AU2016222404A1

AU2016222404A1 - Foaming of set-delayed cement compositions comprising pumice and hydrated lime

Info

Publication number: AU2016222404A1
Application number: AU2016222404A
Authority: AU
Inventors: Kyriacos Agapiou; Peter James Boul; Lance Everett Brothers; Samuel J. Lewis; Pauline Akinyi Otieno; Thomas Jason Pisklak
Original assignee: Halliburton Energy Services Inc
Current assignee: Halliburton Energy Services Inc
Priority date: 2013-09-09
Filing date: 2016-08-31
Publication date: 2016-09-22
Anticipated expiration: 2034-09-08
Also published as: WO2015035280A1; AU2016222404B2; GB2535857B; RU2016103916A; BR112016002545A2; CA2920756A1; RU2655669C2; NO20160086A1; AU2014317923B2; CA2920756C; GB201600816D0; GB2535857A; AU2018232978A1; AU2014317923A1; MX2016001651A; AU2018232978B2

Abstract

A variety of methods and compositions are disclosed, including, in one embodiment a method of cementing in a subterranean formation comprising: providing a set-delayed cement composition comprising water, pumice, hydrated lime, and a set retarder; foaming the set delayed cement composition; activating the so set-delayed cement composition; introducing the set-delayed cement composition into a subterranean formation; and allowing the set delayed cement composition to set in the subterranean formation. Additional methods, foamed set-delayed cement composition, and systems for cementing are also provided.

Description

FOAMING OF SET-DELAYED CEMENT COMPOSITIONS COMPRISING

PUMICE AND HYDRATED LIME

BACKGROUND

The present application is a divisional application from Australian patent application no. 2014317923, filed on 8 September 2014, which claims priority to and the benefit from US 14/032,734 , filed on 20 September 2013, and US 61/875,410, filed on 9 Sepember 2013, the entire contents of which are to be taken as incorporated herein by this reference.

[0001] Cement compositions may be used in a variety of subterranean operations. For example, in subterranean well construction, a pipe string (e.g., casing, liners, expandable tubulars, etc.) may be run into a wellbore and cemented in place. The process of cementing the pipe string in place Is commonly referred to as "primary cementing." In a typical primary cementing method, a cement composition may be pumped into an annulus between the walls of the wellbore and the exterior surface of the pipe string disposed therein. The cement composition may set in the annular space, thereby forming an annular sheath of hardened, substantially impermeable cement (i.e., a cement sheath) that may support arid position the pipe string in the wellbore and may bond the exterior surface of the pipe string to the subterranean formation. Among other things, the cement sheath surrounding the pipe string functions to prevent the migration of fluids in the annulus, as well as protecting the pipe string from corrosion. Cement compositions also may be used in remedial cementing methods, for example, to seal cracks or holes in pipe strings or cement sheaths, to seal highly permeable formation zones or fractures, to place a cement plug, and the like.

[0002] A broad variety of cement compositions have been used in subterranean cementing operations. In some instances, set-delayed cement compositions have been used. Set-delayed cement compositions are characterized by remaining in a pumpable fluid state for at least about one day (e.g. at least about 7 days, about 2 weeks, about 2 years or more) at room temperature (e.g. about 80° F) in quiescent storage. When desired for use, the set-delayed cement compositions should be capable of being activated whereby reasonable compressive strengths are developed. For example, a cement set accelerator may be added to a set-delayed cement composition whereby the composition sets into a hardened mass. Among other things, the set-delayed cement composition may be suitable for use in wellbore applications, for example, where it is desired to prepare the cement composition in advance. This may allow, for example, the cement composition to be stored prior to its use, In addition. this may allow, for example, the cement composition to be prepared at a convenient location and then transported to the job site. Accordingly, capital expenditures may be reduced due to a reduction in the need for on-site bulk storage and mixing equipment. This may be particularly useful for offshore cementing operations where space onboard the vessels may be limited.

[0003] While set-delayed cement compositions have been developed heretofore, challenges exist with their successful use in subterranean cementing operations. For example, set-delayed cement compositions prepared with Portland cement may have undesired gelation issues which can limit their use and effectiveness in cementing operations. Other set-delayed compositions that have been developed, for example, those comprising hydrated lime and quartz, ma he effective in some operations but may have limited use at lower temperatures as they may not develop sufficient compressive strength when used in subterranean formations having lower bottom hole static temperatures.

[0003a] The above discussion of background art is included to explain the context of the present invention. It is not to be taken as an admission that any of the documents or other material referred to was published, known or part of the common general knowledge in Australia at the priori ty date of any one of the claims of this specification.

SUMMARY OF INVENTION

[0003b] According to a first aspect of the present invention there is provided a foamed set-delayed cement composition comprising: water, pumice, hydrated lime, a foaming additive, entrained gas, and a set retarder.

BRIEF DESCRIPTION OF THE DRAWINGS

[0001] These drawinp iliusiMe certain aspects of 3¾¾¾¾ of the embodiments of the present method* and should not be used to limit or define the method.

[0002] FIO, 1 illustrates a system for preparation mi delivery of g set-delayed Seepteni composition to a wellbore in sccordanes with certain embodiments, [0003 ] FIB. 2k illustnaes surface equipment that may be used in placement of a set-delayed eoraad composition in a wellbore hi acetmfence with vedaiu smtedlments, f01104] FIO. 28 Illustrates placement of a set-deb?· ed cement composition into a wellbore annulus In accordance with eedsln embodiments. 10

DESCRIPTION OF PREFERRED EMBODIMENTS

[0005] The example embodiments relate to subterranean cementing operations and, more particularly, in certain embodiments, to set-delayed cement compositions and methods of using ad-delayed cement compositions in subterranean formations.

