WO2024034516A1 - 導電ペースト及び接続構造体 - Google Patents

導電ペースト及び接続構造体 Download PDF

Info

Publication number
WO2024034516A1
WO2024034516A1 PCT/JP2023/028427 JP2023028427W WO2024034516A1 WO 2024034516 A1 WO2024034516 A1 WO 2024034516A1 JP 2023028427 W JP2023028427 W JP 2023028427W WO 2024034516 A1 WO2024034516 A1 WO 2024034516A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
thixotropic agent
electrode
conductive paste
solder particles
Prior art date
Application number
PCT/JP2023/028427
Other languages
English (en)
French (fr)
Inventor
雄太 山中
主 國澤
Original Assignee
積水化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 積水化学工業株式会社 filed Critical 積水化学工業株式会社
Priority to JP2023562725A priority Critical patent/JP7526371B2/ja
Publication of WO2024034516A1 publication Critical patent/WO2024034516A1/ja

Abstract

スクリーン印刷性を高めることができ、タック性を維持することができ、かつ、電極上にはんだ粒子を効率的に配置することができる導電ペーストを提供する。　本発明に係る導電ペーストは、熱硬化性成分と、複数のはんだ粒子と、フラックスと、チキソトロピック剤とを含み、前記はんだ粒子の平均粒子径が、５．０μｍ以下であり、前記フラックスが、２５℃で固体であり、前記チキソトロピック剤が、２５℃で液体であり、かつ水酸基を有するチキソトロピック剤であるか、又は、２５℃で固体であり、かつ前記チキソトロピック剤を２５℃及び５０％ＲＨで２４時間放置したときの、重量増加率が０．２重量％以上であるチキソトロピック剤である。

Description

導電ペースト及び接続構造体
　本発明は、はんだ粒子を含む導電ペーストに関する。また、本発明は、上記導電ペーストを用いた接続構造体に関する。
　異方性導電ペースト及び異方性導電フィルム等の異方性導電材料が広く知られている。上記異方性導電材料では、バインダー樹脂中に導電性粒子が分散されている。
　上記異方性導電材料は、各種の接続構造体を得るために使用されている。上記異方性導電材料による接続としては、例えば、フレキシブルプリント基板とガラス基板との接続（ＦＯＧ（Ｆｉｌｍ　ｏｎ　Ｇｌａｓｓ））、半導体チップとフレキシブルプリント基板との接続（ＣＯＦ（Ｃｈｉｐ　ｏｎ　Ｆｉｌｍ））、半導体チップとガラス基板との接続（ＣＯＧ（Ｃｈｉｐ　ｏｎ　Ｇｌａｓｓ））、並びにフレキシブルプリント基板とガラスエポキシ基板との接続（ＦＯＢ（Ｆｉｌｍ　ｏｎ　Ｂｏａｒｄ））等が挙げられる。
　近年、はんだ粒子等の導電性粒子を含む導電材料では、プリント配線板等における配線及びコネクター等のファインピッチ化により、導電性粒子の小粒子径化が進行している。
　下記の特許文献１では、平均粒子径０．４μｍ～２．０μｍの金属粒子を主成分として含む導電性ペーストが開示されている。上記導電性ペーストでは、上記金属粒子の全個数１００％中、粒子径が０．２μｍ以下の金属粒子の個数が５％以下である。
特開平１０－１３４６３７号公報
　はんだ粒子を含む導電ペーストを用いて導電接続を行う際には、上方の複数の電極と下方の複数の電極とが電気的に接続されて、導電接続が行われる。はんだ粒子は、上下の電極間に配置されることが望ましく、隣接する横方向の電極間には配置されないことが望ましい。隣接する横方向の電極間は、電気的に接続されないことが望ましい。
　一般に、はんだ粒子を含む導電ペーストは、スクリーン印刷等により基板上の特定の位置に配置された後、リフロー等により加熱されて用いられる。導電ペーストがはんだ粒子の融点以上に加熱されることで、はんだ粒子が溶融し、電極間にはんだが凝集することで、上下の電極間が電気的に接続される。
　しかしながら、特許文献１のような従来の導電ペーストがファインピッチ化されたプリント配線板等にスクリーン印刷された場合には、導電ペーストの外表面積が大きくなることにより、導電ペーストの表面に皮張りが生じることがある。導電ペーストの表面に皮張りがあると、導電ペーストのタック性が低下することがある。タック性の低い導電ペーストでは、導電接続時に、電極の位置ずれが生じるという課題がある。
　さらに、導電ペーストの表面に皮張りがあると、はんだ粒子の凝集が阻害され、接続されるべき上下の電極間にはんだ粒子を効率的に配置できないことがある。結果として、導電ペーストに含まれるはんだ粒子が、電極が形成されていない領域に配置されて、接続されるべき上下の電極間に配置されるはんだ粒子の量が減少することがある。このため、接続されるべき上下の電極間の導通信頼性が低くなったり、隣接する横方向の電極間の絶縁信頼性が低くなったりすることがある。
　また、従来の導電ペーストは、揮発性が高いために、保管環境や使用条件によっては、印刷時の導電ペーストの粘度が高くなり、導電ペーストをプリント配線板等に均一に塗布することができないことがある。
　本発明の目的は、スクリーン印刷性を高めることができ、タック性を維持することができ、かつ、電極上にはんだ粒子を効率的に配置することができる導電ペーストを提供することである。また、本発明の目的は、上記導電ペーストを用いた接続構造体を提供することである。
　本発明の広い局面によれば、熱硬化性成分と、複数のはんだ粒子と、フラックスと、チキソトロピック剤とを含み、前記はんだ粒子の平均粒子径が、５．０μｍ以下であり、前記フラックスが、２５℃で固体であり、前記チキソトロピック剤が、２５℃で液体であり、かつ水酸基を有するチキソトロピック剤であるか、又は、２５℃で固体であり、かつ前記チキソトロピック剤を２５℃及び５０％ＲＨで２４時間放置したときの、下記の重量増加率が０．２重量％以上であるチキソトロピック剤である、導電ペーストが提供される。
　重量増加率（重量％）＝（Ｗ２－Ｗ１）×１００／Ｗ１
　Ｗ１：放置前の前記チキソトロピック剤の重量
　Ｗ２：放置後の前記チキソトロピック剤の重量
　本発明に係る導電ペーストのある特定の局面では、前記導電ペースト１００重量％中、前記チキソトロピック剤の含有量が、０．００５重量％以上２重量％以下である。
　本発明に係る導電ペーストのある特定の局面では、前記はんだ粒子１００重量部に対して、前記チキソトロピック剤の含有量が、０．００３重量部以上２重量部以下である。
　本発明に係る導電ペーストのある特定の局面では、前記チキソトロピック剤が、２５℃で液体であり、かつ水酸基を有するチキソトロピック剤である。
　本発明に係る導電ペーストのある特定の局面では、前記チキソトロピック剤が、２５℃で液体であり、水酸基を有し、かつ沸点が８０℃以上であるチキソトロピック剤である。
　本発明に係る導電ペーストのある特定の局面では、前記チキソトロピック剤が、２５℃で固体であり、かつ前記重量増加率が１重量％以上であるチキソトロピック剤である。
　本発明の広い局面によれば、第１の電極を表面に有する第１の接続対象部材と、第２の電極を表面に有する第２の接続対象部材と、前記第１の接続対象部材と、前記第２の接続対象部材とを接続している接続部とを備え、前記接続部の材料が、上述した導電ペーストであり、前記第１の電極と前記第２の電極とが、前記接続部中のはんだ部により電気的に接続されている接続構造体が提供される。
　本発明に係る導電ペーストは、熱硬化性成分と、複数のはんだ粒子と、フラックスと、チキソトロピック剤とを含む。本発明に係る導電ペーストでは、上記はんだ粒子の平均粒子径が、５．０μｍ以下である。本発明に係る導電ペーストでは、上記フラックスが、２５℃で固体である。本発明に係る導電ペーストでは、上記チキソトロピック剤が、２５℃で液体であり、かつ水酸基を有するチキソトロピック剤であるか、又は、２５℃で固体であり、かつ上記チキソトロピック剤を２５℃及び５０％ＲＨで２４時間放置したときの、上記の重量増加率が０．２重量％以上であるチキソトロピック剤である。本発明に係る導電ペーストでは、上記の構成が備えられているので、スクリーン印刷性を高めることができ、タック性を維持することができ、かつ、電極上にはんだ粒子を効率的に配置することができる。
図１は、本発明の一実施形態に係る導電ペーストを用いて得られる接続構造体を模式的に示す断面図である。
　以下、本発明の詳細を説明する。
　（導電ペースト）
　本発明に係る導電ペーストは、熱硬化性成分と、複数のはんだ粒子と、フラックスと、チキソトロピック剤とを含む。本発明に係る導電ペーストでは、上記はんだ粒子の平均粒子径が、５．０μｍ以下である。本発明に係る導電ペーストでは、上記フラックスが、２５℃で固体である。本発明に係る導電ペーストでは、上記チキソトロピック剤が、（Ａ）２５℃で液体であり、かつ水酸基を有するチキソトロピック剤であるか、又は、（Ｂ）２５℃で固体であり、かつ上記チキソトロピック剤を２５℃及び５０％ＲＨで２４時間放置したときの、下記の重量増加率が０．２重量％以上であるチキソトロピック剤である。
