AU616700B2 - A catalyst and process for production of hydrocarbons - Google Patents

Description

6 16 7 0 0 OPI DATE 23/05/89 1 PCT AOJP DATE 29/06/89 APPLE ID 25446 88 PCT NUMBER PCT/N088/00081 INTERNATIONAL APPLICATION PUBLISHED UNDER THE PATENT COOPERATION TREATY (PCT) (51) International Patent Classification 4 B01J 23/84, C07C 1/04 (11) International Publication Number: A (43) International Publication Date: WO 89/ 03725 5 May 1989 (05.05.89) (21) International Application Number: PCT/NO8 (22) International Filing Date: 24 October 1988 (2 (31) Priority Application Number: 8/00081 (74) Agent: LORENTZEN, Geir, Den norske stats oljeselskap a.s, Postboks 300, Forus, N-4001 Stavanger ,4.10.88) (NO).

113,095 (81) Designated States: AU, BR, FI, JP, KR.

(32) Priority Date: (33) Priority Country: 23 October 1987 (23.10.87) Published With international search report.

(71) Applicant: DEN NORSKE STATS OLJESELSKAP A.S [NO/NO]; Postboks 300, Forus, N-4001 Stavanger

(NO).

(72) Inventors: GOODWIN, James, Jr. 24 Timberline Court, Pittsburgh, PA 15217 ERI, Sigrid Venusveien 30E, N-7000 Trondheim MARCELIN, George 5853 Hobart Street, Pittsburgh, PA 15217 RIIS, Trygve Holtegt. 8, N-0259 Oslo 2 (NO).

(54) Title: A CATALYST AND PROCESS FOR PRODUCTION OF HYDROCARBONS Effect of Rhenium on CO Conversion Catalysts Containing 12% Cobalt An- /o 00 A1 2 0 3 S10 2 ,i ii i Rhenium Content, wt (57) Abstract A process for converting synthesis gas composed of hydrogen and carbon monoxide to hydrocarbons and a catalyst for the same. The process includes the step of contacting at reaction conditions a synthesis gas feed to a catalyst which includes cobalt in catalytically active amounts up to about 60 wt of the catalyst and rhenium in catalytically active amounts of about 0.5 to 50 wt of the cobalt content of the catalyst supported on alumina. An alkali metal promoter and further a metal oxide promoter may be added.

i I j:Ir .O 89/03725 PCT/N088/00081 A CATALYST AND PROCESS FOR PRODUCTION OF HYDROCARBONS TECHNICAL FIELD The present invention relates to a process and a catalyst for converting synthesis gas to hydrocarbons, and more particularly to a process using a catalyst comprising cobalt and rhenium on an alumina support and the catalyst as such.

BACKGROUND ART The reaction to convert carbon monoxide and hydrogen mixtures (defined herein as synthesis gas or syngas) to higher hydrocarbons over metallic catalysts has been known since the turn of the centurv. This reaction is commonly referred to as the Fischer-Tropsch or or F-T synthesis. During World War II, Germany exploited a process employing the F-T synthesis for the production of gasoline and other hydrocarbon products. By 1944 a total of nine F-T plants were operating in Germany. The German process used primarily a catalyst composed of cobalt, magnesium oxide, thorium oxide and kieseluhr, in the relative proportions of 100:5:8:200.

Later, most of the thoria was replaced by magnesia, primarily for economic reasons. Currentlv, commercial Fischer- Tropsch plants are operating in South Africa. These plants use a process employing a precipitated iron-based catalyst which contains various promoters to imorove the stability and product distribution.

The common F-T catalvsts are nickel, cobalt and iron. Nickel was probably the first substance to be recognized as capable of catalyzing the reaction of syngas to hydrocarbons, producing mainly methane (see, for example, "The Fischer- Tropsch Synthesis" by R.B. Anderson, Academic Press (1984), SUBSTITUTE SHEET WO 89/03725 PCT/N088/00081 Particle Diameter, microns Weight of Sample 3 WO 89/03725 PCT/N088/0008! S2 Iron and cobalt are able to produce longer chain length hydrocarbons and are thus preferred as catalysts for the production of liquid hydrocarbons. However, other metals are also capable of catalyzing the F-T synthesis. Ruthenium is a very active catalyst for the formation of hydrocarbons from syngas. Its activity at low temperatures is higher than that of iron, cobalt or nickel, and it produces a high proportion of heavy hydrocarbons. At high pressures, it produces a high proportion of high molecular weight wax. Osmium has bee found to be moderately active, while platinum, palladium and iridium exhibit low activities (see Pichler, "Advances in Catalysis", vol. IV, Academic Press, N.Y., 1952). Other metals which are active, such as rhodium, yield high percentages of oxygenated materials (Ichikawa, Chemtech, 6, 74 (1982)). Other metals that have been investigated include rhenium, molybdenum and chromium, but these exhibit very low activities with most of the product being methane.

Various combinations of metals can also be used for synthesis. Doping cobalt catalysts with nickel causes and increase in methane production during F-T synthesis (see "Catalysis", vol. IV, Reinhold Publishing Co,, (1956), p.29) In U.S.

Patent 4,088,671 to T.P. Kobylinski, entitled "Conversion of Synthesis Gas Using a Cobalt-Ruthenium Catalyst", the addition of small amounts of ruthenium to cobalt is shown to result in an active F-T synthesis catalyst with a low selectivity to methane. Thus, these references teach that the combination of two or more metals can result in an active F-T catalyst. In general, the catalysts of these teachings have activities and selectivities which are within the ranges of the individual components.

Combinations of metals with certain oxide supports have also been reported to result in an improved hydrocarbon yield during F-T synthesis, probably due to an increase in the surface area of the active metal. The use of titania to support cobalt or cobalt-thoria is taught in U.S. Patent SUbeSTTUTE SHEET

S"

i 1 WWwa- WO 89/03725 PCT/N 88/00081 4,595,703, entitled "Hydrocarbons from Synthesis Gas". In this case the support serves to increase the activity of the metal(s) toward hydrocarbon formation.In fact, titania belong to a class of metal oxides known to exhibit strong metal-support interactions and, as such, has been reported to give improved F-T activity for a number of metals (see, for example, S.J. Tauster et al, Science, 211, 1121 (1981)).

Combinations of titania and two or more metals have also been shown to yield improved F-T activity. In U.S. Patent 4,568,663, entitled "Cobalt Catalysts In the Conversion of Methanol to Hydrocarbons and for Fischer-Tropsch Synthesis", combinations of cobalt, rhenium and thoria and cobalt and rhenium supported on titania are claimed useful for the production of hydrocarbons from methanol or synthesis gas.

This patent also indicates that similar improvements in activity can be obtained when cobalt-rhenium or cobaltrhenium-thoria is compounded with other inorganic oxides.

However, titania is the only support specifically discussed.

The typical improvement in activity gained by promotion of cobalt metal supported on titania with rhenium is less than a factor of 2. We have found that the addition of rhenium to cobalt metal supported on a number of other common supports results in similar improvements in activity.

The only other examples in the literature of catalysts involving mixtures of cobalt and rhenium refer to completely different chemical reactions. For example, in Soviet Union Patent 610558, a catalyst composed of cobalt and rhenium supported on alumina is taught to result in improved performance for the steam reforming of hydrocarbons. Steam reforming of hydrocarbons is a process completely different from hydrocarbon production via F-T synthesis and is believed to proceed by a completely different mechanism. Although some steam reforming catalysts can convert synthesis gas to hydrocarbons, such catalysts are not selective for the production of high carbonnumber hydrocarbons (C 3 and above) during conversion of synthesis gas. In fact, most commonly used steam reforming catalysts contain nickel as their SUBSTITUTE SHEET t r $i i_ WO 89/03725 PCT/N088/00081 active metal, and nickel produces mostly methane when used for syngas conversion.

