WO2022129130A1

WO2022129130A1 - Hybrid pultrusion plates for a non-conductive wind turbine blade spar cap

Info

Publication number: WO2022129130A1
Application number: PCT/EP2021/085831
Authority: WO
Inventors: Jeppe JØRGENSEN
Original assignee: Lm Wind Power A/S
Priority date: 2020-12-17
Filing date: 2021-12-15
Publication date: 2022-06-23

Abstract

The present invention relates to a method of manufacturing a wind turbine blade shell component (38). The method comprises the steps of providing a plurality of pultrusion plates (64), arranging the pultrusion plates (64) on a blade shell material (89) in a mould (77) for the blade shell component, and bonding the pultrusion plates (64) with the blade shell material to form the blade shell component. Each pultrusion plate (64) is formed of a pultrusion fibre material comprising glass fibres and carbon fibres, wherein each pultrusion plate (64) comprises a top surface (81), an opposing bottom surface (82) and two lateral surfaces (83, 84), and wherein the top surface and the opposing bottom surface are free from carbon fibres.

Description

Title

Hybrid pultrusion plates for a non-conductive wind turbine blade spar cap

Field of the Invention

The present invention relates to a method of manufacturing a wind turbine blade shell component and to a reinforcing structure for a wind turbine blade, the reinforcing structure comprising a plurality of pultrusion plates.

Background of the Invention

Wind power provides a clean and environmentally friendly source of energy. Wind turbines usually comprise a tower, generator, gearbox, nacelle, and one or more rotor blades. The wind turbine blades capture kinetic energy of wind using known airfoil principles. Modern wind turbines may have rotor blades that exceed 90 meters in length.

Wind turbine blades are usually manufactured by forming two shell parts or shell halves from layers of woven fabric or fibre and resin. Spar caps or main laminates are placed or integrated in the shell halves and may be combined with shear webs or spar beams to form structural support members. Spar caps or main laminates may be joined to, or integrated within, the inside of the suction and pressure halves of the shell.

As the size of wind turbine blades increases, various challenges arise from such blades being subjected to increased forces during operation, requiring improved reinforcing structures. In some known solutions, pultruded fibrous strips of material are used. Pultrusion is a continuous process in which fibres are pulled through a supply of liquid resin and then heated in an open chamber where the resin is cured. Such pultruded strips can be cut to any desired length. As such, the pultrusion process is typically characterized by a continuous process that produces composite parts having a constant cross-section. Thus, a plurality of pultruded strips can be vacuum infused together in a mould to form the spar caps.

Typically, a spar cap in a wind turbine blade is made from either carbon pultrusions or glass pultrusions. Carbon fibres are typically lighter than glass fibres by volume, and have improved tensile and compressive strength. Also, carbon fibres are electrically conductive. Thus, since most turbine blades also comprise a lightning protection system, blade components comprising carbon fibre material must be carefully designed according to their intended interaction with the lightning protection system. Hence, there is an ongoing need for an improved pultruded spar cap and method for incorporating such spar cap in a wind turbine blade.

It is therefore an object of the present invention to provide a wind turbine blade with an improved reinforcing structure, such as a spar cap.

It is another object of the present invention to provide an optimized arrangement of materials used in the manufacture of a spar cap.

It is another object of the present invention to provide a reinforcing structure for a wind turbine blade which is a cost efficient structure and has optimized material characteristics for use in a turbine blade that comprises a lightning protection system.

It is another object of the present invention to provide a suitable reinforcing structure for a wind turbine blade which can be manufactured efficiently.

Summary of the invention

It has been found that one or more of the aforementioned objects can be obtained by providing a method of manufacturing a wind turbine blade shell component, the method comprising the steps of providing a plurality of pultrusion plates, wherein each pultrusion plate comprises a top surface, an opposing bottom surface and two lateral surfaces, arranging the pultrusion plates on a blade shell material in a mould for the blade shell component, and bonding the pultrusion plates with the blade shell material to form the blade shell component, wherein each pultrusion plate is formed of a pultrusion fibre material comprising a plurality of tows of glass fibre material and a plurality of tows of carbon fibre material, and wherein adjoining tows of glass fibre material are provided along the entire top surface and along the entire bottom surface of the pultrusion plate. The present inventors have found that the method of the present invention allows for tailoring the architecture of a hybrid glass/carbon pultrusion for use in a wind turbine blade spar cap, such that the carbon fibre material is utilized in the best possible way, in particular for improving the mechanical compression strain of the pultrusion plates. Carbon fibres usually have high stiffness per weight. These properties are desirable in the spar cap of a wind turbine blade. However, drawbacks of carbon fibres include the relatively low strain to failure and the comparatively high price per kg. Glass fibres are typically cheaper and have higher strain to failure. By contrast, the electrical conductivity of glass fibres is minimal and stiffness per weight is significantly lower.

It is thus preferred that the top surface and the opposing bottom surface, and preferably the lateral surfaces, are free from carbon fibres. Advantageously, no tows of carbon fibre material are arranged along the top surface and along the bottom surface of the plate, and preferably no tows of carbon fibre material are arranged along the lateral surfaces of the plate. It is thus preferred that only glass is provided as fibre material within the uppermost and lowermost layers of the pultrusion plate.

The pultrusion plates of the present invention and the shell component comprising said pultrusion plates also enable a blade configuration in which the spar cap is no longer a conducting part of the blade lightning protection system. Since, the electrical conductivity of the outer surfaces of the pultrusion plates is significantly reduced or eliminated altogether, the risk of lightning damage of the main spar is lowered.

