WO2019241675A1 - Enhanced thermally conductive cushioning foams by addition of metal materials - Google Patents

Enhanced thermally conductive cushioning foams by addition of metal materials Download PDF

Info

Publication number
WO2019241675A1
WO2019241675A1 PCT/US2019/037256 US2019037256W WO2019241675A1 WO 2019241675 A1 WO2019241675 A1 WO 2019241675A1 US 2019037256 W US2019037256 W US 2019037256W WO 2019241675 A1 WO2019241675 A1 WO 2019241675A1
Authority
WO
WIPO (PCT)
Prior art keywords
foam
combinations
group
metal material
mattress
Prior art date
Application number
PCT/US2019/037256
Other languages
French (fr)
Inventor
Bruce W. PETERSON
Mark L. Crawford
Matthew D. MCKNIGHT
Original Assignee
L&P Property Management Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US16/009,458 external-priority patent/US20180298264A1/en
Application filed by L&P Property Management Company filed Critical L&P Property Management Company
Priority to EP19819552.1A priority Critical patent/EP3810715A4/en
Priority to CA3101495A priority patent/CA3101495A1/en
Priority to CN201980040299.4A priority patent/CN112437799A/en
Publication of WO2019241675A1 publication Critical patent/WO2019241675A1/en

Abstract

Methods and combinations for making and using one or more thermally conductive cellular foam layers (1) and other structures comprising flexible cellular foam (2, 3) and metallic material particulates, and said thermally-conductive cellular foam layers (1) may be located on, under, or in cushioning foams and mattresses (20, 110, 120) or placed between on, under, within, or between other layering substrates (2, 3), columns, and other structures to increase the overall cooling capability of the composite. The thermally conductive foam (1) may be used in mattresses (20, 110, 120), pillows (130, 140), bedding products, seat cushions (150), medical cushioning foams, pet beds, and similar materials used in bedding and comfort products.

Description

ENHANCED THERMALLY CONDUCTIVE CUSHIONING
FOAMS BY ADDITION OF METAL MATERIALS
CROSS-REFERENCES TO RELATED APPLICATIONS
[0001] This application is a continuation-in-part application of U.S. Patent Application Serial No. 15/360,474 filed November 23, 2016, which is a divisional application of U.S. Patent Application Serial No. 14/054,071 filed October 15, 2013, issued as U.S. Pat.
No. 9,534,098 on January 3, 2017, which was a continuation-in-part application of U.S. Patent Application Serial No. 13/932,492, issued as U.S. Pat. No. 8,933,140 on January 13, 2015 (which claims the benefit of U.S. Provisional Patent Application 61/667,810 filed July 3, 2012 and is a continuation-in-part application of U.S. Patent Application Serial No. 12/713,586 filed February 26, 2010, issued as U.S. Pat. No. 8,933,139 on January 13, 2015) and a continuation-in-part application of U.S. Patent Application Serial No. 13/932,535, abandoned, (which claimed the benefit of U.S. Provisional Patent Application 61/667,824 filed July 3, 2012 and was a continuation-in-part application of U.S. Patent Application Serial No. 12/713,586 filed February 26, 2010, issued as U.S. Pat. No. 8,933,139 on January 13, 2015), both of which were filed on July 1 , 2013, and all of which are incorporated herein by reference in their entirety.
TECHNICAL FIELD
[0002] This invention relates to methods for making and using one or more thermally conductive foam layers and other structures comprising flexible cellular foam and metal material particulates, and said layers and structures are located on, under, or in mat tresses and bedding products. This invention more specifically relates to various types of thermally conductive foams containing metal material particulates including, but not necessarily limited to, mattresses, pillows, mattress topper pads, quilted toppers, medi cal mattresses and other bedding products.
TECHNICAL BACKGROUND
[0003] Flexible cellular foams such as open-cell polyurethane flexible foams, closed cell polyurethane flexible foams, latex foams and melamine foams typically have low thermal conductivities in the range of about 0.035 to about 0.060 W/(m K). Materials with low thermal conductivities typically function as insulators, such as rigid polyure thane foam insulation board or expanded polystyrene insulation board.
[0004] Heat transfer consists of a combination of the phenomena of conduction, convection and radiation. In a cushion or mattress, heat transfer by radiation is not a significant mode of heat transfer in a cushion or mattress. Instead, heat transfer by conduction and convection are the primary paths for moving heat in and through a cushion or mattress. As a person sleeps on a mattress, the compressed foam under neath the body has reduced air flow paths, and the primary mode of heat transfer in the region below the body is conduction.
[0005] Heat is conducted from the body, through the compressed foam and dis persed into cushion or mattress regions where the foam is not compressed as much, which allows natural convection to occur more readily to remove heat from the mattress. Due to the low thermal conductivity of foam, this this mode of heat transfer is too low to manage the production of heat by a human or animal's body, causing the foam to heat up and thus become uncomfortable. This results in a large region of hot foam around the body which makes the foam uncomfortable.
[0006] U.S. Pat. No. 3,255,128 discloses polyurethane foam compositions contain ing small particles of metallic aluminum and methods for treating the aluminum particles with phosphoric acid to enhance their usefulness in polyurethane foam. The phosphate aluminum flake was added to insulating polyurethane foam panels to decrease the heat flow through the panels by reducing absorption of heat and radiation.
