WO 99/27792 PCT/AU98/00984 -1- "IMPROVED BIOCIDE AND BIOCIDAL CLOTH" TECHNICAL FIELD This invention relates to a biocidal cleaning composition and the incorporation thereof into a biocidal cloth. sponge. paper. wound dressing, plastic or other substrate.

BACKGROUND ART In domestic and hospital environments one of the most common methods of i0 cleaning large surfaces is to wipe a cloth over such surfaces. Typically. the cloth will be moistened with water and may additionally have added a detergent or disinfectant.

Cloths which do not contain a disinfectant are ineffective in controlling the growth of microorganisms. Indeed. the cloth itself may provide favourable conditions for the proliferation of such microorganisms and the action of wiping such an infected cloth over a surface may produce an effect counter to the desired outcome of making the surface more hygienic. Ordinary cleaning cloths which remain damp for a period are also notorious for the odours they develop, which are a result of microbial action.

Soaking a cloth in disinfectant provides fairly short term relief and requires the reapplication of the disinfectant to the cloth. While this method uses only modest amounts of disinfectant. the quantity is nevertheless much more than is required to achieve adequate bactericidal action. An extremely efficacious disinfectant is also required to prevent bacterial proliferation in the cleaning cloth itself. especially against the wide range of bacteria which are present, in domestic and hospital situations. This somewhat unsophisticated method is also wasteful in that every time the cloth is rinsed or washed the disinfectant is removed and a new aliquot must be applied.

WO 99/27792 PCT/AU98/00984 -2- It has been practiced to incorporate an antimicrobial agen in a non-woven fabric as a colloidal suspension within an amorphous polymeric binder. The antimicrobial is not bound and is available to migrate to the surface of the binding agent. Such systems require an internal reservoir having a very large quantity of antimicrobial agent typically 12 to 30 grams per square yard. and are more costly and less durable than is desired.

Cellulose sponges containing zinc pyridinethione as an active antibacterial agent are known. These sponges suffer from the drawback that a single wash in a washing machine is sufficient to remove much of the zinc pyridinethione. Thus. the sponge remains an effective weapon against bacteria for only a limited portion of its' working life. and may lead to users having false confidence in its' potency.

The reason that the zinc pyridinethione is so readily removed under normal washing conditions is that it is hydrolysed markedly at around pH 11. Zinc pyridinethione is an effective biocide. but suffers from the drawback that its optimal range of efficacy is within the pH range of 4.5 to 9.5. Many detergents and household cleaning agents have pH's above this range (for instance, washing powders give rise to solutions of around pH 11 and household bleaches have a pH of around 13). and. as in use they are often present in greater quantities than the zinc pyridinethione. are capable of rendering it ineffective.

The use of high concentrations of zinc pyridinethione to compensate for it's high loss under domestic cleaning conditions is undesirable as it has some human toxicity and is mildly irritating to the skin. and severely so to the eye. Further. the zinc pyridinethione has been shown to leach irreversibly out of the sponge over time.

-3- There remains the problem then of providing a cleaning device, such as a cloth, sponge or similar, which will remain effective against a wide range of bacteria for a significant period of time, yet will not be unacceptably toxic.

Surprisingly, the inventor has found that one or more selected biocides, for example triclosan, dichlorophen (sometimes known as "dichlorophene" or DCP) or other chlorinated phenolic biocides, phenolic biocides, or trichlorocarban, in combination with an organometallic biocide, for example a metallic pyridinethione, exhibit a synergy which enables the combination to be effective against a wide range of bacteria under a wide range of pH conditions. Further, the addition of an acrylate binder, with or without 10 other immobilising agents such as PVP, has also been found to render the biocidal mixture suitable for incorporation into a substrate for example a woven or non-woven cloth.

It is to be appreciated that such a biocide and method of binding is not limited to textiles used for cleaning, but may also be applicable to other materials, such as sponges, 15 paper, wound dressings, plastics or even concrete.

**oo DESCRIPTION OF THE INVENTION It is to be understood that the use of the term "biocidal" throughout this specification is used in the sense that it refers to killing one or more organisms, and thus it embraces both the terms "biocidal" and "biostatic" as commonly referred to in relation to reducing or maintaining the number of microorganisms in a colony.

