CN108211775A - Load biological enzyme removes formaldehyde composition and preparation method thereof - Google Patents
Load biological enzyme removes formaldehyde composition and preparation method thereof Download PDFInfo
- Publication number
- CN108211775A CN108211775A CN201810233304.0A CN201810233304A CN108211775A CN 108211775 A CN108211775 A CN 108211775A CN 201810233304 A CN201810233304 A CN 201810233304A CN 108211775 A CN108211775 A CN 108211775A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- composition
- dehydrogenase
- parts
- remove
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of complicated pore passage structures for removing formaldehyde composition and preparation method thereof, should removing formaldehyde composition composition depending for loading biological enzyme, will be attached to inside composition with the biological enzyme particle of catalysis Degradation Formaldehyde, so as to fulfill the purpose except formaldehyde.This method uses composition as carrier, carries out activation modification to composition by using moisture retention liquid, biological enzyme loads and post processing is prepared.Should be except formaldehyde composition heavy metal free ingredient, bioaffinity is good, easy to use, can be widely applied to a variety of living scenes.
Description
Technical field
The present invention relates to a kind of room temperatures except formaldehyde materials, more particularly to it is a kind of load biological enzyme except formaldehyde composition and its
Preparation method.
Background technology
Formaldehyde is one of common air pollutants of modern society, is mainly derived from indoor plank, wall covering, plastic cement system
Product.Formaldehyde is mainly strong carcinogenesis and strong mutagenicity to the harm of human body.Long Term Contact formaldehyde can cause respiratory tract, digestion
The mucosa infection in road, and then lead to lung function and dysfunction of liver, immune system is finally influenced, generates canceration.Children and pregnant woman
The reaction of PARA FORMALDEHYDE PRILLS(91,95) is especially big, therefore formaldehyde is listed in China's toxic chemical priority acccess control list second.
The minimizing technology of formaldehyde includes the methods of physical absorption, chemical catalysis, chemical reaction, living things catalysis, most often at present
What is seen is the composition adsorption method in physical absorption.Composition absorption method is mainly special using the high-specific surface area of composition
Property, come the purpose realized fully absorption, decompose formaldehyde in air.It is advantageous that porous material large specific surface area, can load more
More biological enzyme, therefore can realize more efficient suction-operated.Market it is common usually carry heavy metal except formaldehyde composition
The industrial chemicals such as oxide or pitch, tar are likely to cause the pollution of environment during producing and using, directly exposed to connect
Touching also has certain danger.
Invention content
The purpose of the present invention is to provide a kind of carrying biological enzyme except formaldehyde composition preparation method, it is mainly used for first
Aldehyde gas effective protection.In view of the possible pollution on the environment of heavy metallic oxide, present invention employs biological enzymes
Principle.This method is mainly a large amount of active formaldehyde dehydrogenases by being attached on porous material micropore, by the first in air
Aldehyde is converted into harmless formic acid, and then realizes the purpose for eliminating formaldehyde.Since formaldehyde dehydrogenase plays catalyst during the reaction
Effect, the consumption of enzyme is less in reaction process, therefore the drying that only needs periodically to divulge information can restore to remove formaldehyde activity again.
To achieve the above object, the application provides following technical solution:
A kind of formaldehyde composition that removes for loading biological enzyme, it is described except formaldehyde composition uses porous material as carrier, thereon
Load has the formaldehyde dehydrogenase of 0.5%wt-1.0%wt, the nano-titanium dioxide of 5%-10%.
The porous material is MCM, TUD, activated carbon or starch, algin, pectin carbide in it is one or more.
Preferably, the aperture of the porous material is 4-10,000nm.
Preferably, the porous material is the carbide of starch, algin, pectin.
Preferably, the porous material is activated carbon.
The composition is coal quality composition, one or more in carbo lignius, bamboo charcoal, fruit shell carbon.
The present invention's removes formaldehyde composition, and the formaldehyde dehydrogenase is dimer protein.
The present invention's removes formaldehyde composition, and the formaldehyde dehydrogenase is tetramer albumen.
The present invention's removes formaldehyde composition, and the formaldehyde dehydrogenase is glutathione-dependence formaldehyde dehydrogenase.
The present invention's removes formaldehyde composition, and the formaldehyde dehydrogenase is glutathione-independent form formaldehyde dehydrogenase.
The present invention's removes formaldehyde composition, and the formaldehyde dehydrogenase is by Escherichia coli, Spherical red antibacterial, Pseudomonas putida
One or more fermentations in bacterium, Paracoccus denitrificans, saccharomycete or sulfuric acid ore deposit sulfolobus solfataricus obtain.
