WO2024103106A1 - Procédé de lixiviation préférentielle de métaux de valeur à partir de concentrés de sulfure - Google Patents
Procédé de lixiviation préférentielle de métaux de valeur à partir de concentrés de sulfure Download PDFInfo
- Publication number
- WO2024103106A1 WO2024103106A1 PCT/AU2023/051149 AU2023051149W WO2024103106A1 WO 2024103106 A1 WO2024103106 A1 WO 2024103106A1 AU 2023051149 W AU2023051149 W AU 2023051149W WO 2024103106 A1 WO2024103106 A1 WO 2024103106A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- leach
- concentrate
- electronegative
- hydrometallurgical method
- sulphide
- Prior art date
Abstract
La présente invention concerne un procédé hydrométallurgique de traitement d'un concentré de sulfure (101) dans un réacteur de lixiviation oxydante fonctionnant en continu, le concentré de sulfure (101) comprenant un mélange d'éléments électronégatifs et électropositifs, le procédé comprenant les opérations consistant à soumettre une bouillie comprenant le concentré (101) dans un courant aqueux contenant au moins de l'eau à une lixiviation oxydante ciblant la récupération d'un ou de plusieurs éléments électronégatifs sur les éléments plus électropositifs à l'intérieur du concentré; et à ajuster le potentiel électrochimique en commandant la pression partielle d'oxygène à l'intérieur du circuit de lixiviation pour lixivier un ou plusieurs des éléments électronégatifs de façon préférentielle par rapport aux éléments plus électropositifs à l'intérieur du concentré ; et les éléments électronégatifs comprenant au moins l'un parmi le cuivre, le nickel, le cobalt ou le zinc.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU2022903424 | 2022-11-14 | ||
AU2022903424A AU2022903424A0 (en) | 2022-11-14 | Method for the preferential leach of value metals from sulphide concentrates |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2024103106A1 true WO2024103106A1 (fr) | 2024-05-23 |
Family
ID=91083435
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/AU2023/051149 WO2024103106A1 (fr) | 2022-11-14 | 2023-11-13 | Procédé de lixiviation préférentielle de métaux de valeur à partir de concentrés de sulfure |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2024103106A1 (fr) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6428604B1 (en) * | 2000-09-18 | 2002-08-06 | Inco Limited | Hydrometallurgical process for the recovery of nickel and cobalt values from a sulfidic flotation concentrate |
US20090293680A1 (en) * | 2006-03-28 | 2009-12-03 | Ian Christopher Ritchie | Processing of Metal Values from Concentrates |
WO2016100453A2 (fr) * | 2014-12-16 | 2016-06-23 | Flsmidth A/S | Système et procédé pour la lixiviation de sulfures métalliques dans des conditions supérieures aux conditions atmosphériques |
WO2021074482A1 (fr) * | 2019-10-15 | 2021-04-22 | Outotec (Finland) Oy | Autoclave et procédé d'oxydation sous pression |
WO2022178628A1 (fr) * | 2021-02-24 | 2022-09-01 | Sherritt International Corporation | Co-traitement de concentré de sulfure de cuivre avec du minerai latéritique de nickel |
-
2023
- 2023-11-13 WO PCT/AU2023/051149 patent/WO2024103106A1/fr unknown
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US6428604B1 (en) * | 2000-09-18 | 2002-08-06 | Inco Limited | Hydrometallurgical process for the recovery of nickel and cobalt values from a sulfidic flotation concentrate |
US20090293680A1 (en) * | 2006-03-28 | 2009-12-03 | Ian Christopher Ritchie | Processing of Metal Values from Concentrates |
WO2016100453A2 (fr) * | 2014-12-16 | 2016-06-23 | Flsmidth A/S | Système et procédé pour la lixiviation de sulfures métalliques dans des conditions supérieures aux conditions atmosphériques |
WO2021074482A1 (fr) * | 2019-10-15 | 2021-04-22 | Outotec (Finland) Oy | Autoclave et procédé d'oxydation sous pression |
WO2022178628A1 (fr) * | 2021-02-24 | 2022-09-01 | Sherritt International Corporation | Co-traitement de concentré de sulfure de cuivre avec du minerai latéritique de nickel |
Non-Patent Citations (2)
Title |
---|
ALEKSEI KRITSKII, KIRILL KARIMOV; STANISLAV NABOICHENKO: "Pressure leaching of chalcopyrite concentrate", PROCEEDINGS OF THE INTERNATIONAL SEMINAR ON METALLURGY AND MATERIALS (ISMM2017) AIP CONF. PROC. 1964, vol. 1964, 1 January 2018 (2018-01-01), pages 020048-1 - 020048-5, XP093175492, DOI: 10.1063/1.5038330 * |
KIM D H, KIM W.J.; KIM H.S.; HAN K.S.; TRAN T.; KIM M.J.: "Galvanic enhancement for high pressure leaching of chalcopyrite", JOURNAL OF MINING AND METALLURGY. SECTION: B, METALLURGY, TECHNICAL FACULTY AND COPPER INSTITUTE, BOR, YU, vol. 52, no. 2, 1 January 2016 (2016-01-01), YU , pages 119 - 126, XP093175497, ISSN: 1450-5339, DOI: 10.2298/JMMB150723022K * |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
EP1931807B1 (fr) | Procede pour traiter une matiere premiere portant du nickel dans le cadre d'une lixiviation a base de chlorure | |
EP0815270B1 (fr) | Procede de lixiviation de minerais sous une pression atmospherique | |
US8052774B2 (en) | Method for concentration of gold in copper sulfide minerals | |
CA2454821C (fr) | Procede d'extraction electrolytique directe de cuivre | |
FI125575B (en) | Recycling of solids in oxidative pressure extraction of metals using halide ions | |
AU2011228956B2 (en) | Method of processing nickel bearing raw material | |
MXPA03000744A (es) | Metodo para la recuperacion de minerales brutos con metal de materiales que contienen metal utilizando lixiviacion de temperatura a presion elevada. | |
CA2639165A1 (fr) | Procede de recuperation du metal d'un minerai | |
AU2002329630A1 (en) | Process for direct electrowinning of copper | |
US10151016B2 (en) | Process for extraction of copper from arsenical copper sulfide concentrate | |
US7169371B2 (en) | Process for the treatment of molybdenum concentrate | |
US10323296B2 (en) | Process for extraction of copper from arsenical copper sulfide concentrate | |
EP1507878B1 (fr) | Extraction hydrometallurgique de metaux effectuee au moyen de chlorure | |
WO2024103106A1 (fr) | Procédé de lixiviation préférentielle de métaux de valeur à partir de concentrés de sulfure | |
Hyvärinen et al. | Recovering gold from copper concentrate via the HydroCopper™ process | |
US11584975B1 (en) | Integrated pressure oxidative leach of copper sulphidic feed with copper heap leach | |
AU5401801A (en) | Processing gold containing copper sulphide feeds |