[0007] U.S. Pat. No. 3,833,951 discloses flameproofed mattresses, pillows and sleep ing bags. A metallized heat conductive layer is made by mixing a metal with an aque ous vinyl binder, and the frothed mixture is spread on a polyurethane foam having foam thickness between 0.1 to 1.0 inches and dried around 280 °C. The final dried coating is 0.5 to 6 mils in thickness.
[0008] U.S. Pat. No. 6,772,825 B2 discloses a support surface for patient comfort and to maintain a cool skin temperature by having a refrigerant bladder with boiling point between 23 and 35 degrees Celsius contained within a bladder, a flexible spacer in the bladder such as polyurethane foam, and thermally-conductive aluminum or copper metal strips and a top metal layer located on the outside of the bladder. The strips of metal are used to transfer heat away from refrigerant gas into the surrounding environ ment. Metallic material was not added to the polyurethane foam reactants prior to pro ducing the foam substrate. [0009] It is useful and desirable to develop improved heat transfer in a cushion or mattress to provide a cooler and more comfortable sleep.
SUMMARY
[0010] There is provided, in one non-limiting form, methods of forming an flexible cellular foam with improved thermally conductivity (referred as“TC Foam” or thermally- conductive foam) comprised of a flexible polyurethane foam and/or polyester polyure thane foam and/or latex foam, which may be open or closed celled in nature, and a plurality of metallic material particulates selected from a wide ranging group of metals and metal derivatives. Phase change materials, colorants, plasticizers, and other performance modifying additives may optionally be incorporated into the TC Foam.
The TC Foam contains a metal material in the range of 0.01 % to 70% on a weight basis; alternatively from about 0.5 wt% to about 25 wt%. The average particle size of the metal material particulates range between about 0.1 to about 2000 microns.
[0011] Optionally, the TC Foam may be comprised of a plurality of metal material particulates and a latex foam, which may be of open or close celled nature. In this embodiment, phase change materials, colorants, plasticizers, and other performance modifying additives may optionally be incorporated into the TC Foam. The TC Foam contains a metal material in the range of 0.01 % to 70% on a weight basis.
[0012] Optionally, the TC Foam may be comprised of a plurality of metal material particulates and a melamine foam, which may be of open or close celled nature. In this embodiment, phase change materials, colorants, plasticizers, and other performance modifying additives may optionally be incorporated into the TC Foam. The TC Foam contains a metal material in the range of 0.01 % to 70% on a weight basis.
[0013] The metal material to be used in methods and compositions described herein may be selected from a non-limiting list of aluminum, copper, iron, steel, silver, gold, platinum, nickel, tin, chromium, vanadium, tungsten, titanium, and combinations thereof, or derivatives made from any of those materials combined with oxygen, halo gens, carbon, or silicon, and any combination thereof. Among other things, these derivatives would encompass nitrates, carbides, carbonates, and the like. The metal material may be flakes, powders, crystalline arrangements, particulates, and combina tions thereof.
[0014] The TC Foam may be cut or molded in many structures such as, but not limited to, planar layers, convoluted layers, CNC cut layer, surface modified layers, 3D surface texturing, molded pillows, smooth molded surfaces, molded surfaces with regular or irregular patterns, supportive columns, conduits, such as but not necessarily limited to conduits to channel or flow air, or modified in any way as to generate a desired physical structure such as but not limited to hole punching, channeling, reticu lation or other method known to the art of foaming for modifying the structure of foam. The TC Foam may be adhered in the cushion or mattress composite with adhesive or melting of a thermoplastic on the foam surface and allowing the thermoplastic to re solidify and lock the TC Foam in place on the substrate foam. Alternatively, TC foam can be used as the entire cushion or mattress product without attaching it to any other material such as a mattress topper, mono-block mattress or pillow product. That is, the TC foam may be the only foam in the foam component of a product, or may be a part of the foam component of a product, including but not necessarily limited to a layer of the product.
[0015] There is also provided, in a non-restrictive embodiment, combinations of suitable layering substrates including, but not limiting to, flexible polyurethane foam, latex foam, flexible melamine foam, and other substrates such as thermoplastic or thermoset elastomers, fibers in woven or non-woven form and combinations thereof with one or more TC Foams. Articles that may be manufactured from these combina tions of one or more TC Foams substrates including, but not necessarily limited to, mattresses, mattress toppers, pillows, bedding products, pet beds, quilted mattress toppers, pillow or mattress inserts, contoured support foam or other materials com monly used in the bedding environment.
BRIEF DESCRIPTION OF THE DRAWINGS
[0016] Figure 1 is an illustration of a possible heat transfer pathway in a mattress cross section;
[0017] Figure 2 is the first example construction using a cushion and/or mattress application;
[0018] Figure 3 is the second example construction using a cushion and/or mattress application;
[0019] Figure 4 is the third example construction using a cushion and/or mattress application; [0020] Figure 5 is the fourth example construction using a cushion and/or mattress application;
[0021] Figure 6 is the fifth example construction using a cushion and/or mattress application;
[0022] Figure 7 is the sixth example construction using a cushion and/or mattress application;
[0023] Figure 8 is the seventh example construction using a cushion and/or mat tress application;
[0024] Figure 9 is the eighth example construction using a cushion and/or mattress application;
[0025] Figure 10 is the ninth example construction using a cushion and/or mattress application;
[0026] Figure 1 1 is example breakdown of lateral mattress zones in a cushion and/or mattress application;
[0027] Figure 12 is example breakdown of longitudinal mattress zones in a cushion and/or mattress application;
[0028] Figure 13 is an example of a molded pillow product where the entire struc ture is molded from TC Foam;
[0029] Figure 14 is an example of a molded pillow product where the TC Foam is a region or layer within the pillow;
[0030] Figure 15 is an example of a wheelchair seat using TC Foam in its construe- tion; and [0031] Figure 16 is a picture of TC Foam from Example I with thermally conductive particulates incorporated in an open cell flexible polyurethane foam.
