AU2005205614B2 - Method and apparatus for testing fibres - Google Patents

Description

WO 2005/068974 PCT/AU2005/000061 METHOD AND APPARATUS FOR TESTING FIBRES FIELD AND BACKGROUND OF THE INVENTION The present invention relates to a method and 5 apparatus for measuring the maturity or degree of cell wall thickening of a sample of naturally occurring cellulosic fibre including cotton fibre. Cellulosic fibre such as cotton typically has a central lumen or hollow region that represents the 10 residual protoplasm of the living fibre cell which has a cell wall. An important property affecting the quality of fibre having the structure of cellulosic fibre is the degree of thickening of the cell wall by cellulose which is sometimes referred to as fibre maturity or circularity. 15 Fabric manufactures and spinners regard fibre maturity as an important indicator of the suitability of the fibre for processing from both a chemical and a physical perspective. For example, immature fibre which is fibre with 20 little or no cell wall thickening is known for causing the following problems during processing: small entanglements called neps; irregularities in processed fibre assemblies including finished yarns; and non-uniform in dyeing of fabrics. 25 More generally immature fibre decreases processing efficiency and particular steps may be taken to reduce the processing difficulties depending on the maturity of the fibre. In addition pressure to manage fibre maturity is 30 increasingly being exerted on research agronomists and plant breeders and therefore there is a need to develop a suitable technique for testing the maturity of cellulosic crops in a farming and harvesting environment. The measurement of fibre maturity particularly 35 cotton fibre has been the subject of 40 years of research and is still viewed as a difficult technical problem. A technique that has in the past been used for measuring WO 2005/068974 PCT/AU2005/000061 -2 fibre maturity involves the direct measurement of the cross-sections of a fibre using a microscope to determine fibre maturity and is regarded as a benchmark for all other tests. However, this direct technique suffers from 5 significant experimental error due to the microscope measurements involved and the limited numbers of fibres that can be practically measured. Other indirect techniques have failed to generate sufficient industry confidence because of their lack of accuracy and/or 10 precision. Polarized light microscopy is a technique that has long been used to investigate the crystalline structures of inorganic and inert organic materials, e.g., minerals, fibres (natural and synthetic), bone, china, 15 chitin and some fixed sections of organisms. The technique has been used extensively in textile and industrial fibre identification and particularly of fibres that exhibit birefringent properties, i.e., fibres that behave like a uni-axial optical crystal. The optical axis 20 in birefringent fibres is usually parallel along the fibre axis with the refractive index being dependent upon the plane of polarization of the incident light. When plane polarized light is transmitted through a birefringent object the light ray is split into two mutually 25 perpendicular vibrating fast and slow rays, which propagate through the object at two different speeds. Upon emerging from the object a phase difference occurs between the fast and slow rays. When recombined into a single ray by passage through a second polarizor 30 (analyzer) the rays interfere with each other, which in turn create different interference colours that highlight different crystalline characteristics. A standard test for determining the maturity of fibres by viewing them through crossed polarizing lenses 35 and a first-order red Selenite compensator plate is described in a text entitled "The Standard Method of Test for Maturity of Cotton Fibres (Sodium Hydroxide Swelling WO 2005/068974 PCT/AU2005/000061 -3 and Polarized Light Procedure), 354-359, Designation: D1442-00, ASTM Textile and Fibre Test Methods 2000". The compensator plate is inserted between the polarizing lenses to increase the level of retardation between the 5 slow and fast rays and hence improve the intensity of colours produced when the rays are recombined. The compensator is also known as wavelength retardation plate or wavelength filter. The standard test involves arranging a bundle of 10 fibres parallel to each other with a minimum of overlapping in a solution such as water or a clear mineral oil on a glass microscope slide. A cover slide is then positioned on top of the fibres before being placed between the crossed polar lens arrangement. The 15 interference colours appearing from the fibres are the result of the optical phenomena described above and have been classified in a text entitled "Polarized Light Preferred for Maturity Tests" Textile World, February 1945, by Grimes. 