　重量増加率（重量％）＝（Ｗ２－Ｗ１）×１００／Ｗ１
　Ｗ１：放置前の前記チキソトロピック剤の重量
　Ｗ２：放置後の前記チキソトロピック剤の重量
　本発明に係る導電ペーストでは、上記の構成が備えられているので、スクリーン印刷性を高めることができ、タック性を維持することができ、かつ、電極上にはんだ粒子を効率的に配置することができる。
　また、本発明に係る導電ペーストでは、電極間の導電接続時に、複数のはんだ粒子が、上下の対向した電極間に集まりやすく、複数のはんだ粒子を電極（ライン）上に配置することができる。また、複数のはんだ粒子の一部が、接続されてはならない横方向の電極間に配置され難く、接続されてはならない横方向の電極間に配置されるはんだ粒子の量をかなり少なくすることができる。結果として、本発明では、接続されるべき上下の電極間の導通信頼性を効果的に高めることができ、接続されてはならない隣接する横方向の電極間の絶縁信頼性を効果的に高めることができる。
　さらに、本発明では、電極間の位置ずれを防ぐことができる。本発明では、導電ペーストを上面に配置した第１の接続対象部材に、第２の接続対象部材を重ね合わせる際に、第１の接続対象部材の電極と第２の接続対象部材の電極とのアライメントがずれた状態でも、そのずれを補正して電極同士を接続させることができる（セルフアライメント効果）。
　電極上にはんだ粒子をより一層効率的に配置する観点からは、上記導電ペーストの２５℃での粘度（η２５）は、好ましくは３０Ｐａ・ｓ以上、より好ましくは５０Ｐａ・ｓ以上であり、好ましくは２５０Ｐａ・ｓ以下、より好ましくは２００Ｐａ・ｓ以下である。上記粘度（η２５）は、配合成分の種類及び配合量により適宜調整することができる。
　上記粘度（η２５）は、例えば、Ｅ型粘度計を用いて、２５℃及び５ｒｐｍの条件で測定することができる。上記Ｅ型粘度計としては、東機産業社製「ＴＶＥ２２Ｌ」等が挙げられる。
　上記導電ペーストは異方性導電ペーストであることが好ましい。上記導電ペーストは、電極の電気的な接続に好適に用いられる。上記導電ペーストは、回路接続ペーストであることが好ましい。
　上記導電ペーストの使用環境は、特に限定されない。上記導電ペーストは、２５℃及び５０％ＲＨの環境で使用されてもよく、それ以外の環境で使用されてもよい。
　以下、上記導電ペーストに含まれる各成分を説明する。なお、本明細書中において、「（メタ）アクリル」は「アクリル」と「メタクリル」との一方又は双方を意味する。
　（熱硬化性成分）
　本発明に係る導電ペーストは、熱硬化性成分を含む。上記導電ペーストは、熱硬化性成分として、熱硬化性化合物を含むことが好ましい。上記導電ペーストは、熱硬化剤を含んでいてもよく、含んでいなくてもよい。上記導電ペーストは、熱硬化性成分として、熱硬化性化合物と熱硬化剤とを含んでいてもよい。上記導電ペーストが、熱硬化性化合物と熱硬化剤とを含む場合には、導電ペーストをより一層良好に硬化させることができる。
　（熱硬化性成分：熱硬化性化合物）
　上記熱硬化性化合物は、特に限定されない。上記熱硬化性化合物としては、オキセタン化合物、エポキシ化合物、エピスルフィド化合物、（メタ）アクリル化合物、フェノール化合物、アミノ化合物、不飽和ポリエステル化合物、ポリウレタン化合物、シリコーン化合物及びポリイミド化合物等が挙げられる。導電ペーストの硬化性及び粘度をより一層良好にする観点、導通信頼性をより一層高める観点、及び絶縁信頼性をより一層高める観点からは、上記熱硬化性化合物としては、エポキシ化合物又はエピスルフィド化合物が好ましく、エポキシ化合物がより好ましい。導電ペーストの硬化性及び粘度をより一層良好にする観点、導通信頼性をより一層高める観点、及び絶縁信頼性をより一層高める観点からは、上記熱硬化性化合物は、エポキシ化合物を含むことが好ましい。上記熱硬化性化合物は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記エポキシ化合物は、少なくとも１個のエポキシ基を有する化合物である。上記エポキシ化合物としては、ビスフェノールＡ型エポキシ化合物、ビスフェノールＦ型エポキシ化合物、ビスフェノールＳ型エポキシ化合物、フェノールノボラック型エポキシ化合物、ビフェニル型エポキシ化合物、ビフェニルノボラック型エポキシ化合物、ビフェノール型エポキシ化合物、ナフタレン型エポキシ化合物、フルオレン型エポキシ化合物、フェノールアラルキル型エポキシ化合物、ナフトールアラルキル型エポキシ化合物、ジシクロペンタジエン型エポキシ化合物、アントラセン型エポキシ化合物、アダマンタン骨格を有するエポキシ化合物、トリシクロデカン骨格を有するエポキシ化合物、ナフチレンエーテル型エポキシ化合物、及びトリアジン核を骨格に有するエポキシ化合物等が挙げられる。上記エポキシ化合物は１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記エポキシ化合物は、常温（２５℃）で液状又は固体であり、上記エポキシ化合物が常温で固体である場合には、上記エポキシ化合物の溶融温度は、上記はんだ粒子の融点以下であることが好ましい。上記の好ましいエポキシ化合物を用いることで、接続対象部材を貼り合わせた段階では、粘度が高く、搬送等の衝撃により、加速度が付与された際に、第１の接続対象部材と、第２の接続対象部材との位置ずれを抑制することができる。さらに、硬化時の熱により、導電ペーストの粘度を大きく低下させることができ、はんだ粒子の凝集を効率よく進行させることができる。
　接続信頼性を高める観点からは、上記エポキシ化合物は、フェノールノボラック型エポキシ化合物、又は、ビスフェノールＦ型エポキシ化合物を含むことが好ましい。
　導電ペースト１００重量％中、上記熱硬化性成分の含有量は、好ましくは１０重量％以上、より好ましくは１５重量％以上、さらに好ましくは２０重量％以上であり、好ましくは９０重量％以下、より好ましくは８５重量％以下、さらに好ましくは８０重量％以下、特に好ましくは７５重量％以下である。上記熱硬化性成分の含有量が、上記下限以上及び上記上限以下であると、電極上にはんだ粒子をより一層効率的に配置することができ、電極間の絶縁信頼性をより一層高めることができ、電極間の導通信頼性をより一層高めることができる。耐衝撃性を効果的に高める観点からは、上記熱硬化性成分の含有量は多い方が好ましい。
　導電ペースト１００重量％中、上記熱硬化性化合物の含有量は、好ましくは５重量％以上、より好ましくは１０重量％以上、さらに好ましくは１５重量％以上であり、好ましくは９０重量％以下、より好ましくは８５重量％以下、さらに好ましくは８０重量％以下、特に好ましくは７５重量％以下である。上記熱硬化性化合物の含有量が、上記下限以上及び上記上限以下であると、電極上にはんだ粒子をより一層効率的に配置することができ、電極間の絶縁信頼性をより一層高めることができ、電極間の導通信頼性をより一層高めることができる。耐衝撃性を効果的に高める観点からは、上記熱硬化性化合物の含有量は多い方が好ましい。
　導電ペースト１００重量％中、上記エポキシ化合物の含有量は、好ましくは５重量％以上、より好ましくは１０重量％以上、さらに好ましくは１５重量％以上であり、好ましくは９０重量％以下、より好ましくは８５重量％以下、さらに好ましくは８０重量％以下、特に好ましくは７５重量％以下である。上記エポキシ化合物の含有量が、上記下限以上及び上記上限以下であると、電極上にはんだ粒子をより一層効率的に配置することができ、電極間の絶縁信頼性をより一層高めることができ、電極間の導通信頼性をより一層高めることができる。耐衝撃性を効果的に高める観点からは、上記エポキシ化合物の含有量は多い方が好ましい。
　（熱硬化性成分：熱硬化剤）
　上記熱硬化剤は、特に限定されない。上記熱硬化剤は、上記熱硬化性化合物を熱硬化させる。上記熱硬化剤としては、イミダゾール硬化剤、アミン硬化剤、フェノール硬化剤、ポリチオール硬化剤等のチオール硬化剤、酸無水物硬化剤、熱カチオン開始剤（熱カチオン硬化剤）及び熱ラジカル発生剤等が挙げられる。上記熱硬化剤は、１種のみが用いられてもよく、２種以上が併用されてもよい。
　導電ペーストを低温でより一層速やかに硬化可能とする観点からは、上記熱硬化剤は、イミダゾール硬化剤、チオール硬化剤、又はアミン硬化剤であることが好ましい。また、上記熱硬化性化合物と上記熱硬化剤とを混合したときの保存安定性を高める観点からは、上記熱硬化剤は、潜在性の硬化剤であることが好ましい。潜在性の硬化剤は、潜在性イミダゾール硬化剤、潜在性チオール硬化剤又は潜在性アミン硬化剤であることが好ましい。なお、上記熱硬化剤は、ポリウレタン樹脂又はポリエステル樹脂等の高分子物質で被覆されていてもよい。
　上記イミダゾール硬化剤は、特に限定されない。上記イミダゾール硬化剤としては、２－メチルイミダゾール、２－エチル－４－メチルイミダゾール、１－シアノエチル－２－フェニルイミダゾール、１－シアノエチル－２－フェニルイミダゾリウムトリメリテート、２，４－ジアミノ－６－［２’－メチルイミダゾリル－（１’）］－エチル－ｓ－トリアジン、及び２，４－ジアミノ－６－［２’－メチルイミダゾリル－（１’）］－エチル－ｓ－トリアジンイソシアヌル酸付加物、２－フェニル－４，５－ジヒドロキシメチルイミダゾール、２－フェニル－４－メチル－５－ヒドロキシメチルイミダゾール、２－フェニル－４－ベンジル－５－ヒドロキシメチルイミダゾール、２－パラトルイル－４－メチル－５－ヒドロキシメチルイミダゾール、２－メタトルイル－４－メチル－５－ヒドロキシメチルイミダゾール、２－メタトルイル－４，５－ジヒドロキシメチルイミダゾール、２－パラトルイル－４，５－ジヒドロキシメチルイミダゾール等における１Ｈ－イミダゾールの５位の水素をヒドロキシメチル基で、かつ、２位の水素をフェニル基またはトルイル基で置換したイミダゾール化合物等が挙げられる。
