NL2021322B1 - Continuous methods of making glass ribbon and as-drawn glass articles from the same - Google Patents

Continuous methods of making glass ribbon and as-drawn glass articles from the same Download PDF

Info

Publication number
NL2021322B1
NL2021322B1 NL2021322A NL2021322A NL2021322B1 NL 2021322 B1 NL2021322 B1 NL 2021322B1 NL 2021322 A NL2021322 A NL 2021322A NL 2021322 A NL2021322 A NL 2021322A NL 2021322 B1 NL2021322 B1 NL 2021322B1
Authority
NL
Netherlands
Prior art keywords
glass
cast
less
cooling
poise
Prior art date
Application number
NL2021322A
Other languages
Dutch (nl)
Inventor
Luc Alain Dannoux Thierry
Yuryevich Golyatin Vladislav
Lee Rhoads Randy
Original Assignee
Corning Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Corning Inc filed Critical Corning Inc
Priority to KR1020217001642A priority Critical patent/KR20210024558A/en
Priority to CN201980043347.5A priority patent/CN112334419B/en
Priority to JP2020571847A priority patent/JP2021529718A/en
Priority to PCT/US2019/036948 priority patent/WO2020005555A1/en
Priority to TW108120831A priority patent/TWI828709B/en
Priority to US16/446,849 priority patent/US10906831B2/en
Priority to EP19182925.8A priority patent/EP3587364B1/en
Priority to EP20192760.5A priority patent/EP3792226A1/en
Application granted granted Critical
Publication of NL2021322B1 publication Critical patent/NL2021322B1/en
Priority to US17/145,970 priority patent/US11912605B2/en

Abstract

A method for making a glass ribbon that includes: flowing a glass into a caster having a width (W……) from about 100 mm to about 5 m and a thickness (I) from about 1 mm to about 500 mm to form an a cast glass; cooling the cast glass in the caster to a viscosity of at least 107 Pa-s (108 Poise); conveying the cast glass from the caster; drawing the cast glass, the drawing comprising heating the cast glass to an average viscosity of less than 106 Pa-s (107 Poise) and drawing the cast glass into a glass ribbon having a width (Wribbon) that is less than Wa…; and thereafter cooling the glass ribbon to ambient temperature. Further, the cast glass during the cooling, conveying and drawing steps is about 50 °C or higher.

Description

Θ 2021322 ©B1 OCTROOI (2?) Aanvraagnummer: 2021322 (51) Int. Cl.:
C03B 17/06 (2018.01) C03C 3/068 (2019.01) (22) Aanvraag ingediend: 17 juli 2018 (30) Voorrang:
juni 2018 US 62/691,031 (73) Octrooihouder(s):
Coming Incorporated te Coming, New York, Verenigde Staten van Amerika, US
2) Aanvraag ingeschreven:
januari 2020 (43) Aanvraag gepubliceerd:
Octrooi verleend:
januari 2020 (72) Uitvinder(s):
Thierry Luc Alain Dannoux te Coming, New York (US)
Vladislav Yuryevich Golyatin te Coming, New York (US)
Randy Lee Rhoads te Coming, New York (US)
45) Octrooischrift uitgegeven:
januari 2020 (74) Gemachtigde:
ir. P.J. Hylarides c.s. te Den Haag (54) CONTINUOUS METHODS OF MAKING GLASS RIBBON AND AS-DRAWN GLASS ARTICLES FROM THE SAME (57) A method for making a glass ribbon that includes: flowing a glass into a caster having a width (Wcast) from about 100 mm to about 5 m and a thickness (t) from about 1 mm to about 500 mm to form an a cast glass; cooling the cast glass in the caster to a viscosity of at least 107 Pa s (108 Poise); conveying the cast glass from the caster; drawing the cast glass, the drawing comprising heating the cast glass to an average viscosity of less than 106 Pa s (107 Poise) and drawing the cast glass into a glass ribbon having a width (Wribbon) that is less than Wcast; and thereafter cooling the glass ribbon to ambient temperature. Further, the cast glass during the cooling, conveying and drawing steps is about 50 °C or higher.
NLB1 2021322
Dit octrooi is verleend ongeacht het bijgevoegde resultaat van het onderzoek naar de stand van de techniek en schriftelijke opinie. Het octrooischrift komt overeen met de oorspronkelijk ingediende stukken.
CONTINUOUS METHODS OF MAKING GUASS RIBBON AND AS-DRAWN GLASS ARTICLES FROM THE SAME
The present disclosure relates generally to methods of making glass ribbon and, more particularly, continuous methods of making glass ribbon with high dimensional stability from glass compositions with relatively low liquidus viscosities.
Conventional methods of making lenses and other optical components from glass compositions having low liquidus viscosities, including compositions with high refractive indices, are very high in cost with low utilization of the melted glass borne from these methods. Typically, these methods include casting the compositions into long bars with a thickness that is significantly greater in thickness than the final end product. That is, these forming methods produce a cast bar that requires additional processing to obtain a final product form and dimensions.
The additional processing of these cast bars is often extensive. In particular, the cast bar is then sawed into discs. Next, the discs are ground to polish their outer diameter to the final outer dimension of the end product lens. The discs are then wire sawed to a thickness on the order of the final lens end product, and then subjected to a significant battery of grinding and polishing steps to achieve the required warp and dimensional uniformity of the end product lens. Consequently, the conventional processes for forming lenses and other optical components from these glass compositions is high in cost and low in utilization of the melted glass.
According to the present disclosure, a method of making a glass ribbon is provided that includes: flowing a glass into a caster having a width from about 100 mm to about 5 m and a thickness (/) from about 1 mm to about 500 mm to form an a cast glass; cooling the cast glass in the caster to a viscosity of at least 107 Pa-s (108 Poise); conveying the cast glass from the caster; drawing the cast glass, the drawing comprising heating the cast glass to an average viscosity of less than 106 Pa-s (107 Poise) and drawing the cast glass into a glass ribbon having a width (Wrii,hmi) that is less than and thereafter cooling the glass ribbon to ambient temperature. Further, the cast glass during the cooling, conveying and drawing steps is about 50 °C or higher.
Also according the present disclosure, a glass article is provided that includes: an unpolished glass ribbon having a thickness from about 1 mm to about 25 mm and a width of 25 mm to about 200 mm, or a width of 100 mm to about 200 mm. The ribbon preferably comprises a glass selected from the group consisting of borosilicate glasses, aluminoborosilicate glasses, aluminosilicate glasses, fluorosilicate glasses, phosphosilicate glasses, fluorophosphate glasses, sulfophosphate glasses, germanate glasses, vanadate glasses, borate glasses, and phosphate glasses. Further, the composition comprises an upper liquidus viscosity of less than 5x104 Pa-s (5x 107 Poise). In addition, the glass ribbon can be sectioned into glass wafers having a thickness variation from about 0.01 pm to about 50 pm and a warp from about 0.01 pm to about 200 pm, and/or the glass wafer has a thickness variation from about 0.01 μιη to about 50 pm and a warp from about 0.01 μηι to about 200 pm.
Additional features and advantages will be set forth in the detailed description which follows, and will be readily apparent to those skilled in the art from that description or recognized by practicing the disclosure as described herein, including the detailed description which follows, the claims, as well as the appended drawings.
It is to be understood that both the foregoing general description and the following detailed description describe various examples and are intended to provide an overview or framework to understanding the nature and character of the claimed subject matter.
The accompanying drawings are included to provide a further understanding of the present disclosure and are incorporated into and constitute a part of this specification. The drawings illustrate the various examples described herein, and together with the description serve to explain the principles and operation of the claimed subject matter.
The following is a description of the figures in the accompanying drawings. The figures are not necessarily to scale, and certain features and certain views of the figures may be shown exaggerated in scale or in schematic in the interest of clarity and conciseness.
In the drawings:
FIG. 1 is a schematic view of a method of making a glass ribbon, according to the present disclosure.
FIG. 2 is a schematic view of apparatus that can be employed according to a method of making a glass ribbon, particularly a melting apparatus with an orifice, a caster and a heating apparatus, according to the present disclosure.
FIGS. 3A and 3B are schematic views of an overflow forming device with an isopipe for flowing glass as employed in the method of making a glass ribbon, according to the present disclosure.
The foregoing summary, as well as the following detailed description of certain inventive techniques, will be better understood when read in conjunction with the figures. It should be understood that the claims are not limited to the arrangements and instrumentality shown in the figures. Furthermore, the appearance shown in the figures is one of many ornamental appearances that can be employed to achieve the stated functions of the apparatus.
