CN206979990U - Glof club head is forged altogether - Google Patents
Glof club head is forged altogether Download PDFInfo
- Publication number
- CN206979990U CN206979990U CN201720722819.8U CN201720722819U CN206979990U CN 206979990 U CN206979990 U CN 206979990U CN 201720722819 U CN201720722819 U CN 201720722819U CN 206979990 U CN206979990 U CN 206979990U
- Authority
- CN
- China
- Prior art keywords
- club head
- glof club
- adjustment member
- forging
- weight adjustment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses one kind to forge iron golf club altogether.More specifically, it the utility model is related to following one kind and forge iron golf club altogether, the iron golf club of forging altogether has main part and at least one weight adjustment member integratedly loaded in the main part for forging iron golf club head altogether made of the first material, it is not necessary to auxiliary attachment or machining operations.It the utility model is related to and iron golf club head is created by preforming blank, the preforming blank contains two or more materials before actual forging technology;Result is to manufacture the glof club head of multiple material, it is not necessary to any subsequent fabrication operations, machining, welding, swaged forging, bonding etc..
Description
The cross reference of related application
The application is that the part for the U.S. Patent Application Serial Number 14/078.380 submitted on November 12nd, 2013 is continued, institute
State the part that U.S. Patent application is the U.S. Patent Application Serial Number 13/927.764 submitted on June 26th, 2013 to continue, institute
It is that the U.S. Patent Application Serial Number 13/305.087 submitted on November 28th, 2011 is now special for the U.S. to state U.S. Patent application
The part of profit number 8926451 is continued, and the U.S. Patent application or Disclosure of U.S. patent are all by quoting overall knot
Close herein.
Technical field
The utility model relates generally to a kind of common forging glof club head formed by two or more materials and system
The method for making such glof club head.Swage golf is created by preforming blank more specifically, the utility model is related to
Club head, the preforming blank contain two or more materials before actual forging technology;Result is that manufacture is more
The glof club head of kind material, it is not necessary to any subsequent fabrication operations, machining, welding, swaged forging, bonding etc..
Background technology
Golf is difficult!When common horizontal linksman brandishes golf clubs, he or she is brandishing
Unexpected change occurs during golf clubs, this causes many off-center hits, and it causes compared with direct center hits
Cause the reduction of achievement.But, it is intended to common horizontal linksman is more enjoyed this very difficult motion, Gao Er
Husband's club designer employs the golf club design of uniqueness, and it can mitigate the harsh of less perfect golf and show
It is real.
In the embodiment of an early stage, Igarashi United States Patent (USP) No.4,523,759 disclose a kind of perimeter weighting
Hollow Golf club iron, it has foam core, the foam core have to centre of moment concentrate effective hitting region, it is intended to help
Helping is easier golf sports.The moment of inertia that the distribution of weight of golf clubs to periphery is allowed to make glof club head
(MOI) increase, reduce the undesirable torsion of the golf clubs when golf clubs hits golf.
Doran et al. United States Patent (USP) No.4,809,977 show another embodiment, and it is attempted by golf
Additional weight is placed to increase the moment of inertia of glof club head in the heel part of club head and toe office.By increase with
The increase of the moment of inertia of part and the achievable glof club head of toe portion counterweight can further prevent golf clubs
Reversed in heel part and toe portion direction, which reduce the adverse consequences for deviateing expected orbit launching golf.
Although the preliminary trial for the pardon and playability for increasing golf clubs for common horizontal linksman is
It is laudable, but it obtains the bag of extreme not over using different materials to form the different piece of glof club head
Capacitive.In one embodiment, Takeda United States Patent (USP) No.5,885,170 show using multiple material to create confrontation
Measure the advantages of more extremely adjustment of attribute.More specifically, United States Patent (USP) No.5,885,170 teach a kind of main body, main body tool
There is the face being formed of one material, while hosel is formed by another material, another material has the material with head main body
Expect different proportion.Helmstetter et al. United States Patent (USP) No.6,434,811 show it is another using multiple material come
The embodiment of glof club head performance is improved, it is realized by setting Weighting system on glof club head, described to match somebody with somebody
Weight system is combined after whole glof club head is formed.
Recently, it is significantly ripe that multiple material is attached to the improvement of glof club head, will be permitted by being machined chamber
The multiple material of more different qualities is attached in glof club head.More specifically, Cole et al. United States Patent (USP) No.7,938,
739 disclose a kind of glof club head for the chamber for having and being integrated with glof club head, and the wherein chamber extends to from region
Toe region;Extend along the bottom at the back side of glof club head;It is roughly parallel to impact surface extension;And on region
The center line for traversing glof club head between toe region is substantially symmetric.
However, because main body completed after just multiple material is incorporated into golf clubs, different materials it
Between interface tolerance may potentially result in change glof club head sensation undesirable side effect.Hettinger
Et al. United States Patent (USP) No.6,095,931 to confirm to sacrifice feel this by using a variety of different parts specific not
Good side effect.United States Patent (USP) No.6,095,931 is by between glof club head and the main part including impact front waist section
Separation layer is provided to solve this problem.
Kubota United States Patent (USP) No.7828674 recognizes the seriousness of this problem, and it is claimed with visco-elastic element
Hollow golf club head allows more preferable linksman to feel lighter and hollow, therefore they show no favouritism to such golf
Club.United States Patent (USP) No.7828674 only uses metal cap close in a metal by that will wait to be embedded into and/or wait to be pressed into be formed
MAG block in the recess of envelope is insufficient to solve such multiple material golf clubs.
Although improve the whole of the performance of glof club head above to attempt all while attempt to making the sensation of golf clubs
Sacrifice minimize, but all methods describeds are required for creating chamber and recess in club head to be combined auxiliary material
A large amount of subsequent fabrication operations.The auxiliary operation of these types is not only costliness, and remains tight enough between a variety of parts
The ability of tolerance to be very difficult to keep solid sensation typically associated with the glof club head being unitarily formed.
Therefore, more than it can be seen that, although all exploitation be all do not sacrifice it is related to conventional golf club head
The glof club head with bigger pardon is created in the case of the sensation of connection, but current area can not be led not utilizing
Such golf clubs is created in the case of causing the follow-up manufacture of harshness of poor sensation to be machined.
Utility model content
Of the present utility model to relate in one aspect to a kind of forging glof club head, it includes main part and at least one heavy
Adjustment member is measured, the main part is made up of the first material, has striking face, and at least one adjustment member is by second
Material is made, is loaded into the main part;Wherein, in the case of no any auxiliary attachment operation, described at least one
Individual weight adjustment member is integratedly loaded in the main part of the glof club head.
Another aspect of the present utility model is related to a kind of method for forging glof club head, and it comprises the following steps:Wound
The cylinder blank made of the first material is built, one or more chambers are machined into the cylinder blank, with second
One or more of chambers are filled to material part, to create weight adjustment member, are filled with first material one
Or the residual volume of multiple chambers to be to load the weight adjustment member, and the forging cylinder blank is to create the Gao Er
The main part of husband's club head;Wherein, in the case of no any auxiliary attachment operation, the main part is by the weight
Adjustment member integratedly loads in the main body of the glof club head.
