AU2015200002B2 - UV Curable Coating Compositions Containing Aliphatic Urethane Acrylate Resins - Google Patents

Abstract

H:\j13hi~eoveneR Prlb\CCLL\7~33370_ 1 dci-2/0 I/20,13 Described in preferred embodiments are UV curable coating compositions including a unique blend of aliphatic urethane 5 acrylate resins. Also described are coated articles and methods for their production involving the use of the coating c:orpositions. WO 2009/145781 PCTIUJS2008/065301

Description

H:\jHeven RPrlbD CCLL 7 ;33 710 1 .- 2/P0 1/20 . UV Curable Coating Compositions Containing Aliphatic Urethane Acrylate Resins BAC KGROJN D 5 This application is a divisional of Australian Patent Apli cation No. 2C08356852, the entire content of which is incorporated herein by reference. 10 The present Invention relates generally to forming polvmeric coatings on substrates, and in certain embodiments to coatiLng compositions, coat articles, and methods for their production, that involve the use of a blend of selected types of resins. 15 As further background, plastic subsr 'ates such as out not listed to polycarboIate, acrylic and povester often are used in a variety of applications as replacements for more traditional materials such as glass. Plastics can offer excel ent properties sucn as impact resistance and optical clarity while providing 20 weight reduction and abundant design flexibility. Despite the numerous benefits that plastic offers, they have a major drawback in that they often do not provide the desired degree of chemical, scratch, mar and abrasion resistance, UV resistance and/or exterior durability. 25 It is known that both conventional thermal cured and ultraviolet (UV) cured coatings for exterior applications ex hitinq scratch and abrasion resistance have offered adequate protection and performance of these various plast-ic substrates 30 when direct exposure angles or durations are limited. It is also known that UV cured coatings are often the preferred coating of choice because they offer distinct advantages such as improved cvcles tines and reduced work in process over conventionally cured alternatives.

WO 2009/145781 PCT/US2008/065301 2 Despite the many advantages of current exterior coatings - and more specifically of UV curable coatings they still do not meet the all expectations and often lack 5 desirable properties and combinations of properties that are very difficult to achieve with traditionally available technology. Traditional UV topcoats for scratch and abrasion resistant applications most often are comprised primarily of high functionality and highly reactive 10 acrylates. Although these characteristics impart the desired hardness properties, they are prone to cured resin shrinkage and steric hindrance. The steric hindrance results in a higher than desired number of unreacted acrylate bonds in the cured polymer resin which make the 15 cured coating more susceptible to premature UV and environmental degradation. Additionally, known UV topcoats upon curing create a rigid, inflexible coating. Such inflexible coatings when subjected to conditions of expansion or contraction during processing or field use or 20 when applied to materials containing high internal stress result in inadequate performance such as cracking, compromised exterior durability or other imperfections. Thus it can be difficult for a single coating composition to provide the desired level of a high surface hardness, 25 scratch resistance, chemical resistance, UV resistance and exterior durability. In preferred embodiments, the present invention addresses the need for UV curable coatings that along with 30 high scratch and abrasion resistance offer properties of improved exterior durability, UV stability, thermal stability and flexibility especially for design applications that subject the coated material to strenuous WO 2009/145781 PCT/US2008/065301 3 environments. Additionally, the current invention describes the processes for using these materials and the resulting coated articles.

