AU2001296513A1 - Spray polyurea coating systems - Google Patents
Spray polyurea coating systemsInfo
- Publication number
- AU2001296513A1 AU2001296513A1 AU2001296513A AU9651301A AU2001296513A1 AU 2001296513 A1 AU2001296513 A1 AU 2001296513A1 AU 2001296513 A AU2001296513 A AU 2001296513A AU 9651301 A AU9651301 A AU 9651301A AU 2001296513 A1 AU2001296513 A1 AU 2001296513A1
- Authority
- AU
- Australia
- Prior art keywords
- weight
- process according
- isocyanate
- isocyanate reactive
- mdi
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Description
SPRAY POLYUREA COATING SYSTEMS
This application claims the benefit of U.S. Provisional Application No. 60/275,928, filed on March 15, 2001, and U.S. Provisional Application No. 60/237,303, filed on October 2, 2000, the subject matter of which are herein incorporated by reference.
BACKGROUND OF THE INVENTION
Spray polyurea systems can be prepared by mixing or combining together a diphenylmethane diisocyanate ("MDI")-containing prepolymer and at least one amine resin.
Spray polyurea systems prepared from MDI-containing prepolymers having a 2,4' MDI-isomer content of about greater than or equal to 25% by weight and more preferably greater than or equal to 30% by weight (hereinafter "high 2,4'-isomer MDI") have several characteristics that coating applicators find attractive. The high 2,4'-isomer MDI content prepolymers have increased storage stability, lower viscosities, and slower reactivity. The slower reactivity allows the spray applicators to use less expensive equipment to spray the polyurea coatings. Spray polyurea coatings prepared with high 2,4'-isomer MDI content prepolymers possess a smoother surface, increased elongation and lower modulus. High 2,4'-isomer MDI content prepolymers also have some negative effects on spray polyurea systems. The coatings obtained from such systems have lower tensile strength and lower tear resistance than coatings prepared from relatively low 2,4'-isomer MDI content prepolymers. The high 2,4'-isomer MDI coatings also develop physical properties at a slower rate.
Coating formulators currently blend a relatively low NCO prepolymer with a high 2,4'-isomer MDI and optionally propylene carbonate to obtain a "quasi-prepolymer." This blend solves several processing problems. The low NCO prepolymer generally is prepared from a difunctional MDI and a difunctional polyol. The high 2,4'-isomer MDI that is blended with the low NCO prepolymer may often have a 2,4'-isomer content of about 30 to 56% by weight, preferably about 50 to 56 % by weight, and more preferably about 56 % by weight. This method of blending prepolymers is currently the preferred method in the industry. The quasi-prepolymer is then combined or mixed with at least one amine resin to form the spray polyurea system. The initial low NCO prepolymers are
generally made from a base MDI isocyanate having a 2,4' -MDI content of at least about 25% by weight of the base isocyanate.
Uretonimine modified MDI has also been used to solve processing problems. A prepolymer made from uretonimine modified MDI with propylene carbonate back-added has increased gel and tack free times. With the exception of elongation, this prepolymer, when combined with at least one amine resin, produces excellent polyurea coatings.
SUMMARY OF THE INVENTION
The present invention relates to new, improved spray polyurea systems and methods for making the same. The spray polyurea systems are prepared by a method comprising the steps:
A) providing a first isocyanate composition of at least one diphenylmethane diisocyanate isomer, the composition containing greater than 75 % by weight 4,4'-MDI;
B) providing a first isocyanate reactive organic material of one or more compounds containing a plurality of isocyanate reactive groups;
C) providing a second isocyanate composition of a mixture of two or more diphenylmethane diisocyanate isomers, wherein the mixture contains at least 25% by weight of 2,4'-MDI;
D) forming an isocyanate group terminated intermediate prepolymer by reacting the first isocyanate reactive organic material with a stoichiometric excess of the first isocyanate composition, wherein the prepolymer contains from 1 to 13% by weight of free isocyanate groups; E) mixing the intermediate prepolymer with the second isocyanate composition to produce a blended quasiprepolymer composition having a final free isocyanate group content of from 12 to 28% by weight;
F) providing a second isocyanate reactive organic material comprising at least one compound which contains two or more isocyanate reactive amine groups; and G) combining the quasiprepolymer composition and the second isocyanate reactive material under conditions suitable for the formation of an elastomer comprising a plurality of urea linkages.
