AU695079B2

AU695079B2 - Filter fabric

Info

Publication number: AU695079B2
Application number: AU65760/94A
Authority: AU
Inventors: Barrie Edward Green
Original assignee: Eco Filters Ltd
Current assignee: Eco Filters Ltd
Priority date: 1993-05-01
Filing date: 1994-04-28
Publication date: 1998-08-06
Anticipated expiration: 2014-04-28
Also published as: EP0697944A1; DE69426876T2; WO1994025236A3; CA2161677C; DE69426876D1; AU6576094A; GB9309066D0; GB2277536A; GB9322488D0; EP0697944B1; GB2277536B; WO1994025236A2; CA2161677A1

Description

WO 94/25236 PCT/GB94/00905 FILTER FABRIC The invention relates to a filter fabric, and a filter assembly for use in a press mould for moulding of cementitious products.

Press moulds are used for forming cementitious products such as paving slabs by compressing a mixture of water, sand and cement whilst simultaneously removing excess water usually assisted by vacuum. The mixture may contain other constituents such as aggregate, fibres (textile or glass etc), wood, straw etc.

The mixture is placed into a chamber of the press mould and compressed between the surfaces of a static table and piston operated platen.

Normal practice is to place a filter paper between the contacting surfaces of the mixture and the table and platen. This serves to prevent particulate material from entering the press mould ducts along which extracted water is conducted and also prevents cementitious product sticking to the surfaces of the table or platen on removal of the product.

A major limitation of paper when used as a filter medium is the necessity for a fresh piece of paper to be used on each surface during each product cycle. In addition, use of paper involves subsequent removal of the paper each time the product is removed from the mould.

Repeatedly removing and destroying the paper filter after use is a labour intensive, time-consuming and expensive task.

It is therefore desirable to provide a reusable filter that would allow water to filter out from a compressed mixture of water, sand and cement M. I r i I; i 2 whilst preventing adhesion of the contacting surfaces. It is also desirable to enable the filter to be mounted for retention by the table/platen for repeated moulding of cementitious products.

The invention provides a filter fabric for use in a concrete press mould, the fabric being knit or woven, at least in part, from a hydrophobic yarn and having a fabric density which permits the passage of water therethrough but prohibits the passage of particulate material, the fabric 15 being woven or knitted so as to have a ground construction 'which provides integrity for the fabric and a plurality of surface yarns which are secured in the ground construction so as to define at least one face of the fabric which in use contacts the cementitious mixture, said surface yarns 4 20 being arranged to define closely spaced side by side floats lying flat against the ground construction to collectively define a substantially continuous flat surface for said Sface.

eQ a H:\Susnn\Keep\peci\65760-94D. I.DOC 22/06/98 L 1 I

I

3 The invention also provides a filter assembly comprising a filter fabric as above described secured about its periphery to a perforate plate adapted for detachable securance to a table or platen of a press mould.

Embodiments of the invention are now described by way of example only, with reference to the accompanying drawings, in which: Figure 1 is a side view of a press mould according to a first embodiment of the present invention; Figure 2 is a plan view of Figure 1; Figure 3 is a plan view of a filter fabric according to the first embodiment; Figure 4 is a section through III-III of Figure 3; Figure 5 is a lapping diagram for producing a warp knitted filter fabric according to the present invention; Figure 6 is a perspective view of a filter according to a second embodiment of the present invention; and Figure 7 is a side view of Figure 6.

H:\Susan\Keep\speci\65760-94-DP.1.DOC 22/06/98 L 19 I 4ii Referring to Figures 1 to 5, there is shown a a first embodiment. The filter 19 comprises a fabric which is knit or woven from a hydrophobic yarn 30 to produce a i 18

I

:i i.

4 Si 11

N

B a 1 1 )J i c1 H:\Susan\Keep\speci\6560.94-DP 1.DOC 22/06/98 -r ICIIICC------I~ WO 94/25236 PCT/GB94/00905 therethrough but prohibits the passage of particulate material such as sand or cement 17.