4 SUMMARY The present invention provides a product, comprising: 5 - a molded plastic article; and - a cured coating formed with a composition characterized by: - a first aliphatic urethane acrylate resin formed by the reaction of an aliphatic 10 polyisocyanate component comprising iminooxadiazine dione, isocyanurate, uretdione, urethane, allophanate, biuret or oxadiazine trione groups, with an alcohol component comprising at least one monobasic, 15 hydroxylfunctional linear or branched alkyl ester of meth(acrylic) acid; and - a second aliphatic urethane acrylate resin formed by the reaction of a multifunctional acrylate with an aliphatic urethane based on a 20 polymer of alkyl carbomonocycle diisocyanate. The present invention also provides a process for forming a coated article, comprising the steps of: - coating an article with a coating composition 25 characterized by: - a first aliphatic urethane acrylate resin formed by the reaction of an aliphatic polyisocyanate component comprising iminooxadiazine dione, isocyanurate, uretdione, 30 urethane, allophanate, biuret or oxadiazine trione groups, with an alcohol component comprising at least one monobasic, hydroxylfunctional linear or branched alkyl ester of meth(acrylic) acid; and 4A - a second aliphatic urethane acrylate resin formed by the reaction of a multifunctional acrylate with an aliphatic urethane based on a polymer of alkyl carbomonocycle diisocyanate; and 5 - curing the coating composition. In certain aspects, the invention includes the use of a coating composition that includes a unique blend of UV curable resins. A first resin of the blend is an aliphatic 10 urethane acrylate formed by the reaction of an aliphatic polyisocyanate component containing iminooxadiazine dione, isocyanurate, uretdione, urethane, allophanate, biuret or oxadiazine trione groups, with an alcohol component with a molecular weight of about 100 to about 2000 and containing 15 at least one monobasic, hydroxyl-functional linear or branched alkyl ester of meth(acrylic) acid. This coating composition also includes at least a second aliphatic urethane acrylate, which in certain embodiments (i) is formed by the reaction of a multifunctional acrylate with an 20 aliphatic urethane based on a polymer of alkyl carbomonocycle diisocyanate; or (ii) is encompassed by Formula II disclosed hereinbelow. In preferred aspects, the first aliphatic urethane acrylate has a molecular weight in the range of about 800 to about 2500 g/Mol, and/or the first 25 aliphatic urethane acrylate contains about 3 to about 5 polymerizable acrylate groups per molecule. In preferred aspects, the molecular weight of the second aliphatic urethane acrylate is in the range of about 500 to about 2000 g/Mol. The coating compositions can also contain a solvent 30 that assists in controlled application and processing of the material. The coating compositions can also contain at least two and more preferably three or more multifunctional acrylates each having molecular weights between 170 and 1000 and a minimum of two polymerizable unsaturated groups per 4B molecule. The coating compositions can also include stabilizers such as hindered amine light stabilizers 5 and/or UV absorbers of the benzotriazole or benzotriazine families, or derivatives thereof. The coating compositions can also contain one or more organic-inorganic hybrid materials synthesized through a sol gel process. 5 Accordingly, the present invention provides coated articles and coating processes involving the use of the coating compositions described herein. In certain forms, an inventive coated article will have a base plastic material 10 having a thickness of about 0.75 to 20 mm, and a cured top coating formed by reaction of a coating composition as described herein and having a thickness in the range of about 3 to about 35 microns. The cured top coating can provide a high degree of scratch, abrasion, mar and chemical 15 resistance along with superior UV resistance, exterior durability and thermal stability. In certain forms, inventive processes will include the application of a coating composition as described herein by spray coat, flowcoat or curtain coat techniques. 20 Additional embodiments of the present invention as well as features and advantages thereof will be evident from the descriptions herein.

WO 2009/145781 PCT/US2008/065301 6 BRIEF DESCRIPTION OF THE FIGURES FIG. 1 provides a perspective partial cutaway illustration of a vehicle having a coated forward lighting 5 lens according to one aspect of the invention. FIG. 2 provides a side partial cutaway illustration of the vehicle of FIG. 1. 10 WO 2009/145781 PCT/US2008/065301 7 DETAILED DESCRIPTION For the purposes of promoting an understanding of the principles of the invention, reference will now be made to 5 certain embodiments and specific language will be used to describe the same. It will nevertheless be understood that no limitation of the scope of the invention is thereby intended, such alterations and further modifications in the illustrated device, and such further 10 applications of the principles of the invention as described herein being contemplated as would normally occur to one skilled in the art to which the invention relates. 15 As disclosed above, in certain of its aspects, the present invention relates to unique coating compositions and to methods and coated articles that employ or include the coating compositions. In preferred forms, coating compositions include a novel blend of resins, the blend 20 including first and second acrylated aliphatic urethane resins. Such coating compositions include at least a first urethane acrylate resin which is formed by the reaction of an aliphatic polyisocyanate component containing iminooxadiazine dione, isocyanurate, uretdione, 25 urethane, allophanate, biuret or oxadiazine trione groups with an alcohol component containing at least one monobasic, hydroxyl-functional linear or branched alkyl ester of meth(acrylic) acid. 30 In preferred forms, the first urethane acrylate resin has a molecular weight between about 800 and about 2500 g/Mol. More preferably, the first acrylated aliphatic urethane has a molecular weight of about 1000 to about WO 2009/145781 PCT/US2008/065301 8 1600 g/Mol, with a molecular weight of about 1400 g/Mol being the most preferred in work to date. As would be understood, molecular weights for polymerizable resins given herein are number average molecular weights unless 5 otherwise specified. The alcohol component used in the formation of the first urethane acrylate resin can have a molecular weight of about 100 to about 2000 g/Mol. In certain variants, the first urethane acrylate can be the reaction product of: 10 (a) a polyisocyanate component containing from 20 to 100 mole%, based on the moles of the polyisocyanate component, of iminooxadiazine dione group-containing polyisocyanate trimers encompassed by the formula I: 15 x C 0 R0 wherein: 25 R , R2 and R3 of formula I are the same or different and represent linear or branched, C 4

