WO2021166165A1 - Composition de caoutchouc - Google Patents

Composition de caoutchouc Download PDF

Info

Publication number
WO2021166165A1
WO2021166165A1 PCT/JP2020/006811 JP2020006811W WO2021166165A1 WO 2021166165 A1 WO2021166165 A1 WO 2021166165A1 JP 2020006811 W JP2020006811 W JP 2020006811W WO 2021166165 A1 WO2021166165 A1 WO 2021166165A1
Authority
WO
WIPO (PCT)
Prior art keywords
rubber composition
phr
composition according
epoxy
preferred
Prior art date
Application number
PCT/JP2020/006811
Other languages
English (en)
Inventor
Tomoya SAKURADA
Original Assignee
Compagnie Generale Des Etablissements Michelin
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Compagnie Generale Des Etablissements Michelin filed Critical Compagnie Generale Des Etablissements Michelin
Priority to PCT/JP2020/006811 priority Critical patent/WO2021166165A1/fr
Publication of WO2021166165A1 publication Critical patent/WO2021166165A1/fr

Abstract

Composition de caoutchouc contenant au moins une matrice élastomère, une charge renforçante comprenant principalement une charge inorganique renforçante, un époxy et un système de réticulation à base de peroxyde.
PCT/JP2020/006811 2020-02-20 2020-02-20 Composition de caoutchouc WO2021166165A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/JP2020/006811 WO2021166165A1 (fr) 2020-02-20 2020-02-20 Composition de caoutchouc

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2020/006811 WO2021166165A1 (fr) 2020-02-20 2020-02-20 Composition de caoutchouc

Publications (1)

Publication Number Publication Date
WO2021166165A1 true WO2021166165A1 (fr) 2021-08-26

Family

ID=69960675

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2020/006811 WO2021166165A1 (fr) 2020-02-20 2020-02-20 Composition de caoutchouc

Country Status (1)

Country Link
WO (1) WO2021166165A1 (fr)

Citations (21)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1996037547A2 (fr) 1995-05-22 1996-11-28 Cabot Corporation Composes elastomeres incorporant des noirs de carbone traites au silicium
WO1999009036A1 (fr) 1997-08-21 1999-02-25 Osi Specialties, Inc. Agents de couplage a base de mercaptosilanes bloques, utilises dans des caoutchoucs a charge
WO1999028380A1 (fr) 1997-11-28 1999-06-10 Compagnie Generale Des Etablissements Michelin - Michelin & Cie Composition de caoutchouc pour pneumatiques, renforcee d'un noir de carbone revetu d'une couche alumineuse
WO2002030939A1 (fr) 2000-10-13 2002-04-18 Societe De Technologie Michelin Organosilane polyfonctionnel utilisable comme agent de couplage et son procede d'obtention
WO2002031041A1 (fr) 2000-10-13 2002-04-18 Societe De Technologie Michelin Composition de caoutchouc comportant a titre d'agent de couplage un organosilane polyfonctionnel
WO2002083782A1 (fr) 2001-04-10 2002-10-24 Societe De Technologie Michelin Pneumatique et bande de roulement comportant comme agent de couplage un tetrasulfure de bis-alkoxysilane
WO2003002648A1 (fr) 2001-06-28 2003-01-09 Societe De Technologie Michelin Bande de roulement pour pneumatique renforcee d'une silice a basse surface specifique
WO2003002649A1 (fr) 2001-06-28 2003-01-09 Societe De Technologie Michelin Bande de roulement pour pneumatique renforcee d'une silice a tres basse surface specifique
WO2004033548A1 (fr) 2002-10-11 2004-04-22 Societe De Technologie Michelin Ceinture de pneumatique a base dune charge inorganique et d'un silane-polysulfure
US6849754B2 (en) 2001-08-06 2005-02-01 Degussa Ag Organosilicon compounds
WO2006023815A2 (fr) 2004-08-20 2006-03-02 General Electric Company Compositions cycliques de silanes mercaptofonctionnels bloquees derivees de diol
WO2006125532A1 (fr) 2005-05-26 2006-11-30 Societe De Technologie Michelin Composition de caoutchouc pour pneumatique comportant un agent de couplage organosiloxane
WO2006125534A1 (fr) 2005-05-26 2006-11-30 Societe De Technologie Michelin Composition de caoutchouc pour pneumatique comportant un systeme de couplage organosilicique
WO2006125533A1 (fr) 2005-05-26 2006-11-30 Societe De Technologie Michelin Compostion de cautchouc pour pneumatique comportant un agent de couplage organosilicique et un agent de recouvrement de charge inorganique
WO2007098080A2 (fr) 2006-02-21 2007-08-30 Momentive Performance Materials Inc. Composition de matière de charge non agglomérante à base de silane organofonctionnel
WO2008055986A2 (fr) 2006-11-10 2008-05-15 Rhodia Operations Procede de preparation d'alcoxysilanes (poly)sulfures et nouveaux produits intermediaires dans ce procede
WO2010072685A1 (fr) 2008-12-22 2010-07-01 Societe De Technologie Michelin Agent de couplage mercaptosilane bloque
US20130267640A1 (en) * 2010-11-26 2013-10-10 Michelin Recherche Et Technique S.A. Snow tyre tread
WO2016069007A1 (fr) * 2014-10-31 2016-05-06 Compagnie Generale Des Etablissements Michelin Bande de roulement pour pneu formée d'une composition de caoutchouc vulcanisée à l'aide de peroxyde
WO2017074423A1 (fr) * 2015-10-30 2017-05-04 Compagnie Generale Des Etablissements Michelin Bande de roulement comprenant un agent de vulcanisation à base de peroxyde
JP2018188601A (ja) 2017-05-11 2018-11-29 住友ゴム工業株式会社 スタッドレスタイヤ用ゴム組成物