DISCLOSURE OF INVENTION SI It has been found in accordance with the present invention that synthesis gas comprising hydrogen and carbon monoxide can be converted to liquid hydrocarbons by using catalyst and a process employing a catalyst consisting of cobalt and rhenium suppcrted on alumina andmprom-ted with an alkali. As used herein, alkali refers to one or more of the elements lithium, sodium, potassium, rubidium, and cesium of group IA of the periodic table. The catalyst preferably contains from about 5 to 60 cobalt, has a rhenium content between and 50 of the amount of cobalt, and an alkali content between 0.5 and 5 atom of the amount of cobalt. The alumina preferably is gamma alumina.

It has been found that the addition of small amounts of rhenium to catalysts consisting predominantly of cobalt supported on alumina unexpectedly results in greatly enhanced activity of this catalyst for hydrocarbon production from syngas. This is surprising in light of the fact that rhenium supported on alumina show very low activity, with most of the product being methane. Furthermore, rhenium addition to cobalt supported on supports other than alumina results in catalysts with much lower activity levels. In addition, the more active cobalt plus rhenium catalyst maintains the high selectivity to higher hydrocarbons and the low selectivity to methane found with an aluminasupported 4 cobalt catalyst. It has also been found that the addition of small amounts of an alkali to these catalysts serves to increase the average carbon number of the products produced during F-T synthesis. Both the high activity and the low methane production of cobalt-rhenium on alumina are unexpected in light of the facts that rhenium shows very lo; activity for F-T synthesis, the main products from F-T Ssynthesis over a rhenium catalyst are methane and carbon SUBSTITUTE SHEET \fk h0 cl ._i dioxide, and the use of alumina as a support for catalysts containing only cobalt results in no, or at best only a slight, increase in activity compared to the use of cobalt on other supports. Thus, for reasons not fully understood, the combination of cobalt and rhenium and optionally an alkali supported on alumina results in a catalyst which is significantly more active than either of the two individual metals supported on alumina or the combination of the two metals supported on other inorganic supports, such as silica, magnesia, silicaalumina, titania, chromia or zirconia. Furthermore, the product distribution with a high selectivity to C 2 hydrocarbons and low selectivity to methane and carbon dioxide would not have been predicted based on the known product distribution from rhenium catalysts. The addition of an alkali to the catalyst serves to increase the average carbon number of the product. This is advantageous in situations where the market value of the lighter products is lower than that of the heavier products.

The process includes the step of contacting a synthesis gas feed comprised of hydrogen and carbon monoxide over a catalyst comprised of cobalt and rhenium composited on an alumina support wherein rhenium is present in relatively lesser amount than the cobalt content of the catalyst.

The reaction conditions preferably include a temperature in the range of about 150 to 300'C, a pressure in the range of about atmospheric to 100 atmospheres and a gaseous hourly space velocity, based on the total amount of synthesis gas fee, in the range of about 100 or 20,000 cm 3 of gas per gram of catalyst per hour. The catalyst 910812,dbdaLO74,25446.res,5 1* 1i -6used in the process of this invention preferably contains from about 5 to 60% cobalt and has a rhenium content between 0.5 and 50% of the amount of cobalt. The alumina preferably is gamma alumina.

BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a graph showing the effect of rhenium content on CO conversion using catalysts containing 12% cobalt; Figure 2 is a graph showing the effect on CO conversion of adding rhenium to catalysts containing various amounts of cobalt on an alumina support; 910812,dbda074,25446.res,6 -j PCT/N088/00081 I NY 89/03725 7 Figure 3 is a typical graph of CO conversion as a function of time on stream for the process of this invention when operated using slurry reaction; and Figure 4 is a gas chromatagram of a typical middle distillate and heavier liquid product from the process of this invention.

Figure 5 is a graph showing the effect of potassium to cobalt ratio on the Schulz-Flory N of the product using the catalysts of this invention; and Figure 6 is a graph showing the effect of potassium to cobalt ratio on CO conversion when using the catalysts of this invention.

MODES FOR CARRYING OUT THE INVENTION The catalyst of the present invention comprises as the active catalytic ingredients cobalt and rhenium supported on alumina with rhenium present in a relatively smaller amount than cobalt. Optionally, the catalyst can also comprise an alkali metal, that is an element from Group IA of the Periodic Table.

The process of the present invention comprises contacting at reaction conditions a feed comprised of hydrogen and carbon monoxide over a catalyst which comprises as the active catalytic ingredients cobalt and rhenium supported on alumina with rhenium present in a relatively smaller amount than cobalt.

Operating conditions suitable for use in the process of this invention are reaction temperature between 150 and 300 C, preferably between 180 and 280 0 C, and more preferably between 190 and 250°C; a total pressure from atmospheric to around 100 atmospheres, preferably between 1 and 40 atmoFpheres, and more preferably between 1 and 30 atmospheres; SUBSTITUTE SHEET 1 a WO 89/03725 PCT/N088/00081 8 and a gaseous hourly space velocity, based on the total amount of synthesis gas feed, between 100 and 20.000 cm 3 of gas per gram of catalyst per hour, and preferably from 100 to 10.000 cm3/g/h, where gaseous hourly space velocity is defined as the volume of gts (measured at standard temperature and pressure) fed per unit weight of catalyst per hour.

The catalyst used in the process of this invention has been found to be highly active for the conversion of synthesis gas, a mixture of hydrogen and carbon monoxide, into a mixture of predominantly paraffinic hydrocarbons. As indicated above, it has long been known that cobalt is an active catalyst for the F-T syntheis. It is also known that the addition of rhenium to a cobalt catalyst supported on titania gives improved activity, even if rhenium by itself shows very low activity for F-T synthesis and produces methane as the main product. Surprisingly, we have found that the choice of support for the cobalt plus rhenium catalyst is very critical, and that the addition of rhenium to an alumina-supported cobalt catalyst gives a much higher improvement in activity than addition of rhenium to cobalt supported on other inorganic oxides. Also, the alkali increases the average carbon number of the product.

The cobalt is added to the alumina support in some amount up to about 60 wt% of the catalyst, including cobalt. Preferably, amounts between 5 and 45 wt% are used; and more preferably between 10 and 42 wt%. The content of rhenium is between about 0.5 and 50 wt% of the cobalt content; preferably between 1 and 30 wt%; and more preferably from about 2 to around 20 wt%. The content of alkali is between about and 5 atom of the cobalt content.

In addition to cobalt, rhenium and alkali, it is beneficial to include a small amount of a metal oxide promoter in an amount between about 0.1 and 5 wt%, and more preferably between about 0.2 and 2 wt%, based on the weight of the complete catalyst. The promoter is suitably chosen frorm- SUBSTITUTE

SHEET

WO 89/03725 PCT/N 088/00081 elements in groups IIIB, IVB or VB of the periodic chart, the lanthanides and the actinides. The promoter oxide can be chosen from, for example, Sc03, Y 2 0 3 La 2

O

3 Ce 2

O

3 ,Pr 2 0 3 ZrO 2 Ac 2 0 3 PaO 2 Nd 2 0 3 CeO 2 V20 or Nb205. The most preferable oxide is La 2 0 3 or a mixture of lanthanides, rich in lanthanum. Oxides like MnO or MgO can also be included.

