DE102009007779B3 - A method for producing a visually perceptible without technical aids security feature, security feature for plastic-based value or security document and document with at least one such security feature - Google Patents

A method for producing a visually perceptible without technical aids security feature, security feature for plastic-based value or security document and document with at least one such security feature Download PDF

Info

Publication number
DE102009007779B3
DE102009007779B3 DE102009007779A DE102009007779A DE102009007779B3 DE 102009007779 B3 DE102009007779 B3 DE 102009007779B3 DE 102009007779 A DE102009007779 A DE 102009007779A DE 102009007779 A DE102009007779 A DE 102009007779A DE 102009007779 B3 DE102009007779 B3 DE 102009007779B3
Authority
DE
Germany
Prior art keywords
security feature
lacquer layer
layer
feature according
structuring
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
DE102009007779A
Other languages
German (de)
Other versions
DE102009007779C5 (en
Inventor
Hans-Peter Seijo-Bollin
André Dr. Leopold
Detlef Märtens
Jeffry Gahlbeck
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bundesdruckerei GmbH
Original Assignee
Bundesdruckerei GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=42122788&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=DE102009007779(B3) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by Bundesdruckerei GmbH filed Critical Bundesdruckerei GmbH
Priority to DE102009007779.0A priority Critical patent/DE102009007779C5/en
Priority to PCT/EP2010/000954 priority patent/WO2010089155A1/en
Priority to CN201080004334.6A priority patent/CN102271929B/en
Priority to EP10704330.9A priority patent/EP2393668B1/en
Application granted granted Critical
Publication of DE102009007779B3 publication Critical patent/DE102009007779B3/en
Publication of DE102009007779C5 publication Critical patent/DE102009007779C5/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

Um die Echtheit und/oder Unverfälschtheit eines Wert- oder Sicherheitsdokuments abzusichern, werden ein ohne technische Hilfsmittel visuell wahrnehmbares Sicherheitsmerkmal, ein Wert- oder Sicherheitsdokument mit einem solchen Sicherheitsmerkmal sowie ein Verfahren zur Herstellung eines solchen Sicherheitsmerkmals und eines Wert- oder Sicherheitsdokuments mit einem solchen Sicherheitsmerkmal geschaffen. Das Sicherheitsmerkmal 10 wird durch eine erste Materialschicht 11 und eine erste Lackschicht 12 gebildet, wobei die erste Lackschicht 12 eine Strukturierung aufweist und wobei die erste Lackschicht 12 einen Brechungsindex aufweist, der sich um wenigstens 0,1 vom Brechungsindex der ersten Materialschicht 11 unterscheidet. Das Sicherheitsmerkmal 10 ist aufgrund von Brechung elektromagnetischer Strahlung ohne technische Hilfsmittel visuell wahrnehmbar. Das Verfahren zur Herstellung ist derart, dass das erfindungsgemäße Sicherheitsmerkmal 10 während der Herstellung eines Dokumentes in dieses eingebracht oder anschließend auf eine Oberfläche eines Dokumentenrohlings aufgebracht werden kann.In order to ensure the authenticity and / or authenticity of a security or security document, a security feature which can be visually perceived without technical aids, a value or security document having such a security feature and a method for producing such a security feature and a security document having such a security feature created. The security feature 10 is formed by a first material layer 11 and a first resist layer 12, wherein the first resist layer 12 has a structuring and wherein the first resist layer 12 has a refractive index which differs by at least 0.1 from the refractive index of the first material layer 11. The security feature 10 is visually perceptible due to refraction of electromagnetic radiation without technical aids. The method of production is such that the security feature 10 according to the invention can be introduced into the document during production or can subsequently be applied to a surface of a document blank.

Description

Gebiet der ErfindungField of the invention

Die Erfindung betrifft ein Verfahren zur Herstellung eines ohne technische Hilfsmittel visuell wahrnehmbaren Sicherheitsmerkmals, ein ohne technische Hilfsmittel visuell wahrnehmbares Sicherheitsmerkmal, ein Verfahren zur Herstellung eines Dokumentes mit einem solchen Sicherheitsmerkmal sowie ein Dokument mit einem solchen Sicherheitsmerkmal.The The invention relates to a method for producing a non-technical Aids visually perceptible security feature, one without technical Aid visually perceptible security feature, a procedure for producing a document with such a security feature as well a document with such a security feature.

Stand der TechnikState of the art

Wert- oder Sicherheitsdokumente bestehen häufig aus einem Kunststoffkörper, welcher mittels Fügen, insbesondere mittels Lamination, aus einer Mehrzahl von Kunststoffschichten hergestellt wird. Derartige Wert- oder Sicherheitsdokumente weisen eine hohe Lebensdauer auf und sind aufgrund der komplexeren Herstellungstechniken gegenüber einfachen Papier-basierten Dokumenten besser geschützt. Zur weiteren Absicherung, insbesondere der in ein Wert- oder Sicherheitsdokument eingebrachten personalisierten oder individualisierten Daten, werden Sicherheitsmerkmale in den Dokumentenkörper integriert oder nachträglich auf diesen appliziert. Hierbei ist es besonders bevorzugt, wenn das Sicherheitsmerkmal sich an der gleichen Position befindet wie die personalisierten oder individualisierten Daten, da im Falle einer Manipulation oder eines Austausches der personalisierten oder individualisierten Daten das Sicherheitsmerkmal beschädigt oder zerstört wird und so die Manipulation offensichtlich ist. Unter personalisierten Daten werden hier und im Folgenden personenbezogene Daten, zum Beispiel Name oder Geburtsdatum eines Dokumenteninhabers, und unter individualisierten Daten dokumentspezifische Daten, zum Beispiel eine Seriennummer, verstanden.Value- or security documents often consist of a plastic body, which by means of joining, in particular by lamination, from a plurality of plastic layers will be produced. Such value or security documents have a high durability and are due to the more complex manufacturing techniques across from better protected on simple paper-based documents. to further protection, in particular in a value or security document personalized or individualized data Security features integrated into the body of the document or added later this applied. It is particularly preferred if the Security feature is located in the same position as the personalized or individualized data, as in the case of a Manipulation or exchange of personalized or individualized data the security feature is damaged or destroyed and so the manipulation is obvious. Under personalized Data becomes here and in the following personal data, for example name or date of birth of a document holder, and under individualized Data document-specific data, for example, a serial number understood.

Zur Absicherung von Wert- oder Sicherheitsdokumenten werden oftmals Sicherheitsmerkmale eingesetzt, welche eine vom Blickwinkel abhängige Erscheinung aufweisen. Derartige Sicherheitsmerkmale sind nur schwer und mit handelsüblichen Kopiersystemen nicht nachstellbar. Wichtig ist hierbei, dass bei einfacher Betrachtung des Wert- oder Sicherheitsdokuments ein nicht geschulter Beobachter auch ohne technische Hilfsmittel das Vorhandensein und die Echtheit des Sicherheitsmerkmals feststellen kann. Hierzu werden zum Beispiel optisch variable Farben eingesetzt. Diese sind jedoch nur in einer begrenzten Anzahl an Variationen verfügbar und können insbesondere zur Absicherung über personalisierte oder individualisierte Daten nur sehr begrenzt eingesetzt werden. Deshalb werden sehr oft Beugungsstrukturen in Wert- oder Sicherheitsdokumente eingebracht beziehungsweise nach der Personalisierung von Dokumentenrohlingen nachträglich auf diese aufgebracht. Vorteil holografischer Sicherheitsmerkmale ist die Einbringung komplexer Informationen, zum Beispiel eine komplexe Darstellung, wie Wappen oder Logos.to Securing value or security documents often becomes Security features used, which is dependent on the perspective appearance exhibit. Such security features are difficult and with commercial Copying systems not adjustable. It is important that at simple consideration of the value or security document trained observer also without technical aids the presence and determine the authenticity of the security feature. To do this For example, optically variable colors used. These are however only available in a limited number of variations and can especially for hedging over personalized or individualized data used only very limited become. Therefore, very often diffraction structures in value or Security documents introduced or after personalization of document blanks later applied to this. Advantage of holographic security features is the introduction of complex information, for example a complex one Presentation, such as coats of arms or logos.

Aus der DE10013410A1 ist eine räumliche, beugungsoptisch wirksame Struktur bekannt, welche durch eine mit einer reflexionserhöhenden Beschichtung versehene Oberfläche einer Lack- oder Polymerschicht erzeugt ist. Die Dicke eines solchen Sicherheitselements beträgt insgesamt nur etwa 3 bis 10 μm. Als reflexionserhöhende Beschichtungen können Metalle, aber auch dielektrische Schichten, zum Beispiel TiO2, eingesetzt werden. Die dielektrischen Schichten müssen einen hinreichend vom Lack unterschiedlichen Brechungsindex aufweisen, um reflexionserhöhend zu wirken. Nachteil eines solchen Sicherheitselements liegt darin, dass Strukturen, welche beugungsoptisch wirksam sind, mit einer Präzision unterhalb der Größenordnung der Wellenlänge hergestellt werden müssen, weshalb für den Schritt der Erzeugung der räumlichen, beugungsoptisch wirksamen Schicht entsprechend präzise und aufwendige Verfahren eingesetzt werden müssen. Weiter ist zur Betrachtung beugungsoptisch wirksamer Strukturen eine geeignete Beleuchtung aus einer bestimmten Orientierung notwendig, was das Sicherheitsmerkmal schwerer verifizierbar macht als zum Beispiel eine optisch variable Farbe.From the DE10013410A1 is a spatial, diffractive optical effective structure is known, which is produced by a provided with a reflection-enhancing coating surface of a paint or polymer layer. The thickness of such a security element is only about 3 to 10 microns in total. As reflection-enhancing coatings metals, but also dielectric layers, for example TiO 2 , can be used. The dielectric layers must have a refractive index which is sufficiently different from the lacquer in order to have a reflection-enhancing effect. Disadvantage of such a security element is that structures which are effective diffraction optical, must be made with a precision below the order of the wavelength, which is why for the step of generating the spatial, diffractive optical effective layer must be used according to precise and expensive procedures. Furthermore, suitable illumination from a specific orientation is necessary for viewing diffraction-optically effective structures, which makes the security feature more difficult to verify than, for example, an optically variable color.

