AU1504501A

AU1504501A - Intaglio printing inks

Info

Publication number: AU1504501A
Application number: AU15045/01A
Authority: AU
Inventors: Odi Batistatos; Ana Ghioghiu; Bruce Alfred Hardwick; Joshua Nemeth
Original assignee: Note Printing Australia Ltd
Current assignee: Note Printing Australia Ltd
Priority date: 1999-11-22
Filing date: 2000-11-22
Publication date: 2001-06-04
Also published as: AUPQ417399A0; EP1268687A4; WO2001038445A1; CA2391847A1; EP1268687A1; NZ518898A

Description

WO 01/38445 PCT/AUOO/01421 INTAGLIO PRINTING INKS Technical Field This invention relates to printing inks and in particular to printing inks known as Intaglio printing inks. The invention also relates to a process of obtaining 5 a dry Intaglio printing ink film on a substrate. Background of the Invention Intaglio printing is a process whereby an image is transferred to a sheet of paper or other substrate from a plate with recessed portions, where printing ink is located in the recessed portions of the plate. After transfer of the printing ink to the 10 paper or other substrate the ink may be dried either under ambient conditions or under forced drying conditions of elevated temperatures and/or .increased air flow. The printing ink also dries or cures by undergoing chemical reactions. The Intaglio technique is well known and produces high quality raised images that can be used for the manufacture of banknotes and other documents as 15 well as for artworks. One of the features of the Intaglio printing technique is that the film build of the printing ink that is transferred to the paper or other substrate may vary from a few microns to fifty microns or more. This ability to vary the film build is a desirable feature of Intaglio printing and may be used to advantage to produce embossing and other desirable features such as tactility without embossing. 20 This feature also distinguishes inks suitable for use as Intaglio inks from other printing inks. The high film build characteristic of Intaglio printing accentuates the problem of "set-off'. "Set-off' is the transfer of ink from one finished sheet to the next finished sheet in the run. It is caused by residual tackiness on the surface of 25 the printed sheet and often is exacerbated when pressure is applied by the weight of a pile of stacked sheets. "Set-off' is usually worst on sheets towards the bottom of the stack as these are under the most weight . One method used to reduce the problem of "set-off' is to interleave sheets between adjoining sheets. However interleaving is a very cumbersome and costly process and not desirable for 30 commercial printing operations. The type of substrate can also affect "set-off'. The ''set-off' problem tends to be worse with substrates that cannot readily absorb WO 01/38445 PCT/AUOO/01421 -2 solvents from the printing ink. In the case of banknotes, the "set-off' is generally worse when polymer substrates are used compared to cellulosic natural product paper substrates. EP 486092 (Akzo) discloses fatty acid resinous derivatives of starch type 5 polyether polyols. The acid value of the resins have acid values of about 10 mgKOH/g. There is no suggested use as Intaglio inks. EP 750026 (Sun Chemical) relates to Intaglio printing inks. The resins disclosed in that citation are addition polymerised modified epoxy resin fatty acid esters. The epoxy resin is bisphenol A type resin which are polyethers.~ After 10 application, the inks are thermally cured. It is an object of the present invention to improve the "set-off' of Intaglio printing inks, especially on polymer substrates. Summary of the Invention This invention provides in one form an Intaglio ink wherein the binder 15 includes an autoxidisable polyester resin with a fatty acid content in the range 40 60% by weight, more preferably 45 - 55% and most preferably 47 - 52%. Preferably the fatty acid has at least 25% of its chain as linolenic acid, more preferably at least 40%. Preferably the iodine value of the fatty acid is at least 150gl100g. Preferably the fatty acid is selected from the group consisting of 20 linseed fatty acid, tung oil fatty acid or synthetic equivalents. Preferably the fatty acid is linseed fatty acid. Preferably the acid value of the resin is in the range 40 - 80 mg KOH/g of resin and more preferably 50 - 70 mg KOH/g of resin and most preferably 55 - 65 mg KOH/g of resin. 25 Preferably the resin has a viscosity as measured by Gardner-Holt viscosity bubble tubes in the range R - Y and more preferably T - X and most preferably T W when measured as a 60% solution in ethyl di-icinol (monoethyl ether of diethyleneglycol). This invention provides in an alternative form an Intaglio ink which 30 comprises: WO 01/38445 PCT/AUOO/01421 -3 20 - 40% an autoxidisable polyester resin 10 - 30% organic solvents 1 - 60%, preferably 1 - 50% pigments 0 - 5% catalysts 5 wherein the autoxidisable polyester resin is as described above. Preferably the ink composition further comprises a wax dispersion. The glass transition temperature (Tg) of the wax dispersion is preferably less than the maximum temperature achieved during the printing process and more preferably more than 20'C less than the maximum temperature achieved 10 during the printing process. Suitable wax dispersions include polyurethane dispersions and micronised polyolefin dispersions. The invention provides in a further form a method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as described above, exposing the film to a UV light source and curing the ink. 15 The solvent present in the Intaglio printing ink composition may consist of a single solvent. However it is preferred that a mixture of solvents is used. Different solvents may be used to influence various properties of the ink composition, including viscosity, ink stability and transfer properties. Solvents that are released reasonably quickly from the inked substrate may be useful as their release will tend 20 to aid the time to achieve satisfactory "set-off". Illustrative of such solvents are aliphatic type blends of hydrocarbons that have boiling points in the range 150 270'C. Slower solvents may also be used in conjunction with these hydrocarbon solvents and these other solvents may be retained to a certain extent after the ink has dried. Effectively these solvents, at their residual levels, can function as plasticisers 25 and provide greater levels of flexibility to the dried ink. Examples of such solvents are glycols and ether - glycols. Good flexibility in the dried ink is particularly preferred with bank notes where the notes are frequently subjected to bending, flexing and folding. Driers that may be used in the ink compositions of the present invention 30 include the transition metal salts commonly used in accelerating the drying of alkyd or oil based house paints. A particularly preferred drier is a combination of cobalt WO 01/38445 PCT/AUOO/01421 -4 and manganese. These metals are usually in the form of soluble or compatible salts such as, for example, cobalt naphthenate or cobalt octoate. Some of the metal driers facilitate surface cure while others enhance through cure. In certain embodiments of the present invention it is believed to be desirable to achieve a greater amount of 5 surface cure compared to through cure. It is believed this surface cure will lead to the desired "set-off' property while the lack of extensive through cure will assist in increasing the flexibility of the film. The pigments that may be used in the printing ink compositions of the present invention include those commonly used in printing inks. Examples include 10 organic pigments, carbon black and iron oxide. The levels of pigment present may vary depending on the particular application but are generally in the range of 5 60% by weight. Pigments also include fillers and extenders. In practice the pigments may be dispersed using the Intaglio ink resin as a pigment dispersant. This resin functions effectively as a pigment dispersant and 15 this is believed to be a consequence of the relatively high acid value of the resin. However a separate pigment dispersant