[0006J Embodiments of the set-delayed cement compositions may generally comprise water, pumice, hydrated lime, and a set retarder. Optionally., the set-delayed cement compositions may further comprise a dispersant. Embodiments of the set-delayed cement compositions may he foamed. Advantageously, embodiments of the set-delayed cement compositions .may be capable of remaining in a pumpable fluid state for an extended period of time. For example, the set-delayed cement compositions may remain in a pumpable fluid state for at least about 1 day, about 2 weeks, about 2 years, or longer. Advantageously, the set-delayed cement compositions may develop reasonable compressive strengths after activation at relatively low temperatures, While the set-delayed cement compositions may be suitable for a number of subterranean cementing' operations, they maybe particularly suitable for use in subterranean formations, having relatively low bottom hole static temperatures, e.g., temperatures less than about 200° F or ranging from about 10CAP to about 200°'F, hi alternative embodiments, the set-delayed cement compositions may be used in subterranean formations having bottom hole static temperatures up ίο 45CPF or higher. {'0007} The water used in embodiments of the set-delayed cement compositions may be from any source provided that h does not contain an excess of compounds that may undesirably affect other components in the set-delayed cement compositions. For example, a set-delayed cement composition may comprise fresh wafer or salt water. Salt water generally may include one or more dissolved salts therein and may be saturated or unsaturated as desired for a particular application. Seawater or brines may be suitable for use in embodiment. Further, the water may be present in an amount sufficient to form a pumpable slurry, in certain embodiments, the water may be present in the set-delayed eemeni composition in an amount in the range of from about 33% to about 200% by weight of the pumice. In certain embodiments, the water may be present in the set-delayed cement compositions in an amount in the range of from about 33% to about 70% by weight of the pumice. One of ordinary skill in the art with the benefit of this disclosure will recognize the appropriate amount of water for a chosen application. {0008} Embodiments of the set-delayed cement compositions may comprise pumice. Generally, pumice is a volcanic rock that, can exhibit cementitious properties in that, it may set and harden in the presence of hydrated lime and water. The pumice may also be ground Generally, the· pumice may have any particle size distribution as desired it”· a particular application, in certain embodiments, the pumice may Hau. a mean particle size in a range of from about .1 micron to about 200 microns. The .mean particle size corresponds to dSQ values as .measured by particle size analyzers such as those manufactured by Malvern Instruments, Worcestershire, United Kingdom. In specific embodiments, the pumice may have a mean particle size in a range of from about I micron to about .200 microns, front about 5 microns to about 100 microns, or front about 10 microns to about 50 microns. In one particular embodiment, the pumice may have a mean particle size of less than, about 15 microns. An example of a suitable pumice is available from Hess Pumice Products, Inc., Malad, Idaho, as 0S-325 lightweight aggregate, having a particle size of less than about 15 microns, It should be appreciated that particle sizes too small may have mixability problems while particle sizes fix's large may not be effectively suspended in the compositions. One of ordinary skill in the art. with the benefit of this disclosure, should, be able to select a particle size for the purmco suitable for a chosen application.

[000¾ Embodiments of the set-delayed cement compositions may comprise hydrated lime. As used herein, the term “hydrated lime” will be understood to mean calcium hydroxide. In some embodiments, the hydrated lime may be pros tded as quicklime (calcium oxide) which hydrates when mixed with water to form, the hydrated lime. The hydrated lime may be included in embodiments of the set-delayed cement compositions, for example, to form a hydraulic composition, with the pumice. For example, the hydrated lime may be included in a pumiee-to-bydrated-lime weight ratio of about 10:1 to about 1:1 or 3:1 to about 5:1. Where present, the hydrated lime may be included in the set-delayed cement compositions in an amount in the range of from about 10% to about 100% by weight of the pumice, for example·. In some embodiments, the hydrated lime may he present m an amount ranging between any of and/or including any of about 10%, about 20%. about 40%. about 60%, about. 80%, or about 100% by weight of the pumice. In some embodiments, the cementitious components present in the set-delayed cement composition .may consist essentially of the pumice and the hydrated lime. For example, the cementitious components stray primarily comprise the pumice and the hydrated time without any additional components (e.g„ Portland cement, fly ash, slag cement) that hydraulically set. in the presence of water. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the hydrated lime to include for a chosen application, [DO 10] Embodiments of the set-delayed cement compositions may comprise a set retarder. A broad variety of set retarders may be suitable for use its the set-delayed cement compositions. For example, the set retarder may comprise pbosphoaic acids, such as eihylenedmintne tetratmethylene phosphoaic acid), dieihylettetriamme pe«ta{meth.ylene phospbonie acid), etc,; Hgnostdfbmttes, such ss sodium Signosuifbnate, calcium Hgnosulfonate, etc.; salts such as stannous sulfate, lead acetate., monobasic calcium phosphate, organic acids, such as citric acid, tartaric add, etc.: cellulose derivatives such as hydroxyl ethyl cellulose- (HEO and catboxymethy! hydrosyethyI cellulose (CMHJbC); synthetic co» or ler-polyroers comprising sulfonate and carboxylic acid groups such as sulfonate-functionslixed acrylamide-acrylic acid eo-polymers; borate compounds such as alkali borates, sodium inelaborate·, sodium tetraborate, potassium pentaborate; derivatives thereof, or mixtures thereof. Examples of suitable set retarders include, among others, phosphomc add derivatives. One example of a suitable set iciarder is Micro Matrix**' cement retarder, available fmm Halliburton Energy Services, lac. Generally, the set retarder may be present in the set-delayed cement compositions in m amount sufficient to delay the setting for a desired time, in some embodiments, the set retarder may be present in the set-delayed cement compositions in an amount, in the range of from about 0.01% to about 10% by weight of the pumice, in spceilic embodiments, the set retarder may be present in an amount' ranging between any of and/or including any of about 0.01%, about 0,1%, about ! %, about 2%, about 4%, about. 6%, about 8%, or about 10% by weight of the pumice. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of the set retarder to include for a chosen application.

