WO2020236513A1 - Relithiation in oxidizing conditions - Google Patents
Relithiation in oxidizing conditions Download PDFInfo
- Publication number
- WO2020236513A1 WO2020236513A1 PCT/US2020/032877 US2020032877W WO2020236513A1 WO 2020236513 A1 WO2020236513 A1 WO 2020236513A1 US 2020032877 W US2020032877 W US 2020032877W WO 2020236513 A1 WO2020236513 A1 WO 2020236513A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- lithium
- positive
- electrode material
- solution
- oxidizing agent
- Prior art date
Abstract
Description
Claims