may be used and in this case the pigment dispersant would be an additional ingredient in the Intaglio printing ink composition. Preferably the acid value of the resin is in the range 40 - 80 mg KOH/g of 20 resin and more preferably 50 - 70 mg KOH/g of resin and most preferably 55 - 65 mg KOH/g of resin. Preferably the resin has a viscosity as measured by Gardner-Holt viscosity bubble tubes in the range R - Y and more preferably T - X and most preferably T W when measured as a 60% solution in ethyl di-icinol (monoethyl ether of 25 diethyleneglycol). These viscosities indicate relatively high molecular weight and branched chain networks. These are believed to contribute to the desired "set-off' behaviour. In an alternative form the Intaglio ink further comprises a photoinitiator. In a still further alternative form this invention provides a process of preparing a dry 30 Intaglio printing ink on a substrate, the process comprising the steps of transferring an Intaglio printing ink from a plate to a substrate at a temperature in the range 60 - WO 01/38445 PCT/AUOO/01421 -5 90*C, more preferably 80 - 84'C, irradiating the printed substrate from a UV radiation source. Detailed Description of the Invention The use of UV curable coatings has been known for many years. A 5 particularly well known example is that of any clear finishes over timber substrates. These timber substrates are coated in a factory. These precoated timber materials may then be used for flooring or other applications where further coating is not required. UV curable coatings are particularly applicable to clear, unpigmented coatings. The presence of pigments tends to limit the penetration of UV radiation 10 and hence has not been as widely used in pigmented coatings. The general composition of UV coatings includes resins or polymers as -binders that have addition polymerisable ethylenic unsaturation. Typically these resins or polymers as well as oligomers or monomers, have multi-functional addition polymerisable unsaturation. Examples include polyols that have been modified as polyacrylates, 15 such as trimethylolpropane triacrylate, and pentaerythritol tri and tetra acrylate. Photoinitiators are commonly used in such compositions to accelerate the rate of cure or crosslinking. Polyester resins or polymers that include fatty acid side chains are well known in coating technology. They are referred to as alkyds. They are used as the 20 binders in household "oil" paints. Coatings prepared using alkyd resins as binders form films both by evaporation of solvent as well as chemical reaction utilising oxygen in the atmosphere. They are generally referred to as autoxidisible coatings as a result of the mechanism of curing involving atmospheric oxygen. Generally the fatty acids that are used as binders in household coatings are derived from 25 naturally occurring soya or safflower oils. Linseed fatty acids are generally not used because of problems with yellowing. The percentage of fatty acid present is usually about 60% by weight. Typical alkyd based coatings take 2- 4 hours to achieve tack free condition. While lower levels of fatty acid lead to improve "tack-free" times the best balance of properties 30 is achieved at about the 60% level of fatty acid. Lower levels of fatty acids generally require the presence of aromatic solvents which are undesirable for WO 01/38445 PCT/AUOO/01421 -6 domestic applications. Generally improved "tack-free" times are achieved with lower percentages of fatty acids and these binders are used in industrial applications. "Tack-free" is generally achieved in such applications by evaporation of solvent alone. The mechanism of curing alkyd based coatings has been widely 5 studied. While the fatty acid side chains have unsaturated groups it is generally recognised that the mechanism of cure does not involve addition polymerisation reactions with this unsaturation. In contrast the binders for UV coatings generally require the presence of addition polymerisable ethylenic unsaturation. Accordingly, it would not be expected that alkyd based coatings would be susceptible to' curing 10 reactions in response to UV radiation. Furthermore, the autoxidation type mechanisms would be anticipated to be too slow to lead to acceptable "set-off' times when used as a printing ink. The polyester resin of the present invention may be prepared by known methods that are applicable to the preparation of alkyds. The composition of the 15 polyester binders of the present invention may be varied within the parameters outlined in the Summary of the Invention. It is preferred that the acid value of the resins is relatively high and it is believed this contributes to good adhesion to the substrate, particularly when these are polymer substrates used for bank notes. As discussed previously, it also aids pigment dispersion The polyester resin of the 20 present invention preferably includes at least 20% by weight of aromatic polyfunctional carboxylic acids and it is believed this contributes to a relatively high Tg of the polyester backbone. This relatively high aromatic content is believed to assist in obtaining satisfactory "set-off'. While the resins are described as polyesters other minor levels of non ester groups may be incorporated. However 25 the polymer backbone of the resin is required to be essentially a polyester. Minor amounts of amide or ether groups could also be included. The printing inks of the present invention may be used conventionally, that is without UV radiation. However, generally improved results are achieved when they are subjected to UV radiation. Typically when used conventionally "set-off' is 30 adequate to allow 250 sheets to be stacked. However, with UV irradiation 2,000 3,000 sheets may be stacked. Generally, the Intaglio printing is carried out at 80 - WO 01/38445 PCT/AUOO/01421 -7 84'C as a primary source of heat, and curing/drying continues afterwards at normal temperatures. The curing may be accelerated with other radiation. We have found that by using a combination of heated plates and a UJV system incorporating exhaust ventilation, acceptable initial cure of the ink is achieved. Generally UV systems 5 have a significant infra-red component which assists thermal curing/drying. In this alternative embodiment involving UV curing photoinitiators may also be used. These initiators that are well known in the UV curing of coatings, for example Irgacure 184 (ex Ciba-Geigy). As well as the components outlined in the Summary of the Invention; other 10 materials may be included without detracting from the overall properties of the printing ink. As an example, fillers or extenders can be used to vary the gloss of the printing ink image. These are included within the pigment category and include calcium carbonate as an example. The driers or catalysts that may be used are well known. Some driers are known more as "surface driers", while other driers are 15 known as "through driers". The selection of driers for the present invention may be made to obtain the requisite balance of properties. It is believed desirable in many banknote applications that "through dry" is limited. This ensures adequate flexibility of the printing ink. It is believed that the UV irradiation accentuates the "surface cure" and hence to an extent limits the "through cure". Minor amounts of 20 other binders as well as plasticisers may be used without detracting from the properties of the compositions of the present invention. While the printing inks of the present invention are particularly suitable for plastic substrates, they can also be used on other substrates such as cellulosic type substrates. The compositions are particularly useful on polymer substrates used for security documents such as 25 banknotes. The types of apparatus that may be used to irradiate the sheets of substrate may vary but generally involve the exposure of a substrate to which the printing ink has been applied for a short period of time with UV radiation. The invention will be further described by reference to a preferred 30 embodiment in the following examples.

