WO2022114262A1 - 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재 - Google Patents

종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재 Download PDF

Info

Publication number
WO2022114262A1
WO2022114262A1 PCT/KR2020/016921 KR2020016921W WO2022114262A1 WO 2022114262 A1 WO2022114262 A1 WO 2022114262A1 KR 2020016921 W KR2020016921 W KR 2020016921W WO 2022114262 A1 WO2022114262 A1 WO 2022114262A1
Authority
WO
WIPO (PCT)
Prior art keywords
bio
paper
packaging material
weight
polyethylene
Prior art date
Application number
PCT/KR2020/016921
Other languages
English (en)
French (fr)
Inventor
고의석
Original Assignee
고의석
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 고의석 filed Critical 고의석
Priority to US18/042,979 priority Critical patent/US20230356515A1/en
Publication of WO2022114262A1 publication Critical patent/WO2022114262A1/ko

Abstract

본 발명은 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재에 관한 것으로, 더욱 상세하게는 산소 및 수분에 대한 차단성을 갖는 종이(1), 상기 종이(1)의 양면에 형성되는 베리어층(2), 및 상기 베리어층(2) 중 어느 하나 또는 둘 모두에 적층되는 바이오 폴리에틸렌층(3)을 포함하는 것을 특징으로 한다. 본 발명에 의하면, 종래 석유 유래의 플라스틱 제품에 비하여 물성이 저하되지 않으면서도, 환경오염을 방지할 수 있으며, 수분과 산소에 대한 차단성이 우수하다는 장점이 있다.

Description

종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재
본 발명은 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재에 관한 것으로, 더욱 상세하게는 종이, 바이오 폴리에틸렌을 라미네이팅함으로써, 종래 석유 유래의 플라스틱 제품 및 알루미늄 포함 제품에 비하여 물성이 저하되지 않으면서도, 환경오염을 방지할 수 있는 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재에 관한 것이다.
최근 현대 산업의 발전에 따라, 각종 제품의 다양화와 상품성이 중요시되고 있으며, 제품의 생산, 저장, 유통 및 판매를 위한 포장에 있어서, 취급 편리성 및 품질 보존 등에 대한 소비자의 요구가 점차 증가하고 있다.
따라서, 포장재 산업 분야에서는 이러한 사회 환경에 발맞추어, 기존 포장의 단순 제품보호 및 품질보존의 수동적인 목적에서 벗어나, 제품의 특성에 따라 적극적으로 포장 제품에 능동적 효과를 제공하려고 하며, 포장재에 기능성 요인을 부여하여 상품성을 증대시키는 연구 노력을 활발히 진행하고 있다.
오늘날 다양한 식품, 의약품, 전자 및 광학분야, 생활용품에서의 포장재로, 가볍고 우수한 가스 차단성, 수분 차단성, 연신성 및 가공성 등으로 인해 플라스틱 포장재의 개발이 많이 이루어지고 있다.
한편, 수분에 민감한 식품, 화장품, 의약품, 전자제품 등의 경우, 포장 내부를 건조한 상태로 유지시킬 필요가 있는데, 이는 수분 활성도가 제품의 물성 변화, 산패 발생, 영양적 손실, 관능적 가치 저하 및 미생물 성장을 통한 부패 발생 등의 원인이 되기 때문이다.
일반적으로 이러한 문제를 해결하기 위하여, 즉, 수분 및 산소의 차단을 위하여, 알루미늄 또는 알루미늄 증착 필름을 일반 플라스틱 필름에 적층하여 포장재를 제조하거나, 수분 차단성 합성고분자인 에틸비닐알코올(EVOH), 폴리염화비닐리덴(PVDC), 나일론, 폴리에스터 등을 사용한 필름에 무기물을 코팅하여 포장재를 제조한다.