The step of arranging the pultrusion plates on blade shell material in a mould for the blade shell component preferably comprises arranging the pultrusion plates into adjacent stacks of pultrusion plates, wherein adjacent refers to a substantially chordwise direction. These stacks usually extend in a substantially spanwise direction of the shell half. The step of bonding the pultrusion plates with the blade shell material to form the blade shell component usually comprises a resin infusion step in which the pultrusion plates and the blade shell material are infused with a resin, for example in a VARTM process. When arranged in the mould for the shell component, such as a shell half, the first lateral surface of each pultrusion plates faces the leading edge whereas the second lateral surface faces the trailing edge. The top and bottom surfaces usually face up and down, respectively, in a flapwise direction of the blade. A tip end edge or front edge or surface of the pultrusion plate, which may be chamfered, faces towards the tip end of the blade, whereas a root end edge or rear edge or surface of the pultrusion plate, which also may be chamfered, faces towards the root end of the blade.

Each pultrusion plate comprises glass fibres and carbon fibres. In addition, each pultrusion plate preferably comprises a resin or binding agent which is used in the pultrusion process for joining the various fibre tows into a single pultrusion string. Preferably, each pultrusion plate comprises a matrix of fibre tows arranged in rows, and optionally in columns, as seen in a vertical cross section of the plate. Thus, the pultrusion fibre material may comprise glass fibres, carbon fibres, a resin or binding agent, and optionally additional reinforcing material. Typically, the pultrusion plate has a constant cross-section along its length, or along at least 90% of its length if the root end edge and/or tip end edge is chamfered.

Each stack of pultrusion plates may comprise 2-30, such as 5-20 pultrusion plates successively arranged on top of each other. Thus, each stack will usually extend in a spanwise direction of the blade. In a midsection between a root end and a tip end, each stack may comprise 8-15 layers of pultrusion plates, whereas towards the root end and towards the tip end the number of layered pultrusion plates may decrease to 1 -3. Thus, the stack of pultrusion plates is preferably tapered towards both the root end and the distal end. Such configuration advantageously allows for a profile that is consistent with the thickness profile of the shell. Typically, two or more, or three or more stacks of pultrusion plates are arranged next to each other, adjacent to each other in a substantially chordwise direction. Typically, a resin will be infused in the stack of pultrusion plates. This can, for example, be done using vacuum-assisted resin transfer moulding.

The blade shell component is usually a shell half, such as a shell half with a reinforcing structure such as a spar cap. The blade shell material may include one or more fibre layers and/or a gelcoat. The plurality of pultrusion plates will typically extend in a spanwise direction of the shell half or of the blade. Thus, at least some of the pultrusion plates have preferably a length corresponding to 60-95% of the blade length. A polymer resin is typically infused into pultrusion plates following the lay-up into the shell half.

Each pultrusion plate comprises a top surface, an opposing bottom surface and two lateral surfaces. Usually, the top and bottom surfaces face opposing flapwise directions, whereas the lateral surface face towards the trailing edge and towards the leading edge of the blade component, respectively.

The pultrusion fibre material comprises a plurality of tows or rovings of glass fibre material and a plurality of tows or rovings of carbon fibre material. Thus, the ratio of numbers of carbon fibre tows to numbers of glass fibre tows in the pultrusion plate is preferably between 1/5 to 1/1 , such as 1/3 to 1/1 . In a preferred embodiment, each tow comprises 10,000 to 100,000 filaments, preferably 20,000 to 60,000 filaments, of glass or carbon fibre.

In some embodiments, the respective geometric centers or midpoints of adjacent tows are spaced apart by a distance of 0.5-5 mm, preferably by a distance of 1 -3 mm. The exact spacing may depend on the diameter of the tows, which may vary since a range of 10,000 to 100,000 filaments could be used for each tow.

In a particularly preferred embodiment, the distance between adjoining tows of fibre material is less than 100 pm, preferably less than 50 pm, more preferably less than 20 pm, most preferably less than 10 pm. In some embodiments, the distance between adjoining tows of carbon fibre material is zero.

In a preferred embodiment, the tows of glass fibre material and the tows of carbon fibre material extend substantially parallel to each other within the pultrusion plate. In a preferred embodiment, the tows of glass fibre material and the tows of carbon fibre material are arranged in an array, preferably a regular array, of rows and columns of tows, as seen in a vertical cross section of the pultrusion plate. The rows will typically extend in a substantially horizontal or chordwise direction, whereas the columns will typically extend in a substantially vertical or flapwise direction. The array of rows and columns of tows will typically be constant over the length of the pultrusion plate.

In a preferred embodiment, the ratio of carbon fibre material to glass fibre material in the pultrusion plate is between 1/5 to 1/1 , preferably between 1/5 to 7/10. This was found to provide optimised properties of the pultrusion plate in terms of electrical conductivity and overall stiffness.

According to a particularly preferred embodiment, all carbon fibre material in the pultrusion plate is isolated from the top surface, the bottom surface, and the lateral surfaces of the pultrusion plate. In particular it is preferred that glass fibre material isolates the carbon fibre material from said surfaces, in that the glass fibre material is arranged between the carbon fibre material and said surfaces. Thus, in one embodiment, the carbon fibre material is electrically isolated in the centre of the pultrusion plate, seen in a vertical cross section, in that a Faraday cage is formed by glass fibre material arranged around the carbon fibre material to prevent an electrical connection to other blade components.

It is particularly preferred that at least one fibre layer along the top surface and at least one fibre layer along the bottom surface of the pultrusion plate only comprises glass fibres as fibre material. In some embodiments, the tows of carbon fibre material are spaced from the top surface and from the bottom surface, and optionally the lateral surfaces, of the pultrusion plate, by at least one, more preferably at least two layers, such as at least three layers, of tows of glass fibre material. In a preferred embodiment, the tows of carbon fibre material are spaced from the top surface and from the bottom surface, and optionally the lateral surfaces, of the pultrusion plate, by a linear distance of at least 0.5 mm, more preferably at least 1 mm.

