AU2006241323C1

AU2006241323C1 - Fiber cement building materials with low density additives

Info

Publication number: AU2006241323C1
Application number: AU2006241323A
Authority: AU
Inventors: James A. Gleeson; David L. Melmeth; Kalynne H. Paradis; Dean M. Seligman; Brian Patrick Sloane
Original assignee: James Hardie Technology Ltd
Current assignee: James Hardie Technology Ltd
Priority date: 2000-03-14
Filing date: 2006-11-22
Publication date: 2017-01-12
Anticipated expiration: 2021-03-09
Also published as: AU2010246457C1; AU2010246457B2; AU2010246457A1; AU2006241323A1; AU2006241323B2

Abstract

This invention relates to a formulation with the addition of low density additives of volcanic ash, hollow ceramic microspheres or a combination of microspheres and volcanic ash or other low 5 density additives into cementitious cellulose fiber reinforced building materials. This formulation is advantageously lightweight or low density compared as compared to current fiber cement products without the increased moisture expansion and freeze-thaw degradation usually associated with the addition of light-weight inorganic materials to fiber cement mixes. The low density additives also give the material improved thermal dimensional stability. K .------ ---- -r

Description

AUSTRALIA PATENTS ACT 1990 COMPLETE SPECIFICATION FOR A STANDARD PATENT ORIGINAL Name of Applicant/s: James Hardie International Finance B.V. Actual Inventor/s: James A.- Gleeson and Kalynne H. Paradis and Brian Patrick Sloane and David L. Melmeth and Dean M. Seligman Address for Service is: SHELSTON IP 60 Margaret Street Telephone No: (02) 9777 1111 SYDNEY NSW 2000 Facsimile No. (02) 9241 4666 CCN: 3710000352 Attorney Code: SW Invention Title: FIBER CEMENT BUILDING MATERIALS WITH LOW DENSITY ADDITIVES Details of Original Application No. 2001250832 dated 09 Mar 2001 The following statement is a full description of this invention, including the best method of performing it known to me/us: File: 36576AUP01 FIBER CEMENT BUILDING MATERIALS WITH LOW DENSITY ADDITIVES Background of the Invention 5 The present application is a divisional application of Australian Application No. 2001250832, which is incorporated in its entirety herein by reference. Field of the Invention This invention relates to building materials and methods for making the same, and more 10 particularly to the addition of low density additives (LDA) into cementitious cellulose fiber reinforced building materials. Description of the Related Art Fiber-reinforced cement (FRC) products such as water-resistant building sheets have been used for building since 1895. In recent history reinforcing fibers used in such products have 15 included not only asbestos fibers, but also cellulose fibers (see Australian Patent No. 515151), metal fibers, glass fibers and other natural and synthetic fibers. Typically, the density of such building sheets is from about 1.2-1.7 g/cm3, the variation in density typically being achievable by compression and dewatering of the fiber cement slurries used in manufacture and by varying the amount of fiber used. At these densities, the cement based matrix has few voids, which results in 20 lower water absorption which has usually been considered necessary for good durability performance of cement matrices. The densities of fiber cement described above mean the products are heavier than timber based products of equal dimension and have reduced workability. Workability encompasses the ease with which the board is handled and installed. Therefore, fiber cement building products are 25 more difficult to cut, machine and nail than timber and timber based products. In this regard, the density of natural timber sheets typically ranges from about 0.7-0.9 g/cm 3 for dry hardwoods and from about 0.38-0.6 g/cm 3 for dry softwoods. Thus, a density-modified fiber cement material with density similar to timber may be expected to improve workability and enable lighter, more nailable, easier to cut and easier to machine products to be manufactured. However, this would 30 have to be achieved while retaining the durability, fire resistant, rot proof and water resistant properties of fiber cement if the density modified fiber cement is to be used in the same range of applications. Prior art describes how lightweight inorganic powders can be added as density modifiers in cement or fiber reinforced cement materials. Low density additives for FRC products are 35 defined as having a loose bulk density of about 0.8glum3 (about 50 lbs./cu.ft.) or less. The typical low density additives (LDA) used include low bulk density calcium silicate hydrates (CSH), expanded polystyrene beads( EPS), expanded vermiculite, expanded perlite, expanded shale, and expanded clay. The density modification of cement-based materials with such inorganic particles is primarily achieved by introducing porosity into the material. Typically, the - 1apore spaces are filled with water when the material is submerged in water or exposed to rain for a length of time. This causes these materials to have poorer wet to dry dimensional stability (moisture resistance), a higher saturated mass, and poor freeze-thaw resistance. Accordingly, there is a need for a lightweight FRC building material and method for 5 manufacturing the same with improved wet to dry dimensional stability over that of typical density modified products. Secondly, the lightweight building material should maintain similar wet to dry dimensional stability as that of FRC products without - 1b- -2 density modifiers if the density modified material is to be used in the same range of applications. In addition, it is highly preferred in some applications that the material also have a low saturated mass, good freeze-thaw resistance, and high temperature dimensional stability. Finally, it is also desirable to have a FRC building product where 5 lower ranges of densities closer to that of timber and timber based products can be achieved with improved durability. Any discussion of the prior art throughout the specification should in no way be considered as an admission that such prior art is widely known or forms part of common general knowledge in the field. 10 [t is an object of the present invention to overcome or ameliorate at least one of the disadvantages of the prior art, or to provide a useful alternative. Summary of the Invention According to a first aspect the present invention provides a building material, comprising: 15 a cellulose fiber-reinforced cement formulation; and a low density additive incorporated into the formulation, wherein the low density additive includes ceramic microspheres, wherein the low density additive lowers the density of the building material to between 0.9 to 1.2 g/cm 3 while at the same time the low density additive maintains moisture expansion of the building material at a level of 20 between about 0.15% and 0.2%. According to a second aspect the present invention provides a building material formulation used to form a building product, comprising: a hydraulic binder; an aggregate; 25 cellulose fibers; and a low density additive, wherein the low density additive includes ceramic microspheres, the building product when formed having a density between 0.9 to 1.2 g/cm 3 while at the same time the low density additive maintains moisture expansion in the building product at a level between 0.15% and 0.2%. 30 According to a third aspect the present invention provides a method of forming a low density building material, comprising: mixing hydraulic binder, reinforcing cellulose fibers, aggregate, a low density additive and water to create a slurry, wherein the low density additive includes ceramic microspheres; - 2a processing the slurry into a green shaped article; and curing the green shaped article to form the low density building material, the building material when formed having a density of between 0.9 to 1.2 g/cm 3 while at the same time the building material with the low density additive maintains moisture 5 expansion at a level between 0.15% and 0.2%. According to a fourth aspect the present invention provides a low density building material when produced by the method according to the third aspect. Preferably the formulation comprises between 7 to 15 wt% cellulose fibers. Preferably the cellulose fiber is wood fiber. 10 Preferably the wood fiber is fibrillated. Preferably the building material is produced by the Hatschek production process. Preferably the formulation comprises about 10-45% Portland cement. Preferably the aggregate comprises silica. Preferably the formulation comprises up to 60% silica. 15 Preferably the formulation comprises about 5-30% microspheres. Unless the context clearly requires otherwise, throughout the description and the claims, the words "comprise", "comprising", and the like are to be construed in an inclusive sense as opposed to an exclusive or exhaustive sense; that is to say, in the sense of "including, but not limited to". 20 Two low density additives have been evaluated that have properties more desirable to FRC building materials than typical low density additives. These two low density additives are volcanic ash and hollow ceramic microspheres. One embodiment of the invention includes the addition of volcanic ash (VA) into an FRC building material. A second embodiment comprises the addition of hollow ceramic 25 microspheres (microspheres) into the FRC building material. A third embodiment incorporates the blending of microspheres with volcanic ash and/or other typical low density additives into the FRC building material. The third emboirnent with a blend of microspheres and VA and/or other low density additives may be more preferable than the first embodiment with the introduction of volcanic ash by itself. The second 30 embodiment with the addition of microspheres by themselves may be more preferable than either the first or third embodiments as described above, depending on the properties being considered for a particular application.