-C

2 : (cyclo)alkyl groups, and X is the same or different and represents 30 isocyanate groups or isocyanate group-containing radicals that also contain iminooxadiazine dione, isocyanurate, uretdione, urethane, allophanate, WO 2009/145781 PCT/US2008/065301 9 biuret or oxadiazine trione groups, wherein R', R 2 and R3 of formula I are attached to a nitrogen atom, with h) an alcohol component containing at least one 5 monobasic, hydroxy-functional, linear or branched C 2 -C1 2 alkyl ester of (meth)acrylic acid. Additional information concerning such urethane acrylate resins suitable for use in the present invention is found in United States Patent No. 6,191,181, which is hereby incorporated herein by 10 reference in its entirety, including for its disclosure of preparative methods and final urethane acrylate resin compounds that can be used in the present invention. Suitable resins for use as the first aliphatic urethane acrylate may be obtained for example from Bayer 15 MaterialScience under the tradename Desmolux. In certain embodiments, the first urethane acrylate has a functionality of about 2 to about 6, more preferably about 3 to about 5, and most preferably about 3.5 to about 20 4. In addition or alternatively, the first urethane acrylate can exhibit the capacity for ultraviolet radiation curing to provide a hard coating, for example having a pencil hardness above 4, e.g. about 4 to about 7. 25 The first aliphatic urethane acrylate resin can be provided alone or can be provided admixed with one or more reactive diluents, for example HDDA (1,6 Hexanediol diacrylate), TPGDA (tripropyleneglycol diacrylate), DPGDA (dipropyleneglycol diacrylate), TMPTA (trimethylolpropane 30 triacrylate), and/or GPTA (glycerolpropoxy triacrylate). When admixed with one or more reactive diluents, the first aliphatic urethane acrylate resin can constitute about 70% to about 90% of the mixture in certain embodiments.

WO 2009/145781 PCT/US2008/065301 10 In certain embodiments, the coating compositions of the invention also include a second urethane acrylate 5 resin different from the first urethane acrylate resin. The second urethane acrylate resin can he formed by the reaction of a multifunctional acrylate (e.g. with a molecular weight of about 190 to about 500 and containing at least three polymerizable unsaturated groups per 10 molecule) with an aliphatic urethane based on a polymer of alkyl carhomonocycle diisocyanate with alkanepolyol polyacrylates. In certain embodiments, the second urethane acrylate resin is encompassed by the formula II: 15 II 20 Q wherein A 1 , A 2 , and A3 are each a group of the formula III: 25 WO 2009/145781 PCT/US2008/065301 11 0 11 H 0 5 0 C C| CH2 NH '=0 1 0 10 C2-CH2-O-C -CH=c3H4 wherein R , R2, and R3 of formula III, which can be the same or different, are each a linear aliphatic group 15 having from 2 to about 12 carbon atoms, or a cycloaliphatic group having from 4 to about 12 carbon 1 21 atoms. R , R , and R3 of formula III are each preferably an alkylene group having from 2 to about 12 carbon atoms. Compounds of Formula II can be prepared, for example, as 20 described in United States Patent No. 5,658,672, which is hereby incorporated herein by reference in its entirety, including for its disclosure of preparative methods and of final compounds encompassed by formula II above that may be used in the present invention. This '672 patent 25 teaches that Ebecryl 8301 (Cytec Surface Specialties, Smyrna, GA), which may be used in the present invention, is a blend including a diluent and a hexafunctional acrylate oligomer according to formula II in a weight ratio of about 48:52, respectively, with the diluent being 30 (ethylene-/diethylene glycol diacrylate (based on hydroxyethylacrylate), mostly ethylene glycol diacrylate.

