WO2023091880A1 - Panneau de placoplâtre à teneur élevée en sel contenant des absorbants de sel et procédés de fabrication de celle-ci - Google Patents

Panneau de placoplâtre à teneur élevée en sel contenant des absorbants de sel et procédés de fabrication de celle-ci Download PDF

Info

Publication number
WO2023091880A1
WO2023091880A1 PCT/US2022/079718 US2022079718W WO2023091880A1 WO 2023091880 A1 WO2023091880 A1 WO 2023091880A1 US 2022079718 W US2022079718 W US 2022079718W WO 2023091880 A1 WO2023091880 A1 WO 2023091880A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
parts
cover sheet
gypsum
typically
Prior art date
Application number
PCT/US2022/079718
Other languages
English (en)
Inventor
Qinghua Li
Mark Hemphill
Original Assignee
United States Gypsum Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US17/851,709 external-priority patent/US11999658B2/en
Application filed by United States Gypsum Company filed Critical United States Gypsum Company
Priority to CA3237378A priority Critical patent/CA3237378A1/fr
Publication of WO2023091880A1 publication Critical patent/WO2023091880A1/fr

Abstract

L'invention concerne un panneau de placoplâtre ayant un noyau ayant une couche de noyau centrale et une ou plusieurs couches densifiées. Au moins une couche densifiée contient des particules absorbantes de sel de zéolite et/ou d'hydrotalcite pour améliorer l'adhérence du noyau de gypse à une feuille de revêtement. L'invention concerne également des procédés de fabrication du panneau de placoplâtre et un système de paroi pour utiliser le panneau de placoplâtre.
PCT/US2022/079718 2021-11-16 2022-11-11 Panneau de placoplâtre à teneur élevée en sel contenant des absorbants de sel et procédés de fabrication de celle-ci WO2023091880A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CA3237378A CA3237378A1 (fr) 2021-11-16 2022-11-11 Panneau de placoplatre a teneur elevee en sel contenant des absorbants de sel et procedes de fabrication de celle-ci

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US202163279869P 2021-11-16 2021-11-16
US63/279,869 2021-11-16
US17/851,709 2022-06-28
US17/851,709 US11999658B2 (en) 2021-11-16 2022-06-28 High salt gypsum wallboard containing salt absorbents and methods of making same

Publications (1)

Publication Number Publication Date
WO2023091880A1 true WO2023091880A1 (fr) 2023-05-25

Family

ID=84982243

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2022/079718 WO2023091880A1 (fr) 2021-11-16 2022-11-11 Panneau de placoplâtre à teneur élevée en sel contenant des absorbants de sel et procédés de fabrication de celle-ci

Country Status (1)

Country Link
WO (1) WO2023091880A1 (fr)

Citations (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5643510A (en) 1994-09-23 1997-07-01 Usg Corporation Producing foamed gypsum board using a foaming agent blend
US5683635A (en) 1995-12-22 1997-11-04 United States Gypsum Company Method for preparing uniformly foamed gypsum product with less foam agitation
US6342284B1 (en) 1997-08-21 2002-01-29 United States Gysum Company Gypsum-containing product having increased resistance to permanent deformation and method and composition for producing it
US6494609B1 (en) 2001-07-16 2002-12-17 United States Gypsum Company Slurry mixer outlet
US6632550B1 (en) 1997-08-21 2003-10-14 United States Gypsum Company Gypsum-containing product having increased resistance to permanent deformation and method and composition for producing it
US6694695B2 (en) 2001-08-27 2004-02-24 Dietrich Industries, Inc. Wall stud spacer system with spacer retainers
US6815049B2 (en) 2001-12-11 2004-11-09 United States Gypsum Company Gypsum-containing composition having enhanced resistance to permanent deformation
US6822033B2 (en) 2001-11-19 2004-11-23 United States Gypsum Company Compositions and methods for treating set gypsum
US7364676B2 (en) 2005-09-01 2008-04-29 United States Gypsum Company Slurry spreader for cementitious board production
US20100247937A1 (en) 2009-03-31 2010-09-30 United States Gypsum Company Cementitious article and method for preparing the same
US20120168527A1 (en) 2010-12-30 2012-07-05 United States Gypsum Company Slurry distribution system and method
US20120170403A1 (en) 2010-12-30 2012-07-05 United States Gypsum Company Slurry distributor, system and method for using same
US8323785B2 (en) 2011-02-25 2012-12-04 United States Gypsum Company Lightweight, reduced density fire rated gypsum panels
US20190270675A1 (en) * 2018-03-05 2019-09-05 Georgia-Pacific Gypsum Llc Gypsum panels, methods, and systems
US20200055277A1 (en) 2018-08-14 2020-02-20 United States Gypsum Company Gypsum board from gypsum having high level of chloride salt and a perforated sheet and methods associated therewith
US20200055278A1 (en) 2018-08-14 2020-02-20 United States Gypsum Company Gypsum board from gypsum having high level of chloride salt and a starch layer and methods associated therewith
CN111606665A (zh) 2019-05-08 2020-09-01 北新集团建材股份有限公司 高钠脱硫石膏纸面石膏板及其制备方法
CN111606657A (zh) * 2019-05-08 2020-09-01 北新集团建材股份有限公司 一种高氯离子含量脱硫石膏纸面石膏板及其制备方法
WO2020224120A1 (fr) 2019-05-08 2020-11-12 北新集团建材股份有限公司 Plaque de plâtre revêtue de papier de gypse désulfuré à teneur élevée en impuretés ioniques et son procédé de fabrication
CN111943624A (zh) * 2020-08-19 2020-11-17 湖州五好建材有限公司 一种具有防火耐冲击性能的纸面石膏板