[0032] It will be appreciated that FIGS. 1 -15 are schematic and that the various elements are not necessarily to scale or proportion, and that many details have been removed or simplified for clarity, and thus the methods and compositions are not necessarily limited to the embodiments depicted in the Figures.
[0033] Before the methods and compositions are explained in detail, it is to be understood that these methods and compositions are not limited in its application to the details of construction and the arrangements of the components set forth in the follow ing description or illustrated in drawings. Also, it is understood that the phraseology and terminology used herein are for the purpose of description and should not be regarded as limiting.
DETAILED DESCRIPTION
[0034] It is useful to develop improved heat transfer in a mattress or bedding to provide a cooler and more comfortable sleep or contact by incorporating one or more TC foam layers comprising a flexible cellular foam and metal material, such as in the form of particulates, and said one or more TC foam layers are used on, under, or within mattresses, pillows, bedding products, medical cushioning foams, and similar materials used in bedding environments. TC Foam exhibits enhanced heat transfer properties due to possessing an enhanced thermal conductivity. [0035] Flexible cellular foams may be open cell polyurethane foam, closed cell polyurethane foam, open cell polyester polyurethane foam, closed cell polyester polyurethane foam, latex foam, melamine foam, and combinations thereof.
[0036] Heat transfer consists of a combination of conduction, convection and radia tion. In a mattress or bedding, heat transfer by radiation is not very large. Instead, heat transfer by conduction and convection are the primary paths for moving heat in a mattress or bedding. As a person sleeps on a mattress, the compressed foam under neath the body has reduced air flow paths, and the primary mode in the region below the body is conduction. Heat is conducted from the body, through the compressed foam, into mattress or bedding regions where the foam is not compressed as much, which allows natural convection to occur more readily to remove heat from the mat tress. A cooler and more comfortable sleep may be obtained by increasing the thermal conductivity of a mattress or bedding and allowing the heat from the body to migrate away more rapidly. It will be appreciated that when a person sleeping on a mattress is discussed, the same principles of heat transfer and cool or warm sleep apply if a dog or other pet or warm-blooded animal is sleeping or lying on a mattress or pillow.
[0037] Enhanced heat transfer reduces the amount of a temperature gradient that is required to generate a given amount of heat flow. This means that for the same amount of body heat, a mattress or bedding with TC foam will be able to have a lower surface temperature of the foam in contact with a person, while still conducting the heat away. This will result in a cooler sleep. [0038] Figure 1 is a general representation of a heat transfer path when a person sleeps on a mattress with TC Foam 1 located below the first layer of foam 2. Flowever, Figure 1 does not represent all the possible combinations of TC Foams and substrate foams.
[0039] TC Foams are comprised of an open or closed celled flexible polyurethane or polyester foam that has one or more metallic materials (such as in the form of partic ulates) dispersed throughout the foam. The term“dispersed” covers random disper sions, uniform dispersions, dispersions that are more concentrated in one area or volume of the foam as compared to adjacent areas or volumes, and combinations thereof of the metallic material particulates in the foam. The TC Foam contains metal material in the range of about 0.01 % independently to about 70% on a weight basis. Alternatively, the TC Foam contains metal material in the range of about 1 % independ ently to about 55%, and in another non-limiting embodiment in the range of about 2.5% independently to about 40%, and in a different non-restrictive version in the range of about 4% independently to about 25%. The term“independently” as used in associa tion with various ranges herein means that any lower threshold may be combined with any upper ratio to form a suitable alternative range.
[0040] The thermal conductivity of metals is isotropic. The thermal conductivities in all directions in a metal are approximately 5 - 440 W/(m-°K). The thermal conductivity of polyurethane foam is also isotropic with thermal conductivities in all directions of about 0.035-0.06 W/(m-°K). [0041] Addition of a highly thermally conductive metallic material in a cushion or mattress provides a cooler and more comfortable sleep. The specific metals of interest have thermal conductivities in the range of 5 - 440 W/(m-°K). If the thermal conductivity of the metallic additives are approximately 200 W/(m-°K), the metallic additives have about 1 ,500 times the thermal conductivity of foam. Metallic materials are generally anisotropic in nature exhibiting approximately the same thermal conductivity in all directions. As the foam containing the metallic materials is compressed, the metallic materials may touch or contact one another, or at least will be positioned more closely to each other, resulting in greater ability for the metallic materials to distribute heat, for instance to channel or move heat away from a body lying on a mattress.
