AU2009201545A1 - Ductile magnesium alloy - Google Patents
Ductile magnesium alloy Download PDFInfo
- Publication number
- AU2009201545A1 AU2009201545A1 AU2009201545A AU2009201545A AU2009201545A1 AU 2009201545 A1 AU2009201545 A1 AU 2009201545A1 AU 2009201545 A AU2009201545 A AU 2009201545A AU 2009201545 A AU2009201545 A AU 2009201545A AU 2009201545 A1 AU2009201545 A1 AU 2009201545A1
- Authority
- AU
- Australia
- Prior art keywords
- magnesium alloy
- total weight
- relative
- magnesium
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
Australian Patents Act 1990 - Regulation 3.2 ORIGINAL COMPLETE SPECIFICATION STANDARD PATENT Invention Title Ductile magnesium alloy The following statement is a full description of this invention, including the best method of performing it known to me/us: P/00/01I la The present invention relates to a corrosion-resistant magnesium alloy. It is known that magnesium alloys are corrosion-resistant if the copper, iron and nickel contents are very small. In the alloys of the AZ (magnesium with aluminium and zinc), AM (magnesium with aluminium and manganese) , AS (magnesium with aluminium and silicon) and AJ (magnesium with aluminium and strontium) groups, the maximum permitted levels are mostly set at 250 ppm copper, 10 ppm nickel and 50 ppm iron. According to Bakke et al., Soc. Automotive Engineers, paper 1999-01-0926, 1999, pages 1-10 and Kammer (Ed.): Magnesiumtaschenbuch, Aluminiumverlag Dasseldorf, 2000, 1 st edition, marked corrosion occurs above all due to pitting if the maximum permitted levels of copper, nickel and/or iron are exceeded. Secondary magnesium alloys can be prepared with much less expenditure of energy than primary alloys, but inevitably contain copper, nickel and iron in quantities above the maximum permitted levels. Magnesium alloys with copper, nickel and/or iron contents below the maximum permitted levels can be produced only at very high cost, or not at all, by recycling bought scrap. A corrosion-resistant secondary magnesium alloy is however known from WO 2007/009435 Al. Despite higher copper and nickel contents, the magnesium alloys disclosed in WO 2007/009435 Al display corrosion properties comparable with or better than a high-purity primary magnesium alloy, and contain 10-20 wt.-% aluminium, 2.5 to 10 wt.-% zinc, 0.1 to 2 wt.-% manganese, 0.3 to 2 wt.-% copper and/or up to 1.5 wt.-% total nickel, cobalt, iron, silicon, zirkon, beryllium. However, these alloys have the drawback that they are comparatively brittle, which makes them unusable for some processing methods -2 such as extrusion, forging, rolling but also for applications which require energy absorption via plastic deformation. The object of the present invention is thus to provide a corrosion-resistant magnesium alloy which can be prepared without a very high expenditure of energy by recycling bought scrap and is ductile. This object is achieved by a magnesium alloy containing, relative to the total weight of the magnesium alloy, 1 to 9 wt.-% aluminium, 0.6 to 6 wt.-% zinc, 0.1 to 2 wt.-% manganese, 0 to 2 wt.-1 rare earth elements, 0.5 to 2 wt.-% copper, wherein the weight ratio of aluminium to zinc lies in the range from 1:1 to 2:1. Preferred embodiments result from the dependent claims. Surprisingly it was found that, despite higher copper contents in the magnesium alloy according to the invention, the corrosion behaviour is similarly good compared with high-purity primary magnesium alloys. Furthermore, the magnesium alloy according to the invention remains ductile. The aluminium content of the magnesium alloy according to the is preferably, relative to the total weight of the magnesium alloy, 2 to 7.5 wt.-%, more preferably 3 to 6 wt.-%. The zinc content of the magnesium alloy according to the invention is preferably, relative to the total weight of the magnesium alloy, 1 to 5 wt.-%, more preferably 2 to 4 wt.-%. The manganese content of the magnesium alloy according to the invention is preferably 0.1 to 1 wt.-%, more preferably 0.2 to 0.75 wt.-%. The copper content of the magnesium alloy according to the invention is preferably 0.5 to 1 wt.-%, more preferably 0.5 to 0.7 wt.-%.