　上記チオール硬化剤は、特に限定されない。上記チオール硬化剤としては、トリメチロールプロパントリス－３－メルカプトプロピオネート、ペンタエリスリトールテトラキス－３－メルカプトプロピオネート、及びジペンタエリスリトールヘキサ－３－メルカプトプロピオネート等が挙げられる。
　上記アミン硬化剤は、特に限定されない。上記アミン硬化剤としては、ヘキサメチレンジアミン、オクタメチレンジアミン、デカメチレンジアミン、３，９－ビス（３－アミノプロピル）－２，４，８，１０－テトラスピロ［５．５］ウンデカン、ビス（４－アミノシクロヘキシル）メタン、メタフェニレンジアミン及びジアミノジフェニルスルホン等が挙げられる。
　上記酸無水物硬化剤は、特に限定されない。上記酸無水物硬化剤としては、エポキシ化合物等の熱硬化性化合物の硬化剤として用いられる酸無水物を広く用いることができる。上記酸無水物硬化剤としては、無水フタル酸、テトラヒドロ無水フタル酸、トリアルキルテトラヒドロ無水フタル酸、ヘキサヒドロ無水フタル酸、メチルヘキサヒドロ無水フタル酸、メチルテトラヒドロ無水フタル酸、メチルブテニルテトラヒドロ無水フタル酸、フタル酸誘導体の無水物、無水マレイン酸、無水ナジック酸、無水メチルナジック酸、無水グルタル酸、無水コハク酸、グリセリンビス無水トリメリット酸モノアセテート、及びエチレングリコールビス無水トリメリット酸等の２官能の酸無水物硬化剤、無水トリメリット酸等の３官能の酸無水物硬化剤、並びに、無水ピロメリット酸、無水ベンゾフェノンテトラカルボン酸、メチルシクロヘキセンテトラカルボン酸無水物、及びポリアゼライン酸無水物等の４官能以上の酸無水物硬化剤等が挙げられる。
　上記熱カチオン開始剤は、特に限定されない。上記熱カチオン開始剤としては、ヨードニウム系カチオン硬化剤、オキソニウム系カチオン硬化剤及びスルホニウム系カチオン硬化剤等が挙げられる。上記ヨードニウム系カチオン硬化剤としては、ビス（４－ｔｅｒｔ－ブチルフェニル）ヨードニウムヘキサフルオロホスファート等が挙げられる。上記オキソニウム系カチオン硬化剤としては、トリメチルオキソニウムテトラフルオロボラート等が挙げられる。上記スルホニウム系カチオン硬化剤としては、トリ－ｐ－トリルスルホニウムヘキサフルオロホスファート等が挙げられる。
　上記熱ラジカル発生剤は、特に限定されない。上記熱ラジカル発生剤としては、アゾ化合物及び有機過酸化物等が挙げられる。上記アゾ化合物としては、アゾビスイソブチロニトリル（ＡＩＢＮ）等が挙げられる。上記有機過酸化物としては、ジ－ｔｅｒｔ－ブチルペルオキシド及びメチルエチルケトンペルオキシド等が挙げられる。
　上記熱硬化剤の反応開始温度は、好ましくは５０℃以上、より好ましくは６０℃以上、さらに好ましくは７０℃以上であり、好ましくは２５０℃以下、より好ましくは２００℃以下、さらに好ましくは１７５℃以下、特に好ましくは１５０℃以下である。上記熱硬化剤の反応開始温度が、上記下限以上及び上記上限以下であると、電極上にはんだ粒子をより一層効率的に配置することができる。上記熱硬化剤の反応開始温度は、７０℃以上１５０℃以下であることが特に好ましい。
　上記熱硬化剤の反応開始温度は、示差走査熱量測定（ＤＳＣ）での発熱ピークの立ち上がり開始の温度を意味する。
　上記熱硬化剤の含有量は、特に限定されない。上記熱硬化性化合物１００重量部に対して、上記熱硬化剤の含有量は、好ましくは０．０１重量部以上、より好ましくは１重量部以上であり、好ましくは２００重量部以下、より好ましくは１００重量部以下、さらに好ましくは７５重量部以下である。上記熱硬化剤の含有量が、上記下限以上であると、導電ペーストを十分に硬化させることが容易である。上記熱硬化剤の含有量が、上記上限以下であると、硬化後に硬化に関与しなかった余剰の熱硬化剤が残存し難くなり、かつ硬化物の耐熱性がより一層高くなる。
　（はんだ粒子）
　上記はんだ粒子は、中心部分及び外表面のいずれもがはんだにより形成されている。上記はんだ粒子は、中心部分及び外表面のいずれもがはんだである粒子である。上記はんだ粒子の代わりに、はんだ以外の材料から形成された基材粒子と該基材粒子の表面上に配置されたはんだ部とを備える導電性粒子を用いた場合には、電極上に導電性粒子が集まり難くなる。また、上記導電性粒子では、導電性粒子同士のはんだ接合性が低いために、電極上に移動した導電性粒子が電極外に移動しやすくなる傾向があり、電極間の位置ずれの抑制効果も低くなる傾向がある。
　上記はんだ粒子の平均粒子径は、５．０μｍ以下である。上記はんだ粒子の平均粒子径は、好ましくは０．１μｍ以上、より好ましくは０．５μｍ以上、さらに好ましくは１．０μｍ以上であり、好ましくは４．９μｍ以下、より好ましくは４．５μｍ以下、さらに好ましくは４．０μｍ以下である。上記はんだ粒子の平均粒子径が、上記下限以上及び上記上限以下であると、電極上にはんだ粒子をより一層効率的に配置することができる。上記はんだ粒子の平均粒子径が、上記上限以下であると、ファインピッチ化した基材等に対するスクリーン印刷性をより一層高めることができる。本発明に係る導電ペーストでは、上記はんだ粒子の平均粒子径が小さいほど、本発明の上記の効果がより一層効果的に発揮される。即ち、本発明に係る導電ペーストでは、上記はんだ粒子の平均粒子径が小さいほど、電極上にはんだ粒子をより一層効率的に配置することができ、接続されるべき上下の電極間の導通信頼性を効果的に高めることができ、接続されてはならない隣接する横方向の電極間の絶縁信頼性を効果的に高めることができる。
　上記はんだ粒子の平均粒子径は、数平均粒子径であることが好ましい。上記はんだ粒子の平均粒子径は、例えば、任意のはんだ粒子５０個を電子顕微鏡又は光学顕微鏡にて観察し、各はんだ粒子の粒子径の平均値を算出することや、レーザー回折式粒度分布測定を行うことにより求められる。電子顕微鏡又は光学顕微鏡での観察では、１個当たりのはんだ粒子の粒子径は、円相当径での粒子径として求められる。電子顕微鏡又は光学顕微鏡での観察において、任意の５０個のはんだ粒子の円相当径での平均粒子径は、球相当径での平均粒子径とほぼ等しくなる。レーザー回折式粒度分布測定では、１個当たりのはんだ粒子の粒子径は、球相当径での粒子径として求められる。上記はんだ粒子の平均粒子径は、レーザー回折式粒度分布測定により算出することが好ましい。
　上記はんだ粒子の粒子径の変動係数（ＣＶ値）は、好ましくは５％以上、より好ましくは１０％以上であり、好ましくは４０％以下、より好ましくは３０％以下である。上記はんだ粒子の粒子径の変動係数が、上記下限以上及び上記上限以下であると、電極上にはんだ粒子をより一層効率的に配置することができる。但し、上記はんだ粒子の粒子径のＣＶ値は、５％未満であってもよい。
　上記変動係数（ＣＶ値）は、以下のようにして測定できる。
　ＣＶ値（％）＝（ρ／Ｄｎ）×１００
　ρ：はんだ粒子の粒子径の標準偏差
　Ｄｎ：はんだ粒子の粒子径の平均値
　上記はんだ粒子の形状は、特に限定されない。上記はんだ粒子の形状は、球状であってもよく、球状以外の形状であってもよく、扁平状等の形状であってもよい。
　電極上にはんだ粒子をより一層効率的に配置する観点からは、上記はんだ粒子の比重は、好ましくは４以上、より好ましくは５以上、さらに好ましくは６以上である。
　上記はんだ粒子の比重は、例えば、島津製作所社製「アキュピックＩＩ　１３４０」により求められる。
　上記はんだは、融点が４５０℃以下である金属（低融点金属）であることが好ましい。上記はんだ粒子は、融点が４５０℃以下である金属粒子（低融点金属粒子）であることが好ましい。上記低融点金属粒子は、低融点金属を含む粒子である。該低融点金属とは、融点が４５０℃以下の金属を示す。低融点金属の融点は好ましくは３００℃以下、より好ましくは２６０℃以下である。上記はんだは、融点が２５０℃未満の低融点はんだであることが好ましい。
　接続信頼性をより一層高める観点からは、上記はんだ粒子の融点は、好ましくは１００℃以上、より好ましくは１５０℃以上、さらに好ましくは２００℃以上であり、好ましくは４００℃以下、より好ましくは３５０℃以下、さらに好ましくは３００℃以下である。
　上記はんだ粒子の融点は、示差走査熱量測定（ＤＳＣ）により求めることができる。示差走査熱量測定（ＤＳＣ）装置としては、ＳＩＩ社製「ＥＸＳＴＡＲ　ＤＳＣ７０２０」等が挙げられる。
　また、上記はんだ粒子は錫を含むことが好ましい。上記はんだ粒子に含まれる金属１００重量％中、錫の含有量は、好ましくは３０重量％以上、より好ましくは４０重量％以上、さらに好ましくは７０重量％以上、特に好ましくは９０重量％以上である。上記はんだ粒子における錫の含有量が、上記下限以上であると、はんだ部と電極との導通信頼性及び接続信頼性がより一層高くなる。
　なお、上記錫の含有量は、高周波誘導結合プラズマ発光分光分析装置（例えば、堀場製作所社製「ＩＣＰ－ＡＥＳ」）、又は蛍光Ｘ線分析装置（例えば、島津製作所社製「ＥＤＸ－８００ＨＳ」）等を用いて測定することができる。
　上記はんだ粒子を用いることで、はんだが溶融して電極に接合し、はんだ部が電極間を導通させる。例えば、はんだ部と電極とが点接触ではなく面接触しやすいため、接続抵抗が低くなる。また、上記はんだ粒子の使用により、はんだ部と電極との接合強度が高くなる結果、はんだ部と電極との剥離がより一層生じ難くなり、導通信頼性及び接続信頼性がより一層高くなる。
　上記はんだ粒子を構成する低融点金属は特に限定されない。該低融点金属は、錫、又は錫を含む合金であることが好ましい。該合金は、錫－銀合金、錫－銅合金、錫－銀－銅合金、錫－ビスマス合金、錫－亜鉛合金、錫－インジウム合金、及び錫－アンチモン合金等が挙げられる。電極に対する濡れ性に優れることから、上記低融点金属は、錫、錫－銀合金、錫－銀－銅合金、錫－ビスマス合金、錫－インジウム合金、又は錫－アンチモン合金であることが好ましく、錫－銀－銅合金、錫－ビスマス合金、錫－インジウム合金、又は錫－アンチモン合金であることがより好ましい。