[0011] As previously mentioned, embodiments of the set-delayed cement compositions may optionally comprise a dispersant. Examples of suitable dispersants Include, without limitation, sulfbnated-fb«naldehyde-based dispersants (e,g., sulfonated acetone tbnnaidchydc condensate), examples of which may include Daxad'*" 19 available from Geo Specialty Chemicals. Ambler. Pennsylvania. Other suitable, dispersants may be polycarboxylated ether dispersants such as Uqumtenf* 558 IF and Liquiment*’ 5I4L available from BASF Corporation Houston, Texas; or Btbacryl G available from Coatex, Genay, France, An additional example of a suitable commercially available dispersant is CFR’^-3 dispersant, available from Halliburton Energy Services, l.nc, Houston, Texas. Of particular importance in regards to the examples that follow, is that the Uquiroem*' 3141.. dispersant comprises 36% by weight of the polycarboxylated ether in water. While a variety of dispersants may be used in accordance with embodiments, polycarboxylated ether dispersants may be particularly suitable for use in some embodiments. Without being limited by theory, it is believed that polycarboxylated ether dispersants may syoergisticaliy interact with other components of the set-delayed cement composition, for example, it is believed that the polycarboxylated ether dispersants may react with certain set retarders (e.g.. pbosphonic acid derivatives'! resulting m formation of a gel that suspends the pumice and hydrated lime in the d imposition for an extended period of time. {0012( In some embodiments, the dispersant may be included m the set-delayed cement compositions in an amount in the range of from about 0,01% to about 5% by weight of'the pumice, in specific embodiments, the dispersant, may be present in an amount ranging between any of and/or including any of about 0.01%. about 0,1%, 0.5%, about. 1%, about 2%, about 3%, about 4%, or about 5% by weight of die pumice. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the· appropriate amount of the dispersant to include lor a chosen application.

[0013] Embodiments of the set-delayed cement compositions may comprise a mechanical property enhancing additive. Meohanical-pfoperty-enhancing additives may be inducted in embodiments of the set-delayed compositions to, for example, ensure adequate compressive strength and long-term structural integrity. These properties can be affected by the strains, stresses, temperature, pressure, and impact effects from a subterranean environment. Examples of mechanical property enhancing additives include fibers, such as graphitic carbon fibers, glass fibers, steel fibers, mineral fibers, silica fibers, polyester fibers, polyamide fibers, and polyolefin fibers, among others. Specific examples of graphitic carbon, fibers include fibers derived from -polyacrylonitrile. rayon, and petroleum 'pitch. Where used, the ntechanuc:d'g\nx>perty-etfivancing additives may be present, in an amount from about 0.01% to about. 5% by weight of the pumice, in specific embodiments, the meehanieai-property-eohaneing additives may be present in an amount ranging between any of and/or including any of about 0.01%, about 0,1%, 0.5%, about 1%, about 2%, about 3%, about 4%, or about 5% by weight of the pumice. One of ordinary skill in the an. with the benefit of this disclosure, will recognize the appropriate, amount of the meehantcal-property-enhandng &ddiw\os to include for a chosen application. (0014] Other additives suitable for use in subterranean cementing operations also may be included in embodiments of the set-delayed cement compositions. Examples of such additives include, but are not limited to, weighting agent'». lightweight, additives, gasgenerating additives, lost-circulation materials, filtration-control additives, Huid-foss-contnol additives, detbaming agents, foaming agents, thixotropic additives, and combinations thereof. In embodiments, one or more of these additives may be added to the set-delayed cement composition after storing but: prior to placement of the set-delayed cement composition into a subterranean formation. A person having ordinary skill in the art, with the benefit of this disclosure, will readily be able to determine the type and amount of additive useful for a particular application and desired result [0015] Those of ordinary skill in the art. will appreciate that embodiment's of the set-delayed cement compositions generally should have a density stumble for a particular application. By way of example, the set-delayed cement compositions may have a density in the range of from about 4 pounds per gallon Cib/gaP) to about 20 Ib/gaL In certain embodiments, the set-delayed cement compositions may have a density in the range of from about 8 Ib/gal to about 17 fh/gaf. Embodiments of the set-ddayed cement compositions may be foamed or unlearned or may comprise other means to reduce their densities, such as hollow mictosphercs, low-density elastic beads, or other density-reducing additives known in the art. In embodiments, the density may be reduced after storing the composition, but prior to placement in a subterranean formation. Those of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate density for a particular application, [0016] As discussed above, embodiments of the set-delayed cement compositions may be foamed. Embodiments of the set-delayed cement compositions may be foamed to provide a lightweight composition that does not exert excessive force on formations penetrated by the wellbore. In addition to being lightweight, a foamed composition may also improve the ability of the composition to maintain pressure and prevent the flow of formation fluids into and through the composition during its transition time. Foamed compositions may also be advantageous because they have low fluid loss properties, thus limiting loss of fluid circulation. Additionally, foamed compositions when Set may also have a lower modulus of elasticity than non-foamed 'compositions, which is often desirable as it enables the resultant set cement composition to resist stresses exerted on ihe composition in situ.