DETAILED DESCRIPTION OF THE INVENTION
The spray polyurea systems generally are prepared by combining or mixing together an "A" component and a "B" component, usually referred to as the "A side" and the "B side". Because of the fast reactivity of an isocyanate and a primary amine, the A and B components should not be mixed together until they reach the spray gun.
The A component includes a prepolymer formed by reacting a low 2,4'-isomer content MDI containing greater than 75% by weight 4,4'-MDI, with an MDI reactive component containing a plurality of isocyanate reactive groups. Preferably, the low 2,4'- isomer content MDI is a relatively pure MDI (as used herein "pure MDI" means MDI having a 2,4'-isomer content of about 1 to 2 % by weight, balance 4,4'-isomer). In an aspect of the invention, the low 2,4'-isomer content MDI has a 2,4'-isomer content of less than 25% by weight. The MDI reactive component is usually a polyol, and any suitable polyol may be used to form desirable prepolymers. For example, the MDI reactive component may comprise at least one material selected from polyols, polyamines, compounds containing both amine and alcohol groups, and mixtures of these. Preferred polyols include polyether diols and triols with number averaged molecular weights of from about 1,000 to about 10,000, with diols being particularly preferred. In an aspect of the invention the MDI reactive component contains at least 75% by weight of one or more nominal diols. Generally, when preparing the prepolymer, excess MDI is reacted with polyol to form an about 5 to 13 % NCO content prepolymer.
After forming the prepolymer, a second isocyanate composition containing a mixture of two or more diphenylmethane diisocyanate isomers with at least 25% by weight 2,4'-isomer content MDI is blended with the prepolymer to form the A component quasi-prepolymer. In an aspect of the invention the second isocyanate composition can have a 2,4'-isomer content of greater than or equal to about 35% by weight, preferably from about 35 to 56% by weight, more preferably from about 50 to 56% by weight, and even more preferably about 56% by weight. Generally, the second isocyanate composition is added to increase the NCO content of the final product to a final free - NCO content of between about 12 and 23 %.
Additives and the like may be added to the A component, depending on desired end properties, processing considerations, etc. For example, it may be desirable to add at
least some non- volatile liquid non-isocyanate-reactive diluent such as an alkylene carbonate. Specific examples of suitable alkylene carbonates include, but are not limited to, ethylene carbonate, propylene carbonate, butylene carbonate, dimethyl carbonate, and the like. Propylene carbonate is preferred. The amounts and types of additives added will vary, as those skilled in the art will understand.
The B component includes any suitable amine resin. Suitable amine resins are disclosed in, for example, U.S. Patent Nos. 5,962,618 and 6,013,755 and may be the same or different from the MDI reactive component used in the A component. Particularly suitable amine resins include, for example, JEFF AMINE® D-2000, JEFF AMINE® T- 5000 (both available from Huntsman Petrochemicals Corp.), ETHACURE® 100
(available from Albemarle Corp., Baton Rouge, LA), UNILINK® 4200, UNILINK® 4100 (both available from UOP, Des Plaines, IL), and mixtures of these. At least some polyether polyol may also be added to the amine resin to form a blend. These blends are known and are used in the spray polyurea industry to produce "hybrid polyurea systems." In an aspect of the invention the B component contains greater than 50% by weight of compounds containing isocyanate reactive amine groups and more preferably it consists essentially of compounds containing isocyanate reactive amine groups. Further, the MDI reactive material may consist predominately of amine terminated polyether resins by weight, the amine terminated polyether resin having a number averaged molecular weight of 2,000 or greater and containing primary or secondary amine termini. Moreover, in an aspect of the invention the amine terminated polyether resin can have number averaged molecular weights of from 2,000 to 5,000 and isocyanate reactive terminal groups of predominately primary amine groups. In a further aspect, the amine terminated polyether resins can consist by weight predominately of diamines or triamines. The MDI reactive material can also further contain by weight at least some (i.e., minor amounts) of a relatively low molecular weight diamine chain extender containing predominately primary or secondary amine groups.
Preferably, the A component and the B component are employed in a 1 : 1 volume ratio. Other volume ratios may also be useful. Moreover, in an aspect of the invention the A component and the B component can be processed as a two component system at an A:B weight ratio of from 60:40 to 40:60. Further, the ratio of isocyanate groups to isocyanate reactive groups in such a two component system can be from 0.9 to 1.15.
The polyurea spray systems can be prepared from high pressure impingement mixing of the A component and the B component. Such processes are well known to the skilled artisan.
