WO2023133534A1 - Techniques de génération de structures composites qui combinent des compositions de métal et de polymère - Google Patents

Techniques de génération de structures composites qui combinent des compositions de métal et de polymère Download PDF

Info

Publication number
WO2023133534A1
WO2023133534A1 PCT/US2023/060268 US2023060268W WO2023133534A1 WO 2023133534 A1 WO2023133534 A1 WO 2023133534A1 US 2023060268 W US2023060268 W US 2023060268W WO 2023133534 A1 WO2023133534 A1 WO 2023133534A1
Authority
WO
WIPO (PCT)
Prior art keywords
polymeric skin
polymeric
skin
depositing
nurbs
Prior art date
Application number
PCT/US2023/060268
Other languages
English (en)
Inventor
Francesco Iorio
Massimiliano Moruzzi
Original Assignee
Augmenta Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US18/150,765 external-priority patent/US20230211545A1/en
Application filed by Augmenta Inc. filed Critical Augmenta Inc.
Publication of WO2023133534A1 publication Critical patent/WO2023133534A1/fr

Abstract

Procédé de fabrication d'une structure multi-matériau comprenant : la formation d'un élément structural (120) avec au moins un vide à cellules ouvertes (123) qui est formé sur une surface de l'élément structural (120); le dépôt d'une première partie d'une peau polymère (130) sur la surface; et le dépôt d'une seconde partie de la peau polymère (130) à l'intérieur du ou des vides à cellules ouvertes (123).
PCT/US2023/060268 2022-01-06 2023-01-06 Techniques de génération de structures composites qui combinent des compositions de métal et de polymère WO2023133534A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US202263297022P 2022-01-06 2022-01-06
US63/297,022 2022-01-06
US18/150,765 US20230211545A1 (en) 2022-01-06 2023-01-05 Techniques for generating composite structures that combine metal and polymer compositions
US18/150,765 2023-01-05

Publications (1)

Publication Number Publication Date
WO2023133534A1 true WO2023133534A1 (fr) 2023-07-13

Family

ID=85172865

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2023/060268 WO2023133534A1 (fr) 2022-01-06 2023-01-06 Techniques de génération de structures composites qui combinent des compositions de métal et de polymère

Country Status (1)

Country Link
WO (1) WO2023133534A1 (fr)

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050173045A1 (en) * 2002-05-13 2005-08-11 Jonathan Hayes Method of registering and bonding coatings to form a part, apparatus for manufacturing a part
US20160075089A1 (en) * 2014-09-15 2016-03-17 Massachusetts Institute Of Technology Methods and apparatus for additive manufacturing along user-specified toolpaths
CN105500712B (zh) * 2016-01-08 2018-01-30 浙江理工大学 一种三自由度三维打印机的控制方法
WO2018045120A1 (fr) * 2016-09-01 2018-03-08 3D Systems, Inc. Fabrication additive améliorée d'un objet tridimensionnel
US20180104917A1 (en) * 2016-10-19 2018-04-19 GM Global Technology Operations LLC Method of manufacturing a composite article
US20180243981A1 (en) * 2017-02-24 2018-08-30 Additive Orthotics and Prosthetics LLC Printed hollow channels formed within an object during formation for injection of a bonding material
US20180321659A1 (en) * 2015-11-06 2018-11-08 Sabic Global Technologies B.V. Systems and methods for optimization of 3-d printed objects
US20200130256A1 (en) * 2016-10-21 2020-04-30 Mosaic Manufacturing Ltd. Joiners, Methods of Joining, and Related Systems for Additive Manufacturing
US20200290271A1 (en) * 2019-03-15 2020-09-17 GM Global Technology Operations LLC Filament deposition head and method of depositing filament material for joining workpieces
EP3046749B1 (fr) * 2013-09-19 2021-02-17 Markforged, Inc. Procédés de fabrication additive renforcée par fibres