12 Preferably, the second urethane acrylate resin has a molecular weight in the range of about 500 to about 2000 g/Mol, more preferably about 800 to about 1000 g/Mol, and most preferably to date about 800 g/Mol. In certain 5 embodiments, the second urethane acrylate has a functionality of about 2 to about 10, more preferably about 4 to about 8, and most preferably about 6. As disclosed above, embodiments of the invention 10 involve the use of coating compositions which include a blend of resins including a first urethane acrylate resin as discussed above and a second urethane acrylate resin as discussed above. In preferred such embodiments, exclusive of any inert solvent present in the composition, the first 15 urethane acrylate resin constitutes about 10% to about 40% by weight of the composition. More preferably in such embodiments, exclusive of any inert solvent present, the first urethane acrylate resin makes up about 10% to about 30% of the composition, even more preferably about 15 to 20 about 25%. As to the second urethane acrylate resin, exclusive of any solvent present, it preferably constitutes about 20% to about 50% by weight of the coating composition, more preferably about 25 to 35%. 25 In other embodiments of the invention defined herein, the first urethane acrylate resin and the second acrylate resin are included in the coating composition in a weight ratio, or in a molecular ratio, of about 1:10 to about 10:1, respectively, more preferably about 1:5 to 5:1, and most 30 preferably about 1:3 to about 3:1. In certain specified embodiments, the first and second urethane acrylate resins will be present in a weight ratio, or in a molecular ratio, of about 1:2 to about 2:1, respectively.

WO 2009/145781 PCT/US2008/065301 13 When included in a blended resin coating composition, the first and second urethane acrylate resins can provide preferred compositions which form UV-cured coatings of 5 with a high degree of surface hardness as measured with steel wool per FMVSS108 and taber abrasion per ASTM D1044. Additionally, preferred blended coatings including these urethane acrylates provide excellent weathering properties as quantified by well accepted accelerated and natural 10 weathering test methods and thermal crack resistance. Also, they offer advantageous curing rates and material compatibility. The surface hardness of resin blend coating 15 compositions as disclosed herein can be further improved with the addition of an acrylated organic-inorganic hybrid material, typically produced through a sol gel process. The preferred organic-inorganic hybrid is compromised of silica particles in the range of about 5 nm to about 100 20 nm that are spherical, non-porous and amorphous and a multifunctional acrylate with a molecular weight of about 200 to about 450 and at least two polymerizable unsaturated groups per molecule. The preferred final molecular weight the organic-inorganic hybrid is between 25 about 500 and about 3000. Improved surface hardness properties can be achieved with additions of about 5% to about 35% by weight (exclusive of any inert solvent present) of such acrylated organic-inorganic hybrid materials. More preferably the content of the acrylated 30 organic-inorganic hybrid, when included, is about 8% to about 18% by weight, exclusive of any inert solvent present. Examples of suitable organic-inorganic materials that can be used in compositions, coatings and coated 14 articles of the invention include Etercure 601A-35, Etercure 601B-35, Etercure 601C-35, Etercure 601H-35, (Eternal Chemical Company, Ltd, Taiwan) and RX11402 (Cytec Surface Specialties, Smyrna, GA) 5 Coating compositions for use in the invention can also include one or a plurality of multifunctional acrylates. The multifunctional acrylate(s) employed in coating compositions used in the invention will depend upon the 10 desired application viscosity, application method and performance properties. Typical multifunctional acrylates are of the reactive diluent type having a molecular weight of about 170 to about 1000 and contain at least two polymerizable unsaturated groups per molecule. 15 Representative multifunctional acrylates include dipropylene glycol diacrylate, triproplyene glycol diacrylate, 1,6 hexanediol diacrylate, pentaerythritol triacrylate, pentaerythritol tetra acrylate, tricyclodecane dimethanol diacrylate, di-trimethylolpropane tetraacrylate, 20 dipentaertyhritol pentaacrylate, trimethylolpropane triacrylate, tetraethleneglycol diacrylate, and the like. The preferred coating composition includes two such multifunctional acrylates each in an amount of about 5% to about 55% by weight. In certain preferred embodiments, a 25 coating composition of the invention will include about 5% to about 15% of a first such multifunctional acrylate with two polymerizable unsaturated groups per molecule and about 15% to about 25% of a second such multifunctional acrylate with three polymerizable unsaturated groups per molecule. 30 Many photoinitiators and/or sensitizers are suitable for use in coating compositions used in the invention. Among WO 2009/145781 PCT/US2008/065301 15 the groups of suitable photoinitiators are dipenyiphosphine oxide type photoinitiators such as 2,4,6 trimethylbenzoyl diphenylphosphine oxide and bis-2,4,6 trimethylbenzoyldiphenylphosphine oxide; phenylglyoxylate 5 type such as oxy-phenyl-acetic acid 2-[2 oxo-2 phenyl acetoxy-ethoxy]-ethy ester and oxy-phenyl-acetic 2-[2 hydroxy-ethoxy]-ethyl ester; a-hydroxyketone type such as 1-hydroxy-cyclohexyl-phenyl-ketone, 2-hydroxy-l-[4-(2 hydroxyethoxy) phenyl]-2-methyl-l-propanone, 2-hydroxy-2 10 methyl-l-pheyl-l-propanone, and difunctional a hydoxyketones. The preferred embodiment includes a blend of diphenylphosphine oxide and a-hydroxyketone type photoinitiators with a more preferred blend of bis-2,4,6 trimethylbenzolydiphenylphosphine oxide and difunctional 15 a-hydroxy-cyclohexyl-phenyl-ketone. At least one photoinitiator is added to the preferred formulations in amounts sufficient to obtain the desired cure response. In preferred formulations of the 20 invention, a blend of at least two photoinitiators is included in amounts of about 0.25% to about 15% by weight. The range of the first preferred photoinitiator (a diphenylphosphine oxide type as noted above) is about 0.5% to about 2.5% in certain embodiments. The range of the 25 second preferred photoinitiator (an a-hydroxyketone type as noted above) is about 4% to about 13% in certain embodiments. In certain inventive formulations, a further benefit is gained by the addition of a third photoinitiator, for example a hydroxyalkylphenone type 30 photoinitiator, in the range of about 0.5% to about 4.5%. The amounts of photoinitiator(s) included will vary based upon many factors such as the types of UV cure equipment, the UV equipment set up, cure rate and durability desired.