A series of coatings was prepared and tested to evaluate the effects of 2,4'-isomer
MDI on spray polyurea systems. It was observed that polyurea coatings prepared from a spray system formed with a prepolymer containing pure MDI as base isocyanate had a much higher tensile strength and tear resistance than coatings prepared from polyurea spray systems prepared from a prepolymer containing 50% by weight 2,4'-isomer MDI as the base isocyanate. While the coating obtained from the polyurea system prepared with the pure MDI-based prepolymer gave the best physical properties when sprayed as a coating, the prepolymer itself was unstable at room temperature and tended to crystallize at room temperature.
Although it is less desirable, it is within the scope of the invention to use prepolymers that are not stable liquids at room temperature (25°C).
From this data it was observed that a prepolymer with a higher pure MDI content would have better physical properties. I have discovered that if a prepolymer is prepared with a high pure MDI content as the base isocyanate and then back blended with an MDI with a high 2,4'-isomer content to form a quasi-prepolymer, then a polyurea spray system coating could be prepared with both low reactivity and high physical properties. Quasiprepolymers prepared in this manner are usually storage stable liquids at room temperature (25°C), like the prepolymers used in prior art spray polyurea systems.
Glossary:
JEFF AMINE® D-2000: A 2000 MW aliphatic primary amine terminated polyoxypropylene diamine, available commercially from Huntsman Petrochemical Corporation.
ETHACURE® 100: An 80:20 mixture of 3,5-diethyl-2,4-toluenediamine and 3,5- diethyl-2,6-toluenediamine, commercially available from Albemarle Corporation.
• RUBINATE® 9009: A quasiprepolymer based on a uretonimine modified mixture of 4,4'-MDI and 2,4'-MDI (with an isomer ratio of about 98:2), commercially available from Huntsman Polyurethanes. This quasiprepolymer has a free isocyanate group content of about 15.6%.
RUBINATE® 9480: A quasiprepolymer based on a mixture of 4,4' -MDI and 2,4'-MDI, commercially available from Huntsman Polyurethanes. This quasiprepolymer has a free isocyanate group content of about 15.0% by weight
Silane A-187: A silane adhesion promoter, commercially available from Witco
(OSi Division).
The following examples are provided to further illustrate the features of the present invention and should not be construed as limiting thereof.
EXAMPLES:
Example 1
A prepolymer was prepared from MDI having about 10 % by weight 2,4'-isomer and about 90% by weight 4,4'-isomer (18.53 % by weight) and a difunctional, ethylene oxide capped, polyether polyol (41.47 % by weight) with a hydroxyl number of 40. This prepolymer was back blended with propylene carbonate (10% by weight) and MI-50, a 1:1 weight ratio mixture of 4,4'-MDI and 2,4'-MDI from Huntsman Polyurethanes (30% by weight) to form a quasi-prepolymer. All weights are based on the total final weight of the quasi-prepolymer. The quasi-prepolymer had an NCO content of 15.1% and a viscosity of about 350 cps at 25°C. The quasi-prepolymer also had an overall 2,4'-isomer content of about 35 % by wt. This prepolymer was sprayed with a B-component to make a polyurea coating (Polyurea Coating I). The B-component was composed of JEFF AMINE® D-2000 amine resin (74.7 wt. % of B-component) and ETHACURE® 100 amine resin (25.3 wt. %). This polyurea spray system was compared to another polyurea spray system prepared utilizing a commercially available prepolymer of similar composition, but having an overall 2,4'-MDI content of less than 2% by weight. This commercial prepolymer is RUBINATE® 9009, and is not a prepolymer according to the invention. Ten percent by weight propylene carbonate was added to the RUBINATE® 9009 before spraying with the B component (Polyurea Coating II). The B-component
was composed of JEFF AMINE® D-2000 amine resin (74.7 wt. % of B-component) and ETHACURE® 100 amine resin (25.3 wt.%). The propylene carbonate slows the reactivity of the A and B components. The reactivity data for (gel and tack-free time), tensile strength, maximum elongation, and tear resistance properties Polyurea Coating I and Polyurea Coating II are shown in Table I.
TABLE I
To the best of my knowledge, the physical properties of Polyurea Coating I are at least comparable to the best combination of physical properties measured for any sprayed polyurea coating in the prior art.
The coatings from this Example 1 were sprayed onto a plastic panel coated with a mold release. The coatings were removed from the plastic panels by gently pulling on one corner of the coating.