Another aspect of the present utility model is related to a kind of forging glof club head, and it includes main part and at least one
Weight adjustment member, the main part are made up of the first material, have striking face, at least one weight adjustment member
It is made up, is encased in the main part of the second material;Wherein, in the case of no any auxiliary attachment operation, institute
At least one weight adjustment member is stated integratedly to be loaded in the main part.First material is in the first forging temperature
There is down the first flow stress, and second material has the second flow stress under the second forging temperature, wherein, described
One flow stress and second flow stress are substantially similar to each other, and first forging temperature and second forging
Temperature is substantially similar to each other.First material has the first thermal coefficient of expansion, and second material has the second heat
The coefficient of expansion, wherein first thermal coefficient of expansion is more than or equal to second thermal coefficient of expansion.
Another aspect of the present utility model is related to a kind of forging glof club head, and it includes:Main part, the master
Body portion is made up of the first material, has face chamber and at least one weight chamber;At least one high density weight adjustment member, it is described
At least one high density weight adjustment member is made up of the second material, is loaded into the weight intracavitary;Lightweight weight adjustment portion
Point, the lightweight weight adjustment member is made up of the 3rd material, is loaded into the face intracavitary;And striking face insert, institute
Striking face insert is stated to be made up of first material, suitable for covering the face chamber;Wherein, the lightweight weight adjustment member
Also include multiple otch (cutout), and wherein, the high density weight adjustment member is integratedly loaded the weight intracavitary.
Other side of the present utility model, the multiple otch have it is round-shaped, and it is described it is round-shaped have
Diameter between about 1.0mm to about 3.0mm.
Other side of the present utility model, the multiple otch can be filled at least in part with polymer.
Another aspect of the present utility model is related to a kind of method for forging glof club head, and it includes:Forging in advance
Cylinder blank is to create the main part of the glof club head, wherein the main part of the glof club head
Including face chamber and at least one weight chamber.Once the forging in advance is completed, described in the second material is filled at least in part extremely
A few weight chamber, to create high density weight adjustment member, and fills the face chamber at least in part with the 3rd material, with wound
Build lightweight weight adjustment member.Then lid is provided to be at least partially enclosed the high density weight adjustment member, and is provided
Striking face insert is to cover the lightweight weight adjustment member.Finally, follow-up forging adjusts containing the high density weight
The main part of part and the lightweight weight adjustment member to create glof club head, wherein, the follow-up forging
Making technique makes the inner surface of the striking face insert be deformed into the multiple otch.
These and other features, aspect and advantage of the present utility model will by reference to the following drawings, explanation and right
Claim becomes better understood.
Brief description of the drawings
Foregoing and other feature and advantage of the present utility model following will retouch from as the figures show of the present utility model
Stating becomes obvious.With reference to herein and formed the part of this specification accompanying drawing be additionally operable to explain principle of the present utility model with
And those skilled in the relevant art is manufactured and use the utility model.
Fig. 1 of accompanying drawing is shown according to the common forging glof club head of an exemplary of the present utility model
Perspective view;
Fig. 2A-Fig. 2 D are shown according to an exemplary of the present utility model for creating golf clubs
The perspective view of the preforming blank of head;
Fig. 3 A-3D are shown according to an exemplary of the present utility model for creating glof club head
Preforming blank perspective view;
Fig. 4 A- Fig. 4 D are shown according to an exemplary of the present utility model for creating golf clubs
The perspective view of the preforming blank of head;
Fig. 5 A- Fig. 5 D are shown according to an exemplary of the present utility model for creating golf clubs
The perspective view of the preforming blank of head;
Fig. 6 is shown forges what method created using multi-step altogether according to another alternate embodiment of the present utility model
The rear view of the decomposition of glof club head;
Fig. 7 is shown forges what method created using multi-step altogether according to another alternate embodiment of the present utility model
The front perspective view of the decomposition of glof club head;
Fig. 8 is shown to be used to create according to an alternate embodiment of the present utility model in multi-step altogether forging method
The preforming blank of glof club head;
Fig. 9 shows the step in multi-step altogether forging process according to an alternate embodiment of the present utility model
The preforming blank of bending during rapid;
Figure 10 A and Figure 10 B are shown according to an alternate embodiment of the present utility model in the common forging process of multi-step
In a step during glof club head rearview and front view;
Figure 11 A and Figure 11 B are shown according to an alternate embodiment of the present utility model in the common forging process of multi-step
In a step during glof club head rearview and front view;
Figure 12 A and Figure 12 B are shown according to an alternate embodiment of the present utility model in the common forging process of multi-step
In a step during glof club head decomposition rearview and front view;
Figure 13 A and Figure 13 B are shown according to an alternate embodiment of the present utility model in the common forging process of multi-step
In a step during glof club head rearview and front view.
Figure 14 A and Figure 14 B are shown according to an alternate embodiment of the present utility model in the common forging process of multi-step
In a step during glof club head backsight and front view.
Figure 15 shows the front view of the glof club head according to an alternate embodiment of the present utility model;
Figure 16 shows the front view of the glof club head according to an alternate embodiment of the present utility model, wherein
Without striking face, chamber is shown;
Figure 17 is shown to be regarded according to the stereo decomposing of the glof club head of an alternate embodiment of the present utility model
Figure;
Figure 18 shows the rearview of the glof club head according to an alternate embodiment of the present utility model;
Figure 19 shows the side decomposition view of the glof club head according to an alternate embodiment of the present utility model;
Figure 20 is shown to be regarded according to being decomposed with side for glof club head of an alternate embodiment of the present utility model
Figure;
Figure 21 shows the decomposition diagram of the glof club head according to an alternate embodiment of the present utility model;
Figure 22 shows another point of the glof club head according to another alternate embodiment of the present utility model
Solve perspective view;
Figure 23 shows the front view of the glof club head according to an alternate embodiment of the present utility model, it is allowed to
Transversal upper thread A-A ' is shown;
Figure 24 shows the viewgraph of cross-section of the glof club head according to an alternate embodiment of the present utility model;
And
Figure 25 shows the transversal of the amplification of the glof club head according to an alternate embodiment of the present utility model
Face view.
Embodiment
Described in detail below is to implement current optimal desired pattern of the present utility model.The description should not be in restrictive, sense
To understand, but only it is shown merely for illustrating that the mesh of General Principle of the present utility model is made, because model of the present utility model
Enclose and most preferably limited by appended claims.
Each of various features described below can be used independently of each other or are used in combination with other features.So
And any single feature may not solve any one problem or all problems as discussed above, or may address only
A problem in the problem of text discusses.In addition, one or more of problems discussed above may be completely under
Any one solution in feature described by text.