- 2b Compared to current FRC products, one advantage of the first embodiment with volcanic ash is that it provides the product with low densities and improved workability at an economical price, as well as improved dimensional stability over that of typical low density additives. 5 The second embodiment encompasses the addition of microspheres in fiber cement products. Compared to current FRC products, the benefits of adding microspheres include the low density and improved workability of the product without increased moisture expansion or freeze-thaw degradation associated with the addition of lightweight inorganic materials to FRC mixes. Moreover, the addition of microspheres 10 provides improved thermal dimensional stability for FRC material. The third embodiment relates to the addition of microspheres in combination with VA and/or other typical low density additives in FRC material. Blending microspheres with other low density additives is advantageous because lower density FRC products can be achieved with less weight percent addition (as compared to microspheres only) 15 due to the lower densities of VA and other typical LDA relative to microspheres. This also enables fiber cement products to achieve lower density ranges to further improve workability, while microspheres minimize the adverse effects typical low density additives have on wet-to-dry dimensional stability and overall durability. Thus, in one aspect of the present invention, a building material is provided 20 comprising a fiber-reinforced cement formulation and a low density additive incorporated into the formulation. The addition of the low density additive to the formulation lowers the density of the building material as compared to a building material having an equivalent fiber-reinforced cement formulation without the low density additive, while at the same time the building material with the low density 25 additive has less than about a 20% increase in moisture expansion as compared to a building material having an equivalent fiber-reinforced cement formulation without the low density additive. More preferably, the addition of the low density additive to the formulation lowers the density of the building material as compared to a building material having an equivalent fiber-reinforced cement formulation without the low density additive, while at the same time the low density additive either maintains or decreases the moisture expansion of the building material as compared to a building material having an equivalent fiber-reinforced cement formulation without the low density additive. The density of the building material is preferably about 1.2 glcm 3 or less. 5 In another aspect of the present invention, a building material formulation is provided to form a building product. The formulation comprises a hydraulic binder, an aggregate, fibers and volcanic ash. In one embodiment, the volcanic ash improves the workability and lowers the density of the final building product by more than about 10% as compared to a building product made from an equivalent formulation without volcanic ash. In another embodiment, the formulation with volcanic ash has a negigible difference in the moisture expansion of the final product whereby the 10 product either maintains or increases moisture expansion by less than about 20% as compared to a building product made from an equivalent formulation without volcanic ash. For the degree of density modification achieved, this moisture movement increase is surprisingly low. With nominally the same formulation ingredients, it has been found that the differences in moisture expansion for volcanic ash formulations exist. Such differences are primarily due to fluctuations in the surface area of raw materials. 15 In another aspect of the present invention, a method of forming a low density building material is provided. Hydraulic binder, aggregate, volcanic ash and water are mixed to create a slurry. The slurry is processed into a green shaped article. The green shaped article is cured to form the low density building material. In one embodiment, the article is cured by autoclaving. In another embodiment, the low density building material formed has a density of about 1.2 glan 3 or less, and a moisture expansion of about 0.17% or less. 20 In another aspect of the present invention, a building material formulation comprises a hydraulic binder, an aggregate, fibers and hollow ceramic microspheres. The final building material has a density of about 1.2 glcn? or less. In one embodiment, about 4.1%-15% cellulose fibers are provided in the formulation. In one preferred embodiment, the microspheres lower the density of the final building product by more than about 15%, even more preferably more than about 30%, as compared to a building product made from an equivalent formulation without 25 microspheres. In another embodiment, the microspheres decrease the moisture expansion of the final product as compared to a building product made from an equivalent formulation without microspheres, preferably by more than about 5%, more preferably by more than about 10%. In one preferred embodiment, a combination of microspheres with other additional low density additives such as volcanic ash and/or low bulk density CSH are provided in the formulation. 30 In another aspect of the present invention, a method of forming a low density building material, comprising mixing hydraulic binder, aggregate, fibers, hollow ceramic microspheres and water to create a slurry. The slurry is processed into a green shaped article. The green shaped article is cured to form the low density building material. The resulting building material has a density of about 1.2 glem 3 or less. In one embodiment, more than about 4% fibers are mixed to create the slurry. In another embodiment, the article is cured by autoclaving. 35 Brief Description of the Drawings -3- FIGURE 1 is a graph of MIP pore size distribution for a Hatschek manufactured board with and without hollow ceramic microspheres after freeze-thaw testing. FIGURE 2 is a graph of BET pore size distribution for a Hatschek manufactured board with and without hollow ceramic microspheres after freeze-thaw testing. 5 FIGURE 3 is an SEM photograph illustrating a Hatschek manufactured board with 10 wt.% hollow ceramic microspheres showing no degradation after 147 freeze-thaw cycles. FIGURE 4 is a graph illustrating the relationship between low density additive addition, density and strength. Detailed Description of the Preferred Embodiments The preferred embodiments of the present invention describe a fiber-reinforced cement building material 10 incorporating at least one of two low density additives, hollow ceramic microspheres andlor volcanic ash. It wig be appreciated that these additives may be used not only for the types of building materials described herein (i.e., fiber reinforced materials), but may be used for other building materials as well. In addition, various combinations of microspheres andlor volcanic ash with other density modifiers are also contemplated to lower the density and improve the overall performance of the building material. Furthermore,' other low density additives similar to hollow ceramic 15 microspheres and volcanic ash that achieve the properties of lowering density while maintaining or decreasing moisture expansion of the final product, as well as improving workability, durability and other properties (as discussed below), are also contemplated as being within the scope of this invention. 