CN109334033A - A kind of dummy slider Shooting Technique based on automobile interior decoration - Google Patents
A kind of dummy slider Shooting Technique based on automobile interior decoration Download PDFInfo
- Publication number
- CN109334033A CN109334033A CN201811066210.5A CN201811066210A CN109334033A CN 109334033 A CN109334033 A CN 109334033A CN 201811066210 A CN201811066210 A CN 201811066210A CN 109334033 A CN109334033 A CN 109334033A
- Authority
- CN
- China
- Prior art keywords
- film
- minutes
- drying
- heat
- injection
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The dummy slider Shooting Technique based on automobile interior decoration that the invention discloses a kind of, comprising the following steps: Step 1: prepared by film: major ingredient each component is used into low temperature drying, 12 hours or more, drying temperature was 50-60 DEG C;Each component is sufficiently mixed, the revolving speed of blender is 600 revs/min, and mixing time is 45 minutes, then that the mixture after stirring is cooling.Advantage is: can decorate more complex three-dimensional surface, Handicraft decorative region can be deeper, and is able to achieve back-off coating;It is with the obvious advantage the performances such as piece surface hardness, wet-heat resisting, wear-resisting, anticorrosive;The film surface that can be used for imitation wood line and metal effect realizes noble surface decoration result, traditional hot stamping effects, electroplating effect, grain effect;Pattern can be quickly carried out, design replacement, color adjustment reach better fidelity;Lower to injection mold requirement, common injection mould is just able to use this technique, and grain effect can be generated out of die cavity: environment friendly and pollution-free.
Description
Technical field
The present invention relates to technical field of automotive trim, specially a kind of dummy slider Shooting Technique based on automobile interior decoration.
Background technique
Automobile interior decoration is primarily referred to as the used automobile product of automotive interior repacking, is related to side's aspect of automotive interior
Face, such as automobile steering wheel cover, automobile cushion, automatic foot-mat, automobile perfume, automobile pendant, internal goods of furniture for display rather than for use, containing box etc. are all
It is automotive interior product, since this partial automobile components has certain dicoration, so common translation at present in the industry
All it is called " automobile interior decoration ", it can be appreciated that this parts thereof not only only has decoration function, the function involved by them
Property, safety and engineering attribute are very abundant.
In-mold decoration is a kind of relatively new automatic production process, and (IMD) can simplify production step compared with traditional handicraft
Building block is disassembled in rapid and reduction, therefore can quickly be produced and be saved time and cost, while also being had and being improved quality, and image is increased
Complexity and improve durability of product advantage apply in product appearance, (IMD) is the method for current full blast, it be
Printing, high-pressure molding, punching are imposed on film surface, finally with plastics connecting shaping, exempt secondary operation program and its manpower
Working hour is especially generally needing the printings spray painting processing procedure such as backlight, more curved surfaces, imitative metal, hair line processing, logic light line and rib cage interference
When can not handling, the opportunity of IMD processing procedure is even more used;
The incrustation of automotive upholstery and the incrustation of casing of domestic electrical equipment, it is main using spraying, water transfer etc.
Process, due to itself being limited by these processes, existing deficiency is mainly manifested in: decorative effect is single
Change, production process is complicated, low efficiency so that product overall cost is higher, generate pollution, not environmentally, influence injection molding efficiency and
Using effect, therefore we have proposed a kind of dummy slider Shooting Techniques based on automobile interior decoration to solve the above problems.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the dummy slider Shooting Technique based on automobile interior decoration that the present invention provides a kind of, has pair
Injection mold requires lower and the advantages that cost is relatively low, solves the problems, such as complex process and green and bright higher.
(2) technical solution
For realize it is above-mentioned lower and cost is relatively low purpose is required to injection mold, the invention provides the following technical scheme:
A kind of dummy slider Shooting Technique based on automobile interior decoration, comprising the following steps:
Step 1: film prepare: by major ingredient each component use low temperature drying, 12 hours or more, drying temperature 50-60
℃;Each component is sufficiently mixed, the revolving speed of blender is 600 revs/min, and mixing time is 45 minutes, then will be mixed after stirring
Material cooling is closed, is cooled to 35 DEG C in 7 minutes, is kept for 30 minutes under being 40% in humidity, is then cooled to 20 in 15 minutes again
DEG C, it is plasticized, the film for being plasticized extrusion immediately is attached directly on chill roll cooling plasticizing forming;
Step 2: film pre-processes: the drying process of 3 hours is carried out to film by drying equipment, then by film
100 DEG C -130 DEG C are heated to, drying to moisture content is not higher than 0.04%;
Step 3: raw material is classified: injection molding thermosetting material and heat-fusible materials will be needed to carry out classification and put in order, then will
Thermosetting material and heat-fusible materials and auxiliary material press the proportion of 5-1, are then mixed object and are added to 270 DEG C~300 DEG C temperature
Melting is carried out in degree smelting equipment;
Step 4: being molded: by step 3 be made raw material be put into injection molding machine, by equipment be heated to 300 DEG C-
360 DEG C, raw material is molded, guarantees injection pressure in 30-40MPa, by the heat of the thermosetting material injection mold after injection molding
Fixed end, by the hot melt end of the heat-fusible materials injection mold of melting, after the completion of material injection, opening injection molding machine makes hot melt in mold
Property material and thermosetting material merged, fusion stood after twenty minutes;
Step 5: being cooled and shaped: material obtained in step 4 is put into vacuum pressure equipment and has suffered cooling and shaping, it is cooling
Time is 40 minutes;
Step 6: slice molding: raw material obtained in step 5 being printed off to the figure of needs using printing equipment, using just
The method of pressure plus vacuum makes the substrate be processed into required shape;After cutting away extra side using laser cutting device, it is put into
It is projected in mold.