Additional features and advantages will be set forth in the detailed description which follows and will be apparent to those skilled in the art from the description, or recognized by practicing the disclosure as described in the following description, together with the claims and appended drawings.
As used herein, the term “and/or”, when used in a list of two or more items, means that any one of the listed items can be employed by itself, or any combination of two or more of the listed items can be employed. For example, if a composition is described as containing components A, B, and/or C, the composition can contain A alone; B alone; C alone; A and B in combination; A and C in combination; B and C in combination; or A, B, and C in combination.
In this document, relational terms, such as first and second, top and bottom, and the like, are used solely to distinguish one entity or action from another entity or action, without necessarily requiring or implying any actual such relationship or order between such entities or actions.
As used herein, the term “about” means that amounts, sizes, formulations, parameters, and other quantities and characteristics are not and need not be exact, but may be approximate and/or larger or smaller, as desired, reflecting tolerances, conversion factors, rounding off, measurement error and the like, and other factors known to those of skill in the art. When the term “about” is used in describing a value or an end-point of a range, the disclosure should be understood to include the specific value or end-point referred to. Whether or not a numerical value or end-point of a range in the specification recites “about”, the numerical value or end-point of a range is intended to include two examples: one modified by “about”, and one not modified by “about.” It will be further understood that the end-points of each of the ranges are significant both in relation to the other end-point, and independently of the other end-point.
The terms “substantial”, “substantially”, and variations thereof as used herein are intended to note that a described feature is equal or approximately equal to a value or description. For example, a “substantially planar surface is intended to denote a surface that is planar or approximately planar. Moreover, “substantially” is intended to denote that two values are equal or approximately equal. In some examples, “substantially” may denote values within about 10% of each other, such as within about 5% of each other, or within about 2% of each other.
Directional terms as used herein—for example up, down, right, left, front, back, top, bottom—are made only with reference to the figures as drawn and are not intended to imply absolute orientation.
As used herein the terms “the”, “a”, or “an”, mean “at least one”, and should not be limited to only one unless explicitly indicated to the contrary. Thus, for example, reference to a component includes examples having two or more such components unless the context clearly indicates otherwise.
As used herein, the terms “upper liquidus viscosity” and “upper liquidus temperature” refer to the respective viscosity and temperature of the glass employed in the articles and methods of the disclosure at which the glass forms a homogenous melt with no crystals. Further, the terms “upper liquidus viscosity” and “liquidus viscosity” are used interchangeably herein; and the terms “upper liquidus temperature” and “liquidus temperature” are also used interchangeably herein.
As also used herein, the “lower liquidus viscosity” and “lower liquidus temperature” refer to the respective viscosity and temperature of the glass employed in the articles and methods of the disclosure at which the glass can be susceptible to the growth of one or more crystalline phases.
As used herein the “devitrification zone” of the glass employed in the articles and methods of the disclosure is the temperature range given by the upper liquidus temperature to the lower liquidus temperature, e.g., the temperature range in which the glass experiences crystal growth of one or more crystalline phases above 0.01 pm/min.
As used herein, the “average viscosity” of the glass employed in the articles and methods of the disclosure refers to the viscosity of the glass, glass ribbon, glass sheet or other article of the disclosure, as measured during the referenced process or method step (e.g., drawing) over a region of the article and over a time duration sufficient to ascertain an average viscosity value according to analytical and measurement methods understood by those of ordinary skill in the field of the disclosure.
As used herein, the term “continuous” refers to the methods and processes of the disclosure that are configured to form glass sheet, ribbon and other articles without the need for any intermediate and/or post-cooling thermal processing, such as annealing or re-drawing. Put another way, the processes and methods of the disclosure are configured to form glass sheet, glass ribbon and other articles that are not cut or sectioned prior to its drawing step.
As used herein, the “maximum crystal growth rate” refers to the maximum growth rate of any crystalline phases of the glass employed in the articles and methods of the disclosure at a referenced temperature or within a referenced temperature range, e.g., in units of pm/min. As also used herein, the “crystal growth rate” refers to the growth rate of any crystalline phases of the glass employed in the articles and methods of the disclosure at a referenced temperature or within a referenced temperature range, e.g., in units of pm/min.
As used herein, the “thickness variation” of the glass wafer, glass ribbon, glass sheet or other article of the disclosure is measured by determining the difference between the minimum and maximum thickness of the glass wafer, glass ribbon, glass sheet, or other article by a mechanical contact caliper or micrometer, or a non-contact laser gauge for articles having a thickness of 1 mm or greater.
As used herein, the “warp” of the glass wafer, glass ribbon, glass sheet or other article of the disclosure is measured according to the distance in between two planes containing the article, minus the average thickness of the article. For glass ribbons, glass sheet and other glass articles of the disclosure with a substantially rectangular shape, the warp is measured according to principles understood by those of ordinary skill in the field of the disclosure. In particular, the warp is evaluated from a square measurement area with a length defined by the quality area between the beads of the article minus five (5) mm from the inner edge of each of the beads. Similarly, for glass wafers of the disclosure with a substantially circular disk-like shape, the warp is also measured according to principles understood by those of ordinary skill in the field of the disclosure. In particular, the warp is evaluated from a circular measurement area with a radius defined by the outer radius of the wafer minus five (5) nun.
As used herein, the “critical cooling rate” of the glass, glass ribbon, glass sheet or other article of the disclosure is determined by melting multiple samples of the glass, glass sheet or other article down to its glass transition temperature at various, selected cooling rates. The samples are then cross-sectioned according to standard sectioning and polishing techniques, and evaluated with optical microscopy at 1 OOx to ascertain the presence of crystals in the bulk and at its free surfaces (i.e., the top, exposed surface and the bottom surface with an interface with a crucible or the like). The critical cooling rate corresponds to the samples with the lowest cooling rate not exhibiting crystals at its surfaces and bulk.
Referring to the drawings in general and to FIG. 1 in particular, it will be understood that the illustrations are for the purpose of describing particular examples and are not intended to limit the disclosure appended claims thereto. The drawings are not necessarily to scale, and certain features and certain views of the drawings may be shown exaggerated in scale or in schematic form in the interest of clarity and conciseness.
Described in this disclosure are methods of making glass ribbon and, more particularly, continuous methods of malting glass ribbon for lenses and other optical components from glass compositions with relatively low liquidus viscosities (e.g. < 5xl04 Pa-s (5xl05 Poise)) and/or relatively high refractive indices. The glass ribbon produced according to these methods has high dimensional stability and low warpage, and is produced at final dimensions comparable to those of the intended end products. As a result, the glass ribbon produced according to the methods of the disclosure requires limited post-processing. Consequently, the methods of the disclosure possess a significantly lower manufacturing cost in comparison to conventional glass-forming processes employed in making lenses from glass compositions having low liquidus viscosities. Further, the methods of the disclosure have a significantly higher utilization of the as-melted glass, with low waste.
Notably, the methods of making a glass ribbon of the disclosure are continuous in the sense that they do not require any post-production annealing or other post-production thermal treatments. The methods employ a cooling through the devitrification zone to a temperature above ambient (e.g., > 50 °C), e.g., by conveying cast glass through a caster. After cooling the glass to a temperature above ambient, the methods employ an additional drawing step, with some re-heating into the devitrification zone. The drawing step results in a glass ribbon with thickness dimensions on the order of those intended in the final end product, e.g., a waler, a lens or other optical component having a high refractive index. Further, the drawing step is advantageously conducted for a limited duration at a glass viscosity and temperature that minimizes, or eliminates any possibility of, devitrification. In addition, the methods are particularly advantageous in the sense that they do not require any post-cooling (i.e., after reaching ambient temperature) thermal processing, such as annealing or re-drawing, to obtain the end product, e.g., a glass ribbon, wafer, lens or other glass article. Also advantageously, aspects of the methods of the disclosure result in glass ribbons, wafers, lenses or other glass articles that do not require any additional mechanical processing, e.g., polishing, grinding, etc., to meet warp and/or thickness variation levels of optical components.