Fig. 1 in accompanying drawing is shown according to the glof club head 100 of an exemplary of the present utility model
Perspective view.Figure 1 illustrates glof club head 100 generally include main part 102 and hosel part 104, wherein main body
Portion 102 has several parts being individually identified, such as lineback part 106, base part 108, heel part 110 and toe portion
112.Generally included to load golf clubs according to the glof club head 100 of an exemplary of the present utility model
At least one weight adjustment member in first 100 main part 102.In a preferred embodiment, the weight is adjusted
Whole point integratedly can be loaded in main part 102, to ensure in the feelings without departing from the scope of the utility model and content
The weight adjustment member is fixed in main part 102 under shape.Because the weight adjustment member is integratedly loaded high
It is invisible in the described Fig. 1 of these weight adjustment members in the accompanying drawings in the main part 102 of golf ball head 100.However,
When a variety of different views are presented, these weight adjustment members will be illustrated in greater detail in figure later.
Before being moved on subsequent figure, it is worth it is noted that current glof club head 100 is using forging
Make that technique creates and do not need any subsequent fine machining operations with reference to the weight.This will establish an important area
Not, because being extremely hard to realize the identical knot of integratedly loading weight adjustment member using manufacturing process (such as casting) is substituted
Fruit.Alleged " integratedly loading ", which is generally defined as having, such as in current patent application is placed on single external component
Internal specific internal part and there is no joint or seam in the product of completion.As for the utility model, have " integratedly
Weight adjustment member of the loading " in the main part 102 of glof club head 100, which can typically refer to, is not manufacturing work subsequently
Have in the case of the commonly required joint of skill (milling, welding, soldering, bonding or swaged forging etc.) or seam in golf
The ability for the weight adjustment member that the inside of main part 102 of head 100 is placed.
It is also noted herein that in the case of the scope of the utility model and content is not departed from, work as of the present utility model
The weight of " being integratedly fitted into " in preceding definition can potentially have some of exposed weight inside in the product of completion
Aspect, to show the presence of weight adjustment member.More specifically, " integratedly loading " refers to being used to create as described above
Final products method, and may be not necessarily limited to visually hide weight adjustment member.
Fig. 2A-Fig. 2 D are shown for creating the common forging golf according to an exemplary of the present utility model
The method of club head 200.More specifically, Fig. 2A-Fig. 2 D are shown is forged into height in glof club head from its basic blank 201
Involved step in the final product of golf ball head 200.
Fig. 2A shows the preforming blank 201 according to an exemplary of the present utility model.Such as from Fig. 2A
It can be seen that, preforming blank 201 can typically start the cylindrical bar to be formed by the first material, because it is for Gao Er
The forging of husband's club head 200 is common.In order to create the main part 202 that can integratedly load glof club head 200
Interior weight adjustment member 215, one or more chambers 216 are processed in the preforming internal mechanical of blank 201.Show in fig. 2
This current exemplary in, two chambers 216 are machined into the end of preforming blank 201.Preform
The position of chamber 216 in material 201 and geometry are important, because it directly exists with weight adjustment member 215 after forging
Final position association in glof club head 200.
It is moved on Fig. 2 B, it can be seen that once chamber 216 is machined into, with regard to the second material part filled cavity
216, second material has the density different from the density of first material, to create weight adjustment member 215.It is similar
In discussion above, the position of weight adjustment member 215, size, position, the size and shape no less important of shape and chamber 216,
Because weight adjustment member 215 and most final position of the weight adjustment member 215 in glof club head in preforming blank 201
Put association.
Finally, Fig. 2 C are shown when the residual volume of chamber 216 is filled with the first material and passes through Conventional attachment methods
The final stage of preforming blank 201 during (such as welding, soldering and swaged forging) sealing.Annular seal space 216 allows weight adjustment member
215 are integratedly loaded in the main body of preforming blank 201, and this will allow identical weight adjustment portion after forging technology
215 are divided integratedly to load in the main body 202 of glof club head 200.After chamber 216 is filled, pass through preforming blank 201
By the conventional wrought processes associated with the forging of glof club head 200.It is although involved in glof club head 200 is forged
And basic step for understanding that the utility model is important, but it is related to technology that is relatively outmoded and having established, this
Application will be no longer to this too many details of input.On in no basic golf clubs for integratedly loading weight adjustment member
The more information of involved step can be in Cornell United States Patent (USP) No.6,666,779 and Iwata etc. in the forging of head
The United States Patent (USP) No.6 of people, find in 666,779, the Disclosure of U.S. patent, which all passes through to quote, overall combines this
Text.
Although the described above of the forging on golf clubs being incorporated by reference can describe actual forging well
Technique, but it fails solve the additional of the forging process altogether of the present utility model for being related to two kinds of different materials in this forging technology
Concerned issue.More specifically, because weight adjustment member 215 is by can be with the remainder for creating preforming blank 201
Different the second material of the first material be made, it is therefore necessary to pay special attention to ensure that the different materials can be forged one
Rise to form glof club head 200.Therefore, in order to select can forging two kinds of coherency materials together altogether, the first material
Must typically have the very specific material related to their flow stress and their thermal coefficient of expansion to the second material
Attribute specification.Although most preferably described two materials is keep forging uniformity to have identical material property,
It cannot provide basis of the present utility model required any adjustment of weight benefit using identical material.
First, ability together is forged, it is necessary to account properly for every in the material altogether in order to which metal material has
The respective flow stress of kind material.The flow stress of material can typically be defined as making material continuous modification (keep metal
Flowing) needed for stress instantaneous value;And forming coherency forged part by two kinds of different materials will need in the material
Them are subjected to during the stress of forging technology to flow with relatively the same speed.It is generally known that the flow stress of material is general
It is the function of bending strength, the flow stress of material can typically be summarized as below equation (1)
Yf=KenFormula (1)
Wherein
Yf=flow stress (MPa)
The K=coefficients of strain (MPa)
N=strain hardening exponents
Except above formula, it is that the flow stress of material can not be explained in vacuum, phase referred in this to be worth
Instead, it is equally the function of the forging temperature of material.Therefore, in a present exemplary embodiment of the present utility model,
First flow stress of first material under its first forging temperature be substantially similar to but unlike that the second material its
The second flow stress under two forging temperatures;Wherein described first forging temperature and second forging temperature are generally classes
As.More specifically, in a more detailed embodiment, first material can be the forging temperature at about 1200 DEG C
1025 steel of lower the first flow stress with about 10ksi (thousand pounds/square inch) of degree, and second material can be
The niobium material of the second flow stress with about 12ksi under 1100 DEG C of forging temperature.
Although in exemplary of the present utility model as described above, first material can be 1025
Steel and second material can be niobium material, but can also in the case of the scope of the utility model and content is not departed from
Using various other materials, as long as their flow stress is similar under similar forging temperature.In other words, it is as long as described
Second flow stress is not higher than or 20% not less than first flow stress, then any two material may be incorporated for
In current common forging process.
As previously mentioned, in addition to flow stress, the thermal coefficient of expansion of the first material and the second material is for two kinds
The appropriate forging altogether of different materials is also important.More specifically, the first thermal coefficient of expansion of the first material may typically need greatly
In or equal to the second material the second thermal coefficient of expansion.Because thermal coefficient of expansion is also relevant with the contraction of material after forging,
It is important that there is the first material for integratedly loading the second material higher thermal coefficient of expansion to prevent on the boundary of the material
Facial office forms gap.In one of the present utility model more detailed embodiment, the first material can be had about
1025 steel of 8.0 μ in/in °F the first thermal coefficient of expansion, and the second material can be with about 3.94 μ in/in °F the
The niobium of two thermal coefficient of expansions.