(3) beneficial effect
Compared with prior art, the dummy slider Shooting Technique based on automobile interior decoration that the present invention provides a kind of, having following has
Beneficial effect:
More complex three-dimensional surface can be decorated, Handicraft decorative region can be deeper, and is able to achieve back-off coating;Piece surface is hard
It is with the obvious advantage the performances such as degree, wet-heat resisting, wear-resisting, anticorrosive;It can be used for the film surface of imitation wood line and metal effect, realize high
Expensive surface decoration result, traditional hot stamping effects, electroplating effect, grain effect;Pattern, design replacement, color can quickly be carried out
Adjustment, reaches better fidelity;Lower to injection mold requirement, common injection mould is just able to use this technique, and can be from mould
Intracavitary generation grain effect: environment friendly and pollution-free;It can make local dress with plastic covering current mark defect, more stable color adjustment
Decorations.
Detailed description of the invention
Fig. 1 is a kind of dummy slider Shooting Technique flow chart based on automobile interior decoration proposed by the present invention.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment one
Referring to Fig. 1, a kind of dummy slider Shooting Technique based on automobile interior decoration, which comprises the following steps:
Step 1: prepared by film: major ingredient each component being used low temperature drying, 12 hours or more, drying temperature was 50 DEG C;It will
Each component is sufficiently mixed, and the revolving speed of blender is 600 revs/min, and mixing time is 45 minutes, then by the mixture cold after stirring
But, 35 DEG C are cooled in 7 minutes, are kept for 30 minutes under being 40% in humidity, 20 DEG C is then cooled in 15 minutes again, by it
It is plasticized, the film for being plasticized extrusion immediately is attached directly on chill roll cooling plasticizing forming;
Step 2: film pre-processes: the drying process of 3 hours is carried out to film by drying equipment, then by film
100 DEG C of C are heated to, drying to moisture content is not higher than 0.04%;
Step 3: raw material is classified: injection molding thermosetting material and heat-fusible materials will be needed to carry out classification and put in order, then will
Thermosetting material and heat-fusible materials and auxiliary material press the proportion of 5-1, are then mixed object and are added to 270 DEG C of C temperature meltings
Melting is carried out in equipment;
Step 4: being molded: it is put into raw material is made in step 3 in injection molding machine, equipment is heated to 300 DEG C, it will
Raw material is molded, and guarantees that injection pressure will melt at the thermosetting end of the thermosetting material injection mold after injection molding in 30MPa
Heat-fusible materials injection mold hot melt end, material injection after the completion of, open injection molding machine make heat-fusible materials and heat in mold
Thermoset material is merged, and fusion is stood after twenty minutes;
Step 5: being cooled and shaped: material obtained in step 4 is put into vacuum pressure equipment and has suffered cooling and shaping, it is cooling
Time is 40 minutes;
Step 6: slice molding: raw material obtained in step 5 being printed off to the figure of needs using printing equipment, using just
The method of pressure plus vacuum makes the substrate be processed into required shape;After cutting away extra side using laser cutting device, it is put into
It is projected in mold.
Embodiment two
Referring to Fig. 1, a kind of dummy slider Shooting Technique based on automobile interior decoration, which comprises the following steps:
Step 1: prepared by film: major ingredient each component being used low temperature drying, 12 hours or more, drying temperature was 55 DEG C;It will
Each component is sufficiently mixed, and the revolving speed of blender is 600 revs/min, and mixing time is 45 minutes, then by the mixture cold after stirring
But, 35 DEG C are cooled in 7 minutes, are kept for 30 minutes under being 40% in humidity, 20 DEG C is then cooled in 15 minutes again, by it
It is plasticized, the film for being plasticized extrusion immediately is attached directly on chill roll cooling plasticizing forming;
Step 2: film pre-processes: the drying process of 3 hours is carried out to film by drying equipment, then by film
115 DEG C are heated to, drying to moisture content is not higher than 0.04%;
Step 3: raw material is classified: injection molding thermosetting material and heat-fusible materials will be needed to carry out classification and put in order, then will
Thermosetting material and heat-fusible materials and auxiliary material press the proportion of 5-1, are then mixed object and are added to 285 DEG C of temperature meltings and set
Standby middle carry out melting;
Step 4: being molded: it is put into raw material is made in step 3 in injection molding machine, equipment is heated to 330 DEG C, it will
Raw material is molded, and guarantees that injection pressure will melt at the thermosetting end of the thermosetting material injection mold after injection molding in 35MPa
Heat-fusible materials injection mold hot melt end, material injection after the completion of, open injection molding machine make heat-fusible materials and heat in mold
Thermoset material is merged, and fusion is stood after twenty minutes;
Step 5: being cooled and shaped: material obtained in step 4 is put into vacuum pressure equipment and has suffered cooling and shaping, it is cooling
Time is 40 minutes;
Step 6: slice molding: raw material obtained in step 5 being printed off to the figure of needs using printing equipment, using just
The method of pressure plus vacuum makes the substrate be processed into required shape;After cutting away extra side using laser cutting device, it is put into
It is projected in mold.