Zur Absicherung von Wert- oder Sicherheitsdokumenten werden oftmals Linsenstrukturen eingesetzt, um Kippbild-Effekte zu erzielen. So ist zum Beispiel aus dem deutschen Führerschein ein solches laser-beschriebenes Kippbild bekannt. Vorteil derartiger Strukturen ist die extrem einfache Verifikation, welche keine besonderen Beleuchtungsbedingungen zur Rekonstruktion benötigt. Ferner müssen Linsenstruktur und eingebrachte Information räumlich sehr genau aufeinander abgestimmt sein, sodass eine Manipulation extrem erschwert wird.to Securing value or security documents often becomes Lens structures used to achieve tilt image effects. So is for example from the German driver's license such a laser-described Tilting picture known. Advantage of such structures is the extremely simple Verification, which does not require special lighting conditions Reconstruction needed. Furthermore, must Lens structure and introduced information spatially very precisely be coordinated so that manipulation is extremely difficult.

Aus der WO2008/098753A1 ist ein hochbrechender Prägelack bekannt, welcher zur Erzeugung von mikrooptischen Anordnungen als Sicherheitselement in Wertdokumenten geeignet ist. Der erfindungsgemäße Prägelack weist mindestens eine organische Verbindung auf, welche wenigstens ein polarisierbares Element aufweist, sodass der Brechungsindex größer 1,5 beträgt. Der Brechungsindex des Prägelackes kann durch den Zusatz von Nanopartikeln erhöht sein. Der Prägelack wird zur Herstellung von Sicherheitselementen verwendet, welche in Sicherheitsmerkmalen in Form von Mikrostrukturen ausgestattet werden. Nachteil der mikrooptischen Sicherheitselemente ist die notwendige Präzision der Mikrolinsen und die Einheitlichkeit aller Mikrolinsen eines Sicherheitselementes sowie die extreme Passergenauigkeit zwischen den Mikrolinsen und den von diesen vergrößerten Mikrostrukturen.From the WO2008 / 098753A1 is a high-breaking embossing lacquer is known, which is suitable for the production of micro-optical devices as a security element in value documents. The embossing lacquer according to the invention has at least one organic compound which has at least one polarizable element, so that the refractive index is greater than 1.5. The refractive index of the embossing lacquer may be increased by the addition of nanoparticles. The embossing lacquer is used for the production of security elements, which are equipped in security features in the form of microstructures. Disadvantage of the micro-optical security elements is the necessary precision of the microlenses and the uniformity of all microlenses of a security element and the extreme registration accuracy between the microlenses and the from these enlarged microstructures.

Aus der DE3231460A1 ist eine Ausweiskarte bekannt, welche aus mehreren Kunststoffschichten aufgebaut ist, wobei wenigstens zwei aneinandergrenzende Kunststoffschichten eine unter schiedliche Transparenz aufweisen und wenigstens eine dieser Schichten Vertiefungen aufweist, welche vom Material der angrenzenden Schicht wenigstens teilweise ausgefüllt werden. Die Dicken der unterschiedlich transparenten Schichten variieren, sodass sich im Auflicht ein Licht-Schatten-Effekt ergibt, der sich im Durchlicht umkehrt. Die verformende Schicht kann mit einem Aufdruck versehen sein, der sich in Abhägigkeit von den Vertiefungen plastisch verformt, wodurch ein räumlicher Eindruck des Druckbildes erhalten werden kann. Ferner kann die Ausweiskarte an den Stellen der Vertiefungen durch diese ein Oberflächenrelief aufweisen, sodass das Muster als Oberflächenrelief fühlbar ist. Nachteilig ist bei dem hier beschriebenen Verfahren zur Herstellung einer Ausweiskarte, dass das Merkmal ausschließlich zum Zeitpunkt der Herstellung des Kartenkörpers der Ausweiskarte eingebracht werden kann. Eine spätere Einbringung, zum Beispiel nach Einbringung personalisierter Daten zu deren Schutz, oder eine Einbringung personalisierter oder individualisierter Daten ist nicht möglich. Außerdem ist das so erzeugte Merkmal totalreflektierend, stark glänzend oder matt, weshalb es nicht über anderen Sicherheitsmerkmalen oder Daten angebracht werden kann.From the DE3231460A1 An ID card is known, which is composed of a plurality of plastic layers, wherein at least two adjoining plastic layers have a different transparency under and at least one of these layers has depressions, which are at least partially filled by the material of the adjacent layer. The thicknesses of the different transparent layers vary, so that in reflected light a light-shadow effect results, which is reversed in transmitted light. The deforming layer may be provided with a print that plastically deforms in dependence on the depressions, whereby a spatial impression of the printed image can be obtained. Furthermore, the identification card can have a surface relief at the locations of the depressions through them, so that the pattern can be felt as a surface relief. A disadvantage of the method described here for producing a badge that the feature can be introduced only at the time of manufacture of the card body of the badge. A later contribution, for example, after the introduction of personalized data to protect them, or a contribution of personalized or individualized data is not possible. In addition, the feature thus created is totally reflective, highly glossy or dull, so it can not be mounted over other security features or data.

Aus der DE 10 2004 016 596 A1 ist ein Sicherheitselement in Form eines mehrschichtigen Folienkörpers bekannt. Der Folienkörper weist eine Replizierlackschicht und eine Dünnfilmschicht zum Erzeugen eines blickwinkelabhängigen Farbverschiebungseffekts mittels Interferenz auf. Die Grenzfläche zwischen der Replizierlackschicht und dem Dünnschichtfilm weist einen ersten Bereich auf, in welchem eine erste Reliefstruktur zur Unterdrückung der Erzeugung eines Farbverschiebungseffekts abgeformt ist. Hierdurch wird die Herstellung von Sicherheitselementen verbilligt, bei denen der von der Dünnfilmschicht erzeugte Farbverschiebungseffekt nicht vollflächig, sondern lediglich in einem Musterbereich vorgesehen sein soll. Weiter sind hierdurch sehr hohe Auflösungen erzielbar.From the DE 10 2004 016 596 A1 is a security element in the form of a multilayer film body known. The film body has a replication lacquer layer and a thin film layer for generating a viewing angle-dependent color shift effect by means of interference. The interface between the replication lacquer layer and the thin film has a first region in which a first relief structure for suppressing the generation of a color shift effect is formed. As a result, the production of security elements is cheapened, in which the color shift effect generated by the thin-film layer is not intended to be provided over the entire surface but only in a pattern region. Furthermore, very high resolutions can be achieved hereby.

Aus der DE 10 2006 032 660 A1 ist ein Mehrschichtkörper mit Mikrooptik bekannt. Die Mikrooptischen Strukturen werden mittels Intagliodruck aufgebracht. Bei dem Mehrschichtkörper kann es sich um eine Transferfolie, ein Sicherheitsdokument oder ein Sicherheitsdokument mit Transferfolie handeln. Vorteil des Verfahrens ist es, dass der Aufwand für die registergenaue Ausrichtung nur der Druckplatten zueinander besteht und der Mehrschichtkörper danach in hohen Stückzahlen vervielfältigt werden kann.From the DE 10 2006 032 660 A1 is a multi-layer body with micro-optics known. The micro-optical structures are applied by intaglio printing. The multilayer body can be a transfer film, a security document or a security document with a transfer film. Advantage of the method is that the cost of register-accurate alignment of only the printing plates to each other and the multi-layer body can then be duplicated in large quantities.

Problem nach dem Stand der Technik und Aufgabe der ErfindungProblem according to the state of Technology and object of the invention

Sicherheitsmerkmale der oben beschriebenen Art können nicht mit einfachen Mitteln an einer beliebigen Stelle des Herstellungs- und/oder Personalisierungsprozesses eingesetzt werden, um Wert- oder Sicherheitsdokumente, insbesondere die in diese Dokumente eingebrachten personalisierten oder individualisierten Informationen, gegen Fälschung und Verfälschung abzusichern.security features of the type described above not with simple means anywhere in the manufacturing and / or personalization process are used to value or Security documents, in particular those incorporated in these documents personalized or individualized information, against counterfeiting and adulteration secure.

Es stellt sich somit die Aufgabe, ein Sicherheitsmerkmal zu schaffen, welches einfach einzubringen und ohne Hilfsmittel mit dem bloßen Auge und unter beliebigen Beleuchtungsverhältnissen leicht verifiziert werden kann. Dieses Sicherheitsmerkmal soll an beliebiger Stelle im Herstellungs- und/oder Personalisierungsverfahren des Wert- oder Sicherheitsdokumentes auf einfache und kostengünstige Weise in das Dokument eingebracht werden können, insbesondere zum Schutz von personalisierten oder individualisierten Informationen.It Thus, the task is to create a security feature, which is easy to apply and without aids to the naked eye and easily verified under any lighting conditions can be. This security feature should be at any point in the manufacturing and / or personalization process of the value or security document on simple and inexpensive Can be incorporated into the document, in particular for protection of personalized or individualized information.

