DE4315339A1

DE4315339A1 - Method of producing basic materials for laser-writable forgery-proof documents

Info

Publication number: DE4315339A1
Application number: DE4315339A
Authority: DE
Inventors: Bert Feron; Lothar Hoels; Ruediger Bohsem
Original assignee: Aluminium Feron GmbH and Co KG
Current assignee: Aluminium Feron GmbH and Co KG
Priority date: 1993-05-08
Filing date: 1993-05-08
Publication date: 1994-11-10

Abstract

A method is described for producing basic materials for laser-writable forgery-proof documents, such as banknotes, securities and identity documents. In this method, at least one plastic film is laminated onto at least one layer of paper. The paper layer is a layer provided with at least one security feature, and the lamination is carried out cold, using a polycarbonate film.

Description

Die vorliegende Erfindung betrifft ein Verfahren zur Herstellung von Basismaterialien für laserbeschriftbare fälschungssichere Dokumente, wie Banknoten, Wertpapiere, Ausweisdokumente, bei dem mindestens eine Kunststoffolie gegen mindestens eine Lage aus Papier kaschiert wird.The present invention relates to a method for producing Base materials for laser-inscribable forgery-proof documents, such as Banknotes, securities, identification documents, in which at least one Plastic film is laminated against at least one layer of paper.

Derartige fälschungssichere Dokumente werden heute in einer Vielzahl von Fällen aus Kunststoff/Papier-Verbunden hergestellt, wobei ein oder mehrere Kunststoffolien gegen eine Papierlage kaschiert werden. Danach werden nach einem speziellen Verfahren mit Hilfe eines Laserstrahles spezielle Informationen auf die Papierlage durch die Kunststoffolie aufgebracht. Solche Informationen können beispielsweise persönliche Daten des Ausweisinhabers, ein Lichtbild des Ausweisinhabers, spezielle Merkmale zur Fälschungssicherung etc. sein. Dieses sogenannte "Personifizieren" des Basismateriales mit Hilfe eines Lasers hat den Vorteil, daß die mit dem Laserstrahl behandelten Stellen sich aufgrund der lokalen Verbrennungen innerhalb des Dokumentes befinden, so daß diese Daten ohne Zerstörung der Papierlage nicht verändert werden können. Such forgery-proof documents are used today in a variety of Cases made of plastic / paper composites, one or several plastic films are laminated against a paper layer. After that are made using a special process using a laser beam special information on the paper layer through the plastic film upset. Such information can, for example, be personal ID card details, photo of ID card holder, special Features to prevent counterfeiting, etc. This so-called "Personalize" the base material with the help of a laser Advantage that the areas treated with the laser beam due to of local burns are within the document so that this data cannot be changed without destroying the paper layer can.

Ein Verfahren mit den Merkmalen des Oberbegriffs des Patentanspruchs 1 ist aus der DE 29 07 004 C2 bekannt. Dieses Verfahren betrifft die Herstellung einer Ausweiskarte, bestehend aus zwei Deckfolien, von denen wenigstens eine transparent ist, und einem Karteninlett aus einem lichtundurchlässigen Material, insbesondere Papier, bei dem Informationen mittels eines gesteuerten Laserstrahls durch die fertig aufkaschierte transparente Deckfolie hindurch auf das Inlett aufgebracht werden. Bei diesem bekannten Verfahren bestehen die Deckfolien aus PVC, und das Karteninlett ist weißes Papier. Die beiden Deckfolien werden unter gleichzeitiger Einwirkung von Druck und Wärme heiß auf das Karteninlett aufkaschiert. Danach werden die entsprechenden Informationen mit Hilfe eines Laserstrahles in die Karte eingebracht.A method with the features of the preamble of claim 1 is known from DE 29 07 004 C2. This procedure concerns the Production of an identity card consisting of two cover foils, one of which at least one is transparent, and a card insert from one opaque material, especially paper, in which Information by means of a controlled laser beam through the finished laminated transparent cover film applied to the ticking become. In this known method, the cover films consist of PVC, and the card inlay is white paper. The two cover films are with simultaneous exposure to pressure and heat hot on the Laminated card card. After that, the appropriate ones Information is inserted into the card using a laser beam.