Patent Citations (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5643510A (en) 1994-09-23 1997-07-01 Usg Corporation Producing foamed gypsum board using a foaming agent blend
US5683635A (en) 1995-12-22 1997-11-04 United States Gypsum Company Method for preparing uniformly foamed gypsum product with less foam agitation
US6342284B1 (en) 1997-08-21 2002-01-29 United States Gysum Company Gypsum-containing product having increased resistance to permanent deformation and method and composition for producing it
US6632550B1 (en) 1997-08-21 2003-10-14 United States Gypsum Company Gypsum-containing product having increased resistance to permanent deformation and method and composition for producing it
US6494609B1 (en) 2001-07-16 2002-12-17 United States Gypsum Company Slurry mixer outlet
US6874930B2 (en) 2001-07-16 2005-04-05 United States Gypsum Company Slurry mixer outlet
US6694695B2 (en) 2001-08-27 2004-02-24 Dietrich Industries, Inc. Wall stud spacer system with spacer retainers
US6822033B2 (en) 2001-11-19 2004-11-23 United States Gypsum Company Compositions and methods for treating set gypsum
US6815049B2 (en) 2001-12-11 2004-11-09 United States Gypsum Company Gypsum-containing composition having enhanced resistance to permanent deformation
US7364676B2 (en) 2005-09-01 2008-04-29 United States Gypsum Company Slurry spreader for cementitious board production
US20100247937A1 (en) 2009-03-31 2010-09-30 United States Gypsum Company Cementitious article and method for preparing the same
US20120168527A1 (en) 2010-12-30 2012-07-05 United States Gypsum Company Slurry distribution system and method
US20120170403A1 (en) 2010-12-30 2012-07-05 United States Gypsum Company Slurry distributor, system and method for using same
US8323785B2 (en) 2011-02-25 2012-12-04 United States Gypsum Company Lightweight, reduced density fire rated gypsum panels
US20190270675A1 (en) * 2018-03-05 2019-09-05 Georgia-Pacific Gypsum Llc Gypsum panels, methods, and systems
US20200055277A1 (en) 2018-08-14 2020-02-20 United States Gypsum Company Gypsum board from gypsum having high level of chloride salt and a perforated sheet and methods associated therewith
US20200055278A1 (en) 2018-08-14 2020-02-20 United States Gypsum Company Gypsum board from gypsum having high level of chloride salt and a starch layer and methods associated therewith
CN111606665A (zh) 2019-05-08 2020-09-01 北新集团建材股份有限公司 高钠脱硫石膏纸面石膏板及其制备方法
CN111606657A (zh) * 2019-05-08 2020-09-01 北新集团建材股份有限公司 一种高氯离子含量脱硫石膏纸面石膏板及其制备方法
WO2020224120A1 (fr) 2019-05-08 2020-11-12 北新集团建材股份有限公司 Plaque de plâtre revêtue de papier de gypse désulfuré à teneur élevée en impuretés ioniques et son procédé de fabrication
CN111943624A (zh) * 2020-08-19 2020-11-17 湖州五好建材有限公司 一种具有防火耐冲击性能的纸面石膏板

Similar Documents

Publication Publication Date Title
US11186066B2 (en) Gypsum board from gypsum having high level of chloride salt and a perforated sheet and methods associated therewith
CN101272993B (zh) 墙板中的硅氧烷聚合
US11186067B2 (en) Gypsum board from gypsum having high level of chloride salt and a starch layer and methods associated therewith
AU2013221770B2 (en) Gypsum products with high efficiency heat sink additives
CA2670942A1 (fr) Compositions de gypse a sulfonate de naphtalene et modificateurs
US20210198148A1 (en) Composite gypsum board formed from high-salt stucco and related methods
US11999658B2 (en) High salt gypsum wallboard containing salt absorbents and methods of making same
WO2023091880A1 (fr) Panneau de placoplâtre à teneur élevée en sel contenant des absorbants de sel et procédés de fabrication de celle-ci
CA3217242A1 (fr) Panneau de gypse leger resistant a l'affaissement a haute temperature
US11891336B2 (en) Gypsum board containing high absorption paper and related methods
CA3076828A1 (fr) Migration d'amidon dote d'une solubilite elevee dans l'eau froide pour une utilisation dans la preparation de plaque de platre
US11993054B2 (en) Method of preparing gypsum wallboard from high salt gypsum, and related product
RU2797758C2 (ru) Гипсокартон из гипса, содержащий высокий уровень хлоридной соли и перфорированный лист, а также связанный с ним способ
US20230357085A1 (en) Gypsum board from gypsum having high level of chloride salt and a polymer layer and methods associated therewith
US20220356114A1 (en) High temperature sag resistant lightweight gypsum board
RU2789870C2 (ru) Гипсокартон из гипса, содержащий высокий уровень хлоридной соли и слой крахмала, а также связанный с ним способ
US20230250019A1 (en) Gypsum panel containing ammonium-exchanged vermiculite and methods
WO2023154662A1 (fr) Panneau de gypse contenant de la vermiculite à échange d'ammonium et procédés associés
EP4061784A1 (fr) Plaque de plâtre contenant du papier à haute absorption, et procédés associés
EP4081394A1 (fr) Plaque de plâtre composite formée à partir de stuc à haute teneur en sel et procédés associés

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22844702

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 3237378

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 2022844702

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2022844702

Country of ref document: EP

Effective date: 20240617