[0017] In particular embodiments, the set-delayed cement composition may he foamed at the well site. By way of example, the set-delayed cement compositions may be foamed immediately prior to use. Embodiments may be foamed with a foaming additive and by entraining gas Into the set-delayed cement compositions. In particular embodiments, the foaming additive and gas may be introduced after combination of the composition with an activator, The set-ddayed cement compositions may be foamed, for example, to provide a set-delayed cement composition with a reduced density.

[OOlbj The gas used for foaming the composition may be any suitable gas for foaming, including, but not limited to: air, nitrogen, and combinations thereof Generally, the gas should be in an amount sufficient to form the desired foam. Foaming additives may be included in embodiments to, for example, facilitate foaming and/or stabilize the resultant foam formed therewith.

[0019} in particular embodiments, Ihe foaming additive may include a surfactant or combination of surfactants that reduce the surface tension of the water. By way of example, the foaming ageni may comprise an anionic, nonionie, amphoteric (including .awmsriook: surfactants), cationic surfactant, or mixtures thereof. Examples of suitable foaming additives include, hut are not limited to: betaines; anionic surfactants such as hydrolyzed keratin: amine oxides such as a alkyl or alkene dimethyl amine oxides; eocoamidopropyl dimethylamine oxide: methyl ester sulfonates; alkyl or alkene amidobetaines such as cocoimtidopropyl betaine: alpha-olefin sulfonates; quaternary surfactants such as trimethyllaiknvamnionium chloride and triroethylcocoammonium chloride; C8 to C22 alkyiethoxylate sulfate; and combinations thereof. Specific examples of suitable foaming agents include mixtures of an ammonium sail of an alkyl ether sulfate, a eoeoamidopropyl betaine surfactant, a eocoamidopropyl dimethylamine oxide surfactant, sodium chloride, and water; mixtures of an ammonium salt of an alkyl ether sulfate surfactant, a eocoamidopropyl hydroxysuHaine surfactant, a eocoamidopropyl dimethylamine oxide surfactant, sodium chloride, and water; mixtures of an eihoxylated alcohol ether suf&te surfactant, an alkyl or alkene amidopropyt betaine surfactant, and an alkyl or alkene dimethylamine oxide surfactant; aqueous solutions of an alpba-olefmic sulfonate surfactant and a betaine surfactant; and combinations thereof, Examples of suitable foaming additives are ZONIlSi-ALANT’" 2000 agent and Eoamer !026>M, both available from Halliburton Energy Services .foe·.. Houston, Texas. Emhodimemx may be foamed within a foam quality range of between about 5% to about 80% and, more particularly, from about 18% to about 38%. As used herein, the term ‘loam quality"· refers to the volume of entrained gas and is defined by the following formula; Foam Quality - (Total Foam Volume - Liquid Volume) / Total Foam Volume.

[0020] As previously mentioned, the cement compositions may have a delayed set in that they remain in a pumpable fluid state for at least one day fe.g., at least about I day. about 2 weeks, about 2 years, or longer) at room temperature In quiescent storage. For example, the set-delayed cement compositions may .remain in a pumpable fluid state for a period of time from about I day, about· 2 weeks, about 2 years, or longer. In some embodiments, (he set-delayed cemenr compositions may remain in a pumpable fluid state for at least about I day, about 7 days, about 10 days, about 20 days, about 30 days, about 40 days, about 50 days, about. 60 days, about 2 years, or longer. A fluid is considered to be in a pumpable fluid state where the fluid has a consistency of less than 70 Bearden units of consistency c‘Be”), as measured on a high-tempeta«ure high-pressure cousistometer at room temperature (eg., about iu.’f'F) in accordance with the procedure for determining cement thickening times set forth in API RP Practice iOB-2, ReuttnMemted Practice for Testing Weil Cements, First Edition, July 2005.

[0021] When desired for use, embodiment's of the set-deiaved cement' compositions may be activated (e.g„ by combination with an activator) to thereby set into a hardened mass. By way of example, embodiments of the sex-delayed cement compositions may he activated, to set to form a hardened mass lit a time period in the range of from about 1 hour to about 12 hours. For example, embodiments of the set-delayed cement compositions may set to form a hardened mass in a time period ranging between any of and/or including any of about 1 day, about 2 days, about 4 days, about 6 days, about 8 days, about 10 days, or about 12 days, [0022] In some embodiments, the seUdelayed cement compositions may set to have a desirable compressive strength after activation. Compressive strength is generally the capacity of a material or structure to withstand axially directed pushing forces. Hie compressive strength may be measured at a specified lime alter the set-delayed cement composition hits been activated and the resultant composition is maintained under specific temperature and pressure controls. Compressive strength can be measured by either a destructive method or non-destructive method. The destructive method physically tests the Strength of treatment fluid samples at various points in time by crushing the samples in a compression-testing machine. The compressive strength is calculated from the failure load divided by the cross-sectional area resisting the load and is reported in units of pound-force per square inch (psi). Non-destructive methods typically may employ an Ultrasonic Cement Analyzer (“UCA"), available from Farm Instrument Company, Houston, IX. Compressive strengths may be determined in accordance with API RP 10B-2, Recommended Practice Jar Testing Weil Cements, First Edition, July 2005.