Beschreibung der Erfindung und bevorzugte AusführungsformenDescription of the invention and preferred embodiments

Erfindungsgemäß wird die Aufgabe gelöst, indem ein Sicherheitsmerkmal geschaffen wird, welches ohne technische Hilfsmittel visuell wahrnehmbar ist. Das erfindungsgemäße Sicherheitsmerkmal wird aus wenigstens zwei Materialschichten gebildet, wobei die zweite Materialschicht eine erste Lackschicht ist. Diese erste Lackschicht bedeckt die erste Materialschicht zumindest in Teilbereichen. Diese Bedeckung kann sich vollflächig über die erste Materialschicht, über einen Teilbereich der ersten Materialschicht oder über wenigstens zwei voneinander getrennte Teilbereiche der ersten Materialschicht erstrecken. Bei der Bedeckung kann es sich zum Beispiel auch um ein Punktmuster handeln. Die erste Lackschicht weist gegenüber der ersten Materialschicht einen Brechungsindexunterschied von wenigstens 0,1 auf. Die erste Lackschicht weist eine Strukturierung auf beziehungsweise stellt eine Strukturierung dar. Erstreckt die erste Lackschicht sich vollflächig über die erste Materialschicht, so ist die Strukturierung der ersten Lackschicht durch eine Variation der Dicke der Lackschicht gegeben. Erstreckt sich die erste Lackschicht über eine Mehrzahl an Teilbereichen der ersten Materialschicht, so stellt die räumliche Anordnung der Lackschicht eine Strukturierung dar. Die Strukturierung ist dergestalt, dass elektromagnetische Strahlung, welche von der ersten Materialschicht in die erste Lackschicht übergeht, gebrochen wird. Die Strukturierung weist erfindungsgemäß eine Strukturgröße parallel zur Oberfläche (zur Hauptebene der ersten Materialschicht) von wenigstens 10 μm auf. Ist die Strukturierung durch ein Punktmuster gegeben, so beträgt die Punktgröße wenigstens 10 μm, wobei hier unter einem Punkt ein zusammenhängender, zweidimensional abgeschlossener Teilbereich der ersten Lackschicht verstanden wird. Ist die Strukturierung durch eine Variation der Dicke der ersten Lackschicht gegeben, so weisen Bereiche mit annähernd gleicher Dicke eine laterale Ausdehnung von wenigstens 10 μm auf. Die Strukturierung weist weiter erfindungsgemäß eine Strukturgröße senkrecht zur Oberfläche von wenigstens 5 μm, bevorzugt zwischen 5 μm und 10 μm, auf. Ist die Strukturierung durch ein Punktmuster gegeben, so beträgt die Punkthöhe wenigstens 5 μm, bevorzugt zwischen 5 μm und 10 μm. Ist die Strukturierung durch eine Variation der Dicke der ersten Lackschicht gegeben, so weisen Bereiche mit unterschiedlicher Dicke einen Unterschied der Dicke von wenigstens 5 μm, bevorzugt zwischen 5 μm und 10 μm, auf.According to the invention the object is achieved by a security feature is created, which is visually perceptible without technical aids. The security feature according to the invention is formed from at least two material layers, wherein the second material layer is a first lacquer layer. This first lacquer layer covers the first material layer at least in partial areas. This covering may extend over the entire surface over the first material layer, over a partial region of the first material layer or over at least two separate partial regions of the first material layer. The coverage may also be a dot pattern, for example. The first lacquer layer has a refractive index difference of at least 0.1 relative to the first material layer. The first lacquer layer has a structuring or represents a structuring. If the first lacquer layer extends over the entire surface over the first material layer, then the structuring of the first lacquer layer is given by a variation of the thickness of the lacquer layer. If the first lacquer layer extends over a plurality of partial regions of the first material layer, then the spatial arrangement of the lacquer layer forms a structuring. The structuring is such that electromagnetic radiation which passes from the first material layer into the first lacquer layer is refracted. The structuring according to the invention has a structure size parallel to the surface (to the main plane of the first material layer) of at least 10 .mu.m. If the structuring is given by a dot pattern, the point size is at least 10 microns, which is understood here by a point, a contiguous, two-dimensionally completed portion of the first lacquer layer. If the structuring is given by a variation of the thickness of the first lacquer layer, then regions with approximately the same thickness have a lateral extent of at least 10 μm. The structuring furthermore has, according to the invention, a structure size perpendicular to the surface of at least 5 μm, preferably between 5 μm and 10 μm. If the structuring is given by a dot pattern, then the dot height is at least 5 μm, preferably between 5 μm and 10 μm. If the structuring is given by a variation of the thickness of the first lacquer layer, regions with different thicknesses have a thickness difference of at least 5 μm, preferably between 5 μm and 10 μm.

Die Vorteile des erfindungsgemäßen Sicherheitsmerkmals ergeben sich aus der einfachen Herstellung sowie der einfachen Verifikation. Da das erfindungsgemäße Sicherheitsmerkmal aufgrund von Brechung elektromagnetischer Strahlung visuell wahrnehmbar ist, sind keine besonderen Beleuchtungsbedingungen zu dessen Beobachtung notwendig, wie diese zum Beispiel bei der Beobachtung von Hologrammen, welche aufgrund von Beugung elektromagnetischer Strahlung visuell wahrnehmbar sind, notwendig sind. Die Herstellung eines erfindungsgemäßen Sicherheitsmerkmals ist einfacher und flexibler als die der oben genannten Sicherheitsmerkmale, da weder die hohe Präzision, welche für eine Beugungsstruktur benötigt wird, noch die relative Positioniergenauigkeit, welche für Mikrolinsensysteme benötigt wird, notwendig ist. Durch die Herstellung des Sicherheitsmerkmals durch das Aufbringen einer Lackschicht ist eine Integration des erfindungsgemäßen Sicherheitsmerkmals sowohl in eine Innenlage eines Dokumentes bei der Herstellung als auch auf die Oberfläche eines fertigen Dokumentenrohlings, insbesondere zur Absicherung von Personalisierungsdaten, möglich.The Advantages of the security feature according to the invention result from the simple production as well as the simple verification. As the security feature of the invention visually perceptible due to refraction of electromagnetic radiation are no special lighting conditions for its observation necessary, as for example in the observation of holograms, which visually due to diffraction of electromagnetic radiation are perceptible, necessary. The production of a security feature according to the invention is simpler and more flexible than the security features mentioned above, because neither the high precision, which one for one Diffraction structure needed is still the relative positioning accuracy, which for micro lens systems needed is necessary. By making the security feature by applying a lacquer layer is an integration of inventive security feature both in an inner layer of a document in the production as also on the surface a finished document blank, especially for hedging of personalization data, possible.

In einer bevorzugten Ausführungsform der Erfindung weist das Sicherheitsmerkmal eine Strukturierung parallel zur Oberfläche mit einer Strukturgröße von wenigstens 100 μm auf.In a preferred embodiment According to the invention, the security feature has a structuring in parallel to the surface with a feature size of at least 100 μm.

In einer bevorzugten Ausführungsform der Erfindung weist das Sicherheitsmerkmal eine Strukturierung parallel zur Oberfläche mit einer Strukturgröße von wenigstens 1 mm auf.In a preferred embodiment According to the invention, the security feature has a structuring in parallel to the surface with a feature size of at least 1 mm up.

In einer bevorzugten Ausführungsform der Erfindung weist das Sicherheitsmerkmal zusätzlich eine zweite Lackschicht auf, welche über der ersten Lackschicht angeordnet ist. Vorteil dieser Ausführungsform ist der Schutz der Strukturierung der ersten Lackschicht gegenüber mechanischer Belastung, insbesondere Schutz vor Abrieb. Die zweite Lackschicht kann einen Brechungsindexunterschied von mindestens 0,1 gegenüber der ersten Lackschicht aufweisen. Besonders bevorzugt weist die zweite Lackschicht den gleichen oder einen ähnlichen Brechungsindex wie die erste Materialschicht auf. Unter ähnlich wird ein Brechungsindexunterschied von kleiner 0,02 betrachtet. Die Strukturierung der ersten Lackschicht senkrecht zur Oberfläche des Sicherheitsmerkmals wird von der zweiten Lackschicht wenigstens teilweise, bevorzugt vollständig, ausgeglichen, sodass das Sicherheitsmerkmal kaum, bevorzugt nicht, fühlbar ist.In a preferred embodiment According to the invention, the security feature additionally has a second lacquer layer on which over the first lacquer layer is arranged. Advantage of this embodiment is the protection of the structuring of the first lacquer layer compared to mechanical Load, in particular protection against abrasion. The second coat of paint can have a refractive index difference of at least 0.1 over the first paint layer. Particularly preferably, the second lacquer layer the same or a similar one Refractive index as the first material layer. Under becomes similar considered a refractive index difference of less than 0.02. The structuring the first lacquer layer perpendicular to the surface of the security feature is at least partially preferred by the second lacquer layer Completely, balanced so that the security feature is hardly, preferably not, palpable is.

In einer bevorzugten Ausführungsform des Sicherheitsmerkmals weist die zweite Lackschicht eine Schichtdicke auf, welche geringer ist als die Strukturgröße der ersten Lackschicht. Hierdurch bleibt die Strukturierung der ersten Lackschicht des Sicherheitsmerkmals fühlbar. Diese Ausführungsform ist bevorzugt, wenn bereits eine solch dünne zweite Lackschicht die Gebrauchseigenschaften des Sicherheitsmerkmals deutlich verbessert, insbesondere die Abriebfestigkeit.In a preferred embodiment of the security feature, the second lacquer layer has a layer thickness which is smaller than the structure size of the first lacquer layer. This leaves the structuring of the first lacquer layer of the security feature palpable. This embodiment is preferred if even such a thin second lacquer layer the Performance characteristics of the security feature significantly improved, in particular the abrasion resistance.

In einer bevorzugten Ausführungsform des Sicherheitsmerkmals weist die zweite Lackschicht abriebfeste Eigenschaften auf. Bevorzugt werden die abriebfesten Eigenschaften durch den Zusatz von ZnO und/oder SiO2 erzeugt.In a preferred embodiment of the security feature, the second lacquer layer has abrasion-resistant properties. The abrasion-resistant properties are preferably produced by the addition of ZnO and / or SiO 2 .

In einer bevorzugten Ausführungsform des Sicherheitsmerkmals sind die erste Materialschicht und die erste Lackschicht transparent.In a preferred embodiment of the security feature are the first layer of material and the first Lacquer layer transparent.

In einer bevorzugten Ausführungsform des Sicherheitsmerkmals sind die erste Materialschicht sowie die erste und die zweite Lackschicht transparent.In a preferred embodiment of the security feature are the first layer of material and the first and second paint layer transparent.

In einer alternativen bevorzugten Ausführungsform des Sicherheitsmerkmals ist die erste Lackschicht transluzent und die zweite Lackschicht transparent.In an alternative preferred embodiment of the security feature the first lacquer layer is translucent and the second lacquer layer is transparent.

In einer alternativen bevorzugten Ausführungsform des Sicherheitsmerkmals ist die erste Materialschicht opak oder transluzent, die erste Lackschicht und die zweite Lackschicht sind transparent.In an alternative preferred embodiment of the security feature the first layer of material is opaque or translucent, the first layer of lacquer and the second lacquer layer are transparent.

