AU2014200267B2 - Brazing material, a method of brazing, a brazed article and a paste comprising this brazing material - Google Patents

Abstract

The present invention relates an iron based brazing material comprising an alloy consisting essentially of: 15 to 30 wt% chromium (Cr); 0 to 5.0 wt% manganese (Mn); 15 to 30 wt% nickel (Ni); 1.0 to 12 wt% molybdenum (Mo); 0 to 4.0 wt% copper (Cu); 0 to 1.0 wt% nitrogen (N); 0 to 20 wt% silicone (Si); 0 to 2.0 wt% boron (B); 0 to 16 wt% phosphorus (P); optionally 0.0 to 2.5 wt% of each of one or more of elements selected from the group consisting of carbon (C), vanadium (V), titanium (Ti), tungsten (W), aluminium (Al), niobium (Nb), hafnium (Hf), and tantalum (Ta); the alloy being balanced with Fe, and small inevitable amounts of contaminating elements; and wherein Si, B and P are in amounts effective to lower melting temperature, and Si, B, and P are contained in amounts according to the following formula: Index = wt% P + 1.1 x wt% Si + 3 x wt% B, and the value of the Index is within the range of from about 5 wt% to about 20. The present invention relates also to a method of brazing article of stainless steel, and an article of stainless steel.