20 Table 1 below provides the accepted standard interference colours for mature and immature cotton fibres compiled by Grimes. TABLE 1 - Colours of cotton fibres under polarized light 25 FIBRE WITHOUT WITH SELENITE PLATE CLASSIFICATION SELENITE PLATE First Order Additive Subtractive Colours Colours Second Order First Order MATURE light yellow Yellow Light yellow white Green Yellow IMMATURE gray-blue Blue Orange gray Purple yellow I___ _Orange A disadvantage of the standard test is that the WO 2005/068974 PCT/AU2005/000061 -4 operator must make an assessment of the colours of the fibres and make a subjective decision on the colour of the fibres which gives rise to large discrepancies in the results from different laboratories. Furthermore, the 5 test is too slow to be carried out for routine testing applications in terms of both specimen preparation and test time. According to our experience, ordinarily the time period required to carry out the standard test on a sample of fibres is in excess of 30 minutes. There would 10 also be additional time in preparing the specimen prior to testing. It is an object of the present invention to alleviate the disadvantages of the standard test method described above while measuring the maturity or cell wall 15 thickening of cellulosic fibres including cotton. SUMMARY OF THE INVENTION According to the present invention there is provided a method for measuring the maturity of a sample 20 of cellulosic fibre, the method including the steps of: a) exposing the sample of fibres to polarised light; b) capturing one or more images of the sample through crossed polar lenses and compensator plate so that the image(s) include interference colours from the sample; 25 and c) conducting computer analysis on the image(s) captured in step b) to determine the maturity of the cellulosic fibre by comparing the image(s) interference colour data to reference maturity data. 30 The term "interference colours" has a well-known meaning in the field of polarized light microscopy and has been used in this sense throughout the specification. In addition, throughout this specification the term "cellulosic fibre(s)" includes but is not limited to, 35 cotton, linen, rayon, jute and hemp. An advantage provided by the present invention is that the colours of the fibre in the image(s) are not WO 2005/068974 PCT/AU2005/000061 -5 evaluated by an operator as is the case with prior art polarization techniques. In other words, conducting computer image analysis enables the interference colours of fibre to be analytically determined without subjective 5 interpretation. Another advantage provided by the present invention is that the method can be carried out in test times of less than 2 minutes whereas as noted above, conventional polarised light microscopy can take up to 30 10 minutes to perform per sample. It is preferred that step c) involves determining the area of particular interference colours in the image(s). It is preferred that the reference maturity data 15 be in the form of reference colour interference data. It is preferred that the area of interference colours in the image(s) be determined by analysing the areas of any one or a combination of yellow, red, green and blue in the image(s). 20 Surprisingly, we have found that the percent area of interference colours of the fibre relate directly to cotton fibre maturity and contrary to previous thought, maturity can be evaluated completely independently of fibre perimeter or cross-sectional area. This means that 25 the images captured can be analysed to produce values of average fibre maturity and the distribution of fibre maturity, particularly cotton fibre maturity, on the basis of interference colours alone. It is preferred that an algorithm is used to 30 compare the interference colours of the image(s) captured with the reference maturity data to determine an average value and/or distribution of maturity values for the sample. Depending on how the analysis is carried out, it 35 is possible to determine fibre maturity on the basis of each fibre in the image(s), a segment within each image, or on the basis of all of the fibres appearing in one or WO 2005/068974 PCT/AU2005/000061 -6 many images. In the instance when the image(s) captured in step b) is a digital image(s), or is converted into a digital image, it is preferred that the area of particular 5 interference colours appearing in the images be determined by analysing the number of pixels in the image(s) of a particular colour. It is preferred that step c) involves determining the total area of fibre appearing in the image(s). 10 It is preferred that the total area of fibre in the image(s) be determined by any one or a combination of the following: i) the number of fibres in each image(s); ii) the length of the fibres in the image(s); 15 iii) the ribbon width of the fibres in the image(s); and iv) the number of convolutions or twists per unit length of the fibre in the image(s). Although it is possible that the total area of fibre appearing in the image(s) can be determined by 20 analysing the image(s) in colour, it is preferred the method involves converting the image(s) in colour into monochrome image(s) to assist determining features i) to iv) (mentioned in the preceding paragraph). In the situation when the image(s) are captured or are converted 25 into digital image(s), suitable image analysis techniques including pixel analysis can be employed. It is preferred that computer analysis of the image(s) in step c) can also be used for determining the degree of attack on the fibres by micro-organisms 30 including bacteria and fungi. The degree of attack is also an important indicator for fibre that is susceptible to processing problems such as differential dye uptake, and poor spinning performance and yarn quality generally. It is even more preferred that the degree of 35 attack on the fibre