In einer bevorzugten Ausführungsform des Sicherheitsmerkmals ist der Brechungsindex der ersten Lackschicht durch den Zusatz mindestens eines hochbrechenden Zusatzstoffes um wenigstens 0,1 höher als der Brechungsindex der ersten Materialschicht eingestellt. Mindestens einer der hochbrechenden Zusatzstoffe ist ausgewählt aus der Gruppe umfassend Glas, Feldspat, TiO2, ZrO2 und Diamant. Bevorzugt liegt ein hochbrechender Zusatzstoff nanokristallin vor, also mit einer Partikelgröße kleiner 100 nm, besonders bevorzugt mit einer Partikelgröße kleiner 25 nm.In a preferred embodiment of the security feature, the refractive index of the first lacquer layer is adjusted by the addition of at least one high-index additive by at least 0.1 higher than the refractive index of the first material layer. At least one of the high refractive index additives is selected from the group comprising glass, feldspar, TiO 2 , ZrO 2 and diamond. A high-index additive is preferably nanocrystalline, that is to say having a particle size of less than 100 nm, particularly preferably having a particle size less than 25 nm.

In einer bevorzugten Ausführungsform des Sicherheitsmerkmals besteht die erste Materialschicht aus einem Material ausgewählt aus der Gruppe, umfassend Polycarbonat (PC), Polyethylenterephthalat (PET) sowie dessen Derivaten, Polyvinylchlorid (PVC), Polypropylen (PP), Polyethylen (PE), thermoplastischen Elastomeren (TPE), Papier und Glas sowie Mischungen dieser Materialien. Die erste Materialschicht kann eine Dicke von mindestens 50 μm aufweisen.In a preferred embodiment of the security feature, the first material layer consists of a Material selected from the group comprising polycarbonate (PC), polyethylene terephthalate (PET) and its derivatives, polyvinyl chloride (PVC), polypropylene (PP), polyethylene (PE), thermoplastic elastomers (TPE), paper and glass and mixtures of these materials. The first material layer may have a thickness of at least 50 microns.

In einer bevorzugten Ausführungsform des Sicherheitsmerkmals ist die erste Materialschicht ein Dokumentenrohling. Bei einem Dokumentenrohling kann es sich um einen Mehrschichtverbund handeln, zum Beispiel ein Mehrschichtlaminat, in welchem Schichten identischer oder verschiedener Materialien vorhanden sein können. Wenn es sich um einen Dokumentenrohling aus verschiedenen Materialien handelt, wird als Brechungsindex der ersten Materialschicht der Brechungsindex einer obersten transparenten Schicht angesehen. Bei der obersten transparenten Schicht kann es sich um eine Lackschicht handeln.In a preferred embodiment of the security feature, the first material layer is a document blank. A document blank may be a multi-layer composite act, for example, a multi-layer laminate, in which layers identical or different materials may be present. If It is a document blank made of different materials is the refractive index of the first material layer of the Refractive index of an uppermost transparent layer considered. at the uppermost transparent layer may be a lacquer layer.

In einer bevorzugten Ausführungsform des Sicherheitsmerkmals enthält wenigstens die erste Lackschicht wenigstens einen zur Lumineszenz anregbaren Stoff.In a preferred embodiment of the security feature at least the first lacquer layer at least one for luminescence stimulable substance.

Ein erfindungsgemäßes Dokument weist wenigstens ein ohne technische Hilfsmittel visuell wahrnehmbares Sicherheitsmerkmal gemäß der vorliegenden Erfindung auf. Des Weiteren kann das Dokument über ein oder mehrere weitere Sicherheitsmerkmale verfügen. Beispielsweise seien genannt Guillochendruck, Irisdruck, optisch variable Farbe, Lasergravur, Lumineszenzfarbe, Hologramm, elektronische Bauteile, zum Beispiel RF-Chip und/oder Display, sowie metamere Farben. Bei dem Dokument kann es sich um ein Wert- oder Sicherheitsdokument, einen Reisepass, einen Personalausweis, eine Geburtsurkunde, ein Visum, einen Führerschein, eine Kreditkarte, eine Bankkarte, einen Firmenausweis, einen Mitgliedausweis, einen Fahrzeugschein, eine Banknote, einen Scheck, eine Aktie, eine Briefmarke oder ein Steuerzeichen handeln. Das Dokument kann aus Polycarbonat (PC), Polyethylenterephthalat (PET) sowie dessen Derivaten, Polyvinylchlorid (PVC), Polypropylen (PP), Polyethylen (PE), thermoplastischen Elastomeren (TPE), Papier sowie aus Mischungen dieser Materialien aufgebaut sein.One document according to the invention has at least one without technical aids visually perceptible Security feature according to the present Invention on. Furthermore, the document may have one or more additional ones Have security features. For example, may be called Guillochendruck, iris, optically variable color, laser engraving, luminescent color, hologram, electronic Components, for example RF chip and / or display, as well as metamere Colours. The document may be a value or security document, a Passport, identity card, birth certificate, visa, a driver's license, a credit card, a bank card, a company card, a membership card, a Vehicle registration certificate, a banknote, a check, a share, a stamp or to act a control character. The document can be made of polycarbonate (PC), Polyethylene terephthalate (PET) and its derivatives, polyvinyl chloride (PVC), Polypropylene (PP), polyethylene (PE), thermoplastic elastomers (TPE), paper and mixtures of these materials be.

In einer bevorzugten Ausführungsform des erfindungsgemäßen Dokumentes ist das ohne technische Hilfsmittel visuell wahrnehmbare Sicherheitsmerkmal auf der Oberfläche des Dokumentes angeordnet. Insbesondere wird das Sicherheitsmerkmal auf einen Dokumentenrohling, bevorzugt nach der Personalisierung, aufgebracht. Um das Sicherheitsmerkmal zum Beispiel gegenüber Abrieb zu schützen, kann über dem Sicherheitsmerkmal eine weitere Materialschicht angeordnet sein. Die weitere Materialschicht kann eine Folie aus einem Fotopolymer, in welches ein Volumenhologramm einbelichtet ist oder werden kann, oder eine Abriebschutzfolie sein.In a preferred embodiment of the document according to the invention is the visually perceptible security feature without technical aids on the surface of the document. In particular, the security feature is on a document blank, preferably after personalization applied. To protect the security feature against abrasion, for example, may be above the Security feature another material layer may be arranged. The further material layer may be a film of a photopolymer, in which a volume hologram is or can be imprinted, or an abrasion protection film.

In einer weiteren bevorzugten Ausführungsform des erfindungsgemäßen Dokumentes ist das ohne technische Hilfsmittel visuell wahrnehmbare Sicherheitsmerkmal im Inneren des Dokumentes angeordnet. Zur Einbringung kann das Sicherheitsmerkmal auf eine Schicht, zum Beispiel eine Folie, aufgebracht sein, welche mit weiteren Schichten, zum Beispiel mittels Lamination zu einem Dokument verbunden werden. Der Vorteil dieser Ausführungsform ist dadurch gegeben, dass durch das Sicherheitsmerkmal in das Dokument eingebrachte Informationen, zum Beispiel mittels Laserpersonalisierung eingebrachte Personalisierungsdaten, abgesichert werden können, wenn zum Beispiel das Sicherheitsmerkmal zwischen zwei laserfähige Folien eingebracht wird.In a further preferred embodiment of the document according to the invention is the visually perceptible security feature without technical aids arranged inside the document. For incorporation, the security feature be applied to a layer, for example a film, which with further layers, for example by means of lamination to one Document. The advantage of this embodiment is given by the fact that by the security feature in the document introduced information, for example by means of laser personalization introduced personalization data, can be hedged, if for example, the security feature between two laserable films is introduced.

Das erfindungsgemäße Verfahren zur Herstellung eines ohne technische Hilfsmittel visuell wahrnehmbaren Sicherheitsmerkmals umfasst folgende Schritte:

  • a) Bereitstellen einer ersten Materialschicht
  • b) Aufbringen einer durch eine erste Lackschicht gebildeten zweiten Materialschicht zumindest in Teilbereichen der ersten Materialschicht, wobei die erste Lackschicht einen Brechungsindex aufweist, der sich vom Brechungsindex der ersten Materialschicht um wenigstens 0,1 unterscheidet, sowie
  • c) Erzeugen einer Strukturierung der ersten Lackschicht, wobei die Strukturierung eine Strukturgröße parallel zur Oberfläche des Sicherheitsmerkmals von wenigstens 10 μm und senkrecht zur Oberfläche des Sicherheitsmerkmals von wenigstens 5 μm aufweist und
wobei das so hergestellte Sicherheitsmerkmal aufgrund von Brechung elektromagnetischer Strahlung visuell wahrnehmbar ist.The method according to the invention for producing a security feature which can be visually perceived without technical aids comprises the following steps:
  • a) providing a first material layer
  • b) applying a second material layer formed by a first lacquer layer at least in partial regions of the first material layer, wherein the first lacquer layer has a refractive index which differs from the refractive index of the first material layer by at least 0.1, and
  • c) generating a structuring of the first lacquer layer, wherein the structuring has a feature size parallel to the surface of the security feature of at least 10 microns and perpendicular to the surface of the security feature of at least 5 microns, and
wherein the security feature so produced is visually perceptible due to refraction of electromagnetic radiation.

Bei der ersten Materialschicht kann es sich zum Beispiel um eine Kunststofffolie mit einer Dicke zwischen 25 μm und 300 μm aus Polycarbonat (PC), Polyethylenterephthalat (PET) sowie dessen Derivaten, Polyvinylchlorid (PVC), Polypropylen (PP), Polyethylen (PE), thermoplastischen Elastomeren (TPE), Papier sowie aus Mischungen dieser Materialien oder um einen Dokumentenrohling handeln.at the first material layer may be, for example, a plastic film with a thickness between 25 microns and 300 μm Polycarbonate (PC), polyethylene terephthalate (PET) and its Derivatives, polyvinyl chloride (PVC), polypropylene (PP), polyethylene (PE), thermoplastic elastomers (TPE), paper and mixtures of these materials or to act on a document blank.

Im Verfahrensschritt b) wird ein Lack auf die erste Materialschicht aufgebracht. Durch Aushärtung des Lackes entsteht die erste Lackschicht, welche einen Brechungsindexunterschied von wenigstens 0,1 gegenüber der ersten Materialschicht aufweist.In method step b), a lacquer is applied to the first material layer. By curing the paint creates the first coat of paint, which egg a refractive index difference of at least 0.1 relative to the first material layer.