Description

Brazing material, a method of brazing, a brazed article and a paste comprising this brazing material The present invention relates to a high alloyed iron-based braze filler material, a method of brazing, a product brazed with the high alloyed iron based braze filler material. 5 The Invention Objects of different steel materials or iron-based alloy materials are usually assembled by brazing or soldering with Nickel-based or Copper based brazing materials. Hereinafter the term brazing is used, but it 10 should be understood that the term also comprises soldering. Brazing is a process for joining parts of metals, but brazing can also be used for sealing objects or coating objects. The brazing temperature is below the original solidus temperature of the base material. During brazing of materials the brazing material is completely or partly melted during the 15 heat treatment. Traditional brazing of iron-based materials is performed by Nickel-based or Copper-based brazing materials, and these brazing materials can cause corrosion due to for example differences in electrode potential. The 20 corrosion problem will be enhanced when the brazed object is exposed to a chemically aggressive environment. The use of Nickel-based or Copper-based brazing material can also be limited- in a number of food applications due to jurisdictions. 25 One problem is the melting point of the coating or brazing materials, which are highly alloyed. When selecting a brazing material or a coating material considerations are based on the solidus or liquidus temperatures of the alloy and the base material. Lately iron-based brazing materials have been developed for brazing objects of traditional stainless steel. 30 These iron-based brazing materials are functioning quite well. One 2 problem will evidently occur when the base material of an object is a high alloyed iron-based material, since these lately developed iron-based brazing materials will have a different electrode potential compared to the high-alloyed iron-based material. Differences' in electrode potential 5 between the brazed areas and the base material of the object can cause corrosion problems when the high-alloyed steel objects are use in certain environments and applications. The high-alloyed steels have been developed to obtain improved properties for applications in environments, which are corrosive, chemically aggressive etc. Therefore there is a need 10 that the brazing material, when brazing highly alloyed steels, has similar properties such as corrosion resistance as the high alloyed base material, otherwise the brazing material may be limiting the properties of the brazed product. 15 High-alloyed iron-based materials are today mainly welded, since the difference in properties between the present brazing materials like for instance Cu-, Ni, and Fe based brazing materials are too wide. The welding technique is costly and time consuming and thus not wished for because the welding normally results in quite large stresses in the 20 produced product. Accordingly, the present invention provides a new iron-based brazing material, which has a more equal electrode potential between the brazed areas and the high-alloyed iron-based base material of the object. The 25 present invention does also have a property to braze an area below the temperature where the brazing material is fully melted and be able to fill and wet the area and crevices etc. when brazing. The present invention thus relates to an iron-based brazing material comprising an alloy containing three or more elements of the group consisting of iron (Fe), 30 chromium (Cr), nickel (Ni), copper (Cu) and molybdenum (Mo). The alloy 3 contains also one or more melting point depressing elements selected from the group consisting of silicon (Si), boron (B), and phosphorus (P). According to one alternative may the' alloy contain an amount of chromium (Cr), an amount of nickel (Ni), and an amount of molybdenum 5 (Mo), which being defined by the formula (wt% Cr + wt% Ni + wt% Mo) > 33 wt%. According to another alternative may the amount of chromium (Cr), the amount of nickel (Ni), and the amount of molybdenum (Mo), be defined by the formula (wt% Cr + wt% Ni + wt% Mo) ? 