그러나 이와 같이 포장재에 알루미늄 재질이 포함되는 경우, 재활용이 불가능하다는 문제가 있다. 또한, 상기 알루미늄 재질이 포함된 포장재 및 수분 차단성 합성 고분자가 포함된 포장재 모두 일반 자연상태에서 버려진 후에 분해가 되지 않아, 심각한 환경오염을 초래하고 있다. 이러한 문제점들로 인하여, 플라스틱을 규제하는 등 포장재에 대한 필요성이 커지고 있는 실정이다.
따라서, 알루미늄 재질을 포함하지 않으면서도, 포장재 내부의 내용물의 변질을 보호를 위하여 충분한 차단성을 갖고 또한 자연상태에서 생분해 가능한 포장재가 요구되는 실정이다.
본 발명이 속하는 기술분야의 선행기술문헌에는 한국 등록특허공보 제10-1240684호, 한국 등록특허공보 제10-2159935호, 한국 등록특허공보 제10-1559044 호 등이 있다.
본 발명의 목적은 종래 석유 유래의 플라스틱 제품에 비하여 물성이 저하되지 않으면서도, 환경오염을 방지할 수 있으며, 알루미늄 재질을 포함하지 않으면서도 수분과 산소에 대한 차단성이 우수한 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재를 제공하는 데 있다.
상기한 목적을 달성하기 위한 본 발명의 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재는, 산소 및 수분에 대한 차단성을 갖는 종이, 상기 종이의 양면에 형성되는 베리어층 및 상기 베리어층 중 어느 하나 또는 둘 모두의 베리어층에 적층되는 바이오 폴리에틸렌층을 포함하는 것을 특징으로 한다.
상기 바이오 폴리에틸렌층은, 식물체 유래의 전분계 바이오매스, 식물체 유래의 셀룰로오스계 바이오매스 또는 이들 모두; 왁스; 계면활성제; 불가사리로부터 추출된 단백질; 순지트 파우더; 및 폴리에틸렌;을 포함하는 것을 특징으로 한다.
상기 바이오 폴리에틸렌층은, 코코섬유 및 버개스를 더 포함하는 것을 특징으로 한다.
상기 베리어층은, 식물성 폴리올 20~50중량%, 디이소시아네이트(diisocyanate) 20~50중량%, 사슬연장제(chain extender) 5~10중량% 및 잔량의 유기용매를 포함하는 조성물의 우레탄 반응물로 구성되는 것을 특징으로 한다.
본 발명의 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재에 의하면, 종래 석유 유래의 플라스틱 제품에 비하여 물성이 저하되지 않으면서도, 환경오염을 방지할 수 있으며, 수분과 산소에 대한 차단성이 우수하다는 장점이 있다.
도 1은 본 발명의 일실시예에 의한 포장재의 단면도.
도 2는 본 발명의 다른 실시예에 의한 포장재의 단면도.
이하, 본 발명을 도 1 및 도 2를 참조하여 상세히 설명한다.
본 발명의 가장 큰 특징은, 종이와 바이오 폴리에틸렌층을 라미네이팅하여 포장재를 제조함으로써, 친환경성이 우수하면서도 종래 석유 유래의 플라스틱 제품에 비하여 물성이 저하되지 않고, 수분과 산소에 대한 차단성 역시 우수한 포장재를 제공한다는 데 있다.
이러한 본 발명의 포장재는, 도 1, 2와 같이, 산소 및 수분에 대한 차단성을 갖는 종이(1), 상기 종이(1)의 양면에 형성되는 베리어층(2) 및 상기 베리어층(2) 중 어느 하나 또는 둘 모두에 적층되는 바이오 폴리에틸렌층(3)을 포함하는 것을 특징으로 한다.
상기 종이(1)는 포장재에 수분, 산소 및 자외선에 대한 차단성을 부여하는 것으로, 종래 산소 및 수분 차단층, 즉 재활용이 어려운 알루미늄 또는 에틸비닐알코올(EVOH), 폴리염화비닐리덴(PVDC), 나일론, 폴리에스터 등의 생분해되지 않는 필름층을 대체하는 것이다. 이러한 종이(1)는 미생물 등에 의하여 생분해 가능함으로써, 포장재가 친환경성을 갖도록 한다.