According to a first aspect the invention consists in a biocidal composition comprising a first biocide which is a metal pyridinethione; and a second synergistic biocide selected to be biocidally effective in a pH range complementary to the metal S pyridinethione, said 173aupOO.doc/CmW PCT/AU98/00984 Received 28 September 1999 -4second biocide selected from the group consisting of halogenated phenols, phenols, derivatives of halogenated phenols, derivatives of phenols and trichlorcarban.

Examples of derivatives include diphenyl ether derivatives, methylene bridged derivatives and the like. The most preferred compounds are triclosan, dichlorophen and trichlorcarban. Examples of phenolic biocides which may be used include, but are not limited to, ortho-phenylphenol, methyl parahydroxybenzoate, propyl parahydroxybenzoate, ortho-cresol, meta-cresol and para-cresol.

Preferably the metal pyridinethione is zinc, sodium or magnesium pyridinethione, and most preferably it is zinc pyridinethione.

According to a second aspect the invention consists in a biocidal cleaning device comprising a biocidal composition according to the first aspect and a substrate.

According to a third aspect the invention consists in a method of making a biocidal cleaning device comprising the steps of combining a biocidal composition according to the first aspect with a binding agent and contacting the resultant formulation with a substrate. Preferably the method further includes the step of binding the composition to the substrate.

According to a fourth aspect, the invention consists in a biocidal plastic material comprising a biocidal composition according to the first aspect.

According to a fifth aspect, the invention consists in a method of making a biocidal plastic material according to the fourth aspect comprising the steps of dissolving a biocidal composition according to the first aspect in a plasticiser then compounding the plasticiser into a polymer and forming the polymer into a desired shape.

AMENDED SHEET

IPEA/AU

WO 99/27792 PCT/AU98/00984 Preferably in a biocidal cleaning device the metal pyridinethione is present in amounts up to 2.5% of the weight of the device. More preferably it is present in amounts of 0.05 to 1.0% of the weight of the device. Most preferably it is present in amounts of 0.1 to 1.0% of the weight of the device.

Preferably in the biocidal cleaning device the second biocide is present in amounts up to 6% of the weight of the device. More preferably it is present in amounts of 0.05 to 2.0% of the weight of the device. Most preferably it is present in amounts of 0.1 to 2.0% of the weight of the device.

Desirably the biocidal composition is prepared as a concentrate which is diluted prior to impregnation into the substrate. In the concentrate the metal pyridinethione is present in amounts up to 40% w/w. and more preferably 20 to 30 wiw.

Preferably the second biocide is present in the biocidal concentrate in amounts up to 60% w/w. and more preferably 20 to 40% w/w.

The biocidal composition or concentrate may also include, in any combination, a mineral oil. (PVP) polyvinylpyrrolidone. an alcoholic solvent, an anionic surfactant. a non-ionic surfactant and water.

The substrate for use in the biocidal cleaning device is preferably cloth.

Preferably the cloth weight is from 30 to 200 g/m. and more preferably from 120 g/m- and the cloth is comprised of from: 70-100% rayon and 0-30% polyester.

Preferably. the cloth also includes 0-30% polypropylene.

The substrate may also be sponge or a synthetic equivalent, paper or woven textile. In the case of a sponge. the weight can be up to 250g/m 2 or more.

WO 99/27792 PCT/AU98/00984 -6- When binding the biocidal mixture onto a substrate. preferably the binding means comprises a heat activated crosslinking reaction. The heat activated crosslinking reaction may be carried out by a steam heated drum or by infra red means. The crosslinking reaction may also be activated by UV or visible light, electron beam or the like or chemical initiation.

The binding agent used in binding a biocidal mixture to a substrate may be a polymer latex formulation or acrylate. in particular acrylate copolymers.

When making a biocidal plastic material the plasticiser is optionally a hydrocarbon. preferably selected from the group comprising polybutene. low density polyethylene. low density polypropylene and paraffin wax. The plasticiser may also be.

for example, an ester preferably selected from the group comprising dibutyl phthalate.

dioctylphthalate. or epoxidised vegetable oil or blends thereof..

Unless the context clearly requires otherwise. throughout the description and the claims, the words 'comprise'. 'comprising', and the like are to be construed in an inclusive sense as opposed to an exclusive or exhaustive sense: that is to say, in the sense of"including. but not limited to".

BEST MODE FOR CARRYING OUT THE INVENTION Preferred embodiments of the invention will now be described by way of example only. In the embodiments described zinc pyridinethione is used as the first biocide and triclosan as the second. However it will be understood that the invention is not limited to this embodiment.