[0042] In one non-limiting embodiment, the TC foam (foam plus metal material particulates dispersed therein) may be at least about 0.01 W/(m-°K) higher than the flexible cellular foam with the absence of metal material particulates; alternatively at least about 0.005 W/(m-°K) higher than the flexible cellular foam with the absence of metal material particulates; and in another non-restrictive version, at least about 0.002 W/(m-°K) higher than the flexible cellular foam with the absence of metal material particulates.
[0043] The term“metals” shall be taken to mean an element or its oxides, com pound, or alloy or combination thereof that exhibits good thermal conductivity (k > 5 W/(m-°K)), and may, but is not necessarily required to, exhibit good electrical conductiv ity (resistivity, p < 102 W m). [0044] Metal materials may include, but are not necessarily limited to, lithium, sodium, potassium, rubidium, caesium, francium, beryllium, magnesium, calcium, strontium, barium, radium, zinc, molybdenum, cadmium, scandium, titanium, vanadium, chromium, manganese, iron, cobalt, nickel, copper, yttrium, zirconium, niobium, techne tium, ruthenium, rhodium, palladium, silver, hafnium, tantalum, tungsten, rhenium, osmium, iridium, platinum, gold, mercury, rutherfordium, dubnium, seaborgium, boh- rium, hassium, copernicum, aluminum, gallium, indium, tin, thallium, lead, bismuth, polonium, lanthanum, cerium, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium, actinium, thorium, protactinium, uranium, neptunium, plutonium, americium, curium, berkelium, californium, einsteinium, fermium, mendelevium, nobelium, lawren- cium, meitnerium, darmstadtium, roentgenium, ununtrium, flerovium, ununpentium, livermorium, germanium, arsenic, antimony, astatine, and combinations thereof.
[0045] Suitable metal materials may include, but are not necessarily limited to, aluminum, copper, iron, steel, silver, gold, platinum, nickel, tin, chromium, vanadium, tungsten, titanium, or made from any of those materials combined with oxygen, halo gens, carbon, or silicon, or any combination thereof.
[0046] Metal compounds have been used in foam as catalytic materials with com mon materials of this type including, but not necessarily limited to, stannous octoate, dibutyl tin dilaurate, bismuth neodecanoate, and zinc octoate. These catalytic com pounds are used in small amounts, typically 0.01 % to 0.40% of the foam formulation. Additionally, the binding of the ion in a catalyst structure greatly restricts its ability to function as an element for enhanced thermal transport. In some non-limiting embodi ments, metal material particulates are defined herein to exclude catalysts, pigments, and fire retardants that comprise metals. In another non-restrictive embodiment, the TC foam has an absence of castor oil.
[0047] In a non-limiting embodiment, the metal material can be flake, powder, spherical, crystalline arrangements, or other various particulate forms. A suitable size of metal materials may be between about 0.1 independently to about 2000 microns, alternatively between about 1 independently to about 1000 microns, in another non limiting embodiment between about 80 independently to about 500 microns, in a differ ent non-restrictive embodiment from about 50 independently to about 1500 microns. Most preferred size of metal materials is less 80 independently to about 500 microns, alternatively from about 100 independently to about 250 microns, for reducing acceler ated compression fatigue.
[0048] The TC Foam may also contain useful amounts of conventionally employed additives (“property-enhancing additives”) such as plasticized triblock copolymer gels, cross-linked gels, extruded polyurethane gels, stabilizers, antioxidants, antistatic agents, antimicrobial agents, ultraviolet stabilizers, phase change materials, surface tension modifiers such as silicone surfactants, emulsifying agents, and/or other surfac tants, solid flame retardants, liquid flame retardants, grafting polyols, compatible hydroxyl-containing chemicals which are completely saturated or unsaturated in one or more sites, solid or liquid fillers, anti-blocking agents, colorants such as inorganic pigments, carbon black, organic colorants or dyes, reactive organic colorants or dyes, heat-responsive colorants, heat-responsive pigments, heat-responsive dyes, pH- responsive colorants, pH-responsive pigments, pH-responsive dyes and combinations thereof, fragrances, and viscosity-modifiers such as fumed silica and clays, other TC- enhancing additives and other polymers in minor amounts and the like to an extent not affecting or substantially decreasing the desired properties of the TC Foam.
[0049] Metallized plasticized triblock copolymer gels may be produced from high viscosity triblock copolymers and metal materials, cross-linked gels, extruded polyure thane gels, optionally with diblock copolymers that have been melted or mixed with a plasticizing agent, such as mineral oil, synthetic oil, etc., and optionally mixed with additives such as colorants, polyols, etc.
[0050] Addition of phase change materials to the TC Foam allows the construction composite to store or release energy, which is higher than heat absorbed or released by heat capacity of the non-thermally enhanced construction. Fleat is stored if the solid phase change material changes to a liquid, and heat is released when the liquid phase change material changes to a solid. The melting point temperature is usually chosen to be in the 20 °C to 35 °C range to match the human comfort zone. Once the solid phase change material melts completely, all of the latent heat is used, and the phase change material must be cooled back down below its melting point to solidify the phase change material and regenerate for the next melt cycle. Suitable phase change materials have a solid/liquid phase transition temperature from about -10°F to about 220 °F (about -23 °C to about 104°C). In another non-limiting version, the phase change solid/liquid phase transition temperature is from about 68 °F to about 95 °F (about 20 °C to about 35 °C).
