WO2024072561A1 - Utilisation de matériaux décorés de métal granulés dans un four de fusion par induction - Google Patents

Utilisation de matériaux décorés de métal granulés dans un four de fusion par induction Download PDF

Info

Publication number
WO2024072561A1
WO2024072561A1 PCT/US2023/030509 US2023030509W WO2024072561A1 WO 2024072561 A1 WO2024072561 A1 WO 2024072561A1 US 2023030509 W US2023030509 W US 2023030509W WO 2024072561 A1 WO2024072561 A1 WO 2024072561A1
Authority
WO
WIPO (PCT)
Prior art keywords
carbon
metal
matter
composition
recited
Prior art date
Application number
PCT/US2023/030509
Other languages
English (en)
Inventor
Michael Stowell
Daniel Jacobson
Lauren Sienko
Bruce Lanning
Original Assignee
Lyten, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US17/957,989 external-priority patent/US11873563B2/en
Priority claimed from US17/957,937 external-priority patent/US11827987B2/en
Application filed by Lyten, Inc. filed Critical Lyten, Inc.
Publication of WO2024072561A1 publication Critical patent/WO2024072561A1/fr

Abstract

L'invention concerne des techniques de formation de compositions uniques de matière, ainsi que diverses caractéristiques physiques avantageuses et des propriétés associées des matériaux résultants. En particulier, un ou plusieurs métaux (y compris divers alliages, tels que des superalliages Inconel) sont caractérisés en ce qu'ils comportent du carbone disposé à l'intérieur de sa structure matricielle métallique. Le carbone est principalement, ou entièrement, présent au niveau de sites interstitiels de la matrice métallique, et peut être présent dans des quantités allant d'environ 15 % en poids à environ 90 % en poids. De plus, le carbone forme des liaisons covalentes non polaires avec, à la fois, les atomes métalliques de la matrice et d'autres atomes de carbone présents dans la matrice. Ceci facilite la dispersion sensiblement homogène du carbone dans tout le matériau résultant, le transport de propriétés uniques et avantageuses telles que le rapport résistance/poids, la densité, la ténacité mécanique, la résistance au cisaillement, la résistance à la flexion, la dureté, l'anticorrosivité, la conductivité électrique et/ou thermique, etc. Dans certaines approches, la composition de matière peut être pulvérisée ou granulée.
PCT/US2023/030509 2022-09-30 2023-08-17 Utilisation de matériaux décorés de métal granulés dans un four de fusion par induction WO2024072561A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US17/957,989 US11873563B2 (en) 2018-08-02 2022-09-30 Carbon disposed in inconel alloy metal lattices and metal lattices with high carbon loading
US17/957,937 2022-09-30
US17/957,937 US11827987B2 (en) 2018-08-02 2022-09-30 Coherent graphene in a metal lattice
US17/957,989 2022-09-30

Publications (1)

Publication Number Publication Date
WO2024072561A1 true WO2024072561A1 (fr) 2024-04-04

Family

ID=90478952

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2023/030509 WO2024072561A1 (fr) 2022-09-30 2023-08-17 Utilisation de matériaux décorés de métal granulés dans un four de fusion par induction

Country Status (2)

Country Link
TW (1) TW202415470A (fr)
WO (1) WO2024072561A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20200028155A1 (en) * 2017-12-22 2020-01-23 Lyten, Inc. Structured composite materials
US20200263285A1 (en) * 2018-08-02 2020-08-20 Lyten, Inc. Covetic materials
US20200340080A1 (en) * 2019-04-26 2020-10-29 United States Of America, As Represented By The Secretary Of The Navy Inconel Nanotube Composite
US20230147825A1 (en) * 2021-11-10 2023-05-11 Lyten, Inc. Tuning porous surface coatings using a plasma spray torch
US20230145800A1 (en) * 2018-08-02 2023-05-11 Lyten, Inc. Using pelletized metal-decorated materials in an induction melting furnace
US20230416896A1 (en) * 2018-08-02 2023-12-28 Lyten, Inc. Pristine graphene disposed in a metal matrix