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20050173045A1 (en) * 2002-05-13 2005-08-11 Jonathan Hayes Method of registering and bonding coatings to form a part, apparatus for manufacturing a part
EP3046749B1 (fr) * 2013-09-19 2021-02-17 Markforged, Inc. Procédés de fabrication additive renforcée par fibres
US20160075089A1 (en) * 2014-09-15 2016-03-17 Massachusetts Institute Of Technology Methods and apparatus for additive manufacturing along user-specified toolpaths
US20180321659A1 (en) * 2015-11-06 2018-11-08 Sabic Global Technologies B.V. Systems and methods for optimization of 3-d printed objects
CN105500712B (zh) * 2016-01-08 2018-01-30 浙江理工大学 一种三自由度三维打印机的控制方法
WO2018045120A1 (fr) * 2016-09-01 2018-03-08 3D Systems, Inc. Fabrication additive améliorée d'un objet tridimensionnel
US20180104917A1 (en) * 2016-10-19 2018-04-19 GM Global Technology Operations LLC Method of manufacturing a composite article
US20200130256A1 (en) * 2016-10-21 2020-04-30 Mosaic Manufacturing Ltd. Joiners, Methods of Joining, and Related Systems for Additive Manufacturing
US20180243981A1 (en) * 2017-02-24 2018-08-30 Additive Orthotics and Prosthetics LLC Printed hollow channels formed within an object during formation for injection of a bonding material
US20200290271A1 (en) * 2019-03-15 2020-09-17 GM Global Technology Operations LLC Filament deposition head and method of depositing filament material for joining workpieces

Similar Documents

Publication Publication Date Title
Dezaki et al. An overview of fused deposition modelling (FDM): Research, development and process optimisation
Wulle et al. Workpiece and machine design in additive manufacturing for multi-axis fused deposition modeling
Friel Power ultrasonics for additive manufacturing and consolidating of materials
Llewellyn-Jones et al. Curved layer fused filament fabrication using automated toolpath generation
Alsharhan et al. Enhancing mechanical properties of thin-walled structures using non-planar extrusion based additive manufacturing
Shen et al. Fused deposition modeling five-axis additive manufacturing: machine design, fundamental printing methods and critical process characteristics
Steuben et al. Design for fused filament fabrication additive manufacturing
Kim et al. Cooperative tool path planning for wire embedding on additively manufactured curved surfaces using robot kinematics
Kumar et al. Experimental investigations on suitability of polypropylene (PP) and ethylene vinyl acetate (EVA) in additive manufacturing
CN1874863A (zh) 分层制造的具有小宽度流体引流口的制品及其制造方法
EP2998110B1 (fr) Fabrication de pièces par filament fusionné au moyen de stratification de renforcement multidirectionnelle
Lynn et al. Direct digital subtractive manufacturing of a functional assembly using voxel-based models
Gardner et al. Aligning material extrusion direction with mechanical stress via 5-axis tool paths
Novakova-Marcincinova et al. Applications of rapid prototyping fused deposition modeling materials
Vicente et al. Large-format additive manufacturing of polymer extrusion-based deposition systems: review and applications
Weflen et al. Hybrid additive and subtractive manufacturing of multi-material objects
Schuh et al. Feature-based print method for multi-axis material extrusion in additive manufacturing
US20230211545A1 (en) Techniques for generating composite structures that combine metal and polymer compositions
Lalegani Dezaki et al. Experimental study of drilling 3D printed polylactic acid (PLA) in FDM Process
WO2023133534A1 (fr) Techniques de génération de structures composites qui combinent des compositions de métal et de polymère
WO2023133532A1 (fr) Techniques de génération de structures composites qui combinent des compositions métalliques et polymères
Ishak et al. An algorithm for generating 3D lattice structures suitable for printing on a multi-plane FDM printing platform
Doherty et al. Selective directional reinforcement of structures for multi-axis additive manufacturing
Kulkarni et al. Deposition strategies and resulting part stiffnesses in layered manufacturing
Riddick et al. Effect of manufacturing parameters on failure in acrylonitrile-butadiane-styrene fabricated by fused deposition modeling

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 23703394

Country of ref document: EP

Kind code of ref document: A1