While not essential, the use of these metal oxides is common in the art, since they are believed to promote the production of products with higher boiling points, while maintaining or improving catalytic activity. However, the catalyst is highly active and selective without the addition of one or more these metal oxide promoters.

The catalytically active metals, the alkali, and the promoter metal oxide, if present, are distended on alumina.

Although other supports may be used, it has been found, for example, that silica, titania, chromia, magnesia, silicaalumina and zirconia produce catalysts with much lower activities.

To be most effective when used as a support, alumina should be characterized by low acidity, high surface area, and high purity. These properties are se:ssin order to enable the catalyst to have high activity and a low deactivation rate, and to-produce high molecular weight hydrocarbon products. The surface area of the alurmina support is at least, and preferably greater than, about 100 m 2/q; and more preferably greater than 150 m2/g. The pore volume is at least, and preferably greater than, about 0.3 cm g. The catalyst support must be of high purity. That is, the content of elements, e.g. sulfur and phosphorous, that have a deleterious effect on catalytic activity must be kept low. The sulfur content of the catalyst support should be kept below 100 ppm and preferably below 50 ppm. Although gamma alumina has generally been used and is preferred, a number of alumina structures, if prepared properly, car meet these conditions c Lly and are s u itable supports. For example, eta-alumina, SUBSTITUTE SHEET y WO 89/03725 PCT/N088/00081 boehmite and pseudo-boehmite can all be used as supports.

The method of depositing the active metals, the alkali, and the promoter oxide on the alumina support is not critical, and can be chosen from various methods well known to those skilled in the art. One suitable method that has been employed is known as incipient wetness impregnation. In this method the metal salts are dissolved in an amount of a suitable solvent just sufficient to fill the pores of the catalyst. In another method, the metal oxides or hydroxides are coprecipitated from an aqueous solution by adding a precipitating agent. In still another method, the metal salts are mixed with the wet support in a suitable blender to obtain a substantially homogeneous mixture. In the present invention, if incipient wetness impregnation is used, the catalytically active metals and the alkali can be deposited on the support using an aqueous or an organic solution. Suitable organic solvents include, for example, acetone, methanol, ethanol, dimethyl formamide, diethyl ether, cyclohexane, xylene and tetrahydrofuran. Aqueous impregnation is preferred when Co(NO3)2 is used as the salt, while an organic solvent is the preferred solvent when the catalyst is prepared from cobalt carbonyl.

Suitable cobalt compounds include, for example, cobalt nitrate, cobalt acetate, cobalt chloride and cobalt carbonyl, with the nitrate being the most preferable when impregnating from an aqueous solution. Suitable rhenium compounds include, for example, rhenium oxide, rhenium chloride and perrhenic acid. Perrhenic acid is the preferred compound when preparing a catalyst using an aqueous solution.

Suitable alkali salts for incorporating the alkali into the catalyst include, for example, the nitrates, chlorides, carbonates, and hydroxides. The metal oxide oxide promoter can suitably be incorporated into the catalyst in the form, for examnple, of the nitrate or chloride.

SUBSTITUTE

SHEET

S WO 89/03725 PCT/N088/00081 24 As can be seen from comparison of the results in Table 1

K

I

d '0 89/03725 PCT/N088/00081 After aqueous impregnation, the catalyst is dried at 110 to 120 0 C for 3 to 6 hours. When impregnating from organic solvents, the catalyst is preferably first dried in a rotary evaporator apparatus at 50 to 60 0 C under low pressure, then dried at 110 to 120 C for several hours longer.

The dried catalyst is calcined under flowing air by slowly increasing the temperature to an upper limit of between 200 and 500 0 C, preferably between 250 and 350 0 C. The rate of temperature increase is preferably between 0.5 and 2 0 C per minute, and the catalyst is held at the highest temperature for a period of 2 to 5 hours. The impregnation procedure is repeated as many times as necessary to obtain a catalyst with the desired metals content. Cobalt, rhenium and the promoter, if present, can be impregnated together, or in separate steps. If separate steps are used, the order of impregnating the active components can be varied.

Before use, the calcined catalyst is preferably reduced with hydrogen. This can suitably be done in flowing hydrogen at atmospheric pressure at a flow rate between 30 and 100 3 cm !min. when reducing about 2 q of catalyst. The flow rate should suitably be increased for laraer cuantities of catalyst. The temperature is increased at a rate between 0.5 and 2°C per minute from ambient to a maximum level of 250 to 450 0 C, preferably between 300 and 400 0 C, and maintained at the maximum temperature for about 6 to 24 hours, more preferably 10 to 24 hours.

After the reduction step, the catalN7sts may be oxidized and reduced before use.To carry out the oxidation step, the catalyst is treated with dilute oxygen (1-3 oxygen in nitrogen) at room temperature for a period of 1/2 to 2 hours before the temperature is increased at the same rate and to the same temperature as used during calcination. After holding the high temperature for 1 to 2 hours, air is slowly introduced, and the treatment is continued under air at the high temperature for another 1 to 4 hours. The second reduc- SUBSTITUTE

SHEET

WO 89 2 WO 89/03725 PCT/N088/00081 12 tion is carried out under the same conditions as the first reduction.

The reactor used for the synthesis of hydrocarbons from synthesis gas can be chosen from various types well known to those skilled in the art, for example, fixed bed, fluidized bed, ebullating bed or slurry. Because of the exothermic nature of the F-T reaction, the reactor must be designed with heat removal capabilities so that the desired reaction temperature can be carefully controlled. The above listed reactor types have characteristics that make them well suited for use in the process of this invention. The catalyst particle size for the fixed or ebullating bed is preferably between 0.1 and 10 mm and more preferably between 0.5 and mm. For the other types of reactors a particle size between 0.01 and 0.2 mm is preferred.

The synthesis gas used as feed to the process is a mixture of carbon monoxide and hydrogen and can be obtained from any source known to those skilled in the art, such as, for example, steam reforming of natural gas or partial oxidation of coal. The molar ratio of H2:CO is normally between 0.5 to 3:1; preferably between 1:1 to 3:1; and more preferably between 1.5:1 to 2.5:1. Carbon dioxide is not a desired feed component for use with the process of this invention, but it does not adversely affect the process or the activity of the catalyst, other than acting as a diluent. All sulfur compounds must, on the other hand, be held to very low levels in the feed, preferably below 1 ppm, because they have an adverse effect on the activity of the catalyst employed in this process.

The process of this invention is described as follows. Synthesis gas from any suitable source, as discussed previously, is fed to the process. The ratio of hydrogen to carbon monoxide in this synthesis gas may be between 1 and 3 and more preferably between 1.5 and 2.5. A highly desirable ratio is the stoichiometric ratio of H 2 to CO usace within SUBSTITUTE SHEET i 'WO 89/03725 PCT_N088000_8 13 the process, which is about 1.2 to 2.2. Providing syngas at this stoichiometric ratio results in the most efficient utilization of the syngas in the process, since neither hydrogen nor carbon monoxide is in excess. In addition to H.

and CO, the syngas may contain quantities of other gases, such as carbon dioxide, methane, and nitrogen. These gases act as diluents which may be disadvantageous for some kinds of reactor systems, while being advantageous for other reactor systems, as will be more fully discussed below. The hydrogen sulfide content of the syngas must be kept very low, preferable below 1 ppm by volume, because sulfur is a sever catalyst poison.