Referring now to FIG. 1, a schematic illustration of a method 100 of making a glass ribbon 30b is provided. As shown in FIG. 1, a method 100 of making a glass ribbon 30b is provided that includes a step 110 of flowing a glass 30 from a melting apparatus 10 into a caster 20 having a width (W„is;) 22 from about 200 mm to about 5 m and a thickness (t) 24 (see FIG. 2) of 1 mm or greater to form a cast glass 30a. The method 100 of making a glass ribbon 30b further includes a step 120 of cooling the cast glass 30a in the caster 20 to a viscosity of at least 108 Poise and a temperature of no lower than 50 °C. The method 100 of making a glass ribbon 30b also includes a step 130 of conveying the cast glass 30a from the caster 20. In addition, the method 100 of making a glass ribbon 30b further includes a step 140 of drawing the cast glass 30a at an average viscosity of less than 107 Poise into a glass ribbon 30b having a width (W,.*/,<,„) 32 that is less than the width (WJ 22 of the cast glass 30a, and to a final thickness 24 (r). Further, the drawing step 140 comprises heating the cast glass 30a to an average viscosity of less than 107 Poise. The method 100 of making a glass ribbon 30b further includes a step 150 of cooling the glass ribbon 30b to ambient temperature.
With regard to the step 110 of flowing the glass shown in FIG. 1, a suitable melting apparatus 10 may deliver the glass 30 via an exit element 4 having a maximum dimension 12, which is the approximate width of the glass 30 as it leaves the melting apparatus 10 and flows into the caster 20. Depending on the viscosity of the glass 30 flowing from the melting apparatus 10, it can have a width that is about the same as, or smaller, than the maximum dimension 12 of the exit element 4. According to the method 100 of making a glass ribbon 30b, the maximum dimension 12 of the exit element 4 can be less than or equal to the width (WiiUf) 22 of the caster 20. The maximum dimension 12 of the exit element 4 can be larger than the width (Wa,st) 22 of the caster 20, e.g., for compositions of the glass 30 that have a relatively low upper liquidus viscosity (e.g., 0.5 Pa-s (5 Poise) to 500 Pa-s (5000 Poise)). In particular, these glasses upon melting can neck’ as they leave the exit element 4 of the melting apparatus 10, allowing them to flow into a caster 20 having a width 22 that is smaller in dimension than the maximum dimension 12 of the exit element 4 of the melting apparatus 10.
Referring again to the method 100 of making a glass ribbon 30b depicted in FIG. 1, the melting apparatus 10 can include an overflow forming device in which the exit element 4 serves to distribute the glass 30 or a melter with an exit element 4 in the form of an orifice. In the latter, the melting apparatus 10 can include a weir, which allows the glass 30 to overflow and spread along an exit element 4 in the form of an isopipe (see, e.g., the overflow forming device with an isopipe depicted in FIGS. 3A and 3B). Here, the glass 30 can spread on one or both sides of the isopipe. As to the former, the melting apparatus 10 can include a melter with an orifice that distributes the melted glass 30 as it leaves the melting apparatus 10. Further, those with ordinary skill in the field of the disclosure can construct other melting apparatus 10 suitable for use in the method 100 of making a glass ribbon 30b.
In the method 100 of making a glass ribbon 30b depicted in FIG. 1, the glass 30 is preferably derived from a glass composition including borosilicate glasses, aluminoborosilicate glasses, aluminosilicate glasses, fluorosilicate glasses, phosphosilicate glasses, fluorophosphate glasses, sulfophosphate glasses, germanate glasses, vanadate glasses, borate glasses, and phosphate glasses., The glass 30 can be derived from any of the glass compositions, as exhibiting optical properties (e.g., transmissivity, refractive index, coefficient of thermal expansion, etc.) suitable for lenses and optical components. The glass 30 can be derived from the following glass composition (referred herein as “Glass A”): 40.2 mol% SiO2; 2.4 mol% B2O3; 11.3 mol% Li2O; 22.9 mol% CaO; 5.4 mol% La2O3; 3.8 mol% ZrO2; 4.8 mol% Nb2O5; and 9.3 mol% TiO2. According to another example, the glass 30 is derived from from the following glass composition (referred herein as “Glass B”): 42.7 mol% SiO2; 3.9 mol% B2O3; 4.7 mol% BaO; 26.6 mol% CaO; 4.5 mol% La2O3; 2.2 mol% ZrO2; 6.1 mol% Nb2O5; and 9.3 mol% TiO2.
In the method 100 of making a glass ribbon 30b depicted in FIG. 1, the glass 30 may comprise tin upper liquidus viscosity of less than 5xl04 Pa-s (5xl05 Poise). The glass 30 may be comprised of a composition that exhibits an upper liquidus viscosity of less than 5xl04 Pa-s (5xl05 Poise), of less than IxlO4 Pa-s (IxlO5 Poise), of less than 5xl03 Pa-s (5xl04 Poise), of less than IxlO3 Pa-s (IxlO4 Poise), of less than5x!03 Pa-s (5x10’ Poise), of less than IxlO2 Pa-s (IxlO3 Poise), of less than 5x10* Pa-s (5xl02 Poise), of less than 10 Pa-s (100 Poise), of less than 5 Pa-s (50 Poise), of less than 4 Pa-s (40 Poise), of less than 3 Pa-s (30 Poise), of less than 2 Pa-s (20 Poise), of less than 1 Pa-s (10 Poise), and all upper liquidus viscosities between these levels. The upper liquidus viscosity of the glass 30 during the step 110 can range from about 0.5 Pa-s (5 Poise) to about 5000 Pa-s (50000 Poise). Further, the glass 30 can be derived from a glass composition having a refractive index from about 1.5 to about 2.1. The glass 30 can be derived from a glass composition having a refractive index from about 1.6 to about 2.0, from about 1.65 to about 1.9, from about 1.7 to about 1.85, and all refractive index values between these levels.
Referring again to the flowing step 110 of the method 100 of making a glass ribbon 30b depicted in FIG. 1, this step can be conducted such that the glass 30 is flowed at a temperature of 1000 °C or greater. The glass 30 may be flowed at a temperature from about 1000 °C to about 1500 °C, from about 1000 °C to about 1400 °C, from about 1000 °C to about 1300 °C, from about 1000 °C to about 1250 °C, from about 1000 °C to about 1200 °C, from about 1000 °C to about 1150 °C, and all values between these levels. The flowing step 110 may be conducted such that the glass 30 has a viscosity of less than 5xl03 Pa-s (5xl04 Poise) as it flows from the melting apparatus 10. The glass 30, as it leaves the exit element 4 of the melting apparatus 10 and flows into the caster 20, can have a viscosity of less than 5xlO3 Pa-s (5xl04 Poise), of less than IxlO3 Pa-s (IxlO4 Poise), of less than 5xl02 Pa-s (5xl03 Poise), of less than IxlO2 Pa-s (IxlO3 Poise), of less than 5x10 Pa-s (5xl02 Poise), of less than 10 Pa-s (100 Poise), of less than 5 Pa-s (50 Poise), of less than 4 Pa-s (40 Poise), of less than 3 Pa-s (30 Poise), of less than 2 Pa-s (20 Poise), of less than IPa-s (10 Poise), and all viscosities between these levels. According to some implementations of the method 100, the glass 30, as it leaves the melting apparatus 10, has a viscosity during the step 110 that ranges from about 1 Pa-s (10 Poise) to about 100 Pa-s (1000 Poise), or from about 1 Pa-s (10 Poise) to about 5000 Pa-s (50,000 Poise).
Referring again to the step 110 of the method 100 of making a glass ribbon 30b depicted in FIG. 1, the step includes flowing the glass 30 into a caster 20 having a width (VF«tt() 22 from about 200 mm to about 5 meters (m) and a thickness (ƒ) 24 from about 1 mm to about 500 mm to form the cast glass 30a (see also FIG. 2). The width (144^,) 22 of the caster 20 can be from about 200 mm to about 5 meters (m), from about 250 mm to about 5 m, from about 300 mm to about 5 m, from about 350 mm to about 5 m, from about 400 mm to about 5 m, from about 450 mm to about 5 m, from about 500 mm to about 5 m, and all width values between these levels. The width (W(«s;) 22 of the caster 20 can be from about 200 mm to about 5 m, from about 200 mm to about 4 m, about 200 mm to about 3 m, about 200 mm to about 2 m, about 200 mm to about 1 m, about 200 mm to about 0.9 m, about 200 mm to about 0.8 m, about 200 mm to about 0.7 m, about 200 mm to about 0.6 m, about 200 mm to about 0.5 m, and all width values between these levels. Further, the thickness (0 24 (see FIG. 2) of the caster 20 can be about 1 mm or greater, about 2 mm or greater, about 3 mm or greater, about 4 mm or greater, about 5 mm or greater, about 7 mm or greater, about 8 mm or greater, about 9 mm or greater, about 10 mm or greater, about 15 mm or greater, about 20 mm or greater, about 25 mm or greater, about 30 mm or greater, about 35 mm or greater, about 40 mm or greater, about 45 mm or greater, about 50 mm or greater, or any thickness up to about 500 mm.