1. First Embodiment -Volcanic Ash In a first embodiment, this invention relates to the addition of volcanic ash into cementitious cellulose fiber 20 reinforced building materials. Volcanic ash is also commonly referred to as "airbome perlite". "pumice" or "pumicsite". Volcanic ash is typically a natural glass derived from the magma of volcanoes during an eruption. Volcanic ash is a relatively lightweight sand sediment formed by the cooling of high temperature magma, giving rise to a material comprising about 30 wt.% crystalline minerals and 70 wt.% amorphous volcanic ash glass. It has a typical bulk density of ab'ut 25-75 lbs.icu.ft. Usually this volcanic ash is expanded with the introduction of heat to change the 25 morphology and achieve a lighter material with a typical bulk density ranging from about 2.25 lbsJcu.ft Expanded volcanic ash can have a wide range of particle sizes from less than about 10 microns up to about 425 microns, with median particles sizes ranging between about 20 to 100 microns. The chemical composition primarily consists of silica (Si0 2 ), alumina (A1 2 01), and potassium oxides (K 2 0). Volcanic ash or expanded volcanic ash is available through suppliers such as Tufflite Inc. of Phoenix, AZ; 30 California Industrial Minerals of Friant, CA; US Pumice of Chatsworth, CA; Amcor Precast of Idaho Falls, ID; Hess Pumice Products of Malad City, ID; Kansas Minerals Inc. of Mankato, KS; Calvert Corporation of Norton, KS; Copar Pumice Company of Espanola, NM; C.R. Minerals of Santa Fe, NM; Utility Block of Alburquerque NM; and Cascade Pumice of Bend, OR. One preferred formulation of the first embodiment of the present invention comprises a hydraulic binder, 35 aggregate, fiber, volcanic ash and additives. The hydraulic binder is preferably Portland cement but can also be, but is -4not limited to, high alumina cement, lime, ground granulated blast furnace slag cement and gypsum plasters or mixtures thereof. The aggregate is preferably ground silica sand but can also be, but is not limited to, amorphous silica, diatomaceous earth, rice hull ash, blast furnace slag, granulated slag, steel slag, mineral oxides, mineral hydroxides, clays, magnasite or dolomite, polymeric beads, metal oxides and hydroxides, or mixtures thereof. The fiber 5 is preferably cellulose wood pulp but can also be, but is not limited to, ceramic fiber, glass fiber, mineral wool, steel fiber, and synthetic polymer fibers such as polyamides, polyester, polypropylene, polymethylpentene, polyacrylonitrile, polyacrylamide, viscose, nylon, PVC, PVA, rayon, glass ceramic, carbon or any mixtures thereof. The additives can include, but are not limited to, silica fume, geothermal silica, fire retardant, thickeners, pigments, colorants, plasticisers, dispersants, foaming agents, flocculating agents, water-proofing agents, organic density modifiers, 10 aluminum powder, kaolin, alumina trihydrate, mica, metakaolin, calcium carbonate, wollastonite, polymeric resin emulsions, or mixtures thereof. Volcanic ash can be used in a variety of building products all having different proportions of hydraulic binder, aggregate, volcanic ash and additives to obtain optimal properties for a particular application (e.g., siding, roofing, trim, soffit, backerboard for tile underlay, etc.). It will be appreciated that the percentage of volcanic ash may be varied 15 depending on the desired application. One preferred composition may include about 5%-80% Portland cement, about 0%-80% silica, about 4.1%-15% cellulose, about 0%-10% additives and about 2%-50% volcanic ash. One particular example of a typical formulation with volcanic ash is as follows: Portland Cement (binder) 28% Silica (aggregate) 54% 20 Cellulose (fiber) 7% Metal Hydroxide (additive) 4% Volcanic Ash (LOA) 7%. Preferably, the cement and silica have a fineness index of about 200 to 450 nIkg. The fineness index for both cement and silica is tested in accordance with ASTM C204-96a. 25 The material may be formed into a green shaped article from a waterbome mixture or slurry by a number of conventional processes as would be known to one of skill in the art, such as the: e Hatschek sheet process; e Mazza pipe process; e Magnani process; 30 S Injection molding; e Extrusion; e Hand lay-up; e Molding; e Casting; 35 e Filter pressing; -5- * Flow on machine, roll forming, etc. with or without post pressing. The processing steps and parameters used to achieve the final product using a Hatschek process are described in Australian Patent No. 515151. The material is preferably pre-cured for up to 80 hours, most preferably 24 hours or less, to establish the 5 formulation to set. The material is then air-cured (approximately 28 days) or more preferably, autoclaved at an elevated temperature and pressure in a steam saturated environment at 120 to 180*C for 3 to 30 hours, most preferably 24 hours or less. The length and time chosen for curing is dependent on the formulation, the manufacturing process, and the form of the article. Test Results 10 Density & Workability The addition of volcanic ash in fiber cement materials lowers density and improves overall workability properties at an economical price while reducing the moisture expansion observed with that of typical low density additives. Products with volcanic ash are lighter, and therefore easier to handle, nail, and score and snap to the desired dimensions. Formulations with volcanic ash also reduce edge cracking or crumbling (if any) when the board is 15 nailed close to the edge (e.g., 318-3141. Tables 1 and 2 below illustrate FRC formulations and test results for these formulations, more particularly demonstrating the advantages of adding volcanic ash to lower density and improve workability. Table 1- Formulations for Table 2 Test Results Fonn . iPortlisd - Sii -Cellulo I-R 8 28.7 60.3 7.0 4.0 K 28.7 52.8 7.0 4.0 7.5 20 Table 2- Comparison of Properties With and Without Volcanic Ash tla 0.D. Density (glcn?) 1.11 1.34 Nail Penetration (Equilibrium conditions) mm. of nail in material 45.4 33.0 50 mm (2 in.) - length of nail Standard Deviation 1.1 1.0 7.5 wt. % of the aggregate from the control, Formulation B, has been displaced by 7.5% Volcanic Ash for Formulation K. -6- 2 Equilibrium conditions - samples are conditioned in a controlled atmosphereof 73±4