involve determining the number and dimensions of surface fractures of the fibres. It is also preferred that the number and WO 2005/068974 PCT/AU2005/000061 -7 dimensions of surface fractures of the fibres be determined by pixel analysis. Although it is possible that the sample of fibre being tested by the present invention can be prepared in 5 several different ways to facilitate their image being captured and analysed, it is preferred that the images of the fibre captured in step b) be captured while the fibre is randomly spread over a microscope slide or alike transparent support member at a density which allows 10 unmitigated expression of the first and second order interference colours. Moreover, it is preferred that the fibre density range from 200 to 300 pg/cm 2 . Unlike conventional prior art techniques, the present invention is capable of operating with fibres overlapping on the 15 microscope slide. It is also preferred that the images be suspended in a liquid medium on the slide. On account that the fibre being tested is a relative small object, it is necessary to magnify the 20 fibre in the image(s) to achieve results of acceptable accuracy. It is possible that the fibre captured in the image(s) be magnified up to 100 times or more. However, it is preferred that the image(s) capture the fibres at a magnification ranging from 1.5 to 5 times its normal size. 25 The magnification used is a trade-off between a too higher magnification which reduces the field of the view and thus the amount of fibre in the image(s) and reducing the magnification to a point where the fibres appearing in the image(s) is too small to be analysed. 30 In order to reduce the impact of increasing the magnification to a point where each image captures only a segment of the fibre being tested, it is preferred that the method also includes capturing a series of images, each of a different segment of the fibre, and that an 35 average value and/or fibre maturity distribution can be determined from the images. In the situation where a series of image(s) are WO 2005/068974 PCT/AU2005/000061 -8 captured, it is preferred that the images capture different segments of the sample of fibre. This may be achieved using different techniques, however, the most straightforward technique would be to move the sample of 5 fibres between each image being captured. According to the present invention there is also provided an apparatus for measuring the maturity or cell wall thickening of a sample of cellulosic fibre, the apparatus including: 10 a) an optical light path having a polarised light source that can be directed through a compensator plate before being transmitted through a sample of fibre being tested and a polarising lens that is crossed to the polarized light source and through which light from the 15 sample can pass; b) an image capturing means for capturing one or more images of the sample in (a) so that the image(s) include interference colours of the sample; and c) a computer capable of analysing the image(s) to 20 determine the maturity of the fibre by comparing the image(s) interference colour data to reference maturity data. It is preferred that the reference maturity data be in the form of colour interference data. 25 In the instance when the image(s) captured are not digital images, it is recommended that the image(s) can be converted into digital image(s) so that the preferred analysis technique in the form of pixel image analysis can be carried out. 30 It is preferred that the polarising lens be crossed at a range from 85 to 95* to the polarized light source. It is even more preferred that the polarising lens be crossed at approximately 90* to the polarized light 35 source. It is preferred that the image capturing means record the image(s) digitally and that the size of each WO 2005/068974 PCT/AU2005/000061 -9 pixel be equal to or greater than 6.45pm X 6.45pm. It is also preferred that the computer be capable of analysing the image(s) captured in a manner described above to determine any one or a combination of the 5 following characteristics of the fibre mentioned above: i) the average maturity and/or a maturity distribution of the sample of fibres; ii) the number of fibres in each image; iii) the ribbon width of the fibres in the image(s); 10 and iv) the number of convolutions or twists per unit length of fibre in the image(s). It is preferred that the optical light path includes: a tungsten filament bulb or white light emitting 15 diode; two polarising lenses that are crossed at approximately 900; and a compensator plate for enhancing the interference colours. It is preferred that the optical light path be incorporated in a microscope that is capable of magnifying 20 the sample of fibres up to 100 times its actual size. However, in order to optimise the accuracy of the apparatus, it is preferred that the image(s) be captured under a magnification ranging from 1.5 to 5 times the actual size. 25 BRIEF DESCRIPTION OF THE DRAWINGS A preferred embodiment of the present invention will now be described with reference to the accompanying drawings, of which: 30 Figure 1 is a schematic illustration of an apparatus utilised for carrying out fibre image analysis; and Figure 2 is a block diagram showing the equipment items and an outline of the steps carried out in conducting fibre image analysis using the apparatus shown 35 in Figure 1.