Referring now to step 120 of the method 100 of making a glass ribbon 30b depicted in FIG. 1, this step is for cooling the cast glass 30a in the caster 20 to a viscosity of at least 107 Pa-s (108 Poise) and a temperature of no lower than 50 °C. As such, the caster 20 can be of varied construction, e.g., of various materials with or without additional cooling capabilities, as understood by those of ordinary skill in the field of the disclosure, provided that it is capable of cooling the glass 30 through its devitrification zone to cool the cast glass 30a to a temperature of no lower than 50 °C, e.g., as it is being conveyed in the direction of the arrows shown in FIG. 1 by the tractor 40. The step 120 of cooling the cast glass 30a may be conducted such that the maximum growth rate of any crystalline phase is less than 10 pm/min from the upper liquidus viscosity to the lower liquidus viscosity of the glass 30a (also referred to herein as the “devitrification zone”). The step 120 of cooling the cast glass 30a can be conducted such that a maximum growth rate of any crystalline phase of the glass 30 through the devitrification zone is less than 10 pm/min, less than 9 pm/min, less than 8 pm/min, less than 7 pm/min, less than 6 pm/min, less than 5 pm/min, less than 4 pm/min, less than 3 pm/min, less than 2 pm/min, less than 1 pm/min, less than 0.5 pm/min, less than 0.1 pm/min, less than 0.01 pm/min, and all growth rates below and/or between these rates. Notably, the maximum crystal growth rate (Vmax) for the Glass A and Glass B compositions is about 6-7 pm/min at 1030 °C and about 2-3 pm/min at 1050 °C, respectively. Accordingly, aspects of the method 100 include performing the cooling step 120 such that the crystal growth rate of glass 30, when fabricated from the Glass A or Glass B composition, are less than these maximum crystal growth rate (Vmax) values.
According to the method 100 of making a glass ribbon 30b depicted in FIG. 1, the cooling step 120 can be conducted to cool the cast glass 30a to a temperature (i.e., no lower than 50 °C) at or above a critical cooling rate for the cast glass 30a. As used herein, the “critical cooling rate” is determined by melting multiple samples of a given glass composition down to its glass transition temperature at various, selected cooling rates. The samples are then cross-sectioned according to standard sectioning and polishing techniques, and evaluated with optical microscopy at lOOx to ascertain the presence of crystals in the bulk and at its free surfaces (i.e., the top, exposed surface and the bottom surface with an interface with a crucible or the like). The critical cooling rate corresponds to the samples with the slowest cooling rate not exhibiting crystals at its surfaces and bulk.
The tractor 40 preferably includes one or more rollers for controlling the velocity of the cast glass 30a as it travels through and exits the caster 20 during the cooling step 120 and conveying step 130, respectively. Advantageously, the cooling step 120 is conducted in a fashion to ensure that the cast glass 30a does not fall below 50 °C, to ensure that the method 100 can remain continuous in view of the additional heating that occurs during the subsequent conveying step 130 and drawing step 140, respectively. The thermal energy remaining in the cast glass 30a after the cooling step 120 can be employed to re-heat the cast glass 30a from its core toward its surface during the subsequent conveying and drawing steps 130 and 140, respectively.
In the method 100 depicted in FIG. 1, the temperature during the cooling step 120 is preferably no lower than 50 °C, no lower than 100 °C, no lower than 150 °C, no lower than 200 °C, no lower than 250 °C, no lower than 300 °C, no lower than 350 °C, no lower than 400 °C, no lower than 450 °C, no lower than 500 °C, and all temperature values between these lower threshold levels. In the method 100, the cooling step 120 can comprise cooling the cast glass 30a in the caster 20 to a temperature of less than 800 °C and no lower than 50 °C. According the method 100, the flowing, cooling, pulling and drawing steps 110-140 can be conducted such that the cast glass 30a does not reach a temperature below 50 °C, e.g., to ensure that the method 100 can be run in a continuous fashion. According to the method 100, the step of cooling 120 can be conducted such that the cast glass 30a in the caster 20 is at a viscosity of at least 107 Pa-s (108 Poise), at least 5xl07 Pa-s (5xl0‘8 Poise), at least 10s Pa-s (109 Poise), at least 5xl08 Pa-s (5xl09 Poise), at least 109 Pa-s (10iO Poise), at least 5xl09 Pa-s (5x1010 Poise), or higher viscosities. In the method 100 of making a glass ribbon 30b, the cooling step 120 can be conducted such that the cast glass 30a is preferably maintained at a temperature between about 650 °C and about 750 °C and a viscosity of at least 108 Pa-s (109 Poise).
Referring again to the method 100 of making a glass ribbon 30b depicted in FIG. 1, the method preferably further includes a conveying step 130 for conveying the cast glass 30a from the caster 20. The conveying aspect of step 130 can be effected in part by the action of the tractor 40. In particular, the cast glass 30a can be moved or otherwise conveyed during step 130 by the tractor 40 from the end of the caster 20 toward an optional bank of heaters 50 and edge rollers 60. According to the method 100, the conveying step 130 can be conducted to control the velocity of the cast glass 30a, e.g., such that the flow rate of the cast glass 30a varies by no more than 1%.
The method 100 of making a glass ribbon 30b preferably also includes a step 140 of drawing the cast glass 30a at an average viscosity less than the viscosity of the cast glass 30a in the conveying step 130, e.g., at an average viscosity of less than 109 Pa-s (107 Poise). Step 140 also comprises heating the cast glass 30a to an average viscosity of less than 106 Pa-s (107 Poise), e.g., with the optional bank of heaters 50. When present, the heaters 50 can include any of various structures and components for heating the cast glass 30a to an average viscosity of less than 106 Pa-s (107 Poise) including but not limited to resistance heating elements, induction heating elements, infrared heating elements, and others as understood by those with ordinary skill in the field of the disclosure. In some examples the aspect of step 140 that involves heating the cast glass 30a to an average viscosity of less than 106 Pa-s (107 Poise) does not impart any additional thermal energy on the cast glass 30a. For example, the drawing step 140 can be conducted such that a core of the cast glass 30a heats the surface of the cast glass 30a at least in part to an average viscosity of less than 10° Pa-s (107 Poise).
Further, the drawing step 140 of drawing the cast glass 30a can be conducted to draw the cast glass 30a into a glass ribbon 30b having a width 32 (Wrihho>i) that is less than or equal to the width 22 (IKasi) of the caster 20 and a final thickness (f) 34 that is less than or equal to the thickness (/) 24 of the cast glass 30a (see also FIG. 2). The width 32 ( Wrii,hmi) of the glass ribbon 30b can be from about 10 mm to about 5 mm, from about 20 mm to about 5 mm, from about 30 mm to about 5 mm, from about 40 mm to about 5 mm, from about 50 mm to about 5 mm, from about 100 mm to about 5 mm, from about 200 mm to about 5 mm, from about 250 mm to about 5 mm, from about 300 mm to about 5 mm, from about 350 mm to about 5 mm, from about 400 mm to about 5 mm, and all width values between these levels. The aspect of the step 140 of drawing the cast glass 30a into the ribbon 30b can be effected in part by the action of the edge rollers 60 depicted in FIG. 1.
According to the method 100 of making a glass ribbon 30b, the drawing step 140 can be conducted on the cast glass 30a for no more than 30 minutes (i.e., after the step 120 for cooling the cast glass 30a and step 130 for conveying the cast glass 30a, and before a subsequent step 150 for cooling the glass ribbon 30b to ambient temperature). It should be understood that according to the method 100, the cast glass 30a is at a temperature of about 50 °C or higher during each of the steps 110-140. The drawing step 140 may be conducted for 30 minutes or less, 25 minutes or less, 20 minutes or less, 15 minutes or less, 10 minutes or less, 5 minutes or less, and all durations less than these upper threshold duration values while maintaining a duration of at least 30 seconds. As noted earlier, aspects of the method 100 of making a glass ribbon 30b are conducted such that the temperature and/or time during the drawing step 140 are advantageously minimized to ensure that the cast glass 30a does not experience any or very little crystallization, while maintaining the cast glass 30a at a sufficiently low viscosity to effect the drawing aspect of this step - i.e., transforming the cast glass 30a into a glass ribbon 30b having a width 32 that is less than the width 22 of the cast glass 30a.