The combination of zinc pyridinethione and triclosan or dichlorophen provides important advantages over the use of either disinfectant alone.

WO 99/27792 PCT/AU98/00984 -7- Zinc pyridinethione is effective at pH ranges from 4.5 to 9.5. As many detergents are strongly basic in nature, they can render zinc pyridinethione ineffective at very high pH's. Triclosan. dichlorophen. trichlorcarban. chlorinated phenolic biocides and phenolic biocides generally, on the other hand become more effective at higher pH ranges. in particular, at pH 9.5 and above.

In pH neutral or near neutral conditions. i.e. in the absence of large amounts of detergent, both the zinc pyridinethione and the complementary biocide work well.

However. zinc pyridinethione. while effective against gram positive microorganisms. has been shown to be intrinsically only of limited effectiveness against gram negative bacteria. Triclosan and dichlorophen. for example, on the other hand while having some gram negative activity are particularly effective against gram positive bacteria. In particular, the combination of the zinc pyridinethione and the complementary biocide as described above, has been shown to exhibit a marked synergistic effect in killing Pseudomonas Aeruginosa.

The quantity of zinc pyridinethione used in the mixture to achieve a given bactericidal result is much less than if it was used alone, with the added advantage that less of this relatively toxic compound is used.

Thus. the combination of the two active ingredients is effective against a wide range of microorganisms at neutral pH's. and retains a good deal of this efficacy at higher pH's. in the presence of detergents.

The compositions of the present invention may also be used against mould.

Toxicologically. DCP is much safer than Zinc pyridinethione. Toxicological data is shown in table 1. It is possible to formulate a biocidal mixture which has a high WO 99/27792 PCT/AU98/00984 -8biocidal activity over a wide pH range, against a broad spectrum of microorganisms vet exhibiting with a low level of toxicity to humans.

Table I PROPERTY DICHLOROPHEN ZINC PYRIDINETHIONE Melting Point OC 175 240 Decomp. °C 290 240 pH Stability >activity>pH decomposes Oxidising Agents incompatible decomposes Reducing Agents no effect decomposes Biodegradability Yes No Acute Toxicity Oral 3300 mgikg 160 mg/kg Dermal 5000 mg/kg 100 mg/kg Subcut >3000 mg/kg 730 mg/kg LD 50 IV 17 mg/kg 10 mg/kg Teratogenicity no effect reduced wt Fish Toxicity 23 mgilt not available Irritancv Slight dermal Moderate dermal Moderate eye Severe eye Genotoxicitv None None Regulatory: Max 0. 1 mg/It Max 0.1 mg/It Pesticide in waste water in waste water Heavy Metal none Max 10 mgilt WO 99/27792 PCT/AU98/00984 -9- PVP (poly vinyl pyrrolidone) may be added optionally as a complexing material.

PVP modifies the solubility and dispersibility of the biocide in water, as disclosed in PCT/AU96/00224.

The ability of PVP to modify the solubility and dispersibility have been found extremely useful when incorporating composite biocidal mixtures of the present invention onto a substrate. for example, cloth.

It is postulated that the PVP and the second (non-zinc pyridinethione) biocidal compound form a complex which provides excellent binding between the cloth and the active ingredients, retaining the biocidal dispersion and providing a longer effective life for the biocidal cloth. A postulated complex is shown in Figure I. It will be appreciated that the dichlorophen need not be complexed with a sinle polymeric strand of the PVP.

but may cross-link one or more other strands.

Figure I. The structure of the complex formed between Dichlorophen and PVP N N N Ci CH Cl Preferably for disinfecting and cleaning. polyvinylpyrrolidones with a degree of polymerisation (K value) of 15. 30. 60 and 90. most preferably 90 or copolymers with vinvlacetate comprising from 20 to 80% polyvinylpyrrolidone (most preferably WO 99/27792 PCT/AU98/00984 comprising at least 50% vinylacetate and can possibly possess cationic character) are used.

For impregnation, the amount of PVP polymer used is preferably in the range of from 0.01 to 99.9 parts of the polymer for each part of biocide. More preferably the polymer is in the range of from 0.01 to 50 parts and most preferably 0.01 to 10 parts for each part of phenolic biocide.

The triclosan. DCP. trichlorocarban or other complementary biocide can at any time be substituted by a PVP/DCP. PVP/triclosan. PVP/trichlorocarban of PVP/complementary biocide combination.