-3 Furthermore, it was surprisingly found that, by adding rare earths such as cerium, neodymium, yttrium, scandium, gadolinium or mixtures of same, the corrosion behaviour is further improved. In particular the negative influence of nickel can - if present - thus be reduced. The total rare earth elements content preferably lies in the range of up to 2 wt.-%, relative to the total weight of the magnesium alloy. The magnesium alloy according to the invention can further contain nickel, iron and/or silicon. It is preferred that the nickel content is less than 0.005 wt.-%, relative to the total weight of the magnesium alloy, more preferably less than 0.001 wt. -%, even more preferably less than 0.0005. The iron content should be less than 0.05 wt.-%, relative to the total weight of the magnesium alloy, preferably less than 0.01 wt.-%, more preferably less than 0.005 wt.-% and the silicon content should be less than 0.1 wt.-%, relative to the total weight of the magnesium alloy, preferably less than 0.05 wt.-%. The magnesium alloy according to the invention can be prepared as a secondary alloy by melting scrap or impure magnesium precursors which contain copper, nickel and/or iron, after which the level of constituents in the alloy is set to correspond to that of a magnesium alloy according to the invention. Such a magnesium alloy can be prepared at favourable cost with a comparatively small expenditure of energy. The magnesium alloy according to the invention can be used both as a casting material (sand, ingot, die- and semi-solid casting) and as a kneading material for extrusion, forging, rolling, etc. Example: -4 The invention will now be explained in more detail with the help of the following examples. The comparative corrosion examinations took place by immersion in 3.5% sodium chloride solution and using the salt-spray test according to DIN 50021. In the immersion measurements, the rate of corrosion was determined by measuring the developed quantity of hydrogen. In the salt-spray test, the mass loss is determined. In Table 1 the rates of corrosion of a magnesium alloy according to the invention (AMZC) , a pure, zinc-containing magnesium alloy (AMZ 503), a pure AM50 alloy and a copper-modified AMSO alloy (AMC) are compared. The aluminium, zinc, manganese, copper, nickel, iron and silicon contents of the magnesium alloys listed in Table 1 (in wt.-%) are given in Table 2. Table 3 shows the mechanical properties of the alloy according to the invention and the comparison alloys AMZ501, AMZ502, AMZ505 and AM50 and also AZC1231 according to WO 2007/009435 Al, wherein the remainder is always magnesium. Table 1: Alloy Corrosion rate Corrosion rate Salt-spray test Immersion (mm/year) (mm/year) AMZC 0.6 1.7 AMZ503 0.17 1.1 AM50 0.63 4.5 AMC 8.99 32.9 AZC1231 1.00 6.57 -5 Table 2: Alloy Al Zn Mn Cu Ni Fe Si AMZC 5.59 3.18 0.25 0.54 0.00014 0.0013 0.026 AMZ503 5.3 3.19 0.25 0.0077 0.00021 0.0015 0.028 AM50 4.9 0.02 0.26 0.0077 0.00017 0.00068 0.026 AMC 4.84 0.023 0.26 0.52 0.000082 0.00092 0.028 AZC1231 11.7 3.04 0.48 0.47 0.0032 0.0087 0.39 Table 3: Alloy Yield point Tensile. Elongation at (MPa) strength (MPa) break (%) AMZC 73 226 10.9 AMZ501 67 214 13.2 AMZ502 65 207 10.2 AMZ505 67 193 11.2 AMS0 54 199 13.2 AZC1231 152 189 0.5 The data show that the rate of corrosion of the magnesium alloys according to the invention (AMZC) is comparable with the rate of corrosion of the pure alloys AMZ503 and AMSO or is even improved. On the other hand, the copper-modified AM50 alloy displays an unacceptable rate of corrosion. Without wishing to be bound to a theory, it is presumed that the microstructure of the magnesium alloy according to the invention is characterized by a low level of secondary phases and a change in the beta phase Mg 17 A1 12 . Unlike the alloys known from WO 2007/009435 Al, the secondary phases do not form a network structure. This has a positive effect on the ductility -6 of the alloys according to