38 wt%. According to another alternative may the alloy contain one or more melting point 10 depressing elements in amounts defined by the formula Index = wt% P + 1.1 x wt% Si + 3 x wt% B, wherein the value of the Index is within the range of from about 5 wt% to about 20 wt%. According to a further alternative of the invention may the iron-based 15 brazing material comprise an alloy containing elements of the group consisting of iron (Fe), chromium (Cr), nickel (Ni), copper (Cu) and molybdenum (Mo), and melting point depressing elements, which comprise one or more of the elements of the group consisting of silicon (Si), boron (B), and phosphorus (P), wherein Si, B and P are present in 20 amounts according the following formula: Index = wt% P + 1.1 x wt% Si + 3 x wt% B wherein the value of the Index is within the range of from about 5 wt% to about 20 wt%, and that chromium (Cr), nickel (Ni), and molybdenum (Mo), being within the ranges defined by the formula wt% Cr + wt% Ni + wt% Mo > 33 wt%, or by the formula wt% Cr + wt% Ni + wt% 25 Mo > 38 wt%, with the proviso that Fe, Cr, Ni, Mo and Cu are present in the alloy and that wt% of Fe > wt% of Cr and that wt% of Ni > wt% of Mo. The present invention relates also to an iron-based brazing material comprising an alloy containing essentially 15 to 30 percent by weight, 30 hereinafter wt%, chromium (Cr), 0 to 5.0 wt% manganese (Mn), 15 to 30 4 wt% nickel (Ni), 0 to 12 wt% molybdenum (Mo), 0 to 4.0 wt% copper (Cu), 0 to 1.0 wt% nitrogen (N), 8.0 to 12 wt% silicone (Si), 0.1 to 1.5 wt% boron (B), 0 to 16 wt% phosphorus (P), and optionally 0.0 to 2.5 wt% of each of one or more of elements selected from the group consisting of carbon (C), vanadium (V, titanium 5 (Ti), tungsten (W), aluminium (Al), niobium (Nb), hafnium (Hf), and tantalum (Ta); the alloy being balanced with Fe, and small inevitable amounts of contaminating elements; and wherein Si, B and P are in amounts effective to lower melting temperature, and Si, B, and P are contained in amounts according to the following formula: Index = wt% P + 1.1 x wt% Si + 3 x wt% B, and the value of the 10 Index is within the range of from about 5.5 wt% to about 18 wt%. According to one alternative of the invention may the alloy consist of the above-mentioned elements wherein chromium is within the range from about 18 to about 26 wt% or nickel is within the range of from about 16 to about 26 wt% or molybdenum is within the range from about 1.0 to about 12.0 wt%, or combinations thereof. 15 According to another alternative of the invention may the alloy consist of the above-mentioned elements wherein chromium is within the range from about 19 to about 25 wt% or nickel is within the range of from about 17 to about 26 wt% or molybdenum is within the range from about 3.5 to about 8.0 wt%, or combinations thereof. According to another alternative of the invention may the alloy consist of 20 the above-mentioned elements wherein copper (Cu) being within the range 0.1 to 4.0 wt%. According to another alternative of the invention may the alloy consist of the above-mentioned elements wherein molybdenum is within the range from about 2.0 to about 12.0 wt%. According to another alternative of the invention may the alloy consist of the above-mentioned elements wherein molybdenum is 25 within the range from about 3.0 to about 9.0 wt%.