16 Preferred coating compositions for use in the invention also include stabilizing materials to maximize exterior durability and UV resistance. Suitable stabilizers include hindered amines and UV absorbers such as 5 benzotriazole or benzotriazine derivatives. The amount of stabilizers in the system vary depending on application parameters and desired performance properties to maximize weatherability without sacrificing cure response and surface hardness. In more preferred compositions, the hindered 10 amine is in the range of about 0.5% to about 4.5%, hydroxyphenyl benzotriazine (or other suitable compound) is in the range of about 2% to about 15% and an antioxidant is in the range of about 0.25% to about 2.0%. 15 Preferred coating compositions for use in the invention include one or more inert solvents. In certain embodiments, the compositions include a blend of inert solvents. Examples of suitable inert solvents include ester solvents such as ethyl acetate and butyl acetate; ketone 20 solvents such as acetone and methyl ethyl ketone; alcohol solvents such as isopropyl alcohol and secondary butyl alcohol. The amount and type of solvent in the composition will vary depending on application method and equipment capabilities and preference. For example, in a flowcoat or 25 curtain coat application, inert solvents should not be excessively aggressive to the base plastic of the molded article. In certain forms of the invention, the inert solvent content in the coating composition as a whole can range from 0% to 80% by weight with a preferred solvent 30 content of 35% to 65% by weight.