One or more of the edges of the pultrusion plates may require chamfering, typically a tip end edge/surface, i.e. an edge facing towards the tip end of the blade, and/or a root end edge/surface, i.e. an edge facing towards the root end of the blade, are provided as chamfered edges. Thus, by providing only glass as fibre material within the uppermost and lowermost layers of the pultrusion plate, the plank drop strength can be improved since any chamfer tip will be primarily made up of glass fibre material, which is less rigid than carbon fibre material, and can be made comparatively thin. It is an advantage when the chamfer tip of the pultrusion plate can be designed comparatively thin and compliant. However, there are limits on how thin it can become, as a too thin design would render the chamfer tip fragile. Since glass fibres are approximately three times less stiff (i.e. more compliant) than carbon, it is advantageous to provide glass fibres at the pultrusion chamfer tip.

In some embodiments, a chamfered edge of the pultrusion plate, or of the reinforcing structure comprising the pultrusion plates, may be covered with an insulating material, such as a glass biax layer. This could be done if said chamfered edge contains exposed carbon fibre material, for example in a central region of the plate. In a preferred embodiment, each pultrusion plate comprises a central region, as seen in a vertical cross section, wherein the central region is spaced apart from each of the top surface, the bottom surface and the lateral surfaces, wherein all tows of carbon fibre material of the pultrusion plate are located in said central region. Preferably, all carbon fibre material in the pultrusion plate is electrically isolated from the top surface, the bottom surface, and the lateral surfaces of the pultrusion plate. In some embodiments, said central region may have a rectangular cross section.

In a preferred embodiment, each tow of carbon fibre material is surrounded by tows of glass fibre material in the pultrusion plate, as seen in a vertical cross section of the pultrusion plate. This was found to increase the compression strain to failure of the pultrusion plates.

In a preferred embodiment, the tows of glass fibre material and the tows of carbon fibre material are arranged in a plurality of rows of tows, and optionally a plurality of columns of tows, as seen in a vertical cross section of the pultrusion plate.

In a preferred embodiment, adjoining tows of glass fibre material are provided along the top surface and along the opposing bottom surface of the pultrusion plate, and preferably along the lateral surfaces of the pultrusion plate. Such arrangements are found to allow for an improved edge grinding process carried out on the pultrusion plates or the reinforcing structure, as an improved adhesion and thus transverse inter-plank strength is obtained. Also, it was found that this results in fewer problems in relation to rework as there is a lower risk of grinding into carbon fibre material, which can be problematic. By arranging glass fibre material around the carbon fibre material, this risk is significantly reduced. Thus, it is preferred that the pultrusion plate comprises no free carbon fibre material edges or outer surfaces. Defects on surfaces and edges, such as surface scratches, edge splinters, grooves etc., become accordingly less critical as compared to pure carbon fibre pultrusions.

In a preferred embodiment, the pultrusion plates are arranged into adjacent stacks of pultrusion plates. In some embodiments, the stacked pultrusion plates are pre-bonded together prior to being bonded to the blade shell. Alternatively, the stacked pultrusion plates are co-bonded with the blade shell materials. In a preferred embodiment, the stacked pultrusion plates are bonded with the blade shell material using an adhesive or in a vacuum assisted resin transfer moulding (VARTM) process. In a preferred embodiment, the lateral surfaces of each pultrusion plate are free from carbon fibres, preferably by providing a continuous path of adjoining tows of glass fibre material along the lateral edges of the pultrusion plate, the continuous path of adjoining tows of glass fibre material extending from the top surface to the opposing bottom surface of the pultrusion plate.

In a preferred embodiment, the plurality of tows of glass fibre material and the plurality of tows of carbon fibre material form a non-random pattern, preferably a symmetrical pattern, as seen in a vertical cross section of the pultrusion plate. In other embodiments, each pultrusion plate comprises a central region, as seen in a vertical cross section, wherein the central region is spaced from the top surface, the bottom surface and the lateral surface, wherein the central region comprises a pattern of tows of glass fibre material and carbon fibre material. In some embodiments, the pattern has reflectional symmetry or bilateral symmetry as appearing on the vertical cross section of the pultrusion plate, such that the left and right sides are mirror images of each other. In other embodiments, the pattern is a random pattern.

In one embodiment, an insulating encapsulation, such as an insulation foil, is provided inside the pultrusion plate, for encapsulating all carbon fibre material present in the pultrusion plate, as seen in a vertical cross section of the pultrusion plate. This can be used to further insulate the carbon fibres in a central region of the pultrusion plate, as seen in a vertical cross section. In another embodiment, an insulating encapsulation, such as an insulation foil, is provided around the entire pultrusion plate, as seen in a vertical cross section of the pultrusion plate.

In another aspect, the present invention relates to a pultrusion plate comprising a top surface, an opposing bottom surface and two lateral surfaces, wherein the pultrusion plate is formed of a pultrusion fibre material comprising a plurality of tows of glass fibre material and a plurality of tows of carbon fibre material, and wherein adjoining tows of glass fibre material are provided along the entire top surface and along the entire bottom surface, and preferably along the entire lateral surfaces, of the pultrusion plate.

In a preferred embodiment, the tows of glass fibre material and the tows of carbon fibre material are arranged in a plurality of rows of tows, and optionally a plurality of columns of tows, as seen in a vertical cross section of the pultrusion plate. In a preferred embodiment, the lateral surfaces of the pultrusion plate are free from carbon fibres, preferably by providing a continuous path of adjoining tows of glass fibre material along the lateral edges of the pultrusion plate, the continuous path of adjoining tows of glass fibre material extending from the top surface to the opposing bottom surface of the pultrusion plate.

In a preferred embodiment, the plurality of tows of glass fibre material and the plurality of tows of carbon fibre material form a non-random pattern, preferably a symmetrical pattern, as seen in a vertical cross section of the pultrusion plate.

In a preferred embodiment, each tow of carbon fibre material is surrounded by tows of glass fibre material in the pultrusion plate, as seen in a vertical cross section of the pultrusion plate.

In another aspect, the present invention relates to a reinforcing structure for a wind turbine blade, the reinforcing structure comprising a plurality of pultrusion plates according to the present invention.