Im Verfahrensschritt c) wird eine Strukturierung der ersten Lackschicht erzeugt, welche eine Strukturgröße parallel zur Oberfläche des Sicherheitsmerkmals von wenigstens 10 μm und senkrecht zur Oberfläche des Sicherheitsmerkmals von wenigstens 5 μm aufweist. Diese Strukturierung kann dadurch erfolgen, dass die Aufbringung des Lackes im Verfahrensschritt b) strukturiert erfolgt, dass der Lack im Verfahrensschritt b) unstrukturiert aufgebracht wird und in einem nachfolgenden Schritt strukturiert wird, oder dass die erste Materialschicht in einem zwischen den Verfahrensschritten a) und b) liegenden weiteren Verfahrensschritt strukturiert wird, sodass die erste Lackschicht bei der Aufbringung die Strukturierung der ersten Materialschicht annimmt.in the Process step c) is a structuring of the first lacquer layer generates which one structure size parallel to the surface the security feature of at least 10 microns and perpendicular to the surface of the Security feature of at least 5 microns. This structuring can be done by applying the paint in the process step b) structured, that the paint in process step b) unstructured is applied and structured in a subsequent step is, or that the first material layer in one between the Process steps a) and b) lying further process step is structured so that the first coat of paint in the application takes the structuring of the first material layer.

In einer bevorzugten Ausführungsform des Verfahrens zur Herstellung des erfindungsgemäßen Sicherheitsmerkmals erfolgt die Aufbringung der ersten Lackschicht im Verfahrensschritt b) drucktechnisch im Hoch-, Flach-, Tief-, Durch- oder Digitaldruck auf die erste Materialschicht.In a preferred embodiment the process for producing the security feature according to the invention takes place the application of the first lacquer layer in process step b) by printing technology in high, flat, gravure, through or digital printing on the first Material layer.

In einer weiteren bevorzugten Ausführungsform des erfindungsgemäßen Verfahrens zur Herstellung des Sicherheitsmerkmals erfolgt die Aufbringung der ersten Lackschicht im Verfahrensschritt b) mittels Verguss, Sprühbeschichtung oder Walzenbeschichtung auf die erste Materialschicht.In a further preferred embodiment the method according to the invention for the production of the security feature, the application takes place the first lacquer layer in process step b) by means of encapsulation, spray or roll coating on the first layer of material.

In einer weiteren bevorzugten Ausführungsform des Verfahrens zur Herstellung des Sicherheitsmerkmals erfolgt die drucktechnische Aufbringung der ersten Lackschicht unter gleichzeitiger Erzeugung der Strukturierung gemäß Verfahrensschritt c). Insbesondere geeignet für die Herstellung von Linienmustern ist der Stichtiefdruck. Insbesondere geeignet für die Herstellung individualisierter Strukturierung ist der Tintenstrahldruck.In a further preferred embodiment the method for producing the security feature is carried out the technical printing application of the first lacquer layer with simultaneous Generation of structuring according to method step c). Especially suitable for the production of line patterns is intaglio printing. Especially suitable for the production of individualized texturing is inkjet printing.

In einer weiteren bevorzugten Ausführungsform des Verfahrens zur Herstellung des Sicherheitsmerkmals wird die im Verfahrensschritt a) bereitgestellte erste Materialschicht zunächst mittels Umformen strukturiert. Als Verfahren zur Umformung kommen insbesondere alle Verfahren des Prägens und/oder der Ultraschall-Behandlung der ersten Materialschicht in Frage. Anschließend wird im Verfahrensschritt b) die erste Lackschicht aufgetragen, welche durch die Strukturierung der ersten Materialschicht gemäß Verfahrensschritt c) strukturiert wird.In a further preferred embodiment of the method for producing the security feature is the in method step a) first provided by means of material Forming structured. As a method of forming in particular all methods of embossing and / or the ultrasound treatment of the first material layer in question. Subsequently in step b), the first lacquer layer is applied, which by the structuring of the first material layer according to method step c) is structured.

In einer weiteren bevorzugten Ausführungsform des Verfahrens zur Herstellung des Sicherheitsmerkmals kann die erste Lackschicht im Verfahrensschritt b) zunächst unstrukturiert aufgetragen werden. In einem anschließenden Verfahrensschritt c) wird die erste Lackschicht mittels fotolithografischer Techniken strukturiert. Hierbei kann in einer ersten Ausführungsform ein Lack aufgetragen werden, welcher mittels UV-Licht gehärtet wird. Die Härtung kann mittels gezielter Belichtung mit UV-Licht erfolgen. Anschließend wird der nicht gehärtete Lack entfernt, zum Beispiel mit einem Lösemittel abgewaschen. In einer zweiten Ausführungsform wird zunächst ein Lack aufgetragen und gehärtet. Die entstehende Lackschicht wird belichtet, sodass der Lack sich an den belichteten Stellen zersetzt und abgewaschen werden kann.In a further preferred embodiment of the method for producing the security feature, the first paint layer in step b) initially applied unstructured become. In a subsequent Process step c) becomes the first lacquer layer by means of photolithographic techniques structured. In this case, a lacquer can be applied in a first embodiment which is cured by means of UV light. The curing can by means of targeted exposure to UV light. Subsequently, will the unhardened Paint removed, for example, washed off with a solvent. In a second embodiment will be first applied a paint and cured. The resulting paint layer is exposed, so that the paint itself can be decomposed and washed off at the exposed areas.

In einer weiteren bevorzugten Ausführungsform des Verfahrens zur Herstellung des Sicherheitsmerkmals wird die erste Lackschicht während des Verfahrensschrittes c) gehärtet. Insbesondere wird hierbei im Verfahrensschritt b) ein Lack unstrukturiert aufgetragen. Anschließend erfolgt die Erzeugung der Strukturierung gemäß Verfahrensschritt c) zum Beispiel durch Eindrücken eines Prägestempels. Da der Lack noch nicht gehärtet ist, tritt nur ein sehr geringer Verschleiß am Prägewerkzeug ein. Während sich der Prägestempel auf der Lackschicht befindet, wird diese zum Beispiel thermisch gehärtet. Anstelle eines Prägestempels kann eine Deckfolie auf die erste Lackschicht aufgebracht werden, welche eine strukturierte Oberfläche aufweist. Die Strukturierung der Lackschicht wird durch Abformung der strukturierten Oberfläche der Deckfolie erzeugt. Nach dem Aufbringen der Deckfolie wird die Lackschicht gehärtet und anschließend die Deckfolie entfernt.In a further preferred embodiment of the method for producing the security feature is the first coat of paint during of process step c) hardened. In particular, in this process step b) a paint is applied unstructured. Subsequently the structuring is carried out in accordance with method step c) Example by impressions an embossing stamp. Since the paint is not cured yet is, only a very low wear on the embossing tool. While the stamp on the lacquer layer, this becomes, for example, thermally hardened. Instead of an embossing stamp a cover sheet can be applied to the first lacquer layer, which a structured surface having. The structuring of the lacquer layer is achieved by impression taking the structured surface the cover sheet produced. After applying the cover sheet is the Lacquer layer hardened and subsequently removed the cover sheet.

In einer weiteren bevorzugten Ausführungsform des Verfahrens zur Herstellung des Sicherheitsmerkmals wird auf die erste Lackschicht eine zweite Lackschicht aufgetragen. Die Auftragung der zweiten Lackschicht kann drucktechnisch im Hoch-, Flach-, Tief-, Durch- oder Digitaldruck, mittels Verguss, Sprühbeschichtung oder Walzenbeschichtung auf die erste Lackschicht erfolgen.In a further preferred embodiment of the method for producing the security feature is on the first lacquer layer applied a second lacquer layer. The application the second lacquer layer can be printed in high, low, low, Through or digital printing, by means of potting, spray coating or roller coating done on the first coat of paint.

In einer besonders bevorzugten Ausführungsform des Verfahrens zur Herstellung des Sicherheitsmerkmals umfasst die Aufbringung der zwei Lackschichten folgende Verfahrensschritte:

  • u) Aufbringen eines zur Bildung der ersten Lackschicht verwendeten ersten Lackes,
  • v) Partielles Härten des ersten Lackes,
  • w) Aufbringen eines zur Bildung der zweiten Lackschicht verwendeten zweiten Lackes,
  • x) Gleichzeitiges vollständiges Härten beider Lacke.
In a particularly preferred embodiment of the method for producing the security feature, the application of the two lacquer layers comprises the following method steps:
  • u) applying a first lacquer used to form the first lacquer layer,
  • v) partial curing of the first paint,
  • w) applying a second lacquer used to form the second lacquer layer,
  • x) simultaneous complete curing of both paints.

Hierzu weist der erste Lack zwei Härtungsschritte auf, zum Beispiel durch Polyaddition und durch radikalische Polymerisation. Der erste Härtungsschritt führt dazu, dass der erste Lack ausreichend fest wird, sodass die eingebrachte Struktur durch die folgenden Schritte nicht mehr zerstört wird. Der zweite Lack verfügt über einen Härtungsschritt, der mit dem zweiten Härtungsschritt des ersten Lackes identisch ist. Hierdurch kommt es zu einer chemischen Reaktion zwischen den beiden Lacken im Verfahrensschritt x), sodass beide Lackschichten untrennbar miteinander verbunden werden.For this purpose, the first coating has two curing steps, for example by polyaddition and by radical polymerization. The first hardening step causes the first lacquer to become sufficiently firm so that the introduced structure is no longer destroyed by the following steps. The second paint has a curing step that is identical to the second curing step of the first paint. This leads to a chemical reaction between the two paints in process step x), so that both paint coats are inseparably bonded together.

In einer weiteren bevorzugten Ausführungsform des Verfahrens zur Herstellung des Sicherheitsmerkmals wird auf die erste Lackschicht eine zweite Lackschicht aufgetragen, bevor die erste Lackschicht gehärtet ist. Beide Lackschichten werden anschließend in einem gemeinsamen Härtungsschritt gehärtet.In a further preferred embodiment of the method for producing the security feature is on the first coat of paint applied a second coat of paint before hardened the first lacquer layer is. Both paint layers are then in a common curing step hardened.