[0023] By way of example, the set-delayed cement composition, may develop a-24-hour compressive strength m the range of from about 50 psi to about 5000 psi, alternatively, from about 100 psi to about 4500 psi, or alternatively from about 500 psi to about 4000 psi, in some embodiments, the set-delayed cement composition may develop a compressive strength in 24 hoars of at least about 50 psi. at least about 100 psi, at least'about 500 psi, or more, in some embodiments, the compressive strength values may be determined using destructive or non-destructive methods at a temperature ranging from KM)SP to 20G°!\ [00241 Embodiments may include the addition of a cement set activator to the set-delayed cement compositions. Examples of suitable cement set activators include, but are not limited to; amines such as triethanolamine, diethanolamine; silicates such as sodium silicate; xinc formate; calcium acetate; Groups 1A and liA hydroxides such as sodium hydroxide, magnesium hydroxide, and calcium hydroxide; monovalent sails such as sodium chloride;, divalent salts such as calcium chloride; nanosilicu (i.e., silica having a particle sfee of less than or equal to abom 100 nanometers); polyphosphates; and combinations thereof. In some embodiments, a combination of the polyphosphate and a monovalent salt may be used for activation. The monovalent salt may be any salt dial dissociates to form a monovalent cation, such as sodium and potassium salts. Specific examples of suitable monovalent salts include potassium sulfate, and sodium sulfate, A variety of different .polyphosphates may be used in combination with the monovalent salt for activation of the set-delayed cement compositions, including polymeric metaphosphate salts, phosphate salts, and combinations thereof. Specific examples of polymeric metaphosphate salts that may be used include sodium hexametaphosphaie. sodium trimctaphosphaie. sodium ietrametaphosphaie, sodium peruametaphosphate, sodium heptametaphosphate, sodium octametaphosphate, and combinations thereof. A specific example of a suitable cement set activator comprises a combination of'Sodium sulfate and sodium hexametaphosphaie. In particular embodiments, the activator may be prox ided and added to the set-delayed cement composition as a liquid additive, for example, a liquid additive comprising a monovalent salt, a polyphosphate, and optionally a dispersant.

[0025] The cement set activator should be added to embodiments of the set-delayed cement composition in an amount sufficient to activate the set-delayed cement composition to set into a hardened, mass. In certain embodiments, the cement set activator .may he added to the set-delayed cement composition, in an amount in the range of about 1% to about 20% by weight of the pumice. In specific embodiments, the cement set activator may be present in an amount ranging between any of and/or including any of about 1%, about 5%, about .10%, about 15%, or about 20% by weight of the pumice. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of foe cement set activator to include for a chosen application, [0026] As will be appreciated by those of ordinary skill in foe art, embodiments of the set-delayed cement compositions may be used in a variety of subterranean operations, including primary and remedial cementing. In some embodiments, a set-delayed cement composition may be ptox ided that comprises water, pumice, hydrated lime, a set retarder, and optionally a dispersant. The set-delayed cement composition may be introduced into a subterranean formation and allowed to set therein. As used herein, introducing the set-delayed cement composition into a subterranean formation includes introduction into any portion of the subterranean formation. Including, without limitation, into a wellbore drilled into the Subterranean formation, into a near wellbore region surrounding the wellbore, or into both. Embodiments may further include activation of the set-delayed cement composition. The activation of the set-delayed cement composition may comprise, for example, the addition of a cement set activator to the set-delayed cement composition. |0027] in some embodiments, a set-delayed cement composition may be provided that.comprises water, pumice, hydrated iime, a sei retarder, and optionally a dispersant, The set-delayed cement composition may be stored, for example, in a vessel or other suitable container. The set-delayed cement composition may be permitted to remain in storage for a desired time period. For example, the set-delayed cement composition may remain in stnrave for a time period of about 1 day, about 2 weeks, about 2 years, or longer. For example, the set-delayed cement composition may remain in storage for a time period of about I day, about 2 days, about 5 days, about 7 days, about 10 days, about 20 days, about 30 days, about 40 days, about 50 days, about 00 days, about 2 years, or longer, fo some embodiments, the set-delayed cement composition may remain in storage for a time period in a range of from about 1 day to about 2 years or longer. Thereafter, the set-delayed cement composition may be activated, for example, by addition of a cement set activator, introduced into a subterranean formation, and allowed to set therein. Optionally, the set-delayed cement composition mm be foamed prior to introduction into the subterranean formation.

[0028] in primary' cementing embodiments, for example, embodiments of the set-delayed cement composition may be .introduced into an annular space between a conduit located in a wellbore and the walls of a wellbore (and/or a larger conduit in the wellbore), wherein the wellbore penetrates the subterranean formation. The wn-ddayed cement composition may be allowed to set in the annular space to form an annular sheath of hardened cement. The set-delayed cement composition may form a barrier that prevents the migration of fluids in the wellbore. The set-delayed cement composition may also, for example, support the conduit in the wellbore.

[0029] in remedial cementing embodiments, a set-delayed cement composition may be used, for example, in squeeze-cementing operations or in foe placement of cement pings. By way of example, the set-delayed composition may be placed in a wellbore to ping an opening such as a void or crack that i- m the 1'-rnnuiv», in a gravel pack, in the conduit, in foe cement sheath, and/or between the cement sheath and the conduit (e.g., a microannulus), [0030] An example embodiment comprises a method of cementing in a subterranean formation comprising: providing a set-delayed cement composition comprising water, pumice, hydrated lime, and a set retarder; foaming foe set-delayed cement composition; activating the foamed set-delayed cement composition; introducing the foamed set-delayed cement composition into a subterranean formation; and allowing the foamed «-delayed cement composition to ad in the subterranean formation.

[0031] An example embodiment comprises a foamed set-delayed cement composition comprising: water, pumice, hydrated lime, a foaming additive, entrained gas, and a set retarder.