5 According to one alternative aspect of the invention may any one of the elements selected from the group consisting of carbon (C), vanadium (V), titanium (Ti), tungsten (W), aluminium (Al), niobium (Nb), hafnium (Hf), and tantalum (Ta) be in an amount within the range from about 0 to 1.5 5 wt%. According to yet another alternative aspect of the present invention may the contaminating elements in the alloy be any one of carbon (C), oxygen (0), and sulphur (S). According to another alternative may Ni be present 10 in the alloy and the amount is within the range of 0.1 to 1.0. According to another alternative may manganese be present in the alloy and the amount is within the range of 0.1 to 4.5. According to yet another alternative aspect of the present invention may the alloy contain silicone within the range from about 8.0 to about 12 wt% or boron within the range 15 from about 0.1 to about 1,0 wt% or phosphorus within the range from about 5.0 to about 14 wt%, or combinations thereof. According to yet another alternative aspect of the present invention may the alloy contain silicone within the range from about 8.0 to about 12 wt% 20 or boron within the range from about 0.1 to about 1.0 wt% or phosphorus within the range from about 5.0 to about 14 wt%, or combinations thereof. According to yet another alternative aspect of the present invention may the alloy contain silicone within the range from about 8.0 to about 12 wt% 25 and boron within the range from about 0.25 to about 0.80 wt% B. According to yet another alternative aspect of the present invention may the alloy contain phosphorus within the range from about 7.0 to about 13 wt%. 30 6 According to yet another alternative aspect of the present invention may the alloy contain silicone within the range from about 2.0 to about 8.0 wt% and phosphorus within the range from about 2.0 to about 8.0 wt%. 5 According to further alternative aspect of the present invention may the alloy contain silicone less than 10 wt% or boron less than 1.5 wt% or phosphorus less than 12 wt%, or combinations thereof. According to further alternative aspect of the present invention may the 10 alloy contain silicone within the range of from about 8.0 to about 12 wt% and boron is within the range of from about 0.1 to about 1.5 wt%. According to further alternative aspect of the present invention may the alloy contain silicone within the range of from about 2.5 to about 9.0 wt% 15 and phosphorous is within the range of from about 2.5 to about 9.0 wt%. The brazing cycle involves both melting and solidifying of the brazing material. The melting temperature and solidifying temperature may be the same for very specific materials, but the usual situation is that materials 20 are melting within temperature range of melting, and solidifying within another temperature range of solidifying. The temperature range between the solidus state and the liquidus state is herein defined as the temperature difference between the solidus state and the liquidus state, and is measured in a number of *C. The brazing material of the invention 25 has thus a temperature range between the solidus state and the liquidus state, which according to one alternative aspect of the invention. may be within a temperature range of 200"C. According to another alternative may the alloy have solidus temperature and a liquidus temperature within a temperature range of 150*C. According to another alternative may the 30 alloy have solidus temperature and a liquidus temperature within a 7 temperature range of 100 0 C. According to another alternative aspect of the invention may the alloy have solidus temperature and a liquidus temperature within a range of 750C. According to another alternative aspect of the invention may the alloy have solidus temperature and a 5 liquidus temperature within a range of 500C. The alloy of the invention may suitable be obtained by gas or water atomising processes, by melt-spinning process, by crushing of ingots containing the iron-based alloy material, or by mixing alloy such as high 10 alloyed steels with alloys containing Si, P, B, or combinations thereof, in a higher amount than the high alloyed steels used when blending or by mixing alloy such as alloys with high chromium content, nickel content, molybdenum content, or combinations thereof, with alloys containing Si, P, B, or combinations thereof, in a higher amount than the alloys used 15 when blending. According to a further alternative aspect of the present invention may the iron-based brazing material be manufactured as a paste. The iron-based brazing paste of the invention may comprise the iron-based brazing 20 material and an aqueous binder system or an organic binder system. The binder system may comprise a solvent, which could be hydrophilic or hydrophobic i.e. water-based or oil-based. The oil-based binder could be polymers such as poly (met) acrylate. among others, Could be biopolymers such as cellulose derivatives, starches, waxes, etc. 25 According to another alternative may the iron-based brazing paste of the invention comprise the iron-based brazing material and an aqueous binder system or an organic binder system based on a solvent such as water, oils, or combinations thereof. The alloy comprised in the paste may be in form of powder, granules etc. 30 8 The present invention relates also to a method of brazing articles of stainless steel, comprising the following steps: step (i) applying the brazing material of the invention on to parts of stainless steel; step (ii) optionally assembling the parts; step (iii) heating the parts from step (i) or 5 step (ii) in a non-oxidizing atmosphere, in a reducing atmosphere, in vacuum or combinations thereof up to a temperature of at least 900*C, and then brazing the parts at the temperature of at least 10700C for at least 15 minutes; and optionally step (iv) repeating one or more of step (i), step (ii) and step (iii). Different brazed products need different brazing 10 procedures; some products could be brazed by just going through step (i), step (ii) and step (iii), but other products are more complicated and one or more of step (i), step (ii) and step (iii) need to be repeated is indicated in step (iv). 15 According to an alternative of the invention the parts are brazed at the temperature of at least 1100*C. According to an alternative of the invention may the method also comprise that the parts in step (iii) are heated in a non-oxidizing 20 atmosphere, in a reducing atmosphere, in vacuum, or combinations thereof, up to a temperature of at least 250 0 C for at least 10 minutes, then heating the parts up to a temperature of less then 10800C for at least 30 minutes, then heating the parts up to a temperature over about 1100C for less than 720 minutes, and then cooling the parts. 25 According a to one alternative of the invention may the heating the parts up to a temperature over about 1100"C be for less than 360 minutes before the cooling the parts. According a to another alternative of the invention may the heating the parts up to a temperature over about 30 1100*C be for less than 180 minutes before the cooling the parts.