In some embodiments of the reinforcing structure, a non-conductive interlayer material is arranged in between individual pultrusion plates within a stack of pultrusion plates. The interlayer material may, for example, be a polyester veil, glass veil, glass biax, 0/90 glass fabric or other glass fabrics.

In a preferred embodiment, a continuous path of adjoining tows of glass fibre material is provided along the lateral edges of the pultrusion plate, the continuous path of adjoining tows of glass fibre material extending from the top surface to the opposing bottom surface of the pultrusion plate. While the top and bottom surface of a pultrusion plate can be covered by peel ply, its lateral edges are typically not. A lateral edge grinding process is usually used to ensure that the resin rich surface on the edges is removed to allow for adhesion of the infusion resin to the pultrusion; otherwise the adhesion between the pultrusion plates and the resin in the blade main spar may not be satisfactory. The inventors have found that bonding of a resin to a ground carbon fibre surface yields low adhesion, whereas, bonding of a resin to a ground glass fibre surface yields better adhesion. Also, it is advantageous if comparatively cheap material and less stiff material is ground off on the edges. Thus, it was found advantageous to place glass fibres along the lateral edges of the pultrusion plate. Therefore, in a preferred embodiment no carbon fibre material is present at the respective lateral edges of the pultrusion plates. In a preferred embodiment, the continuous path of adjoining tows of glass fibre material extends substantially vertically within the pultrusion plate.

In a preferred embodiment, the plurality of tows of continuous glass fibre material and the plurality of tows of continuous carbon fibre material form a non-random pattern, preferably a symmetrical pattern, as seen in a vertical cross section of the pultrusion plate. Typically, the pattern is constant over the length of the pultrusion plate. In one embodiment, the pattern is a checkerboard pattern, for example with alternating glass fibre tows and carbon fibre tows in some columns and in some rows of the pultrusion plate. Such pattern is found to be comparatively easy to manufacture. An evenly or uniformly distributed pattern, particularly in a centre region of the pultrusion plate, is found to yield a comparatively high compression strength of the plates.

In a preferred embodiment, the pultrusion plates have a length corresponding to an entire length of a spar cap for a wind turbine blade shell. In a preferred embodiment, the pultrusion plates are bonded with the blade shell material in a resin infusion process.

In one aspect, the present invention relates to a wind turbine blade shell component, such as shell half, obtainable by the method of the present invention. The present invention also relates to a wind turbine blade having a pressure side shell and a suction side shell, wherein the suction and pressure side shells are joined along a leading and trailing edge of the blade. One or both of the suction and pressure side shell components further include a reinforcing structure, such as a spar cap bonded to an interior surface of the shell, wherein the spar cap includes a plurality of pultrusion plates according to the present invention. The pultrusion plates preferably have a continuous unbroken length along an entire length of the spar cap.

In another aspect, the present invention relates to a method of manufacturing a wind turbine blade shell component, the method comprising the steps of providing a plurality of pultrusion plates, wherein each pultrusion plate comprises a top surface, an opposing bottom surface and two lateral surfaces, arranging the pultrusion plates on a blade shell material in a mould for the blade shell component, and bonding the pultrusion plates with the blade shell material to form the blade shell component, wherein each pultrusion plate is formed of a pultrusion fibre material comprising glass fibre material and carbon fibre material, wherein the top surface and the bottom surface, and preferably the lateral surfaces, of each pultrusion plate is free from carbon fibre material. In another aspect, the present invention relates to a pultrusion plate with a top surface, an opposing bottom surface and two lateral surfaces, the plate being formed of a pultrusion fibre material comprising glass fibres and carbon fibres, wherein the top surface and the bottom surface, and preferably the lateral surfaces, of the pultrusion plate is free from carbon fibre material. Preferably, the pultrusion plate is suitable for use in the afore-described method of manufacturing a wind turbine blade shell component.

In a preferred embodiment, the pultrusion plate has a rectangular cross section. In a preferred embodiment, the pultrusion plate has the shape of a rectangular cuboid. The pultrusion plate has a length, which typically extend in a substantially spanwise direction when the pultrusion plate is arranged in the blade shell. The pultrusion plate also has a width, which typically extends in a substantially chordwise direction when the pultrusion plate is arranged in the blade shell. The pultrusion plate also has a height or thickness, which typically extends in a substantially flapwise direction when the pultrusion plate is arranged in the blade shell. The length of the plate is typically its largest dimension. The length of the plate extends in the same direction as its longitudinal axis.

The length of the pultrusion plate is typically between 50 and 150 meters, preferably between 50 and 100 meters, more preferably between 70 and 100 meters. The height/thickness of the pultrusion plate is preferably between 2 and 10 millimeters, preferably between 3 and 7 millimeters, most preferably between 4 and 6 millimeters. The width of the plate is preferably between 20 and 300 millimeters, most preferably between 80 and 150 millimeters. In a preferred embodiment, the reinforcing structure, such as the spar cap, comprises between 1 and 15 stacks of pultrusion plates arranged next to each other, more preferably between 3 and 9 stacks. Each stack may comprise up to 20 pultrusion plates arranged on top of each other, such as 2-20 pultrusion plates or 2-10 pultrusion plates. Thus, each reinforcing section, such as each spar cap, may comprise 10 to 200 pultrusion plates.

In a preferred embodiment, the pultrusion fibre material comprises a plurality of tows of glass fibre material and a plurality of tows of carbon fibre material. Thus, each pultrusion plate may comprise 50-300 tows of fibre material in total, preferably 25-180 tows of fibre material. It is preferred that 10-70%, more preferably 15-30% of the tows of fibre material are tows of carbon fibre material. Thus, the tows of carbon fibre material may account for 15-30% of all tows in a pultrusion plates, whereas the tows of glass fibre material may account for 70-85% of all tows of fibre material. The tows will usually extend in the length direction of the pultrusion plate, i.e. substantially parallel to its longitudinal axis, or parallel to the spanwise direction when arranged in the blade shell.