If not at sufficient pressure, the syngas is compressed to process pressure, which can be from atmospheric to about 100 atmospheres, preferably from 1 to 40 atmospheres, and more preferably from 1 to 30 atmospheres. Anything lower than 1 atmosphere would require operation at vacuum conditions which is not necessary and unduly expensive. The rate of reaction would decrease. Pressures greater than about 100 atmospheres would increase the cost significantly due to the increased strength of the equipment necessary to withstand high pressures. The syngas is then preheated before entering the reactcr. Because the F-T reaction is highly exothermic, it is not normally necessary to heat the feed gas all the way to reaction temperature, the final heatup taking place in the reactor itself. As discussed previously, the reactor can suitably be chosen from a variety of reactor types, the most important criterion being the ability to control carefully the temperature of the exothermic F-T reaction. The three most suitable reactor types are tubular fixed bed reactors, in which the catalyst is placed in tubes and a fluid is circulated on the outside of the tubes for heat removal, fluidized bed reactors, and slurry reactors, in which finely divided catalyst is slurried in a vehicle oil.

In these latter two reactor types, heat can be removed in a variety of ways, including increases in the sensible heat cf the feed, internal heat exchangers, and removal of a slip stream for cooling and return to the reactor.

SUBSTITUTE SHEET

:~A

WO 89/03725 PCT/N088/00081 14 Temperature in the reactor should be between 150 and 325 C, and more preferably between 180 and 280 C. The total pressure can be from atmospheres to around 100 atmospheres between 1 and 30 atmospheres. These temperature ranges are typical to Fischer-Tropsch reactions. The rate of reaction at temperatures below 150 C would be so low as to be uneconomical on a commercial scale due to the large reactor size which would be required. Where temperatures are about 325°C are employed, the selectivity to liquid hydrocarbons is so low that the process becomes economically infeasible. There are less expensive ways to make methane. Gaseous hourly space velocity (based only on the H 2 plus CO content of the 3 feed) should be between 0.1 and 20 m per kg catalyst per 3 hour and preferably between 0.1 and 10 m per kg catalyst per hour. Once the desired working temperature and pressure are determined, the space velocity is chosen to give the desired per pass conversion.

The acceptable form of the catalyst will depend upon the type of reactor being used. For tubular fixed bed reactors, the catalyst can be in the form of extrudates, pellets, spheres, granules, etc. with a nominal diameter of about to 6 mm, and preferably about 1.5 mm. For fluidized bed or slurry reactors, the catalyst should be in finely divided form. A typical analysis for a catalyst suitable for slurry reactor operation is: USTI$TUTE SHEET t WO 89/03725 PCT/N088/00081 Particle Diameter, microns Weight of Sample 0.2 5-7 7-9 1.3 9-13 13-19 1.1 19-27 27-38 3.3 38-53 5.7 53-75 15.7 75-106 25.7 106-150 26.4 150-212 13.9 212-300 3.2 For either fluidized bed or slurry operation, it is important that catalyst charge contain neither too large a fraction of large particles nor too large a fraction of small particles. A proper size consist is important for successful fluidization or suspension of the catalyst. In slurry operation, it is also important to have a proper vehicle. Normally, a fraction of the product oil will be used for this purpose. Generally, a carbon number distritation in the range from C20 to C50 is satisfactory. For startup purposes, in addition to a F-T liquid, C30 to C50 poly-alpha-olefins may be used or a highly refined, i.e. heteroatom and aromatic free, petroleum oil.

In the reactor, contact between the syngas and the catalyst results in the production of largely paraffinic hydrocarbons, along with small amounts of olefins and oxygenates. In general, part of the product will remain in the gas phase and be carried out of the reactor along with inerts and unconverted feed gas, and part of the product will form a liquid phase. The fraction of the product that is carried out in the vapor phase will depend upon the operating conditions being used.

SUBSTITUTE SHEET WO 89/03725 PCT/N088/00081 16 i In a fixed bed reactor, the liquid phase will either drain out the bottom of the catalyst tubes or else be entrained out with the offgas. In a fluidized bed reactor, operating conditions must be adjusted so that the amount of liquid product is very low. Otherwise, the product builds upon the 'I catalyst and destroys the fluidization properties of the catalyst. In the slurry reactor, the liquid products will jdissolve in the vehicle oil and can be recovered by any of the techniques familiar to those skilled in the art, such as filtration, centrifugation, settling and decanting, etc.

The offgas from the reactor is cooled to condense liquid products (both hydrocarbons and water, which is produced as a byproduct). This is typically done in a series of steps at progressively lower temperatures. This is necessary to prevent wax from solidifying and causing plugging. After the final cooler/separator, additional hydrocarbons can be recovered by absorption or adsorption, if desired.

Per pass conversion in the reactor can vary from 10 to over preferably from 40 to over 90 If once through conversion is not sufficiently high, the offgas, after product recovery and bleeding off of a slip stream to prevent inerts from building up in the system, can be mixed with the fresh syngas feed and recycled to the reactor.

As mentioned above, the syngas may contain some quantity of nitrogen. For fixed bed operation, this may be undersirable, I since dilution with nitrogen reduces the partial pressure of reactive gases and increases the pressure drop. However, for fluidized bed and slurry reactor operation, the nitrogen may be beneficial by providing additional mixing energy and helping keep the catalyst suspended. In these types of reactors, pressure drop is not a strong function of flow rate.

I:|

As'a final step in the process, all the liquid products may be combined. If desired they may be stabilized by distillaticr to remove highly volatile components. The SUBSTITUTE

SHEET

WO 89/03725 PCT/N088/00081 il rril, 4 1 4- :I 1 .3 1- I WO 89/03725 PCT/N088/00081 17 liquid product may then be marketed as a synthetic crude or, alternatively, distilled into individual product cuts which can be marketed separately. As a further alternative, the product may be catalytically dewaxed or hydorcracked before being marketed. These latter processes can improve product properties by lowering pour point, increasing octane number, and changing boiling ranges.

The products from this process are a complicated mixture, consisting predominantly of normal paraffins, but also containing small amounts of branced chain isomers, olefins, alcohols and other oxygenated compounds. The main reaction can be illustrated by the following equation: nCO 2nH (-CH 2 nHO2 2 2 n 4 where (-CH 2 represents a straight chain hydrocarbon of carbon number n. Carbon number refers to the number of carbon atoms making up the main skeleton of the molecule. Products range in carbon number from one to 50 or higher.

In addition, with many catalysts, for example those based on iron, the water gas shift reaction is a well known side reaction: CO H 2 H2

CO

2 With the catalyst used in the process of this invention, the rate of this last reaction is usually very low. However, it is found that, even though rhenium catalysts exhibit a relatively high selectivity to carbon dioxide, the cobalt plus rhenium catalyst used in the process of this invention surprisingly does not have a higher selectivity to carbon dioxide than the cobalt only catalyst.

The hydrocarbon products from processes employing the Fischer-Tropsch synthesis are generally distributed from methane to high boiling compounds according to the so called SUBSTITUTE SHEET

I

WO 89/03725 PCT/NO88/0001 18 Schulz-Flory distribution, well known to those skilled in the art. The Schulz-Flory distribution is expressed mathematically by the Schulz-Flory equation.

81 W. (I 2 i-i 1 where i represents carbon number,o( is the Schulz-Flory distribution factor which represents the ratio of the rate of chain propagation to the rate of chain propagation plus the rate of chain termination, and W i represents the weight fraction of product of carbon number i. This equation shows that an increased o results in a higher average carbon number of the products. Highera values are desirable when heavier products, such as diesel fuel, are relatively more valuable than lighter products, such as naphtha.

