WO2023032820A1 - Composition de résine, produit durci, stratifié, procédé de production de produit durci, procédé de production de stratifié, procédé de production de dispositif à semi-conducteur, dispositif à semi-conducteur et composé - Google Patents

Composition de résine, produit durci, stratifié, procédé de production de produit durci, procédé de production de stratifié, procédé de production de dispositif à semi-conducteur, dispositif à semi-conducteur et composé Download PDF

Info

Publication number
WO2023032820A1
WO2023032820A1 PCT/JP2022/032119 JP2022032119W WO2023032820A1 WO 2023032820 A1 WO2023032820 A1 WO 2023032820A1 JP 2022032119 W JP2022032119 W JP 2022032119W WO 2023032820 A1 WO2023032820 A1 WO 2023032820A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
compound
formula
acid
resin composition
Prior art date
Application number
PCT/JP2022/032119
Other languages
English (en)
Japanese (ja)
Inventor
敦靖 野崎
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to JP2023545514A priority Critical patent/JPWO2023032820A1/ja
Priority to CN202280058926.9A priority patent/CN117881745A/zh
Publication of WO2023032820A1 publication Critical patent/WO2023032820A1/fr

Abstract

L'invention concerne : une composition de résine comprenant au moins une résine choisie dans le groupe constitué par des résines cyclisées et des précurseurs de celles-ci, et un composé B, qui comporte un groupe polymérisable par ouverture de cycle, qui possède également au moins une structure choisie dans le groupe constitué par des liaisons urée, des liaisons uréthane et des liaisons amide non incluses dans des structures cycliques, et qui comprend en outre un groupe polymérisable par voie radicalaire ; un produit durci obtenu par durcissement de la composition de résine ; un stratifié comprenant le produit durci ; un procédé de production du produit durci ; un procédé de production du stratifié ; un procédé de production d'un dispositif à semi-conducteur qui comprend le procédé de production du stratifié ; un dispositif à semi-conducteur comprenant le produit durci ou le stratifié ; et un nouveau composé.
PCT/JP2022/032119 2021-08-31 2022-08-25 Composition de résine, produit durci, stratifié, procédé de production de produit durci, procédé de production de stratifié, procédé de production de dispositif à semi-conducteur, dispositif à semi-conducteur et composé WO2023032820A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2023545514A JPWO2023032820A1 (fr) 2021-08-31 2022-08-25
CN202280058926.9A CN117881745A (zh) 2021-08-31 2022-08-25 树脂组合物、固化物、层叠体、固化物的制造方法、层叠体的制造方法、半导体器件的制造方法及半导体器件、以及化合物

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021-141454 2021-08-31
JP2021141454 2021-08-31

Publications (1)

Publication Number Publication Date
WO2023032820A1 true WO2023032820A1 (fr) 2023-03-09

Family

ID=85412610

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/032119 WO2023032820A1 (fr) 2021-08-31 2022-08-25 Composition de résine, produit durci, stratifié, procédé de production de produit durci, procédé de production de stratifié, procédé de production de dispositif à semi-conducteur, dispositif à semi-conducteur et composé

Country Status (4)

Country Link
JP (1) JPWO2023032820A1 (fr)
CN (1) CN117881745A (fr)
TW (1) TW202319451A (fr)
WO (1) WO2023032820A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2024101266A1 (fr) * 2022-11-07 2024-05-16 富士フイルム株式会社 Composition de résine, produit durci, stratifié, procédé de production de produit durci, procédé de production de stratifié, procédé de production de dispositif à semi-conducteur et dispositif à semi-conducteur

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005103793A (ja) * 2003-09-29 2005-04-21 Fuji Photo Film Co Ltd 重合性樹脂組成物、インクジェット記録ヘッド及びその製造方法
JP2006193745A (ja) * 2005-01-14 2006-07-27 Xerox Corp 硬化性ゲル化剤添加剤を含む放射線硬化性インク
WO2019117082A1 (fr) * 2017-12-15 2019-06-20 富士フイルム株式会社 Copolymère à photo-alignement, film photo-aligné et produit stratifié optique
JP2020152857A (ja) * 2019-03-22 2020-09-24 富士フイルム株式会社 硬化性樹脂組成物、硬化膜、積層体、硬化膜の製造方法、及び、半導体デバイス
WO2020196363A1 (fr) * 2019-03-27 2020-10-01 富士フイルム株式会社 Composition de résine durcissable, film durci, produit stratifié, procédé de production de film durci, et dispositif à semi-conducteurs
CN113185544A (zh) * 2021-05-25 2021-07-30 吉林奥来德光电材料股份有限公司 一种用于封装薄膜的化合物、包含其的油墨组合物及封装结构

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2005103793A (ja) * 2003-09-29 2005-04-21 Fuji Photo Film Co Ltd 重合性樹脂組成物、インクジェット記録ヘッド及びその製造方法
JP2006193745A (ja) * 2005-01-14 2006-07-27 Xerox Corp 硬化性ゲル化剤添加剤を含む放射線硬化性インク
WO2019117082A1 (fr) * 2017-12-15 2019-06-20 富士フイルム株式会社 Copolymère à photo-alignement, film photo-aligné et produit stratifié optique
JP2020152857A (ja) * 2019-03-22 2020-09-24 富士フイルム株式会社 硬化性樹脂組成物、硬化膜、積層体、硬化膜の製造方法、及び、半導体デバイス
WO2020196363A1 (fr) * 2019-03-27 2020-10-01 富士フイルム株式会社 Composition de résine durcissable, film durci, produit stratifié, procédé de production de film durci, et dispositif à semi-conducteurs
CN113185544A (zh) * 2021-05-25 2021-07-30 吉林奥来德光电材料股份有限公司 一种用于封装薄膜的化合物、包含其的油墨组合物及封装结构