[0051] TC Foams may be prepared by a method or methods including batch-wise or continuous pouring in a form, mold or on a bun production line, and in one non-limiting embodiment, the metal material may be incorporated or blended into the polyol blend in a batch-wise or continuous process in a blending system such as a continuous stirred tank, static mixing elements, air mixers, or any other equipment known in the skill of the art that is used for mixing solids and additives with liquids.
[0052] The TC Foam can be poured in a standard bun form on a conveyor, poured in a mold having planar or non-planar surfaces, texturing, and 3D modification, or poured in a mold with rods to make the foam perforated.
[0053] In one non-limiting embodiment, one or more TC Foams may be added within or on the surface or in any location within the interior cavity of a mold for making molded products such as, but not limited to, pillows, mattresses, or mattress toppers, and individual substrate components added to the mold to react, bind, or encapsulate the TC Foam.
[0054] In another non-limiting embodiment, there may be a smooth gradient transi tion from a TC foam to a substrate foam of any desired type. By“smooth gradient” is meant that there is no sharp demarcation or boundary between the TC foam and the substrate foam. For a non-restrictive example, a pillow with high TC side and low TC side. Such a gradient dispersion of TC solids in cellular foam may be produced by molded or free rise techniques or combinations of these techniques. A non-limiting example of a gradient-transition foam is using one polyurethane reactant stream with a TC additive and one polyurethane reactant stream without a TC additive, injecting the stream with TC additive in the mold first, followed by injecting the stream without TC additive in the mold, closing mold, and allowing foam to expand in the mold cavity. The resulting molded article would have a higher thermally conductive region on one side of the foam and a lower thermally conductive region on the other side of the foam with a gradient transition between regions. For example, during the summer, a person may select the TC side for a cooler pillow; and during the winter, a person may select the non-TC side to reduce heat transfer from the body. The gradient transition also pro vides the benefit of higher thermally conductivity while reducing the overall cost of the foam article.
[0055] Combinations of using both molding and free rise processes include, but are not necessarily limited to producing a TC layer by a free rise method, cutting it, placing it in a mold, and molding it into a vehicle seat. Alternatively, the mold can be first par tially filled with a TC foam and during the same mold pour, the components may be switched to a non-TC foam-forming formulation.
[0056] In another non-limiting example, rotational molding techniques may be used. In a non-limiting embodiment, a mold may be coated with TC foam followed up by inserting or forming the substrate within the foam mold.
[0057] It will be appreciated that the method described herein is not limited to these examples, since there are many possible combinations for making TC Foams with open or closed cell polyurethane foams or polyester foams that can be used in cushion foams or mattresses. Further details about making foams, including gel-foams, and the foam and gel-foam compositions so made may be seen in U.S. Patent No. 8,933,139 B2, 8,933,140 B2, and 9,080,051 B2, and U.S. Patent Application Publication No.
2013/0296449 A1 , incorporated herein by reference in their entirety.
APPLICATIONS OF THE TC FOAM
[0058] TC Foam can be manufactured and combined with substrate foams for use in a variety of bedding, comfort, and/or cushioning applications, including but not necessarily limited to, mattresses, pillows, pillow toppers, mattress toppers, quilted toppers, body support foam, other common bedding materials, furniture foams, wheelchair cushions, and the like where a cooler feeling foam is desirable.
[0059] Layering substrates in combination with one or more TC Foams and optional property-enhancing materials described herein may find utility in a very wide variety of applications. Suitable layering substrates include, but are not limited to, flexible poly urethane foam, flexible polyester polyurethane foam, latex foam, flexible melamine foam, and other substrates (such as fibers in woven or non-woven form), and combina tions thereof. More specifically, in other non-limiting embodiments, the combination of TC Foam and substrate would be suitable as pillows or pillow components, including, but not necessarily limited to, pillow wraps or shells, pillow cores, pillow toppers, for the production of medical comfort pads, medical mattresses and similar comfort and sup port products, and residential/consumer mattresses, mattress toppers, and similar comfort and support products, typically produced with conventional flexible polyure- thane foam or fiber. All of these uses and applications are defined herein as“bedding products”.
[0060] Alternatively, articles may be produced such as a vehicle seat cushion, a back support, and a combination thereof, which comprises of a TC foam layer, flexible cellular foam produced by molding, free rise, and combinations thereof, and a tempera ture adjustment system. The temperature adjustment system is selected from the group including, but not necessarily limited to, heating through electrical resistance, cooling through a refrigerant, and a combination of both.
[0061] Figure 1 depicts a heat source 10, in one non-limiting embodiment a body mass, which is introducing thermal energy into the standard, open cell viscoelastic foam layer 2 through conduction. This figure imitates a human or other warm-blooded body lying on a mattress 20. The TC Foam 1 draws heat in and uses enhanced ther mal conductivity properties to move heat laterally through the mattress. In turn, heat is conducted and convected through open air cells up through layer 2 to the top of the mattress. At this point, natural convection works to remove heat from the system. In this example, the viscoelastic layer 2 and TC Foam 1 are constructed upon another viscoelastic layer 2 and a foundation of base prime foam 3.
