WO2023047018A1 - A process for preparing an alkaline cellulose dope - Google Patents
A process for preparing an alkaline cellulose dope Download PDFInfo
- Publication number
- WO2023047018A1 WO2023047018A1 PCT/FI2022/050627 FI2022050627W WO2023047018A1 WO 2023047018 A1 WO2023047018 A1 WO 2023047018A1 FI 2022050627 W FI2022050627 W FI 2022050627W WO 2023047018 A1 WO2023047018 A1 WO 2023047018A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cellulose
- alkaline
- dope
- cellulose dope
- cold
- Prior art date
Abstract
Description
Claims