Das bekannte Verfahren hat den Nachteil, daß sich infolge der Heißkaschierung mit den PVC-Deckfolien durch die damit einhergehende hohe Temperatur thermisch bedingte Veränderungen an der Papierlage ergeben können. Bei diesem Verfahren wird daher als Karteninlet vorzugsweise weißes Papier eingesetzt, was bedeutet, daß sämtliche Informationen durch die nachfolgende Laserbeschriftung in die Karte eingebrannt werden müssen.The known method has the disadvantage that due to the Hot lamination with the PVC cover foils due to the accompanying high temperature thermally induced changes in the paper layer can result. This method is therefore used as a card inlet preferably white paper, which means that all Information from the subsequent laser inscription on the card need to be branded.

Der Erfindung liegt die Aufgabe zugrunde, ein Verfahren der angegebenen Art zu schaffen, mit dem sich Basismaterialien herstellen lassen, die von Hause aus weitgehend fälschungssicher und für die Laserbeschriftung besonders geeignet sind.The invention has for its object a method of the specified To create a way to produce base materials that largely counterfeit-proof by nature and for laser marking are particularly suitable.

Diese Aufgabe wird erfindungsgemäß durch ein Verfahren der angegebenen Art gelöst, das dadurch gekennzeichnet ist, daß als Papierlage eine mit mindestens einem Sicherheitsmerkmal versehene Lage verwendet und die Kaschierung mittels einer Polycarbonatfolie kalt durchgeführt wird.This object is achieved by a method of the specified Kind solved, which is characterized in that as a paper layer with used at least one security feature and the Lamination is carried out cold using a polycarbonate film.

Die Erfindung wendet sich daher von dem Gedanken ab, möglichst viele Informationen, auch solche zur Fälschungssicherung, mit Hilfe einer Laserbeschriftung nachträglich auf das Basismaterial aufzubringen. Statt dessen schlägt die Erfindung die Verwendung eines Sicherheitspapieres vor, d. h. eines Papieres, das von Hause aus mit mindestens einem Sicherheitsmerkmal versehen ist. Es besteht keine Gefahr, daß dieses Sicherheitsmerkmal durch die nachfolgende Kaschierung nachteilig beeinflußt bzw. verändert wird, da die Kaschierung in erfindungsgemäßer Weise kalt erfolgt. Damit kann das Sicherheitspapier beispielsweise von Hause aus mit fälschungssicheren Druckfarben, Wasserzeichen, Hologrammen und ähnlichen Merkmalen versehen sein, ohne daß diese zur Fälschungs sicherung dienenden Merkmale durch die nachfolgende Kaschierung beeinträchtigt bzw. verändert werden.The invention therefore turns away from the idea of as many as possible Information, including counterfeit protection, with the help of a Apply laser marking to the base material later. Instead of the invention proposes the use of a security paper before, d. H. a paper that is made with at least one Security feature is provided. There is no risk of this Security feature disadvantageous by the subsequent lamination is influenced or changed, since the lamination in the invention Way cold. The security paper can thus be used, for example, by At home with forgery-proof printing inks, watermarks, holograms and similar features can be provided without these to counterfeit securing features by the subsequent lamination impaired or changed.