　上記はんだ粒子は、ＪＩＳ　Ｚ３００１：溶接用語に基づき、液相線が４５０℃以下である溶加材であることが好ましい。上記はんだ粒子の組成としては、例えば亜鉛、金、銀、鉛、銅、錫、ビスマス、及びインジウム等を含む金属組成が挙げられる。低融点で鉛フリーである錫－インジウム系（１１７℃共晶）、又は錫－ビスマス系（１３９℃共晶）が好ましい。すなわち、上記はんだ粒子は、鉛を含まないことが好ましく、錫とインジウムとを含むか、又は錫とビスマスとを含むことが好ましい。
　はんだ部と電極との接合強度をより一層高めるために、上記はんだ粒子は、ニッケル、銅、アンチモン、アルミニウム、亜鉛、鉄、金、チタン、リン、ゲルマニウム、テルル、コバルト、ビスマス、マンガン、クロム、モリブデン、及びパラジウム等の金属を含んでいてもよい。また、はんだ部と電極との接合強度をさらに一層高める観点からは、上記はんだ粒子は、ニッケル、銅、アンチモン、アルミニウム又は亜鉛を含むことが好ましい。はんだ部と電極との接合強度をより一層高める観点からは、接合強度を高めるためのこれらの金属の含有量は、はんだ粒子に含まれる金属１００重量％中、好ましくは０．０００１重量％以上、好ましくは１重量％以下である。
　上記導電ペースト１００重量％中、上記はんだ粒子の含有量は、好ましくは５０重量％以上、より好ましくは５５重量％以上、さらに好ましくは６０重量％以上、特に好ましくは６５重量％以上、最も好ましくは７０重量％以上である。上記導電ペースト１００重量％中、上記はんだ粒子の含有量は、好ましくは９０重量％以下、より好ましくは８５重量％以下、さらに好ましくは８０重量％以下、特に好ましくは７５重量％以下である。上記はんだ粒子の含有量が、上記下限以上及び上記上限以下であると、電極上にはんだ粒子をより一層効率的に配置することができ、電極間にはんだを多く配置することが容易であり、導通信頼性がより一層高くなる。導通信頼性をより一層高める観点からは、上記はんだ粒子の含有量は多い方が好ましい。
　（フラックス）
　本発明に係る導電ペーストは、フラックスを含む。上記フラックスは、２５℃で固体である。具体的には、上記熱硬化性成分、複数のはんだ粒子、及びチキソトロピック剤と混合されていない状態で、上記フラックス（フラックス単体）が、２５℃で固体である。
　上記導電ペーストでは、２５℃の導電ペースト中で、上記フラックスが固体であることが好ましい。上記導電ペーストでは、２５℃の導電ペースト中で、上記フラックスが固体で存在することが好ましい。
　なお、上記フラックス（フラックス単体）が２５℃で固体であるか否かについては、以下のように判断することができる。本明細書において、２５℃で液体ではないフラックスに関しては、２５℃及び５０％ＲＨでフラックス単体を５分間静置したときに形状を保つフラックスを、２５℃で固体のフラックスと定義する。また、２５℃及び５０％ＲＨでフラックス単体を５分間静置したときに形状を保たないフラックスを、２５℃で半固体のフラックスと定義する。また、２５℃で半固体のフラックスは、２５℃で固体のフラックスに含まれない。
　なお、上記フラックスが２５℃の導電ペースト中で固体であるか否かについては、以下のように判断することができる。本明細書において、２５℃で液体ではないフラックスに関しては、２５℃及び５０％ＲＨでフラックスを含む導電ペーストを５分間静置したときに形状を保つフラックスを、２５℃で固体のフラックスと定義する。また、２５℃及び５０％ＲＨでフラックスを含む導電ペーストを５分間静置したときに形状を保たないフラックスを、２５℃で半固体のフラックスと定義する。また、２５℃で半固体のフラックスは、２５℃で固体のフラックスに含まれない。
　上記フラックスとしては、塩化亜鉛、塩化亜鉛と無機ハロゲン化物との混合物、塩化亜鉛と無機酸との混合物、溶融塩、有機リン化合物、有機ハロゲン化物、ヒドラジン、アミン化合物、有機酸、有機酸の塩、及び松脂等が挙げられる。上記フラックスは、１種のみが用いられてもよく、２種以上が併用されてもよい。
　上記溶融塩としては、塩化アンモニウム等が挙げられる。
　上記有機リン化合物としては、有機ホスホニウム塩、有機リン酸、有機リン酸エステル、有機ホスホン酸、有機ホスホン酸エステル、有機ホスフィン酸、及び有機ホスフィン酸エステル等が挙げられる。
　上記アミン化合物としては、シクロヘキシルアミン、ジシクロヘキシルアミン、ベンジルアミン、ベンズヒドリルアミン、イミダゾール、ベンゾイミダゾール、フェニルイミダゾール、カルボキシベンゾイミダゾール、ベンゾトリアゾール、及びカルボキシベンゾトリアゾール等が挙げられる。
　上記松脂は、アビエチン酸を主成分とするロジン類である。上記ロジン類としては、アビエチン酸、及びアクリル変性ロジン等が挙げられる。
　上記有機酸の塩としては、有機酸と塩基化合物との中和反応物（塩）が挙げられる。上記有機酸の塩は、有機酸と塩基化合物との中和反応により生じた塩であることが好ましい。上記中和反応の条件としては、２５℃～１５０℃の加熱温度及び５分間～３０分間の加熱時間の条件であることが好ましい。上記有機酸は、金属の表面を洗浄する効果を有することが好ましく、上記塩基化合物は、上記有機酸を中和する作用を有することが好ましい。
　上記有機酸は、カルボキシル基を有する有機化合物（カルボン酸）であることが好ましい。上記有機酸としては、脂肪族系カルボン酸、脂環式カルボン酸、及び芳香族カルボン酸等が挙げられる。上記脂肪族系カルボン酸としては、マロン酸、コハク酸、グルタル酸、アジピン酸、ピメリン酸、スベリン酸、アゼライン酸、セバシン酸、クエン酸、及びリンゴ酸等が挙げられる。上記脂環式カルボン酸としては、シクロヘキシルカルボン酸、及び１，４－シクロヘキシルジカルボン酸等が挙げられる。上記芳香族カルボン酸としては、イソフタル酸、テレフタル酸、トリメリット酸、及びエチレンジアミン四酢酸等が挙げられる。電極上にはんだ粒子をより一層効率的に配置し、絶縁信頼性を高め、導通信頼性をより一層効果的に高める観点からは、上記有機酸は、グルタル酸、シクロヘキシルカルボン酸、又はアジピン酸であることが好ましい。
　上記塩基化合物は、アミノ基を有する有機化合物（アミン化合物）であることが好ましい。上記塩基化合物としては、ジエタノールアミン、トリエタノールアミン、メチルジエタノールアミン、エチルジエタノールアミン、シクロヘキシルアミン、ジシクロヘキシルアミン、ベンジルアミン、ベンズヒドリルアミン、２－メチルベンジルアミン、３－メチルベンジルアミン、４－ｔｅｒｔ－ブチルベンジルアミン、Ｎ－メチルベンジルアミン、Ｎ－エチルベンジルアミン、Ｎ－フェニルベンジルアミン、Ｎ－ｔｅｒｔ－ブチルベンジルアミン、Ｎ－イソプロピルベンジルアミン、Ｎ，Ｎ－ジメチルベンジルアミン、イミダゾール化合物、及びトリアゾール化合物が挙げられる。電極上にはんだ粒子をより一層効率的に配置し、絶縁信頼性を高め、導通信頼性をより一層効果的に高める観点からは、上記塩基化合物は、ベンジルアミンであることが好ましい。
　上記有機酸の塩としては、アジピン酸ベンジルアミン塩、グルタル酸ベンジルアミン塩、及びコハク酸シクロヘキシルアミン塩等が挙げられる。
　タック性をより一層効果的に維持し、電極上にはんだ粒子をより一層効率的に配置する観点からは、上記フラックスは、有機酸の塩であることが好ましく、アジピン酸ベンジルアミン塩であることが特に好ましい。
　上記フラックスは、導電ペースト中に分散されていてもよく、はんだ粒子の表面上に付着していてもよい。
　上記フラックスの形状は、特に限定されない。上記フラックスは、球状であってもよく、球状以外の形状であってもよく、扁平状等の形状であってもよい。スクリーン印刷性をより一層高める観点からは、上記フラックスの形状は、球状であることが好ましい。
　上記フラックスの粒子径は、好ましくは０．１μｍ以上、より好ましくは０．５μｍ以上、さらに好ましくは１．０μｍ以上であり、好ましくは３０μｍ以下、より好ましくは２５μｍ以下、さらに好ましくは２０μｍ以下である。
　上記フラックスの粒子径は、平均粒子径であることが好ましく、数平均粒子径であることがより好ましい。上記フラックスの平均粒子径は、例えば、任意のフラックス５０個を電子顕微鏡又は光学顕微鏡にて観察し、各フラックスの粒子径の平均値を算出することや、レーザー回折式粒度分布測定を行うことにより求められる。電子顕微鏡又は光学顕微鏡での観察では、１個当たりのフラックスの粒子径は、円相当径での粒子径として求められる。電子顕微鏡又は光学顕微鏡での観察において、任意の５０個のフラックスの円相当径での平均粒子径は、球相当径での平均粒子径とほぼ等しくなる。レーザー回折式粒度分布測定では、１個当たりのフラックスの粒子径は、球相当径での粒子径として求められる。上記フラックスの平均粒子径は、レーザー回折式粒度分布測定により算出することが好ましい。
　上記フラックスの平均粒子径の、上記はんだ粒子の平均粒子径に対する比（フラックスの平均粒子径／はんだ粒子の平均粒子径）は、好ましくは０．０１以上、より好ましくは０．１以上、さらに好ましくは０．２以上であり、好ましくは１５．０以下、より好ましくは１０．０以下、さらに好ましくは５．０以下である。上記比（フラックスの平均粒子径／はんだ粒子の平均粒子径）が上記下限以上及び上記上限以下であると、フラックスをはんだ粒子に対して効果的に接触させることができ、加熱時のフラックス性能をより一層高めることができる。
　本発明の効果をより一層効果的に発揮する観点からは、上記フラックスは、吸水性を有さないことが好ましく、吸湿性を有さないことが好ましい。