According to the method 100 of making a glass ribbon 30b depicted in FIG. 1, the conveying step 130 and the drawing step 140 may be conducted such that the cast glass 30a is preferably maintained at an average viscosity of less than 106 Pa-s (107 Poise), of less than 5x10' Pa-s (5xl06 Poise), of less than 105 Pa-s (106 Poise), of less than 5xl04 Pa-s (5x 103 Poise), of less than 104 Pa-s (105 Poise), of less than 5x10'’ Pa-s (5xl04 Poise), while no lower than 103 Pa-s (104 Poise), and all average viscosities between these levels. In the method 100, the average viscosity of the cast glass 30a can be maintained during the conveying step 130 and the drawing step 140 between 105 Pa-s (106 Poise) and 103 Pa-s (104 Poise), at temperatures between 750 °C and 900 °C.
Referring again to the method 100 of making a glass ribbon 30b depicted in FIG. 1, a final cooling step 150 of the method can include cooling the glass ribbon 30b to ambient temperature. As noted earlier, the method 100 is preferably conducted such that the glass 30 and cast glass 30a are maintained at a temperature no lower than 50 °C during steps 110-140, thus ensuring that the method 100 can be run in a continuous fashion. According to the method 100, steps 110-140 can be conducted a temperatures of no lower than 50 °C, no lower than 75 °C, no lower than 100 °C, no lower than 150 °C, no lower than 200 °C, no lower than 250 °C, no lower than 300 °C, and all lower temperature threshold values between these lower temperature limits. Further, the step 150 for cooling the glass ribbon 30b can be conducted with or without external cooling, as understood by those with ordinary skill in the field of the disclosure. Further, in some aspects of the method 100, the edge rollers 60 can include a cooling capability for effecting some or all of the cooling within the cooling step 150.
Still referring to the method 100 of making a glass ribbon 30b depicted in FIG. 1, the method 100 can be conducted such that the glass ribbon 30b has a thickness variation of less than 200 pm. The glass ribbon 30b can have a thickness variation of less than 200 pm, less than 150 pm, less than 100 pm, less than 75 pm, less than 50 pm, less than 40 pm, less than 30 pm, less than 20 pm, less than 10 pm, less than 5 pm, less than 4 pm, less than 3 pm, less than 2 pm, less than 1 pm, less than 0.5 pm, and all thickness variation levels between these levels. From a practical standpoint, the glass ribbon 30h fabricated according to the method 100 may have a thickness variation as low as 0.01 pm. In the method 100, the glass ribbon 30b produced by the method 100 may have a warp of less than 500 pm. The glass ribbon 30b produced by the method 100 can have a warp of less than 500 pm, less than 400 pm, less than 300 pm, less than 200 pm, less than 150 pm, less than 100 pm, less than 50 pm, less than 40 pm, less than 30 pm, less than 20 pm, less than 10 pm, less than 5 pm, less than 0.1 pm, above 0.05 pm, and all warp values between these levels. From a practical standpoint, the glass ribbon 30b fabricated according to the method 100 may have a warp as low as 0.01 pm. Still further, the method 100 can be conducted such that the glass ribbon 30b has a surface roughness (Ra) of less than 5 pm (as measured prior to any post-processing). The glass ribbon 30b produced by the method 100 may have a surface roughness (Ra) of less than 5 pm, less than 4 pm, less than 3 pm, less than 2 pm, less than 1 pm, less than 0.75 pm, less than 0.5 pm, less than 0.25 pm, less than 0.1 pm, less than 50 nm, as low as 10 nm, and all surface roughness values between these levels. The glass ribbon 30b produced by the method 100 may have a surface roughness (Ra) of less than 1 pm, less than 0.9 pm, less than 0.8 pm, less than 0.7 pm, less than 0.6 pm, less than 0.5 pm, less than 0.4 pm, less than 0.3 pm, less than 0.2 pm, as low as 0.1 pm, less than 90 nm, less than 80 nm, less than 70 nm, less than 60 nm, less than 50 nm, less than 40 nm, less than 30 nm, less than 20 nm, as low as 10 nm, and all surface roughness values between these levels.
Referring now to FIG. 2, a schematic view is provided of apparatus that can be used according to the method 100 of making a glass ribbon 30b (see FIG. 1), according to the disclosure. In particular, FIG. 2 depicts a melting apparatus 10a with an orifice 4a, a caster 20 and heaters 50, among other features. In all other respects, the apparatus depicted in FIG. 2 is the same or substantially similar to the apparatus depicted in FIG. I for use with the method 100 of making a glass ribbon 30b (see FIG. 1 and earlier description). Accordingly, like-numbered elements in FIG. 2 have the same or substantially similar functions and structures as those depicted in FIG. 1. Further, according to the method 100 (see FIG. 1), the flowing step 110 can be conducted by flowing a glass 30 from an orifice 4a of the melting apparatus 10a (see FIG. 2) having a maximum dimension 12 of less than 5 meters (m). The maximum dimension 12 of the orifice 4a can be less than or equal to the width (VFm«) 22 of the caster 20. Further, the width 14 of the orifice 4a can be about 1 mm or greater, about 2 mm or greater, about 3 mm or greater, about 4 mm or greater, about 5 mm or greater, about 7 mm or greater, about 8 mm or greater, about 9 mm or greater, about 10 mm or greater, about 15 mm or greater, about 20 mm or greater, about 25 mm or greater, about 30 mm or greater, about 35 nun or greater, about 40 mm or greater, about 45 nun or greater, about 50 mm or greater, or any width up to about 500 mm.
Referring again to FIG. 2, depending on the viscosity of the glass 30 flowing from the melting apparatus 10a during the flowing step 110 (see FIG. 1), the glass 30 can have a width that is about the same as, or smaller than, the maximum dimension 12 of the orifice 4a. As such, the maximum dimension 12 of the orifice 4a can be less than or equal to the width (Wauf) 22 of the caster 20. The maximum dimension 12 of the orifice 4a can be larger than the width (22 of the caster 20, e.g., for compositions of the glass 30 that are relatively low in upper liquidus viscosity (e.g., 0.5 Pa-s to 5000 Pa-s (5 Poise to 50000 Poise)). In particular, these glasses upon melting can ‘neck’ as they leave the orifice 4a of the melting apparatus 10a, allowing them to flow into a caster 20 having a width 22 that is smaller in dimension than the maximum dimension 12 of the orifice 4a of the melting apparatus 10a.
As is also shown in FIG 2, the glass ribbon 30b can be sectioned into wafers 36 having outer diameters ranging from substantially equivalent to the width 32 ( W„m,o„) of the glass ribbon 30b to about 50% of the width 32 of the glass ribbon 30b. A step of sectioning the walers 36 from the glass ribbon 30b can be conducted after the cooling step 150 of the method 100 outlined earlier and shown in FIG. 1. The wafers 36, as shown in exemplary form in FIG. 2, are in the form of discs. Nevertheless, the wafers 36 can take on any of a variety of shapes including, but not limited to, squares, rectangles, circles, ellipsoids and others. The wafers 36 can have a thickness 34 (t) of about 2 mm or less and a maximum dimension (e.g., a diameter, width or other maximum dimension) of about 100 mm to about 500 mm. The wafers 36 can have a thickness 34 (ƒ) of about 1 nun or less and a maximum dimension of 150 mm to about 300 mm. The waters 36 can also have a thickness that ranges from about 1 mm to about 50 mm, or about 1 mm to about 25 mm. The wafers 36 can also have a maximum dimension that ranges from about 25 mm to about 300 mm, from about 50 mm to about 250 mm, from about 50 mm to about 200 mm, or about 100 mm to about 200 mm. Advantageously, the walers 36 formed according to the method 100, without any additional surface polishing, can exhibit the same thickness variation levels, surface roughness and/or warp levels outlined earlier in connection with the glass ribbon 30b. The wafers 36 can be subjected to some limited grinding and polishing of their outer diameters to obtain the final dimensions of the end product, e.g., lenses for optical applications.
Referring now to FIGS. 3A and 3B, schematic views of an overflow melting apparatus 10b with an isopipe 8 for flowing glass 30 as employed in a method 100 of making a glass ribbon 30b (see FIG. 1), are provided. . In particular, the overflow melting apparatus 10b can be employed during the step 110 of flowing glass 30. Glass 30 can be melted according to a melting aspect of the method 100 and flowed from a vessel 6 into the isopipe 8. The vessel 6 includes any of a variety of heating elements understood by those with ordinary skill in the field of the disclosure for melting of glass. As the glass 30 overflows from a weir or similar aspect of the isopipe 8, it flows over the isopipe 8 and down into the caster 20 (not shown). As shown in exemplary form in FIGS. 3A and 3B, the overflow melting apparatus 10b can include a weir within the isopipe 8, which allows the glass 30 to overflow and spread along an outer surface of the isopipe 8. The glass 30 can spread on one or both sides of the isopipe 8 to a width 4b. As shown in FIGS. 3A and 3B, the isopipe 8 has a one side, angled from vertical by an angle 9. Typically, angle 9 is between about 0° and 30°, preferably 0° to 20°. According to the method 100 of making a glass ribbon 30b (see FIG. 1), the overflow melting apparatus 10b can have a width 4b of less than 5 m, which is less than or equal to the width 22 (Wr£m) of the caster 20.