the invention, as is shown in Table 3. The beta phase is presumably modified by alloying with zinc and partially suppressed and replaced by quaternary MgAlZnCu phases. The local element formers copper, nickel, cobalt and iron and their intermetallic phases are bound in this phase and nickel, cobalt and iron additionally via Al 8 Mns phases and their negative influence on corrosion resistance clearly reduced. The microstructure of the pure AMSO alloy, on the other hand, contains predominantly the beta phase as secondary phase, which accelerates the corrosion via local element formation without formation as a network. The alloy according to the invention can therefore tolerate higher copper, nickel, cobalt and iron contents. The zinc and copper contents increase the strength of the alloy without greatly influencing ductility (see Table 3) and in addition make the alloy more creep-resistant. Also, the magnesium alloys according to the invention, unlike the pure alloys AMZ503 or AM5O, can be prepared with a justifiable expenditure of energy as secondary alloys by melting scrap or impure precursors which contain copper, nickel and/or iron, after which the level of the constituents of the alloy can be set. Throughout this specification and the claims which follow, unless the context requires otherwise, the word "comprise", and variations such as "comprises" or "comprising", will be understood to imply the inclusion of a stated integer or step or group of integers or steps but not the exclusion of any other integer or step or group of integers or steps. The reference in this specification to any prior publication (or information derived from it), or to any matter which is known, is not, and should not be taken as an acknowledgment or admission or any form of suggestion that that prior publication (or information derived from it) or known matter -7 forms part of the common general knowledge in the field of endeavour to which this specification relates.
Claims (11)
1. Magnesium alloy, containing, relative to the total weight of the magnesium alloy, 1 to 9 wt.-% aluminium, 0.6 to 6 wt.-% zinc, 0.1 to 2 wt.-% manganese, 0 to 2 wt.-% rare earth elements, 0.5 to 2 wt.-% copper, wherein the weight ratio of aluminium to zinc lies in the range from 1:1 to 2:1.
2. Magnesium alloy according to claim 1, characterized in that the aluminium content, relative to the total weight of the magnesium alloy, is 2 to 7.5 wt.-%.
3. Magnesium alloy according to one of claims 1 or 2, characterized in that the zinc content, relative to the total weight of the magnesium alloy, is 1 to 5 wt.-%.
4. Magnesium alloy according to one of the preceding claims, characterized in that the manganese content, relative to the total weight of the magnesium alloy, is 0.1 to 1 wt.-%.
5. Magnesium alloy according to one of the preceding claims, characterized in that the copper content, relative to the total weight of the magnesium alloy, is 0.5 to 1 wt.-%.
6. Magnesium alloy according to one of the preceding claims, characterized in that it further contains nickel, iron and/or silicon.
7. Magnesium alloy according to claim 6, characterized in that the nickel content, relative to the total weight of the magnesium alloy, is less than 0.005 wt.-%. -9
8. Magnesium alloy according to one of claims 6 or 7, characterized in that the iron content, relative to the total weight of the magnesium alloy, is less than 0.01 Wt.-%.
9. Magnesium alloy according to one of claims 6 to 8, characterized in that the silicon content, relative to the total weight of the magnesium alloy, is less than 0.1 wt. -%.
10. Method for the preparation of a magnesium alloy according to one of claims 1 to 9, characterized in that magnesium scrap or impure, copper-containing precursors are melted and the level of constituents of the alloy is then set according to one of claims 1 to 9.
11. Use of a magnesium alloy according to one of claims 1 to 9 as a casting and/or kneading material.