　上記フラックスを２５℃及び５０％ＲＨで２４時間放置したときに、上記フラックスの重量は、増加してもよく、減少してもよく、変化しなくてもよい。上記フラックスを２５℃及び５０％ＲＨで２４時間放置したときに、放置後の上記フラックスの重量は、放置前の上記フラックスの重量よりも、大きくてもよく、小さくてもよい。上記フラックスを２５℃及び５０％ＲＨで２４時間放置したときに、放置後の上記フラックスの重量は、放置前の上記フラックスの重量と、同じであってもよい。
　本発明の効果をより一層効果的に発揮する観点からは、上記フラックスを２５℃及び５０％ＲＨで２４時間放置したときの、下記の重量変化率Ｆは、好ましくは１重量％未満、より好ましくは０．９重量％以下、さらに好ましくは０．５重量％以下である。上記重量変化率Ｆは、０重量％以上であってもよく、０．１重量％以上であってもよい。本発明の効果をより一層効果的に発揮する観点からは、上記重量変化率Ｆは、最も好ましくは０重量％（放置前後で重量変化なし）である。
　重量変化率Ｆ（重量％）＝｜Ｗ４－Ｗ３｜×１００／Ｗ３
　Ｗ３：放置前の上記フラックスの重量
　Ｗ４：放置後の上記フラックスの重量
　上記フラックスの重量変化率Ｆは、以下の方法で測定することができる。フラックス１０ｇ（Ｗ３）を２５℃及び０％ＲＨのデシケータから取り出し、２５℃及び５０％ＲＨで２４時間放置したときの、放置後のフラックスの重量（Ｗ４）を測定する。Ｗ３及びＷ４より、重量変化率Ｆを求める。
　上記フラックスの融点（活性温度）は、好ましくは５０℃以上、より好ましくは８０℃以上、さらに好ましくは１００℃以上であり、好ましくは３００℃以下、より好ましくは２５０℃以下、さらに好ましくは２００℃以下である。上記フラックスの融点が、上記下限以上及び上記上限以下であると、電極上にはんだ粒子をより一層効率的に配置することができる。
　上記フラックスの融点は、示差走査熱量測定（ＤＳＣ）により求めることができる。示差走査熱量測定（ＤＳＣ）装置としては、ＳＩＩ社製「ＥＸＳＴＡＲ　ＤＳＣ７０２０」等が挙げられる。
　上記導電ペースト１００重量％中、上記フラックスの含有量は、好ましくは１重量％以上、より好ましくは５重量％以上であり、好ましくは３０重量％以下、より好ましくは２５重量％以下である。上記フラックスの含有量が、上記下限以上及び上記上限以下であると、はんだ粒子及び電極の表面に酸化被膜がより一層形成され難くなり、さらに、はんだ粒子及び電極の表面に形成された酸化被膜をより一層効果的に除去できる。
　上記熱硬化性成分１００重量部に対して、上記フラックスの含有量は、好ましくは１重量部以上、より好ましくは５重量部以上であり、好ましくは３０重量部以下、より好ましくは２５重量部以下である。上記フラックスの含有量が、上記下限以上及び上記上限以下であると、はんだ粒子及び電極の表面に酸化被膜がより一層形成され難くなり、さらに、はんだ粒子及び電極の表面に形成された酸化被膜をより一層効果的に除去できる。
　上記はんだ粒子１００重量部に対して、上記フラックスの含有量は、好ましくは１重量部以上、より好ましくは５重量部以上であり、好ましくは３０重量部以下、より好ましくは２５重量部以下である。上記フラックスの含有量が、上記下限以上及び上記上限以下であると、はんだ粒子及び電極の表面に酸化被膜がより一層形成され難くなり、さらに、はんだ粒子及び電極の表面に形成された酸化被膜をより一層効果的に除去できる。
　（チキソトロピック剤）
　本発明に係る導電ペーストは、チキソトロピック剤を含む。上記チキソトロピック剤は、（Ａ）２５℃で液体であり、かつ水酸基を有するチキソトロピック剤であるか、又は、（Ｂ）２５℃で固体であり、かつ上記チキソトロピック剤を２５℃及び５０％ＲＨで２４時間放置したときの、下記の重量増加率が０．２重量％以上であるチキソトロピック剤である。
　重量増加率（重量％）＝（Ｗ２－Ｗ１）×１００／Ｗ１
　Ｗ１：放置前の上記チキソトロピック剤の重量
　Ｗ２：放置後の上記チキソトロピック剤の重量
　上記チキソトロピック剤は、（Ａ）２５℃で液体であり、かつ水酸基を有するチキソトロピック剤（以下、「チキソトロピック剤Ａ」とすることがある）であってもよい。また、上記チキソトロピック剤は、（Ｂ）２５℃で固体であり、かつ上記重量増加率が０．２重量％以上であるチキソトロピック剤（以下、「チキソトロピック剤Ｂ」とすることがある）であってもよい。上記チキソトロピック剤は、上記チキソトロピック剤Ａ又は上記チキソトロピック剤Ｂである。
　上記導電ペーストでは、上記チキソトロピック剤が、上記チキソトロピック剤Ａ又は上記チキソトロピック剤Ｂであるので、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。
　上記導電ペースト１００重量％中、上記チキソトロピック剤の含有量は、好ましくは０．００５重量％以上、より好ましくは０．０１重量％以上、さらに好ましくは０．０５重量％以上であり、好ましくは２重量％以下、より好ましくは１重量％以下、さらに好ましくは０．５重量％以下である。上記チキソトロピック剤の含有量が、上記下限以上及び上記上限以下であると、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。
　上記はんだ粒子１００重量部に対して、上記チキソトロピック剤の含有量は、好ましくは０．００３重量部以上、より好ましくは０．００５重量部以上、さらに好ましくは０．０１重量部以上であり、好ましくは２重量部以下、より好ましくは１重量部以下、さらに好ましくは０．７重量部以下である。上記チキソトロピック剤の含有量が、上記下限以上及び上記上限以下であると、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。
　上記熱硬化性成分１００重量部に対して、上記チキソトロピック剤の含有量は、好ましくは０．１重量部以上、より好ましくは０．３重量部以上であり、好ましくは５重量部以下、より好ましくは３重量部以下である。上記チキソトロピック剤の含有量が、上記下限以上及び上記上限以下であると、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。
　上記熱硬化性化合物１００重量部に対して、上記チキソトロピック剤の含有量は、好ましくは０．１重量部以上、より好ましくは０．３重量部以上であり、好ましくは５重量部以下、より好ましくは３重量部以下である。上記チキソトロピック剤の含有量が、上記下限以上及び上記上限以下であると、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。
　［チキソトロピック剤Ａ］
　上記チキソトロピック剤Ａは、２５℃で液体であり、かつ水酸基（－ＯＨ基）を有する。
　上記チキソトロピック剤Ａは、２５℃で液体である。具体的には、上記熱硬化性成分、複数のはんだ粒子、及びフラックスと混合されていない状態で、上記チキソトロピック剤Ａ（チキソトロピック剤Ａ単体）が、２５℃で液体である。
　上記導電ペーストでは、２５℃の導電ペースト中で、上記チキソトロピック剤Ａが液体であることが好ましい。上記導電ペーストでは、２５℃の導電ペースト中で、上記チキソトロピック剤Ａが液体で存在することが好ましい。
　上記チキソトロピック剤Ａは、水酸基を少なくとも１個有する。上記チキソトロピック剤Ａは、水酸基を１個有していてもよく、２個有していてもよく、２個以上有していてもよく、３個有していてもよく、３個以上有していてもよく、４個以上有していてもよい。上記チキソトロピック剤Ａは、１価アルコールであってもよく、多価アルコールであってもよい。上記チキソトロピック剤Ａは、２価アルコールであってもよく、３価アルコールであってもよく、４価アルコールであってもよい。導電ペーストの揮発を防ぎ、スクリーン印刷性をより一層高める観点からは、上記チキソトロピック剤Ａは、水酸基を２個以上有することが好ましく、３個以上有することがより好ましい。導電ペーストの揮発を防ぎ、スクリーン印刷性をより一層高める観点からは、上記チキソトロピック剤Ａは、ポリオール化合物（多価アルコール）であることが好ましい。上記チキソトロピック剤Ａは、水酸基を１０個以下で有していてもよく、７個以下で有していてもよい。
　上記チキソトロピック剤Ａのうち水酸基を１個有するチキソトロピック剤としては、メタノール、エタノール、プロパノール、及びＮ－オレオイルサルコシン等が挙げられる。
　上記チキソトロピック剤Ａのうち水酸基を２個有するチキソトロピック剤としては、プロピレングリコール、プロパンジオール、及びジエチレングリコール等が挙げられる。
　上記チキソトロピック剤Ａのうち水酸基を３個有するチキソトロピック剤としては、グリセロール（グリセリン）、トリメチロールプロパン、及び１，２，４－ブタントリオール等が挙げられる。
　上記チキソトロピック剤Ａのうち水酸基を４個以上有するチキソトロピック剤としては、ジグリセリン、及びポリグリセリン等が挙げられる。
　導電ペーストの揮発を防ぎ、スクリーン印刷性をより一層高める観点からは、上記チキソトロピック剤Ａは、グリセロール（グリセリン）、Ｎ－オレオイルサルコシン、又は１，２，４－ブタントリオールであることが好ましく、グリセロール（グリセリン）であることがより好ましい。
　タック性をより一層効果的に維持する観点からは、上記チキソトロピック剤Ａの沸点は、好ましくは８０℃以上、より好ましくは１００℃以上、さらに好ましくは１５０℃以上、特に好ましくは２００℃以上であり、好ましくは４５０℃以下、より好ましくは４００℃以下、さらに好ましくは３５０℃以下である。導電ペーストの揮発を防ぎ、スクリーン印刷性をより一層高める観点からは、上記チキソトロピック剤Ａは、（Ａ１）２５℃で液体であり、水酸基を有し、かつ沸点が８０℃以上であるチキソトロピック剤であることが好ましい。