WO 2005/068974 PCT/AU2005/000061 - 10 DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT The preferred apparatus for conducting image analysis includes a microscope 7, a digital camera 8 for capturing images of a sample of fibres and a computer 9 5 for analysing the images. The microscope is adapted for polarised light microscopy and has an optical light path 10 that includes polarising lenses 11 and 12 and a compensator plate 13 to enhance the interference colours appearing from the 10 sample. The optical light path 10 also includes objectives lenses 14 capable of magnifying the sample of fibres up to 100 times its actual size. Preferably the microscope is operated at a magnification ranging between 1.5X and 5X so that the number of fibres in the images 15 captured is as high as possible without compromising the accuracy of the images captured. The compensator plate 13 is preferably made of a quartz or selenite material which retards the light by at least a quarter of a wavelength and produces the required 20 interference colours on a red background and thus on which the properties of positive and negative bireferingence can be seen. The compensator plate is therefore often referred to a "red plate". The optical light path 10 of the microscope 7 25 also includes a light source 15 that illuminates the fibre being-tested. The type of light source 15 is dependent upon the interference colours to be analysed. According to the preferred apparatus a tungsten filament bulb or white light emitting diode(s) (LEDs) is used with a 30 polarizing lens 11 and analyser 12 ordinarily crossed at 900 to each other and a first-order compensator 13 or full wavelength filter ordinarily mounted at 450 between the crossed lenses 11 and 12 to enhance the interference colours. The light source 15 and the lens 11, 12, 13, 14 35 defining the optical light path 10 are in some respects similar to the systems presently being used by standard polarised light microscopy techniques.