Not only does this invention improve the performance of spray polyurea coatings; it also reduces the quantity of 2,4'-isomer MDI required by the plant manufacturing the prepolymer.
Example 2
A prepolymer (Prepolymer III) was prepared from MDI having about 10 % by weight 2,4'-isomer and about 90 % by weight 4,4'-isomer (28.09 % by weight) and a difunctional, polyoxypropylene polyether polyol (46.5 % by weight) with a hydroxyl number of 56. This prepolymer was back blended with MI-50, a 1 : 1 weight ratio mixture of 4,4'-MDI and 2,4'-MDI from Huntsman Polyurethanes, (25.41% by weight) to form a quasi-prepolymer. All weights are based on the total final weight of the quasiprepolymer. The quasi-prepolymer had an NCO content of 15.7 % and a viscosity of
about 898 cps at 25°C. The quasi-prepolymer also had an overall 2,4'-isomer content of about 15.5 %.
A second prepolymer (Prepolymer IV) was prepared from MDI having about 2 % by weight 2,4'-isomer and about 98 % by weight 4,4'-isomer (28.09 % by weight) and a difunctional, polyoxypropylene polyether polyol (46.5 % by weight) with a hydroxyl number of 56. This prepolymer was back blended with MI-50, a 1 : 1 weight ratio mixture of 4,4'-MDI and 2,4'-MDI from Huntsman Polyurethanes, (25.41% by weight) to form a quasi-prepolymer. All weights are based on the total final weight of the quasiprepolymer. The quasi-prepolymer had an NCO content of 15.9 % and a viscosity of about 825 cps at 25°C. The quasi-prepolymer also had an overall 2,4'-isomer content of about 13.3 %.
A third prepolymer (Prepolymer V) was prepared from MDI having about 30 % by weight 2,4'-isomer and about 70% by weight 4,4'-isomer (28.09 % by weight) and a difunctional, polyoxypropylene polyether polyol (46.5 % by weight) with a hydroxyl number of 56. This prepolymer was back blended with MI-50, a 1:1 weight ratio mixture of 4,4'-MDI and 2,4'-MDI from Huntsman Polyurethanes, (25.41% by weight) to form a quasi-prepolymer. All weights are based on the total final weight of the quasiprepolymer. The quasi-prepolymer had an NCO content of 15.7 % and a viscosity of about 919 cps at 25 °C. The quasi-prepolymer also had an overall 2,4'-isomer content of about 21.1 %.
These prepolymers (Prepolymers III, IV, and V) were reactively processed into sprayed polyurea elastomers by using the B-component indicated below to make polyurea coatings (Polyurea Coatings III, IV, and V). This B-component was composed of JEFFAMI E® D-2000 amine resin (52.3 wt. % of B-component), JEFFAMINE® T- 5000 amine resin (10.46 wt.%), ETHACURE® 100 amine resin (26.15 wt.%), Silane A- 187 (0.84 wt.%), and titanium dioxide powder (10.25 wt.%).
These polyurea spray systems were compared to a polyurea sprayed system (Polyurea Coating VI) prepared utilizing a commercially available prepolymer of similar composition. This commercial prepolymer is RUBINATE® 9480, and it is not according to the invention. The B-component was composed of JEFFAMINE® D-2000 amine resin (52.3 wt. % of B-component), JEFFAMINE® T-5000 amine resin (10.46 wt. %), ETHACURE® 100 amine resin (26.15 wt.%), Silane A- 187 (0.84 wt.%), and titanium dioxide powder (10.25 wt.%).
As shown in Table II, Polyurea Coating III had the highest tensile strength and a higher maximum elongation compared to Polyurea Coatings IV and V. Moreover, tear resistance was improved.
The physical properties of Polyurea Coating III were also compared to the physical properties of Polyurea Coating NL The maximum elongation and tear resistance of Polyurea Coating III were slightly lower for Polyurea Coating NL
TABLE II
The coatings of these examples were sprayed onto a plastic panel coated with a mold release. The coatings were removed from the plastic panels by gently pulling on one corner of the coating.
Not only does this invention improve the performance of spray polyurea coatings; it also reduces the quantity of 2,4'-isomer MDI required by the plant manufacturing the prepolymer.