WO 2009/145781 PCT/US2008/065301 17 Various other additives can also be included in coating compositions of the invention to further improve appearance and/or performance properties of the cured coating. Examples of suitable additives are reactive and 5 non-reactive acrylic or silicone flow, slip and mar and leveling agents that assist in substrate wetting and leveling of the composition and phenolic based antioxidants that provide thermal and process stability. One particularly preferred additive is a polysilixoane 10 solution, such as that commercially available under the tradename Byk 301 (BYK-CHEMIE, Wallingford, CT) In certain preferred embodiments, a resin blend coating composition is provided that includes an inert 15 organic solvent in an amount of about 10-50% by weight, a first aliphatic urethane acrylate as discussed above in an amount of about 3% to about 20% by weight, a second aliphatic urethane acrylate as discussed above in an amount of about 3% to about 20% by weight, a reactive 20 diluent component in an amount of about 5% to about 30% by weight wherein the reactive diluent component includes one or more multifunctional acrylates, one or more photoinitiators, e.g. selected from those identified herein, and one or more light stabilizers, e.g. selected 25 from those identified herein. More preferred compositions of this embodiment further include an antioxidant and a flow additive, e.g. as identified herein. In certain forms, in the preparation of the first aliphatic urethane acrylate, X of Formula I represents isocyanate groups. In 30 other preferred forms, X of Formula I represents isocyanate group-containing radicals that also contain iminooxadiazine dione groups; or X of Formula I represents isocyanate group-containing radicals that also contain 18 isocyanurate groups; or X of Formula I represents isocyanate group-containing radicals that also contain uretdione groups; or X of Formula I represents isocyanate group containing radicals that also contain, urethane groups; or X 5 of Formula I represents isocyanate group-containing radicals that also contain allophanate groups; or X of Formula I represents isocyanate group-containing radicals that also contain biuret groups; or X of Formula I represents isocyanate group-containing radicals that also contain 10 oxadiazine trione groups. In these embodiments, the first aliphatic urethane acrylate, and the second aliphatic urethane acrylate, may also have any of the other characterizing features as disclosed herein. 15 Coating compositions for use in the invention can be applied to a selected article by various conventional coating methods such as conventional spray, HVLP spray, air assisted/airless spray, rotary atomization, flowcoat, curtain coat or rollcoat. Further, the coating compositions 20 can be applied directly to the substrate or over a previously-cured or uncured coating. The desired film thickness of the cured film formed with coating compositions of the invention is about 3 microns to about 40 microns with the most preferred dry film thickness being about 5 microns 25 to about 20 microns. Once applied, the coating composition can be cured by irradiation with ultraviolet energy as is known to those skilled in the art. In this regard, the irradiation is 30 continued until curing is complete, with preferred exposure times typically being less than 300 seconds and more preferably about 20 to about 100 seconds. Curing temperatures can range from room temperature to the heat WO 2009/145781 PCT/US2008/065301 19 distortion temperature of the substrate, while curing distances are typically between about 2 and 18 inches from the UV source achieving a minimum of about 100 mW/cm 2 of intensity. 5 An ultraviolet light source having a wavelength range of between about 180 nanometers and 450 nanometers is preferred for curing the topcoat. Acceptable light sources that emit ultraviolet energy include sunlight, sun 10 lamps, LED lamps, carbon or xenon arc lamps, and mercury vapor lamps. More preferred examples of suitable light sources include electrode type arc lamps or electrodeless type microwave lamps equipped with mercury vapor type or metal halide type bulbs that provide strong UV energy 15 output in the aforementioned range. The most preferred irradiation is achieved through a series of medium to high pressure mercury lamps having an intensity of about 100 W/in to about 600 W/in and 20 provides about 1500 to about 15000 mJ/cm 2 of UV energy in about 20 to about 75 seconds of exposure when measured with a suitable compact radiometer. More preferred energy 2 outputs are about 3000 to about 8000 mJ/cm2. It should be noted that intensity and energy measurement equipment vary 25 depending on the bandwidths that they measure. When the aforementioned preferred coating compositions are processed under these described irradiation conditions, the final coatings provide a unique blend of properties that adequately protect the molded plastic article from 30 environmental and chemical degradation under severe exposure conditions.

20 In the invention, coating compositions as described herein are used to form a coated article, especially a coated plastic article such as one made with polycarbonate or polyester. Preferred embodiments provide coated plastic 5 lenses, and in particular forms coated, clear plastic lenses such as vehicle forward lighting lenses, e.g. made with polycarbonate. In this regard, with reference to Figures 1 and 2, shown is one embodiment of a coated vehicle forward lighting lens. Lens 11 is illustrative of a "wrapped 10 lighting" lens in which the lens includes a significant upper component 12 that occurs in a non-vertical orientation (e.g. including at least about 10% of the total external surface area of the lens) and is designed into the hoodline of the vehicle 13, and thus is more directly exposed to 15 incident radiation from sunlight. Such wrapped lenses have become common in current vehicles, and present challenges for coatings designed to provide UV protection to prevent yellowing due to sun exposure. In preferred inventive embodiments, the exterior surface 14 of the lens 11, 20 including the exterior surface of the upper component 12, is topcoated with a UV-cured, clear coating composition of the invention. Additional embodiments of the present invention thus provide such coated forward vehicle lighting lenses as well as vehicles including them. 25 For the purpose of promoting a further understanding of the invention and certain embodiments thereof, the following Examples are provided. It will be understood that these Examples are illustrative, and not limiting, in 30 nature.