*

F and 50±5% humidity. Refer to text below for definition and description of nail penetration test. * Refer to text below for definition and description of nail penetration test. 5 Table 2 above compares test results of 10" x 10" filter pressed prototype boards with and without volcanic ash. Prototype boards are produced by mixing the desired formulation with a Hobart Mixer to form a homogenous slurry. The slurry is then compressed between two steel dewatering plates at 3500 psi for one minute with a Wabash Press (model # PC-75-4TM) to form a monolithic sheet. The slurry is supported with steel wire mesh screens (30 to 10 40 US mesh) placed underneath and on top of the slurry mix within the steel frame mold. The monolithic sheet is then pre-cured for a minimum of about 12 hours and autoclaved at an elevated temperature and pressure in a steam saturated environment at 150 *C for about 12 hours. In Table 2, Formulation K with 7.5 wt.% volcanic ash lowers the density by about 17% from 1.34 glem 3 to 1.11 gicm 3 when compared to an equivalent formulation, Formulation B, the control formulation without volcanic ash. 15 An equivalent formulation is herein defined as one in which the 'preferred LDA (e.g., volcanic ash) is displaced by an equivalent percentage of binder, aggregate andlor additives, and more preferably is displaced by an equivalent percentage of aggregate. This lowered density also improves the nailability, or ease of driving a nail into the board. Testing showed an increase in nail penetration from 33.0 mm to 45.4 mm, where 50 mm represents the length of the nail and therefore the maximum nail penetration attainable. Nail penetration testing consists of nailing a layered stack 20 of board using a Paslode Impulse' cordless framing hardware gun (positive placement) to ensure consistent nailing pressure. The layered stack typically comprises A - 1 'thick board stacked to a height greater than the length of the nail (2 in. or 50 mm). Senco 6d galvanized clipped head nails (part #GC21 AABN) were used. Thus, in one embodiment, as compared to a typical building sheet having a density of about 1.3 glcm", the building material formulation described above results in a final product having a density of less than about 1.2 glcm". 5 More preferably, the addition of volcanic ash to the building material formulation can preferably be adjusted to give a final product density of about 1.2 glcm 3 or less, or about a 10% or more reduction in density as compared to an equivalent formulation without volcanic ash. It is further contemplated that larger additions of volcanic ash will further lower the density of the building product. Wet-Dry Dimensional Stability 30 Cured fiber cement formulations with conventional density modifiers have increased moisture expansion and increased moisture absorption on a percentage weight increase basis compared to FRC formulations with no .DA. One advantage of the first embodiment over prior art is that the addition of volcanic ash attains the desired density and workability with less moisture expansion than other conventional low density additives when introduced on a similar weight percent basis. Wet-dry dimensional stability is desired in building products for quality and durability of the 35 installed product, especially in exterior applications subject to severe climatic changes. Good dimensional stability minimizes any gaps that may open between sheets or lengths of building panel or plank. Good dimensional stability -7also reduces the likelihood of sheet cracking due to developed stress between the dimensionally changing panel or plank and the supporting framework that the product is fastened. Tables 3 and 4 below illustrate FRC formulations and test results for these formulations, more particularly demonstrating the advantages of adding volcanic ash to lower density while minimizing moisture expansion typical of 5 other low density additives added on an equivalent weight basis. Table 3- Formulations for Table 4 Test Results Formda - Portland Sil ia i Celiion. 3pad identification Cement . - Hydroxid Volca i Hydraulic -e, '7 Bind Aggregate Fiber Addftvey,] LDA IDA, B 28.7 60.3 7.0 4.0 K 28.7 52.8 7.0 4.0 7.5 L 28.7 55.3 7.0 4.0- 5.0 Table 4. Moisture Expansion' Comparison of Volcanic Ash & Perlite. pemlation. Detserjton... 11-- 6H ~ ~t ____________y - - 3__ xaso piso~iriefri B2 Control- No LDA 1.33 0.18 ± 0.02 Ka _7.5% VA 1.11 0.17 0.02 -5.5 L 5% Perite 1.22 0.22 ± 0.02 22.2 10 Moisture expansion is the change in product length from saturated to oven dry conditions. The % change moisture expansion equation is: Length. - Lengthf, xl0. Length, 2 Throughout this description of the preferred embodiments Formulation B is used for the control. However, as no one sample incorporating Formulation B is used for all of the tests, nominal differences may be found in the test 15 results for any one sample. 3 7.5 wt. % of the aggregate from the control, Formulation B, has been displaced by 7.5% Volcanic Ash for Formulation K. Table 4 above displays test results of 10' x 10' filter-pressed prototype boards comparing formulations with 20 7.5 wt.% volcanic ash and 5.0% perlite (Harborlite 2000 from Harborlite Corp.), a typical low density additive. Formulation L with 5.0% perlite has a 22.2% increase in moisture expansion from the control whereas Formulation K with 7.5% volcanic ash actually shows a decrease of more than about 5% in moisture expansion from the control. Thus, the addition of volcanic ash provides better dimensional stability than typical density modifiers at equivalent or lower weight percent additions. This allows volcanic ash to achieve lower densities and better 25 workability properties with equivalent or higher additions of volcanic ash relative to conventional low density additives. -8- More preferably, the addition of volcanic ash can be adjusted to show a negligible difference in moisture expansion as compared to an equivalent formulation without volcanic ash. In one embodiment, the volcanic ash preferably will increase the moisture expansion of the final product by less than about 20% compared to a building product formed from an equivalent formulation without volcanic ash, and will more preferably decrease the moisture 5 expansion of the final product. In one preferred embodiment, the moisture expansion of a building product made from a formulation having volcanic ash is about 0.17% or less. 2. Second Embodiment -Hollow Ceramic Microspheres A second embodiment of this invention encompasses the addition of hollow ceramic microspheres into cementitious cellulose fiber-reinforced building materials. This second embodiment with hollow ceramic microspheres 10 may be preferred over the first embodiment including volcanic ash because the addition of microspheres in FRC materials has even better moisture resistance coupled with other durability advantages, including freeze-thaw resistance, and thermal dimensional stability. It will be appreciated that the preferred embodiments for the second embodiment are not limited to these types of microspheres or building materials. Thus, other types of fillers and building materials are also contemplated. 15 Microspheres can be natural, synthetic or a by-product. The material can be crystalline but is more typically amorphous or glass. One preferred type of microspheres are hollow ceramic microspheres commonly known as cenospheres. Cenospheres are a coal ash by-product that is typically separated from fly ash by a floatation process where the spheres float to the surface of water from clarifiers, ponds or lakes. The microspheres are available, for example, under the names Extendospheres', Recyclospheres' and Zeeospheres', and are available from suppliers such 20 as PO Corporation of Chattanooga, Tennessee; Zeelan Industries Inc.13M of St. Paul, Minnesota; Sphere Service, Inc. of Oak Ridge, Tennessee; and Advanced Cement Technologies (A.C.T.) of Blaine, Washington. The microspheres have typical particle sizes ranging from about 12 to 300 microns, with median particle sizes ranging about 80 to 120 microns. These sizes can, of course, vary between samples. The preferred microspheres typically contain about 62-65% silica (SiO 2 ), about 23-26% alumina (A120,) and about 3.0 to 4.0% iron 25 oxides (Fe 2