Claims (25)
1. A process for preparing a polyurea elastomer, comprising:
A) providing a first isocyanate composition of at least one diphenylmethane diisocyanate isomer, the composition containing greater than 75 % by weight 4,4'-MDI;
B) providing a first isocyanate reactive organic material of one or more compounds containing a plurality of isocyanate reactive groups;
C) providing a second isocyanate composition of a mixture of two or more diphenylmethane diisocyanate isomers, wherein the mixture contains at least 25% by weight of 2,4'-MDI;
D) forming an isocyanate group terminated intermediate prepolymer by reacting the first isocyanate reactive organic material with a stoichiometric excess of the first isocyanate composition, wherein the prepolymer contains from 1 to 13% by weight of free isocyanate groups; E) mixing the intermediate prepolymer with the second isocyanate composition to produce a blended quasiprepolymer composition having a final free isocyanate group content of from 12 to 28% by weight;
F) providing a second isocyanate reactive organic material comprising at least one compound which contains two or more isocyanate reactive amine groups; and G) combining the quasiprepolymer composition and the second isocyanate reactive material under conditions suitable for the formation of an elastomer comprising a plurality of urea linkages.
2. The process according to Claim 1, wherein the intermediate prepolymer contains from 5 to 13% by weight of free isocyanate groups, and the quasiprepolymer composition contains from 12 to 23% by weight of free isocyanate groups.
3. The process according to Claim 1, wherein the first isocyanate composition contains at least 98% by weight of 4,4'-MDI, and the second isocyanate composition contains 35% or more by weight of 2,4'-MDI.
4. The process according to Claim 3, wherein the second isocyanate composition contains 50 to 56% by weight of 2,4'-MDI and at least 40% by weight of 4,4*-MDL
5. The process according to Claim 1, wherein the second isocyanate reactive material contains greater than 50% by weight of compounds containing isocyanate reactive amine groups.
6. The process according to Claim 5, wherein the second isocyanate reactive material consists essentially of compounds containing isocyanate reactive amine groups.
7. The process according to Claim 5, wherein the second isocyanate reactive material contains at least some polyether polyol.
8. The process according to Claim 1, wherein the first isocyanate reactive material consists essentially of one or more members selected from the group consisting of polyols, polyamines, compounds containing both amine and alcohol groups, and mixtures of these.
9. The process according to Claim 8, wherein the first isocyanate reactive material consists essentially of one or more polyols.
10. The process according to Claim 9, wherein the first isocyanate reactive material consists essentially of one or more nominal diols or triols having number averaged molecular weights of from 1,000 to 10,000.
11. The process according to Claim 10, wherein the first isocyanate reactive material contains at least 75% by weight of one or more nominal diols.
12. The process according to Claim 1, wherein the second isocyanate reactive material consists predominantly of amine terminated polyether resins by weight, the amine terminated polyether resins having number averaged molecular weights of 2,000 or greater and containing primary or secondary amine termini.
13. The process according to Claim 12, wherein the amine terminated polyether resins have number averaged molecular weights of from 2,000 to 5,000 and wherein the isocyanate reactive terminal groups are predominantly primary amine groups.
14. The process according to Claim 13, wherein. the amine terminated polyether resins consist predominantly of diamines or triamines by weight.
15. The process according to Claim 12, wherein the second isocyanate reactive material further contains a minor amount by weight of a relatively low molecular weight diamine chain extender containing predominantly primary or secondary amine groups.
16. The process according to Claim 1, wherein the quasiprepolymer and the second isocyanate reactive composition are processed as a two component system at a component weight ratio of from 60:40 to 40:60.
17. The process according to Claim 16, wherein the ratio of isocyanate groups to isocyanate reactive groups in the two component system is from 0.9 to 1.15.
18. The process according to Claim 16, wherein the two component system is processed by spraying.
19. The process according to Claim 18, wherein the component ratio is about 1:1 by volume.
20. The process according to Claim 1, wherein the quasiprepolymer is a clear liquid at 25°C which does not form solids or separate on standing at 25°C for at least 30 days.
21. The process according to Claim 2, wherein the second isocyanate reactive material is liquid at 25°C and does not form solids or separate on standing at 25°C for at least 30 days.
22. The process according to Claim X, wherein alkylene carbonate is provided to at least one of the quasiprepolymer and the second isocyanate reactive material.
23. The process according to Claim 22, wherein the alkylene carbonate is selected from the group consisting of ethylene carbonate, propylene carbonate, butylene carbonate, and dimethyl carbonate.
24. The process according to Claim 23, wherein the alkylene carbonate is propylene carbonate.
25. The polyurea elastomer produced according to the process of Claim 1.