It should be noted that although the second thermal coefficient of expansion described in foregoing exemplary embodiment is less than first thermal expansion
Coefficient, but in the case of the scope of the utility model and content is not departed from, the numeral can be identical to realize
State the perfect matching between two kinds of materials.In fact, in an exemplary of the present utility model, can be preferable
It is that the first material and the second material have identical thermal coefficient of expansion, because internally excessive shrink can on material for exterior material
Potentially to produce additional stress in the interface portion office of described two materials.
Alternatively, attempt to provide different weight characteristics, the second material can be made up of 6-4 titanium material to reduce weight tune
Whole point 215 of weight.The titanium material can typically have about 10ksi flowing under about 1100 DEG C of forging temperature
The thermal coefficient of expansion of stress and about 6.1 μ in/in °F.
Now, forging technology has been discussed and has been related to the special attention problem of the common forging of different materials, in accompanying drawing
Fig. 2 D show the perspective view of glof club head 200 of the more than use completion that common forging process creates, the wherein golf clubs
First 200 integratedly load at least one weight adjustment member 215 in main part 202.More specifically, of the present utility model
In present exemplary embodiment, weight adjustment member 215 is placed on the heel part 210 and toe of glof club head 200
Divide near 212.Weight adjustment member 215 is placed around allowing glof club head 200 to exist in heel part 210 and toe portion 212
There is increased moment of inertia (MOI) in the case of not needing any auxiliary attachment operation;This will be when with golf ball
Produce more consistent sensation.
It is noticeable herein before carrying out being related to discussion the utility model of the utility model different embodiments example
It is that weight adjustment member 215 is placed exactly in each single difference in the main part 202 of glof club head 200
Club head in it is slightly different, this is the achievement for the common technique of the utility model for being related to different materials.More specifically, weight is adjusted
Whole point 215 of accurate placement can be different with each single glof club head 200, because first material and described
The flow stress of second material will be helpful to determine the final position of weight adjustment member 215.In addition to above, it should be noted that
Interface between the weight adjustment member 215 and main part 202 of glof club head 200 typically can be irregular interface,
With uneven border to show that whole glof club head 200 is forged altogether.This is markedly different from via follow-up machine
The chamber that tool processing auxiliary operation (such as milling and drilling) creates;Subsequent mechanical processing auxiliary operation typically has two kinds of differences
The clear Y-track of material.
Scheme attached Fig. 3 A- Fig. 3 D and show an alternate embodiment of the present utility model, the single weight of two of which
Adjustment member 314 and 315 is placed at the diverse location of preforming blank 301, to create the height with different performance standard
Golf ball head 300.More specifically, the glof club head 300 shown in Fig. 3 D can be in the top line of glof club head 300
Part 306 is nearby with weight with lightweight weight adjustment member 314 and near the substrate 308 of glof club head 300
Level weight adjustment member 315, to help to make center (CG) skew of glof club head 300 lower, to contribute to this practicality new
The service characteristic and revolving property of the glof club head 300 of type.
With above similar, Fig. 3 A- Fig. 3 C show the forming process of glof club head 300 of the present utility model, the shape
Into process since preforming blank 301.More specifically, Fig. 3 A are shown according to an exemplary embodiment party of the present utility model
The perspective view of the preforming blank 301 of case, wherein drilling out multiple chambers 316 at key position in blank 301.It should be noted that
It is, in this current exemplary, at the top of preforming blank 301 and bottom point nearby rather than every
Individual end drills out multiple chambers 316 because this specific embodiment focus on by by weight from the top of glof club head 300
Line part 306 is removed to reduce the center of gravity of glof club head 300 and make center of gravity towards the basal part of glof club head 300
Divide 308 skews.
Fig. 3 B of accompanying drawing show two recanalization parts 314 and 315 inside the chamber 316 placed and created in figure 3 a.
Although when expectation lowers the center of gravity CG, the weight near top that may be it typically would be desirable to make glof club head 300 minimizes,
But it can not be complete empty that chamber 316 is pushed up in current embodiment of the present utility model, because whole preforming blank 301 will
The final shape for being forged into glof club head 300, this can cause any empty chamber 316 itself to collapse.Therefore, in this practicality
In this new present exemplary embodiment, the filling of lightweight weight adjustment member 314 top chamber 316 can be used, and can be used
Heavyweight weight adjustment member 315 fills cavity of resorption 316.Lightweight weight adjustment member 314 typically can be by with triple density
The 3rd material be made, its middle heavyweight weight adjustment member 315 can typically be made up of the second material with the second density.
In an exemplary of the present utility model, the triple density may be generally less than about 7.0g/cc, wherein institute
About 7.8g/cc can be typically more than by stating the second density;And it is used for the of main part 302 to form glof club head 300
One material can typically have about 7.8g/cc the first density.
Fig. 3 C of accompanying drawing show the terminal stage of preforming blank 301, and the preforming blank 301 has had integratedly
The weight adjustment member 314 and 315 loaded in the inner chamber 316 of preforming blank 301.More specifically, what is shown in Fig. 3 C is pre-
The establishment of shaping blank, which is related in the residual volume of chamber 316, fills the first material, and weight adjustment member 315 and 316 is filled
Enter in preforming blank 301.Similar to described above, the preforming blank 301 is then forged what is shown to create in Fig. 3 D
Glof club head 300, wherein weight adjustment member 314 and 315 are integratedly loaded the main part of glof club head 300
In 302.
Similar to method as described above, the intracavitary formed in the first material forges the 3rd material, the 3rd material altogether
It may typically need with threeth flow stress similar with the first flow stress of the first material and less than the first material
3rd thermal coefficient of expansion of the first thermal coefficient of expansion.More specifically, in an exemplary of the present utility model, institute
It can be 6-4 titanium material to state the 3rd material, and the 6-4 titaniums material has about 10ksi under about 1100 DEG C of forging temperature
The 3rd flow stress, and with about 6.1 μ in/in °F the 3rd thermal coefficient of expansion.
Of the present utility model it is respectively used to realize higher MOI and relatively low CG although Fig. 2A-Fig. 2 D and Fig. 3 A- Fig. 3 D are shown
Different embodiments, but these features are not repelled each other.In fact, this practicality shown in Fig. 4 A- Fig. 4 D
In another new alternate embodiment, feature can be derived from two embodiments discussed above, to create with higher
The glof club head of MOI and relatively low CG common forging, all without departing from the scope of the utility model and content.More specifically,
Shown in Fig. 4 A- Fig. 4 D and lightweight weight adjustment member 414 is combined near the top 406 in Gao Er club heads 400, even
With combining two or more heavyweight weight adjustment members near the toe portion 412 of glof club head 400 and heel 410
415 step needed for golf clubs of the establishment with higher MOI and relatively low CG.