9 According to an alternative of the invention may the method also comprise that the parts in step (iii) are preheated to a temperature below 1120"C before heating to a temperature of about 1200*C for at least 30 5 minutes. According to another alternative of the invention may the method also comprise that the parts in step (iii) are preheated up to a temperature below 1120"C before heating up to a temperature within the range from 10 11500C to 1250*C for at least 30 minutes. According to another alternative of the invention may the method of also comprise that the parts in step (iii) are preheated to a temperature below 10400C before brazing at a temperature within the range from 1050*C to 15 1150 0 C for at least 15 minutes. According to an alternative of the invention may the method also comprise that the parts in step (iii) are preheated up to a temperature below 11200C before heating up to a temperature of app. 1200"C for at 20 least 120 minutes. And then heat treating the parts at a temperature above 9500C for at least accumulated 20 min, this can be made in the braze cycle, but also after the braze in e.g. at a second heating source. According to another alternative may the brazing material be sprayed as 25 a powder on the surfaces, which shall be joined by for instance by a paint spray gun", rolling, brushing, thermal spraying, e.g. high velocity gxygen fuel (HVOF) etc or may the surface, joint etc. be coated by melts. The iron based brazing filler material may be applied to planar surfaces or 30 to large surfaces by the aid of capillary force breakers. The capillary force 10 breakers can be in form of grooves, traces, paths, passages, v or u shaped tracks or pathways etc. or in form of nets etc. The iron-based brazing filler material may be applied into the capillary force breakers, i.e. into the grooves, traces, paths, passages, v or u shaped tracks, 5 pathways, nets etc., or may the brazing filler material be applied close to the capillary force breakers. During heating the applied iron-based brazing filler material will flow to the area where the capillary force may be broken and braze together the surfaces, which are adjacent to each other. Thus, the brazed area provides brazed, sealed or tight cervices, 10 joints etc. between planar surface where it is hard otherwise to braze uniformly. The capillary force breakers enable also brazing of surfaces having large crevices, parts having odd shape, etc. When the brazing material is applied between two parts close to a 15 capillary force breaker the flowing viscous brazing material will stop the flowing motion and set at the rim of the capillary force breaker. A reactor channel may be functioning as a capillary force breaker. A plate having a reactor channel is applied with brazing material and a barrier plate or the like is placed in contact with the reactor channel plate. The flowing 20 brazing material will stop and set at boarder of the reactor channel, which will seal the reactor plate against the barrier plate without filling the reactor channel with set brazing material. How far the brazing material can flow between two bordering surfaces 25 depends, partly on the brazing materials setting time and the distance between the surfaces, and the amount of brazing material. Since the brazing material "sticks" to each surface, which is to be brazed, the intermediate space between the surfaces becomes smaller. As the intermediate space becomes smaller while at the same time the brazing 30 material sets, it also becomes more difficult for the brazing material to _11 flow in between. The desired amount of brazing material is supplied to the contact points, which are to be brazed together in any of the described or other ways. The brazing material may cover an area that is somewhat larger than the contact joint point. The contact joint points may have a 5 diameter of at least 0.5 mm. Since the brazing process is a metallic process and the respective surfaces for brazing take the form of metallic material, then iron-based brazing material during the brazing process diffuses with bordering surfaces, which are to be brazed together. The joint or seam between the two joined surfaces will more or less 10 "disappear" during. the brazing process according to one aspect of the invention. The brazed seam together with the surfaces of the metallic parts will become a unity with only small changes in material composition of the alloys. 15 During brazing will the brazing material migrate by capillary forces to areas to be joined by brazing. The brazing material according to the invention has good wetting ability and good flow ability, which will result that residual alloys around the brazing areas will be small. According to one alternative will the residual alloys after brazing have a thickness less 20 than 0.1 mm on the applied surfaces. The present invention relates also to an article of stainless steel obtained by the present method. The present invention relates further to a brazed article of stainless steel, which comprises at least one base material of 25 stainless steel and brazed brazing material of the invention. According to one alternative aspect may the articles or the parts be selected from reactors, separators, columns, heat exchangers, or equipments for chemical plants or food plants, or for car industry. 