[0032] An example embodiment comprises a system for cementing comprising: a set-delayed cement composition comprising: water, pumice, hydrated lime, a set retarder, a foaming additive for foaming the «-delayed cement composition; a gas for foaming the set-delayed cement composition; and a cement- set activator for activation of the set-delayed cement composition.

[0033] Referring now to FIG. I, preparation of a set-delayed cement composition in accordance with example embodiments will now be described. FIG, 1 illustrates a system 2 for preparation of a set-delayed cement composition and delivery to & wellbore in accordance with certain embodiments. As shown, the set-delayed cement composition may be mixed in mixing equipment 4, such as a jet mixer, re-cifeulafcing mixer, or a batch mixer, for example, and then pumped via pumping equipment 6 to the well bore, in some embodiments, the mixing equipment 4 and the pumping equipment 6 may be disposed on one or more cement trucks as wdl he apparent to those of ordinary skill its the art.. In some embodiments, a jet mixer .may be used, for example, to continuously mix the lime/sedable material, with the water as it is being pumped to the wellbore, 10034 ] An example technique for placing a set-delayed cement composition into a subterranean formation will now be described with reietcnce to FIGS, 2-A and 2B. FIG, 2A illustrates surface equipment 10 that may he used in placement of a set-delayed cement composition jo accordance with certain embodiments. It should be noted that while FIG, 2A generally depicts a land-based operation, those skilled in the art will readily recognize that the principles described herein are equally applicable to subsea operations that employ floating or sea-based platforms and rigs, without departing from the scope of the disclosure. As illustrated by FIG. 2A. the surface equipment 10 may include a cementing unit 12,'which may include one or more cement trucks. The cementing unit 12 may include mixing equipment 4 and pumping equipment 6 (e.g.. FIG. 1) m will be apparent to those of ordinary skill in- the art. The cementing unit 12 may pump a set-delayed cement composition 14 through a feed pipe 16 and to a cementing head 18 which conveys the set-delayed cement composition, 14 downhole. 10035j Turning now to FIG. 2B, the set-delayed cement composition 14 may be placed Into a subterranean formation 20 in accordance- with example embodiments. As illustrated, a wellbore 22 may be drilled into the subterranean formation 20. While wellbore 22 is shown extending generally vertically into the subterranean formation 20, the principles described herein are also applicable to wellbores that extend at an angle through the subterranean formation 20, such as horizontal and slanted wellbores. As illustrated, the wellbore 22 comprises walls 24. In the illustrated embodiment, a surface casing '26 has been inserted into the wellbore 22, The surface casing 20 may be cemented to the walls 24 of the wellbore 22 hv cement sheath 28, In the illustrated embodiment, one or more additional conduits (e.g., intermediate casing, production casing, liners, etc.), shown here as casing 30 may also be disposed in the wellbore 22. As illustrated, there is a wellbore annulus 32 formed between the casing 30 and the walls 24 of the wellbore 22 and/or the surface casing 26. One or more centralizers 34 may be attached to the casing 30, for example, to centralize the casing 30 in the wellbore 22 prior to and during the cementing operation.

[0036] With continued reference to FIG. 2B, the set-delayed cement composition 14 may be pumped down the interior of the casing 30. The set-delayed cement composition 14 may be allowed to flow down the interior of the casing 30 through the easing shoe 42 at the bottom of the casing 30 and up around the casing 30 Into the wellbore annulus 32, The set-delayed cement composition 14 may be allowed to set in the wellbore annulus 32, for example, to form a cement sheath that supports and positions the easing 30 in the wellbore 22, While not illustrated, other techniques may also be utilized for introduction of the set-delayed cement composition .14., By way of example, reverse Circulation techniques may be used that include introducing the set-delayed cement composition 14 into the subterranean formation 20 by way of the wellbore annulus 32 Instead of through the easing 30.

[0037] As It is introduced, the set-delayed cement composition 14 may displace other fluids 36, such as drilling fluids and/or spacer fluids that may be present in the interior of the casing 30 and/or the wellbore annulus 32. At least a portion of the displaced fluids 36 may exit the wellbore annulus 32 via a flow line 38 and be deposited, for example, in one or more retention pits 40 (e.g.. a. mud pH), as shown on FIG, 2Λ. Referring again to FIG. 28, a bottom plug 44 may be introduced into the wellbore 22 ahead of the set-delayed cement composition 14, for example, to separate the set-delayed cement composition 14 from the fluids 36 that may be inside the casing 30 prior to cementing. After the bottom plug 44 reaches the landing collar 46, a diaphragm or other suitable device should rupture to allow the set-delayed cement composition 14 through the button? plug 44, In FIG, 28. the bottom plug 44 is shown on the landing collar 46. In the illustrated embodiment, a top plug 48 may be introduced into the wellbore 22 behind the set-delayed cement composition 14. The top plug 48 may separate the set-delayed cement composition 14 from a displacement fluid 50 and also push the set-delayed cement composition 14 through the bottom plug 44. 100381 The exemplars·· set-delayed cement compositions disclosed herein may directly or indirectly afie< t «me or more components or pieces of equipment associated with the preparation, delivers··, recapture, recycling, reuse, and/or disposal of the disclosed set-delayed cement compositions. For example, the.disclosed set-delayed cement compositions may directly or indirectly affect one or more mixers, related mixing equipment, mud pits, storage facilities or units, composition separators, heat exchangers, sensors, gauges, pumps, compressors, and the like used generate, store, monitor, regulate, and/or recondition the exemplary set-delayed cement compositions. The disclosed set-delayed cement compositions may also directly or indirectly affect any transport or delivery equipment used to convey the set-delayed cement compositions to a well site or downhole such as, for example, any transport vessels, conduits, pipelines, trucks, tubulars, and/or pipes used to cotnpositionally move the set-delayed cement compositions from one location to another, any pumps, compressors, or motors (e.g,, topside or downhole) used to drive the set-delayed cement compositions into motion, any valves or related joints used to regulate the pressure or flow ..rate of the-sewlelayed cement-compositions, and any sensors (i.e.„ pressure and temperature), gauges, and/or combinations thereof, and the like. The disclosed set-delayed cement compositions may also directly or indirectly affect the various downhole equipment and tools that may come into contact with the set-delayed cement compositions such as, but not limited to, wellbore casing, wellbore liner, completion string, insert strings, drill string, coiled tubing, slickline, wireline, drill pipe, drill collars, mud motors, downhole motors and/or pumps, cement pumps, surface-mounted motors and/Or pumps, centralizers, turbolteers, scratches, floats (e.g.. shoes, collars, valves, etc.), logging tools and related telemetry equipment, actuators (e.g,, electromechanical devices, hydromechanics} devices, etc.), sliding sleeves, production sleeves, plugs, screens, fillers, flow control devices (e.g., inflow control devices, autonomous inflow control devices, outflow control devices, etc.), couplings (e.g., electro-hydraulic wet connect, dry connect, inductive coupler, etc,), control lines (e,g., electrical, fiber optic, hydraulic, etc.), surveillance Hues, drill bits and reamers, sensors or distributed sensors, downhole heat exchangers, valves and corresponding actuation devices, tool seals, packers·, cement plugs, bridge plugs, and other wellbore isolation device*·, or components, and the like.