WO 01/38445 PCT/AUOO/01421 -8 Example 1 Preparation of an Intaglio resin according to the invention. The following reagents were charged to a three litre flanged top flask equipped with mechanical stirrer, condenser, nitrogen sparge and electric mantle. ethylene glycol 168g fatty acid 882g A trimethylol propane 262g B terephthalic acid 202g C isophthalic acid 202g D dibutyl tin oxide 0.7g E styrene maleic anhydride resin 104g F trimellitic anhydride 179g G isopar G 636g H 5 Stage A was charged to the stirred reactor and B to E stages were added in that order. The reactants were heated to 182*C and maintained at that temperature until 66ml of water was removed. The refractive index of the collected water was 10 monitored to ensure no loss of ethylene glycol. The column temperature was not allowed to exceed 1 10*C. The batch was then heated to 260*C again ensuring that the column head temperature was maintained below 1 10 C. After a total of 104 mls of water had been collected the acid value was monitored until it was in the range 6 - 9 mg 15 KOH/g and the batch was clear. The Gardner Holt viscosity was in the range A - C as measured in a 60% solution in ethyl di-icinol. Total water removed was 123ml. F stage was then added and the batch maintained at 260 - 265'C until the AV was in the range 6 - 9 and the viscosity was G - I (using the same method as used previously). The batch was cooled to 170'C and G stage was added. The 20 temperature was maintained at 170"C until the acid value was in the range 55 - 65 and the viscosity was in the range T - W. H stage was then added to give the final resin. The fatty acid content of this resin was 44%.