Fig. 5 A- Fig. 5 D of accompanying drawing show another alternate embodiment of the utility model, wherein glof club head 500
Main part 502 can include the weight adjustment member 514 that integratedly loads.It is real in this present exemplary of the present utility model
To apply in scheme, weight adjustment member 514 can have relatively large size, once forging technology is completed, it is allowed to and the weight adjusts
Part replaces the major part of the main part 502 of glof club head 500.It is real in this current Alternative exemplary of the present utility model
Apply in scheme, the weight adjustment member 514 integratedly loaded can typically be made up of the 3rd material with triple density, described
Triple density is substantially less than the first density of the first material of the main part 502 for being used to be formed glof club head 500;Allow
Weight is taken out from the main part 502 of glof club head 500.Because the lightweight for forming weight adjustment member 514
3rd material is general relatively soft compared with the first material, so it typically would be desirable to weight adjustment member 514 is integratedly loaded to height
In the inside subject of golf ball head 500, this allows the notable mitigation that weight is realized in the case of sensation is not sacrificed.
More specifically, Fig. 5 A of accompanying drawing are similar to previous figure, preforming blank 501 is shown.However, currently show herein
In example property embodiment, the chamber 506 in preforming blank 501 itself is significantly larger.Then can be big using this in figure 5b
Chamber 506 carrys out filling weight adjustment member 514 to adjust the weight of glof club head 500, density and common sensation.In Fig. 5 C
In, similar to described above, the residual volume of chamber 516 is filled with the first original material, afterwards whole preforming blank
501 are subjected to forging technology to create glof club head 500.
It is to be noted here that in this present exemplary embodiment, the hosel part of glof club head 500
504 are specially made of the first material of routine, because the flexural property one of the second material for forming weight adjustment member 514
As may be not suitable for the bending requirement of iron golf club head 500.More specifically, for forming weight adjustment member 514
3rd material can be with close less than 7.10g/cc, even more preferably less than 7.05g/cc and more preferably less than 7.00g/cc
The lightweight iron aluminum of degree, all without departing from the scope of the utility model and content.It is however, of the present utility model not departing from
In the case of scope and content, many other materials can also be used as the 3rd material for forming weight adjustment member 514
Material, as long as the 3rd material has the density in scope described above.
Fig. 6 of accompanying drawing is shown utilizes the common forging process of multi-step according to another alternate embodiment of the present utility model
Glof club head 600 exploded rear perspective view.This multi-step described in Fig. 8-Figure 14 is then total to the details of forging process,
Forging process allows improvement to be placed exactly in different weight component in the different piece of glof club head 600 to this multi-step altogether
Ability.This improvement of the accurate ability for placing weighted is not only that allow together to provide the forging of a variety of different materials can
Can-due to the intrinsic material limitation of different materials, therefore be previously impossible together by the forging of a variety of different materials, and
And also allow the performance characteristics of golf clubs 600 than previously having bigger improvement.
More specifically, Fig. 6 of accompanying drawing is shown using the multi-step common forging glof club head 600 that forging process creates altogether.
Glof club head 600 has corresponding to the corresponding of them at the heel part 610 and toe portion 612 of glof club head 600
Chamber 616 greater density weight adjustment member 615.Then weight adjustment member 615 is combined with common forging process with lid 617
Period makes weight adjustment member 615 and the main body of glof club head 600 keep together.It should be noted that present exemplary Gao Er
Husband's club head 600 installs the weight adjustment member 615 of weight using the common forging process of multi-step, is manufactured without subsequent fine, all
Such as welding, soldering, swaged forging.As previously mentioned, using it is such altogether forging process benefit be material uniformity with it is consistent
Property, this brings superior performance and sensation.It is of the present utility model current however, in addition to the removal clearly expressed above
Embodiment allows the end that the adjustment of weight part 615 of weight is placed on to glof club head 600, This further improves
The position of centre of gravity and moment of inertia of glof club head 600.
Fig. 7 of accompanying drawing is shown according to the glof club head 700 of another alternate embodiment of the present utility model
Exploded front perspective view.More specifically, in multi-step altogether forging process, glof club head 700 is hit glof club head 700
Beat and combine lightweight weight adjustment member 714 behind the part of face 718 in chamber 716.In this present exemplary of the present utility model
Property embodiment in, due to accurately forging process altogether discussed above, therefore can more accurately arrange lightweight weight adjustment portion
Divide 714 position and layout, therefore create the chance of the weight for the part of impact surface 718 for reducing glof club head 700.For
Understanding current multi-step forging process altogether, it is involved in this multi-step altogether forging process to be described in detail following present Fig. 8-Figure 14
Step.
Similar to figure 2 above-Fig. 5, Fig. 8 of accompanying drawing shows the preforming blank for creating forging glof club head
801.This forging blank 801 is then bent to L-shaped as shown in Figure 9, so that blank 901 prepares to be used to start the forging
The mould of technique.Figure 10 A and Figure 10 B show the glof club head for the first step for being already subjected to the common forging process of multi-step
1000 front view and rearview.In this earlier step, the blank has been forged into and glof club head 1000
The substantially similar shape of shape.In fact, even if in this early stage, it can also be seen that the shape of glof club head 1000,
Because it has hosel part 1004, heel part 1010 and toe portion 1012.The glof club head shown in Figure 10 A
In 1000 rearview, the first of chamber 1016 has been can see in the heel part 1010 and toe portion 1012 of glof club head
Vestige is walked, and can be seen in the front view of the glof club head 1000 shown in fig. 1 ob near impact surface
Chamber 1016.
After initially forging step, excessive trimming 1030 can remove from glof club head 1000, and after this
Another rough forging step is subjected to afterwards.During the forging technology, excessive material can flow to the outer of the boundary of mould
Portion, this causes commonly called " overlap ".This overlap material as previously discussed can be trimmed between each more forging steps
Material, to improve the adhesion in later step to mould.
The result of this auxiliary forging step can be illustrated in Figure 11 A and Figure 11 B.Such as since Figure 11 A and Figure 11 B
Arrive, the glof club head 1100 under current state starts to present and the closer shape of final products.Except more limited
Outside fixed overall shape, the border of chamber 1116 and shape also begin to that their own shape is presented.After this auxiliary forging step
Afterwards, weight adjustment member can be added in specific chamber 1116, and glof club head 1100 is subjected to finally forging afterwards
Step.
The weight adjustment for the chamber 1116 that can be shown more clearly that in figs. 12 a and 12b on glof club head 1100
Relation between part.Here, in figs. 12 a and 12b, it can be seen that on the rear part of glof club head 1200
Chamber 1216 can be filled with weight adjustment member 1215, and the weight adjustment member 1215 can typically have than golf clubs
The higher density of first 1200 main body.Then can be with made of the material similar with the main body of glof club head 1200
The upper high density weight adjustment member 1215 of the covering of lid 1217, this allows high density weight adjustment member 1215 being maintained at chamber 1216
It is interior.Before glof club head 1200, chamber 1216 can be filled with the main part with than glof club head 1200
Divide the weight adjustment member 1214 of lower density.Similar to below, this weight adjustment member 1214 can be consolidated with lid mechanism
It is scheduled in chamber 1216, the lid mechanism also serves as impact surface 1218.Similar to lid 1217, impact surface 1218 can by with golf
The material that the main body of club head 1200 is similar is made.Make lid 1217 and impact surface 1218 by the main body with glof club head 1200
Remainder identical material to be made be favourable because it allows both parts being welded to glof club head 1200
Main part.These parts is welded to appropriate position allows to walk in the final forging for completing the common forging process of current multi-step
Weight adjustment member 1215 is fixed in the corresponding chamber 1216 of themselves before rapid.