　上記導電ペースト１００重量％中、上記チキソトロピック剤Ａの含有量は、好ましくは０．００１重量％以上、より好ましくは０．００５重量％以上、さらに好ましくは０．０５重量％以上であり、好ましくは２重量％以下、より好ましくは１重量％以下、さらに好ましくは０．５重量％以下である。上記チキソトロピック剤Ａの含有量が、上記下限以上及び上記上限以下であると、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。
　上記はんだ粒子１００重量部に対して、上記チキソトロピック剤Ａの含有量は、好ましくは０．００３重量部以上、より好ましくは０．００５重量部以上、さらに好ましくは０．０１重量部以上であり、好ましくは２重量部以下、より好ましくは１重量部以下、さらに好ましくは０．７重量部以下である。上記チキソトロピック剤Ａの含有量が、上記下限以上及び上記上限以下であると、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。
　［チキソトロピック剤Ｂ］
　上記チキソトロピック剤Ｂは、２５℃で固体であり、かつ上記チキソトロピック剤を２５℃及び５０％ＲＨで２４時間放置したときの、下記の重量増加率が０．２重量％以上である。
　重量増加率（重量％）＝（Ｗ２－Ｗ１）×１００／Ｗ１
　Ｗ１：放置前の上記チキソトロピック剤の重量
　Ｗ２：放置後の上記チキソトロピック剤の重量
　上記チキソトロピック剤Ｂは、２５℃で固体である。具体的には、上記熱硬化性成分、複数のはんだ粒子、及びフラックスと混合されていない状態で、上記チキソトロピック剤Ｂ（チキソトロピック剤Ｂ単体）が、２５℃で固体である。
　上記導電ペーストでは、２５℃の導電ペースト中で、上記チキソトロピック剤Ｂが固体であることが好ましい。上記導電ペーストでは、２５℃の導電ペースト中で、上記チキソトロピック剤Ｂが固体で存在することが好ましい。
　なお、上記チキソトロピック剤Ｂ（チキソトロピック剤Ｂ単体）が２５℃で固体であるか否かについては、以下のように判断することができる。本明細書において、２５℃で液体ではないチキソトロピック剤Ｂに関しては、２５℃及び５０％ＲＨでチキソトロピック剤Ｂ単体を５分間静置したときに形状を保つチキソトロピック剤Ｂを、２５℃で固体のチキソトロピック剤Ｂと定義する。また、２５℃及び５０％ＲＨでチキソトロピック剤Ｂ単体を５分間静置したときに形状を保たないチキソトロピック剤Ｂを、２５℃で半固体のチキソトロピック剤Ｂと定義する。なお、２５℃で半固体のチキソトロピック剤Ｂは、２５℃で固体のチキソトロピック剤Ｂに含まれない。
　なお、上記チキソトロピック剤Ｂが２５℃の導電ペースト中で固体であるか否かについては、以下のように判断することができる。本明細書において、２５℃で液体ではないチキソトロピック剤Ｂに関しては、２５℃及び５０％ＲＨでチキソトロピック剤Ｂを含む導電ペーストを５分間静置したときに形状を保つチキソトロピック剤Ｂを、２５℃で固体のチキソトロピック剤Ｂと定義する。また、２５℃及び５０％ＲＨでチキソトロピック剤Ｂを含む導電ペーストを５分間静置したときに形状を保たないチキソトロピック剤Ｂを、２５℃で半固体のチキソトロピック剤Ｂと定義する。なお、２５℃で半固体のチキソトロピック剤Ｂは、２５℃で固体のチキソトロピック剤Ｂに含まれない。
　上記チキソトロピック剤Ｂは、２５℃及び５０％ＲＨで２４時間放置したときに、重量が増加する。上記チキソトロピック剤Ｂを２５℃及び５０％ＲＨで２４時間放置したときに、放置後の上記チキソトロピック剤Ｂの重量は、放置前の上記チキソトロピック剤Ｂの重量よりも大きい。
　フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置する観点からは、上記チキソトロピック剤Ｂは、吸水性又は吸湿性を有することが好ましく、吸湿性を有することがより好ましい。フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置する観点からは、上記チキソトロピック剤Ｂは、２５℃及び５０％ＲＨで吸湿性を有することがさらに好ましい。
　上記チキソトロピック剤Ｂの重量増加率は、０．２重量％以上である。上記チキソトロピック剤Ｂの上記重量増加率は、好ましくは０．３重量％以上、より好ましくは０．５重量％以上、さらに好ましくは１重量％以上であり、好ましくは１０重量％未満、より好ましくは８重量％以下、さらに好ましくは５重量％以下である。上記チキソトロピック剤Ｂの重量増加率が、上記下限以上であると、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。上記チキソトロピック剤Ｂの重量増加率が、上記上限以下又は上記上限未満であると、スクリーン印刷性をより一層高めることができる。フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置する観点からは、上記チキソトロピック剤Ｂが、２５℃で固体であり、かつ上記重量増加率が１重量％以上であるチキソトロピック剤であることが特に好ましい。
　上記チキソトロピック剤Ｂの重量増加率は、以下の方法で測定することができる。チキソトロピック剤Ｂ１０ｇ（Ｗ１）を２５℃及び０％ＲＨのデシケータから取り出し、２５℃及び５０％ＲＨで２４時間放置したときの、放置後のチキソトロピック剤Ｂの重量（Ｗ２）を測定する。
　上記チキソトロピック剤Ｂとしては、三フッ化ホウ素－モノエチルアミン錯体、ペンタエリスリトール、ソルビトール、マンニトール、ソルビタン、ジペンタエリスリトール、ショ糖、グルコース、マンノース、フルクトース、及びメチルグルコシド等が挙げられる。
　電極上にはんだ粒子をより一層効率的に配置する観点からは、上記チキソトロピック剤Ｂは、三フッ化ホウ素－モノエチルアミン錯体、又はグルコースであることが好ましく、三フッ化ホウ素－モノエチルアミン錯体であることがより好ましい。
　上記チキソトロピック剤Ｂの形状は、特に限定されない。上記チキソトロピック剤Ｂは、球状であってもよく、球状以外の形状であってもよく、扁平状等の形状であってもよい。スクリーン印刷性をより一層高める観点からは、上記チキソトロピック剤Ｂの形状は、球状であることが好ましい。
　上記チキソトロピック剤Ｂの粒子径は、好ましくは０．１μｍ以上、より好ましくは０．５μｍ以上、さらに好ましくは１μｍ以上であり、好ましくは３０μｍ以下、より好ましくは２５μｍ以下、さらに好ましくは２０μｍ以下である。
　上記チキソトロピック剤Ｂの粒子径は、平均粒子径であることが好ましく、数平均粒子径であることがより好ましい。上記チキソトロピック剤Ｂの平均粒子径は、例えば、任意のチキソトロピック剤Ｂ５０個を電子顕微鏡又は光学顕微鏡にて観察し、各チキソトロピック剤Ｂの粒子径の平均値を算出することや、レーザー回折式粒度分布測定を行うことにより求められる。電子顕微鏡又は光学顕微鏡での観察では、１個当たりのチキソトロピック剤Ｂの粒子径は、円相当径での粒子径として求められる。電子顕微鏡又は光学顕微鏡での観察において、任意の５０個のチキソトロピック剤Ｂの円相当径での平均粒子径は、球相当径での平均粒子径とほぼ等しくなる。レーザー回折式粒度分布測定では、１個当たりのチキソトロピック剤Ｂの粒子径は、球相当径での粒子径として求められる。上記チキソトロピック剤Ｂの平均粒子径は、レーザー回折式粒度分布測定により算出することが好ましい。
　上記チキソトロピック剤Ｂの融点（活性温度）は、好ましくは５０℃以上、より好ましくは６０℃以上、さらに好ましくは７０℃以上であり、好ましくは１４０℃以下、より好ましくは１２０℃以下、さらに好ましくは１００℃以下である。上記チキソトロピック剤Ｂの融点が、上記下限以上及び上記上限以下であると、電極上にはんだ粒子をより一層効率的に配置することができる。
　上記チキソトロピック剤Ｂの融点は、示差走査熱量測定（ＤＳＣ）により求めることができる。示差走査熱量測定（ＤＳＣ）装置としては、ＳＩＩ社製「ＥＸＳＴＡＲ　ＤＳＣ７０２０」等が挙げられる。
　電極上にはんだ粒子をより一層効率的に配置する観点からは、上記チキソトロピック剤Ｂの融点は、上記はんだ粒子の融点よりも低いことが好ましい。電極上にはんだ粒子をより一層効率的に配置する観点からは、上記チキソトロピック剤Ｂの融点は、上記はんだ粒子の融点よりも、５℃以上低いことがより好ましく、１０℃以上低いことがさらに好ましい。
　上記導電ペースト１００重量％中、上記チキソトロピック剤Ｂの含有量は、好ましくは０．００１重量％以上、より好ましくは０．００５重量％以上であり、好ましくは２重量％以下、より好ましくは１重量％以下、さらに好ましくは０．５重量％以下である。上記チキソトロピック剤Ｂの含有量が、上記下限以上及び上記上限以下であると、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。
　上記はんだ粒子１００重量部に対して、上記チキソトロピック剤Ｂの含有量は、好ましくは０．００５重量部以上、より好ましくは０．０１重量部以上であり、好ましくは２重量部以下、より好ましくは１重量部以下、さらに好ましくは０．７重量部以下である。上記チキソトロピック剤Ｂの含有量が、上記下限以上及び上記上限以下であると、フラックス性能を良好に補助し、電極上にはんだ粒子をより一層効率的に配置することができる。
　（他の成分）
　上記導電ペーストは、必要に応じて、例えば、充填剤、増量剤、軟化剤、可塑剤、レベリング剤、重合触媒、硬化触媒、着色剤、酸化防止剤、熱安定剤、光安定剤、紫外線吸収剤、滑剤、帯電防止剤及び難燃剤等の各種添加剤を含んでいてもよい。
　（接続構造体）