The products produced by the catalyst and the process of this invention generally follow the Schulz-Flory distribution, except that the yield of methane is usually higher than expected from this distribution. This indicates that methane is apparently produced by an additional mechanism.

Catalysts promoted with alkali in the manner prescribed in this invention produce a product having a higher average carbon numoer than the products from non-alkali promoted catalysts. That is, the Schulz-Flory X for the product from an alkali promoted catalyst is higher than for a non-alkali promoted catalyst.

It is well known, and also shown in one of the following examples, that rhenium alone is a low activity catalyst for Fischer-Tropsch synthesis producing a product which is predominantly methane. On the other hand, cobalt is a well known catalyst for producing higher carbon number hydrocarbons. In U.S. Patent No. 4,568,663, it has been shown that adding small amounts of rhenium to cobalt supported on titania improves the catalytic activity. In the present invention, it has been found that the hydrocarbon yield SUBSTITUTE SHEET p Ia WO~~ 89 032 PC/08/0 I WO 89/03725 PCT/N088/00081 19 obtained by adding rhenium is surprisingly much larger for an alumina supported cobalt catalyst than that obtained from cobalt and rhenium on several other inorganic supports. The improved activity and increased selectivity to heavier hydrocarbons is followed by no deleterious effect on the selectivity to methane.

The catalyst and the process of this invention is further described in the following examples.

EXPERIMENTAL WORK The following examples describe the preparation of various catalysts and the results obtained from testing these catalysts for conversion of synthesis gas into hydrocarbons.

Before being tested, each catalyst was given a pretreatment consisting of reduction by passing hydrogen over the catalyst at a rate of 3000 cm3 /g/h while heating the catalyst at a rate of 1 C/min to 350 0 C and maintaining this temperature for 10 hours. In all the process tests except for Example 42, synthesis gas consisting of 33 vol% carbon monoxide and 67 vol% hydrogen was passed over 0.5 g of the catalyst in a small fixed bed reactor at atmospheric pressure at temperature of 185, 195 and 205 0 C according to the following schedule: 9 hr. 50 min. at 195°C 4 hr. 20 min. at 205°C 4 hr. 30 min. at 185°C 9 hr. 50 min. at 195°C The flow rate of synthesis gas was 1680 cm 3 /g of catalyst/h.

Products from the reactor were sent to a gas chromatograph for analysis. Catalysts were comparee based on the results over the period from 10 to 30 hours on stream.

SUBSTITUTE SHEET WO 89/03725 PCT/N088/00081 EXAMPLE 1 Catalyst Containing Cobalt But No Rhenium This example describes the preparation of a control cobalt catalysc which was used for comparative purposes. This catalyst was prepared as follows: A solution was prepared by dissolving 17.03 g of cobalt nitrate, Co(No 3 2 .6H 2 0, and 0.76 g of mixed rare earth nitrate, RE(NO3) 3 where RE stands for rare earth with a composition of 66 La203, 24 Nd203, 8.2 Pr 6 0 1 0.7 CeO 2 and 1.1 other oxides (Molycorp 5247), in 30 ml of distilled water. The total solution was added with stirring to 25 g of Ketjen CK300 gamma-alumina which had been calcined 10 hours at 500 C. The prepared catalyst was then dried for 5 hours in an oven aL a temperature of 115 C. The dried catalyst was then calcined in air by raising its temperature at a heating rate of l°C/minute to 3000C and holding at this temperature for 2 hours. The finished catalyst contained 12 wt% cobalt and 1 wt% rare earth oxide with the remainder being alumina. This catalyst is referred to as preparation in Table 1. The above procedure was repeated to produce preparation catalyst in Table 1.

The results of the tests with this catalyst are shown in Table 1. In this and the following tables, selectivity is defined as the percent of the carbon monoxide converted that goes to the indicated product.

SUBTITUTE SHEET SUBSTITUTE SHEET 1 WO 89/03725 PCT/N088/00081 Table X WO 89/03725 PCT/N088/00081 21 Table 1 C2+ Select ivi ty CH 4 Selectivity CO 2 Selectivity Temp. Preparation 0oC Conversion 185 195 205 91. 1 91.8 90.0 90.2 87.7 86.7 7.2 7.1 8.9 9.0 11. 3 12.4 1.7 1.1 1. 1 0. 8 0.9 This example shows that a cobalt catalyst ei:hibits good selectivity to ethane and longer chain lengrth hydrocarbons and low selectivity to methane and carbon dioxide.

EXAMPLE 2 Catalyst Contaning Rhenium But No Cobalt This example describes a rhenium catalyst prepared for comn- -parative purposes. The procedure employed was the same as for Example 1 except that the solution contained 0.33 g of perrhenic acid, HReO. as 82.5 aqueous solution, and 0.54 g of rare earth nitrate to make 24 ml of solution which then was added to 20 g of calcined alumina. The finished catalyst contained 1 wt% rhenium and 1 wt% rare earth oxide with the remainder being alumina.

The results of the tests with the catalyst of Example 2 arp shown in Table !I.

SUBSTITUTE SHEET ~1j j"I WO 89/03725 PCT/N088/00081 22 Table II C2+ CH 4

CO

2 Temp.

OC

Conversion Selectivity Selectivity Selectivity 185 195 205 0.3 0.3 0.3 EXAMPLE 3 Catalyst Containinq Rhenium But No Cobalt Repetition of the procedure from Example 2, except that 0.83 g of perrhenic acid were used, gave a catalyst containing 4 wt% rhenium. The results of the tests with the catalyst of Example 3 are shown in Table III.

Table III C2+ CH 4

CO

2 Temp. Conversion Selectivity Selectivity Selectivity °C 195 205 0.3 0.3 0.3 The results from Example 2 and 3 shoe that catalysts containing rhenium but no cobalt have very low activity for producing desirable liquid hydrocarbons from synthesis gas.

SUBSTITUTE SHEET WO 89/03725 Furthermore, about ha.

most of the hydrocarb PCT/N088/00081 If the product is carbon dioxide, and on product is methane.

EXAMPLES 4 THROUGH 11 Catalysts Containing Both Cobalt And Rhenium The preparation procedure of Example 1 was employed except that varying amounts of perrhenic acid were added to the solution. This produced a series of catalysts containing 12 wt% cobalt and 0.1, 0.2, 0.3, 0.5, 1.0, 2.0, 4.0, and wt% rhenium in addition to 1.0 wt% rare earth oxide.

The results of the tests with the catalysts of Example 4 through 11 at 195 C are shown in Table IV and further illustrated in Figure 1. Figure 1 shows the effect on carbon monoxide conversion of adding rhenium to catalysts containing 12 cobalt.

Table IV C2+ CH4 CO2 Example Co Re Conversion Selectivity Selecttivity Selectivity No wt% wt% 4 6 7 8 9 11 0.1 0.2 0.3 0.5 1.0 2.0 4.0 8.0 89.8 88.9 88.2 88.3 87.'7 85.7 84.7 84.5 9.6 10.4 11.0 10.9 11.4 13.3 14.2 14.2 0.6 0.7 0.8 0.8 0.9 1.1 1.3

A--

SUBSTITUTE

SHEET

WO 89/03725 PCT/N088/00081 24 i As can be seen from comparison of the results in Table 1 with Table IV and Figure 1, the addition of small amounts for rhenium to a cobalt supported on alumina catalyst significantly increases the conversion of the carbon monoxide in the feed. Levels of rhenium as low as 0.1 wt% result in approximately doubling the CO conversion. The exact level of Re for optimum activity is very important, as the rate of carbon monoxide conversion increases rapidly at low rhenium addition levels, reaches a maximum and then decreases gradually at levels greater than 1 wt% rhenium. However, even at the highest rhenium level investigated (8 a clear improvement in conversion is evident when compared to the catalyst not containing rhenium.