WO 2005/068974 PCT/AU2005/000061 - 11 In addition, if necessary coloured LEDs can be used to augment specific areas of the image by selectively augmenting interference colours that correspond to structural features of the fibres in the images in 5 accordance with standard practices. The microscope 7 also includes a stage 16 upon which the fibres can be presented for analysis. Ideally the stage 16 can be moved in a plane perpendicular to the optical light path 10 by an electric stepping motor that 10 is controlled using software integrated with the image and data analysis software of the computer 9. A microscope slide containing the sample of fibre is mounted to the stage by clamps that prevent the slide from moving so that malfocus effects are kept to a minimum. 15 The camera 8 for capturing the images is mounted on top of the polarized microscope 7 via a standard mount system which is not shown in the Figures. The optical light path 10 may include a condensing lens between the camera 8 and the microscope 7 to reduce the magnification 20 so that a larger field of view can be captured. In this regard a CCD sensor large enough to capture a field of view at the preferred magnification may also be required. The preferred camera 8 is an industrial type colour digital camera that is equipped with a 1.45 25 megapixel 2/3" progressive CCD sensor that uses a Bayer mosaic colour filter. The cell size of each pixel on the sensor is not less than 6.45 pm x 6.45 pm with a spectral response that is relatively stronger in the red colour region than the green or blue regions. A strong yellow 30 response is also recommended. The power and data transfer requirements should ideally be combined in the one cable via an IEEE 1394, USB1 or USB2 interface. In use, it is preferred that the sample of fibres be prepared and presented in a way that provides 35 consistently accurate results. Initially the fibres are guillotined into snippet lengths, e.g., 0.5 mm, 1 mm or 2 mm, and randomly spread over a large, e.g., 50 mm x 70 mm, WO 2005/068974 PCT/AU2005/000061 - 12 glass microscope slide using a spreading device. It is recommended that the density of fibres spread on the slide not compromise the expression of interference colours described in Table 1. A mounting medium providing good 5 contrast is then applied in small drops over the snippets and another glass slide pressed carefully over the top as a cover slide. The microscope slide is then positioned on the microscope stage 16 and the microscope operating nobs 10 adjusted to the desired magnification and illumination of the sample. One or more colour images of the sample are then captured using the digital camera 8. In order to increase the sample size of the fibres being tested and thus reduce 15 the testing error, separate images may be taken of different segments of the sample of fibres. The images are then sent from the camera 8 to the computer 9 which is programmed to analyse the images with reference to a preselected set of reference interference 20 colour data for the type of fibre being tested. Specifically, analysis is carried out by the computer 9 analysing the colour of the pixels in the images which are then compared to maturity reference data to determine maturity values and maturity distributions. 25 Any suitable algorithm may be used by the computer 9 for determining average maturity values and distribution values. The computer 9 may also be programmed so as to be capable of converting colour images into monochrome images 30 whereby the computer 9 can carry out pixel analysis to determine other properties of the fibre in the image(s) such as: * the total area of the fibres in each image; e the number of fibres in each image; 35 e the length of the fibres in the image(s); e the ribbon width of the fibres in the image(s); and 0 the number of convolutions or twists per unit length of WO 2005/068974 PCT/AU2005/000061 - 13 the fibre in the image(s). In addition, if the fibre includes fractures caused by micro-organisms and/or bacteria, the computer 9 can also carry out pixel analysis to determine the number 5 and dimensions of the fractures on the surface of the fibre and thus the level or degree of attack on the fibres. The right hand column in Figure 2 provides a detailed breakdown of the steps taken by the computer 9 10 during the analysis of the image(s). The information included in Figure 2 has been included for illustration purposes only and is by no means limiting of the preferred embodiment. The left hand column of Figure 2 lists the 15 physical features of the apparatus; namely a microscope having an optical path for carrying out polarizing light microscopy, a camera in the form of a digital camera, and computer software operated by the computer 9. The central provides a range of specification data and information on 20 each component of the apparatus. It would be appreciated by those skilled in the art that many modifications may be made to the preferred embodiment without departing from the spirit and scope of the present invention. 25 For example, computer analysis of the images captured may be carried out using any suitable algorithms and programs entered on the computer.