While examples have been set forth for the purpose of illustration, the foregoing description is not intended in any way to limit the scope of disclosure and appended claims. Accordingly, variations and modifications may be made to the above-described examples without departing substantially from the spirit and various principles of the disclosure. All such modifications and variations are intended to be included herein within the scope of this disclosure and protected by the following claims.
Unless otherwise expressly stated, it is in no way intended that any method set forth herein be construed as requiring that its steps be performed in a specific order. Accordingly, where a method claim does not actually recite an order to be followed by its steps or it is not otherwise specifically stated in the claims or description that the steps are to be limited to a specific order, it is no way intended that any particular order be inferred.
It will be apparent to those skilled in the art that various modifications and variations can be made without departing from the spirit or scope of the illustrated embodiments. Since modifications, combinations, sub-combinations and variations of the disclosed embodiments that incorporate the spirit and substance of the illustrated embodiments may occur to persons skilled in the art, the description should be construed to include everything within the scope of the appended claims and their equivalents.

Claims (26)

CLAUSESCLAUSES 1. A method for making a glass ribbon, comprising:1. A method for making a glass ribbon, including: - flowing a glass into a caster having a width (WCiUZ) from about 100 mm to about 5 m and a thickness (/) from about 1 mm to about 500 mm to form a cast glass;- flowing a glass into a caster having a width (W CiUZ ) from about 100 mm to about 5 mm and a thickness (/) from about 1 mm to about 500 mm to form a cast glass; - cooling the cast glass in the caster to a viscosity of at least 107 Pa-s (10s Poise);- cooling the cast glass in the caster to a viscosity or at least 10 7 Pa-s (10 s Poise); - conveying the cast glass from the caster;- conveying the cast glass from the caster; - drawing the cast glass from the caster, the drawing comprising heating the cast glass to an average viscosity of less than 106 Pa-s (107 Poise) and drawing the cast glass into a glass ribbon having a width (Wrihho„) that is less than W^·,; and thereafter- drawing the cast glass from the caster, the drawing including heating the cast glass to an average viscosity of less than 10 6 Pa-s (10 7 Poise) and drawing the cast glass into a glass ribbon having a width (W rihho „) that is less than W ^ · ,; and thereafter - cooling the glass ribbon to ambient temperature, wherein the cast glass during the cooling, conveying and drawing steps is at about 50 °C or higher,- cooling the glass ribbon to ambient temperature, the cast glass during the cooling, conveying and drawing steps is at about 50 ° C or higher, 2. The method according to clause 1, wherein the flowing step comprises flowing the glass at a viscosity of about 5000 Pa-s (50,000 Poise) to about 1 Pa-s (10 Poise).2. The method according to clause 1, the flowing step comprises flowing the glass at a viscosity of about 5,000 Pa-s (50,000 Poise) to about 1 Pa-s (10 Poise). 3. The method according to clause 1 or 2, wherein the cast glass during the cooling, conveying and drawing steps is at about 200 °C or higher,3. The method according to clause 1 or 2, involving the cast glass during the cooling, conveying and drawing steps is at about 200 ° C or higher, 4. The method according to clause 1,2 or 3, wherein the step of cooling the cast glass is conducted such that the cast glass in the caster is cooled to a viscosity of at least 108 Pa-s (109 Poise).4. The method according to clause 1.2 or 3, in which the step of cooling the cast glass is conducted such that the cast glass in the caster is cooled to a viscosity or at least 10 8 Pa-s (10 9 Poise). 5. The method according to any one of the preceding clauses, wherein the drawing step is conducted such that the cast glass is heated to an average viscosity of less than 105 Pa-s (106 Poise).5. The method according to any one of the preceding clauses, following the drawing step is conducted such that the cast glass is heated to an average viscosity or less than 10 5 Pa-s (10 6 Poise). 6. The method according to any one of the preceding clauses, wherein the glass comprises an upper liquidus viscosity of less than 5xl04 Pa-s (5xl05 Poise).6. The method according to any one of the preceding clauses, comprising the glass comprising an upper liquidus viscosity or less than 5xl0 4 Pa-s (5xl0 5 Poise). 7. The method according to any one of the preceding clauses, wherein the glass comprises a composition selected from the group consisting of borosilicate glasses, aluminoborosilicate glasses, aluminosilicate glasses, fluorosilicate glasses, phosphosilicate glasses, fluorophosphate glasses, sulfophosphate glasses, germanate glasses, vanadate glasses, borate glasses, and phosphate glasses.7. The method according to any of the preceding clauses, comprising the glass comprising a composition selected from the group consisting of borosilicate glasses, aluminoborosilicate glasses, aluminosilicate glasses, fluorosilicate glasses, phosphosilicate glasses, fluorophosphate glasses, sulfophosphate glasses, germanate glasses, vanadate glasses, borate glasses, and phosphate glasses. 8. The method according to any one of the preceding clauses, wherein the flowing step comprises flowing the glass at a temperature of 1000 °C or greater and the cooling the cast glass step comprises cooling the cast glass in the caster to a temperature of less than 800 °C and no lower than 50 °C.8. The method according to any one of the preceding clauses, following the flowing step comprises flowing the glass at a temperature of 1000 ° C or greater and the cooling the cast glass step comprising cooling the cast glass in the caster to a temperature of less than 800 ° C and no lower than 50 ° C. 9. The method according to any one of the preceding clauses, wherein the width (W„„J is from about 400 mm to about 5 m and the thickness (t) is from about 5 mm to about 500 mm.9. The method according to any one of the preceding clauses, according to the width (W "" J is from about 400 mm to about 5 mm and the thickness (t) is from about 5 mm to about 500 mm. 10. The method according to any one of the preceding clauses, wherein the drawing step is conducted on the cast glass between about 30 seconds and about 30 minutes after the step of cooling the cast glass.10. The method according to any one of the preceding clauses, the drawing step is conducted on the cast glass between about 30 seconds and about 30 minutes after the step of cooling the cast glass. 11. The method according to any one of the preceding clauses, wherein the drawing is conducted such that a core of the cast glass heats the surface of the cast glass at least in part to an average viscosity of less than 106 Pa-s (107 Poise).11. The method according to any one of the preceding clauses, following the drawing is conducted such that a core of the cast glass heats the surface of the cast glass at least in part to an average viscosity or less than 10 6 Pa-s ( 10 7 Poise). 12. The method according to any one of the preceding clauses, wherein the flowing step is conducted by flowing a glass from an orifice of a melting apparatus having a width from about 100 mm to about 5 m, the width of the orifice less than or equal to the width (W(;atr) of the caster.12. The method according to any one of the preceding clauses, following the flowing step is conducted by flowing a glass from an orifice or a melting apparatus having a width from about 100 mm to about 5 m, the width of the orifice less than or equal to the width (W (; atr ) or the caster. 13. The method according to clause 12, wherein the melting apparatus is an overflow forming device.13. The method according to clause 12, where the melting apparatus is an overflow forming device. 14. The method according to any one of the preceding clauses, wherein a maximum crystal growth rate of any crystalline phase of the cast glass is from about 0.01 pm/min to about 10 pm/min during the cooling, conveying and drawing the cast glass steps.14. The method according to any one of the preceding clauses, subject to a maximum crystal growth rate or any crystalline phase of the cast glass is from about 0.01 pm / min to about 10 pm / min during the cooling, conveying and drawing the cast glass steps. 15. The method according to any one of the preceding clauses, wherein a maximum crystal growth rate of any crystalline phase of the cast glass is from about 0.01 pm/min to about 5 pm/min during the cooling, conveying and drawing the cast glass steps.15. The method according to any one of the preceding clauses, subject to a maximum crystal growth rate or any crystalline phase of the cast glass is from about 0.01 pm / min to about 5 pm / min during the cooling, conveying and drawing the cast glass steps. 