[0062] Figure 2 is a first example of construction using a cushion and/or mattress application. The base of the section may be a prime foam layer 3 or other type of base, including but not necessarily limited to springs, pocket coils, latex core, etc. On top of this is a 2 inch (5 cm) standard, open cell viscoelastic (visco) layer 2. The top layer 1 is a 2 inch (5 cm) layer of TC Foam. It will be appreciated that the dimensions given in the examples and descriptions of the various Figures are merely illustrative and are not intended to be limiting. Throughout the drawings, the same or similar reference numer als will be used for the same or similar structures.
[0063] Figure 3 is the second example construction using a cushion and/or mattress application. The base of the section is a prime foam layer 3 or other base layer type as previously noted. On top of this is a 2 inch (5 cm) layer of TC Foam 1 followed by a 2 inch (5 cm) layer 2 of standard, open cell viscoelastic foam.
[0064] Figure 4 is the third example construction using a cushion and/or mattress application. The base of the section is a prime foam layer 3. On top of this is a 2 inch (5 cm) layer of TC Foam 1 followed by a .75 inch (1.9 cm) layer 3 of prime foam. The top layer is a second 2 inch (5 cm) layer of TC Foam 1.
[0065] Figure 5 is the fourth example construction using a cushion and/or mattress application. The base of the section is a prime foam layer 3. On top of this is a 2 inch (5 cm) layer of TC Foam 1 followed by a 2 inch (5 cm) layer 2 of standard, open cell viscoelastic foam. The top layer is a second 2 inch (5 cm) layer of TC Foam 1.
[0066] Figure 6 is the fifth example construction using a cushion and/or mattress application. The base of the section is a prime foam layer 3. On top of this is a 3 inch layer of TC Foam 1.
[0067] It will be appreciated that the TC Foam may comprise all or part of other structures not explicitly illustrated in the Figures, including, but not necessarily limited to, monoblock mattresses or mattress toppers, mattresses comprising two or more TC Foam layers touching one another that can consist of the same or different TC Foam materials, and the like. TC Foams may be used in conjunction with pocket coils or spring bases. They may be incorporated into a construction using an elastomer layer combined with a TC Foam layer. A CNC cut layer (non-planar or egg-crate texture) may also be added as a TC Foam layer.
[0068] Figure 7 is the sixth example construction using a cushion and/or mattress application. The base of the section is a prime foam layer 3. On top of this is a 3 inch (7.6 cm) layer of TC Foam 1. The interface 4 between the two layers is a non-planar convolution, which may be made by convoluting the surface of either or both interfacing layers.
[0069] Figure 8 is the seventh example construction using a cushion and/or mat tress application. The base of the section is a prime foam layer 3. On top of this is a 2 inch (5 cm) layer of TC Foam 1. The interface 4 between the two layers is a non-planar convolution, which may be made by convoluting the surface of either or both interfacing layers. The top of this example is a 2 inch (5 cm) layer 2 of standard, open-cell visco elastic foam.
[0070] Figure 9 is the eighth example construction using a cushion and/or mattress application. The base of the section is a prime foam layer 3. Above this is a 2 inch (5 cm) layer 2 of standard, open-cell viscoelastic foam. On top of this is a 2 inch layer (5 cm) of TC Foam 1. The interface 4 between the two layers is a non-planar convolution, which may be made by convoluting the surface of either or both interfacing layers.
[0071] Figure 10 is the ninth example construction using a cushion and/or mattress application. The base of the section is a prime foam layer 3. Above this is a 2 inch (5 cm) layer of TC Foam 1. On top of this is another 2 inch (5 cm) layer of TC Foam 1.
The interface 4 between the two layers is a non-planar convolution, which may be made by convoluting the surface of either or both interfacing layers.
[0072] Figure 1 1 is an example breakdown of lateral mattress zones or sections in a mattress 110. These zones include: lower body zone or section 112, torso/”belly band” zone or section 114, and head and shoulders zone or section 116. These zones or sections may or may not include TC Foams, example constructions, other mattress layer constructions, or any variation thereof. Furthermore, the zones shown are not limiting, but used as an example to show the possibility of utilizing enhanced thermally dissipating layers in specific areas of cushions and/or a mattress.
[0073] Figure 12 is an example breakdown of longitudinal mattress zones 122 and 124 in a mattress 120. These zones include left section 122 and right section 124. These zones or sections 122 and 124 may or may not include TC Foams, example constructions, other mattress layer constructions, or any variation thereof. Furthermore, the zones shown are not limiting, but used as an example to show the possibility of utilizing enhanced thermally dissipating layers in specific areas of cushions and/or a mattress.
[0074] Figures 1 1 and 12 are meant to illustrate the usage of TC Foams in different regions of mattresses to enhance thermal conductivity in specific regions. They are not to be interpreted as limiting design figures. The exact configuration of these zoned TC Foams would be dependent on the purpose of the mattress construction. [0075] Figures 13 and 14 are depictions of molded pillow systems. Figure 13 is a pillow 130 molded entirely out of TC Foam 1. Whereas Figure 14 shows a pillow 140 using TC Foam 1 as a region within the overall pillow structure 2.
[0076] Figure 15 depicts the use of TC foam in a wheelchair seat cushion 150.
[0077] The invention will now be described more specifically with respect to particu lar formulations, methods and compositions herein to further illustrate the invention, but which examples are not intended to limit the methods and compositions herein in any way.