WO 01/38445 PCT/AUOO/01421 -9 Example 2 This example illustrates the preparation and testing of an Intaglio printing ink composition. Resin (from Example 1) 10.0 SiO 2 (thickener) 0.6 Irgacure 184 (Ciba-Geigy) 0.2 Co/Mn octoate (6% solution) 0.1 black ink (NNS invis) 0.5 5 The printing ink composition was prepared by combining the above ingredients. The ink was then tested by exposing a film of thickness 50 pm thickness to 150 Watts/cm of UV irradiation at a distance of 75mm. The films were then assessed for set-off after passes of the film across the UV radiation source. After five passes the film was rated as very good while after four 10 passes it was rated as fair. Example 3 Example 2 was repeated but with a resin similar to Example 1 except that the fatty acid content was 49% rather than 44%. When assess as in Example 2 it was rated as excellent after either four or five passes. Even after three passes it was 15 rated as very good. After two passes it was rated as fair. Although the fatty acid content of this example was higher than Example 2, the "set-off' was improved. This is contrary to the expected result for "tack-free" behaviour for alkyds.

Claims

1. An Intaglio ink wherein the binder includes an autoxidisable polyester resin with a fatty acid content in the range 40 - 60% by weight. 5

2. An Intaglio ink as defined in claim 1 wherein the fatty acid content is in the range 45 - 55%.

3. An Intaglio ink as defined in claim 2 wherein the fatty acid content is in the 10 range 47 - 52%.

4. An Intaglio ink as defined in any one of claims 1 to 3 wherein the acid value of the polyester resins is in the range 40 - 80 mg KOH/g of resin. 15

5. An Intaglio ink as defined in claim 4 wherein the acid value of the polyester resins is in the range 50 - 70 mg KOH/g of resin.

6. An Intaglio ink as defined in any one of claims 1 to 3 wherein the acid value of the polyester resins is in the range 55 - 65 mg KOH/g of resin. 20

7. An Intaglio ink as defined in any one of claims 1 - 6 wherein the fatty acid has at least 25% of its chains as linolenic acid.