Darüber hinaus wird bei dem erfindungsgemäßen Verfahren mit mindestens einer Polycarbonatfolie kaschiert. Es hat sich gezeigt, daß sich derartige Polycarbonatfolien besonders gut kalt aufkaschieren lassen, andererseits aber auch für die nachfolgende Laserbeschriftung gut geeignet sind. So erfolgt diese Laserbeschriftung in bekannter Weise durch Einbrennen von den entsprechenden Informationen in die Papierlage. Abhängig von der Energiedosierung des Laserstrahls kann jedoch auch die obere Deckfolie mit aufgeschmolzen werden, so daß sich über dem Linienzug der Information ein deckungsgleiches Relief bildet, das zusätzlich manuell abgefühlt werden kann. Falls die Papierlage mit einem geeigneten Stoff beschichtet ist, der in der Lage ist, eine thermochemische Reaktion durchzuführen, kann durch Bestrahlung der Schicht mit dem Laser statt einer Schwärzung bzw. Zerstörung des Inletts auch lediglich ein Farbumschlag erreicht werden. Alle diese Varianten der Laserbeschriftung lassen sich durch die erfindungsgemäße Verwendung von Polycarbonatdeckfolien in besonders vorteilhafter Weise durchführen.In addition, at least covered with a polycarbonate film. It has been shown that laminate such polycarbonate films particularly well, on the other hand also good for the subsequent laser marking are suitable. So this laser marking is done in a known manner by burning the relevant information into the paper layer. Depending on the energy metering of the laser beam, however, the top cover film are melted with, so that over the Line of information forms a congruent relief that can also be manually sensed. If the paper layer with a coated with a suitable substance that is capable of can carry out thermochemical reaction by irradiation of the Layer with the laser instead of blackening or destroying the inlet only a color change can be achieved. All of these variations laser marking can be achieved through the use according to the invention perform polycarbonate cover films in a particularly advantageous manner.

Es kann daher zusammengefaßt werden, daß sich eine erfindungsgemäß ausgebildete Polycarbonatfolie besonders gut auf Papier kaschieren läßt, ohne die Fälschungssicherheitsmerkmale des Papieres zu beeinflussen, und eine gute Laserbeschriftung der Papierlage, beispielsweise in den vorstehend aufgeführten Varianten, zuläßt. Eine solche Polycarbonatfolie weist ferner eine besonders gute Alterungsbeständigkeit auf, da keine Weichmacher entweichen können. Die Erfindung macht sich ferner die hohe Festigkeit, Steifheit und Härte, gute elektrische Isoliereigenschaft, hohe Beständigkeit gegenüber Witterungs- und Strahlungseinflüssen von Polycarbonaten zunutze.It can therefore be summarized that one according to the invention trained polycarbonate film can be laminated particularly well on paper, without affecting the counterfeit security features of the paper, and good laser marking of the paper layer, for example in the the variants listed above. Such a polycarbonate film also has a particularly good resistance to aging, since none Plasticizers can escape. The invention also makes the high Strength, rigidity and hardness, good electrical insulation properties, high resistance to weather and radiation influences from Use polycarbonates.

Von entscheidender Bedeutung für die Erfindung ist es, daß sich mit derartigen transparenten Polycarbonatfolien ohne Einwirkung von erhöhter Temperatur Verbunde mit Papier herstellen lassen, die eine hohe Bindungsfestigkeit besitzen, so daß mögliche Manipulationen an derartigen Dokumenten ausgeschlossen sind bzw. automatisch ein Beschädigen der mit den Informationen versehenen Papierlage zur Folge haben. Diese Möglichkeit der Kaschierung ohne erhöhte Temperaturen bringt den großen Vorteil mit sich, daß als Papierlage sogenannte Sicherheitspapiere bzw. fälschungssichere Papiere eingesetzt werden können, die eine Vielzahl von Merkmalen zur Fälschungssicherung aufweisen können, ohne daß sich beispielsweise eine Veränderung, beispielsweise Verfärbung, der Sicherheitsmerkmale ergibt. Solche Sicherheitsmerkmale können beispielsweise durch spezielle Druckfarben, eine spezielle Art des Drucks oder eine spezielle Papierart realisiert werden. Besonders gut eignet sich das erfindungsgemäße Verfahren für Sicherheitspapiere, die mit bestimmten Spezialdruckfarben versehen sind, um die Dokumente fälschungssicher zu machen, beispielsweise die Herstellmöglichkeit mit Farbkopieren zu vereiteln. Solche Spezialdruck farben sind beispielsweise goniochromatische, photochrome und metamere Druckfarben, auch Druckfarben, die Farbpigmente enthalten, die durch Magnetismus beeinflußt werden können. Hierzu zahlen auch Druckfarb kombinationen, die aus einzelnen Farben bestehen, die durch Farbkopierer nicht oder nur unzureichend reproduziert werden können. Derartige Druckfarben erfahren durch die erfindungsgemäße Kaschierung keine Veränderung, d. h. insbesondere keine Verfärbung.It is of crucial importance for the invention that such transparent polycarbonate films without the effect of increased Let temperature bonds with paper produce a high Have bond strength, so that possible manipulations such documents are excluded or automatically Damage to the paper layer provided with the information to have. This possibility of lamination without elevated temperatures has the great advantage that so-called paper layers Security papers or counterfeit-proof papers are used can have a variety of anti-counterfeiting features can have without, for example, a change, for example discoloration that gives security features. Such Security features can be achieved, for example, through special printing inks, realized a special type of printing or a special type of paper become. The method according to the invention is particularly suitable for Security papers with certain special printing inks to make the documents tamper-proof, for example the To prevent manufacturing with color copying. Such special printing colors are, for example, goniochromatic, photochromic and metameric Printing inks, also printing inks, which contain color pigments, by Magnetism can be influenced. This includes printing inks combinations consisting of individual colors made by color copiers cannot be reproduced or only inadequately. Such Printing inks are not experienced by the lamination according to the invention Change, d. H. especially no discoloration.