The present invention's removes formaldehyde composition, and the formaldehyde dehydrogenase is fermented to obtain by pseudomonas putida.
A kind of method prepared except formaldehyde composition, production method include the following steps:
Step 1:6-10 parts of amino acid and 1-2 parts of moisturizer are dissolved in 100 parts of pure water, preparation obtains moisture retention liquid;
The moisturizer for glycerine, xylitol, D-sorbite it is one or more;
Step 2:Put into 40-60 parts of porous materials, 0.3-0.5 parts of formaldehyde dehydrogenases, 1.5-3.5 parts of nano-titanium dioxides
It is sufficiently stirred, room temperature immersion 6 hours;
Step 3:90 mesh filter screens filter, and room temperature or low temperature drying 2 hours obtain product.
Having the beneficial effect that prepared by the present invention:
1. except the system for handling bigger of formaldehyde composition PARA FORMALDEHYDE PRILLS(91,95).The physical absorption of conventional composition is that a dynamic is put down
Weighing apparatus process, after the treating capacity for reaching certain, the adsorbance and burst size of formaldehyde are equal, that is, have reached the threshold value of adsorption capacity.
And the preparation-obtained composition of the present invention is due to large specific surface area, increases the load capacity of biological enzyme, formaldehyde be adsorbed onto it is more
After the microcellular structure of Porous materials, harmless formic acid is converted under the action of formaldehyde dehydrogenase quickly and is volatilized from system, so as to
Greatly promote the adsorbance of composition PARA FORMALDEHYDE PRILLS(91,95).
2. with it is commercially available except formaldehyde composition compared with, the present invention do not use the chemical industry such as heavy metallic oxide and pitch, tar
Raw material, and it is mild in working condition, and product has the characteristics that environment friendly and nonhazardous, can be commonly used to a variety of fields
It closes.
3. the present invention is added to nano-titanium dioxide in preparation process, the ingredient is under the conditions of natural lighting, it may have
Certain chemical catalysis Degradation Formaldehyde effect.Formaldehyde hand is removed present invention incorporates physical absorption, chemical catalysis and living things catalysis
Section, except formaldehyde sales volume greatly promotes.
4. prepared by the present invention except formaldehyde composition in use for some time, activity may decrease, this be by
Other impurities or moisture contamination in adsorbance gradually saturation and environment, ventilation drying can activity recovery.
Specific embodiment
It is illustrated below in conjunction with to the preferred embodiment of the present invention.It should be appreciated that preferred embodiment described herein
It is merely to illustrate and explain the present invention, but is not used in the restriction present invention.
Embodiment 1
100g algins carbide is taken as combination carrier, the carrier synthesized by sol-gel method after through carbonization
It obtains.Its specific surface area is 480m2/g.By porous material and 1g formaldehyde dehydrogenases and 5g nano-titanium dioxide mixings, put into
In 200ml moisture retention liquids.Moisture retention liquid is obtained by 20g amino acid and 2ml glycerine to be dissolved in prepare in 200ml pure water.200rpm
It is stirred under rotating speed, room temperature immersion 6 hours.It is filtered using 90 mesh filter screens, 15 DEG C of drying 2 hours, obtains removing formaldehyde composition.
Room temperature adsorption test, initial concentration of formaldehyde are carried out to the simulation 500L of air containing formaldehyde using composition 10g obtained
For 560ppm.After processing 24 hours, endpoint concentration 168ppm, removal rate reaches 92.0%.
Embodiment 2
80g pectin carbide is taken as combination carrier, the carrier synthesized by sol-gel method after through being carbonized
It arrives.Its specific surface area is 480m2/g.By porous material and 0.7g formaldehyde dehydrogenases and 6.5g nano-titanium dioxide mixings, input
Into 200ml moisture retention liquids.Moisture retention liquid is obtained by 20g amino acid and 2ml glycerine to be dissolved in prepare in 200ml pure water.
It is stirred under 200rpm rotating speeds, room temperature immersion 6 hours.It is filtered, 15 DEG C of drying 2 hours, is obtained except formaldehyde combination using 90 mesh filter screens
Object.
It is filtered using 90 mesh filter screens, 15 DEG C of drying 2 hours, obtains removing formaldehyde composition.
Room temperature adsorption test, initial concentration of formaldehyde are carried out to the simulation 500L of air containing formaldehyde using composition 10g obtained
For 560ppm.After processing 24 hours, endpoint concentration 168ppm, removal rate reaches 88.0%.