EXAMPLE I
[0078] A two component system was obtained from Peterson Chemical Technology. The system consisted of a“B” side (PCT-M142B) containing polyols, surfactants, blow ing and gelation catalysts and water, and the“A” side (PCT-M142A) consisted of an isocyanate compound. A pre-blend was made by combining 103.5 parts of the“B” side with 10 parts of LCF-1, an aluminum metal additive particulates (average particle size of about 200 microns) obtained from Peterson Chemical Technology, in a 32 oz. (0.95 L) mix cup. The components were mixed for approximately 45 seconds before adding 43.21 parts of the“A” side component, mixed an additional 10 seconds and poured into a 9” x 9” (23 cm x 23 cm) cake box and allowed to rise and cure in a room temperature environment. A flexible polyurethane foam was produced with aluminum metal material randomly dispersed throughout the foam structure. Physical properties such as density, IFD, and airflow were measured. Additionally measures of the static thermal conductiv ity were obtained by following ASTM E1225 standards for measurement.
[0079] A control foam was produced by an identical procedure but with the omission of the 10 parts of LCF-1 aluminum metal material. This foam was tested by the same procedures and used as a comparative control for the TC Foam.
EXAMPLE II
[0080] A two component system was obtained from Peterson Chemical Technology. The system consisted of a“B” side (PCT-MCFB) containing polyols, surfactants, blow ing and gelation catalysts and water, and the“A” side (PCT-MCFA) consisted of an isocyanate compound. A pre-blend was made by combining 100 parts of the“B” side with 10 parts of copper filament, obtained from Peterson Chemical Technology, in a 32 oz. (0.95 L) mix cup. The components were mixed for approximately 45 seconds before adding 46.08 parts of the“A” side component, mixed an additional 10 seconds and poured into a 9” x 9” (23 cm x 23 cm) cake box and allowed to rise and cure in a room temperature environment. A flexible polyurethane foam was produced with ran domly dispersed copper filaments throughout the foam structure. Physical properties such as density, IFD, and airflow were measured. Additionally measures of the static thermal conductivity were obtained by following ASTM E1225 standards for measure ment. [0081] A control foam was produced by an identical procedure but with the omission of the 10 parts of copper filament. This foam was tested by the same procedures and used as a comparative control for the TC Foam.
DISCUSSION OF RESULTS
[0082] Table 1 shows the formula and test results for the two foams produced by following the procedure of Example I. The results indicate an increase in the thermal conductivity (Static TC) of the control foam by 27.2%, from 0.0478 W/(m-°K) to 0.0608 W/(m-°K). Figure 16 is a black and white photograph of the TC foam produced in Example I, where the aluminum metal particulates were incorporated in an open-cell flexible polyurethane foam. The aluminum metal particulates appear black in color against the relatively lighter background foam color.
[0083] Table 2 shows the formula and test results for the two foams produced by following the procedure of Example II. The results indicate an increase in the thermal conductivity (Static TC) of the control foam by 41.1 %, from 0.051 1 W/(m-°K) to 0.0721 W/(m-°K).
Table 1. Comparison of Formula and Properties of Control and TC Foam of Ex. I
Figure imgf000026_0001
Table 2. Comparison of Formula and Properties of Control and TC Foam of Ex. II
Figure imgf000026_0002
[0084] Many modifications may be made in the methods of and implementation of this invention without departing from the spirit and scope thereof that are defined only in the appended claims. For instance, various combinations of phase change materials or phase change additives, gels, polyols, isocyanates, catalysts, metal materials (including sizes and shapes of metal material particulates) and other additives, and processing pressures and conditions besides those explicitly mentioned herein are expected to be useful.
[0085] The words“comprising” and“comprises” as used throughout the claims is interpreted“including but not limited to”. The present invention may suitably comprise, consist or consist essentially of the elements disclosed and may be practiced in the absence of an element not disclosed. In a non-limiting instance, there may be provided a flexible cellular foam with improved thermally conductivity (TC) foam that consists essentially of or consists of a flexible cellular foam produced by a process comprising, consisting essentially of, or consisting of polymerizing a polyol with a polyisocyanate, and a plurality of metal material particulates dispersed in the flexible cellular foam in an amount effective to improve the thermal conductivity of the flexible cellular foam, in a non-limiting embodiment from about 0.01 to about 25 wt%, where the metal material is that of any of the claimed metal material groups, and having an average particle size range between about 0.1 to about 2000 microns.
[0086] Alternatively, a thermally conductive (TC) latex foam may consists essentially of or consists of a cross-linked latex foam and a plurality of metal material particulates dispersed in the cross-linked latex foam in an amount effective to improve the thermal conductivity of the cross-linked latex foam, where the TC latex foam has improved thermal conductivity as compared to an otherwise identical latex foam with an absence of the metal material particulates, where the improved thermal conductivity is at least 0.002 W/(m-°K) higher than the cross-linked latex foam with an absence of the metal material particles. The proportions, sizes, and types of metal material particulates discussed above are expected to be equally applicable to latex foams.
[0087] There may also be provided a thermally conductive (TC) melamine foam consisting essentially of or consisting of a cross-linked melamine foam and a plurality of metal material particulates dispersed in the cross-linked melamine foam in an amount effective to improve the thermal conductivity of the cross-linked melamine foam, where the TC melamine foam has improved thermal conductivity as compared to an otherwise identical melamine foam with an absence of the metal material particu lates, where the improved thermal conductivity is at least 0.002 W/(m-°K) higher than the cross-linked melamine with an absence of the metal material particles. The propor tions, sizes, and types of metal material particulates discussed above are expected to be equally applicable to melamine foams.