Auch spezielle Druckarten, wie Rasterdrucke unterschiedlicher Auflösung, das Eindrucken von Hologrammen, werden durch die nachfolgende Kaschierung nicht beeinflußt. Dies trifft auch auf die verwendeten Spezialpapiere, beispielsweise solche mit Wasserzeichen oder eingelegten Sicherheitsstreifen, zu.Also special types of printing, such as raster prints of different resolutions, The impression of holograms are explained by the following Lamination not affected. This also applies to the ones used Special papers, for example those with watermarks or inlaid Security strip, too.

Es versteht sich, daß die vorstehende Aufzählung von Sicherheitsmerk malen nur beispielhafter Natur ist und die Erfindung nicht auf die angegebenen Merkmale beschränkt ist.It is understood that the above list of security note paint is only exemplary in nature and the invention is not limited to specified features is limited.

Das erfindungsgemäße Verfahren ist ferner nicht auf die Herstellung eines aus einer einzigen Deckfolie und einer Papierlage bestehenden Verbundes beschränkt. Vielmehr kann beidseitig der Papierlage je eine Deckfolie vorgesehen sein, von denen mindestens eine transparent sein sollte. Auch kann ein aus mehreren sandwichartig zusammengesetzten Papierlagen und Kunststoffolien bestehender Verbund hergestellt werden. Wesentlich ist, daß diejenige Seite der Papierlage, die mit dem mindestens einen Sicherheitsmerkmal, beispielsweise einer Bedruckung, versehen ist, mit der Polycarbonatfolie kaschiert wird, wobei auch von dieser Seite durch die Polycarbonatfolie die entsprechende Laserbeschriftung erfolgt. Die andere Seite, d. h. Rückseite, der Papierlage kann mit einer anderen Kunststoffolie kaschiert sein, wobei dies unter Umständen auch über eine Heißkaschierung erfolgen kann, falls hierdurch das entsprechende Sicherheitsmerkmal der Papierlage nicht in Mitleidenschaft gezogen wird. Dies kann beispielsweise dann der Fall sein, wenn die Papierlage nur einseitig mit Sicherheitsmerkmalen versehen ist.The method according to the invention is also not based on the production one consisting of a single cover film and a paper layer Verbund limited. Rather, there can be one on both sides of the paper layer Cover film may be provided, at least one of which should be transparent should. One can also be composed of several sandwiches Paper layers and plastic films of existing composite can be produced. It is essential that the side of the paper layer that with the at least one security feature, for example printing, is provided, is laminated with the polycarbonate film, also from this side through the polycarbonate film Laser inscription is done. The other side, i.e. H. Backside the Paper layer can be laminated with another plastic film, whereby under certain circumstances this can also be done via hot lamination, if thereby the corresponding security feature of the paper layer is not in Is affected. This can be the case, for example be if the paper layer is only one-sided with security features is provided.