30 According to another alternative aspect may the objects be heat -- 12 exchangers, plate reactors, or combinations thereof. According to another alternative aspect of the invention may the brazed article be a paring disc, which is used in a separator. According to one alternative aspect may the articles, be brazed heat exchanger plates, brazed reactor plates, or 5 combinations thereof. When the parts are heat exchanger plates, the plates can be endplates, adaptor plates, sealing plates, frame plates etc., and constitute a heat exchanger system. Each of the heat exchanger plates comprise at least 10 one port recess, which port recesses together form part of a port channel when the plates are placed on one another. The plates are stacked together in a plate stack or a plate pack in the heat exchanger. The plate package comprises between the plates a number of channels, which accommodate a number of media. The media in adjacent channels are 15 subject to temperature transfer through the heat transfer plate in a conventional manner. The plates may comprise an edge, which may partly extend down and over the edge portion of an adjacent heat transfer plate in the plate stack. The edges of the plates seal against the adjacent heat transfer plate in such a way that a channel may be formed between 20 the plates. This channel either allows flow of a medium or is closed so that no flow takes place and the channel is therefore empty. To stiffen the plate package and the port regions, an adaptor plate or an endplate may be fitted to the package. The surfaces of the endplate or the adaptor plate are with may be planar so that contact surfaces between the surfaces 25 may be maximised. As previously mentioned, the respective port recesses on the plates coincide, thereby forming a channel. On the inside of this port channel there is therefore a joint between the two plates. To prevent leakage at this joint brazing material may be applied round the port region between the plates. The brazing material may be placed in or 30 close by a capillary force breaker, which may extend wholly or partly 13. round the port region between the plates. In the plate package brazing material may be applied on different pre-designed or predetermined parts of the plates. During the brazing process, the brazing material will become viscous and will flow from the applied parts out between the 5 plates due to the action of capillary force. The advantage of applying brazing material on to predetermined places makes it possible to control volume and amount of the brazing material, and to control which parts of the surfaces to be brazed and which are not. When brazing a heat exchanger at least three heat exchanger plates are needed, but it is usual 10 that several plates are brazed together. According to one alternative aspect of the invention are a plate pack of several plates brazed together at the same time in the same furnace. The brazing method of the invention may either comprise brazing the 15 article assembled with all its parts at the same time or may the article be brazed in a stepwise fashion where parts are first assembled and brazed together, and then assembled with further parts and brazed together, and so on using the same type of brazing material in each brazing cycle. 20 Further developments are specified in independent claims and the dependent claims. The invention is explained in more detail in by means the following Examples and Figures 1, 2 and 3. Figures 1 and 2 are showing photos of 25 brazed areas, which are tested in a "bend test". Figure 3 is showing an estimation of melting interval performed by approximation of the melting curve. The purpose of the Examples and Figures 1, 2 and 3 are to test the brazing material of the invention, and are not intended to limit the scope of invention. 30 14 Example I Test samples 1 to 12 were made for checking the solidus and liquidus temperatures of the brazing material of the invention. The compositions of the test.samples are summarised in Table 1. 5 Table I No. Fe Cr Mn Ni Mo Si B P Cu N 1 42.61 20.1 1.03 18.2 6.2 10.58 0.49 0.79 0.19 2 42.04 20.2 1.01 18.3 6.15 10.95 0.57 0.78 0.23 3 41.27 20.4 1.05 18.3 6,11 11.53 0.58 0.76 0.16 4 41.45 20.5 1.05 18.1 6.31 11.22 0.58 0.79 0.065 5 40.84 20.3 0.9 18.4 6.22 11.91 0.66 0.77 0.08 6 41.63 20.5 1.45 18.4 6.18 11.1 0.74 0.13 7 40.33 20.4 1.18 18.1 6.2 13.0 0.79 0.23 8 41.35 20.3 1.1 18.3 6.24 5.66 6.3 0.75 0.095 9 39.49 20:3 1.11 18.1 6.3 6.48 7.5 0.72 0.2 10 37.87 23.0 1.0 19.9 5.95 10.79 0.72 0.77 0.076 11 43.87 20.2 1.15 18.0 6.25 9.46 0.26 0.73 0.08 12 42.547 19.8 1.16 17.8 6.29 11.31 0.28 0.76 0.053 The liquidus and solidus temperature of the samples was tested by means of differential thermal analysis (DTA). The atmosphere used when 10 analysing was Argon. The test was performed with a heating and cooling rate of 10*C/min. The liquidus temperature is the temperature above which a substance is completely liquid. The solidus temperature is the temperature below which a substance is completely solid. The values for 15 the solidus and liquidus temperature were established by estimations where the melting process started and stopped. The estimations were performed by approximation of the melting curve, which was measured and registered as a DTA-curve, see Figure 3. The melting process can be 5 seen in the DTA-curve by the change in the gradient of the heating curve. When the process is finalised, the gradient becomes constant again. To establish the start and stop of the melting process an approximation was made by drawing tangents (5) on the energy drop peak (6). Tangents (7) on the base line is drawn and where the tangents (5) and (7) are crossing 10 each other there are the approximated end values of the melting range. Table 2 Sample No. Solidus Temperature Liquidus Temperature [*Ci ["C] 1 1097 1221 2 1094 1221 3 1101 1216 4 1113 1197 5 1114 1200 6 1038 1074 7 1038 1057 8 1047 1112 9 1037 1119 10 1105 1220 11 1110 1258 12 1111 1242 16 Example 2 A "bend test" was performed on sample no. 6 and a photo was taken on the result, see Figure 1. Sample 6 was placed on a plate of base material 5 and heated in a vacuum furnace for at least 10 minutes at approximately 1200"C. The test plate was then cooled to room temperature and a "bend test" was performed. Figure 1 is showing the base material I at the bottom of the photo, a reaction zone 2 above the base material, which reaction zone is a zone where the brazing material and the base material 10 has diffused together. On top of the reaction zone is the brazed material 3. The photo is showing that the bending test created a crack 4 in the brazed material 3, which was expected. The surprising result was that the crack did not pass the reaction zone 2, but instead the crack turned and stopped. To double check the result a new test was made using sample 15 no. 7 and the same procedure, see photo in Figure 2. The second test did result with a similar crack, which also was turning away from the reaction zone. 20