In the present example, the press mould is intended to produce rectilinear paving slabs. Therefore the filter fabric 19 shown in the first embodiment is generally square shaped allowing it to fit within a chamber of the press mould 10. However, it must be appreciated that any i alternative shape of filter 19 may be used in adapting it to fit a particular cross-section of chamber for moulding alternative shapes of slabs or other products.

The filter fabric 19 is preferably knitted on a raschel warp-knitting machine and is preferably a fall plate type fabric. A suitable fabric may be produced on a raschel warp-knitting machine having a 12 gauge needle bar and in which 3 guide bars are fully threaded with a hydrophobic yarn such as polypropylene yarn and arranged to undergo the following lapping motions, viz Guide bar 1 1-0/0-1 repeat Guide bar 2 1-0/2-3 repeat Guide bar 3 2-3/1-0 repeat This is illustrated in Figure A fall plate is located behind guide bar 3 and in front of guide bars 1 and 2 so that the yarns guided by bars 1 and 2 are knitted to create a ground construction and the yarns guided by guide bar 3 are not knitted but are connected to the ground construction by passing under the underlaps of the ground construction at the extremity of their movement so as to provide flat lying floats which lie on the top of the technical back of the fabric between the points of connection with the ground construction.

IL ,i Ii r r '11 8 i WO 94/25236 PCT/GB94/00905 6 When knitted on a 12 gauge machine, the hydrophobic yarn for bars 1 and 2 preferably collectively have a yarn count of about 350-650 dtex, most preferably about 500-600 dtex. In addition, the courses per inch are preferably about 28-31; more preferably about 29-30.

Typically the yarn count for bar 1 is about 170 dtex and that for bar 2 is about 420 dtex. The yarn count for bar 3 is preferably in the region of 350 to 550 dtex, and is typically about 420 dtex.

It is envisaged that the lapping motions for guide bars may be varied from those given above.

The ground construction is produced by guide bars 1 and 2 and the lapping motions may be altered to provide different densities of fabric construction by for example altering the number of courses per inch which are knitted. This can also alter the flexibility of the fabric.

It is envisaged that guide bar 2 may undergo the following alternative lapping motions, e.g. 1-0/1-2 repeat or 1-0/3-4 repeat.

It is also envisaged that this lapping motion of bar 3 may be varied in order to provide a different loop length. For example, shorter loops may be produced by a 2-1/1-0 lapping motion, or longer loops may be produced by a 3-4/1-0 or even a 4-5/1-0 lapping motion.

After knitting the fabric is preferably heat set, so that it retains its integrity when exposed to use in the press mould.

The above fabric defines a closely knit ground construction having closely spaced side-by-side floats defining a substantially continuous and :rrr4i WO 94/25236 PCT/GB94/00905 7 flat face for the fabric. The closely spaced floats enables water to pass through but which due to the closeness of the yarns acts to restrain passage of cement/sand particles therethrough. Since the yarn is hydrophobic it is not wetted by the water and so on release of the mould parts the yarn is able to leave the surface of the compacted cement/sand f mixture without wetted particles sticking thereto.

On separation the floats tend to be pulled from the surface of the fabric, and since the floats are secured at both ends and not in their middle the centre of the floats tends to lift and thereby enables separation from the surface of the compacted cement/sand mixture by a peeling action.

The length of the floats is chosen to provide the required peeling effect whilst maintaining the desired filtration effect. Preferably the loop length is in the region of 2 to 4mm, more preferably about 3mm. In order to assist release of the loops from the pressed concrete, the yarn forming the loops is preferably smooth walled e.g. a flat yarn.

The ground construction is preferably knit in such a manner as to provide a relatively flexible material which on separation yields in the centre of the fabric and thereby provides a macro peeling effect across the face of the fabric.

Preferably the hydrophobic yarn used in producing the fabric is a non-textured yarn.

The filter fabric 19 of the first embodiment is adapted for mounting on a metal perforate plate 14, adapted for detachable securance to the table 12 and platen 11.

r l---rl WO 94/25236 PCTIGB94/00905 8 The fabric 19 is bounded about its periphery with an integral band 32 which, as shown, has been folded to overlie the remainder of the fabric. The corners of the folded over band 32 are preferably cut to define mitre joints. The band 32 is of a width and is formed by fusing the heat meltable yarn of the fabric 19 to form a smooth i imperforate surface. A band of an adhesive in the form of a double-sided adhesive tape 22 is applied to the band 32. A strong bond is possible due to the smooth surface of band 32 and also the adhesive is shielded from i the concrete due to the imperforate nature of the band 32.