Ein erfindungsgemäßes Verfahren zur Herstellung eines Dokumentes mit dem ohne technische Hilfsmittel visuell wahrnehmbaren Sicherheitsmerkmal umfasst vorzugsweise folgende Schritte:

  • A) Erzeugung eines ohne technische Hilfsmittel visuell wahrnehmbaren Sicherheitsmerkmals gemäß der vorliegenden Erfindung, gebildet aus der ersten Materialschicht, der ersten Lackschicht und gegebenenfalls einer zweiten Lackschicht,
  • B) Bereitstellen von wenigstens einer weiteren Materialschicht,
  • C) Anordnen der Materialschichten übereinander und
  • D) Verbinden der Materialschichten zu einem Dokumentenkörper.
A method according to the invention for producing a document with the security feature which can be visually perceived without technical aids preferably comprises the following steps:
  • A) production of a security feature visually perceptible without technical aids according to the present invention, formed from the first material layer, the first lacquer layer and optionally a second lacquer layer,
  • B) providing at least one further material layer,
  • C) arranging the material layers one above the other and
  • D) connecting the material layers to a document body.

Der Verfahrensschritt A) umfasst die Verfahrensschritte a), b) und c) zur Herstellung des erfindungsgemäßen Sicherheitsmerkmals. Im Verfahrensschritt B) werden weitere Materialschichten bereitgestellt, aus denen das Dokument aufgebaut werden soll. Diese können aus dem gleichen Material bestehen wie die erste Materialschicht, sie können aber auch aus verschiedenen Materialien bestehen. Insbesondere kann es sich bei einer der weiteren Materialschichten um ein Inlay aus einem thermoplastischen Elastomer handeln, insbesondere zur Einbettung elektronischer Bauteile. Die erste und die weiteren Materialschichten werden entsprechend dem Schichtaufbau des Dokumentes im Verfahrensschritt C) übereinander angeordnet. Hierbei wird bevorzugter Weise die erste Materialschicht derart angeordnet, das das im Verfahrenschritt A) erzeugte Sicherheitsmerkmal zwischen zwei Materialschichten angeordnet ist. Im Verfahrens schritt D) werden die Schichten dauerhaft miteinander verbunden, zum Beispiel mittels Lamination.Of the Process step A) comprises the process steps a), b) and c) for the production of the security feature according to the invention. in the Process step B) further material layers are provided, from which the document should be built. These can be out the same material as the first material layer, they can but also made of different materials. In particular, can one of the further layers of material is an inlay a thermoplastic elastomer act, in particular for embedding electronic components. The first and the further material layers become one above the other according to the layer structure of the document in process step C) arranged. Here, preferably, the first material layer arranged such that the security feature generated in step A) is arranged between two layers of material. In the process step D) the layers are permanently connected together, for example by means of Lamination.

Ausführungsbeispiele der Erfindung werden nun unter Bezugnahme auf die beigefügten Figuren beschrieben. Die einzelnen Figuren zeigen:embodiments The invention will now be described with reference to the accompanying drawings. The individual figures show:

1: ein Sicherheitsmerkmal im Schnitt in schematischer Darstellung; 1 : a security feature in section in schematic representation;

2: ein weiteres Sicherheitsmerkmal im Schnitt in schematischer Darstellung; 2 : another security feature in section in a schematic representation;

3: ein weiteres Sicherheitsmerkmal im Schnitt in schematischer Darstellung mit einer zweiten Lackschicht; 3 a further security feature in section in a schematic representation with a second lacquer layer;

4: ein weiteres Sicherheitsmerkmal im Schnitt in schematischer Darstellung mit einer eine Strukturierung aufweisenden ersten Materialschicht; 4 a further security feature in section in a schematic representation with a structure having a first material layer;

5: ein weiteres Sicherheitsmerkmal im Schnitt in schematischer Darstellung mit einer zweiten Lackschicht, welche die Strukturierung der ersten Lackschicht nur teilweise ausgleicht; 5 a further security feature in section in a schematic representation with a second lacquer layer, which only partially compensates for the structuring of the first lacquer layer;

6: ein weiteres Sicherheitsmerkmal im Schnitt in schematischer Darstellung; 6 : another security feature in section in a schematic representation;

7: ein weiteres Sicherheitsmerkmal im Schnitt in schematischer Darstellung mit einer zweiten Lackschicht, welche einen mit der ersten Materialschicht gleichen Brechungsindex aufweist; 7 a further security feature in section in a schematic representation with a second lacquer layer, which has a same refractive index with the first material layer;

8: ein weiteres Sicherheitsmerkmal im Schnitt in schematischer Darstellung mit einem Dokumentenrohling als erster Materialschicht. 8th : Another security feature in section in a schematic representation with a document blank as the first material layer.

In 1 ist ein Sicherheitsmerkmal 10 dargestellt, welches aus einer ersten Materialschicht 11 und einer ersten Lackschicht 12 gebildet wird. Die erste Lackschicht 12 weist eine Strukturierung auf, welche eine Strukturgröße parallel 15 und senkrecht 16 zur Oberfläche des Sicherheitsmerkmals 10 aufweist, das heißt zu einer Ebene, die zur Oberfläche der ersten Materialschicht koplanar ist. Die Strukturgröße 15 parallel zur Oberfläche beträgt wenigstens 10 μm. Die Strukturgröße 16 senkrecht zur Oberfläche beträgt wenigstens 5 μm. Die erste Lackschicht 12 bildet ein Punktmuster und kann zum Beispiel mittels Tintenstrahldruck erzeugt worden sein. Durch die unterschiedlichen Brechungsindices der ersten Materialschicht 11 und der ersten Lackschicht 12 ergibt sich der visuelle Eindruck schwebender Tropfen auf der ersten Materialschicht 11.In 1 is a security feature 10 shown, which consists of a first layer of material 11 and a first coat of paint 12 is formed. The first coat of paint 12 has a structuring which parallelizes a structure size 15 and perpendicular 16 to the surface of the security feature 10 that is, to a plane that is coplanar with the surface of the first material layer. The structure size 15 parallel to the surface is at least 10 microns. The structure size 16 perpendicular to the surface is at least 5 microns. The first coat of paint 12 forms a dot pattern and may be generated by, for example, ink jet printing. Due to the different refractive indices of the first material layer 11 and the first coat of paint 12 The result is the visual impression of floating drops on the first layer of material 11 ,

In 2 ist ein weiteres Sicherheitsmerkmal 10 dargestellt, bei welchem auf der ersten Materialschicht 11 eine erste Lackschicht 12 angeordnet ist. Die erste Lackschicht 12 bedeckt die erste Materialschicht 11 wenigstens im gezeigten Bereich vollständig. Die erste Lackschicht ist jedoch auf der Oberfläche strukturiert und weist eine Strukturgröße parallel 15 und senkrecht 16 zur Oberfläche des Sicherheitsmerkmals 10, welche 5 μm senkrecht zur Oberfläche und 10 μm parallel zur Oberfläche betragen. Die Lackschicht kann auch deutlich dicker sein. Ein solches Sicherheitsmerkmal kann zum Beispiel mittels Auftragung einer gleichmäßigen Lackschicht und Einprägen einer Strukturierung während der Härtung der ersten Lackschicht hergestellt werden. Durch die unterschiedlichen Brechungsindices der ersten Materialschicht 11 und der ersten Lackschicht 12 ergibt sich der visuelle Eindruck schwebender Tropfen auf der ersten Materialschicht 11.In 2 is another security feature 10 illustrated in which on the first material layer 11 a first coat of paint 12 is arranged. The first coat of paint 12 covers the first layer of material 11 at least in the area shown completely. However, the first lacquer layer is structured on the surface and has a structure size in parallel 15 and perpendicular 16 to the surface of the security feature 10 which are 5 μm perpendicular to the surface and 10 μm parallel to the surface. The lacquer layer can also be significantly thicker. Such a security feature can, for example, by applying a uniform lacquer layer and impressing a structuring during curing the first lacquer layer are produced. Due to the different refractive indices of the first material layer 11 and the first coat of paint 12 The result is the visual impression of floating drops on the first layer of material 11 ,

In 3 ist ein weiteres Sicherheitsmerkmal 10 dargestellt, bei welchem über der ersten Materialschicht 11 eine erste Lackschicht 12 und über der ersten Lackschicht 12 eine zweite Lackschicht 13 angeordnet ist. Bevorzugter Weise weist die zweite Lackschicht 13 abriebfeste Eigenschaften auf und gleicht die Strukturierung der ersten Lackschicht 12 vollständig aus, sodass das Sicherheitsmerkmal 10 auf der Oberfläche eines Dokumentes besonders gut gegen Abnutzung geschützt ist. Weiter kann ein solches Sicherheitsmerkmal 10 auch ohne abriebfeste Eigenschaften in das Innere eines Dokumentes integriert werden. Bei einer Lamination würde der Druck aufgrund der glatten Oberfläche gleichmäßig über das Sicherheitsmerkmal 10 verteilt, sodass die Strukturierung der ersten Lackschicht 12 nicht zerstört werden würde. Der Brechungsindex der ersten Lackschicht 12 kann zum Beispiel um wenigstens 0,1 größer sein als der Brechungsindex der ersten Materialschicht 11 sowie um wenigstens 0,1 größer als der Brechungsindex der zweiten Lackschicht 13. Es ergibt sich der visuelle Eindruck von im Volumen des Materials schwebenden Tropfen.In 3 is another security feature 10 illustrated in which over the first material layer 11 a first coat of paint 12 and over the first coat of paint 12 a second coat of paint 13 is arranged. Preferably, the second lacquer layer 13 Abrasion-resistant properties and equalizes the structuring of the first coat of paint 12 completely off, so the security feature 10 is particularly well protected against wear on the surface of a document. Next, such a security feature 10 Even without abrasion-resistant properties are integrated into the interior of a document. With a lamination, the pressure would be even over the security feature due to the smooth surface 10 distributed, so that the structuring of the first coat of paint 12 would not be destroyed. The refractive index of the first lacquer layer 12 For example, it may be at least 0.1 greater than the refractive index of the first material layer 11 and at least 0.1 greater than the refractive index of the second lacquer layer 13 , The result is the visual impression of drops floating in the volume of the material.

