WO2024118701A1 - Procédés de fabrication pour unités de vitrage isolant - Google Patents

Procédés de fabrication pour unités de vitrage isolant Download PDF

Info

Publication number
WO2024118701A1
WO2024118701A1 PCT/US2023/081505 US2023081505W WO2024118701A1 WO 2024118701 A1 WO2024118701 A1 WO 2024118701A1 US 2023081505 W US2023081505 W US 2023081505W WO 2024118701 A1 WO2024118701 A1 WO 2024118701A1
Authority
WO
WIPO (PCT)
Prior art keywords
pane
gas
glass
igu
cte
Prior art date
Application number
PCT/US2023/081505
Other languages
English (en)
Inventor
Peter Steven COLE
James Gregory Couillard
Michael Aaron Mcdonald
Original Assignee
Corning Incorporated
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Corning Incorporated filed Critical Corning Incorporated
Publication of WO2024118701A1 publication Critical patent/WO2024118701A1/fr

Abstract

Procédés de fabrication pour unité de vitrage isolant (IGU) comprenant les étapes suivantes : application d'un premier cordon d'adhésif chauffé sur une première face d'une troisième vitre, la troisième vitre ayant une épaisseur inférieure à 2 mm avec CTE3 ; mise en contact d'une deuxième face de la première vitre ayant CTE1 avec l'adhésif, application d'un deuxième cordon d'adhésif chauffé sur une deuxième face de la troisième vitre, mise en contact d'une première face d'une deuxième vitre avec l'adhésif, la deuxième vitre présentant CTE 2, sachant que CTE 3 < CTE 1, CTE2.
PCT/US2023/081505 2022-11-29 2023-11-29 Procédés de fabrication pour unités de vitrage isolant WO2024118701A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US202263428501P 2022-11-29 2022-11-29
US63/428,501 2022-11-29

Publications (1)

Publication Number Publication Date
WO2024118701A1 true WO2024118701A1 (fr) 2024-06-06

Family

ID=89536027

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2023/081505 WO2024118701A1 (fr) 2022-11-29 2023-11-29 Procédés de fabrication pour unités de vitrage isolant

Country Status (1)

Country Link
WO (1) WO2024118701A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20190264494A1 (en) * 2018-02-23 2019-08-29 Apogee Enterprises, Inc. Glass heating mechanisms and methods of making insulating glass units using the same
WO2020028056A1 (fr) * 2018-07-30 2020-02-06 Corning Incorporated Unité vitrage isolant
WO2021126607A1 (fr) * 2019-12-18 2021-06-24 Corning Incorporated Appareil et procédé de fabrication d'une unité de vitrage multiple

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20190264494A1 (en) * 2018-02-23 2019-08-29 Apogee Enterprises, Inc. Glass heating mechanisms and methods of making insulating glass units using the same
WO2020028056A1 (fr) * 2018-07-30 2020-02-06 Corning Incorporated Unité vitrage isolant
WO2021126607A1 (fr) * 2019-12-18 2021-06-24 Corning Incorporated Appareil et procédé de fabrication d'une unité de vitrage multiple

Similar Documents

Publication Publication Date Title
US11491851B2 (en) Cold formed laminates
US20240140075A1 (en) Dimmable window pane with reduced bow and insulated glazing unit comprising the same
US10611664B2 (en) Thermally strengthened architectural glass and related systems and methods
CA2994236A1 (fr) Verre pour batiment, thermiquement renforce et systemes et procedes associes
US20220220029A1 (en) Multi-layer insulated glass unit comprising a low cte glass layer
US20200325056A1 (en) System and process for forming curved glass laminate article utilizing glass viscosity differential for improved shape matching
WO2024118701A1 (fr) Procédés de fabrication pour unités de vitrage isolant
WO2024118703A1 (fr) Procédés de fabrication d&#39;unités de verre isolantes
JP2022513155A (ja) 低ｃｔｅ中央板ガラスを有する断熱ガラスユニット
EP3728148B1 (fr) Unité de verre isolée multicouche comprenant une couche de verre à faible cte
WO2024118560A1 (fr) Procédés d&#39;assemblage d&#39;unité de verre isolant triple mince
JPH06100337A (ja) 板ガラス構造体