상기 베리어층(2)은 종이(1)의 양면에 형성되어, 종이(1)의 산소 및 수분 침투성을 억제하는 것으로, 이 기술이 속하는 분야에서 공지된 아크릴 수지, 변성 아크릴 수지, 우레탄 수지 및 변성 우레탄 수지 중 1종 이상의 것으로 형성될 수 있다. 즉, 상기 베리어층(2)이 형성된 종이(1)는 더욱 개선된 산소 및 수분에 대한 차단성을 갖는다.
본 발명에서는 종이(1)의 평량, 베리어층(2)의 두께 등을 조절하여 산소 및 수분 차단성을 조절할 수 있는 것으로, 상기 종이(1)의 평량은 30~300g/㎡일 수 있으며, 상기 베리어층(2)의 두께는 1~50㎛일 수 있다.
그리고 상기 종이(1)의 양면에 형성된 베리어층(2) 중 어느 하나 또는 둘 모두에는 바이오 폴리에틸렌층(3)이 적층된다.
상기 바이오 폴리에틸렌층(3)은 바이오매스를 원료를 포함하는 폴리에틸렌으로 구성된 것을 의미하는 것으로, 대기 중의 탄소가 광합성에 의해 고정된 식물자원을 원료로 사용함으로써, 대기 중의 이산화탄소의 농도가 증가하는 것을 억제하는 효과가 있고, 한정된 자원인 석유의 소비량을 줄일 수 있으며, 폐기 후에는 미생물에 의해 분해되기 때문에 친환경적이라는 효과가 있다.
본 발명에서 상기 바이오 폴리에틸렌층(3)은 바이오매스를 10~90중량%로 포함하는 것이라면 그 종류를 제한하지 않고 사용 가능하다.
이러한 상기 바이오 폴리에틸렌층(3)은 그 두께가 10~300㎛일 수 있는바, 두께가 너무 두꺼울 경우 실링 강도 및 중량물 포장을 버티지 못하고, 너무 두꺼울 경우 원가가 필요 이상 상승하기 때문이다.
상기와 같이 구성되는 포장재는, 종이(1)와 바이오 폴리에틸렌층(3)이 미생물에 의해 효과적으로 분해되므로, 환경오염을 야기시키지 않는다는 장점을 갖는다. 아울러, 종이(1)를 기반으로 바이오 폴리에틸렌층(3)을 라미네이팅하여 포장재를 구성함으로써, 종래 바이오 플라스틱을 단독으로 사용시 발생하는 물성 저하의 문제를 해소할 수 있으며, 산소 및 수분 투과도 역시 개선할 수 있다는 장점이 있다.
본 발명에 의한 포장재의 산소 및 수분 투과도는 사용되는 종이(1), 베리어층(2) 및 바이오 폴리에틸렌층(3)의 종류 및 두께에 따라 달라질 수 있으나, 상기 포장재의 산소 투과도는 0.01~50cc/㎡.day이고, 수분 투과도는 0.01~50g/㎡.day의 범위로 제조 가능하다.
그리고 본 발명에서 상기 종이(1)에 베리어층(2)을 형성하고, 이를 바이오 폴리에틸렌층(3)과 라미네이팅하는 방법은 공지된 방법, 코팅, 열적층, 접착제에 의한 적층 등의 방법에 의하는 것으로, 이에 대한 상세한 설명은 생략하며, 그 방법을 제한하지 않음은 당연하다.
한편, 상기 바이오 폴리에틸렌층(3)은 바이오매스의 함량을 높일수록 일반 플라스틱 필름에 비하여 인장 강도 등의 기계적 물성이 저하될 수밖에 없다. 그리고 바이오매스의 함량을 낮출 경우 생분해성이 저하되어 분해에 오랜 기간이 요구된다.