Vorzugsweise wird eine Polycarbonatfolie einer Stärke von 40-60 µm gegen die Papierlage kaschiert. Als Papier können handelsübliche Sicherheitspapiere Verwendung finden, aber auch solche Papiere, die vor der Kaschierung in einem besonderen Verfahrensschritt entsprechende Sicherheitsmerkmale aufgeprägt bekommen, beispielsweise entsprechend bedruckt werden. Kombinationen beider Ausführungsformen sind ebenfalls möglich. Die Daten, Informationen und Merkmale, insbesondere Fälschungs sicherheitsmerkmale, können daher von Hause aus auf dem Papier vorhanden sein und/oder in einem gesonderten Verfahrensschritt vor der Kaschierung auf das Papier aufgebracht werden. In jedem Falle erfolgt eine weitere Aufbringung von Informationen, Daten bzw. Merkmalen, insbesondere eine sogenannte Personifizierung bei Ausweisdokumenten, in einem nachfolgenden Laserbeschriftungsschritt.A polycarbonate film with a thickness of 40-60 μm is preferred laminated against the paper layer. Commercially available paper Security papers are used, but also those papers that come before corresponding to the lamination in a special process step Get security features embossed, for example accordingly be printed. Combinations of both embodiments are also possible. The data, information and features, especially counterfeit security features, can therefore be present on paper from home be and / or in a separate process step before lamination be applied to the paper. In any case, there is another Application of information, data or features, in particular a so-called personalization of identification documents, in one subsequent laser marking step.

Die Art dies Papieres richtet sich daher nach dem jeweiligen Verwendungszweck. Als Beispiel kann Papier mit einem Flächengewicht von 70-120 g/m² zur Anwendung gelangen.The type of this paper therefore depends on the respective Usage. As an example, paper with a basis weight of 70-120 g / m² are used.

Wie vorstehend erläutert, wird die Kaschierung der mindestens einen Polycarbonatfolie gegen die Papierlage auf kaltem Wege durchgeführt. Hierzu bietet sich die Verwendung von lösungsmittelfreien Klebern, Zweikomponentenklebern mit Lösungsmittel oder von wäßrigen Dispersions klebern an. Je nach Art des verwendeten Klebers wird dieser entweder nur auf die Polycarbonatfolie oder auf die Folie und die Papierlage aufgetragen. Die Materialien werden dann aufeinandergelegt und in der Regel einer entsprechenden Pressung ausgesetzt. Kommt ein Kleber mit Lösungsmittel zum Einsatz, wird das Lösungsmittel über geeignete Maßnahmen, beispielsweise Lufttrocknung, verdampft. Bei einem solchen lösungsmittelhaltigen Kleber wird nur die Polycarbonatfolie mit dem Kleber versehen, um eine Kontaktierung der mit dem Sicherheitsmerkmal versehenen Papierlage mit dem Lösungsmittel zu verhindern.As explained above, the lamination of the at least one Polycarbonate film against the paper layer carried out cold. The use of solvent-free adhesives Two-component adhesives with solvents or from aqueous dispersions stick on. Depending on the type of glue used, this is either only on the polycarbonate film or on the film and the paper layer applied. The materials are then placed on top of each other and in the Usually exposed to a corresponding pressure. Come with an adhesive If solvent is used, the solvent will be suitable Measures, such as air drying, evaporate. With such a Solvent-based adhesive is only the polycarbonate film with the Adhesive provided to make contact with the security feature to prevent the paper layer provided with the solvent.

Es versteht sich, daß die erfindungsgemäß hergestellten Basismaterialien auch mit Magnetstreifen versehen sein können, die eine entsprechende Datenkodierung tragen. Auch in bezug auf derartige Magnetstreifen wirkt sich die erfindungsgemäß durchgeführte Kaschierung mit der speziell ausgewählten Polycarbonatfolie vorteilhaft aus.It is understood that the base materials produced according to the invention can also be provided with magnetic strips that have a corresponding Wear data encoding. Also acts in relation to such magnetic strips the lamination carried out according to the invention with the special selected polycarbonate film advantageous.