In an alternate embodiment of the present utility model, even the He of chamber 1216 can need not be completely covered in lid 1217
Weight adjustment member 1214.In fact, in an alternate embodiment of the present utility model, lid 1217 only needs part to cover
Weight adjustment member 1215 is to being enough the degree for preventing that weight adjustment member 1215 from separating with the main body of glof club head 1200.
The final forging technology being related in this process, which generally creates, is considered " forging altogether " glof club head
1200, because present glof club head 1200 contains two or more differences being forged in this final step together
Material.Figure 13 A and Figure 13 B show result of the glof club head 1300 after the final step of forging altogether of its completion.It is current at its
Under state, its presented net shape of glof club head 1300, and weight adjustment member 1316 and 1314 is present all
Their own intracavitary is integratedly loaded by lid 1317 and impact panel 1318.Although glof club head 1300 can be taken
Their form, there are still excessive overlap 1330, the excessive overlap around the periphery of glof club head 1300
1330 need glof club head 1300 after being trimmed to about that its net shape is presented.
Figure 14 A and 14B show result of the glof club head 1400 of completion as this common forging process.Here, scheming
It can be seen that, excessive overlap 1330 has been trimmed to about, and improves the aesthetic feeling of glof club head 1400 in 14A and Figure 14 B.Such as
It is previously mentioned, the result of forging process is total to as this, weight adjustment member 1416 and 1418 passes through lid 1417 and impact panel
1318 seamlessly and integratedly load the main body of glof club head 1400.As previously discussed, being total to forging process by this makes weight
The advantages of measuring adjustment member 1416 seamlessly and integratedly loading the main body of glof club head 1400 is to prevent from sending quack sound,
And improve the solid sensation of glof club head 1400.In fact, using this technique, current glof club head can be with
Realize the hardly recognizable sensation of glof club head with the single forging using conventional forging method.
Or it may also be said that multi-step forges the chamber that method is located in weight adjustment member 1416 and 1418 with it altogether at present
The relation of uniqueness is created between 1216 (see Figure 12).More specifically, it may be said that the exterior surface area of weight adjustment member 1416
Typically can be identical with the inner surface area of chamber 1216.Chamber 1216 can typically include being used to complete to create by rough forging step
Any lid 1217 of chamber 1216 or the surface area of panel 1218.(referring to Figure 12) is although chamber 1216 and weight adjustment member
Symmetric shape and surface area between 1416 may be not as innovation achievement, and real situation is, unless it is related to common forging step,
Otherwise such seamless interface between the two elements is impossible.In view of the difference for glof club head
Partial material bonding constraint, the common forging method currently innovated be between these components realize as seamless interface only
One method.
Figure 15 of accompanying drawing shows the previously described forging altogether of utilization according to an alternate embodiment of the present utility model
The front view of the product glof club head 1500 of the completion of technology.In this embodiment, striking face insert 1518 only may be used
Partly to cover the lower part of glof club head 1500, this permission only creates in the lower part of glof club head 1500
Chamber.This specific bifurcated of club head 1500 can be beneficial to the property that glof club head 1500 is improved in two-chamber design is created
Can, the two-chamber design has been provided about structural support in the center hemisphere of club head 1500, more solid to be provided when hitting
Sensation.
Figure 16 of accompanying drawing shows the glof club head without striking face insert 1518 (showing in fig.15)
1600 front view.This view of glof club head 1600 allows to be shown more clearly that inside face chamber 1616, and showing can be with
For further providing multiple support bars 1630 of structural support for striking face portion.In one embodiment, multiple bars
1630 can be the circular pin for the whole inwall for being dispersed in face chamber 1616 as shown in Figure 16.However, in other embodiments
In, multiple bars 1630 even can not be cylinder, but square, rectangle or any other shape, do not take off all
From the scope of the utility model and content, as long as it provides any kind of localization support for impact surface.Except bar 1630
Outside the change of geometry, the placement of bar 1630 needs not be the whole inwall for being distributed on face chamber 1616, in fact, bar
1630 position can be placed on any one opening position in many positions, all without departing from the scope of the utility model and
Content.Finally, it should be noted that in an alternate embodiment of the present utility model, face chamber 1616 even can need not be any
Support bar 1630, and in the case of the scope of the utility model and content is not departed from, face chamber 1616 can be completely hollow
's.
Figure 17 of accompanying drawing shows the golf according to embodiment of the present utility model shown in Figure 15 and Figure 16
The decomposition diagram of club head.More specifically, this decomposition view allows the impact for being shown more clearly that glof club head 1700
Relation and assembling between face insert 1718 and face chamber 1716.It should be noted that referred to although discussing earlier using forging process altogether
Different metal will not be able to be easily welded together links together, but the main body of glof club head 1700 and
Connection between striking face insert 1718, which is related to, may cause during striking face insert 1718 deforms during forging technology
The empty part of face chamber 1716.Fortunately, in current embodiments, the material for striking face insert 1718 can be similar
In the material of main part 1700, this allows to use conventional soldering techniques after miscellaneous part to be total to forging together by described two
Individual part links together.
Another for being worth identification is characterized in the length of multiple bars 1730.In order to provide structure for striking face insert 1718
Support, multiple bars 1730 can typically contact the rear surface of striking face insert 1718.Or the it can be said that end of multiple bars 1716
The rear surface that end can contact striking face insert 1718 is strengthened with providing structure.However, in an alternative embodiment, it is more
The end of individual bar 1716 can not just reach the rear surface termination of striking face insert 1718, create a gap;When with height
Promote face flexure when golf ball is hit, at the same after creating backstop (backstop) to keep the bullet of the material of striking face insert 1718
Property deformation.
Figure 18 of accompanying drawing is shown with using above-described one or more weight that forging process links together altogether
1815 and lid 1817 glof club head 1800 rearview.Above-described technique is not repeated, Figure 19-Figure 20 will be shown
By using the above-described toe for a variety of parts that forging process creates altogether and with decomposition view.
Figure 19 shows the toe perspective view of the decomposition of glof club head 1900, shows according to this reality of the present utility model
Apply a variety of parts of the Weighting system of scheme.The decomposition view of glof club head 1900 is not intended to create the side of Weighting system
Method is shown, but is presented at this to illustrate how to be used together the part in above-described forging process altogether to create height
Golf ball head 1900.More specifically, the Weighting system includes weight chamber 1916, weight 1915, lid 1979 and welding material herein
Material 1920.Weight chamber 1916 is formed at this in rough forging step, after this, will weight with lid 1917 using welding material 1920
1915 positioning weldings are measured in weight chamber 1916.After a variety of parts are cursorily connected to each other, whole glof club head
1900 are subjected to such as the final forging step described in Figure 13 A and Figure 13 B above.
