.

N.T.

I 18 TABLE 4 Experiment No.

3-1 3-2 3-3 3-4 3-6 Cover Material Nucrel 035 Nucrel 035 ATX 325 ATX 325 ATX 3.5 ATX 325 Cation Li Mg

U

Mg Na

K

Neutralization 100 100 100 100 81 95 PGA COR Comp. IX10OO) 90 792 89 .792 85 790 85 791 85 .790 85 791 Share D Hardness 62 62 51 51 51 Scuff Resistance

S

*..SSS

S

S. 55 S

S

Claims (8)

1. A golf ball including a core and a cover including an ionomeric resin having at least 95 wt of one or more terpolymers which are formed from ethylene, at least one acid selected from the group consisting of acrylic, maleic, itaconic, fumaric and methacrylic acid, and half esters of maleic, fumaric and itaconic acids and at least one comonomer selected from the group consisting of methyl, ethyl, n-propyl, n-butyl, n-octyl, 2-ethylhexyl, and 2-methoxyethyl-l-acrylates, said one or more terpolymers having an overall Shore D hardness of about 40 64.

2. A golf ball according to claim 1, wherein the golf ball has scuff resistance of no higher than

3. A golf ball according to claim 1 or 2, wherein the golf ball has a spin rate of S 15 at least 7,500 revolutions per minute when struck with a 9-iron at a clubhead speed of about 80 feet per second and a launch angle of 26 to 34 degrees.

4. A golf ball according to any preceding claim, wherein said one or more terpolymers comprise.a blend of at least two terpolymers.

A golf ball according to any preceding claim, wherein the acid is acrylic acid.

6. A method of making golf ball having a core and a cover, including the steps of: obtaining a golf ball core, forming a cover over the core, the cover including at least 95 wt of one or more terpolymers of ethylene, an acrylate ester, and an acid selected from the group consisting of acrylic acid and methacrylic acid, the acid being neutralized with cations, the cover having a hardness of 40 64.

7. A golf ball according to claim 1, substantially as herein described with reference to any one of the Examples. W:mnary\MMHNODEL\10148-97.DOC V I.

8. A method according to claim 6, substantially as herein described with reference to any one of the Examples. DATED: 31 July 2000 PHILLIPS ORMONDE FITZPATRICK Patent Attorneys for: SPALDING SPORTS WORLDWIDE, INC. 0 v 0 00 S...4 w:maryMMHN0DELN10148-97.D0C