WO2022204367A1 - Systèmes abradables pour turbomoteur - Google Patents

Systèmes abradables pour turbomoteur Download PDF

Info

Publication number
WO2022204367A1
WO2022204367A1 PCT/US2022/021678 US2022021678W WO2022204367A1 WO 2022204367 A1 WO2022204367 A1 WO 2022204367A1 US 2022021678 W US2022021678 W US 2022021678W WO 2022204367 A1 WO2022204367 A1 WO 2022204367A1
Authority
WO
WIPO (PCT)
Prior art keywords
ceramic
weight
abradable
coating
abrasive
Prior art date
Application number
PCT/US2022/021678
Other languages
English (en)
Inventor
Christopher W. Strock
Kevin C. SEYMOUR
Original Assignee
Raytheon Technologies Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Raytheon Technologies Corporation filed Critical Raytheon Technologies Corporation
Priority to EP22716659.2A priority Critical patent/EP4313909A1/fr
Priority to US18/283,882 priority patent/US20240158303A1/en
Publication of WO2022204367A1 publication Critical patent/WO2022204367A1/fr

Abstract

Selon un procédé de formation d'un matériau abradable (36), ledit matériau abradable présente au moins 20 % en volume de dioxyde de titane rutile (44) et de hBN (46). Le procédé comprend : le mélange d'une première poudre de dioxyde de titane ayant un débit d'oxygène d'au moins 5,0 % avec une seconde poudre de dioxyde de titane ayant un débit d'oxygène, le cas échéant, de moins de 1,0 %. Le mélange est pulvérisé thermiquement. Le mélange pulvérisé est ensuite oxydé.
PCT/US2022/021678 2019-09-20 2022-03-24 Systèmes abradables pour turbomoteur WO2022204367A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP22716659.2A EP4313909A1 (fr) 2021-03-24 2022-03-24 Systèmes abradables pour turbomoteur
US18/283,882 US20240158303A1 (en) 2019-09-20 2022-03-24 Turbine Engine Abradable Systems

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US202163165505P 2021-03-24 2021-03-24
US63/165,505 2021-03-24
US202263320938P 2022-03-17 2022-03-17
US63/320,938 2022-03-17

Publications (1)

Publication Number Publication Date
WO2022204367A1 true WO2022204367A1 (fr) 2022-09-29

Family

ID=81308074

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2022/021678 WO2022204367A1 (fr) 2019-09-20 2022-03-24 Systèmes abradables pour turbomoteur

Country Status (2)

Country Link
EP (1) EP4313909A1 (fr)
WO (1) WO2022204367A1 (fr)

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130071235A1 (en) * 2011-09-20 2013-03-21 Christopher W. Strock Light weight abradable air seal

Patent Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130071235A1 (en) * 2011-09-20 2013-03-21 Christopher W. Strock Light weight abradable air seal

Also Published As

Publication number Publication date
EP4313909A1 (fr) 2024-02-07

Similar Documents

Publication Publication Date Title
EP2521802B1 (fr) Systeme de revetement pour reduction des jeux dans des machines tournantes
US8187717B1 (en) High purity ceramic abradable coatings
EP1951824B1 (fr) Oxydes de titane et de strontium et revetements abradables faits a partir de ceux-ci
EP1484426B1 (fr) Revêtement formant une barrière thermique abradable et rèsistant à l'agglomération
EP3575559B1 (fr) Revêtements abradables coniques
EP3252277B1 (fr) Bande de frottement abradable de joint externe
US20110171488A1 (en) Thermal barrier coating systems
EP3604742B1 (fr) Bande de frottement abradable de joint externe
EP3276038B1 (fr) Matériau abradable
JP7086649B2 (ja) 高温用の物品
EP4031751B1 (fr) Système abradable d'un moteur à turbine
US20240158303A1 (en) Turbine Engine Abradable Systems
EP4313909A1 (fr) Systèmes abradables pour turbomoteur
CN116848285A (zh) 氧化物和非氧化物的复合热喷涂粉末
EP3613869B1 (fr) Revêtement abradable pour composants dans des systèmes mécaniques à haute température

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22716659

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 18283882

Country of ref document: US

WWE Wipo information: entry into national phase

Ref document number: 2022716659

Country of ref document: EP

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2022716659

Country of ref document: EP

Effective date: 20231024