WO2022144458A1 - Matériau thermodurcissable, procédés et utilisations de celui-ci - Google Patents
Matériau thermodurcissable, procédés et utilisations de celui-ci Download PDFInfo
- Publication number
- WO2022144458A1 WO2022144458A1 PCT/EP2022/050038 EP2022050038W WO2022144458A1 WO 2022144458 A1 WO2022144458 A1 WO 2022144458A1 EP 2022050038 W EP2022050038 W EP 2022050038W WO 2022144458 A1 WO2022144458 A1 WO 2022144458A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fibers
- piezoelectric
- piezoresistive
- yarns
- material according
- Prior art date
Abstract
La présente invention concerne un matériau composite thermodurcissable, son procédé d'obtention et son utilisation, comprenant une structure textile tissée et une résine thermodurcissable imprégnée dans la structure textile, la structure textile tissée comprenant des fibres de carbone tissées et des fibres piézoélectriques/piézorésistives, et les fibres piézoélectriques/piézorésistives étant aptes à former le matériau composite avec une auto-détection de volume.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP22700552.7A EP4271565A1 (fr) | 2020-12-30 | 2022-01-03 | Matériau thermodurcissable, procédés et utilisations de celui-ci |
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PT116982 | 2020-12-30 | ||
PT11698220 | 2020-12-30 | ||
EP20218008 | 2020-12-31 | ||
EP20218008.9 | 2020-12-31 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2022144458A1 true WO2022144458A1 (fr) | 2022-07-07 |
Family
ID=80001609
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2022/050038 WO2022144458A1 (fr) | 2020-12-30 | 2022-01-03 | Matériau thermodurcissable, procédés et utilisations de celui-ci |
Country Status (2)
Country | Link |
---|---|
EP (1) | EP4271565A1 (fr) |
WO (1) | WO2022144458A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN113831687A (zh) * | 2021-09-26 | 2021-12-24 | 西安工程大学 | 一种压电纱线增强树脂基复合材料的制备方法 |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4590122A (en) * | 1980-12-18 | 1986-05-20 | Fiberite Corporation | High conductivity graphite material with electrically conductive filaments wrapped around warp and fill elements |
WO1999042643A1 (fr) | 1998-02-18 | 1999-08-26 | Toray Industries Inc. | Matiere a base de fibres de carbone de renforcement, lamine et procede de detection |
US20050146076A1 (en) * | 2003-11-19 | 2005-07-07 | Bogdanovich Alexander | 3-D fabrics and fabric preforms for composites having integrated systems, devices, and/or networks |
WO2006072767A1 (fr) | 2005-01-07 | 2006-07-13 | The University Of Sheffield | Systeme de detection des dommages electriques pour composite autoregenerateur de polymeres |
US20130048841A1 (en) | 2011-08-23 | 2013-02-28 | The Boeing Company | Composite structure having an embedded sensing system |
WO2013034964A1 (fr) | 2011-09-07 | 2013-03-14 | Pielleitalia S.R.L. | Matériau composite comportant une couche de matériau polymère piézoélectrique apparié à un substrat textile et procédé pour la fabrication d'un tel matériau composite |
EP3447463A1 (fr) * | 2017-08-24 | 2019-02-27 | Sefar AG | Capteur de pression et son procédé de fabrication |
-
2022
- 2022-01-03 EP EP22700552.7A patent/EP4271565A1/fr active Pending
- 2022-01-03 WO PCT/EP2022/050038 patent/WO2022144458A1/fr unknown
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US4590122A (en) * | 1980-12-18 | 1986-05-20 | Fiberite Corporation | High conductivity graphite material with electrically conductive filaments wrapped around warp and fill elements |
WO1999042643A1 (fr) | 1998-02-18 | 1999-08-26 | Toray Industries Inc. | Matiere a base de fibres de carbone de renforcement, lamine et procede de detection |