EXAMPLES

[0039] To facilitate a better understanding of the present embodiments, the following samples of certain aspects of some embodiments are given. In no way should the following examples be read to limit, or define, the scope of the embodiments.

Example I 100401 A sample set-delayed cement composition was prepared with the following components; pumice (DS-325 lightweight aggregate), hydrated lime, dispersant (Liquiment*' 558IP), primary retarder (Micro Matrix'’ cement retarder), weighting additive (MicroMax* Weight Additive, available from Halliburton Energy Services, Inc.. Houston, Texas), secondary retarder «HR'¥-S cement retarder, available from Halliburton Energy Services, lne.s Houston, 'Texas). Class H Portland cement, and water. Each component, with the exception of the primary retarder (Micro Matrix* cement retarder), is presented as a percentage of the weight of pumice (hwoP). The primary retarder is measured in units of gallons per 46 pound sack of pumice (gai/sk). The compositional makeup is listed in fable 1 below.

Table 1

Sample Set-Delayed Cement Compositional Makeup

|0041 ] The sample m Example 1 remained fluid. mixable, pumpabk, and stable with no solids settling or gelation for greater chan 40 days. The sample had a measured density of 13.5 pounds per gallon, Minimal doses of dispersant were added daring the storage period to maintain the slurry’s optimal rheology, This exemplary sample serves as the base slurry for the remaining examples provided below,

Example '2 [0042] The rheological properties of the sample set-delayed cement composition, of Example 1 were measured after scoring the samples si room temperature and pressure .for a period of 41 days. After preparation,, the rheological properties of the samples were determined using a Model 35A Farm Viscometer and a No, 2 spring with a Pants Yield Stress Adapter, in accordance with the procedure set forth in API RP Practice 1 OB-2, Recommended Practice fi>r Testing Welt Cements, The results of this test are set forth in Table .2 below.

Table 2

Viscosity Tests

Example 3 [.0043] Three sample set-delayed cement compositions, samples 1-3, and two controls, controls 1 and 2» were prepared from the base slurry described in Example 1. Foamer 1026™, a foam tag additive, was added to each of foe three samples in varying amounts after a time period of 41 days. Additionally, a cement set activator, CaClj, was added to sample 2 and control 2, The amount of the cement set activator added to each sample was sufficient to deliver & 5% by weight of pumice activator amount to the set-delayed cement, composition. The base sod foamed densities were measured. Additionally, the destructive compressive strength was measured using a mechanical press in accordance with API RP Practice 1.0B-2, Recommended Practice for J'estmg Wed Cements, Additionally, the destructive compressive strength was measured by allowing the samples to cure in a 2” by 4” plastic cylinder that was placed in a water bath at 191PP to form set cylinders. Immediately after removal from the water bath, destructive compressive strengths were determined using a. mechanical press in accordance with API RP I OB-2, Recommended

Practice for Testis*# Wei! Cement*. The results of this test are set forth below. The reported compressive strengths are an average for two cylinders of each sample, fhe samples and controls were cured at I atmosphere,. !9(H?; compressive strength measurements were taken at 72 hours.

Table 3

Compositional Makeup and Characteristics

'‘'Density ofConfrei 2 with tin.' Activator.

[0044] hi addition to the characteristics of Table 3. the foam stability of samples 1-3 was measured in both the slurry state and the set state. This data is set forth in 1 able 4 below.

Table 4 ¥<>;·,m Stability Measurements,.

[0045] The Archimedes Method was used to measure the slurry density of Samples 1.-3 in top» middle, and bottom portions. Densities that were close in weight from top to bottom indicate stable foam while considerable variation in densities indicates unstable foam. All units are in pounds per gallon. This data is set forth in Table 5 below.

Tabic S

Dendty Uniformity

[0046] Lastly, the rheology of foamed Samples 1-3 seas measured using the same technique as used in Example 2 to measure the rheology of the base slurry. The base slurry is designated as Control I in Table 6 below. The rheology data is set forth in Table 6 below.