In a preferred embodiment, the tows of glass fibre material and the tows of carbon fibre material are arranged in a regular array or regular grid of rows and columns of tows, as seen in a vertical cross section of the pultrusion plate. The pultrusion plate preferably comprises at least 10 rows and at least 10 columns of tows. In some embodiments, the pultrusion plate preferably comprises 6-8 rows and 6-8 columns of tows. The height/thickness of the pultrusion plate may be 3-10 mm, such as 5 mm, and the width of the pultrusion plate may be 50-200 mm, such as 100 mm.

The pultrusion plate comprises a top surface, an opposing bottom surface and two lateral surfaces, wherein the top surface and the opposing bottom surface are free from carbon fibres. In a preferred embodiment, the plurality of tows of glass fibre material and the plurality of tows of carbon fibre material form a non-random pattern, preferably a symmetrical pattern, as seen in a vertical cross section of the pultrusion plate.

All features and embodiments discussed above with respect to the method of manufacturing a wind turbine blade shell component likewise apply to the pultrusion plate or to the reinforcing structure of the present invention and vice versa.

In another aspect, the present invention relates to a reinforcing structure for a wind turbine blade, the reinforcing structure comprising a plurality of pultrusion plates according to the present invention. The reinforcing structure will typically be a spar cap or a main laminate. In some embodiments, the reinforcing structure comprises a box spar. In other embodiments, the reinforcing structure comprises a spar beam. In a preferred embodiment, the elongate reinforcing structure is a spar structure, such as a spar cap, a spar beam or a box spar. It is preferred that the reinforcing structure extends along the blade in a spanwise direction. Typically, the reinforcing structure will extend over 60-95% of the blade length. The wind turbine blade is usually manufactured from two shell halves, a pressure side shell half and a suction side shell half. Preferably, both shell halves comprise an elongate reinforcing structure, such as a spar cap or a main laminate, according to the present invention. In another aspect, the present invention relates to a wind turbine blade or to a wind turbine blade component comprising a reinforcing structure according to the present invention, or to a wind turbine blade shell component obtainable by the afore-mentioned method of manufacturing a wind turbine blade shell component. The shell halves of the blade will typically be produced by infusing a fibre lay-up of fibre material with a resin such as epoxy, polyester or vinyl ester. Usually, the pressure side shell half and the suction side shell half are manufactured using a blade mould. Each of the shell halves may comprise spar caps or main laminates provided along the respective pressure and suction side shell members as reinforcing structures. The spar caps or main laminates may be affixed to the inner faces of the shell halves. The spar structure is preferably a longitudinally extending load carrying structure, preferably comprising a beam or spar box for connecting and stabilizing the shell halves. The spar structure may be adapted to carry a substantial part of the load on the blade. In some embodiments, the reinforcing structure is arranged within the pressure side shell half. In other embodiments, the reinforcing structure is arranged within the suction side shell half.

In a preferred embodiment, the pressure side shell half and the suction side shell half of the blade are manufactured in respective mould halves, preferably by vacuum assisted resin transfer moulding. According to some embodiments, the pressure side shell half and the suction side shell half each have a longitudinal extent L of 50-100 m, preferably 60-90 m. In a preferred embodiment, the pressure side shell half and the suction side shell half each comprise one or more layers of carbon fibres. According to some embodiments, the method further comprises a step of arranging one or more shear webs in at least one of the shell halves, usually at the location of the reinforcing structure. Each shear web may comprise a web body, a first web foot flange at a first end of the web body, and a second web foot flange at a second end of the web body. In some embodiments, the shear webs are substantially l-shaped. Alternatively, the shear webs may be substantially C-shaped.

In another aspect, the present invention relates to a pultrusion process for manufacturing the pultrusion plate of the present invention, and to a pultrusion plate obtainable by said pultrusion process. Said pultrusion process preferably comprises the provision of a plurality of bobbins carrying respective tows of glass fibre material and a plurality of bobbins carrying respective tows of carbon fibre material. Each tow is advantageously pulled through guide plates, a resin bath, and a heated die by a pulling mechanism. The continuous pultrusion string can be cut into individual pultrusion plates with a length of between 30-200 meters, preferably 50-100 meters, by a cutter. The shaped impregnated plates are then advantageously cured. The guide plates and/or the die may take the form of a spreader or inlet comprising multiple apertures, each aperture receiving a respective carbon fibre tow or glass fibre tow. The apertures can be spaced and they are located so as to guide the fibre tows to form a desired pattern of glass fibre tows and carbon fibre tows in the pultrusion plates.

As used herein, the term “vertical cross section of the pultrusion plate” refers to a cross section of the pultrusion plate on a plane perpendicular to its longitudinal axis, i.e. the axis along the length direction of the pultrusion plate, which is usually the direction in which the pultrusion plate has its greatest extension. When arranged in the blade shell, the longitudinal axis or the length extension of the pultrusion plate will usually coincide substantially with a spanwise direction of the blade.

As used herein, the term “spanwise” is used to describe the orientation of a measurement or element along the blade from its root end to its tip end. In some embodiments, spanwise is the direction along the longitudinal axis and longitudinal extent of the wind turbine blade.

As used herein, the term “horizontal” refers to a direction that is substantially parallel to the chord of the blade when the pultrusion plates are arranged in the blade shell. The vertical direction is substantially perpendicular to the horizontal direction, extending in a substantially flapwise direction of the blade.