It is impdrtant that the increase in activity occur without a corresponding increase in either the methane or the carbon dioxide selectivities. Table IV shows that the increase in carbon monoxide conversion is not accompanied by any substantial change in either the selectivities to methane or carbon dioxide. Thus, after rhenium addition the principal reaction products are still desirable hydrocarbons.

EXAMPLES 12 THROUGH Catalysts Containing Both Cobalt And Rhenium The preparation procedure of Example 1 was employed except that varying amount of cobalt nitrate and perrhenic acid were added to the solution. This produced a series of catalysts containing from 3.0 to 40 wt% cobalt and from 0 to wt% rhenium in addition to 1.0 wt% rare earth oxide.

The results of the tests with the catalysts of Example 12 through 25 at 195 C are shown in Table V.

SUBSTITUTE

SHEET

WO 89/03725 P CTIN 088/00081 Table V C2+

CH

4

CO

2 Example Co Re Conversion Selecttivity Selectivity Selectivity No wt% wt% 12 13 14 16 17 18 19 21 22 23 24 0.0 0.25 0.0 0.5 0.0 0.75 0.0 0.5 1.0 5.0 0.0 1.0 2.0 5.0 90.7 87.2 90.0 88.2 90.0 88.1 89.3 .87.9 86.1 83.9 89.3 85.0 84.3 81.9 8.1 10.4 8.9 10.8 9.1 11.1 9.8 11.1 12.9 14.8 9.7 13.2 13. 7 15.7 1.2 2.4 1.1 0.9 0.8 0.9 1.3 1.8 2.4 The results out rhenium, going from 3 increases in in Table V show that for cobalt catalysts w'iththere is a significant increase in activity in cobalt to 6 cobalt. However, only modest activity occur from this point up to cobalt loadings of as high as 40 At a cobalt loading of 3 the addition of rhenium does not improve the catalytic activity, but the improvement upon rhenium addition is significant for higher cobalt loadings. In fact, the improvement in activity due to the addition of rhenium increases as the cobalt content increases as shown in Figure 2.

SUBSTITUTE

SHEET

WO 89/03725 PCT/N088/00081 26 EXAMPLES 26 AND 27 Cobalt/Rhenium Catalysts With Promoters To illustrate the use of promoters other than rare earth oxides, the following catalysts were prepared. The preparation procedure used to prepare the catalyst of Example 8 was used except that zirconium nitrate, Zr(NO3) 4 or vanadyl oxalate, VO(C 2 0 4

H)

3 was substituted for the rare earth nitrate. The results of tests at 195°C with the catalysts of examples 26 and 27 are shown in Table VI. In addition to the promoter, these catalysts contained 12 cobalt and 1 rhenium and were supported on alumina.

Table VI C2+

CH

4 CO, 2 Example Promoter Conver- Selec- Selec- Selectivity tivity sion tivitv 26 27 ZrO 2 (0.75wt%) V20 5 (0.56wt%) 87.9 89.4 11.3 9.8 0.8 0.8 EXAMPLES 28 THROUGH 41 Cobalt/Rhenium Catalysts On Other Supports For comparison with alumina, several catalysts were prepared on other supports. The preparation procedure used to prepare the catalyst of Example 8 was repeated, but without the addition of rare earth oxide. The titanium-supported catalysts were prepared on titania calcined at both 500 0

C

SUBSTITUTE

SHEET

;1i WO 89/03725 PCT/N08/00081 27 and 600 0 C. After calcination at 600 0 C, the titania is mainly in the crystalline rutile form; while after calcination at 500 0 C the anatase; rutile ratio is about 1:1. The catalysts prepared on the uitania support calcined at these two temperatures showed exactly the same catalytic activity.

The supports used were: Davison Grade 59 silica; Dequssa titania; Alpha Chemicals No. 88272 chromia; magnesia prepared by calcining Fischer basic magnesium carbonate; American Cyanamid AAA Silica-Alumina; and Alpha Chemicals 11852 zirconia (containing 2 alumina). Information on the composition of the catalysts prepared on the different supports is given in Table VII.

Table VII Example No.

Weight of Support Support q Weight of Materials in Composition Impregnating of Finished Solution, g Catalyst. wt% Co(No,) 2 HReO Co Re 4 28 Silica 29 Silica 30 Titania** 31 Titania** 32 Titania*** 33 Titania*** 34 Chromia 35 Chromia 36 Magnesia 37 Magnesia 38 Silica- Alumina 39 Silica- Alumina Zirconia 41 Zirconia 20 20 25 24.64 25 24.64 20 21.3 21.59 14.54 13.47 13.62 16.84 16.78 16.84 16.78 13.47 14.51 14.54 10.67 13.47 13.62 13.47 13.62 0.38 0.46 0.46 0.40 0.29 12 0.38 0.38 SUBSTITUTE

SHEET

28 Weight of 82.5 perrhenic acid solution.

'~Calcined at 500 0

C.

SCalcined at 600 0

C.

A series of tests was conducted to evaluate the activities of the catalysts of the above examples in converting synthesis gas into hydrocarbons. The results of the te&sts with the catalysts of Examples 28 through.41 at 195 0 C are shown in Table VIII. The results from catalysts prepared on alumina are included for comparison.

Table VIII E~:ample Cc No.

Re Support GOC 2 Conver- Selecsion tivitv

CH

4 Selectivi tV Co 2 Selectivitv 1 8 28 29 31 3 2 33 34 36 37 3CG 38 39 41 Al 20 3 12 1AlO20 33 -Sio 2 11 1 SiC 2 12 TiC 2 0 11 1 TiC,* 17 TiC., 11 1TiC 2 17 C Cr20 31 1 C r 2 0 2 MgO 0.3 1 MgC 0.3 SiC.,/A1 0 35 1 5i0 2 /Al 2 01 6 ZrO,. 4 1 ZrO 2 7 calcined at 500 0C calcined at 600 0C 90.0 87.7 90.1 88.1 87.6 86 .5 87.6 85.8 83.5 80.8 20.0 19.1 76.3 78.6 80.9 78.8 8.9 11.4 8.7 10.7 11.8 12.8 11.7 13.5 15.5 12.3 30.0 30.9 19.8 16 18.7 1 .1 0.9 1.2 1.2 0.6 0 .7 0.7 0 .7 1 .0 6.9 50.0 50.0 1 .F, 2. 8 Support Support F' WO 89/03725 PCT/N088/00081 29 The catalysts in Table VII were prepared to test the teaching that various inorganic supports are acceptable for preparing cobalt plus rhenium F-T catalysts. An examination of the data in Table VIII leads to the surprising conclusion that the type of support is extremely important and that vast differences in activity exist between catalysts prepared on one support and catalysts of the same catalytic metals content on another support. More surprisingly, only cobalt plus rhenium on alumina showed a commercially attractive activity level and selectivity.

Catalysts on magnesia and chromia exhibited extremely low activities, both with and without rhenium. Catalysts on zirconia and silica-alumina showed somewhat higher activities, but selectivity to C 2 hydrocarbons was poor. These catalysts showed only modest improvements in activity upon the addition of rhenium.