본 발명은 이를 해소하기 위하여 상기 바이오 폴리에틸렌층(3)을 다음과 같이 구성함이 가장 바람직하다.
즉, 상기 바이오 폴리에틸렌층(3)은, 식물체 유래의 전분계 바이오매스, 식물체 유래의 셀룰로오스계 바이오매스 또는 이들 모두; 왁스; 계면활성제; 불가사리로부터 추출된 단백질; 순지트 파우더; 및 폴리에틸렌;을 포함하는 것을 특징으로 한다. 더욱 구체적으로, 식물체 유래의 셀룰로오스계 바이오매스 또는 이들 모두 10~70중량%; 왁스 5~10중량%; 계면활성제 0.5~5중량%; 불가사리로부터 추출된 단백질 0.5~5중량%; 순지트 파우더 0.5~5중량%; 및 잔량의 폴리에틸렌;을 포함하는 필름층임을 특징으로 한다. 여기서, 상기와 같이 조성비를 제한하는 이유는 생분해성, 항균성, 필름의 기계적 물성 등을 모두 고려한 것이다.
상기 바이오매스로는 식물체 유래의 전분계 바이오매스, 식물체 유래의 셀룰로오스계 바이오매스 중 1종 이상, 가장 바람직하게는 2종 모두를 포함하는 것이다. 상기 식물체 유래의 전분계 바이오매스는, 구체적으로는, 옥수수 전분, 감자 전분, 고구마 전분, 카사바 전분, 이들의 변성 전분일 수 있고, 예를 들면, 산화 전분, 양이온 전분, 크로스링키지 전분, 전분 에스테르, 이들의 결합물에서 선택되는 전분일 수 있고, 또는, 식물종자, 줄기, 뿌리, 잎을 분쇄한 가루로서, 예를 들면, 밀가루, 옥수수 가루, 쌀 가루, 찹쌀 가루, 감자 가루, 고구마 가루, 카사바가루, 이들의 결합물에서 선택되는 식물 가루일 수 있다.
또한, 식물체 유래의 셀룰로오스계 바이오매스는 구체적으로는, 나무섬유, 면섬유, 풀섬유, 갈대섬유, 대나무섬유, 이들의 변성물일 수 있고, 예를 들면, 카르복실메틸셀룰로오스, 카르복시에틸셀룰로오스, 셀룰로오스 에스테르, 셀룰로오스 에테르, 및 그들의 결합물에서 선택될 수 있다.
상기 전분계 바이오매스는 수소 결합을 바탕으로 하여 입자 상을 이루고 있으며, 글루코스 단위에 붙어 있는 수산기로 인하여 수분 흡착성이 뛰어난 친수성의 물질이기에 수분의 자체함량이 10∼13%로 열을 가하여도 흐름성이 나타나지 않으며 약 220℃ 범위에 탄화 현상 발생되며 고분자 간의 결합이 되지 않고, 빈약한 계면 접착력 때문에 기계적 물성이 떨어진다. 따라서 이의 해소를 위하여 셀룰로오스계 바이오매스를 함께 사용함으로써, 결합과 탄화현상을 방지하며, 알칼리에 강하고, 화학약품에 대한 저항성도 있고, 미생물에도 침식당하지 않는 기능을 추가할 수 있는 것이다. 따라서, 본 발명에서 상기 전분계 바이오매스와 셀룰로오스계 바이오매스는 10:1~5 중량비로 사용됨이 가장 바람직하다. 그리고 상기 바이오매스의 입자 크기는 제한하지 않는다.
상기 왁스는 바이오매스와 폴리에틸렌을 연결해주는 역할을 하는 것으로, 파라핀 왁스, 유동 파라핀 왁스, 밀납, 몰다 왁스, 칸데릴라 왁스, 폴리에틸렌 왁스, 폴리프로필렌 왁스 중 선택되는 어느 하나 이상일 수 있으나, 이에 한정되지 않는다.