Description of the Invention

The invention is explained in detail below with reference to embodiments shown in the drawings, in which

Fig. 1 shows a wind turbine,

Fig. 2 shows a schematic view of a wind turbine blade,

Fig. 3 shows a schematic view of a cross-section of a wind turbine blade, Fig. 4 is a schematic top view of a shell half of a wind turbine blade according to the present invention,

Fig. 5 is a schematic vertical cross section through part of a shell half with a reinforcing structure of the present invention,

Fig. 6 illustrates a pultrusion process for manufacturing the pultrusion plates of the present invention,

Fig. 7 is a schematic vertical cross sectional view of one embodiment of the pultrusion plate of the present invention,

Fig. 8 is a schematic vertical cross sectional view of another embodiment of the pultrusion plate of the present invention,

Fig. 9 is a partial longitudinal sectional view of a pultrusion plate of the present invention,

Fig. 10 is a vertical cross sectional view of a reinforcing structure of the present invention,

Fig. 11 is a longitudinal sectional exploded view of one embodiment of a reinforcing structure of the present invention, and

Fig. 12 is an enlarged view of the highlighted area in Fig. 11 .

Detailed description of the figures

Fig. 1 illustrates a conventional modern upwind wind turbine according to the so-called “Danish concept” with a tower 4, a nacelle 6 and a rotor with a substantially horizontal rotor shaft. The rotor includes a hub 8 and three blades 10 extending radially from the hub 8, each having a blade root 16 nearest the hub and a blade tip 14 farthest from the hub 8. The rotor has a radius denoted R.

Fig. 2 shows a schematic view of a wind turbine blade 10. The wind turbine blade 10 has the shape of a conventional wind turbine blade and comprises a root region 30 closest to the hub, a profiled or an airfoil region 34 farthest away from the hub and a transition region 32 between the root region 30 and the airfoil region 34. The blade 10 comprises a leading edge 18 facing the direction of rotation of the blade 10, when the blade is mounted on the hub, and a trailing edge 20 facing the opposite direction of the leading edge 18.

The airfoil region 34 (also called the profiled region) has an ideal or almost ideal blade shape with respect to generating lift, whereas the root region 30 due to structural considerations has a substantially circular or elliptical cross-section, which for instance makes it easier and safer to mount the blade 10 to the hub. The diameter (or the chord) of the root region 30 may be constant along the entire root area 30. The transition region 32 has a transitional profile gradually changing from the circular or elliptical shape of the root region 30 to the airfoil profile of the airfoil region 34. The chord length of the transition region 32 typically increases with increasing distance rfrom the hub. The airfoil region 34 has an airfoil profile with a chord extending between the leading edge 18 and the trailing edge 20 of the blade 10. The width of the chord decreases with increasing distance rfrom the hub.

A shoulder 40 of the blade 10 is defined as the position, where the blade 10 has its largest chord length. The shoulder 40 is typically provided at the boundary between the transition region 32 and the airfoil region 34. Fig. 2 also illustrates the longitudinal extent L, length or longitudinal axis of the blade.

It should be noted that the chords of different sections of the blade normally do not lie in a common plane, since the blade may be twisted and/or curved (i.e. pre-bent), thus providing the chord plane with a correspondingly twisted and/or curved course, this being most often the case in order to compensate for the local velocity of the blade being dependent on the radius from the hub.

The blade is typically made from a pressure side shell part 36 and a suction side shell part 38 that are glued to each other along bond lines at the leading edge 18 and the trailing edge of the blade 20.

Fig. 3 shows a schematic view of a cross section of the blade along the line l-l shown in Fig. 2. As previously mentioned, the blade 10 comprises a pressure side shell part 36 and a suction side shell part 38. The pressure side shell part 36 comprises a spar cap 41 , also called a main laminate, which constitutes a load bearing part of the pressure side shell part 36. The spar cap 41 comprises a plurality of fibre layers 42 mainly comprising unidirectional fibres aligned along the longitudinal direction of the blade in order to provide stiffness to the blade. The suction side shell part 38 also comprises a spar cap 45 comprising a plurality of fibre layers 46. The pressure side shell part 36 may also comprise a sandwich core material 43 typically made of balsawood or foamed polymer and sandwiched between a number of fibre-reinforced skin layers. The sandwich core material 43 is used to provide stiffness to the shell in order to ensure that the shell substantially maintains its aerodynamic profile during rotation of the blade. Similarly, the suction side shell part 38 may also comprise a sandwich core material 47.

The spar cap 41 of the pressure side shell part 36 and the spar cap 45 of the suction side shell part 38 are connected via a first shear web 50 and a second shear web 55. The shear webs 50, 55 are in the shown embodiment shaped as substantially l-shaped webs. The first shear web 50 comprises a shear web body and two web foot flanges. The shear web body comprises a sandwich core material 51 , such as balsawood or foamed polymer, covered by a number of skin layers 52 made of a number of fibre layers. The blade shells 36, 38 may comprise further fibre-reinforcement at the leading edge and the trailing edge. Typically, the shell parts 36, 38 are bonded to each other via glue flanges.

Fig. 4 is a schematic top view of a shell half 38 of a wind turbine blade according to the present invention, illustrating the location of a reinforcing structure 62 having a spanwise extent Se. In the illustrated embodiment, the reinforcing structure 62 comprises three adjacent stacks 66a, 66b, 66c of pultrusion plates. As seen in Fig. 4, the elongate reinforcing structure 62 extends in a substantially spanwise direction of the blade, with adjacent stacks 66a, 66b, 66c of pultrusion plates. The elongate reinforcing structure 62 has a tip end 74, closest to the tip end of the blade, and a root end 76, closest to the root end of the blade. The elongate reinforcing structure also comprises a spanwise extending front edge 78, which is closest to the leading edge 18 of the blade, and a spanwise extending rear edge 80, which is closest to the trailing edge 20 of the blade.

Fig. 5 is a schematic vertical cross section through part of a shell half with a reinforcing structure 62 of the present invention, as seen from the root end of the blade. The reinforcing structure 62, such as a spar cap, comprises a plurality of pultrusion plates 64 according to the present invention, arranged in adjacent stacks 66a-e, which are arranged on blade shell material 89 in mould 77 for the blade shell component, such as a shell half. The stacked pultrusion plates 64 are then bonded with the blade shell material 89 to form the blade shell component, such as the shell half with the spar cap. Core material 85 is arranged on either chordwise side of the reinforcing structure 62. A first shear web 50 and a second shear web 55 is placed on the spar cap 62 via respective bond lines 88.