Embodiment 3
100g coals quality composition is taken to mix itself and 1g formaldehyde dehydrogenases and 5g nano-titanium dioxides as combination carrier
It is even, it puts into 200ml moisture retention liquids.Moisture retention liquid is by 20g amino acid and 2ml glycerine are dissolved in 200ml pure water with obtained
It arrives.It is stirred under 200rpm rotating speeds, room temperature immersion 6 hours.It is filtered using 90 mesh filter screens, 15 DEG C of drying 2 hours, obtains removing formaldehyde group
Close object.
Room temperature adsorption test, initial concentration of formaldehyde are carried out to the simulation 500L of air containing formaldehyde using composition 10g obtained
For 560ppm.After processing 24 hours, endpoint concentration 168ppm, removal rate reaches 70.0%.
Embodiment 4
80g bamboo charcoals is taken, by itself and 0.7g formaldehyde dehydrogenases and 6.5g nano-titanium dioxide mixings, to be thrown as combination carrier
Enter into 200ml moisture retention liquids.Moisture retention liquid is obtained by 17g amino acid and 3ml xylitols to be dissolved in prepare in 200ml pure water.
It is stirred under 200rpm rotating speeds, room temperature immersion 6 hours.It is filtered, 15 DEG C of drying 2 hours, is obtained except formaldehyde combination using 90 mesh filter screens
Object.
Room temperature adsorption test, initial concentration of formaldehyde are carried out to the simulation 500L of air containing formaldehyde using composition 10g obtained
For 578ppm.After processing 24 hours, endpoint concentration 201ppm, removal rate reaches 65.2%.
Embodiment 5
Certain commercially available brand is taken to carry out room temperature adsorption test, formaldehyde to the simulation 500L of air containing formaldehyde except formaldehyde composition 10g
Initial concentration is 558ppm.After processing 24 hours, endpoint concentration 425ppm, removal rate 23.8%.
As can be seen from the above embodiments, it is produced by the invention except formaldehyde there is preferable formaldehyde absorbing to make in a short time
With.And due to the treatment effect of formaldehyde dehydrogenase, the formaldehyde adsorbed is biodegradable as nontoxic metabolite, is avoided
Secondary release after absorption has good environmental protection performance.
It these are only the preferred embodiment of the present invention, be not intended to restrict the invention, for those skilled in the art
For, the present invention can have various changes and transformation.Any modification for all within the spirits and principles of the present invention, being made, etc.
With replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of load biological enzyme removes formaldehyde composition, it is characterised in that described except formaldehyde composition uses porous material to carry
Body, thereon load have the formaldehyde dehydrogenase of 0.5%wt-1.0%wt, the nano-titanium dioxide of 5%-10%.
2. it is according to claim 1 remove formaldehyde composition, it is characterised in that the porous material be MCM, TUD, activated carbon
It is or one or more in the carbide of starch, algin, pectin.
3. according to claim 2 remove formaldehyde composition, it is characterised in that selected composition is coal quality composition, wood
It is one or more in matter charcoal, bamboo charcoal, fruit shell carbon.
4. according to claim 1 remove formaldehyde composition, it is characterised in that the formaldehyde dehydrogenase is dimer protein.
5. according to claim 1 remove formaldehyde composition, it is characterised in that the formaldehyde dehydrogenase is tetramer albumen.
6. according to claim 1 remove formaldehyde composition, it is characterised in that the formaldehyde dehydrogenase is glutathione-dependence
Property formaldehyde dehydrogenase.
7. according to claim 1 remove formaldehyde composition, it is characterised in that the formaldehyde dehydrogenase is glutathione-Fei Yi
Rely type formaldehyde dehydrogenase.
8. according to claim 1 remove formaldehyde composition, it is characterised in that the formaldehyde dehydrogenase is by Escherichia coli, spherical shape
One or more in red bacterium, pseudomonas putida, Paracoccus denitrificans, saccharomycete or sulfuric acid ore deposit sulfolobus solfataricus are fermented
It arrives.
9. according to claim 1 remove formaldehyde composition, it is characterised in that the formaldehyde dehydrogenase is by pseudomonas putida
Fermentation obtains.
10. a kind of prepare the method described in claim 1 except formaldehyde composition, which is characterized in that includes the following steps:
Step 1:6-10 parts of amino acid and 1-2 parts of moisturizer are dissolved in 100 parts of pure water, preparation obtains moisture retention liquid;It is described
Moisturizer for glycerine, xylitol, D-sorbite it is one or more;
Step 2:It is abundant to put into 40-60 parts of porous materials, 0.3-0.5 parts of formaldehyde dehydrogenases, 1.5-3.5 parts of nano-titanium dioxides
Stirring, room temperature immersion 6 hours;
Step 3:90 mesh filter screens filter, and room temperature or low temperature drying 2 hours obtain product.