Die Erfindung wird nachfolgend anhand von Ausführungsbeispielen im einzelnen erläutert.The invention is described below using exemplary embodiments in individual explained.

example 1

Eine laserbeschriftbare Polycarbonatfolie der Stärke 50 µm wurde mit einem Zweikomponenten-Polyurethankleber (Handelsprodukt ET 691 der Firma Morton International) beschichtet. Nach dem Abdampfen der Lösungsmittel mittels warmer Luft resultierte ein Auftragsgewicht von ca. 6 g/m² Feststoff. Die mit dem Kleber versehene Seite der Polycarbonatfolie wurde in einer Kaschierpresse gegen ein Wertpapier gepreßt. Der auf diesem Wege erhaltene zweilagige Verbund erhielt nach einer Aushärtezeit von sechs Tagen die gewünschten Festigkeiten. A laser-inscribable polycarbonate film with a thickness of 50 µm was used a two-component polyurethane adhesive (commercial product ET 691 from the company Morton International) coated. After evaporation of the solvents warm air resulted in an application weight of approx. 6 g / m² Solid. The side of the polycarbonate film with the adhesive was pressed against a security in a laminating press. The on Two-layer composite obtained in this way received after a curing time the desired strengths of six days.

Ebenso kann in einem zweiten Arbeitsschritt der so erhaltene zweilagige Verbund sowohl von der Papierseite als auch von der Folienseite gegen eine zweite nach obigem Verfahren mit Kaschierkleber versehene Folie beliebiger Art oder ein weiteres Papier zur Erzielung weiterer gewünschter Eigenschaften kaschiert werden.Likewise, in a second step, the two-ply so obtained Composite both from the paper side and from the film side a second film provided with laminating adhesive using the above procedure any type or another paper to achieve further desired properties are concealed.

Example 2

Eine laserbeschriftbare Polycarbonatfolie der Stärke 50 µm wurde mit einem wäßrigen Dispersionskleber (Handelsprodukt ACRONAL V205 der Firma BASF) derart beschichtet, daß ein Auftragsgewicht von 10-12 g/m² resultierte. Die mit dem Dispersionskleber versehene Seite der Folie wurde in einer Kaschierpresse gegen ein Wertpapier gepreßt. Nach dem Kaschiervorgang wurde der Verbund zwecks Entfernung des Wassers aus dem Dispersionskleber mit Warmluft getrocknet.A laser-inscribable polycarbonate film with a thickness of 50 µm was used an aqueous dispersion adhesive (commercial product ACRONAL V205 from the company BASF) coated such that an application weight of 10-12 g / m² resulted. The side of the film with the dispersion adhesive was pressed against a security in a laminating press. After this Laminating was done to remove the water from the composite Dispersion glue dried with warm air.

Der so erhaltene zweilagige Verbund kann nun ebenso nach den beschriebenen Verfahren in einen drei- oder mehrlagigen Verbund umgewandelt werden.The two-layer composite obtained in this way can now also be used according to the described method in a three or multi-layer composite being transformed.

Claims

1. A method for producing base materials for laser-inscribable tamper-proof documents, such as banknotes, securities, identification documents, in which at least one plastic film is laminated against at least one layer of paper, characterized in that a layer provided with at least one security feature is used and the lamination is carried out in a cold manner using a polycarbonate film.

2. The method according to claim 1, characterized in that a Multi-layer composite made of polycarbonate films and paper layers becomes.

3. The method according to claim 1 or 2, characterized in that a Paper layer is used, its security feature by a special Ink, a special type of printing and / or the use of a special paper is realized.

4. The method according to any one of the preceding claims, characterized characterized in that the base material by means of laser marking is personalized.

5. The method according to any one of the preceding claims, characterized characterized in that a polycarbonate film with a thickness of 40-60 microns is laminated against the paper layer.

6. The method according to any one of the preceding claims, characterized characterized in that the lamination with the help of a solvent-free Glue is carried out.

7. The method according to any one of claims 1 to 5, characterized in that that the lamination is carried out with the help of a two-component adhesive becomes.

8. The method according to any one of claims 1 to 5, characterized in that the lamination with the help of an aqueous dispersion adhesive is carried out.