상기 계면활성제는 상기 바이오매스, 순지트 파우더 등을 폴리에틸렌과의 균일한 혼합을 위한 것으로, 스테아린산, 미리스트산, 팔미트산, 아라키드산, 올레인산, 리놀렌산 및 경화지방산과 같은 지방산, 글리세린, 부틸렌글리콜, 프로필렌 글리콜, 디프로필렌글리콜, 펜틸렌글리콜, 헥실렌글리콜, 폴리에틸렌글리콜 및 솔비톨과 같은 폴리올 계열 중에서 선택된 어느 하나 이상일 수 있으나 이에 한정하지 않는다.
상기 불가사리로부터 추출된 단백질은 바이오 폴리에틸렌층(3)의 인장 강도를 좋게하고, 생분해성을 높여주는 것은 물론, 항균성 역시 개선해주는 역할을 한다. 상기 불가사리로부터 단백질을 추출하는 방법은 종래 기술에 의하는 것으로, 그 실시를 제한하지 않는다.
상기 순지트(shungite) 파우더는, SiO2(규산염)과 C60(플러렌)을 주성분으로 하는 물질로 무기질 필러로써 사용된다. 상기 순지트는 항산화 기능, 전자파 차단 기능, 오염물질의 정화 및 분해 기능, 그리고 살균 및 항균 기능이 있는 것으로, 포장재에 항균성을 부여하고, 전자파 역시 차단하여 전자제품의 포장에도 용이하다. 아울러, 상기 순지트는 산소 및 수분 차단성 역시 높여준다. 본 발명에서 상기 순지트 파우더로는 엘리트 순지트는 물론, 노멀 순지트 역시 사용 가능한 것으로, 그 종류를 제한하지 않으며, 그 입자 크기도 0.1~5㎛ 정도면 족하다.
그리고 상기 폴리에틸렌은 바이오 폴리에틸렌층(3)의 주 수지로서, LDPE, HDPE 등 그 종류와 무관하게 사용 가능하다.
상기와 같이, 식물체 유래의 셀룰로오스계 바이오매스 또는 이들 모두 10~70중량%; 왁스 5~10중량%; 계면활성제 0.5~5중량%; 불가사리로부터 추출된 단백질 0.5~5중량%; 순지트 파우더 0.5~5중량%; 및 잔부의 폴리에틸렌;을 포함하는 바이오 폴리에틸렌층(3)은 생분해성이 우수함은 물론, 항균성이 우수하고, 인장강도 등의 기계적 특성이 개선된다는 장점이 있다.
한편, 상기 바이오 폴리에틸렌층(3)은, 코코섬유 및 버개스를 더 포함할 수 있다. 즉, 식물체 유래의 셀룰로오스계 바이오매스 또는 이들 모두 10~70중량%; 왁스 5~10중량%; 계면활성제 0.5~5중량%; 불가사리로부터 추출된 단백질 0.5~5중량%; 순지트 파우더 0.5~5중량%; 코코섬유 0.1~1중량%; 버개스 0.1~1중량% 및 잔부의 폴리에틸렌;로 구성되는 것이다.
상기 코코섬유(cocofiber)는 코코야자 열매의 섬유층으로, 미생물에 의해 자연분해되어 환경 피해가 없는 천연소재이며, 유기질 비료로 자연 환원된다는 특징이 있다. 아울러, 물리적 특성이 강하여 포장재(3)의 기계적 물성을 개선해준다는 장점이 있다.
상기 버개스(Bagasse)는 사탕수수의 줄기에서 자당(蔗糖)을 짜고 남은 찌꺼기로, 폴리페놀(Polyphenol) 성분을 다량 함유하고 있어, 천연 접착제로서 작용하는 것은 물론, 항균효과 역시 부여한다. 따라서, 바이오 폴리에틸렌층(3)의 물성을 개선해주며, 항균성을 부여하는 역할을 한다.