The addition of a binding agent such as an acrylate enhances binding of the biocide into a woven or non-woven textile. The addition of polyvinylpyrrolidone has also been found to increase the binding of the biocidal agents to the cloth, either alone or in combination with the acrylate binder. More importantly. the addition of polyvinylpyrrolidone has been found to limit the biocide. so that as the surface wears.

fresh biocide is exposed at the fresh surface.

The biocidal mixture in any of its forms can be mixed into binders such as acrylic or acrylic copolymer lattices or solutions. PVA lattices or PVA copolymer lattices or solutions. or any other polymer latex or solution or blend of any of the previously described polymers.

The biocidal mixture. with or without PVP or binding agents can be used for the treatment of any type of substrate. including woven or non-woven textile. fabrics.

sponges. scourers and the like. paper. or any other material. The treatments can be WO 99/27792 PCT/AU98/00984 1 applied from solutions. suspensions or emulsions at ambient or other operational temperatures.

The inclusion of a mineral oil and an acrylate binder into the any of the above formulation can increase the suitability of the biocidal mixture for cloth impregnation.

The most suitable fabrics for impregnation with the biocidal mixture are those which are rayon/polyester cloths which contain from 70 to 100 percent rayon. although most known fabrics perform adequately. In particular. fabrics which weigh between and 200 g/m and especially 30 and 120 g/m 2 have been found to be the most suitable.

Plasticisers are commonly added to synthetic polymers to modify their hardness and/or flexibility. Some common plasticisers are hydrocarbon polymers, such as polybutene, low density polyethylene. low density polypropylene and paraffin wax.

Other commonly used plasticisers are esters. such as dibutyl phthalate. dioctyl phthalate and similar esters. such as epoxidised vegetable oils or blends thereof and similar esters.

The biocide combination can be dissolved into a plasticiser or plasticisers and then compounded into a polymer which is then moulded by extrusion, injection moulding or some other process. The resulting item would then resist the growth of microorganisms on the surface of the item by virtue of the incorporated biocides. If the plasticiser were selected so as to be incompatible with the bulk material, it leaches out slowly. carrying effective amounts of the biocidal composition with it to the surface.

A use of particular interest is on materials used in evaporative cooling systems.

Such systems typically harbour a wide range of bacterial varieties, including legionella.

The use of a bound bactericide in such systems would provide a low hut long lasting level of activity against bacteria. Such systems typically utilise a number of plastic WO 99/27792 PCT/AU98/00984 12plates. and impregnating these with a biocidal mixture and a binder which was incompatible with the plastic, so as to leach slowly to the surface. would provide a constantly self renewable biocidally active surface.

EXAMPLES

Example 1. Formulation of Biocidal Concentrate The following formulation is prepared: Raw Material %w/w Zinc Pvridinethione 17.19 Dichlorophen 34.39 Mineral Oil 22.92 PVP 8.44 Ethanol 3.44 Sodium Laurvl Ether Sulfate 0.70 Dioctyl Sulfosuccinate 1.50 Water qs 100% Example 2: Alternate Biocidal Concentrate Raw Material %w/w Zinc pyridinethione 24.60 Dichlorophen 24.60 Mineral Oil 16.40 PVP 7.20 Ethanol 2.40 Sodium Laurylether sulfate 0.70 WO 99/27792 PCT/AU98/00984 -13- Dioctvl Sulfosuccinate 1.50 Water qs 100% Example 3. Binder Formulation Raw Material %w/w Acrylic polymer self crosslinking binder emulsion (approx 56% solids) 46.0 Defoamer emulsion (Foam Master. Henkel) 0.15 Acrylic copolymer viscosity controlling emulsion (Latekol DG. BASF) 3.60 Sodium dioctyl sulfosuccinate Ammonium hydroxide Ammonium nitrate Dyestuff dispersion to standard colour qs Water 47.25 The acrylic polymer binder emulsions is of a soft crosslinking type formulated with good tensile strength and rewetting properties for use in non-woven applications.

Example 4. Application to Fabric In this process. bales of textile fibre are fed into a machine for making bonded.

carded or hydroentanglcd non-woven fabric. These fibres can be of one type alone or of various combinations, for example most bonded. carded non wovens used for wipes are made from either rayon fibres or a combination of rayon and polyester fibres.

In the bonded. carded process the fibres are tangled together by one or more carding units in series, whereas the entangling takes place using high pressure water jets in hydroentangling. In both cases. at the end of the entangling stage the material is in WO 99/27792 PCT/AU98/00984 -14continuous web form and is quite damp due to residual water which has been used in the course of each process.