Claims (25)

1. A method for measuring the maturity or cell wall thickening of a sample of cellulosic fibre, the method 5 including the steps of: a) exposing the sample of fibre to polarised light; b) capturing one or more images of the sample through crossed polar lenses and compensator plate so that the image(s) include interference colours from the sample; 10 and c) conducting computer analysis on the image(s) captured in step b) to determine the maturity of the cellulosic fibre by comparing the image(s) interference data to maturity reference data. 15

2. The method according to claim 1, wherein step c) involves determining the area of particular interference colours in the image(s). 20

3. The method according to claim 2, wherein the area of interference colours in the image(s) is determined by analysing the areas of any one or a combination of yellow, red, green and blue in the image(s). 25

4. The method according to claim 2, wherein the image(s) captured are a digital image(s), or are converted into a digital image(s), and the area of particular interference colours appearing in the image(s) is determined by analysing the number of pixels in the 30 image(s) of a particular colour.

5. The method according to any one of claims 1 to 4, wherein conducting computer analysis involves using an algorithm to compare the interference colours of the 35 image(s) captured with reference maturity data to determine an average value and/or distribution of maturity values for the sample. WO 2005/068974 PCT/AU2005/000061 - 15

6. The method according to any one of claims 1 to 5, wherein step c) involves determining a total area of fibre appearing in the image(s). 5

7. The method according to claim 6, wherein the total area of fibre in the image(s) is determined by any one or a combination 6f the following: i) the number of fibres in the image(s); ii) the length of fibre in the image(s); 10 iii) the ribbon width of the fibre in the image(s); and iv) the number of convolutions or twists per unit length of the fibre in the image(s). 15

8. The method according to claim 7, whereby when image(s) captured are colour, the method involves converting the image(s) in colour into monochrome image(s) in determining any one of features i) to iv). 20

9. The method according to claim 7, whereby when the image(s) are captured as digital image(s), or are converted into digital image(s), the method involves pixel analysis in determining any one of features i) to iv). 25

10. The method according to any one of the preceding claims, further including determining the degree of attack on the fibre of the sample using computer analysis of the images to determine the number and dimensions of surface fractures. 30

11. The method according to claim 10, wherein the number and dimensions of surface fractures of the fibres is determined by pixel anaylsis. 35

12. The method according to any one of claims 1 to 11, wherein the image(s) of the fibre captured in step b) is/are captured while the fibre is randomly spread over a WO 2005/068974 PCT/AU2005/000061 - 16 microscope slide at a density that does not mitigate expression of the interference colours.

13. The method according to claim 12, wherein the 5 density of fibre ranges from 200 to 300 pg/cm 2

14. The method according to any one of claims 1 to 13, wherein the image(s) capture the fibres at a magnification ranging from 1.5 to 5 times its normal size. 10

15. The method according to any one of claims 1 to 14, wherein the method also includes capturing a series of images, each of a different segment of the sample fibres, and that an average value and/or fibre maturity 15 distribution is determined from the images.

16. The method according to any one of claims 4, 9 and 11, wherein the size of each pixel is equal to or greater than 6.45pm x 6.45pm. 20

17. An apparatus for measuring the maturity or cell wall thickening of a sample of cellulosic fibre, the apparatus including: a) an optical light path having a polarised light 25 source that can be directed through a compensator plate before being transmitted through a sample of fibre being tested followed by a polarising lens that is crossed to the direction of polarization of the polarized light source; 30 b) an image capturing means for capturing one or more images of the sample of fibres located in the optical light path so that the image(s) include interference colours of the sample; and c) a computer capable of analysing the image(s) to 35 determine the maturity or cell wall thickening of the fibre by comparing the image(s) interference colour data to reference maturity data. - 17

18. The apparatus according to claim 17, wherein the reference maturity data is in the form of colour interference data. 5

19. The apparatus according to claim 17 or 18, wherein the image capturing means record the image(s) digitally and that the size of each pixel be equal to or greater than 6.45pm X 6.45pm. 10

20. The apparatus according to claim 19, wherein the computer is capable of carrying out pixel digital image analysis. 15

21. The apparatus according to any one of claims 17 to 20, wherein the computer be capable of analysing the image(s) to determine any one or a combination of the following characteristics of the fibre: i) the average maturity and/or a maturity 20 distribution of the sample of fibre; ii) the number of fibres in each image; iii) the ribbon width of the fibre in the image(s); and iv) the number of convolutions or twists per unit 25 length of fibre in the image(s).

22. The apparatus according to any one of claims 17 to 21, wherein the optical light path includes: a tungsten filament bulb or white light emitting diode; two 30 polarising lenses that are crossed at approximately 900; and a compensator plate for enhancing the interference colours.

23. The apparatus according to any one of claims 17 35 to 22, wherein the image(s) are captured under a magnification ranging from 1.5 to 5 times their actual size. 140429i1_ (GHMatters) - 17a

24. A method for measuring the maturity or cell wall thickening of a sample of cellulosic fibre substantially as hereinbefore described with reference to the accompanying Figures. 5

25. An apparatus for measuring the maturity or cell wall thickening of a sample of cellulosic fibre substantially as hereinbefore described with reference to the accompanying Figures. 1404291_1 (GHMatlers)