Catalysts without rhenium supported on silica and titania showed activity levels close to comparable cobalt on alumina catalyst. However, upon addition of rhenium, the alumina catalysts showed a surprising increase in activity from about 15 carbon monoxide conversion to 33 carbon monoxide conversion; whereas, the silica supported catalyst showed only a very small increase in activity from 11 carbon monoxide conversion to 12 carbon monoxide conversion, while the titania supported catalyst showed a larger, but still modest, gain in activity from 11 carbon monoxide I conversion to 17 carbon monoxide conversion. 1 From these example, plus those presented previously, it can be concluded that the catalytic activity of a cobalt catalyst supported on alumina is gr.-itly improved by adding minor amounts of rhenium, as long as the cobalt level is greater than about 5 wt%. Although improved activity from rhenium addition is also observed for some other supports, the activity level achieved by adding rhenium to a catalyst supported on alumina is much higher than for other supports.

SUBSTITUTE

SHEET

WO 89/03725 PCT/N088/00081 This result is surprising and would not have been predicted based on teachings in the prior art.

SEXAMPLE 42 A catalyst was prepared according to the procedure of Exam- Sple 24, except that Harshaw 4100P alumina was used as the support. Before being tested in a slurry reactor, the catalyst was pretreated as follows. One hundred grams of this catalyst was loaded into a vertical pipe pretreating reactor i constructed of 5 ft. of 1 in. OD schedule 40 stainless steel pipe. Hydrogen was introduced to the bottom of the pipe reactor at a rate of 1900 se/min., which was sufficient to fluidize the catalyst in the pretreating reactor. After a fluidized bed was established, temperature was increased at the rate of 1 C/min. to a maximum of temperature of 350 0

C.

The catalyst was held at this temperature for 16 hr. and then cooled to 50 C. At this point, the hydrogen was replaced with He, and the catalyst was cooled to ambient temperature. 14.1 g of this reduced catalyst were mixed with 206 grams of Synfluid (Synfluid 8 cSt PAO, Chevron Chemical Company) and loaded into a 1 in. ID by 3 ft. long slurry reactor. A mixture of CO, H 2 and N in a ratio of 1:2:3 was fed to the reactor at a rate of 1080 Sl/hr. Temperature was increased to 225 C and pressure was increased to 450 psig (approximately 31 atmospheres). These conditions were maintained for a total of 388 hr., except for two periods, one of 68 hr. and the other of 94 hr. during which pure N 2 was fed to the reactor. After a transition period of 2 hr., there then followed a period of 90 hr. during which the ratio of CO:H2N 2 in the feed was 1:3:4. There then followed a period of 53 hours during which operation was unstable due to problems with temperature control. During this period some high temperatures were experienced, followed by a short period of no activity from which the catalyst auickly recov-i ered. It is postulated that during the high temperature IA period, an abundance of light hydrocarbons were formed which 4) diluted the vehicle liquid and caused collapse cf the slurrv 0 SUBSTITUTE

SHEET

1 WO 89/03725 PCT/NO88/00081 I 89/37i -irnu;; iii .rrr- _ii-Tir~_X*i~"lSiP~r~i4P~IUII WO 89/03725 rPl/ N u/uuu~I 31 bed. This illustrates the importance of maintaining the proper vehicle properties, mixing energy, etc. It also illustrates the inherent ruggedness of the process, since it was able to recover from this incident. This was followed by 160 hr. during which the ratio of CO:H2N 2 in the feed was 1:1:2. After a 7 hr. transition period, this was followed by a period of 115 hr. in which the ratio of CO:H2N 2 in the feed was again 1:2:3. After a 9 hr. transition period, there then followed a period of 157 hr. with a CO:H2N 2 ratio in the feed gas of 2:3:5. Finally, after a 5 hr. transition period, there was a period of 94 hr. with a CO:H2N 2 feed ratio of 2:5:7. Altogether from startup to shutdown, the run lasted 1080 hr.

Figure 3 is a graph of CO conversion as a function of time on stream. This graph demonstrates the stability of the process and shows that the rate of deactivation is low.

During operation, product was removed continuously from the unit, so that the slurry volume in the reactor remained constant. Figure 4 is a gas chromatogram of a sample of the middle distillate and heavier liquid product. The product is predominately normal paraffins with a typical Schulz-Flory distribution, showing that the catalyst is promoting the Fischer-Tropsch reaction.

This example demonstrates that the catalyst of this invention is active for the Fischer-Tropsch process. Moreover, it shows that the catalyst may be used in a slurry reactor, as well as in a fixed bed reactor, as illustrated by the previous examples.

EXAMPLES 43 THROUGH 57 Catalyst Containing Cobalt, Rhenium and Alkali To demonstrate the advantages of including an alkali in the catalysts of this invention, the catalysts of Examples 43 through were prepared and tested.

SUBSTITUTE SHEET i WO 89/03725 PCT/N088/00081 32 i. The catalysts of Examples 43 to 51 were prepared on Harshaw Al 4100P alumina which had been screened to 100-270 mesh.

The catalysts of Examples 52 to 57 were prepared on Ketjen CK300 gamma-alumina, screened to 20-40 mesh. Both supports i 5 were calcined overnight at 500°C before use. The technique used for preparing the catalysts was incipient wetness, as described in Example 1. The amounts of materials used in the preparation of each catalyst are shown in Table IX. The prepared catalysts were then air dried for 5 to 24 hours in an oven at a temperature of 120 C. The dried catalysts were then calcined in air by raising the temperature at a heating rate of l°C/minute to 300 0 C and holding at this temperature for 2 to 16 hours. The compositions of the finished catalysts are shown in Table IX.

The results from testing these catalysts are shown in Table X. As is clear from these results, the addition of an alkali to the catalyst serves to increase the average molecular weight of the product, as evidenced by an increase in the Schulz-Flory S. Higher levels of the alkali result in higher W's as illustrated in Figure 5. However, activity decreases as the alkali content increases, as illustrated in Figure 6.

Therefore, for any particular situation there is an optimum alkali level that balances desired average product molecular weight and catalyst activity. Also, the effectiveness of the alkali varies from one alkali to another with, for examples, potassium being more effective than lithium.

SUBSTITUTE SHEET WO 89/03725 S33 I Table IX PCT/N088/00081 Wt of Type Weight of Material Composition of A1203 of in Impregnation Solution, g Finished Catalyst Ex.

No.

wt Co Alkali (a) (c) REO Alk.

43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 300.0 75.0 75.0 175.0 100.0 100.0 60.0 60.0 65.0 20.0 20.0 20.0 20.0 20.0 20.0 1039.65 K 260.46 K 256.36 K 609.03 K 349.50 K 354.03 Na 205.49 Cs 209.55 Rb 225.38 13.78 K 13.80 Li 13.64 Li 13.80 Cs 13.67 Cs 13.83 17.21 4.31 4.25 10.08 5.79 5.86 3.40 3.47 4.23 0.38 0.38 0.38 0.38 0.38 0.38 13.99 3 8 4 4 .50 0 0 .20 1 .70 1 .76 4 0 2 1 40 .34 40 .67 40 .59 40 .83 40 .64 40 .93 40 .12 40 .71 40 12 .06 12 .11 12 .12 12 .10 12 .10 12 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 2.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 0.0 1.0 0.1 0.2 1.0 0.2 1.0 0.4 1.0 0.24 1.36 0.87 1.0 1.0 0.1 0.05 1.0 0.05 0.3 1.0 0.3 0.62 0.62 0 0 0.62 0 0.62 0 Co(NO 3 2 .6HO 82.5 HReO 4 solution, except for Example 72.9 HReO 4 Rare earth nitrates (see Example 1) LiNO 3 NaNO 3

KNO

3 RbNO 3 or CsNO 3 SUBSTITUTE

SHEET

50 which was ;1 ~11~ N WO 89/03725 PCT/N088/00081 34 Table X Example No.