O

3 ). When introduced into a building material, the microspheres introduce pores in the material that may not readily fill with water, which is advantageous to the material because of a lower saturated mass, improved wet to dry dimensional stability and improved freeze-thaw resistance. One preferred formulation of the second embodiment comprises a hydraulic binder, aggregate, fiber, hollow ceramic microspheres and additives. It will be appreciated that the various components of the preferred formulation 30 for the second embodiment can include any of the aforementioned materials listed for each component in the first embodiment. The material may also be produced by a number of conventional processes and curing conditions as listed and described in the first embodiment. If applicable, the preferences of the raw materials, processes, steps or conditions are similar to that of the first embodiment. The microspheres can be used in a variety of building products all having different proportions of hydraulic 35 binder, aggregate, microspheres and additives to obtain optimal properties for a particular application (e.g., siding, -9roofing, trim, soffit, backerboard for tile underlay, etc.). One preferred composition may include about 5%-80% Portland cement, about 0%-80% silica, about 4.1%-15% cellulose, about 0%-10% additives and about 2%-90% microspheres. One particular example of a typical formulation with microspheres is as follows: Portland Cement (binder) 28.7% 5 Silica (aggregate) 50.3% Cellulose (fiber) 7% Metal Hydroxide (additive) 4% Microspheres (LDA) 10%. It will be appreciated that the percentage of microspheres may be varied depending on the desired 10 application. For instance, high addition percentages (up to about 90 wt.%) of microspheres may be suitable for building materials and systems that require some type of fire resistance rating. The high addition of microspheres provides the material with low thermal shrinkage. Test Results Density 15 Lowering the density with microspheres improves the overall workability of thicker products without compromising the advantages fiber cement products offer with regard to durability (i.e., dimensional stability) and structural integrity. These attributes are particularly advantageous for product thicknesses above about three eighths of an inch (>318'). The products with microspheres are ighter and therefore easier to handle. Secondly, products with microspheres are easier to nail and score I snap to the desired dimension. Furthermore, microsphere formulations 20 reduce edge cracking or crumbling (if any) when the board is nailed dose to the edge (e.g., 318-518"). Tables 5 and 6 below display formulations and test results for FRC formulations, more particularly illustrating the advantages of adding microspheres to a formulation to improve density and workability. Table 5- Formulations for Table U Test Results Cl m- Mta ? e 25 -10- Table 6 - Comparison of Properties With and Without Microspheres Test Method -FornnlatioiiA ormulation B .* 1D%mirospheres- C,-nol f Density (Equilibrium Conditions) 2 (glcm) 1.16 1.39 Nail Penetration (Equilibrium conditions) mm. of nail in material 47.0 31.7 50 mm (2 in.) - length of nail standard deviation 0.9 1.4 110% microspheres in Formulation A replace 10% of the aggregate in the control, Formulation B. 2 Equilibrium conditions- samples are conditioned in a controlled 5 atmosphere of 73±4*F and 50 ±5% humidity. Table 6 displays test results of 3' x 5' Hatschek manufactured board for Formulations A and B. Formulation A with 10 wt.% microspheres reduces the density by about 15% from 1.39 glcr to 1.16 glcm' when compared to an equivalent formulation without microspheres (Formulation B). In addition, the ease of driving a nail into the board is 10 improved. Testing revealed an increase in nail penetration from 31.7 mm to 47.0 mm, where 50 mm represents the length of the nail and the maximum nail penetration attainable. Overall, testing of prototypes and products produced from trials has revealed about a 15% decrease in density for every 10% addition of microspheres and significant improvements in nailing. Thus, the addition of microspheres may advantageously be used to reduce the density of FRC building material by more than about 15%, 15 even more preferably more than about 30%, as compared to an equivalent formulation without microspheres. The present inventors contemplate that with the addition of microspheres, the density of the material can be reduced to about 0.9 glcrm (see Table 10 below), and more preferably, even as low as about 0.5 glcm 3 . Wet-Dry Dimetisional Stability As stated earlier, cured fiber cement formulations with conventional density modifiers have increased 20 moisture expansion and increased moisture absorption on a percentage weight increase basis. One advantage of the preferred embodiments over prior art is that the addition of microspheres to reduce density does not.increase moisture expansion from wet to dry. This is useful for a number of reasons previously mentioned in the first embodiment. Table 7 below displays test results of 3' x 5' Hatschek manufactured board with and without microspheres. Formulation A with 10% microspheres maintains, or more preferably reduces moisture expansion from that of 25 Formulation B without microspheres. Formulations A and B are in Table 5 above. -11- Table 7 - Comparison of Moisture Expansion With and Without Microspheres Test Method .. Foruitioi rmula B 10% Mirs" t o* aIV : - :aL Density (Equilibrium Conditions? (glcm 3 1.16 1.39 Moisture Expansion % Change 0.15 ± 0.02 0.16 ± 0.02 110% microspheres in Formulation A replace 10% of the aggregate in the control, Formulation B. 5 2 Equilibrium conditions - samples are conditioned in a controlled atmosphere of 73±4 0 F and 50±5% humidity. Tables 8-10 below display formulations and test results for 10" x 10" filter pressed prototype boards comparing microspheres with conventional density modifiers that do increase moisture expansion. Conventional density modifiers 10 include low bulk density calcium silicate hydrate (CSH), and expanded polystyrene, vermiculite, perlite, shale or clay. Table 8- Formulations for Tables 9 and 10 Test Results rintlla Portland- Siliice. 'MCell m ul6o s taw - -d - ,.~ I~d~i~e~. sphres es 04 Hydraul A g~- Z B 28.7 60.3 7.0 4.0 C 35.2 52.8 8.0 4.0 D 26.8 40.2 8.0 25.0 E 26.8 40.2 8.0 25.0 F 28.7 55.3 7.0 4.0 5.0 15 Table 9 data below displays a conventional low density additive, low bulk density CSH (Silasorb from Celite Corp.), at a 5% load that increases moisture expansion from that of the control, Formulation B. Table 9- Moisture Expansion of Low Bulk Density CSH Foniu~- ~ escnptio * M i~pasn B Control 1.41 0.162 ± 0.02

F

2 5.0% low bulk density CSH 1.27 0.188 ± 0.02 'Equilibrium conditions- samples are conditioned in a controlled atmosphere of 73±4*F and 50±5% humidity 20 25% low bulk density CSH in Formulation F replaces 5% of the aggregate in the control, Formulation B. -12- Table 10 below compares two formulations with the same base formula, one with 25 wt.% microspheres and the other with 25 wt.% perlite (Aztec XX from Aztec Perlite). Both the perlite and microsphere formulations decrease the density of control Formulation C from 1.3 glcm 3 to around 0.9 glcm 3 , but moisture expansion increases with the perlite formulation and decreases with the microsphere formulation. 5 Table 10- Moisture Expansion Comparison of Microspheres & Perlite. Formulation Descriition. quilibriu'einsity i-' Iisture Exysio% C Control 1.31 0.230 t 0.02 D 25% Microspheres 0.90 0.202 t 0.02 E 25% Perlite 0.89 0.275 ± 0.02 'Equilibrium conditions- samples are conditioned in a controlled atmosphere of 73±4*F and 50±5% humidity 2 For formulations D and E. microspheres displace both the aggregate and hyrdaulic binder in the control, formulation C. Thus, the addition of microspheres to the fiber cement formulation has the effect of maintaining or reducing moisture expansion of the final product. Preferably, the addition of rnicrospheres can be adjusted to reduce the moisture expansion by about 5%, more preferably by about 10% or more, as compared to a similar formulation without 15 microspheres. Freeze-Thaw Resistance Freeze-thaw resistance refers to a material's resistance to damage when exposed to repeated cycles of freezing and thawing. For instance, concrete can be damaged by frost, and especially by repeated cycles of freezing and thawing. Damage usually begins with flaking at the surface, and gradually extends inward, though deep cracks 20 may occur. Damage associated with freezing generally does not occur unless a sufficient quantity of water is present in the pores, and is minimal in dense concrete of low water-to-cement ratio and low permeability. Similar to high density concrete, freeze-thaw damage is minimal in high-density fiber cement. In the preferred embodiments, the addition of microspheres into a FRC formulation produces a lower density cured product that maintains freeze-thaw resistance, unlike prior art where density modifiers added to the formulation reduce a materials 25 freeze-thaw resistance. FIGURES 1 and 2 display pore size distribution graphs of 3' x 5' Hatschek manufactured board using MIP (mercury intrusion porosimetry) and BET (Brunauer, Emmett and Teller) methods. There is less change in pore size distribution for Formulation A with 10 wt.% microspheres after 147 freeze-thaw cycles than Formulation B without microspheres after 126 cycles. This demonstrates the microsphere formulation's resistance to structural change 30 typical of freeze-thaw damage. To further support the microsphere formulation's resistance to freeze-thaw damage, FIGURE 3 displays a SEM (scanning electron microscope) picture of a Hatschek manufactured board (3' x 5') with 10 wt. % microspheres showing no signs of degradation after 147 freeze-thaw cycles whereas other wood cement composites would typically have degradation at this stage. -13- Freeze-thaw testing of FIGURE 3 was performed in accordance with ASTM (American Standard Test Method) C666A titled 'Standard Test Method for Resistance of Concrete to Rapid Freezing and Thawing. This test method has two different procedures, A or B. Procedure A was followed, meaning samples were submerged in water for both rapid freezing and thawing as opposed to rapid freezing in air and rapid thawing in water (procedure 8). 5 Samples are periodically removed from freeze-thaw cycling and visually inspected for degradation such as cracking, moisture expansion, sponginesslwetting throughout the sample, and overall structural integrity. Samples are moved from freeze-thaw cycling when the degree of degradation is such that the sample does not hold together and would therefore not be functional as a building product. High Temperature Dimensional Stability 10 Reducing a building material's thermal shrinkage prevents high temperature stresses and strains from occurring on building components. This improved thermal- dimensional stability allows building components in building fires to maintain a shield to fire without cracking, falling apart and allowing fire to spread quickly. Tables 11 and 12 below display FRC formulations and test results for 10" x 10* filter-pressed prototype boards, more particularly illustrating the advantages of adding microspheres to a formulation to improve high 15 temperature dimensional stability. Table 11- Formulations for Table 12 Test Results Fomla Portland; Silica Celluise kr 5uj Idhiitio- . - idS llyd"AuUli .;- cf4 f_______ Ceindtti r sph ~- ~ ,~44t A 28.7 50.3 7.0 4.0 10.0 B 28.7 60.3 7.0 4.0 F 28.7 55.3 7.0 4.0 5.0 G 28.7 50.3 7.0 4.0 10.0 H 28.7 40.3 7.0 4.0 20.00 Table 12 20 Thermal Shrinkage Comparison of Microspheres & Low Bulk Density CSHI o 9 rcilptioiii'i i q rnlinulith isia iriea B Control 1.41 3.07