In 4 ist ein weiteres Sicherheitsmerkmal 10 dargestellt, bei welchem eine Strukturierung in die erste Materialschicht 11, zum Beispiel mittels Prägen, Fräsen oder mittels Ultraschall eingebracht worden ist. Die erste Lackschicht 12 kann gleichmäßig aufgetragen werden, die Strukturierung der ersten Lackschicht 12 ergibt sich aus der Strukturierung der ersten Materialschicht 11. Auch hier ergibt sich aufgrund des Unterschiedes der Brechungsindices der ersten Materialschicht 11 und der ersten Lackschicht 12 der visuelle Eindruck von im Volumen des Materials schwebenden Tropfen.In 4 is another security feature 10 in which a structuring into the first material layer 11 , has been introduced for example by means of embossing, milling or by means of ultrasound. The first coat of paint 12 can be applied evenly, the structuring of the first coat of paint 12 results from the structuring of the first material layer 11 , Again, due to the difference in the refractive indices of the first material layer 11 and the first coat of paint 12 the visual impression of drops floating in the volume of the material.

In 5 ist ein weiteres Sicherheitsmerkmal 10 dargestellt, bei welchem über der ersten Lackschicht 12 eine zweite Lackschicht 13 angeordnet ist, welche die Strukturierung der ersten Lackschicht 12 nicht vollständig ausgleicht. Hierdurch bleibt die Strukturierung fühlbar. Ist das Sicherheitsmerkmal 10 auf der Oberfläche eines Dokumentes angeordnet, so kann die Strukturierung nicht nur ohne technische Hilfsmittel visuell beobachtet sondern auch gefühlt werden. Neben dem visuellen Eindruck, welcher dem in 3 gleicht, ergibt sich ein fühlbarer Eindruck, der mit dem visuellen Eindruck korreliert ist. An Stellen, an welchen ein scheinbarer Tropfen wahrgenommen werden kann, ist eine Erhebung spürbar.In 5 is another security feature 10 shown in which over the first lacquer layer 12 a second coat of paint 13 is arranged, which is the structuring of the first lacquer layer 12 not completely compensated. As a result, the structuring remains palpable. Is the security feature 10 arranged on the surface of a document, so the structuring can be visually observed not only without technical aids but also felt. In addition to the visual impression, which the in 3 equals a tactile impression that is correlated with the visual impression. In places where an apparent drop can be perceived, a survey is noticeable.

In 6 ist ein weiteres Sicherheitsmerkmal 10 dargestellt, bei welchem die Strukturierung der ersten Lackschicht 12 verschiedene Strukturgrößen parallel und senkrecht zur Oberfläche des Sicherheitsmerkmals 10 aufweist. Erfindungsgemäß beträgt die kleinste Strukturgröße wenigstens als 5 μm senkrecht zur Oberfläche. Besonders bevorzugt ist die größte Strukturgröße senkrecht zur Oberfläche höchstens 10 μm. Hierdurch ist der visuelle Eindruck der verschiedenen Tropfen verschieden und ein dargestelltes Muster kann komplexer sein.In 6 is another security feature 10 in which the structuring of the first lacquer layer 12 different structure sizes parallel and perpendicular to the surface of the security feature 10 having. According to the invention, the smallest feature size is at least 5 μm perpendicular to the surface. Particularly preferably, the largest structure size perpendicular to the surface is at most 10 μm. As a result, the visual impression of the various drops is different and a displayed pattern can be more complex.

In 7 ist ein weiteres Sicherheitsmerkmal 10 dargestellt, bei welchem über der ersten Lackschicht 12 eine zweite Lackschicht 13 angeordnet ist, wobei die zweite Lackschicht 13 den gleichen Brechungsindex aufweist, wie die erste Materialschicht 11. Der Brechungsindex der ersten Lackschicht 12 unterscheidet sich vom Brechungsindex der ersten Materialschicht 11 und der zweiten Lackschicht 13 um mindestens 0,1. Hierdurch entsteht der optische Eindruck, die Teilbereiche der ersten Lackschicht 12 schweben wie Tropfen im Volumen des Sicherheitsmerkmals. Beispielsweise können sich überlagernde Strukturen dargestellt sein.In 7 is another security feature 10 shown in which over the first lacquer layer 12 a second coat of paint 13 is arranged, wherein the second lacquer layer 13 has the same refractive index as the first material layer 11 , The refractive index of the first lacquer layer 12 differs from the refractive index of the first material layer 11 and the second lacquer layer 13 at least 0.1. This creates the visual impression, the subregions of the first lacquer layer 12 float like drops in the volume of the security feature. For example, overlapping structures can be represented.

In 8 ist ein Dokument 20 dargestellt, bei welchem auf einer ersten Materialschicht 11, welche in diesem Fall einen Dokumentrohling darstellt, eine erste Lackschicht 12 sowie eine zweite Lackschicht 13, insbesondere mit abriebfesten Eigenschaften, erfindungsgemäß angeordnet sind. Auch hier entsteht durch den Brechungsindexunterschied zwischen der ersten Lackschicht 12 und der ersten Materialschicht 11 sowie der zweiten Lackschicht 13 der visuelle Eindruck von im Volumen des Dokuments schwebenden Tropfen.In 8th is a document 20 shown in which on a first layer of material 11 , which in this case represents a document blank, a first lacquer layer 12 and a second coat of paint 13 , in particular with abrasion-resistant properties, are arranged according to the invention. Here, too, arises due to the refractive index difference between the first lacquer layer 12 and the first material layer 11 as well as the second lacquer layer 13 the visual impression of drops floating in the volume of the document.

Claims (30)