Patent Citations (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1996037547A2 (fr) 1995-05-22 1996-11-28 Cabot Corporation Composes elastomeres incorporant des noirs de carbone traites au silicium
WO1999009036A1 (fr) 1997-08-21 1999-02-25 Osi Specialties, Inc. Agents de couplage a base de mercaptosilanes bloques, utilises dans des caoutchoucs a charge
WO1999028380A1 (fr) 1997-11-28 1999-06-10 Compagnie Generale Des Etablissements Michelin - Michelin & Cie Composition de caoutchouc pour pneumatiques, renforcee d'un noir de carbone revetu d'une couche alumineuse
US6774255B1 (en) 2000-10-13 2004-08-10 Michelin Recherche Et Technique, S.A. Polyfunctional organosilane usable as a coupling agent and process for the obtainment thereof
WO2002030939A1 (fr) 2000-10-13 2002-04-18 Societe De Technologie Michelin Organosilane polyfonctionnel utilisable comme agent de couplage et son procede d'obtention
WO2002031041A1 (fr) 2000-10-13 2002-04-18 Societe De Technologie Michelin Composition de caoutchouc comportant a titre d'agent de couplage un organosilane polyfonctionnel
US20040051210A1 (en) 2000-10-13 2004-03-18 Jean-Claude Tardivat Rubber composition comprising a polyfunctional organosilane as coupling agent
WO2002083782A1 (fr) 2001-04-10 2002-10-24 Societe De Technologie Michelin Pneumatique et bande de roulement comportant comme agent de couplage un tetrasulfure de bis-alkoxysilane
US7217751B2 (en) 2001-04-10 2007-05-15 Michelin Recherche Et Technique S.A. Tire and tread comprising a bis-alkoxysilane tetrasulfide as coupling agent
WO2003002648A1 (fr) 2001-06-28 2003-01-09 Societe De Technologie Michelin Bande de roulement pour pneumatique renforcee d'une silice a basse surface specifique
WO2003002649A1 (fr) 2001-06-28 2003-01-09 Societe De Technologie Michelin Bande de roulement pour pneumatique renforcee d'une silice a tres basse surface specifique
US6849754B2 (en) 2001-08-06 2005-02-01 Degussa Ag Organosilicon compounds
WO2004033548A1 (fr) 2002-10-11 2004-04-22 Societe De Technologie Michelin Ceinture de pneumatique a base dune charge inorganique et d'un silane-polysulfure
WO2006023815A2 (fr) 2004-08-20 2006-03-02 General Electric Company Compositions cycliques de silanes mercaptofonctionnels bloquees derivees de diol
WO2006125534A1 (fr) 2005-05-26 2006-11-30 Societe De Technologie Michelin Composition de caoutchouc pour pneumatique comportant un systeme de couplage organosilicique
WO2006125533A1 (fr) 2005-05-26 2006-11-30 Societe De Technologie Michelin Compostion de cautchouc pour pneumatique comportant un agent de couplage organosilicique et un agent de recouvrement de charge inorganique
WO2006125532A1 (fr) 2005-05-26 2006-11-30 Societe De Technologie Michelin Composition de caoutchouc pour pneumatique comportant un agent de couplage organosiloxane
WO2007098080A2 (fr) 2006-02-21 2007-08-30 Momentive Performance Materials Inc. Composition de matière de charge non agglomérante à base de silane organofonctionnel
WO2008055986A2 (fr) 2006-11-10 2008-05-15 Rhodia Operations Procede de preparation d'alcoxysilanes (poly)sulfures et nouveaux produits intermediaires dans ce procede
WO2010072685A1 (fr) 2008-12-22 2010-07-01 Societe De Technologie Michelin Agent de couplage mercaptosilane bloque
US20130267640A1 (en) * 2010-11-26 2013-10-10 Michelin Recherche Et Technique S.A. Snow tyre tread
WO2016069007A1 (fr) * 2014-10-31 2016-05-06 Compagnie Generale Des Etablissements Michelin Bande de roulement pour pneu formée d'une composition de caoutchouc vulcanisée à l'aide de peroxyde
WO2017074423A1 (fr) * 2015-10-30 2017-05-04 Compagnie Generale Des Etablissements Michelin Bande de roulement comprenant un agent de vulcanisation à base de peroxyde
JP2018188601A (ja) 2017-05-11 2018-11-29 住友ゴム工業株式会社 スタッドレスタイヤ用ゴム組成物

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
THE JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, vol. 60, February 1938 (1938-02-01), pages 309

Similar Documents

Publication Publication Date Title
WO2020158695A1 (fr) Stratifié
EP3774384B1 (fr) Pneu comportant une bande de roulement
EP3577143A1 (fr) Pneu comprenant une composition de caoutchouc
US11241912B2 (en) Tire comprising a tread
EP3959086B1 (fr) Composition de caoutchouc
EP3774386B1 (fr) Pneu comprenant une bande de roulement
EP3774385B1 (fr) Pneu comprenant une bande de roulement
EP3724268A1 (fr) Composition de caoutchouc
WO2021193901A1 (fr) Article destiné à venir en contact avec le sol, en particulier un pneu
WO2021166165A1 (fr) Composition de caoutchouc
WO2021166166A1 (fr) Composition de caoutchouc
WO2021005718A1 (fr) Stratifié
WO2020158694A1 (fr) Article
CN111094427B (zh) 具有包括橡胶组合物的胎面的轮胎
EP4284658A1 (fr) Article, en particulier un pneu
WO2020039536A1 (fr) Composition de caoutchouc
EP3724259A1 (fr) Procédé de production d'une composition de caoutchouc

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 20713989

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 20713989

Country of ref document: EP

Kind code of ref document: A1