F

3 5.0% low bulk density CSH 1.21 7.27

G

3 10.0% low bulk density CSH 1.15 8.09 A' 10.0% microspheres 1.15 4.41

H

3 20.0% microspheres 1.01 4.21 Refer to text below for description of thermal shrinkage test. 2 Equilibrium conditions- samples are conditioned in a controlled atmosphere of 73±4*F and 50*5% humidity. 25 'The percent LDA in formulations F, G, A & H replace an equivalent percent of -14aggregate in the control, Formulation B. At lower load levels (e.g., about 10-20%), microspheres minimize the high temperature thermal shrinkage that occurs when typical inorganic density modifiers are introduced in fiber-cement formulations. Table 12 displays results 5 of the percent thermal shrinkage obtained for Formulation A with 10 wt.% microspheres versus Formulation G with 10 wt.% low bulk density CSH (Silasorb from Celite Corp). Compared to the control (Formulation B), both formulations reduce density from about 1.4 to 1.15 glcn', but the formulation with low bulk density CSH has almost twice the thermal shrinkage as the formulation with microspheres. Moreover, Formulation H with 20.0 wt.% microspheres and a density of about 1.0 glcm 3 has over 40% less thermal shrinkage than Formulation F with only 5.0% low bulk density 10 CSH (Silasorb from Celite Corp.) and a higher density of about 1.2 glcn. High temperature thermal shrinkages were determined using a Thermomechanical Analyzer (TMA). Samples were cut to 10 by 25 mm with up to 12 mm thickness. The temperature of the saturated samples was ramped up at a rate of 20* Ciminute to 950* C and sample dimensions were measured with a macroexpansion probe. Thermal shrinkage was taken as the overall dimensional change from 25" to 950' C, and reported as a percentage of total 15 initial length. Another advantage of using microspheres in fiber-cement formulations is thermal shrinkage decreases as microsphere additions increase. Thermal shrinkage with microspheres is inversely proportional to the weight percent added, whereas thermal shrinkage with conventional density modifiers is directly proportional to the weight percent added. Thus, formulations with higher additions of microspheres (up to about 90 wt.%) have lower thermal shrinkage 20 than formulations with lower additions (up to about 20 wt.%). Table 13 below provides formulations with high additions of microspheres and Table 14 provides the high temperature thermal shrinkage results. Formulations I and J with 70 and 90 wt.% microsphere additions produce thermal shrinkage results of about 2.7 and 1.1%, respectively. Thermal shrinkage for Formulations I and J were determined by cutting samples approximately 10 x 10 x 40 mm long, oven drying, firing f or one hour at 1000 C with a 3 muffle furnace, and allowing to cool to oven dry conditions. The percent thermal shrinkage wasdetermined by measuring the overall difference in length from oven dry to 1000' C, and dividing by the initial oven dry length. Table 13- Formulations For Table 14 Results T. Id* t1 __ _ _ _ _ _ _ _ rir _ _26.2 2.9 0.9 70.0 J 8.7 1.0 0.3 90.0 -15- Table 14- Thermal Shrinkage of High-Addition Microsphere Formulations Formula Thermal Identification SliinIage . 2.7 1.1 Thus, in an embodiment where 20% microspheres are used in the fiber cement formulation, the thermal shrinkage of the final product as compared to an equivalent product made from a formulation without microspheres 5 increases by less than about 50%. As described above, with increasing percentages of microspheres, the percent thermal shrinkage decreases, even to a point where, as compared to a product without microspheres, the final product with microspheres exhibits a lower thermal shrinkage, preferably lower from about 10% to about 70%. More particularly, the thermal shrinkage of the product with microspheres is preferably less than about 4%. 3. Third Embodiment -Microspheres and Other Additives 10 A third embodiment of this invention relates to the adilition of hollow ceramic microspheres in combination with volcanic ash andlor other low density additives in cementitious cellulose fiber-reinforced building materials. Descriptions of volcanic ash and hollow ceramic microspheres are found in the detailed descriptions of the first and second embodiments, respectively. The third embodiment with a blend of microspheres and low density additives may be more preferable than the first embodiment with VA given FRC products can achieve a lower range of densities with 15 improved moisture resistance and durability properties. However, the second embodiment with the independent addition of microspheres may be preferable to this third embodiment because of the superlative durability properties offered by the independent addition of microspheres. The preference of the second embodiment to the third embodiment is dependent on the relative importance of durability in a particular application. Similar to the first and second embodiments, one preferred formulation of the third embodiment comprises of 20 a hydraulic binder, aggregate, fiber, hollow ceramic microspheres, low density additives and other additives. It will be appreciated that the various components of the third embodiment can include any of the aforementioned materials listed for each component in the first embodiment. The third embodiment may also be produced by a number of conventional processes and curing conditions as listed and described in the first embodiment. If applicable, the preferences of the raw materials, processes, steps or conditions are similar to that of the first embodiment. 25 The blending of microspheres with VA and [or low density additives can be used in a variety of building products all having different proportions of hydraulic binder, aggregate, low density additives, and other additives to obtain optimal properties for the particular application (e.g., siding, roofing, trim, soffit, backerboard for tile underlay, etc.). One preferred composition of the third embodiment could include about 5-80% Portland cement, about 0%-80% silica, about 4.1%-15% cellulose, about 0%-10% additives and about 2%-60% microspheres and other typical LDA. 30 One particular example of a typical formulation with a blend of microspheres and a typical low density additive is as follows: -16- Portland Cement (binder) 28.7% Silica (aggregate) 50.3% Cellulose (fiber) 7% Metal Hydroxide (additive) 4% 5 Microspheres (LDA) 10% Volcanic Ash (LDA) 5% It will be appreciated that the percentage of microspheres and other LDA's including VA may be varied depending on the desired application. Test Results 10 Lower Densities with Durability There are several advantages to blending microspheres with VA or other typical low density modifiers such as low bulk density CSH, or expanded polystyrene beads, clay, vermiculite, perlite, and shale. One advantage is that an equivalent or lower density can be achieved with less total weight percent addition (than rnicrospheres only) given the lower densities of VA and other typical LDA compared to microspheres. The lower addition rates with the blend 15 are more economical, and the microspheres minimize moisture expansion associated with the addition of typical inorganic density modifiers. Another advantage to blending microspheres with other typical low density additives is that FRC products can achieve lower density ranges and still maintain sufficient product strength for handling. Thus, higher load levels (on a percent weight basis) of the combination of microspheres and other LDA can be added while minimizing the adverse effects typical low density additives have on dimensional stability and overall durability. 