Fig. 6 illustrates a pultrusion process for manufacturing the pultrusion plates 64 of the present invention. The pultrusion process makes use of a pultrusion system 90 which comprises a portion for receiving a plurality of bobbins 92 each supplying a tow of glass fibre material 70 and a plurality of bobbins 93 each supply a tow of carbon fibre material 68 from a creel 91 . Additional reinforcement material 94 may be provided. The tows 68,

70 are pulled through guide plates 95, resin bath 96, and heated die 97 by pulling mechanism 98. The pultrusion string 100 is cut into individual pultrusion plates 64 by cutter 99. The shaped impregnated fibres are cured and can optionally be wound onto a roll. The guide plates and/or the die may take the form of a spreader or inlet comprising multiple apertures, each aperture receiving a respective carbon fibre tow or glass fibre tow. The apertures can be spaced and they are located so as to guide the fibre tows to form a desired pattern of glass fibre tows and carbon fibre tows in the pultrusion plates 64. The enlarged view of the pultrusion plate 64 in Fig. 6 also illustrates its longitudinal axis La and its length I. The height/thickness h and width w of the pultrusion plate are illustrated in Fig. 8.

Fig. 7 is a schematic vertical cross sectional view of a pultrusion plate 64 of the present invention, taken along the line a-a’ in Fig. 6. The pultrusion plate 64 comprises a plurality of tows of glass fibre material 70, indicated as white elliptical shapes, and a plurality of tows of carbon fibre material 68, indicated as black elliptical shapes. Adjoining tows of glass fibre material 70 are provided along the entire top surface 81 and along the entire bottom surface 82 of the pultrusion plate. As illustrated in Fig. 7, the tows of glass fibre material 70 and the tows of carbon fibre material 68 can be arranged in an array of rows

71 and columns 72 of tows, as seen in a vertical cross section of the pultrusion plate. Also, each tow of carbon fibre material 68 is surrounded by tows 70 of glass fibre material in the pultrusion plate, as seen in a vertical cross section of the pultrusion plate.

As illustrated in Fig. 7, each pultrusion plate comprises a top surface 81 , an opposing bottom surface 82 and two lateral surfaces 83, 84, wherein the top surface 81 and the opposing bottom surface 82 are free from carbon fibres. Also, in some embodiments, a continuous path 67 of adjoining tows of glass fibre material is provided along the lateral edges 83, 84 of the pultrusion plate 64, the continuous path 67 of adjoining tows of glass fibre material extending from the top surface 81 to the opposing bottom surface 82 of the pultrusion plate. The top surface 81 and the bottom surface may also comprise a layer of peel ply, e.g. a fabric material such as a woven fabric.

As seen in the various embodiment of Fig. 7, the plurality of tows of glass fibre material 70 and the plurality of tows of carbon fibre material 68 form a non-random pattern, such as a symmetrical pattern, as seen in a vertical cross section of the pultrusion plate 64. Fig. 7 illustrates a checkerboard pattern in the centre of the pultrusion plate. Adjoining tows 70 of glass fibre material are provided along the top surface 81 and along the opposing bottom surface 82 of the pultrusion plate.

In the embodiment illustrated in Fig. 8, an insulating encapsulation 63 is provided inside the pultrusion plate 64, for encapsulating all carbon fibre material 68 present in the pultrusion plate. The encapsulation 63 is arranged around a central region 79, which contains all carbon fibre tows of the plate 68. As seen in the partial longitudinal section of Fig. 9, a tip end edge or front edge 87 of the pultrusion plate 64 may be chamfered towards the tip end of the blade, forming a plank drop tip 86. It was found that providing the lowermost layer of the pultrusion plate as glass fibre material improves plank drop strength in comparison with a full carbon pultrusion.

The arrangement with the chamfered front edges is further illustrated in Figs. 11 and 12, which show details of the reinforcing structure/spar cap 62 in a schematic longitudinal section extending between a tip end 74 of the reinforcing structure and a root end 76 of the reinforcing structure. Fig. 12 is an enlarged view of the hatched rectangular area depicted in Fig. 11. The stack of pultrusion plates 64 is thickest in a centre region between the tip end and the root end. Thus, in a midsection between the root end 76 and a tip end 74, each stack may comprise 8-15 layers of pultrusion plates, whereas towards the root end and towards the tip end the number of layered pultrusion plates may decrease to 1 -3, preferably to 1 . The chamfered edges of the pultrusion plates are used to form a smooth slope towards the tip and towards the root end. A glass biax layer 65 can be arranged on top of this arrangement to insulate any exposed carbon fibre material at the edges. In addition, a non-conductive interlayer 69, such as a polyester veil, woven121 , other glass fibre reinforced materials, can be used in between pultrusion plates. In some embodiments, the non-conductive interlayer 69 is a glass biax interlayer. Fig. 10 is a schematic vertical cross sectional view of a reinforcing structure 62 of the present invention, such as a spar cap, comprising three chordwise adjacent stacks 66a- c of pultrusion plates 64. This figure also illustrates the non-conductive interlayer material 69 in between the stacked pultrusion plates.

The invention is not limited to the embodiments described herein and may be modified or adapted without departing from the scope of the present invention.