Verfahren zur Herstellung eines ohne technische Hilfsmittel visuell wahrnehmbaren Sicherheitsmerkmals, umfassend folgende Schritte: a) Bereitstellen einer ersten Materialschicht, b) Aufbringen einer durch eine erste Lackschicht gebildeten zweiten Materialschicht zumindest in Teilbereichen der ersten Materialschicht, wobei die erste Lackschicht einen Brechungsindex aufweist, der sich vom Brechungsindex der ersten Materialschicht um wenigstens 0,1 unterscheidet, sowie c) Erzeugen einer Strukturierung der ersten Lackschicht, wobei die Strukturierung eine Strukturgröße parallel zur Oberfläche des Sicherheitsmerkmals von wenigstens 10 μm und senkrecht zur Oberfläche des Sicherheitsmerkmals von wenigstens 5 μm aufweist und wobei das so hergestellte Sicherheitsmerkmal aufgrund von Brechung elektromagnetischer Strahlung visuell wahrnehmbar ist.Method for producing a non-technical Aid of visually perceptible security feature comprising following steps: a) providing a first material layer, b) Applying a second formed by a first lacquer layer Material layer at least in partial regions of the first material layer, wherein the first resist layer has a refractive index different from the Refractive index of the first material layer differs by at least 0.1, such as c) generating a structuring of the first lacquer layer, wherein the structuring is a feature size parallel to the surface of the Security feature of at least 10 microns and perpendicular to the surface of the security feature of at least 5 μm and the security feature thus produced due to of refraction electromagnetic radiation is visually perceptible. Verfahren zur Herstellung eines Sicherheitsmerkmals nach Anspruch 1, dadurch gekennzeichnet, dass im Verfahrensschritt b) die erste Lackschicht drucktechnisch im Hoch-, Flach-, Tief-, Durch- oder Digitaldruck, mittels Verguss, Sprühbeschichtung oder Walzenbeschichtung auf die erste Materialschicht aufgebracht wird.Method for producing a security feature according to claim 1, characterized net that in step b) the first coating layer is applied by printing technology in high-, flat-, gravure-, through- or digital printing, by means of potting, spray coating or roll coating on the first material layer. Verfahren zur Herstellung eines Sicherheitsmerkmals nach Anspruch 2, dadurch gekennzeichnet, dass die drucktechnische Aufbringung der ersten Lackschicht unter gleichzeitiger Erzeugung der Strukturierung gemäß Verfahrensschritt c) erfolgt.Method for producing a security feature according to claim 2, characterized in that the printing technology Application of the first lacquer layer with simultaneous production structuring according to method step c). Verfahren zur Herstellung eines Sicherheitsmerkmals nach Anspruch 1, dadurch gekennzeichnet, dass auf der Oberfläche der im Verfahrensschritt a) bereitgestellten ersten Materialschicht zunächst mittels Umformen, zum Beispiel mittels Prägen und/oder Ultraschall, eine Strukturierung erzeugt wird und anschließend im Verfahrensschritt b) die erste Lackschicht aufgetragen wird, wobei durch die Strukturierung der ersten Materialschicht auch die Strukturierung der ersten Lackschicht gemäß Verfahrensschritt c) erzeugt wird.Method for producing a security feature according to claim 1, characterized in that on the surface of the in process step a) provided first material layer first by means of Forming, for example by means of embossing and / or ultrasound, a Structuring is generated and then in step b) the first lacquer layer is applied, wherein the structuring the first material layer also the structuring of the first lacquer layer according to method step c) is generated. Verfahren zur Herstellung eines Sicherheitsmerkmals nach Anspruch 1, dadurch gekennzeichnet, dass das Erzeugen der Strukturierung der ersten Lackschicht im Verfahrensschritt c) mittels fotolithografischer Techniken erfolgt.Method for producing a security feature according to claim 1, characterized in that the generating the structuring the first lacquer layer in process step c) by means of photolithographic Techniques are done. Verfahren zur Herstellung eines Sicherheitsmerkmals nach Anspruch 1, dadurch gekennzeichnet, dass die erste Lackschicht während des Verfahrensschrittes c) gehärtet wird.Method for producing a security feature according to claim 1, characterized in that the first lacquer layer while of process step c) hardened becomes. Verfahren zur Herstellung eines Sicherheitsmerkmals nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass über die erste Lackschicht eine zweite Lackschicht aufgetragen wird.Method for producing a security feature according to one of the claims 1 to 6, characterized in that on the first lacquer layer a second paint layer is applied. Verfahren zur Herstellung eines Sicherheitsmerkmals nach Anspruch 7, dadurch gekennzeichnet, dass die Aufbringung der zwei Lackschichten folgende Verfahrensschritte umfasst: u) Aufbringen eines zur Bildung der ersten Lackschicht verwendeten ersten Lackes, v) Partielles Härten des ersten Lackes, w) Aufbringen eines zur Bildung der zweiten Lackschicht verwendeten zweiten Lackes, x) Gleichzeitiges vollständiges Härten beider Lacke.Method for producing a security feature according to claim 7, characterized in that the application of the two paint layers comprises the following process steps: u) Applying a used to form the first lacquer layer first paint, v) partial curing of the first paint, w) Applying a used to form the second lacquer layer second paint, x) simultaneous complete curing of both paints. Verfahren zur Herstellung eines Sicherheitsmerkmals nach Anspruch 7, dadurch gekennzeichnet, dass die zweite Lackschicht auf die erste Lackschicht vor der Härtung der ersten Lackschicht aufgebracht wird und eine gemeinsame Härtung beider Lackschichten erfolgt.Method for producing a security feature according to claim 7, characterized in that the second lacquer layer on the first lacquer layer before curing the first lacquer layer is applied and a joint hardening of both paint layers he follows. Ohne technische Hilfsmittel visuell wahrnehmbares Sicherheitsmerkmal, gebildet aus wenigstens zwei Materialschichten, wobei wenigstens eine zweite Materialschicht eine erste Lackschicht ist, wobei die erste Lackschicht zumindest in Teilbereichen eine erste Materialschicht bedeckt, wobei die erste Lackschicht gegenüber der ersten Materialschicht einen Brechungsindexunterschied von mindestens 0,1 aufweist, wobei die erste Lackschicht eine Strukturierung darstellt und/oder aufweist, dadurch gekennzeichnet, dass das Sicherheitsmerkmal aufgrund von Brechung elektromagnetischer Strahlung visuell wahrnehmbar ist und wobei die Strukturierung der ersten Lackschicht eine Strukturgröße parallel zur Oberfläche des Sicherheitsmerkmals von wenigstens 10 μm und senkrecht zur Oberfläche des Sicherheitsmerkmals von wenigstens 5 μm aufweist.Visible visually without technical aids Security feature formed of at least two layers of material, wherein at least one second material layer is a first lacquer layer, wherein the first lacquer layer at least in some areas a first Covered material layer, wherein the first lacquer layer opposite to the first material layer has a refractive index difference of at least 0.1, wherein the first lacquer layer is a structuring and / or has, characterized in that the security feature due of refraction electromagnetic radiation is visually perceptible and wherein the patterning of the first lacquer layer is a feature size parallel to the surface the security feature of at least 10 microns and perpendicular to the surface of the security feature of at least 5 μm having. Sicherheitsmerkmal nach Anspruch 10, dadurch gekennzeichnet, dass die Strukturierung der ersten Lackschicht eine Strukturgröße parallel zur Oberfläche des Sicherheitsmerkmals von wenigstens 100 μm aufweist.Security feature according to claim 10, characterized that the structuring of the first lacquer layer parallel a structure size to the surface having the security feature of at least 100 microns. Sicherheitsmerkmal nach einem der Ansprüche 10 und 11, dadurch gekennzeichnet, dass die Strukturierung der ersten Lackschicht eine Strukturgröße parallel zur Oberfläche des Sicherheitsmerkmals von wenigstens 1 mm aufweist.Security feature according to one of claims 10 and 11, characterized in that the structuring of the first lacquer layer a structure size in parallel to the surface of the security feature of at least 1 mm. Sicherheitsmerkmal nach einem der Ansprüche 10 bis 12, dadurch gekennzeichnet, dass die Strukturierung der ersten Lackschicht eine Strukturgröße senkrecht zur Oberfläche des Sicherheitsmerkmals von 5 μm bis 10 μm aufweist.Security feature according to one of claims 10 to 12, characterized in that the structuring of the first lacquer layer a structure size vertical to the surface the security feature of 5 microns up to 10 μm having. Sicherheitsmerkmal nach einem der Ansprüche 10 bis 13, dadurch gekennzeichnet, dass auf der ersten Lackschicht eine zweite Lackschicht angeordnet ist.Security feature according to one of claims 10 to 13, characterized in that on the first lacquer layer a second lacquer layer is arranged. Sicherheitsmerkmal nach Anspruch 14, dadurch gekennzeichnet, dass die zweite Lackschicht einen Brechungsindexunterschied von mindestens 0,1 gegenüber der ersten Lackschicht aufweist.Security feature according to claim 14, characterized the second resist layer has a refractive index difference of at least 0.1 over having the first lacquer layer. Sicherheitsmerkmal nach einem der Ansprüche 14 und 15, dadurch gekennzeichnet, dass die zweite Lackschicht die Strukturierung der ersten Lackschicht senkrecht zur Oberfläche des Sicherheitsmerkmals teilweise ausgleicht.Security feature according to one of claims 14 and 15, characterized in that the second lacquer layer structuring the first lacquer layer perpendicular to the surface of the security feature partially compensates. Sicherheitsmerkmal nach einem der Ansprüche 14 bis 15, dadurch gekennzeichnet, dass die zweite Lackschicht die Strukturierung der ersten Lackschicht senkrecht zur Oberfläche des Sicherheitsmerkmals vollständig ausgleicht.Security feature according to one of claims 14 to 15, characterized in that the second lacquer layer structuring the first lacquer layer perpendicular to the surface of the security feature Completely balances. Sicherheitsmerkmal nach Anspruch 16, dadurch gekennzeichnet, dass die zweite Lackschicht eine Schichtdicke aufweist, welche geringer als die Strukturgröße der ersten Lackschicht senkrecht zur Oberfläche des Sicherheitsmerkmals ist.Security feature according to claim 16, characterized in that the second lacquer layer has a layer thickness which is less than the structure size of the first lacquer layer perpendicular to Surface of the security feature is. Sicherheitsmerkmal nach einem der Ansprüche 14 bis 18, dadurch gekennzeichnet, dass die zweite Lackschicht im Wesentlichen den gleichen Brechungsindex wie die erste Materialschicht aufweist.Security feature according to one of claims 14 to 18, characterized in that the second lacquer layer substantially has the same refractive index as the first material layer. Sicherheitsmerkmal nach einem der Ansprüche 14 bis 19, dadurch gekennzeichnet, dass die zweite Lackschicht abriebfeste Eigenschaften aufweist.Security feature according to one of claims 14 to 19, characterized in that the second lacquer layer abrasion resistant Features. Sicherheitsmerkmal nach Anspruch 20, dadurch gekennzeichnet, dass die abriebfesten Eigenschaften durch Zusatz von ZnO oder SiO2 erzeugt werden.Security feature according to claim 20, characterized in that the abrasion-resistant properties are produced by addition of ZnO or SiO 2 . Sicherheitsmerkmal nach einem der Ansprüche 14 bis 21, dadurch gekennzeichnet, dass die erste und die zweite Lackschicht transparent sind.Security feature according to one of claims 14 to 21, characterized in that the first and the second lacquer layer are transparent. Sicherheitsmerkmal nach einem der Ansprüche 10 bis 22, dadurch gekennzeichnet, dass der Brechungsindex der ersten Lackschicht durch Zusatz mindestens eines hochbrechenden Zusatzstoffes um wenigstens 0,1 höher als der Brechungsindex der ersten Materialschicht eingestellt ist.Security feature according to one of claims 10 to 22, characterized in that the refractive index of the first lacquer layer by adding at least one high-index additive by at least 0.1 higher as the refractive index of the first material layer is set. Sicherheitsmerkmal nach Anspruch 23, dadurch gekennzeichnet, dass mindestens ein hochbrechender Zusatzstoff ausgewählt ist aus Glas, Feldspat, TiO2, ZrO2 und Diamant.Security feature according to claim 23, characterized in that at least one high-index additive is selected from glass, feldspar, TiO 2 , ZrO 2 and diamond. Sicherheitsmerkmal nach einem der Ansprüche 10 bis 24, dadurch gekennzeichnet, dass die erste Materialschicht aus einem Material besteht, ausgewählt aus der Gruppe, umfassend Polycarbonat (PC), Polyethylenterephthalat (PET) sowie dessen Derivaten, Polyvinylchlorid (PVC), Polypropylen (PP), Polyethylen (PE), thermoplastischen Elastomeren (TPE), Papier und Glas sowie Mischungen dieser Materialien.Security feature according to one of claims 10 to 24, characterized in that the first material layer of a Material exists, selected from the group comprising polycarbonate (PC), polyethylene terephthalate (PET) and its derivatives, polyvinyl chloride (PVC), polypropylene (PP), Polyethylene (PE), thermoplastic elastomers (TPE), paper and Glass and mixtures of these materials. Sicherheitsmerkmal nach einem der Ansprüche 10 bis 25, dadurch gekennzeichnet, dass die erste Materialschicht eine Dicke von mindestens 50 μm aufweist.Security feature according to one of claims 10 to 25, characterized in that the first material layer a Thickness of at least 50 microns. Sicherheitsmerkmal nach einem der Ansprüche 10 bis 26, dadurch gekennzeichnet, dass die erste Materialschicht ein Dokumentenrohling ist.Security feature according to one of claims 10 to 26, characterized in that the first material layer is a document blank is. Sicherheitsmerkmal nach einem der Ansprüche 10 bis 27, dadurch gekennzeichnet, dass die erste Lackschicht wenigstens einen zur Lumineszenz anregbaren Stoff enthält.Security feature according to one of claims 10 to 27, characterized in that the first lacquer layer at least contains a stimulable for luminescence substance. Dokument mit wenigstens einem Sicherheitsmerkmal, wobei es sich bei wenigstens einem Sicherheitsmerkmal um ein ohne technische Hilfsmittel visuell wahrnehmbares Sicherheitsmerkmal gemäß einem der Ansprüche 10 bis 28 handelt.Document with at least one security feature, where at least one security feature is one without technical aids visually perceptible security feature according to one the claims 10 to 28 acts. Dokument nach Anspruch 29, dadurch gekennzeichnet, dass es sich bei dem Dokument um ein Wert- oder Sicherheitsdokument, einen Reisepass, einen Personalausweis, eine Geburtsurkunde, ein Visum, einen Führerschein, eine Kreditkarte, eine Bankkarte, einen Firmenausweis, einen Mitgliedausweis, einen Fahrzeugschein, eine Banknote, einen Scheck, eine Aktie, eine Briefmarke oder ein Steuerzeichen handelt.Document according to Claim 29, characterized that the document is a value or security document, a passport, identity card, birth certificate, a Visa, a driving license, a credit card, a bank card, a company card, a membership card, a registration document, a banknote, a check, a share, a Stamp or a tax stamp.
DE102009007779.0A 2009-02-04 2009-02-04 A method for producing a visually perceptible without technical aids security feature, security feature for plastic-based value or security document and document with at least one such security feature Active DE102009007779C5 (en)