WO 2009/145781 PCT/US2008/065301 21 EXAMPLE 1 Preparation of UV Curable Blend Compositions The components listed in Table 1 are combined using 5 known techniques to form a UV curable resin blend composition including amounts of the first and second urethane acrylate resins as described hereinabove, along with multifunctional acrylates, photoinitiators, light stabilizers, an antioxidant and a flow improver. One or 10 more inert solvents as described above can be included in the composition to alter its flow properties. TABLE 1 Weight Percent Component: (exclusive of solvent) First Urethane 10 -40% Acrylate Resin Second Urethane 20 - 50% Acrylate Resin Multifunctional Acrylate #1 5 - 55% (functionality = 2) Multifunctional Acrylate #2 5 55% (functionality = 3) Photoinitiator #1 0.25 - 2.5% Photoinitiator #2 4 - 9% Photoinitiator #3 0.5 - 4% Hindered Amine Light 0.5 - 4.5% Stabilizer WO 2009/145781 PCT/US2008/065301 22 Benzotriazine Absorber 2 - 15% Antioxidant 0.25 - 2.0% Flow Additive 0.1 - 5.0% EXAMPLE 2 5 Preparation of UV Curable Blend Compositions The components listed in Table 2 are combined using known techniques to form a UV curable resin blend composition including amounts of the first and second 10 urethane acrylate resins as described hereinabove, along with multifunctional acrylates, photoinitiators, light stabilizers, an antioxidant and a flow improver. One or more inert solvents as described above can be included in the composition to alter its flow properties. 15 TABLE 2 Weight Percent Component: (exclusive of solvent) First Urethane 10 -40% Acrylate Resin Second Urethane 20 -50% Acrylate Resin Organic-Inorganic 5 - 35% Hybrid Acrylate Multifunctional 5 - 55% Acrylate #1 WO 2009/145781 PCT/US2008/065301 23 (functionality = 2) Multifunctional Acrylate #2 5 - 55% (functionality = 3) Photoinitiator #1 0.25 - 2.5% Photoinitiator #2 4 - 13% Hindered Amine Light 0.5 - 4.5% Stabilizer Benzotriazine Absorber 2 - 15% Antioxidant 0.25 - 2.0% Flow Additive 0.1 - 5.0% 5 EXAMPLE 3 Preparation of Coated Plastic Article by Flowcoat Method A formulation of Example 1 or 2 is prepared also containing one or more inert solvents to achieve a 10 specific gravity that will result in desirable film thickness range upon cure. The preferred specific gravity is in the range of less than about 0.975. Coating is applied to an injection molded polycarbonate lens mounted on a fixture by a flowcoat method in which coating is 15 applied only to the top and side surfaces of the lens. The wet coated lens is subjected to a short ambient flash followed by a convection heated air flash to evaporate solvent. The wet coated lens is then exposed to irradiation with a 240 W/cm standard mercury lamp at WO 2009/145781 PCT/US2008/065301 24 intensity of about 450 mW/cm 2 in air resulting in a coated article with a coating dry film thickness of about 8 - 12 microns. 5 EXAMPLE 4 Preparation of Coated Plastic Article by Spray Method 10 A formulation of Example 1 or 2, also containing one or more inert solvents, is applied to an injection molded polycarbonate lens by a spray method using a conventional spray gun mounted on a robot. A programmed spray pattern is used to achieve consistent coverage of the coating and 15 cured dry film thickness in the range of 8 to 12 microns. The wet coated lens is subjected to heated convection air to evaporate solvent prior to an irradiation with a 240 W/cm standard mercury lamp at intensity of about 450 mW/cm 2 in air. 20 The uses of the terms "a" and "an" and "the" and similar references in the context of describing the invention (especially in the context of the following claims) are to be construed to cover both the singular and 25 the plural, unless otherwise indicated herein or clearly contradicted by context. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and 30 each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, 25 or exemplary language (e.g., "such as") provided herein, is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention unless otherwise claimed. No language in the specification should 5 be construed as indicating any non-claimed element as essential to the practice of the invention. While the invention has been illustrated and described in detail in the drawings and foregoing description, the 10 same is to be considered as illustrative and not restrictive in character, it being understood that only the preferred embodiment has been shown and described and that all changes and modifications that come within the spirit of the invention are desired to be protected. 15 In addition, all publications cited herein are hereby incorporated by reference in their entirety. Throughout this specification and the claims which 20 follow, unless the context requires otherwise, the word "comprise", and variations such as "comprises" and "comprising", will be understood to imply the inclusion of a stated integer or step or group of integers or steps but not the exclusion of any other integer or step or group of 25 integers or steps. The reference in this specification to any prior publication (or information derived from it), or to any matter which is known, is not, and should not be taken as an 30 acknowledgment or admission or any form of suggestion that that prior publication (or information derived from it) or known matter forms part of the common general knowledge in the field of endeavour to which this specification relates.