8. An Intaglio ink as defined in claim 7 wherein the fatty acid has at least 40% 25 of its chains as linolenic acid.

9. An Intaglio ink as defined in any one of claims 1 - 6 wherein the iodine value of fatty acid is at least 150gl/100g. 30

10. An Intaglio ink as defined in any one of claims 1 - 9 wherein the fatty acid is linseed fatty acid. WO 01/38445 PCT/AUOO/01421

11. An Intaglio ink as defined in any one of claims 1 - 10 wherein the resin has a viscosity, as a 60% w/w solution in monoethylether of diethylene glycol, as measured by Gardner-Holt viscosity bubble tubes in the range R - Y. 5

12. An Intaglio ink as defined in claim 11 wherein the resin has a viscosity as measured by Gardner-Holt viscosity bubble tubes in the range T - X.

13. An Intaglio ink as defined in claim 12 wherein the resin has a viscosity as measured by Gardner-Holt viscosity bubble tubes in the range T - W. 10

14. An Intaglio ink which comprises: 20 - 40% an autoxidisable polyester resin 10 - 30% organic solvents 1 - 60% pigments 15 0 - 5% catalysts wherein the autoxidisable polyester resin is as defined in any one of claims 1 - 13.

15. An Intaglio ink as defined in claim 14 further comprising a wax dispersion. 20

16. An Intaglio ink as defined in claim 15 wherein the glass transition temperature (Tg) of the wax dispersion is less than the maximum temperature achieved during the printing process. 25

17. An Intaglio ink as defined in claim 16 wherein the glass transition temperature (Tg) of the wax dispersion is more than 20'C less than the maximum temperature achieved during the printing process.

18. A method for preparing an Intaglio printed substrate by applying a film of 30 Intaglio ink as defined in claim 1, exposing the film to a UV light source and curing the ink. WO 01/38445 PCT/AUOO/01421 -12

19. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 2, exposing the film to a UV light source and curing the ink. 5

20. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 3, exposing the film to a UV light source and curing the ink.

21. A method for preparing an Intaglio printed substrate by applying a film of 10 Intaglio ink as defined in claim 4, exposing the film to a UV light source and curing the ink.

22. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 5, exposing the film to a UV light source and curing 15 the ink.

23. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 6, exposing the film to a UV light source and curing the ink. 20

24. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 7, exposing the film to a UV light source and curing the ink.

25 25. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 8, exposing the film to a UV light source and curing the ink.

26. A method for preparing an Intaglio printed substrate by applying a film of 30 Intaglio ink as defined in claim 9, exposing the film to a UV light source and curing the ink. WO 01/38445 PCT/AUOO/01421 - 13

27. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 10, exposing the film to a UV light source and curing the ink. 5

28. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 11, exposing the film to a UV light source and curing the ink.

29. A method for preparing an Intaglio printed substrate by applying a film of 10 Intaglio ink as defined in claim 12, exposing the film to a UV light source and curing the ink.

30. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 13, exposing the film to a UV light source and 15 curing the ink.

31. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 14, exposing the film to a UV light source and curing the ink. 20

32. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 15, exposing the film to a UV light source and curing the ink. 25

33. A method for preparing an Intaglio printed substrate by applying a film of Intaglio ink as defined in claim 16, exposing the film to a UV light source and curing the ink.

34. A method for preparing an Intaglio printed substrate by applying a film of 30 Intaglio ink as defined in claim 17, exposing the film to a UV light source and curing the ink. WO 01/38445 PCT/AUOO/01421 -14

35. An Intaglio printed substrate as prepared according to claim 18.

36. An Intaglio printed substrate as prepared according to claim 19. 5

37. An Intaglio printed substrate as prepared according to claim 20.

38. An Intaglio printed substrate as prepared according to claim 21.

39. An Intaglio printed substrate as prepared according to claim 22. 10

40. An Intaglio printed substrate as prepared according to claim 23.

41. An Intaglio printed substrate as prepared according to claim 24. 15

42. An Intaglio printed substrate as prepared according to claim 25.

43. An Intaglio printed substrate as prepared according to claim 26.

44. An Intaglio printed substrate as prepared according to claim 27. 20

45. An Intaglio printed substrate as prepared according to claim 28.

46. An Intaglio printed substrate as prepared according to claim 29. 25

47. An Intaglio printed substrate as prepared according to claim 30.

48. An Intaglio printed substrate as prepared according to claim 31.

49. An Intaglio printed substrate as prepared according to claim 32. 30

50. An Intaglio printed substrate as prepared according to claim 33. WO 01/38445 PCT/AUOO/01421 - 15

51. An Intaglio printed substrate as prepared according to claim 34.

52. An Intaglio printed substrate as prepared according to claim 35.