WO2023055347A1 - Gypsum cement with reduced permeability - Google Patents
Gypsum cement with reduced permeability Download PDFInfo
- Publication number
- WO2023055347A1 WO2023055347A1 PCT/US2021/052500 US2021052500W WO2023055347A1 WO 2023055347 A1 WO2023055347 A1 WO 2023055347A1 US 2021052500 W US2021052500 W US 2021052500W WO 2023055347 A1 WO2023055347 A1 WO 2023055347A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- gypsum cement
- cellular glass
- glass insulation
- cement
- waterproofing element
- Prior art date
Abstract
Description
Claims