　本発明に係る接続構造体は、第１の電極を表面に有する第１の接続対象部材と、第２の電極を表面に有する第２の接続対象部材と、上記第１の接続対象部材と、上記第２の接続対象部材とを接続している接続部とを備える。本発明に係る接続構造体では、上記接続部の材料が、上述した導電ペーストである。本発明に係る接続構造体では、上記第１の電極と上記第２の電極とが、上記接続部中のはんだ部により電気的に接続されている。
　電極間でのはんだ部の厚みは、好ましくは１０μｍ以上、より好ましくは２０μｍ以上であり、好ましくは１００μｍ以下、より好ましくは８０μｍ以下である。電極の表面上のはんだ濡れ面積（電極の露出した面積１００％中のはんだが接している面積）は、好ましくは５０％以上、より好ましくは７０％以上であり、好ましくは１００％以下である。
　上記接続構造体の製造方法は、特に限定されない。接続構造体の製造方法の一例としては、第１の接続対象部材と第２の接続対象部材との間に上記導電ペーストを配置し、積層体を得た後、該積層体を加熱する方法等が挙げられる。上記加熱の温度は、好ましくは２３０℃以上、より好ましくは２５０℃以上であり、好ましくは３５０℃以下、より好ましくは３００℃以下である。上記加熱の温度が、上記下限以上及び上記上限以下であると、電極間の導通信頼性及び絶縁信頼性をより一層高めることができる。上記加熱時には、加圧を行ってもよく、加圧を行わなくてもよい。
　以下、図面を参照しつつ、本発明の具体的な実施形態を説明する。
　図１は、本発明の一実施形態に係る導電ペーストを用いて得られる接続構造体を模式的に示す断面図である。
　図１に示す接続構造体１は、第１の接続対象部材２と、第２の接続対象部材３と、第１の接続対象部材２と第２の接続対象部材３とを接続している接続部４とを備える。接続部４は、上述した導電ペーストにより形成されている。本実施形態では、上記導電ペーストは、熱硬化性成分と、はんだ粒子と、フラックスと、チキソトロピック剤とを含む。上記熱硬化性成分は、熱硬化性化合物と熱硬化剤とを含む。上記チキソトロピック剤は、上記チキソトロピック剤Ａ又は上記チキソトロピック剤Ｂである。
　接続部４は、複数のはんだ粒子が集まり互いに接合したはんだ部４Ａと、熱硬化性化合物が熱硬化された硬化物部４Ｂとを有する。
　第１の接続対象部材２は表面（上面）に、複数の第１の電極２ａを有する。第２の接続対象部材３は表面（下面）に、複数の第２の電極３ａを有する。第１の電極２ａと第２の電極３ａとが、はんだ部４Ａにより電気的に接続されている。従って、第１の接続対象部材２と第２の接続対象部材３とが、はんだ部４Ａにより電気的に接続されている。なお、接続部４において、第１の電極２ａと第２の電極３ａとの間に集まったはんだ部４Ａとは異なる領域（硬化物部４Ｂ部分）には、はんだ粒子は存在しない。はんだ部４Ａとは異なる領域（硬化物部４Ｂ部分）には、はんだ部４Ａと離れたはんだ粒子は存在しない。なお、少量であれば、第１の電極２ａと第２の電極３ａとの間に集まったはんだ部４Ａとは異なる領域（硬化物部４Ｂ部分）に、はんだ粒子が存在していてもよい。
　図１に示すように、接続構造体１では、第１の電極２ａと第２の電極３ａとの間に、複数のはんだ粒子が集まり、複数のはんだ粒子が溶融した後、はんだ粒子の溶融物が電極の表面を濡れ拡がった後に固化して、はんだ部４Ａが形成されている。このため、はんだ部４Ａと第１の電極２ａ、並びにはんだ部４Ａと第２の電極３ａとの接触面積が大きくなる。すなわち、はんだ粒子を用いることにより、外表面がニッケル、金又は銅等の金属である導電性粒子を用いた場合と比較して、はんだ部４Ａと第１の電極２ａ、並びにはんだ部４Ａと第２の電極３ａとの接触面積が大きくなる。このことによっても、接続構造体１における導通信頼性及び接続信頼性が高くなる。なお、上記フラックスは、一般に、加熱により次第に失活する。
　接続構造体１では、第１の電極２ａと接続部４と第２の電極３ａとの積層方向に第１の電極２ａと第２の電極３ａとの対向し合う部分をみたときに、第１の電極２ａと第２の電極３ａとの対向し合う部分の面積１００％中の５０％以上に、接続部４中のはんだ部４Ａが配置されていることが好ましい。接続部４中のはんだ部４Ａが、上記の好ましい態様を満足することで、導通信頼性をより一層高めることができる。
　上記第１の電極と上記接続部と上記第２の電極との積層方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分の面積１００％中の５０％以上に、上記接続部中のはんだ部が配置されていることが好ましい。上記第１の電極と上記接続部と上記第２の電極との積層方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分の面積１００％中の６０％以上に、上記接続部中のはんだ部が配置されていることがより好ましい。上記第１の電極と上記接続部と上記第２の電極との積層方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分の面積１００％中の７０％以上に、上記接続部中のはんだ部が配置されていることがさらに好ましい。上記第１の電極と上記接続部と上記第２の電極との積層方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分の面積１００％中の８０％以上に、上記接続部中のはんだ部が配置されていることが特に好ましい。上記第１の電極と上記接続部と上記第２の電極との積層方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分の面積１００％中の９０％以上に、上記接続部中のはんだ部が配置されていることが最も好ましい。上記接続部中のはんだ部が、上記の好ましい態様を満足することで、導通信頼性をより一層高めることができる。
　上記第１の電極と上記接続部と上記第２の電極との積層方向と直交する方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分に、上記接続部中のはんだ部の６０％以上が配置されていることが好ましい。上記第１の電極と上記接続部と上記第２の電極との積層方向と直交する方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分に、上記接続部中のはんだ部の７０％以上が配置されていることがより好ましい。上記第１の電極と上記接続部と上記第２の電極との積層方向と直交する方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分に、上記接続部中のはんだ部の９０％以上が配置されていることがさらに好ましい。上記第１の電極と上記接続部と上記第２の電極との積層方向と直交する方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分に、上記接続部中のはんだ部の９５％以上が配置されていることが特に好ましい。上記第１の電極と上記接続部と上記第２の電極との積層方向と直交する方向に上記第１の電極と上記第２の電極との対向し合う部分をみたときに、上記第１の電極と上記第２の電極との対向し合う部分に、上記接続部中のはんだ部の９９％以上が配置されていることが最も好ましい。上記接続部中のはんだ部が、上記の好ましい態様を満足することで、導通信頼性をより一層高めることができる。
　上記第１，第２の接続対象部材は、特に限定されない。上記第１，第２の接続対象部材としては、具体的には、半導体チップ、半導体パッケージ、ＬＥＤチップ、ＬＥＤパッケージ、コンデンサ及びダイオード等の電子部品、並びに樹脂フィルム、プリント基板、フレキシブルプリント基板、フレキシブルフラットケーブル、リジッドフレキシブル基板、ガラスエポキシ基板及びガラス基板等の回路基板等の電子部品等が挙げられる。上記第１，第２の接続対象部材は、電子部品であることが好ましい。
　上記第１の接続対象部材及び上記第２の接続対象部材の内の少なくとも一方が、樹脂フィルム、フレキシブルプリント基板、フレキシブルフラットケーブル又はリジッドフレキシブル基板であることが好ましい。上記第２の接続対象部材が、樹脂フィルム、フレキシブルプリント基板、フレキシブルフラットケーブル又はリジッドフレキシブル基板であることが好ましい。樹脂フィルム、フレキシブルプリント基板、フレキシブルフラットケーブル及びリジッドフレキシブル基板は、柔軟性が高く、比較的軽量であるという性質を有する。このような接続対象部材の接続に導電フィルムを用いた場合には、はんだ粒子が電極上に集まりにくい傾向がある。これに対して、導電ペーストを用いることで、樹脂フィルム、フレキシブルプリント基板、フレキシブルフラットケーブル又はリジッドフレキシブル基板を用いたとしても、はんだ粒子を電極上に効率的に集めることで、電極間の導通信頼性を十分に高めることができる。樹脂フィルム、フレキシブルプリント基板、フレキシブルフラットケーブル又はリジッドフレキシブル基板を用いる場合に、半導体チップ等の他の接続対象部材を用いた場合と比べて、加圧を行わないことによる電極間の導通信頼性の向上効果がより一層効果的に得られる。
　上記接続対象部材に設けられている電極としては、金電極、ニッケル電極、錫電極、アルミニウム電極、銅電極、モリブデン電極、銀電極、ＳＵＳ電極、及びタングステン電極等の金属電極が挙げられる。上記接続対象部材がフレキシブルプリント基板である場合には、上記電極は金電極、錫電極、銀電極又は銅電極であることが好ましい。上記接続対象部材がガラス基板である場合には、上記電極は銅電極、又は銀電極であることが好ましい。なお、上記電極がアルミニウム電極である場合には、アルミニウムのみで形成された電極であってもよく、金属酸化物層の表面にアルミニウム層が積層された電極であってもよい。上記金属酸化物層の材料としては、３価の金属元素がドープされた酸化インジウム及び３価の金属元素がドープされた酸化亜鉛等が挙げられる。上記３価の金属元素としては、Ｓｎ、Ａｌ及びＧａ等が挙げられる。