US20050146076A1 (en) * | 2003-11-19 | 2005-07-07 | Bogdanovich Alexander | 3-D fabrics and fabric preforms for composites having integrated systems, devices, and/or networks |
WO2006072767A1 (fr) | 2005-01-07 | 2006-07-13 | The University Of Sheffield | Systeme de detection des dommages electriques pour composite autoregenerateur de polymeres |
US20130048841A1 (en) | 2011-08-23 | 2013-02-28 | The Boeing Company | Composite structure having an embedded sensing system |
WO2013034964A1 (fr) | 2011-09-07 | 2013-03-14 | Pielleitalia S.R.L. | Matériau composite comportant une couche de matériau polymère piézoélectrique apparié à un substrat textile et procédé pour la fabrication d'un tel matériau composite |
EP3447463A1 (fr) * | 2017-08-24 | 2019-02-27 | Sefar AG | Capteur de pression et son procédé de fabrication |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN113831687A (zh) * | 2021-09-26 | 2021-12-24 | 西安工程大学 | 一种压电纱线增强树脂基复合材料的制备方法 |
CN113831687B (zh) * | 2021-09-26 | 2023-07-21 | 西安工程大学 | 一种压电纱线增强树脂基复合材料的制备方法 |
Also Published As
Publication number | Publication date |
---|---|
EP4271565A1 (fr) | 2023-11-08 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US4614684A (en) | Reinforced composite comprising resin impregnated metallized polyaramide fabric and method of making same | |
US6265333B1 (en) | Delamination resistant composites prepared by small diameter fiber reinforcement at ply interfaces | |
US4234648A (en) | Electrically conductive prepreg materials | |
Lee | Handbook of composite reinforcements | |
AU2019204250B2 (en) | Conductive compositions of conductive polymer and metal coated fiber | |
EP0090151A1 (fr) | Compositions façonnables en composants renforcés et conducteurs ainsi que les articles renfermant ces compositions | |
CA2865704C (fr) | Materiau aux proprietes de conductivite ameliorees pour la realisation de pieces composites en association avec une resine | |
US20130106245A1 (en) | Fibre composite component acting as an actuator, a sensor and/or a generator and method for the production thereof | |
WO2022144458A1 (fr) | Matériau thermodurcissable, procédés et utilisations de celui-ci | |
KR20190095292A (ko) | 분말 형태의 열가소성 폴리머로 예비 함침된 섬유성 재료를 제조하기 위한 방법 | |
EP0216518A2 (fr) | Fibre ayant un revêtement de résine thermoplastique | |
US4486490A (en) | Electrically conductive prepreg materials | |
US20140097011A1 (en) | Composite component with electrical lines | |
KR20190095293A (ko) | 분무에 의해 열가소성 폴리머로 예비 함침된 섬유성 재료를 제조하기 위한 방법 | |
US20160236636A1 (en) | Airbag assembly and method of making and using the same | |
US20150233858A1 (en) | Composite with integral sensor and method | |
US8893535B2 (en) | Cylinder housing | |
US6127035A (en) | Low dielectric composite fiber and fabric | |
CA3158655A1 (fr) | Composition de revetement polymere conducteur et methode de fabrication | |
US10131112B2 (en) | Carbon composite component | |
Decker et al. | In-line integration of sensors in thermoplastic composite structures using novel continuous orbital winding technology | |
JP7210736B2 (ja) | 繊維複合材部品の製造方法、繊維複合材部品、繊維複合材部品の検査方法、コンピュータプログラム、機械可読記憶媒体及び装置 | |
Laroche et al. | Modeling of the thermo-elastic properties of woven fabric composites in complex shapes | |
US20230016136A1 (en) | Piezoresponsive Fibre Reinforced Polymer Composite | |
Nauman et al. | In situ strain sensing in three dimensional woven preform based composites using flexible textile based sensors |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 22700552 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
ENP | Entry into the national phase |
Ref document number: 2022700552 Country of ref document: EP Effective date: 20230731 |