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20200028155A1 (en) * 2017-12-22 2020-01-23 Lyten, Inc. Structured composite materials
US20200263285A1 (en) * 2018-08-02 2020-08-20 Lyten, Inc. Covetic materials
US20230145800A1 (en) * 2018-08-02 2023-05-11 Lyten, Inc. Using pelletized metal-decorated materials in an induction melting furnace
US20230416896A1 (en) * 2018-08-02 2023-12-28 Lyten, Inc. Pristine graphene disposed in a metal matrix
US20200340080A1 (en) * 2019-04-26 2020-10-29 United States Of America, As Represented By The Secretary Of The Navy Inconel Nanotube Composite
US20230147825A1 (en) * 2021-11-10 2023-05-11 Lyten, Inc. Tuning porous surface coatings using a plasma spray torch

Also Published As

Publication number Publication date
TW202415470A (zh) 2024-04-16

Similar Documents

Publication Publication Date Title
US11739409B2 (en) Apparatuses and methods for producing covetic materials using microwave reactors
US11827987B2 (en) Coherent graphene in a metal lattice
US11873563B2 (en) Carbon disposed in inconel alloy metal lattices and metal lattices with high carbon loading
US20230416896A1 (en) Pristine graphene disposed in a metal matrix
US11932946B2 (en) Tuning porous surface coatings using a plasma spray torch
WO2013056185A1 (fr) Nanomatériaux fabriqués à l'aide de l'électroérosion et d'autres procédés de fabrication de particules
JP2007516827A (ja) 粉末予熱装置が具備された低温スプレー装置
JP2015513002A (ja) 金属粉末及び粉末成形体を製造する方法、並びに前記方法によって製造された粉末及び粉末成形体
Ardila-Rodríguez et al. Surface modification of aluminum alloys with carbon nanotubes by laser surface melting
EP2394952A2 (fr) Nanoparticules élaborées à partir de nanotube de carbone et procédé d'élaboration correspondant
JP2024050642A (ja) コベチック材料
US20230212729A1 (en) Tuned porous surface coatings
Pithawalla et al. Preparation of ultrafine and nanocrystalline FeAl powders
Tepper Nanosize powders produced by electro-explosion of wire and their potential applications
Sun et al. Synthesis of metallic high-entropy alloy nanoparticles
Ergul et al. Electroless nickel–phosphorus and cobalt–phosphorus coatings on multi-walled carbon nanotubes
WO2024072561A1 (fr) Utilisation de matériaux décorés de métal granulés dans un four de fusion par induction
US12018383B2 (en) Coherent or pristine graphene in a polymer matrix
KR20130128809A (ko) Ｆｅ­Ｃｒ­Ａｌ­Ｙ계 합금 와이어의 제조방법, 이에 의해 제조된 Ｆｅ­Ｃｒ­Ａｌ­Ｙ계 합금 와이어 및 이를 이용하여 제조된 합금 나노분말
Sadeghi One-pot synthesis of Ag/Fe3O4 nanocomposite: Preparation, characterization and efficient catalyst
Liu et al. Preparation and Analysis of Amorphous Gradient Composites on TC17 Titanium Alloy by Laser Melting Deposition (LMD).
Ayodele Dispersion Characteristics and Effect of Heating Rates on the Mechanical Properties of Spark Plasma Sintered Multi-Walled Carbon Nanotubes Reinforced Nickel Aluminide Composites
Pesterev et al. Application of Vacuum Plasma Techniques for Preparation of Ni‐Cr-Dy Powders Proposed as Master Alloys for Combustion Synthesis of Ni-Al Intermetallics
Liu et al. Characterisation of the Microstructure of Fe–Al/Cr3C2 Composite Coatings
Lau Thermal spraying of nanocrystalline materials

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23873412

Country of ref document: EP

Kind code of ref document: A1