16. The method according to any one of the preceding clauses, wherein the composition of the glass further comprises a crystal growth rate of any crystalline phase from about 0.01 pm/min to less than 1 pm/min, as measured from the upper liquidus temperature to the lower liquidus temperature of the cast glass.16. The method according to any one of the preceding clauses, according to the composition of the glass further comprises a crystal growth rate or any crystalline phase from about 0.01 pm / min to less than 1 pm / min, as measured from the upper liquidus temperature to the lower liquidus temperature of the cast glass. 17. The method according to any one of the preceding clauses, wherein the glass ribbon has a thickness variation from about 0.01 pm to about 50 pm.17. The method according to any one of the preceding clauses, the glass ribbon has a thickness variation from about 0.01 pm to about 50 pm. 18. The method according to any one of the preceding clauses, wherein the glass ribbon has a warp from about 0.01 pm to about 100 pm.18. The method according to any one of the preceding clauses, the glass ribbon has a warp from about 0.01 pm to about 100 pm. 19. The method according to any one of the preceding clauses, wherein the step of cooling the cast glass is conducted to cool the cast glass to a temperature at or above a critical cooling rate for the cast glass.19. The method according to any one of the preceding clauses, the step of cooling the cast glass is conducted to cool the cast glass to a temperature at or above a critical cooling rate for the cast glass. 20. A glass article, comprising:20. A glass article, including: an unpolished glass ribbon having a thickness from about 1 mm to about 25 mm and a width of about 25 mm to about 200 mm, the composition further comprising an upper liquidus viscosity of less than 5x 104 Pa-s (5x103 Poise).an unpolished glass ribbon having a thickness of about 1 mm to about 25 mm and a width of about 25 mm to about 200 mm, the composition further comprising an upper liquidus viscosity or less than 5x 10 4 Pa-s (5x10 3 Poise). 21. The glass article of clause 20, having a width of about 100 mm to about 200 mm.21. The glass article of clause 20, having a width of about 100 mm to about 200 mm. 22. The glass article of clause 20 or 21, wherein the glass ribbon is capable of being sectioned into glass wafers having a thickness variation from about 0.01 pm to about 50 pm and a warp from about 0.01 pm to about 200 pm.22. The glass article or clause 20 or 21, the glass ribbon is capable of being sectioned into glass wafers having a thickness variation from about 0.01 pm to about 50 pm and a warp from about 0.01 pm to about 200 pm. 23. The glass article according to any one of the preceding clauses 20 - 22, wherein the glass ribbon has a refractive index from about 1.65 to about 1.90.23. The glass article according to any of the preceding clauses 20 - 22, the glass ribbon has a refractive index from about 1.65 to about 1.90. 24. The glass article according to any one of the clauses 20 - 23, wherein the glass ribbon is capable of being sectioned into glass wafers having a thickness variation from about 0.01 pm to about 0.5 pm and a warp from about 0.01 pm to about 10 pm.24. The glass article according to any one of the clauses 20 - 23, the glass ribbon is capable of being sectioned into glass wafers having a thickness variation from about 0.01 pm to about 0.5 pm and a warp from about 0.01 pm to about 10 p.m. 25. The glass article according to any one of the clauses 20 - 24, wherein the glass ribbon has a thickness variation from about 0.01 pm to about 50 pm and a warp from about 0.01 pm to about 200 pm.25. The glass article according to any one of the clauses 20 - 24, the glass ribbon has a thickness variation from about 0.01 pm to about 50 pm and a warp from about 0.01 pm to about 200 pm. 26. The glass composition according to any one of the preceding clauses 20 - 25, wherein the glass ribbon comprises a composition selected from the group consisting of borosilicate glasses, aluminoborosilicate glasses, aluminosilicate glasses, fluorosilicate glasses, phosphosilicate glasses, fluorophosphate glasses, sulfophosphate glasses, germanate glasses, vanadate glasses, phosphate glasses and borate glasses.26. The glass composition according to any of the preceding clauses 20 - 25, comprising the glass ribbon comprises a composition selected from the group consisting of borosilicate glasses, aluminoborosilicate glasses, aluminosilicate glasses, fluorosilicate glasses, phosphosilicate glasses, fluorophosphate glasses, sulfophosphate glasses , germanate glasses, vanadate glasses, phosphate glasses and borate glasses. 5 27. A glass article obtainable according to the method of any of the preceding clauses 1 19.5 27. A glass article available according to the method or any of the preceding clauses 1 19. CONCLUSIESCONCLUSIONS 1. Werkwijze voor het vervaardigen van een glazen band, omvattende:A method for manufacturing a glass band, comprising: - het vloeien van een glas in een gietvorm die een breedte (Wfeyi) van ongeveer 100 mm tot ongeveer 5 m en een dikte (/) van ongeveer 1 mm tot ongeveer 500 mm heeft om een gegoten glas te vormen;- flowing a glass in a mold having a width (W feyi ) of about 100 mm to about 5 m and a thickness (/) of about 1 mm to about 500 mm to form a cast glass; - het koelen van het gegoten glas in de gietvorm tot een viscositeit van tenminste 107 * Pa-s (10s Poise);- cooling the molded glass in the mold to a viscosity of at least 10 7 * Pa-s (10 s Poise); - het vervoeren van het gegoten glas uit de gietvorm;- transporting the cast glass from the mold; - het trekken van het gegoten glas uit de gietvorm, het trekken omvattende het verwarmen van het gegoten glas tot een gemiddelde viscositeit van minder dan 106 Pa-s (107 Poise) en het trekken van het gegoten glas tot een glazen band die een breedte (Wrihhon) heeft die minder is dan Wj.a„; en daarna- pulling the molded glass from the mold, drawing comprising heating the molded glass to an average viscosity of less than 10 6 Pa-s (10 7 Poise) and pulling the molded glass into a glass band that has a width (W rihhon ) that is less than Wj. a '; and after that - het koelen van de glas een band naar omgevingstemperatuur, waarbij het gegoten glas tijdens de koel-, vervoer- en trekstappen ongeveer 50 °C of hoger is.- cooling the glass a band to ambient temperature, wherein the cast glass is approximately 50 ° C or higher during the cooling, transport and draw steps. 2. Werkwijze volgens conclusie 1, waarbij de vloeiingsstap het vloeien van het glas bij een viscositeit van ongeveer 5.000 Pas (50.000 Poise) tot ongeveer 1 Pas (10 Poise) omvat.The method of claim 1, wherein the flow step comprises flowing the glass at a viscosity of from about 5,000 Pas (50,000 Poise) to about 1 Pas (10 Poise). 3. Werkwijze volgens conclusie 1 of 2, waarbij het gegoten glas tijdens de koel-, vervoeren trekstappen ongeveer 200 °C of hoger is.A method according to claim 1 or 2, wherein the poured glass is approximately 200 ° C or higher during the cooling, transporting and drawing steps. 4. Werkwijze volgens conclusie 1, 2 of 3, waarbij de stap van het koelen van het gegoten glas zodanig wordt uitgevoerd dat het gegoten glas in de gietvorm wordt gekoeld tot een viscositeit van tenminste 10s Pa-s (IO9 Poise).Method according to claim 1, 2 or 3, wherein the step of cooling the cast glass is carried out such that the cast glass in the mold is cooled to a viscosity of at least 10 s Pa-s ( 10 9 Poise). 5. Werkwijze volgens één der voorgaande conclusies, waarbij de trekstap zodanig wordt uitgevoerd dat het gegoten glas wordt verwarmd tot een gemiddelde viscositeit van minder dan 10’ Pa-s (106 Poise).A method according to any one of the preceding claims, wherein the drawing step is carried out such that the cast glass is heated to an average viscosity of less than 10 'Pa-s (10 6 Poise). 6. Werkwijze volgens één der voorgaande conclusies, waarbij het glas een bovenste vloeibare viscositeit van minder dan 5xl04 Pa-s (5x10' Poise) omvat.A method according to any one of the preceding claims, wherein the glass comprises an upper liquid viscosity of less than 5x10 4 Pa-s (5x10 'Poise). 7. Werkwijze volgens één der voorgaande conclusies, waarbij het glas een samenstelling omvat geselecteerd uit de groep bestaande uit borosilicaat glas, aluminoborosilicaat glas, aluminosilicaat glas, fluorosilicaat glas, phosphosilicaat glas, fluorofosfaat glas, sulfofosfaat glas, germanaat glas, vanadaat glas, boraat glas, en fosfaat glas.The method of any preceding claim, wherein the glass comprises a composition selected from the group consisting of borosilicate glass, aluminoborosilicate glass, aluminosilicate glass, fluorosilicate glass, phosphosilicate glass, fluorophosphate glass, sulfophosphate glass, germanate glass, vanadate glass, borate glass , and phosphate glass. 