Prior to mounting filter fabric 19 to plate 14 preferably a sponge i layer 41, for example, of a porous foam plastics material, is placed between the fabric 19 and the plate 14. Preferably the size of the foam Slayer 41 is such that it lies within the inner boundary of edges 45 (Figures 15 3,5) and is also of a thickness that, on compression, it has substantially the Ssame thickness as the thickness of band 32. In this way the face of the fabric is substantially flat over its entire length and width defined between the exterior fold 33 when under compression.

The sponge layer 41 is compressible and is capable of absorbing water. When the platen 11 compresses the mixture 17 onto table 12 the sponge layer 41 compresses flat and conveys water passed through the fabric 19 to exit ports 16,16'. As the platen 11 decompresses the sponge layers 41 expand and this helps to draw in surplus water that remains resident at the contacting surface of the filter 19 and compressed mixture 17 and facilitates separation.

It is envisaged however that the sponge layer 41 may be omitted or may extend inbetween the folded over band 32 and the remainder of the fabric 19.

WO 94/25236 PCT/GB94/00905 9 When applied to plate 14, it will be appreciated that the edges of the filter 19 defined by fold 33 can be substantially contiguous with the edges of the plate 14 and thereby present a filter which extends across the full width and length of plate 14. Water is able to escape at the edges of the filter 19 by passage through the fabric underlying the folded over band 32.

Referring to Figures 6 and 7 there is shown a filter 19' for use in a concrete press mould 10 as with the first embodiment.

The filter 19' comprises a fabric 19", having a knitted or woven structure substantially the same as that of the first embodiment, adiapted for mounting on a mount 2. Preferably the mount 2 is made of a relatively thin plastics sheet such as polypropylene sheet having, inter alia, flexibility and hydrophobic properties. The thickness of the mount 2 preferably varies in proportion to the area of sides 8, 9, for example a range of area in the order of about 150mm 2 to 400mm 2 may result in a range of thickness in the order of about 1.5mm to 3mm. A plastics material such as polypropylene is substantially resistive to compressive deformation which results in good recovery after compression in the press mould The mount 2 has a pluraltiy of apertures 2' formed therein to allow the release of water from the mixture 17 under compression in the press i 25 mould 10. Preferably the apertures 2' have a range in diameter in the order of about 1mm to 5mm and the density of apertures 2' also varies according to their size, for example in the order of about 2/cm 2 to 5/cm 2 '1 In the embodiment shown the sponge layer 41 is dispensed with and the filter fabric 19" directly covers one side of the mount 2. The filter EL WO 94/25236 PCT/GB94/00905 fabric 19" is wrapped around one side 8 of the mount 2 and over the edges 7 to leave overlapping marginal portions 5 which are folded over and adhered to the opposite side 9.

The filter fabric 19" is adehered to the opposite side 9 of the mount 2 preferably by means of an adhesive layer (not shown), for example double-sided adhesive tape, between the adjacent overlapping marginal portions 5 of the filter fabric 19" and the mount 2. Preferably the fabric about the marginal portions 5 of the filter 19' is then heat fused to bor: the fabric to the mount 2 followed by heat fusing the edges 7 to accurately size the mount 2 to a dimension providing a snug fit for the filter 19.. in the chamber 40 of the press mould 10 in order to prevent wear about the edges 7 when the filter 19' is in use.

'he filter 19' is adhered to the surface of the table 12 or platen 11 of the press mould 10 preferably by means of double-sided adhesive tape 22' applied between a compression surface of the table 12 or platen 11 and the opposite side 9 of the filter 19'. The double-sided adhesive tape 22' may be applied as continuous elongate bands on the opposite side 9 or preferably as a plurality of individual blocks as shown in Figures 6 and 7.

i

J

As an alternative to using a fall plate warp knitting machine a similar fabric to the fabric of the two embodiments discussed (above) may be formed on a warp knitting machine not using a fall plate. Alternative 25 ground fabrics can be knitted in the following way: a) Using one, or a combination of, yarns preferably of count dtex to 600 dtex; b) Using a machine preferably between 12 and 28 gauge.