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2024101266A1 (fr) * 2022-11-07 2024-05-16 富士フイルム株式会社 Composition de résine, produit durci, stratifié, procédé de production de produit durci, procédé de production de stratifié, procédé de production de dispositif à semi-conducteur et dispositif à semi-conducteur

Also Published As

Publication number Publication date
JPWO2023032820A1 (fr) 2023-03-09
CN117881745A (zh) 2024-04-12
TW202319451A (zh) 2023-05-16

Similar Documents

Publication Publication Date Title
JP7259141B1 (ja) 硬化物の製造方法、積層体の製造方法、及び、半導体デバイスの製造方法、並びに、処理液
KR20230110590A (ko) 수지 조성물, 경화물, 적층체, 경화물의 제조 방법, 및, 반도체 디바이스
JP2023153860A (ja) 硬化性樹脂組成物、硬化膜、積層体、硬化膜の製造方法、半導体デバイス、及び、樹脂
WO2023032820A1 (fr) Composition de résine, produit durci, stratifié, procédé de production de produit durci, procédé de production de stratifié, procédé de production de dispositif à semi-conducteur, dispositif à semi-conducteur et composé
WO2022224838A1 (fr) Composition de résine, produit durci, stratifié, procédé de production de produit durci, dispositif à semi-conducteur et résine
WO2022210225A1 (fr) Composition de résine, article durci, stratifié, procédé de production d'un article durci, et dispositif semi-conducteur
WO2022210226A1 (fr) Composition de résine, objet durci ainsi que procédé de fabrication de celui-ci, stratifié, dispositif à semi-conducteurs, et composé
WO2022210532A1 (fr) Composition de résine, produit durci, stratifié, procédé de production de produit durci, dispositif semi-conducteur et précurseur de polyimide et son procédé de production
WO2022172996A1 (fr) Composition de résine, produit durci, corps stratifié, procédé de production d'un produit durci, dispositif à semi-conducteur et générateur de base
WO2022145355A1 (fr) Composition de résine, objet durci, objet stratifié, procédé de production d'un objet durci et dispositif à semi-conducteur
WO2022145136A1 (fr) Composition de résine, produit durci, stratifié, procédé de production de produit durci, dispositif semi-conducteur, et composé
WO2022050041A1 (fr) Procédé de fabrication d'objet durci, procédé de fabrication de stratifié, et procédé de fabrication de dispositif électronique
JP7528260B2 (ja) 硬化物の製造方法、積層体の製造方法、半導体デバイスの製造方法、樹脂組成物、硬化物、積層体、及び、半導体デバイス
WO2023032475A1 (fr) Procédé de production de produit durci, procédé de production de corps multicouche, procédé de production de dispositif à semi-conducteur, et solution de traitement et composition de résine
JP7500740B2 (ja) 硬化性樹脂組成物、硬化物、積層体、硬化物の製造方法、及び、半導体デバイス、並びに、化合物
WO2022176869A1 (fr) Procédé de production de film permanent, procédé de production de corps multicouche, et procédé de production de dispositif à semi-conducteur
WO2023032821A1 (fr) Composition de résine, produit durci, corps multicouche, procédé de production de produit durci, procédé de production de corps multicouche, procédé de production de dispositif à semi-conducteur et dispositif à semi-conducteur
WO2023026892A1 (fr) Composition de résine, article durci, corps stratifié, procédé de production d'article durci, procédé de production de corps stratifié, procédé de production de dispositif semi-conducteur, dispositif semi-conducteur et agent générateur de base
WO2023008001A1 (fr) Composition de résine, objet durci ainsi que procédé de fabrication de celui-ci, stratifié ainsi que procédé de fabrication de celui-ci, et dispositif à semi-conducteurs ainsi que procédé de fabrication de celui-ci
WO2023286571A1 (fr) Composition de résine, objet durci ainsi que procédé de fabrication de celui-ci, stratifié ainsi que procédé de fabrication de celui-ci, et dispositif à semi-conducteurs ainsi que procédé de fabrication de celui-ci
WO2023008049A1 (fr) Objet durci ainsi que procédé de fabrication de celui-ci, stratifié ainsi que procédé de fabrication de celui-ci, dispositif à semi-conducteurs ainsi que procédé de fabrication de celui-ci, et composition de résine
WO2022210324A1 (fr) Composition de résine, objet durci ainsi que procédé de fabrication de celui-ci, stratifié, dispositif à semi-conducteurs, et générateur de base
WO2022172962A1 (fr) Composition de résine, produit durci, corps stratifié, procédé de fabrication d'un produit durci, dispositif à semi-conducteur et précurseur de résine de cyclisation
WO2022210466A1 (fr) Composition de résine, produit durci, corps stratifié, procédé de fabrication de produit durci, dispositif à semi-conducteur et précurseur de polyimide
JP2023034723A (ja) 樹脂組成物、硬化物、積層体、硬化物の製造方法、積層体の製造方法、半導体デバイスの製造方法、及び、半導体デバイス、並びに、化合物

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22864404

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2023545514

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 202280058926.9

Country of ref document: CN

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 22864404

Country of ref document: EP

Kind code of ref document: A1