8. Werkwijze volgens één der voorgaande conclusies, waarbij de vloeiingstap het vloeien van het glas bij een temperatuur van 1000 °C of groter omvat en de koelstap van het gegoten glas het koelen van het gegoten glas in de gietvorm naar een temperatuur van minder dan 800 °C en niet lager dan 50 °C omvat.A method according to any one of the preceding claims, wherein the flow step comprises flowing the glass at a temperature of 1000 ° C or greater and the cooling step of the cast glass cooling the cast glass in the mold to a temperature of less than 800 ° C and not lower than 50 ° C. 9. Werkwijze volgens één der voorgaande conclusies, waarbij de breedte (Wajyf) van ongeveer 400 mm tot ongeveer 15 m is en de dikte (t) van ongeveer 5 mm tot ongeveer 500 mm is.The method of any one of the preceding claims, wherein the width (W ajyf ) is from about 400 mm to about 15 m and the thickness (t) is from about 5 mm to about 500 mm. 10. Werkwijze volgens één der voorgaande conclusies, waarbij de trekstap wordt uitgevoerd op het gegoten glas tussen ongeveer 30 seconden en ongeveer 30 minuten na de stap van het koelen van het gegoten glas.The method of any one of the preceding claims, wherein the drawing step is performed on the molded glass between about 30 seconds and about 30 minutes after the step of cooling the molded glass. 11. Werkwijze volgens één der voorgaande conclusies, waarbij het trekken zodanig wordt uitgevoerd dat een kern van het gegoten glas het oppervlakte van het gegoten glas tenminste ten dele tot een gemiddelde viscositeit van minder dan 106 Pa-s (107 Poise) verwarmd.A method according to any one of the preceding claims, wherein the drawing is carried out such that a core of the cast glass heats the surface of the cast glass at least in part to an average viscosity of less than 10 6 Pa-s (10 7 Poise). 12. Werkwijze volgens één der voorgaande conclusies, waarbij de vloeiingsstap wordt uitgevoerd door het vloeien van een glas uit een uitstroomopening van een smeltapparaat dat een breedte van ongeveer 100 mm tot ongeveer 5 m heeft, waarbij de breedte van de uitstroomopening minder dan of gelijk is aan de breedte (Wtm7) van de gietvorm.A method according to any one of the preceding claims, wherein the flow step is performed by flowing a glass from an outflow opening of a fuser which has a width of about 100 mm to about 5 m, the width of the outflow opening being less than or equal to the width (W tm7 ) of the mold. 13. Werkwijze volgens conclusie 12, waarbij het smeltapparaat een overstroomvormingsinrichting is.The method of claim 12, wherein the melter is an overflow forming device. 14. Werkwijze volgens één der voorgaande conclusies, waarbij een maximale kristalgroeisnelheid van een kristallijne fase van het gegoten glas van ongeveer 0.01 pm/min tot ongeveer 10 pm/min tijdens de koel-, vervoer- en trekstappen- van het gegoten glas is.A method according to any one of the preceding claims, wherein a maximum crystal growth rate of a crystalline phase of the cast glass is from about 0.01 µm / min to about 10 µm / min during the cooling, transport and draw steps of the cast glass. 15. Werkwijze volgens één der voorgaande conclusies, waarbij een maximale kristalgroeisnelheid van een kristallijne fase van het gegoten glas van ongeveer 0.01 pm/min tot ongeveer 5 pm/min tijdens de koel-, vervoer- en trekstappen van het gegoten glas is.The method of any one of the preceding claims, wherein a maximum crystal growth rate of a crystalline phase of the cast glass is from about 0.01 µm / minute to about 5 µm / minute during the cooling, transport, and drawing steps of the cast glass. 16. Werkwijze volgens één der voorgaande conclusies, waarbij de samenstelling van het glas verder een kristalgroeisnelheid van een kristallijne fase van ongeveer 0.01 pm/min tot minder dan 1 pm/min omvat, gemeten vanaf de bovenste vloeibare temperatuur naar de lagere vloeibare temperatuur van het gegoten glas.The method of any one of the preceding claims, wherein the composition of the glass further comprises a crystal growth rate from a crystalline phase of about 0.01 µm / min to less than 1 µm / min measured from the upper liquid temperature to the lower liquid temperature of the poured glass. 17. Werkwijze volgens één der voorgaande conclusies, waarbij de glazen band een diktevariatie heeft van ongeveer 0.01 pm tot ongeveer 50 pm.The method of any one of the preceding claims, wherein the glass band has a thickness variation from about 0.01 µm to about 50 µm. 18. Werkwijze volgens één der voorgaande conclusies, waarbij de glazen band een deformatie heeft van ongeveer 0.01 pm tot ongeveer 100 pm.The method of any one of the preceding claims, wherein the glass band has a deformation of about 0.01 µm to about 100 µm. 19. Werkwijze volgens één der voorgaande conclusies, waarbij de stap van het koelen van het gegoten glas wordt uitgevoerd om het gegoten glas tot een temperatuur op of boven een kritische koelsnelheid voor het gegoten glas te koelen.A method according to any one of the preceding claims, wherein the step of cooling the cast glass is performed to cool the cast glass to a temperature at or above a critical cooling rate for the cast glass. 20. Glasartikel, omvattende:20. Glass article, comprising: - een ongepolijste glazen band die een dikte heeft van ongeveer 1 mm tot ongeveer 25 mm en een breedte van ongeveer 25 mm tot ongeveer 200 mm, de samenstelling verder omvattende een bovenste vloeibare viscositeit van minder dan 5x104 Pa-s (5x105 Poise).- an unpolished glass band having a thickness of about 1 mm to about 25 mm and a width of about 25 mm to about 200 mm, the composition further comprising an upper liquid viscosity of less than 5 x 10 4 Pa (s) ( 5 x 10 5 Poise) . 21. Het glasartikel volgens conclusie 20 voorzien van een breedte van ongeveer 100 mm tot ongeveer 200 mm.The glass article of claim 20 provided with a width of from about 100 mm to about 200 mm. 22. Het glas artikel volgens conclusie 20 of 21, waarbij de glazen band in staat is om te worden verdeeld in glasschijven die een dikte variatie van ongeveer 0.01 pm tot ongeveer 50 pm en deformatie van ongeveer 0.01 pm tot ongeveer 200 pm hebben.The glass article of claim 20 or 21, wherein the glass band is capable of being divided into glass disks having a thickness variation of about 0.01 µm to about 50 µm and deformation of about 0.01 µm to about 200 µm. 23. Het glasartikel volgens één der conclusies 20 - 22, waarbij de glasband een refractie index heeft van ongeveer 1.65 tot ongeveer 1.90.The glass article of any one of claims 20 to 22, wherein the glass band has a refractive index of about 1.65 to about 1.90. 24. Het glasartikel volgens één der conclusies 20 - 24, waarbij de glasband in staat is om te worden verdeeld in glasschijven die een diktevariatie van ongeveer 0.01 pm tot ongeveer 0.5 pm en deformatie van ongeveer 0.01 pm tot ongeveer 10 pm hebben.The glass article of any one of claims 20 to 24, wherein the glass band is capable of being divided into glass disks having a thickness variation of about 0.01 µm to about 0.5 µm and deformation of about 0.01 µm to about 10 µm. 25. Het glasartikel volgens één der conclusies 20 - 25, waarbij de glasband een diktevariatie van ongeveer 0.01 pm tot ongeveer 50 pm en deformatie van ongeveer 0.01 pm tot ongeveer 200 pm heeft.The glass article of any one of claims 20 to 25, wherein the glass band has a thickness variation of about 0.01 µm to about 50 µm and deformation of about 0.01 µm to about 200 µm. 5 26. Glassamenstelling volgens één der conclusies 20 - 26, waarbij de glasband een samenstelling omvat geselecteerd uit de groep bestaande uit borosilicaat glas, aluminoborosilicaat glas, aluminosilicaat glas, fluorosilicaat glas, phosphosilicaat glas, fluorofosfaat glas, sulfofosfaat glas, germanaat glas, vanadaat glas, fosfaat glas en boraat glas.26. Glass composition according to any of claims 20-26, wherein the glass strip comprises a composition selected from the group consisting of borosilicate glass, aluminoborosilicate glass, aluminosilicate glass, fluorosilicate glass, phosphosilicate glass, fluorophosphate glass, sulfophosphate glass, germanate glass, vanadate glass , phosphate glass and borate glass. 10 27. Glasartikel verkregen volgens de werkwijze volgens één der conclusies 1 - 19.27. Glass article obtained according to the method according to one of claims 1 to 19. 1/31/3 100100 110110 30b v30b v
NL2021322A 2018-06-28 2018-07-17 Continuous methods of making glass ribbon and as-drawn glass articles from the same NL2021322B1 (en)