한편, 본 발명은 생분해성 원료로 조성되어 내구연한의 경과시 미생물에 의해 자연분해되는 포장재로서, 상기 베리어층(2) 역시 바이오 폴리우레탄으로 형성되는 것이 더욱 바람직하다.
상기 바이오 폴리우레탄은 식물성 폴리올 20~50중량%, 디이소시아네이트(diisocyanate) 20~50중량%, 사슬연장제(chain extender) 5~10중량% 및 잔량의 유기용매를 포함하는 조성물의 우레탄 반응물로 구성되는 것으로, 상기 식물성 폴리올은 대두유, 옥수수유, 피마자유, 유채씨유, 야자유, 올리브유, 참깨유, 사탕수수유, 해바라기유 및 팜유 등의 중에서 선택된 1종 이상을 포함할 수 있으며, 이는 이소시아네이트(isocyanate)와 함께 반응하여 폴리우레탄을 제조하는데 사용되는 활성수소화합물인 폴리올 성분으로 사용된다.
상기 디이소시아네이트(diisocyanate)는 TDI(toluene diisocyanate), MDI(4,4-diphenylmethane diisocyanate),PPDI(p-phenylene diisocyanate), XDI(xylene diisocyanate) 중에서 선택된 1종 이상을 포함하는 방향족 계열의 이소시아네이트를 수 있으나, 그 종류를 제한하지 않는다.
상기 사슬연장제(chain exterder)로는 당업계에서 사용하는 일반적인 것을 사용할 수 있으나, 바람직하게는 에틸렌글리콜(ethylene glycol), 1,4-부틸렌글리콜(1,4-butylene glycol), 헥사메틸렌글리콜(1,6-hexamethylene glycol), 1,3-프로판디올(1,3-propanediol) 중에서 선택된 1종 이상을 함유한 글리콜류: 및 에틸렌디아민(ethylene diamine, EDA), 4,4-디페닐메탄디아민(4,4-diphenyl methane diamine, MDA), 이소포렌디아민(isophorene diamine, IPDA) 중에서 선택된 1종 이상을 함유한 디아민류: 중에서 선택된 1종 이상을 사용할 수 있다.
그리고 상기 유기용매 당업계에서 사용하는 일반적인 것을 사용할 수 있으며, 예시적으로 메틸에틸케톤(methylethylketone), 아세톤(acetone), 디에틸케톤(diethylketone) 및 메틸이소부틸케톤(methylisobuthylketone) 중 1종 이상을 사용할 수 있다.
상기와 같이 바이오 폴리우레탄을 이용하여 베리어층(2)을 형성하면, 포장재의 이산화탄소 저감율, 생분해성이 더욱 개선된다는 장점이 있다.
상기와 같은 본 발명의 포장재는 의약품, 화장품, 식품, 전자제품, 각종 산업자재 등의 포장재로서 모두 적용 가능한바, 종래 알루미늄을 포함하는 튜브는 물론, 각종 필름 포장재 등으로 활용할 수 있는 것으로, 그 사용처를 한정하지 않는다.
이하, 본 발명을 구체적인 실시예를 통해 더욱 상세히 설명한다.
(실시예 1)
평량이 150g/㎡인 종이를 준비하고, 상기 종이의 양면에 바이오 폴리우레탄을 캐스팅하고, 80℃에서 30초간 1차 건조하고, 150℃에서 30초간 2차 건조하여 베리어층을 형성하였다. 이때, 베리어층의 두께는 20㎛였다.
이때, 상기 바이오 폴리우레탄은 피마자유(Mw=2,022) 25중량%, MDI(4,4-diphenylmethane diisocyanate) 35중량%, 1,3-프로판디올(1,3-propanediol) 5중량% 및 잔량의 메틸에틸케톤을 혼합한 후, 우레탄 반응시켜서 제조하였다.
그리고 이를 상기 두 베리어층 모두에 100㎛ 두께의 바이오 폴리에틸렌층을 라미네이팅하였다.
