WO2021154701A1 - Yttrium-doped catalyst support - Google Patents
Yttrium-doped catalyst support Download PDFInfo
- Publication number
- WO2021154701A1 WO2021154701A1 PCT/US2021/015046 US2021015046W WO2021154701A1 WO 2021154701 A1 WO2021154701 A1 WO 2021154701A1 US 2021015046 W US2021015046 W US 2021015046W WO 2021154701 A1 WO2021154701 A1 WO 2021154701A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- washcoat
- component
- substrate
- oxidation catalyst
- catalyst composition
- Prior art date
Abstract
Description
Claims