The damp continuous web is then printed using a suitable dilution of the concentrate of example 1 or 2 and the binder of example 3. which is applied to isolated S areas of the web. The damp. printed web passes through a heated zone to dry the printed fabric and cross-link the polymeric binder. These heated zones are usually either composed of steam heated drums over which the fabric passes and dries by contact. or else infra-red lamps which heat by radiation. or combinations of both.

This dry printed web is then rolled up for future slitting and cutting.

Example 5. Simulated Life Cycle of Cloth The treated fabric is put into an automatic domestic clothes washing machine set on a warm wash Five cycles of washing were applied which constitutes the simulated useful life of the fabric. At the end of five cycles of washing the fabric is put through the following tests to validate that biocidal performance is still effective at the end of the working life of the fabric.

Example 6. Standard Sensory Tests Standard sensory tests (stayfresh tests) were applied to the cloth to examine the resistance of the cloth to malodours produced by bacterial attack on food residues entrapped in the cloth in the normal course of kitchen use. Biocidal cloths produced according to the invention gave good results when subjected to the following tests: AS2609.1. AS 2542.1.1. As 2542.1.2 and AS 2542.2.3 WO 99/27792 PCT/AU98/00984 Example 7. Standard Quantitative Microbiological Test A biocidal cloth according to the invention was subjected to a standard quantitative test for microorganisms. "'Assessment of Antibacterial Finishes on Textile Materials": Test Method AATCC 100-1993. This test is specifically designed for the assessment of the biocidal properties of fabric treatments. These treatments are designed to kill microorganisms within the fabric, rather than on surfaces which come into contact with the fabric.

Example 8.

Table II shows the effect of Pseudomonas Aeruginosa of fabric impregnated with zinc pyridinethione (0.85 a second fabric impregnated with dichlorophen (0.85 and a third fabric impregnated with a combination of dichlorophen (0.5 and zinc pyridinethione (0.5 The weights are given relative to the weight of dry fabric. A positive sign indicates an increase in the bacterial population and a negative sign shows a decrease.

Table II BIOCIDE DAY 1 DAY 2 zinc pyridinethione +0.845 +0.35 dichlorophen +0.439 +2.12 dichlorophen/zinc pyridinethione -0.94 -0.98 While the invention has been described herein with reference to zinc pyridinethione. those skilled in the art will appreciate that the use of other metal pyridinethiones also form part of the same inventive concept.

Claims (15)

1. A biocidal concentrate comprising: a first biocide which is a metal pyridinethione; and a second synergistic biocide selected to be biocidally effective in a pH range complementary to said metal pyridinetione, said second biocide selected from the group consisting of: halogenated phenols, phenols, derivatives of halogenated phenols, derivatives of phenols, and trichlorocarban.

2. A biocidal concentrate according to claim 1 wherein said metallo-pyridinethione 10 is zinc pyridinethione.

3. A biocidal concentrate according to claim 1 wherein said metallo-pyridinethione is sodium pyridinethione.

4. A biocidal concentrate according to claim 1 wherein said metallo-pyridinethione is magnesium pyridinethione. 15 5. A biocidal concentrate according to any one of claims 1 to 4 wherein the second metal pyridinethione comprises 5-25% w/w of the mixture.

8. A biocidal concentrate according to any one of the preceding claims wherein the metal pyridinethione comprises 11-16% w/w of the mixture. 173aupo0docCmW WO 99/27792 PCT/AU98/00984

17- 9. A biocidal concentrate according to any one of the preceding claims further including a mineral oil. A biocidal concentrate according to any one of the preceding claims further including polyvinylpyrrolidone. S 11. A biocidal concentrate according to any one of the preceding claims further including an alcoholic solvent. 12. A biocidal concentrate according to any one of the preceding claims further including water. 13. A biocidal cleaning device comprising: A biocidal concentrate according to any one of claims 1 to 12: and a substrate. 14. A biocidal cleaning device according to Claim 13 wherein the metal pyridine thione is present in an amount of up to 2.5% of the weight of the device. A biocidal cleaning device according to Claim 13 or 14 wherein the metal pyridine thione is present in an amount of 0.05-1.0% of the weight of the device. 16. A biocidal cleaning device according to any one of Claims 13-15 wherein the metal pyridine thione is present in an amount of 0. 1-1.0% of the weight of the device. 17. A biocidal cleaning device according to any one of Claims 13-16 wherein the second biocide is present in an amount up to 6% of the weight of the device.