Claims (24)

1. A product, comprising: - a molded plastic article; and - a cured coating formed with a composition characterized by: - a first aliphatic urethane acrylate resin formed by the reaction of an aliphatic polyisocyanate component comprising iminooxadiazine dione, isocyanurate, uretdione, urethane, allophanate, biuret or oxadiazine trione groups, with an alcohol component comprising at least one monobasic, hydroxylfunctional linear or branched alkyl ester of meth(acrylic) acid; and - a second aliphatic urethane acrylate resin formed by the reaction of a multifunctional acrylate with an aliphatic urethane based on a polymer of alkyl carbomonocycle diisocyanate.

2. The product according to claim 1, wherein the composition further comprises one or more inert solvents.

3. The product according to claim 2, wherein, exclusive of the inert solvent(s), the composition comprises about 10% to about 40% by weight of the first aliphatic urethane acrylate resin.

4. The product according to claim 3, wherein, exclusive of the inert solvent(s), the composition comprises about 20% to about 50% by weight of the second aliphatic urethane acrylate resin.

5. The product according to claim 4, wherein the first urethane acrylate resin has an average molecular weight of about 800 to about 2,500 Daltons and the second urethane acrylate has an average molecular weight of about 500 to about 2,000 Daltons.

6. The product according to claim 4, wherein the first urethane acrylate comprises about 3 to about 5 polymerizable acrylate groups per molecule. 27

7. The product according to claim 6, wherein the second urethane acrylate comprises about 4 to about 7 polymerizable acrylate groups per molecule.

8. The product according to any one of the preceding claims, further comprising one or more multifunctional acrylates having an average molecular weight between about 170 and 1,000 Daltons.

9. The product according to claim 8, wherein said one or more multifunctional acrylates comprises at least two multifunctional acrylates.

10. The product according to any one of the preceding claims, wherein the composition further comprises at least one photoinitiator and at least one UV sensitizer.

11. The product according to claim 10, wherein the at least one photoinititator comprises one or more members selected from the group consisting of diphenylphosiphine oxides, pheylglyoxylates, a hydoxyketones and difunctional a-hydoxyketones.

12. The product according to claim 10, further comprising a hindered amine light stabilizer and a UV absorber.

13. The product according to claim 12, wherein the UV absorber comprises a benzotriazole or a benzotriazine.

14. The product according to claim 1, further comprising an organic inorganic hybrid material.

15. The product according to any one of claims 1-14, wherein said polyisocyanate component comprises iminooxadiazine dione groups. 28

16. The product according to any one of claims 1-14, wherein said polyisocyanate component comprises isocyanurate groups.

17. The product according to any one of claims 1-14, wherein said polyisocyanate component comprises uretdione groups.

18. The product according to any one of claims 1-14, wherein said polyisocyanate component comprises urethane groups.

19. The product according to any one of claims 1-14, wherein said polyisocyanate component comprises allophanate groups.

20. The product according to any one of claims 1-14, wherein said polyisocyanate component comprises biuret groups.

21. The product according to any one of claims 1-14, wherein said polyisocyanate component comprises oxadiazine trione groups.

22. The product according to any one of claims 1-21, wherein the molded plastic article comprises a clear polycarbonate lens.

23. The product according to claim 22, wherein the lens comprises a vehicle forward lighting lens.

24. A process for forming a coated article, comprising the steps of: - coating an article with a coating composition characterized by: - a first aliphatic urethane acrylate resin formed by the reaction of an aliphatic polyisocyanate component comprising iminooxadiazine dione, isocyanurate, uretdione, urethane, allophanate, biuret or oxadiazine trione groups, with an alcohol component comprising at least one monobasic, hydroxylfunctional linear or branched alkyl ester of meth(acrylic) acid; and 29 - a second aliphatic urethane acrylate resin formed by the reaction of a multifunctional acrylate with an aliphatic urethane based on a polymer of alkyl carbomonocycle diisocyanate; and - curing the coating composition.