이때, 상기 바이오 폴리에틸렌층은, 식물체 유래의 전분계 바이오매스(옥수수 가루)와 식물체 유래의 셀룰로오스계 바이오매스(카르복시에틸셀룰로오스)를 10:3 중량비로 혼합한 바이오매스 50중량%, 폴리에틸렌 왁스 5중량%, 글리세린 4중량%, 불가사리로부터 추출된 단백질 3중량%; 순지트 파우더 3중량%; 및 잔부의 HDPE로 구성된 조성물을 200℃에서 충분히 혼련하고, 이를 바이오 폴리에틸렌 필름의 제조하여 상기 베리어층에 라미네이팅하였다. 상기 바이오매스, 순지트 파우더, 불가사리로부터 추출된 단백질의 입자크기는 0.1~3㎛였다.
그리고 상기 불가사리로부터 추출된 단백질은 다음과 같이 제조하였다.
건조된 아무르 불가사리(Asterias amurensis)를 분쇄한 후 30mesh 체를 이용하여 선별하였다. 상기 선별된 불가사리 400g과 0.1M 수산화나트륨을 1:6(w/v) 비율로 혼합시킨 후 1시간 동안 교반하였다. 교반 후, 10,000 x g에서 20분 동안 원심분리하여 얻어진 침전물을 수돗물로 세척하였다. 세척 후, 0.5% 주석산을 첨가하여 1시간 동안 교반하였으며, 다시 10,000 x g에서 20분 동안 원심분리하여 침전물을 수돗물로 세척하였다. 세척 후, 1M 주석산으로 pH를 6으로 맞춘 후, 초음파 분쇄기를 사용하여 30분 동안 균질화한 후, 80℃에서 3시간 동안 교반하였다. 이를 다시 원심분리하여 상등액을 취한 후, 동결건조하여 단백질을 수득하였다.
(실시예 2)
실시예 1과 동일하게 실시하되, 바이오 폴리에틸렌 필름의 제조시 코코섬유 1중량% 및 버개스 1중량%를 더 사용하였다. 이때, 코코섬유 및 버개스의 입자크기는 0.1~3㎛였다.
(시험예 1)
실시예 1 및 실시예 2에 의해 제조된 포장재의 산소 투과도(oxygen transmission rate:OTR), 수분 투과도(water vapor transmission rate:WVTR)를 측정하고 그 결과를 하기 표 1에 나타내었다.
산소 투과도는 온도 23±1℃, O2 농도 100%의 조건에서 24시간 동안 포장재를 투과하는 산소의 양으로 나타내며, 산소 투과도 시험기를 이용하여 측정하였다. 수분 투과도는 37±1℃, 습도 100%의 조건에서 24시간 동안 포장재를 투과하는 수증기의 양으로 나타내며, 수증기 투과도 시험기를 이용하여 측정하였다.
시험예 1 결과
구분 실시예 1 실시예 2
OTR(cc/㎡.day) 0.54 0.59
WVTR(g/㎡.day) 0.98 0.99
상기 표 4에서와 같이 본 발명의 실시예 1, 2는 우수한 산소 투과도 및 수분 투과도를 보였다.아울러, 이러한 산소 투과도와 수분 투과도는 종이, 베리어층 및 바이오 폴리에틸렌층의 두께, 조성비 등을 조절하여 각각 0.1~50cc/㎡.day, 0.1~50g/㎡.day로 조절할 수 있는 것이다.
(시험예 2)
실시예 1, 2에 의해 제조된 포장재의 생분해성 시험을 실시하였다. 시험은 ASTM D6954-04 방법에 따랐다. 그리고 그 결과를 하기 표 2에 나타내었다.
시험예 2 결과
구분 CO2 방출량에 의하여 계산된 평균 생분해도
표준물질 실시예 1 실시예 2
%(단위) 76.1 48.7 52.2
상기 표 2에서와 같이, 표준물질인 셀룰로오스의 이산화탄소 방출량에 의하여 계산된 평균 생분해도는 76.1%이고, 본 발명에 따라 제조된 실시예 1, 2는 각각 48.7% 및 52.2%로서 우수한 생분해성을 나타냄을 확인할 수 있었다.