Claims (14)

1. An iron based brazing material including an alloy consisting essentially of: (i) 15 to 30 wt% chromium (Cr); (ii) 0 to 5.0 wt% manganese (Mn); (iii) 15 to 30 wt% nickel (Ni); (iv) 1.0 to 12 wt% molybdenum (Mo); (v) 0 to 4.0 wt% copper (Cu); (vi) 0 to 1.0 wt% nitrogen (N); (vii) 8.0 to 12 wt% silicone (Si); (viii) 0.1 to 1.5 wt% boron (B); (ix) 0 to 16 wt% phosphorus (P); optionally one or more of elements selected from the group consisting of carbon (C), vanadium (V), titanium (Ti), tungsten (W), aluminium (Al), niobium (Nb), hafnium (Hf), and tantalum (Ta), wherein the amount of each element is within the range from about 0.0 to about 2.5 wt%; the alloy being balanced with Fe, and small inevitable amounts of contaminating elements; and wherein Si, B and P are in amounts effective to lower melting temperature, and Si, B, and P are contained in amounts according to the following formula: Index = wt% P + 1.1 x wt% Si + 3 x wt% B, and the value of the Index is within the range of from about 5 wt% to about 20 wt%.

2. The brazing material according to claim 1 , wherein the contaminating elements are any one of carbon (C), oxygen (0), and sulphur (S).

3. The brazing material according to claim 1 or 2, wherein chromium is within the range from about 18 to about 26 wt% or nickel is within the range of from about 16 to about 26 wt% or molybdenum is within the range from about 2.0 to about 12.0 wt%, or combinations thereof.

4. The brazing material according to claim 1 , 2 or 3, wherein silicone is within the range from about 8.0 to about 12 wt% or boron is within the range from about 0.1 to about 1.0 wt% or phosphorus within the range from about 5.0 to about 14 wt%, or combinations thereof. 18

5. The brazing material according to any one of the preceding claims, wherein silicone is within the range of from about 2.5 to about 9.0 wt% and phosphorous is within the range of from about 2.5 to about 9.0 wt%.

6. The brazing material according to any one of the preceding claims, wherein the alloy contain an amount of chromium (Cr), an amount of nickel (Ni), and an amount of molybdenum (Mo), which being defined by the formula (wt% Cr + wt% Ni + wt% Mo) > 33 wt%.

7. The brazing material according to any one of the preceding claims, wherein copper being present in the alloy within the range 0.1 to 4.0 wt%.

8. The brazing material according to any one of the preceding claims, wherein the alloy is produced by gas-atomising or water-atomising or melt spinning.

9. A method of brazing articles of stainless steel, including the following steps: (i) applying the brazing material according to claims 1 to 8 to parts of stainless steel; (ii) optionally assembling the parts; (iii) heating the parts from step (i) or step (ii) in a non-oxidizing atmosphere, a in reducing atmosphere, in vacuum or combinations thereof, up to a temperature of at least 900<0>C, and brazing the parts at the temperature of at least 1070<0>C for at least 15 minutes; (iv) and optionally repeating one or more of step (i), step (ii) and step (iii).

10. The method of brazing according to claim 9, wherein the parts in step (iii) are preheated to a temperature below 1120<0>C before brazing at a temperature within the range from 11 50[deg.]C to 1250[deg.]C for at least 30 minutes.

11. The method of brazing according to claim 9, wherein the parts in step (iii) are preheated to a temperature below 1040<0>C before brazing at a temperature within the range from 1050<0>C to 11 50[deg.]C for at least 15 minutes. 19

12. A brazed article obtained by the method according any one of claims 9 to 11.

13. The brazed article according to claim 12, wherein the article is a plate heat exchanger.

14. A paste including the iron-based brazing material according to any one of claims 1 to 8 and an aqueous binder system or an organic binder system, water based, oil-based or combinations thereof, wherein the oil- based binder could be polymers such as poly (met) acrylate, biopolymers such as cellulose derivatives, starches, waxes, or combinations thereof. ALFA LAVAL CORPORATE AB WATERMARK PATENT AND TRADE MARKS ATTORNEYS P31886AU01