Embodiment three
A kind of dummy slider Shooting Technique based on automobile interior decoration, which comprises the following steps:
Step 1: film prepare: by major ingredient each component use low temperature drying, 12 hours or more, drying temperature 50-60
℃;Each component is sufficiently mixed, the revolving speed of blender is 600 revs/min, and mixing time is 45 minutes, then will be mixed after stirring
Material cooling is closed, is cooled to 35 DEG C in 7 minutes, is kept for 30 minutes under being 40% in humidity, is then cooled to 20 in 15 minutes again
DEG C, it is plasticized, the film for being plasticized extrusion immediately is attached directly on chill roll cooling plasticizing forming;
Step 2: film pre-processes: the drying process of 3 hours is carried out to film by drying equipment, then by film
130 DEG C are heated to, drying to moisture content is not higher than 0.04%;
Step 3: raw material is classified: injection molding thermosetting material and heat-fusible materials will be needed to carry out classification and put in order, then will
Thermosetting material and heat-fusible materials and auxiliary material press the proportion of 5-1, are then mixed object and are added to 300 DEG C of temperature meltings and set
Standby middle carry out melting;
Step 4: being molded: it is put into raw material is made in step 3 in injection molding machine, equipment is heated to 360 DEG C, it will
Raw material is molded, and guarantees that injection pressure will melt at the thermosetting end of the thermosetting material injection mold after injection molding in 40MPa
Heat-fusible materials injection mold hot melt end, material injection after the completion of, open injection molding machine make heat-fusible materials and heat in mold
Thermoset material is merged, and fusion is stood after twenty minutes;
Step 5: being cooled and shaped: material obtained in step 4 is put into vacuum pressure equipment and has suffered cooling and shaping, it is cooling
Time is 40 minutes;
Step 6: slice molding: raw material obtained in step 5 being printed off to the figure of needs using printing equipment, using just
The method of pressure plus vacuum makes the substrate be processed into required shape;After cutting away extra side using laser cutting device, it is put into
It is projected in mold.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (1)
1. a kind of dummy slider Shooting Technique based on automobile interior decoration, which comprises the following steps:
Step 1: prepared by film: major ingredient each component being used low temperature drying, 12 hours or more, drying temperature was 50-60 DEG C;It will
Each component is sufficiently mixed, and the revolving speed of blender is 600 revs/min, and mixing time is 45 minutes, then by the mixture cold after stirring
But, 35 DEG C are cooled in 7 minutes, are kept for 30 minutes under being 40% in humidity, 20 DEG C is then cooled in 15 minutes again, by it
It is plasticized, the film for being plasticized extrusion immediately is attached directly on chill roll cooling plasticizing forming;
Step 2: film pre-processes: carrying out the drying process of 3 hours to film by drying equipment, then heat film
To 100 DEG C -130 DEG C, drying to moisture content is not higher than 0.04%;
Step 3: raw material is classified: injection molding thermosetting material and heat-fusible materials will be needed to carry out classification and put in order, then by thermosetting
Property material and heat-fusible materials and auxiliary material press the proportion of 5-1, being then mixed object, to be added to 270 DEG C~300 DEG C temperature molten
Melting is carried out in refining equipment;
Step 4: being molded: it is put into raw material is made in step 3 in injection molding machine, equipment is heated to 300 DEG C -360 DEG C,
Raw material is molded, guarantees that injection pressure will by the thermosetting end of the thermosetting material injection mold after injection molding in 30-40MPa
The hot melt end of the heat-fusible materials injection mold of melting, after the completion of material injection, opening injection molding machine makes heat-fusible materials in mold
It is merged with thermosetting material, fusion is stood after twenty minutes;
Step 5: being cooled and shaped: material obtained in step 4 being put into vacuum pressure equipment and has suffered cooling and shaping, cooling time
It is 40 minutes;
Step 6: slice molding: raw material obtained in step 5 is printed off to the figure of needs using printing equipment, using positive pressure plus
The method of vacuum makes the substrate be processed into required shape;After cutting away extra side using laser cutting device, it is put into mold
Inside projected.