(시험예 3)
실시예 1, 2에 의해 제조된 바이오 폴리에틸렌 필름의 인장 강도를 측정하였다. 상기 인장 강도의 측정은 ASTM D3039 규준에 따라 필름을 5×150㎜로 재단하여 만능재료시험기(WL2100C UTM, Withlab Corporation, Gunpo, Korea)를 이용하여 측정하였고, 그 결과를 하기 표 3에 나타내었다. 대조구로는 시판 Bio PE 필름을 사용하였다.
시험예 3 결과
구분 대조구 실시예 1 실시예 2
MD TD MD TD MD TD
인장강도(kgf/㎟) 3.112 2.424 4.125 2.825 4.162 2.852
상기 표 3에서와 같이 본 발명에 의한 실시예 1, 2의 바이오 폴리에틸렌 필름은 대조구에 비하여 인장강도가 현저히 개선됨을 확인할 수 있었다.
(시험예 4)
실시예 1, 2에 의해 제조된 포장재의 항균성을 테스트하였다. 그리고 그 결과는 하기 표 4에 나타내었다.
시험예 4의 결과
구분 BLANK 실시예 1 실시예 2
균주 1 접종직후 균수 1.0×104 - -
24시간 후 균수 2.5×104 3.2×102 <0.63
항균활성치 - 1.8 4.5
균주 2 접종직후 균수 1.0×104 - -
24시간 후 균수 1.0×106 <0.63 <0.63
항균활성치 - 6.1 6.1
시험방법:JIS Z 2801:2010, 필름밀착법 : 세균수/㎠, 항균활성치 log
표준필름: Stomacher® 400 POLY-BAG
시험조건: 시험균액을 (35±1)℃, 90% R.H.에서 24시간 정치 배양 후 균 수 측정
항균효과: 항균활성치 2.0 이상
사용공시균주: 균주1-Staphylococcus aureus ATCC 6538P
균주2-Escherichia coli ATCC 8739
상기 표 4에서와 같이 본 발명에 의한 실시예 1, 2의 포장재는 우수한 항균성을 가짐을 확인할 수 있었다.
이상, 본 발명의 바람직한 일 실시예를 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자라면 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 일 실시예는 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 한다.
* 부호의 설명*
1: 종이 2: 베리어층
3: 바이오 폴리에틸렌층

Claims (4)

  1. 산소 및 수분에 대한 차단성을 갖는 종이(1),
    상기 종이(1)의 양면에 형성되는 베리어층(2),
    및 상기 베리어층(2) 중 어느 하나 또는 둘 모두에 적층되는 바이오 폴리에틸렌층(3)을 포함하는 것을 특징으로 하는 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재.
  2. 제1항에 있어서,
    상기 바이오 폴리에틸렌층(3)은,
    식물체 유래의 전분계 바이오매스, 식물체 유래의 셀룰로오스계 바이오매스 또는 이들 모두; 왁스; 계면활성제; 불가사리로부터 추출된 단백질; 순지트 파우더; 및 폴리에틸렌;을 포함하는 것을 특징으로 하는 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재.
  3. 제2항에 있어서,
    상기 바이오 폴리에틸렌층(3)은,
    코코섬유 및 버개스를 더 포함하는 것을 특징으로 하는 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재.
  4. 제1항에 있어서,
    상기 베리어층(2)은,
    식물성 폴리올 20~50중량%, 디이소시아네이트(diisocyanate) 20~50중량%, 사슬연장제(chain extender) 5~10중량% 및 잔량의 유기용매를 포함하는 조성물의 우레탄 반응물로 구성되는 것을 특징으로 하는 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재.
PCT/KR2020/016921 2020-11-25 2020-11-26 종이를 기반으로 하는 바이오베이스 플라스틱 라미네이팅 포장재 WO2022114262A1 (ko)