20 The addition of low density additives in all of the embodiments described herein is not the only means of reducing density in cement based formulations, however. Forulations consisting of cement and aggregate without fiber or low density additives have densities typically ranging from about 1.8- 2.1 glcm 3 . Adding fiber to cement formulations is advantageous because fiber also lowers density in addition to providing strength and products suitable for nailing. Densities for fiber cement formulations with greater than about 4 wt.% fiber typically range from about 25 1.2 to 1.4 gicm'. It has been found that FRC formulations with about 4 wt.% or less fiber do not have sufficient strength and ductility for installation. These FRC products are often too brittle and nailing produces cracks or blowouts during installation. Alternatively, fiber additions greater than about 15 wt.% may in some applications be undesirable because fiber in FRC formulations contributes to moisture expansion, increased permeability and overall compromises in durability. 30 Thus, the right balance of fiber must be advantageously determined for a FRC product, which is dependent on the thickness and shape of the particular product. In one embodiment, fiber percentages of about 4.1% to 15% are preferable. Low density additives are added to FRC formulations to provide additional reductions in density from that of the fiber addition. However, in general, the higher the addition of LDA, the lower the strength properties of the FRC product. Therefore, LDA additions are limited because FRC products should preferably maintain a minimum strength 35 for sufficient handling and installation. The maximum IDA addition is dependent on a multitude of factors such as the -17- LDA, the load level of the specific LDA, and the shape of the particular FRC product. The minimum strength required is also dependent on the FRC product's shape and thickness. FIGURE 4 displays a typical relationship of microsphere wt.% additions to density and strength of 10" x 10' filter-pressed prototype boards. Tables 15-17 below illustrate FRC formulations and test results of 10" x 10' filter-pressed prototype boards, 5 more particularly illustrating the advantages of blending microspheres with other low-density additives to achieve lower density ranges and improve durability. Table 15- Formulations for Tables 16 and 17 Fornii Portland Silica. Cellulos9k MritM o- Lo Bulk-,M. identiCtion Ceent -_ sp DeamsitC - - Hydraulit -t - di~e DA Aggregatek -. DAuA Binder B 28.7 60.3 7.0 4.0 G 28.7 50.3 7.0 4.0 10.0 M 28.0 49.0 7.0 4.0 12.0 N 28.4 49.6 7.0 4.0 6.0 5.0 0 28.7 51.3 7.0 4.0 6.0 3.0 10 Table 16 compares the densities of Formulation M with 12 wt.% microspheres, Formulation 0 with a 9 wt.% blend of microspheres and low bulk density CSH, and the control without low density additives. The low bulk density CSH used in Formulation 0 is produced by James Hardie using a process with silica, lime and water that results in a low bulk density material that is substantially CSH in tobermorite form. Further details are described in U.S. Patent 15 Application Serial No. 091058,444 filed April 9, 1998, the entirety of which is hereby incorporated by reference. Relative to the control, the decreases in density for Formulations M and 0 are not significantly different, but the total addition of low density additives with the blend (Formulation 0) is 3% less than Iormulation M with only microspheres. For Formulations M and 0, the subtle differences in wt.% of hydraulic binder and aggregate do not have an impact on density properties. 20 Table 16- Density Comparisons F Dsnliu ~ B Control- No LDA 1.31 M' 12% Microspheres 1.09 0' 6% Microspheres 1.11 _ 3% Low Bulk Density CSH 1 The percent LDA in Formulations M and 0 replace an equivalent percent of aggregate in the control with no LDA, Formulation B. -18- Table 17 below displays test results of 10' x 10" filter-pressed prototype boards with four formulations containing variances primarily only in additions of various low density additives, and a control without any low density additives. Results show that Formulation M with 12 wt.% microspheres reduces density from that of the control from 1.35 gicma to 1.16 glem 3 , but Formulation N with 11 wt.% addition of the microspheresliow bulk density CSH (Silasorb from Celite) blend lowers the density further to 1.10 glcm?. Moreover, moisture expansion for Formulation N with the 11 wt.% microspherestlow bulk density CSH blend and the control without low density additives is not significantly different at 0.167 and 0.163%, respectively. In comparison, Formulation G with only 10 wt.% low bulk density CSH provides about the same density as Formulation N's 11 wt.% blend, but with a notably higher moisture expansion of 0.197%. The subtle wt.% differences of hydraulic binder and aggregate in the formulations do not have 0 an impact on denisty or moisture expansion properties. Table 17 - Moisture Expansion Comparisons formula Description .- Dns(i -isfli Identification - B Control -No LDA 1.35 0.163 ± 0.02 M 12% Microspheres 1.16 0.156 ± 0.02 N 6% Microspheres 1.10 0.167 ± 0.02 5% Low Bulk Density CSH G 10% Low Bulk Density CSH 1.12 , 0.197 ± 0.02 'The percent LDA in Formulations M, N and G primarily replace the aggregate in the control with no LDA, Formulation B. 15 Conclusions In general, it will be appreciated that the preferred embodiments of the present invention, more particularly, a fiber-reinforced building material containing additives of volcanic ash, hollow ceramic microspheres, or a combination of microspheres, volcanic ash andjor other additives, have several advantages over the prior art. These materials have 20 a low density compared to conventional fiber cement building products. This enables production of a thicker product (e.g., 318" to 1.0") that is lighter and therefore easier to handle, cut, nail and install. The materials also have improved wet-dry dimensional stability and the building material's durability is improved such that building panels do not excessively shrink and crack. Also, excessive gaps between panels or planks do not open up after changes in humidity or from wet to dry seasons. 25 With respect to at least the formulations and building products incorporating hollow ceramic microspheres, the materials' freeze-thaw resistance is maintained at lower density, unlike most inorganic density modified fiber cement materials. This gives these materials good durability in climates that experience frequent freezing and thawing conditions. These materials incorporating microspheresalso have improved fire resistance properties because of improved 30 thermal dimensional stability relative to typical low densityadditives. Thus, the materials are stable in building fires as -19a building component such that the material can maintain a shield to fire without cracking andfalling apart and allowing fire to spread quickly. The preferred embodiments have applicability to a number of building product applications, including but not limited to building panels (interior and exterior), tile backer board (walls and floors), siding, soffit, trim, roofing, fencing 5 and decking. The embodiments illustrated and described above are provided merely as examples of certain preferred embodiments of the present invention. Various changes and modifications can be made from the embodiments presented herein by those skilled in the art without departure from the spirit and scope of the invention. -20-

Claims

1. A building material, comprising: a cellulose fibcr-rcinforced cement formulation; and 5 a low density additive incorporated into the formulation, wherein the low density additive includes ceramic microspheres, wherein the low density additive lowers the density of the building material to between 0.9 to 1.2 g/cm 3 while at the same time the low density additive maintains moisture expansion of the building material at a level of between about 0.15% and 0.2%. 10 2. The building material according to claim 1 wherein said formulation comprises between 7 to 15 wt% cellulose fibers.