List of reference numerals

4 tower

6 nacelle

8 hub

10 blades

14 blade tip

16 blade root

18 leading edge

20 trailing edge

30 root region

32 transition region

34 airfoil region

36 pressure side shell part

38 suction side shell part

40 shoulder

41 spar cap

42 fibre layers

43 sandwich core material

45 spar cap

46 fibre layers

47 sandwich core material

50 first shear web

51 core member

52 skin layers

55 second shear web

56 sandwich core material of second shear web 57 skin layers of second shear web

60 filler ropes

62 reinforcing structure

63 insulating encapsulation

64 pultrusion plate

65 glass biax layer

66 stack of pultrusion plates

67 path of glass fibres

68 tow of carbon fibre material

69 non-conductive interlayer

70 tow of glass fibre material

71 row of tows

72 column of tows

73 peel ply

74 tip end of reinforcing structure

76 root end of reinforcing structure

77 mould

78 front edge of reinforcing structure

79 central region

80 rear edge of reinforcing structure

81 top surface of pultrusion plate

82 bottom surface of pultrusion plate

83 first lateral surface of pultrusion plate

84 second lateral surface of pultrusion plate

85 core material

86 plank drop tip

87 front edge of pultrusion plate

88 bond line

89 shell material

90 pultrusion system

91 creel

92 bobbin with tow of glass fibre material

93 bobbin with tow of carbon fibre material

94 additional reinforcement material

95 guide plate

96 resin bath 97 heated die

98 pulling mechanism

99 cutter

100 pultrusion string L length

I length of pultrusion plate w width of pultrusion plate h height of pultrusion plate

La longitudinal axis of pultrusion plate r distance from hub

R rotor radius

Se spanwise extent of reinforcing structure Ce chordwise extent of reinforcing structure

Claims

23 Claims

1 . A method of manufacturing a wind turbine blade shell component (38), the method comprising the steps of providing a plurality of pultrusion plates (64), wherein each pultrusion plate (64) comprises a top surface (81 ), an opposing bottom surface (82) and two lateral surfaces (83, 84), arranging the pultrusion plates (64) on a blade shell material (89) in a mould (77) for the blade shell component, and bonding the pultrusion plates (64) with the blade shell material to form the blade shell component, wherein each pultrusion plate (64) is formed of a pultrusion fibre material comprising a plurality of tows of glass fibre material (70) and a plurality of tows of carbon fibre material (68), and wherein adjoining tows of glass fibre material are provided along the entire top surface (81) and along the entire bottom surface (82) of the pultrusion plate.

2. A method according to claim 1 , wherein each pultrusion plate comprises a central region, as seen in a vertical cross section of the pultrusion plate on a plane perpendicular to its longitudinal axis, wherein the central region is spaced apart from each of the top surface, the bottom surface and the lateral surfaces, wherein all tows of carbon fibre material of the pultrusion plate are located in said central region.

3. A method according to claims 1 or 2, wherein each tow of carbon fibre material (68) is surrounded by tows of glass fibre material (70) in the pultrusion plate.

4. A method according to any of the preceding claims, wherein the tows of glass fibre material (70) and the tows of carbon fibre material (68) are arranged in a plurality of rows (71 ) of tows, and optionally a plurality of columns (72) of tows, as seen in a vertical cross section of the pultrusion plate.

5. A method according to any of the preceding claims, wherein all tows of carbon fibre material in the pultrusion plate are electrically isolated from the top surface and the bottom surface, and preferably from the lateral surfaces, of the pultrusion plate.

6. A method according to any of the preceding claims, wherein the lateral surfaces of each pultrusion plate are free from carbon fibres, preferably by providing a continuous path of adjoining tows of glass fibre material along the lateral edges of the pultrusion plate, the continuous path of adjoining tows of glass fibre material extending from the top surface to the opposing bottom surface of the pultrusion plate.

7. A method according to any of the preceding claims, wherein the plurality of tows of glass fibre material and the plurality of tows of carbon fibre material form a non-random pattern, preferably a symmetrical pattern, as seen in a vertical cross section of the pultrusion plate.

8. A pultrusion plate (64) comprising a top surface (81 ), an opposing bottom surface (82) and two lateral surfaces (83, 84), wherein the pultrusion plate is formed of a pultrusion fibre material comprising a plurality of tows of glass fibre material (70) and a plurality of tows of carbon fibre material (68), and wherein adjoining tows of glass fibre material are provided along the entire top surface (81 ) and along the entire bottom surface (82) of the pultrusion plate.

9. A pultrusion plate (64) according to claim 8, wherein the pultrusion plate comprises a central region, as seen in a vertical cross section of the pultrusion plate on a plane perpendicular to its longitudinal axis, wherein the central region is spaced apart from each of the top surface, the bottom surface and the lateral surfaces, wherein all tows of carbon fibre material of the pultrusion plate are located in said central region.

10. A pultrusion plate according to claims 8 or 9, wherein the tows of glass fibre material (70) and the tows of carbon fibre material (68) are arranged in a plurality of rows (71) of tows, and optionally a plurality of columns (72) of tows, as seen in a vertical cross section of the pultrusion plate.

11. A pultrusion plate according to any of claims 8-10, wherein all tows of carbon fibre material in the pultrusion plate are electrically isolated from the top surface and from the bottom surface, and preferably from the lateral surfaces, of the pultrusion plate.

12. A pultrusion plate according to any of claims 8-11 , wherein the lateral surfaces of the pultrusion plate are free from carbon fibres, preferably by providing a continuous path of adjoining tows of glass fibre material along the lateral edges of the pultrusion plate, the continuous path of adjoining tows of glass fibre material extending from the top surface to the opposing bottom surface of the pultrusion plate.

13. A pultrusion plate according to any of claims 8-12, wherein the plurality of tows of glass fibre material and the plurality of tows of carbon fibre material form a non-random pattern, preferably a symmetrical pattern, as seen in a vertical cross section of the pultrusion plate.

14. A pultrusion plate according to any of claims 8-13, wherein each tow of carbon fibre material (68) is surrounded by tows of glass fibre material in the pultrusion plate.

15. A reinforcing structure for a wind turbine blade, the reinforcing structure comprising a plurality of pultrusion plates (64) according to any of claims 8-14.

16. A reinforcing structure according to claim 15, wherein the carbon fibre material is electrically isolated in the centre of each pultrusion plate such that a Faraday cage is formed by glass fibre material arranged around the carbon fibre material to prevent an electrical connection to other blade components.

17. A wind turbine blade or a wind turbine blade component comprising a reinforcing structure according to claims 15 or 16.