Figure 20 show the decomposition of golf clubs 2000 with perspective view, show according to this implementation of the present utility model
A variety of parts of the Weighting system of scheme.Similar to the discussion above with respect to Figure 19, there is provided this view with show the part it
Between relation.
In addition to the above, the current multi-step forges method and is different from that it can be no longer in place of the pure method of forging altogether altogether
It is required that two kinds of materials have similar flow stress between different materials.Eliminating the need for material has similar flowing should
This requirement of power can be beneficial, because it allows the material using wider range, particularly when its use provides pole
It is even more so during special material (such as tungsten) of the counterweight benefit at end.The method of forging can be by using altogether for the current multi-step
Before weight adjustment member is entirely encapsulated in lid types of material by the gap around final lid types of material filled cavity, forging
The chamber for the weight is made to realize this purpose.Although eliminate the need for the material with similar flow stress
Will, but in this multi-step altogether forging method, remain that the thermal coefficient of expansion of the second material is less than the first material.It is this to want
It is still existing to ask, although because second material is included in intracavitary via lid, is still subjected to the with outside
One material identical forging temperature.Any excessive expansion of second material will reduce the rigidity of structure of the lid, cause to be bonded
Potentially failed in method.
Figure 21 of accompanying drawing is shown to be divided according to the glof club head 2100 of an alternate embodiment of the present utility model
Diagrammatic view.According in this alternate embodiment of the present utility model, glof club head 2100 can contain with being previously described
Very similar part, such as with multiple high density weight adjustment members similar on Fig. 6 and Fig. 7 discussion in the early time
2115th, multiple lids 2117, lightweight weight adjustment member 2114 and impact surface 2218.However, it can here be seen that lightweight weight
Amount adjustment member 2214 seems to be that it now incorporates elder generation with the significant difference of the embodiment of prior art herein
Preceding unshowned unique geometry.More specifically, lightweight weight adjustment member, which is also wrapped, to be shown to more going through for Figure 21
Include multiple otch 2140 across lightweight weight adjustment member 2114.It is it is to be noted here that current exemplary herein
The multiple otch 2140 shown in embodiment can substantially uniformly divide across whole lightweight weight adjustment member 2114
Cloth, to promote the uniform bonding between a variety of parts, without departing from the scope of the utility model and content.By this knot of otch 2140
Close in lightweight weight adjustment member in many-sided performance for improving glof club head.On the one hand, with reference to multiple
The most direct and recognizable benefit of otch 2140 is that the weight of lightweight weight adjustment member 2114 is further reduced.Except
Outside the benefit for removing weight from lightweight weight adjustment member 2114, multiple otch 2140 can be used for trickle but extremely important
Purpose --- help lightweight weight adjustment member avoid its position relative to glof club head 2100 and impact surface 2128
Skew.
It should be understood that current glof club head 2100 is created using forging process altogether as described above, a variety of portions
The ability that part is formed in (solidary) structure of close concern to each other together for overall club head 2100 normal function very
It is important.When insert is added near the striking face portion 2128 in glof club head 2100, this structural intergrity becomes very
To more important.In order to assist in keeping the structural intergrity of a variety of parts, multiple otch 2140 allow some materials of impact surface 2128
Material is flow in otch 2140, creates the more preferable bonding between different parts.This deformation of the material of impact surface 2128 passes through
Material is prevented to offset relative to each other to help to improve the bonding between part via mechanical interface, which increase structural integrity
Property.Finally, because main part is made of the material similar with striking face portion 2128, so by striking face portion 2128
This anamorphic effect of displaying can occur in the rear surface of lightweight weight adjustment member 2114 and glof club head 2100
Main body at, without departing from the scope of the utility model and content.
In the embodiment in the early time of the present utility model shown in figure 6 and figure 7, titanium lightweight face insert 714 will have
There is about 21 grams of gross weight;However, figure 21 illustrates current exemplary of the present utility model in, light weight
The gross weight of level weight adjustment member 2114 can be reduced more than about 13%, more preferably greater than about 15% and most preferably
Ground is more than about 17%, all without departing from the scope of the utility model and content.Wherein using above has about 4.5g/
cm3Density titanium material identical embodiment in, lightweight weight adjustment quality can be less than about 18.5 grams, more preferably
Ground is less than about 17.5 grams and most preferably less than about 17 grams, all without departing from the scope of the utility model and content.
Figure 22 of accompanying drawing is shown similar to the discussion in Figure 21 according to an alternate embodiment of the present utility model
Glof club head 2200 reversion decomposition view.Inverted at this in decomposition view, dispose lightweight weight adjustment member
2214 chamber 2216 can be perhaps shown more clearly.It is to be noted here that otch 2240 is in this example of the present utility model
Property embodiment in typically can have it is round-shaped, have between about 1.0mm and about 3.0mm, more preferably big
Between about 1.50mm and about 2.5mm and most preferably about 2.0mm diameter.The accurate diameter of otch 2240 is for lightweight
The normal function of weight adjustment member 2214 is most important, because the weight that it does not need only provide for sufficient amount is reduced, Er Qiexu
It is correctly balanced the amount that sandwich material is penetrated into otch 2240.Although preferred embodiment of the present utility model utilizes circular shape
Shape creates otch 2240, but many other shapes such as ellipse, triangle, rectangle or can be from the lightweight weight
Adjustment member 2214 removes any other shape of material, all without departing from the scope of the utility model and content.Quantization is looked for
Another different modes to the importance of the correct balance of the size of otch 2240 are the amounts according to the surface area of removal.At this
In the current exemplary of utility model, the amount of the front surface area removed by otch 2240 can typically be more than
About the 15% of total surface area and about 30% less than total surface area, it is more preferably larger than total surface area about
17.5% and less than total surface area about 27.5% and most preferably more than total surface area about 20% and less than total
About the 25% of surface area.Assuming that impact surface area is in current exemplary of the present utility model
2400mm2, it may be said that the front surface area created in lightweight weight adjustment member 2214 by otch 2240 typically can be
About 360mm2With less than about 720mm2Between, more preferably greater than about 420mm2And it is less than about 660mm2And most preferably
Ground is more than 480mm2And it is less than about 600mm2。
In order to show that the sandwich material of the main part of glof club head 220 and impact surface 2218 enters otch 2240,
The viewgraph of cross-section of offer glof club head 2200 is provided.However, before it can show a viewgraph of cross-section, Figure 23 shows
The front view of glof club head 230 is gone out, it is allowed to which transversal upper thread A-A ' is shown.Transversal upper thread A-A ', it is such as current herein to show
Show in example property embodiment, can typically be taken across the central point in the impact surface region of the glof club head 2300
.