18. biocidal device according to any one of Claims 13-17 wherein the second biocide is present in an amount of 0.05-2.0% of the weight of the device.

19. A biocidal cleaning device according to any one of Claims 13-18 wherein the second biocide is present in an amount of 0.1-2.0% of the weight of the device. -18- A biocidal device according to any one of claims 15-19 wherein the second biocide is present in an amount of 0.05-2.0% of the weight of the device.

21. A biocidal cleaning device according to any one of claims 15-20 wherein the second biocide is present in an amount of 0.1-2.0% of the weight of the device.

22. A biocidal cleaning device according to any one of claims 15-21 wherein the substrate is cloth.

23. A biocidal cleaning device according to claim 22 wherein the cloth weight is from 30-200 g/m 2

24. A biocidal cleaning device according to claim 22 or 23 wherein the cloth weight *ll 10 is from 30-120 g/m.

25. A biocidal cleaning device according to any one of claims 22-24 wherein the cloth is comprised of from:

70-100% rayon; and 0-30% polyester. 15 26. A biocidal cleaning device according to claim 25 further comprising 0-30% polypropylene. 27. A biocidal cleaning device according to any one of claims 15-21 wherein the substrate is sponge or a synthetic equivalent. 28. A biocidal cleaning device according to any one of claims 15-21 wherein the substrate is paper. 29. A biocidal cleaning device according to any one of claims 15-21 wherein the substrate is woven textile. A method of making a biocidal cleaning device comprising the steps of: combining a biocidal concentrate according to any one of claims 1 to 14 with a binding agent; 173aup00.docCmW -19- contacting the resultant formulation with a substrate; and binding the formulation to the substrate with binding means. 31. A method according to claim 30 wherein said binding means is in the form of a heat treatment. 32. A method of making a biocidal cleaning device according to claim 31 wherein the heat treatment is carried out by a steam heated drum. 33. A method of making a biocidal cleaning device according to claim 31 wherein the heat treatment is applied by infra red means. 10 34. A method according to claim 30 wherein the binding means is in the form of UV *o *or visible light. 35. A method of making a biocidal cleaning device according to any one of claims 30-34 wherein the binding agent is a polymer latex formulation. 36. A method of making a biocidal cleaning device according to any one of claims 15 30-34 wherein the binding agent is acrylate. 37. A method of making a biocidal cleaning device according to any one of claims 30-36 wherein the substrate is selected from the group comprising cloth, sponge or a synthetic equivalent, paper and woven textiles. 38. A method of making a biocidal cleaning device according to any one of claims 30-37 wherein the substrate is cloth. 39. Biocidal plastic material incorporating a biocidal concentrate according to any one of claims 1-14. I73aupOO.doIC/MW PCT/AU98/00984 Received 28 September 1999 A method of making a biocidal plastic material comprising the steps of: a) dissolving a biocidal mixture according to any one of claims 1-14 in a plasticiser; b) compounding the above formed biocide-plasticiser mixture into a polymer; and c) forming the plastic into the desired shape 41. A method of making a biocidal plastic material according to claim 40 wherein the plasticiser is a hydrocarbon. 42. A method of making a biocidal plastic material according to claim 41 wherein the plasticiser is selected from the group comprising polybutene, low density polyethylene, low density polypropylene and paraffin wax. 43. A method of making a biocidal plastic material according to claim 40 wherein the plasticiser is an ester. 44. A method of making a biocidal plastic material according to claim 43 wherein the plasticiser is selected from the group comprising dibutyl phthalate and dioctylphthalate. A method of making a biocidal plastic material according to Claim 43 wherein the plasticiser is an epoxidised vegetable oil or a blend thereof. 46. A biocidal concentrate substantially as herein described with reference to any one of the examples. 47. A biocidal cleaning device substantially as herein described with reference to any one of the examples. 48. A method of making a biocidal cleaning device substantially as herein described with reference to any one of the examples. AMENDED SHEET IPEA/AU

21564-00.DOC PCT/AU98/00984 Received 28 September 1999 21 49. A biocidal plastic material substantially as herein described with reference to any one of the examples. A method of making a biocidal plastic material substantially as herein described with reference to any one of the examples. AMENDED SHEET IPFAIAU 21564-00.DOC