Table 6 Viscosity Tests

[0047] Example 3 thus indicates that Che foamed slurries exhibit good compressive strength while maintaining suitable rheologies and uniform densities.

[0048] Two sample set-delayed cement compositions, samples 4 and 5, were prepared from the base slurry described in Example L A cement -set: activator, CiCft, was added to the samples in an amount sufficient to deliver a 5% by weight of pumice activator amount to the set-delayed cement composition. Sample S further included graphitic carbon fibers in an amount of about 0.18% by weight of the pumice. The graphitic carbon fibers were PAN carbon fibers derived from polyacrylonitrile, Foamer 1()26w, a foaming additive, was added to each of the samples in an amount of 0,18% by weight of the pumice. Additionally, the destructive compressive strength was measured by allowing the samples to cure in a 2s* by 4*' plastic cylinder that was placed in a water bath at 190CP to form set cylinders. Immediately after removal from the water bath, destructive compressive strengths were determined using a mechanical press in accordance with API RP 10B-2, Recommended Pmctke.for Testing Well Cements. The results of this test are set forth below. The reported compressive strengths are an average for three cylinders of each sample. The samples and controls were cured at I atmosphere, 19(5%·'; compressive strength measurements were taken at 72 hours.

Table 7

Compositional Makeup arsd Characteristics

[0049] it should be understood that the compos-bom and methods are described in terras of “comprising,” “containing” or “including” various components or steps, the compositions and methods can also “coo-res essentially of’ or “consist of* the various components and steps. Moreover, the indefinite articles “a” or “an,” as. used in the claims, are defined herein to mean one or .more than one of the element that it introduces, |'0050'J for tho sake of brevity, only certain ranges are explicitly disclosed herein, 'However, ranges front any lower limit may be combined with any upper limit to recite a range not explicitly recited, as well as, ranges from any lower limit may be combined with any other lower limit ίο recite a range not explicitly recited, in the same way, ranges from any upper limit may be combined with any other upper limit to recite, a range not explicitly recited. Additionally, whenever a numerical range with a Sower limit and an upper limit is disclosed, any number and any included range .felling within the range arc specifically disclosed. In particular, every range of values {of the form, “from about a to about b,” or, equivalently, “from approximately a to b” or. equivalently, “'from approximately a-b”) disclosed herein is to be understood to set forth ever)' number and range, encompassed within the broader range of values even if not explicitly recited. Thus, every point or individual value may serve as Its own lower or upper limit combined with any other point or individual value or any other lower or upper limiU to recite a range not explicitly recked. I0051] Therefore, the present embodiments are well adapted to attain the ends and advantages mentioned as well as those that are inherent therein. The particular embodiments disclosed above are Illustrative only, and may be modified and practiced in different, but equivalent manners apparent to those skil led in the art having the benefit of the teachings herein. Although individual embodiments are discussed, the invention covers all combinations of all those embodiments. Furthermore·, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. Also, the terms in the claims have their plain, ordinary meaning unless otherwise explicitly and clearly defined by the patentee, it is therefore evident that the particular illustrative embodiments disclosed above may be altered or modified and ail such variations are considered within the scope and spirit of the invention. If there is any conflict in the usages of a word or term in this specification and one or more patent(s) or other documents that may be incorporated herein by reference, the definitions that are consistent with this specification should be adopted.

[0052] Where the terms ’’comprise", "comprises", "comprised" or "comprising" are used in this specification (including the claims) they are to be interpreted as specifying the presence of the stated features, integers, steps or components, but not precluding the presence of one or more other features, integers, steps or components, or group thereof.

Claims

The claims defining the invention are as follows:

1. A foamed set-delayed cement composition comprising: water, pumice, hydrated lime, a foaming additive, entrained gas, and a set retarder.
2. The foamed set-delayed cement composition according to claim 1 wherein the foaming additive is selected from the group consisting of: a betaine; hydrolyzed keratin; an amine oxides; an alkyl or alkene dimethyl amine oxide; a cocoamidopropyl dimethyl amine oxide; a methyl ester sulfonate; an alkyl or alkene dimethyl amidobetaine; cocoamidopropyl betaine; an alpha-olefin sulfonate; a quaternary surfactant; trimethyltallowammonium chloride; trimethylcocoammonium chloride; a C8 to C22 alkylethoxylate sulfate; and any combination thereof.
3. The foamed set-delayed cement composition according to any one of claims 1 to 2 wherein the foamed set-delayed cement composition has a foam quality between about 5% to about 80%.
4. The foamed set-delayed cement composition according to any one of claims 1 to 3 wherein the foamed set-delayed cement composition has a density between about 9 pounds per gallon to about 11 pounds per gallon.
5. The foamed set-delayed cement composition according to any one of claims 1 to 4 wherein the set retarder comprises at least one retarder selected from the group consisting of a phosphonic acid, a phosphonic acid derivative, a lignosulfonate, a salt, an organic acid, a cellulose derivate, a synthetic co- or ter-polymer comprising sulfonate and carboxylic acid groups, a borate compound, and any combination thereof.
6. The foamed set-delayed cement composition according to any one of claims 1 to 5 wherein the foamed set-delayed cement composition further comprises a dispersant.
7. The foamed set-delayed cement composition according to claim 6 wherein the dispersant comprises at least one dispersant selected from the group consisting of a sulfonated-formaldehyde-based dispersant, a polycarboxylated ether dispersant, and a combination thereof.
8. The foamed set-delayed cement composition according to any one of claims 1 to 7 wherein the set retarder comprises a phosphonic acid derivative, and wherein the set-delayed cement composition further comprises a polycarboxylated ether dispersant.