43 44 45 46 47 Alkali Tvpe Content.

CO

Conversion

CH

4 Selectivitv Product alpha* wt% w t ivi ty alpha* 48 49 50 51 52 53 54 56 57 0.1 0.2 0.2 0.4 1.0 0.24 1.36 0.87 0.1 0.05 0.05 0.3 0.3 52.5** 52 43 51 44 41 30 12 9 6 21 14 11 31.7*** 19 22 31 27 21 21 14.2** 8.6 11.1 9.3 9.5 11.6 9.4 7.3 7.8 7.0 7.9 6.2 8.3 8.5 7.3 10.9 7.6 9.8 11.7 12.0 11.1 10.3 0.75** 0.86 0.79 0.83 0.84 0.84 0.81 0.87 0.85 0.88 0.85 0.87 0.82 0.86 0.86 0.77*** 0.78 0.84 0.78 0.78 0.83 0.84 Calculated by plotting In(Wn/) vs. n, where n is carbon number and W is the weight fraction of the product having a carbon number n, and determining the slope of the line.

Average of 21 tests.

Averace of 6 tests.

SUBSTITUTE

SHEET

Claims (25)

1. A catalyst for converting synthesis gas to hydrocarbons characterised in that it comprises catalytically active amounts of cobalt and relatively lesser amounts of rhenium composited on an alumina support.

2. A catalyst as claimed in Claim 1 characterised in that the cobalt is present in an amount ranging from 5 to wt% of the catalyst.

3. A catalyst as claimed in Claim 2 characterised in that the cobalt is present in an amount ranging from to 40 wt% of the catalyst.

4. A catalyst as claimed in any one of Claims 1 to 3 characterised in that the rhenium is present in an amount ranging from about 0.5 to 50 wt% of the cobalt content of 20 the catalyst.

5. A catalyst as claimed in Claim 4 characterised in that the rhenium is present in an amount ranging from 1 to 30 wt% of the cobalt content of the catalyst.

6. A catalyst as claimed in any one of the preceding claims characterised by comprising an effective amount of o* an alkali metal promoter.

7. A catalyst as claimed in Claim 6, characterised in that the alkali metal promoter is present in a smaller amount than the cobalt content of the catalyst.

8. A catalyst as claimed in Claim 7, characterised in that the alkali metal promoter is present in an amount ranging from 0.5 to 5 atom of the cobalt content of the p cLl~q catalyst. 910812,dbdaLO74,25446.res,35 -36-

9. A catalyst as claimed in any one of Claims 6 to 9 characterised in that the alkali is incorporated into the catalyst as a salt selected from the groups consisting of nitrates, chlorides, carbonates and hydroxides. A catalyst as claimed in any one of the preceding claims characterised in that the support has a surface area of at least 100m 2 /g or 150m 2 /g and a pore volume of at least 0.3cm 3 /g.

11. A catalyst as claimed in any one of the preceding claims characterised by comprising an effective amount of metal oxide promoter comprising an element selected from group IIIB, IVB or VB of the periodic table, including the lanthanides and the actinides, MgO or MnO and mixtures thereof.

12. A catalyst as claimed in Claim 11, characterised in that the metal oxide promoter is present in an amount 20 ranging from 0.1 to 5 wt% of the catalyst.

13. A catalyst as claimed in any one of the preceding claims for converting synthesis gas to hydrocarbons, 0o characterised in that it comprises cobalt; rhenium and an alkali metal promoter composited on an alumina support wherein cobalt is present in a catalytically active amount up to about 60 wt% of the catalyst, rhenium is present in an amount from about 0.5 to 50 wt% of the cobalt content of the catalyst and the alkali is present in an amount from about 0.5 to 5 atom percent of the cobalt content of the catalyst.

14. A catalyst as claimed in Claim 13 further comprising an effective amount of a promoter selected from the group consisting of oxides of the elements chosen from Groups ii IIIB, IVB and VB of the periodic table, the lanthanides Sand the actinides, MgO and MnO and mixtures thereof. 910812,dbdat074,25446.res,36 37 A catalyst as claimed in any one of the preceding claims, characterised in that the support is gamma alumina.

16. A catalyst as claimed in any one of the preceding claims, characterised in that the sulfur content of the alumina support is kept to levels below about one hundred part per million.

17. A process for the production of hydrocarbons from synthesis gas, characterised by passing the synthesis gas over a catalyst as claimed in any one of the preceding claims.

18. A process as claimed in Claim 17 for the product of hydrocarbons comprising the step of contacting a synthesis gas feed including hydrogen and carbon monoxide over a catalyst, characterised in that the catalyst comprises cobalt and rhenium composited on an alumina support wherein rhenium is present in relatively lesser amounts than the cobalt content of the catalyst, at a temperature in the range of about 150 to 300°C, a pressure in the range of about atmospheric to 100 S atmospheres and a gaseous hourly space velocity, based on the total amount of synthesis gas feed, in the range of about 100 to 20,000cm 3 of gas per gram of catalyst per ;hour.

19. A process as claimed in Claim 17 or Claim 18, 30 characterised in that the catalyst further comprises an effective amount of an alkali metal promoter. A process as claimed in Claim 19, characterised in that the catalyst comprises an alkali metal promoter in an amount ranging from 0.5 to 5 atom of the cobalt content of the catalyst. l

21. A process as claimed in any one of Claims 17 to 910812,dbdaLt074,25446.res,37 I I I- ~i i -38- characterised in that the catalyst further comprises an effective amount of a metal oxide promoter comprising an element selected from groups IIIB, IVB or VB of the periodic table, including the lanthanides and the actinides, MgO or MnO or mixtures thereof.

22. A process as claimed in any one of Claims 17 to 21, characterised in that the temperature is in the range of about 190 to 2800C.

23. A process as claimed in any one of Claims 17 to 22 characterised in that the pressure in the range of about 1 to 40 atmospheres.

24. A process as claimed in any one of Claims 17 to 23, characterised in that the gaseous hourly space velocity is in the range of about 100 to 10,000 cm 3 of gas per gram of catalyst per hour. 20 25. A process as claimed in any one of Claims 17 to 24, characterised in that the synthesis gas feed is heated before contacting the catalyst. :26. A process as claimed in any one of Claims 17 to characterised in that the contacting step takes place in a fixed bed reactor or in a slurry reactor. 0*

27. A process as claimed in any one of Claims 17 to 26, characterised in that the molar ratio of hydrogen to 30 carbon monoxide is between 1:1 and 3:1.

28. A process as claimed in Claim 27, characterised in that the molar ratio of hydrogen to carbon monoxide is between 1.5:1 and 2.5:1. 91081dbd 7256.s38 d 910812,dbdaL074,25446.res,38 *t .N -39

29. A process as claimed in any one of Claims 17 to 28 characterised by the further step of cooling the gaseous product from the contacting step to a liquid by exposure to progressively lower temperatures. A catalyst substantially as hereinbefore described with reference to the Examples and/or drawings.

31. A process for the production of hydrocarbons substantially as hereinbefore described with reference to the Examples and/or drawings. DATED this 12th day of August, 1991 Den Norske Stats Oljeselskap AS 20 By Its Patent Attorneys DAVIES COLLISON n cr r r 910812,dbd, L074,25446,res,39