AT299336B - Material for the post-acceleration spiral of cathode ray tubes - Google Patents

Material for the post-acceleration spiral of cathode ray tubes

Info

Publication number
AT299336B
AT299336B AT781470A AT781470A AT299336B AT 299336 B AT299336 B AT 299336B AT 781470 A AT781470 A AT 781470A AT 781470 A AT781470 A AT 781470A AT 299336 B AT299336 B AT 299336B
Authority
AT
Austria
Prior art keywords
cathode ray
post
ray tubes
spiral
graphite
Prior art date
Application number
AT781470A
Other languages
German (de)
Inventor
Ferenc Finta
Gyula Laskay
Original Assignee
Egyesuelt Izzolampa
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Egyesuelt Izzolampa filed Critical Egyesuelt Izzolampa
Application granted granted Critical
Publication of AT299336B publication Critical patent/AT299336B/en

Description

  

   <Desc/Clms Page number 1> 
 



  Material für die Nachbeschleunigungsspirale von Kathodenstrahlröhren 
Die Erfindung betrifft ein Material für die Nachbeschleunigungsspirale von Kathodenstrahlröhren, welches Graphit enthält. 



    BekanntlichwerdeninKathodenstrahlröhren dieaus dem Elektronenstrahlsystem gegen den Leucht-    schirm zu gerichteten Elektronen auf ihrer Flugbahn beschleunigt. Der Gleichstrom fliesst in einem auf die Innenwand des   Kathodenstrahlröhrenkolbens   und auf die Längsachse der Röhre senkrecht ausge- 
 EMI1.1 
 gemeinen aus einer Kohlensorte, namentlich aus Russ, ausgeführt. Auf die Innenwand der KathodenStrahlröhre, an welcher vorangehend ein dem Leuchtschirm näher liegender Teil sowie ein dem Hals näher liegender Teil mit Graphit überzogen wurde (Anodenteil), d. h. auf die zwischen den beiden graphitüberzogenen Oberflächenteilen liegende, reine Glasfläche wird die   Russ-Suspensionrnittels   irgendeines Schreibgerätes in Linienform aufgetragen.

   Der Anfang der Linie berührt den einen und das Ende der Linie den andern graphitüberzogenen Oberflächenteil. 



   Danach erfolgt das Trocknen und sodann die Wärmebehandlung bei etwa   4500C.   Die Wärmebehandlung dient zur Beseitigung der flüchtigen Komponenten (teils auch mittels Oxydation) der graphit- überzogenen Oberflächen und der Widerstandsspirale. Nach der Wärmebehandlung wird die Montageeinheit eingebaut und die Kathodenstrahlröhre evakuiert. 



   Der Fertigungsvorgang sowie die Konstruktion der   Kathodenstrahlröhren   sind ausführlicher z. R. im Buche von W. Espe : Werkstoffe der Hochvakuumtechnik (Bd. IIL S. 146 bis 147, hauptsächlich 177, 
 EMI1.2 
 [1961]. VEB,Suspensionen auf die bei der Temperatur der Wärmebehandlung auftretende Oxydation sehr empfindlich sind.

   Daraus folgt, dass sich der Querschnitt der auf der Oberfläche ausgebildeten Nachbeschleunigungsspirale verringert, u. zw. wegen der abweichenden Umstände der Wärmebehandlung und der damit verbundenen Gasspülung auch örtlich ungleichmässig, also lässt sich der Spiralwiderstand nur schwer 
 EMI1.3 
 

 <Desc/Clms Page number 2> 

 welche unter den Umständen der Wärmebehandlung, des Zusammenbaues und der Evakuierung der   Kathodenstrahlröhre nur in minimalem,   unbedeutend geringem Masse gegen Oxydation empfindlich ist und deren Widerstandswert aus diesem Grunde konstant und leicht einstellbar ist. Die Erfindung besteht im wesentlichen darin, dass das Material als mit destilliertem Wasser in einer Kugelmühle gemahlene Be-   standteile ausserdem Graphit Nickel-und/oder   Kobaltoxyd enthält.

   Wenn mit der aus der Mischung von Nickel-und/oder   Kobaltoxyd   und von Graphit zubereiteten Suspension in der bereits beschriebenen bekannten Weise   eine Nachbeschleunigungsspirale hergestellt wird, so zeigt sich, dass der gefertigte Wi-   derstand die gestellten Erfordernisse   erfüllt.   



   Um das Wesen der Erfindung näher zu erläutern und gleichzeitig offensichtlicher zu machen, werden nachfolgend zwei Ausführungsbeispiele näher beschrieben. 



   Beispiel 1
50 g Kobaltoxyd   (Cos04)  
20 g Graphit (zweckmässig feinkörniger Elektrographit)
350 ml dest. Wasser
100 g   Na-Wasserglaslösung   werden in einer Kugelmühle während 250 h gemahlen, danach wird die Masse mit 1, 5 g Fettalkoholsulfonat vermischt und-unter Berücksichtigung der   Schmierbarkeit - auf   die entsprechende Viskosität eingestellt. Die Masse wird auf die Innenwand der Kathoden-Strahlröhre mittels eines Schreibgerätes in Spiralform aufgetragen und sodann die   Kathoden-Strahlröhre - nach   erfolgter Trocknung und Wärmebehandlung-in der bereits beschriebenen Weise fertigmontiert. 



   Orientierungshalber ist zu bemerken, dass in den üblichen Oszilloskopröhren der Widerstandswert der Nachbeschleunigungsspirale (nach erfolgter   Wärmebehandlung) sich im Bereich von 20 bis 200 MQ   bewegt,
Beispiel 2 
 EMI2.1 
 
30 g Nickeloxyd (NiO)
15 g Graphit werden in einer Kugelmühle während 250 h gemahlen und im übrigen ist der Arbeitsvorgang wie unter Beispiel 1. 
 EMI2.2 
 setzungen in anderer Proportion denkbar. 