3. The building material according to claim 2 wherein said cellulose fiber is wood fiber.

4. The building material according to claim 3 wherein said wood fiber is fibrillated. 15 5. The building material according to any one of the preceding claims, wherein the low density additive substantially maintains or decreases the moisture expansion of the building material as compared to a building material having an equivalent fiber reinforced cement formulation without the low density additive.

6. The building material according to any one of the preceding claims, wherein the 20 median particle size of the low density additive is between about 20 and 120 gm.

7. The building material according to any one of the preceding claims, wherein the formulation incorporates about 5-30% by weight ceramic microspheres.

8. The building material according to any one of the preceding claims wherein said ceramic microspheres are cenospheres. 25 9. The building material according to claim 8 wherein said cenospheres comprise about 62-65% Si0 2 , 23-26% A1 2 0 3 and 3-4% Fe 2 O 3 .

10. The building material according to any one of the preceding claims, wherein the formulation further incorporates a further low density additive in addition to the ceramic microspheres, wherein the further low density additive is calcium silicate hydrate. 30 11. The building material according to Claim 10, wherein the formulation incorporates up to about 30% by weight of a low bulk density calcium silicate hydrate.

12. The building material according to any one of the preceding claims further comprising one or more additives selected from silica fume, geothermal silica, fire - 22 retardant, thickeners, pigments, colorants, plasticisers, dispersants, foaming agents, flocculating agents, water-proofing agents, organic density modifiers, aluminium powder, kaolin, alumina trihydrate, mica, metakaolin, calcium carbonate, wollastonitc, polymeric resin emulsions, or mixture thereof 5 13. The building material according to any one of the preceding claims when produced by the Hatschek production process.

14. A building material formulation used to form a building product, comprising: a hydraulic binder; an aggregate; 10 cellulose fibers; and a low density additive, wherein the low density additive includes ceramic microspheres, the building product when formed having a density between 0.9 to 1.2 g/cm 3 while at the same time the low density additive maintains moisture expansion in the building product at a level between 0.15% and 0.2%. is 15. The formulation according to claim 14 wherein said formulation comprises between 7 to 15 wt% cellulose fibers.

16. The formulation according to any one of claims 14 to 15, wherein the cellulose fiber is wood fiber.

17. The formulation according to claim 16 wherein said wood fiber is fibrillated. 20 18. The formulation according to any one of claims 14 to 17 wherein the hydraulic binder is Portland cement.

19. . The formulation according to Claim 18, comprising about 10-45% Portland cement.

20. The formulation according to any one of Claims 14 to 19, wherein the aggregate 25 comprises silica.

21. The formulation according to Claim 20, comprising up to 60% silica.

22. The formulation according to any one of Claims 14 to 21, further comprising up to 10% additives selected from silica fume, geothermal silica, fire retardant, thickeners, pigments, colorants, plasticisers, dispersants, foaming agents, flocculating agents, water 30 proofing agents, organic density modifiers, aluminium powder, kaolin, alumina trihydrate, mica, metakaolin, calcium carbonate, wollastonite, polymeric resin emulsions, or mixture thereof - 23 23. The formulation according to any one of Claims 14 to 22, comprising about 5 30% microspheres.

24. The formulation according to any one of claims 14 to 23 wherein said ceramic microspheres are cenospheres. 5 25. The formulation according to claim 24 wherein said cenospheres comprise about

62-65% SiO 2 , 23-26% A1 2 0 3 and 3-4% Fe 2 0 3 . 26. The formulation according to any one of claims 14 to 25, wherein the low density additive increases the number of cycles at which the building material begins to visually degrade under freczc-thaw cycling as compared to a building material made 10 from an equivalent formulation without microspheres. 27. The formulation according to any one of claims 14 to 26, wherein the low density additive decreases change in pore size distribution in the building material after undergoing a number of freeze-thaw cycles as compared to a building material made from an equivalent formulation without microspheres. 15 28. The formulation according to any one of claims 14 to 27, wherein the low density additive affects thermal shrinkage of the building material as compared to a building material made from an equivalent formulation without microspheres such that the thermal shrinkage of the building material is less than about 50% greater than that of the building material without microspheres. 20 29. The formulation according to claim 28, wherein the thermal shrinkage of the building material is between about 1% and 5%. 30. The formulation according to any one of claims 14 to 29, further comprising a low bulk density calcium silicate hydrate. 31. A method of forming a low density building material, comprising: 25 mixing hydraulic binder, reinforcing cellulose fibers, aggregate, a low density additive and water to create a slurry, wherein the low density additive includes ceramic microspheres; processing the slurry into a green shaped article; and curing the green shaped article to form the low density building material, 30 the building material when formed having a density of between 0.9 to 1.2 g/cm 3 while at the same time the building material with the low density additive maintains moisture expansion at a level between 0.15% and 0.2%. -24 32. The method according claim 31 wherein said formulation comprises between 7 to 15 wt% cellulose fibers. 33. The method according claim 32 wherein said cellulose fibers are wood fibres. 34. The method according to claim 33 wherein said wood fibres are fibrillated. 5 35. The method according to any one of Claims 31 to 34, further comprising mixing in additives to create the slurry, wherein the additives are selected from one or more of silica fume, geothermal silica, fire retardant, thickeners, pigments, colorants, plasticisers, dispersants, foaming agents, flocculating agents, water-proofing agents, organic density modifiers, aluminium powder, kaolin, alumina trihydrate, mica, metakaolin, calcium 10 carbonate, wollastonite, polymeric resin emulsions, or mixture thereof 36. The method according to any one of Claims 31 to 35, wherein the article is cured by autoclaving, 37. The method according to any one of Claims 31 to 36 wherein the article is produced by the Hatschek production process. 15 38. The method according to any one of Claims 31 to 37 wherein the aggregate comprises crystalline silica. 39. The method according to any one of Claims 31 to 38, comprising about 5-30% microspheres. 40. The method according to claim 39 wherein said ceramic microspheres are 20 cenospheres. 41. The method according to claim 40 wherein said cenospheres comprise about 62 65% SiO 2 , 23-26% A1 2 0 3 and 3-4% Fe2O3. 42. A low density building material when produced by the method according to any one of claims 31 to 41. 25 43. A building material substantially as herein described with reference to any one or more of the embodiments of the invention illustrated in the accompanying drawings and/or examples. 44. A building material formulation used to form a building product substantially as herein described with reference to any one or more of the embodiments of the invention 30 illustrated in the accompanying drawings and/or examples. 45. A method of forming a low density building material substantially as herein described with reference to any one or more of the embodiments of the invention illustrated in the accompanying drawings and/or examples. -25 46. A low density building material when produced by the method substantially as herein described with reference to any one or more of the embodiments of the invention illustrated in the accompanying drawings and/or examples.