Two examples for notation for the ground construction would be: i) Guide bar 2 0-1/1-0 repeat i j WO 94/25236 PCT/GB94/00905 11 Guide bar 3 0-0/2-2 repeat; or Sii) Guide bar 2 0-1/1-0 repeat I Guide bar 3 0-1/3-2 repeat To produce the loops shown a hydrophobic yarn is laid on top of i 5 either of these ground fabric constructions, or other similar constructions, a comparable fabric can be formed. For example, using guide bar 1 or a 12-guage machine, the following lapping motions may be possible 0-1/3-2 or 1-0/2-3 lapping motion on a 12 gauge machine. However, for finer gauge machines, longer throws are required to form the preferred loop length in the region of 2mm to 4mm, more preferably 3mm.

Claims

1. Afilter fabric for use in a concrete press mould, the fabric being knit or woven, at least in part, from a hydrophobic yarn and having a fabric density which permits the passage of water therethrough but prohibits the passage of particulate material, the fabric being woven or Sknitted so as to have a ground construction which provides integrity.for the fabric and a plurality of surface yarns which are secured in the ground construction so as to define at least one face of the fabric which in use S contacts the cementitious mixture, said surface yarns being arranged to define closely spaced side by side floats lying flat against the ground construction to collectively define a substantially continuous flat surface for said face,

2. A fabric according to Claim 1 wherein the floats are of a length SI I15 which enables the floats to peel away from the surface of the pressed concrete. I;

3. A fabric according to Claim 1 wherein, at least the surface yarns are Shydrophobic. i 4. A fabric according to Claim 1 or 2 wherein the ground construction i is constructed to be flexible to enable it to peel away from the surface of the pressed concrete. 25 5. A fabric according to Claim 1 wherein the fabric is warp knitted, the ground construction being a two bar knitted structure wherein the yarn counts for both bars collectively range between 350-650 dtex.

6. A fabric according to Claim 5 wherein the yarn count for the surface yarn is between 350-550 dtex. 13

7. A fabric according to Claim 5 or 6 wherein the yarn count for the first bar is about 170 dtex and the yarn count for the second bar is about 420 dtex.

8. A fabric according to Claim 5 or 6 wherein the ground construction comprises a knitted fabric produced by the first bar undergoing a 1-0/0-1 repeat lapping motion.

9. A fabric according to Claim 8 wherein the ground construction comprises a knitted fabric produced by the second bar undergoing either a 1-0/2-3 repeat, or a 1-0/1-2 repeat or a 1-0/3-4 repeat lapping motion. A fabric according to Claim 9 wherein the flat lying floats are I9 produced by a third bar undergoing either a 2-3/1-0 repeat or 2-1/1-0 15 repeat or a 3-4/1-0 repeat or a 4-5/1-0 repeat lapping motion. S11. A fabric according to Claim I wherein the flat lying floats have a length between 2 to 4 mm.

12. A fabric according to Claim 11 wherein the flat lying floats have a length of about 3 mm.

13. A filter fabric substantially as herein described with reference to an as illustrated in Figures I and 3 to 5 of the accompanying drawings.

14. A filter assembly comprising a filter fabric according to Claim 1 secured about its periphery to a perforate plate adapted for detachable securance to a table or platen of a press mould. An assembly according to Claim 14 wherein the periphery of the i. 14 fabric is defined by a folded edging which is secured to the plate, the folded edging comprising a continuous smooth surfaced band formed by fusing the knit or weave structure.

16. An assembly according to Claim 15 wherein the fabric is located on a front face of the plate and the peripheral band is located on and attached to the rear face of the plate.

17. An assembly according to Claim 16 wherein the band is secured to the plate by adhesive.

18. A filter assembly according to claim 14 substantially as described with reference to and as illustrated in the accompanying drawings. Dated this 22nd day of June 1998 BARRIE EDWARD GREEN By their Patent Attorneys GRIFFITH HACK Fellows Institute of Patent Attorneys of Australia t