   Die mittels der Erfindung erzielbaren Vorteile sind in grossen Zügen wie folgt :
Vor allem ist zu betonen, dass bei genauer Einhaltung der Zusammensetzung und der Korngrösse der genaue Widerstandswert gesichert werden kann. Die Erfindung hat ferner die Vorteile, dass die vorhandene Einrichtungund die technologische Reihenfolge beibehalten werden können, jedoch ist der angewandte Stoff gleichzeitig auf Oxydation unempfindlich und dabei preiswert. 



   PATENTANSPRÜCHE 
1. Material für die Nachbeschleunigungsspirale von Kathodenstrahlröhren, welches Graphit enthält, dadurch gekennzeichnet, dass es als mit destilliertem Wasser in einer Kugelmühle gemahlene Bestandteile ausser dem Graphit   Nickel- und/oder   Kobaltoxyd   enthält.  



   <Desc / Clms Page number 1>
 



  Material for the post-acceleration spiral of cathode ray tubes
The invention relates to a material for the post-acceleration spiral of cathode ray tubes which contains graphite.



    As is well known, in cathode ray tubes the electrons from the electron beam system against the fluorescent screen are accelerated on their trajectory to form electrons. The direct current flows in a vertical direction on the inner wall of the cathode ray tube bulb and on the longitudinal axis of the tube.
 EMI1.1
 commonly made from one type of coal, namely soot. On the inner wall of the cathode ray tube, on which a part closer to the luminescent screen and a part closer to the neck were previously coated with graphite (anode part), i. H. The soot suspension is applied in line form to the pure glass surface between the two graphite-coated surface parts using any writing instrument.

   The beginning of the line touches one and the end of the line touches the other graphite-coated surface part.



   This is followed by drying and then heat treatment at around 4500C. The heat treatment serves to remove the volatile components (partly also by means of oxidation) from the graphite-coated surfaces and the resistance spiral. After the heat treatment, the assembly unit is installed and the cathode ray tube evacuated.



   The manufacturing process and the construction of the cathode ray tubes are described in more detail e.g. R. in the book by W. Espe: Materials of High Vacuum Technology (Vol. IIL P. 146 to 147, mainly 177,
 EMI1.2
 [1961]. VEB, suspensions are very sensitive to the oxidation occurring at the temperature of the heat treatment.

   It follows from this that the cross section of the post-acceleration spiral formed on the surface is reduced, u. Because of the different circumstances of the heat treatment and the associated gas purging, it is also locally uneven, so the spiral resistance is difficult to control
 EMI1.3
 

 <Desc / Clms Page number 2>

 which under the circumstances of the heat treatment, the assembly and the evacuation of the cathode ray tube is only minimally, insignificantly insensitive to oxidation and its resistance value is therefore constant and easily adjustable. The invention essentially consists in the fact that the material also contains graphite, nickel and / or cobalt oxide as components ground with distilled water in a ball mill.

   If the suspension prepared from the mixture of nickel and / or cobalt oxide and graphite is used to produce a post-acceleration spiral in the known manner already described, it is shown that the resistance produced meets the requirements.



   In order to explain the essence of the invention in more detail and at the same time to make it more obvious, two exemplary embodiments are described in more detail below.



   example 1
50 g cobalt oxide (Cos04)
20 g graphite (fine-grain electrographite is advisable)
350 ml dist. water
100 g of sodium water glass solution are ground in a ball mill for 250 h, then the mass is mixed with 1.5 g of fatty alcohol sulfonate and - taking into account the lubricity - adjusted to the appropriate viscosity. The mass is applied to the inner wall of the cathode ray tube by means of a writing implement in a spiral form and then the cathode ray tube - after drying and heat treatment has taken place - fully assembled in the manner already described.



   As a guide, it should be noted that in the usual oscilloscope tubes the resistance value of the post-acceleration spiral (after the heat treatment has taken place) is in the range of 20 to 200 MQ,
Example 2
 EMI2.1
 
30 g nickel oxide (NiO)
15 g of graphite are ground in a ball mill for 250 h and otherwise the procedure is as in Example 1.
 EMI2.2
 Settlements in other proportions are conceivable.



   The advantages that can be achieved by means of the invention are broadly as follows:
Above all, it should be emphasized that if the composition and the grain size are strictly adhered to, the exact resistance value can be ensured. The invention also has the advantages that the existing equipment and the technological sequence can be retained, but the substance used is at the same time insensitive to oxidation and at the same time inexpensive.



   PATENT CLAIMS
1. Material for the post-acceleration spiral of cathode ray tubes, which contains graphite, characterized in that it contains nickel and / or cobalt oxide as constituents ground with distilled water in a ball mill, in addition to the graphite.

 

Claims (1)

2. Material nach Anspruch 1, dadurch gekennzeichnet, dass es einen oberflächenaktiven Stoff, z. B. Fettalkoholsulfonat enthält. 2. Material according to claim 1, characterized in that it is a surfactant, e.g. B. contains fatty alcohol sulfonate. Druckschriften, die das Patentamt zur Abgrenzung des Anmeldungsgegenstandes vom Stand der Technik in Betracht gezogen hat : DT-PS 715 038 Publications that the patent office has considered to differentiate the subject matter of the application from the state of the art: DT-PS 715 038
AT781470A 1969-11-05 1970-08-27 Material for the post-acceleration spiral of cathode ray tubes AT299336B (en)