　本発明に係る接続構造体では、上記第１の電極及び上記第２の電極は、エリアアレイ又はペリフェラルにて配置されていることが好ましい。上記第１の電極及び上記第２の電極が、エリアアレイ又はペリフェラルにて配置されている場合において、本発明の効果がより一層効果的に発揮される。上記エリアアレイとは、接続対象部材の電極が配置されている面にて、格子状に電極が配置されている構造のことである。上記ペリフェラルとは、接続対象部材の外周部に電極が配置されている構造のことである。電極が櫛型に並んでいる構造の場合は、櫛に垂直な方向に沿ってはんだ粒子が凝集すればよいのに対して、上記エリアアレイ又はペリフェラル構造では電極が配置されている面において、全面にて均一にはんだ粒子が凝集する必要がある。そのため、従来の方法では、はんだ量が不均一になりやすいのに対して、本発明の方法では、全面にて均一にはんだ粒子を凝集させることができる。
　以下、実施例及び比較例を挙げて、本発明を具体的に説明する。本発明は、以下の実施例のみに限定されない。
　熱硬化性成分（熱硬化性化合物）：
　フェノールノボラック型エポキシ化合物（ＤＯＷ社製「ＤＥＮ４３１」）
　ビスフェノールＦ型エポキシ化合物（ＤＯＷ社製「ＤＥＲ３５４」）
　はんだ粒子：
　はんだ粒子１（ＳｎＡｇＣｕはんだ粒子、三井金属社製「Ｓｎ９６．５Ａｇ３．０Ｃｕ０．５　ＳＴ－３」、平均粒子径：３．０μｍ、融点：２１９℃、比重：７．４）
　はんだ粒子２（ＳｎＢｉはんだ粒子、三井金属社製「Ｓｎ４２Ｂｉ５８　ＳＴ－３」、平均粒子径：３．０μｍ、融点：１３８℃、比重：８．６）
　はんだ粒子３（ＳｎＡｇＣｕはんだ粒子、三井金属社製「Ｓｎ９６．５Ａｇ３．０Ｃｕ０．５　ＤＳ１０」、平均粒子径：１０．０μｍ、融点：２１９℃、比重：７．４）
　はんだ粒子４（ＳｎＡｇＣｕはんだ粒子、三井金属社製「Ｓｎ９６．５Ａｇ３．０Ｃｕ０．５　ＳＴ－７」、平均粒子径：７．０μｍ、融点：２１９℃、比重：７．４）
　フラックス：
　アジピン酸ベンジルアミン塩（昭和化学工業社製「アジピン酸ベンジルアミン塩」、２５℃で固体、平均粒子径：１０μｍ、融点：１８０℃）
　オレイン酸（富士フイルム和光純薬社製「オレイン酸」、２５℃で液体、沸点：２２３℃）
　チキソトロピック剤：
　グリセロール（ナカライテスク社製「グリセロール」、２５℃で液体、水酸基の数：３、沸点：２９０℃）
　Ｎ－オレオイルサルコシン（ＴＣＩ社製「Ｎ－オレオイルサルコシン」、２５℃で液体、水酸基の数：１、沸点：１９７℃）
　三フッ化ホウ素－モノエチルアミン錯体（ＴＣＩ社製「三フッ化ホウ素－モノエチルアミン錯体」、２５℃で固体、２５℃及び５０％ＲＨで吸湿性を有する、融点：８５℃）
　Ｎ，Ｎ’－エチレンビス（ステアロアミド）（三菱ケミカル社製「スリパックスＥ」、２５℃で固体、２５℃及び５０％ＲＨで吸湿性を有しない（重量増加率０重量％））
　（重量増加率の測定）
　ＴＣＩ社製「三フッ化ホウ素－モノエチルアミン錯体」について、２５℃及び５０％ＲＨで２４時間放置したときに、放置後の三フッ化ホウ素－モノエチルアミン錯体の重量の、放置前の三フッ化ホウ素－モノエチルアミン錯体の重量に対する重量増加率を、上述した方法で測定した。三フッ化ホウ素－モノエチルアミン錯体の重量増加率は、１．０重量％～２．０重量％であった。
　（実施例１～６及び比較例１～４）
　（１）導電ペースト（異方性導電ペースト）の作製
　下記の表１～３に示す成分を下記の表１～３に示す配合量で配合して、導電ペースト（異方性導電ペースト）を得た。
　（２）接続構造体の作製
　第１の接続対象部材として、Ｌ／Ｓ＝５０μｍ／５０μｍの銅電極（電極長さ：３ｍｍ、電極厚み：１２μｍ）を表面に有するガラスエポキシ基板（材質：ＦＲ－４、厚み：０．６ｍｍ）を用意した。
　第２の接続対象部材として、Ｌ／Ｓ＝５０μｍ／５０μｍの銅電極（電極長さ：３ｍｍ、電極厚み：１２μｍ）を表面に有するフレキシブルプリント基板（材質：ポリイミド、厚み：０．１ｍｍ）を用意した。
　上記ガラスエポキシ基板の上面に、作製直後の導電ペースト（異方性導電ペースト）を厚み１００μｍとなるように塗工し、導電ペースト（異方性導電ペースト）層を形成した。次に、導電ペースト（異方性導電ペースト）層の上面にフレキシブルプリント基板を電極同士が対向するように積層した。導電ペースト（異方性導電ペースト）層には、上記フレキシブルプリント基板の重量が加わる。その状態から、導電ペースト（異方性導電ペースト）層の温度が、昇温開始から１０秒後にはんだ粒子の融点となるように加熱した。さらに、昇温開始から１５秒後に、導電ペースト（異方性導電ペースト）層の温度が２５０℃となるように加熱し、導電ペースト（異方性導電ペースト）層を硬化させ、接続構造体を得た。加熱時には、加圧を行わなかった。
　（評価）
　（１）スクリーン印刷性
　得られた導電ペースト（異方性導電ペースト）について、開口部１箇所当たりの寸法が８０μｍ×８０μｍ、厚みが３０μｍのメタルマスクを用いて、スライドガラス上にスクリーン印刷を行った。印刷されたパターン５０箇所について、印刷直後の印刷面をレーザー顕微鏡で観察し、スライドガラスに塗布された導電ペーストの体積を計算し、スライドガラスに塗布された導電ペーストの体積の、メタルマスクの開口部１箇所当たりの容積に対する割合Ｘ（％）を計算した。スクリーン印刷性を、以下の基準で判定した。
　［スクリーン印刷性の判定基準］
　○○：割合Ｘが、５０％以上
　○：割合Ｘが、３０％以上５０％未満
　×：割合Ｘが、３０％未満
　（２）タック性
　上記スライドガラスの上面に、作製直後の導電ペースト（異方性導電ペースト）を厚み２５０μｍとなるように塗工し、導電ペースト（異方性導電ペースト）層を形成した。形成直後及び形成から２４時間後の導電ペースト層の表面に、直径５ｍｍの円柱状のプローブを１Ｎ／５ｍｍφの圧力で１秒間押し付けた後、１２５ｍｍ／分の速度でプローブを上記導電ペースト層から引き剥がした。この引き剥がし時の剥離力の値をタック力とした。なお、測定装置として、ＲＨＥＳＣＡ社製「タッキング試験機　ＴＡＣ－ＩＩ」を用い、２５℃の条件で測定した。タック性を、以下の基準で判定した。
　［タック性の判定基準］
　○○：形成直後及び２４時間後のタック力が１Ｎ以上である
　○：形成直後のタック力が１Ｎ以上であり、かつ、２４時間後のタック力が１Ｎ未満である
　×：形成直後及び２４時間後のタック力が１Ｎ未満である
　（３）はんだ粒子の配置精度
　得られた接続構造体において、第１の電極と接続部と第２の電極との積層方向に第１の電極と第２の電極との対向し合う部分をみたときに、第１の電極と第２の電極との対向し合う部分の面積１００％中の、接続部中のはんだ部が配置されている面積の割合Ｙを評価した。はんだ粒子の配置精度を以下の基準で判定した。
　［はんだ粒子の配置精度の判定基準］
　○○：割合Ｙが７０％以上
　○：割合Ｙが５０％以上７０％未満
　×：割合Ｙが５０％未満
　結果を下記の表１～３に示す。
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
Figure JPOXMLDOC01-appb-T000003
　１…接続構造体
　２…第１の接続対象部材
　２ａ…第１の電極
　３…第２の接続対象部材
　３ａ…第２の電極
　４…接続部
　４Ａ…はんだ部
　４Ｂ…硬化物部

Claims (7)

  1. 　熱硬化性成分と、複数のはんだ粒子と、フラックスと、チキソトロピック剤とを含み、
    　前記はんだ粒子の平均粒子径が、５．０μｍ以下であり、
    　前記フラックスが、２５℃で固体であり、
    　前記チキソトロピック剤が、２５℃で液体であり、かつ水酸基を有するチキソトロピック剤であるか、又は、２５℃で固体であり、かつ前記チキソトロピック剤を２５℃及び５０％ＲＨで２４時間放置したときの、下記の重量増加率が０．２重量％以上であるチキソトロピック剤である、導電ペースト。
    　重量増加率（重量％）＝（Ｗ２－Ｗ１）×１００／Ｗ１
    　Ｗ１：放置前の前記チキソトロピック剤の重量
    　Ｗ２：放置後の前記チキソトロピック剤の重量
  2. 　前記導電ペースト１００重量％中、前記チキソトロピック剤の含有量が、０．００５重量％以上２重量％以下である、請求項１に記載の導電ペースト。
  3. 　前記はんだ粒子１００重量部に対して、前記チキソトロピック剤の含有量が、０．００３重量部以上２重量部以下である、請求項１又は２に記載の導電ペースト。
  4. 　前記チキソトロピック剤が、２５℃で液体であり、かつ水酸基を有するチキソトロピック剤である、請求項１～３のいずれか１項に記載の導電ペースト。
  5. 　前記チキソトロピック剤が、２５℃で液体であり、水酸基を有し、かつ沸点が８０℃以上であるチキソトロピック剤である、請求項４に記載の導電ペースト。
  6. 　前記チキソトロピック剤が、２５℃で固体であり、かつ前記重量増加率が１重量％以上であるチキソトロピック剤である、請求項１～３のいずれか１項に記載の導電ペースト。
  7. 　第１の電極を表面に有する第１の接続対象部材と、
    　第２の電極を表面に有する第２の接続対象部材と、
    　前記第１の接続対象部材と、前記第２の接続対象部材とを接続している接続部とを備え、
    　前記接続部の材料が、請求項１～６のいずれか１項に記載の導電ペーストであり、
    　前記第１の電極と前記第２の電極とが、前記接続部中のはんだ部により電気的に接続されている、接続構造体。
PCT/JP2023/028427 2022-08-08 2023-08-03 導電ペースト及び接続構造体 WO2024034516A1 (ja)