Transversal upper thread A-A ' that Figure 24 is shown in showing along Figure 23 obtain according to an example of the present utility model
The viewgraph of cross-section of the glof club head 2400 of property embodiment.In this viewgraph of cross-section of glof club head 2400,
It can be seen that otch 2440 deploys along lightweight weight adjustment member 2414 and is clipped in the back of glof club head 2400
Divide between impact surface 2418.Although Figure 24, which provides one, allows the relation being shown more clearly that between a variety of parts very
Important view, but it is not amplified to and is enough to show to contribute to as overall height during above-described last forging process altogether
Golf ball head 2400 provides the trickle material flowing of the rigidity of structure.In order to show this, golf clubs is provided in fig. 25
The viewgraph of cross-section of the amplification of head.
Figure 25 of accompanying drawing shows the glof club head 2500 according to an exemplary of the present utility model
Amplification viewgraph of cross-section.In the viewgraph of cross-section of this amplification of glof club head 2500, it can be seen that last
Forging step after, some materials of impact surface 2518 have visually been trapped in otch 2540.On it should be noted that
The very vital size of the otch 2540 of text instruction allows this slight deformation in the back side of impact surface 2518, does not make
The preceding areal deformation of impact surface 2518.In addition to the deformation of impact surface 2518, Figure 25 of accompanying drawing also show in chamber 2516
Locate the deformation of the main part of glof club head 2500 below.It should be noted herein that this is current of the present utility model
In exemplary, the deformation of impact surface 2518 is more than the main part for locating glof club head 2500 behind chamber 2516
The deformation divided, to ensure the bigger rigidity of structure.Except front and rear uneven deformation, the main part of glof club head 2500 and hit
Beating face 2518 can also be with uneven deformation from the top to bottom.More specifically, according to one of the present utility model replacement embodiment party
The glof club head 2500 of case can have more large deformation typically at the top near top line than the bottom near substrate
Otch 2540.
In an alternate embodiment of the present utility model, multiple otch 2540 can be completely filled with or partly fill out
Fill or the material full of polymer type.It can hit with the material filling otch 2540 of polymer type by providing vibration damping
The sensation of glof club head 2500 is improved during putt.Polymer fill can be completely filled with otch 2540 or
Otch is partially filled with, the two is all without departing from the scope of the utility model and content.Of the present utility model wherein with polymerization
Thing is completely filled with this alternate embodiment of otch 2540, it is important that the hardness of polymer is controlled, because hardness may
Damage impact surface 2518 and main part creates the ability of mechanical caging.In an exemplary of the present utility model
In, the polymer fill in otch 2540 can be with 20 hardness of Shore 00 and up to 60 Shore D hardness.
Except operation embodiment or unless otherwise expressly provided, otherwise whole digital scope, amount, value and percentage
Such as the amount of material, moment of inertia, position of centre of gravity, high strike inclined-plane, design angle, different performances than those, and
Other in specification preceding sections can be read as be both by the use of wording " about " as prefix, even if term " about " does not have
Have and clearly appear in described value, amount or scope.Therefore, unless the contrary indication, otherwise superincumbent specification and institute
The digital parameters illustrated in attached claims are approximate, and it can be obtained desired according to sought by the utility model
Attribute and change.At least, and it is not intended that with the principle of equivalence each digital parameters should to limit the scope of claim
At least technology is rounded up to explain according to the numerical value for the effective digital reported and by using common.
Although the digital scope and parameter that illustrate the wide scope of the utility model are approximate, in specific embodiment
In the numerical value that illustrates be reported as precisely as possible to report.But any numerical value is substantially contained by being surveyed in their own test
Some errors that standard deviation present in amount is necessarily formed.In addition, when illustrating the digital scope of excursion herein, can
Any combination of these values comprising described value can be used with expection.
It will of course be understood that foregoing teachings are related to exemplary of the present utility model, and do not departing from as in institute
A variety of modifications can be made in the case of the spirit and scope of the present utility model illustrated in attached claims.
Claims (16)
1. one kind forging glof club head, including:
Main part, the main part are made up of the first material, have face chamber and at least one weight chamber;
At least one high density weight adjustment member, at least one high density weight adjustment member is made up of the second material,
It is loaded into the weight intracavitary;
Lightweight weight adjustment member, the lightweight weight adjustment member are made up of the 3rd material, are loaded into the face intracavitary;
And
Striking face insert, the striking face insert are made up of first material, suitable for covering the face chamber,
Wherein, the lightweight weight adjustment member also includes multiple otch, and
Wherein, the high density weight adjustment member is integratedly loaded the weight intracavitary.
2. forging glof club head according to claim 1, wherein, the multiple otch is across the whole lightweight
Weight adjustment member is substantially uniformly distributed.
3. forging glof club head according to claim 1, wherein, the density of second material is more than described first
The density of material, and the density of wherein described first material is more than the density of the 3rd material.
4. forging glof club head according to claim 3, wherein, at least one weight adjustment member is located at institute
State near the substrate of glof club head.
5. forging glof club head according to claim 4, wherein, at least one weight adjustment member is located at institute
State near the heel part of the substrate of glof club head.
6. forging glof club head according to claim 4, wherein, at least one weight adjustment member is located at institute
State near the toe portion of the substrate of glof club head.
7. forging glof club head according to claim 1, wherein, after common forging process, the impact surface insertion
The rear surface of part deforms to the multiple intracavitary.
8. forging glof club head according to claim 7, wherein, after common forging process, the main part
Deformed on the preceding surface of the face intracavitary to the multiple intracavitary.
9. forging glof club head according to claim 7, wherein, the impact is towards described in the multiple intracavitary
Deformation becomes apparent from the top line part towards the glof club head.
10. forging glof club head according to claim 8, wherein, the main part of the face chamber is to described
The deformation of multiple intracavitary becomes apparent from the top line towards the forging glof club head.
11. one kind forging glof club head, including:
Main part, the main part are made up of the first material, have face chamber and at least one weight chamber;
At least one high density weight adjustment member, at least one high density weight adjustment member is made up of the second material,
It is loaded into the weight intracavitary;
Lightweight weight adjustment member, the lightweight weight adjustment member are made up of the 3rd material, are loaded into the face intracavitary;
And
Striking face insert, the striking face insert are made up of first material, suitable for covering the face chamber,
Wherein, the lightweight weight adjustment member also includes multiple otch, and
Wherein, the multiple otch has round-shaped, described round-shaped between about 1.0mm to about 3.0mm
Diameter.
12. forging glof club head according to claim 11, wherein, round-shaped multiple otch it is described
Diameter is between about 1.5mm and about 2.5mm.
13. forging glof club head according to claim 12, wherein, round-shaped multiple otch it is described
Diameter is about 2.0mm.
14. forging glof club head according to claim 13, wherein, the multiple otch removes the lightweight weight
Measure about 15% to about the 30% of total front surface area of adjustment member.
15. forging glof club head according to claim 14, wherein, the multiple otch removes the lightweight weight
Measure about 17.5% to about the 27.5% of total front surface area of adjustment member.
16. forging glof club head according to claim 15, wherein, the multiple otch removes the lightweight weight
Measure about 20% to about the 25% of total front surface area of adjustment member.