[0088] As used herein, the terms“comprising,”“including,”“containing,”“character ized by,” and grammatical equivalents thereof are inclusive or open-ended terms that do not exclude additional, unrecited elements or method acts, but also include the more restrictive terms“consisting of” and“consisting essentially of” and grammatical equivalents thereof. As used herein, the term“may” with respect to a material, struc ture, feature or method act indicates that such is contemplated for use in implementa- tion of an embodiment of the disclosure and such term is used in preference to the more restrictive term“is” so as to avoid any implication that other, compatible materi als, structures, features and methods usable in combination therewith should or must be, excluded.
[0089] As used herein, the singular forms“a,”“an,” and“the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.
[0090] As used herein, the term“and/or” includes any and all combinations of one or more of the associated listed items. As used herein, the term“about” in reference to a given parameter is inclusive of the stated value and has the meaning dictated by the context (e.g., it includes the degree of error associated with measurement of the given parameter.

Claims

CLAIMS What is claimed is:
1. A flexible cellular foam with improved thermally conductivity (TC) foam
comprising:
a flexible cellular foam, and
a plurality of metal material particulates dispersed in the flexible cellular foam in an amount ranging from about 0.01 wt% to about 70 wt% to improve the thermal conductivity of the flexible cellular foam, where the metal material is selected from the group consisting of beryllium, magnesium, strontium, zinc, molybdenum, cadmium, titanium, vanadium, manganese, gallium, chromium, iron, cobalt, nickel, copper, zirconium, palladium, silver, tantalum, tungsten, platinum, gold, aluminum, indium, tin, bismuth, germanium, antimony, derivatives of these metal materials combined with an element selected from the group consisting of oxygen, halogens, carbon, silicon and combinations thereof, and combinations of any of these, and where the metal material particulates have an average particle size range between about 0.1 to about 2000 microns.
2. The TC foam of claim 1 where the flexible cellular foam is selected from the group consisting of foams produced by a process comprising polymerizing a polyol with a polyisocyanate and latex foams.
3. The TC foam of claim 1 where the TC foam is produced by a method comprising: introducing the plurality of metal material particulates into a mixture of flexible cellular foam-forming components comprising a polyol and an isocyanate; and
polymerizing the polyol and the isocyanate to form the flexible cellular foam.
4. An article of manufacture comprising the TC foam of claim 1 where the article of manufacture is selected from the group consisting of medical cushioning foams, mattresses, pillows, bedding products, cushioning products, mattress pillow toppers, quilted mattress toppers, mattress toppers, and combinations thereof.
5. The TC foam of claim 1 where the flexible cellular foam is an open cell polyurethane foam, closed cell polyurethane foam, open cell polyester polyurethane foam, closed cell polyester polyurethane foam, and combinations thereof.
6. The TC foam of claim 1 wherein the metal material is selected from the group consisting of titanium, zinc, nickel, copper, tungsten, platinum, gold, silver, aluminum, tin, chromium, manganese, iron, cobalt, gallium, beryllium, magnesium, strontium, zirconium, molybdenum, derivatives of these metal materials combined with an element selected from the group consisting of oxygen, halogens, carbon, silicon and
combinations thereof, and combinations of any of these.
7. The TC foam of claim 1 wherein the metal material particulates are in the form of flakes, powders, spherical, crystalline arrangement, and combinations thereof.
8. The TC foam of claim 1 wherein the TC foam comprises a structure selected from the group consisting of a solid sheet, a perforated sheet, a non-planar sheet, a planar sheet, a textured sheet, and combinations thereof.
9. The TC foam of claim 1 wherein the TC foam is adhered to a layering substrate.
10. The TC foam of claim 1 comprising a smooth gradient transition from the TC foam to a substrate foam.
1 1. An article of manufacture selected from the group consisting of a cushion foam, a mattress, a mattress topper pad, a pillow, and combinations thereof, where the article of manufacture comprises a TC foam of claim 1.
12. An article of manufacture selected from the group consisting of a cushion foam, a mattress, a mattress topper pad, and combinations thereof, where the article of manufacture comprises a rectangular shape having a relatively long side and a relatively short side, and at least one zone selected from the group consisting of a longitudinal zone parallel to the relatively long side, a lateral zone parallel to the relatively short side, and combinations thereof, where the at least one zone comprises the TC foam of claim 1.
13. An article of manufacture selected from the group consisting of medical cushioning foams, mattresses, pillows, bedding products, cushioning products, mattress pillow toppers, quilted mattress toppers, mattress toppers, and combinations thereof, where the article of manufacture further comprises the TC foam of claim 1.
14. An article of manufacture comprising:
at least one layer comprising a TC foam of claim 1 ; and
a component produced by a process selected from the group consisting of
molding, free-rise, and combinations thereof;
where the article of manufacture is selected from the group consisting of a seat cushion, a back support, and a combination thereof.
15. A thermally conductive (TC) foam comprising:
a flexible cellular foam produced by a process comprising polymerizing a polyol with a polyisocyanate, and
a plurality of metal material particulates dispersed in the flexible cellular foam in an amount ranging from about 0.01 wt% to about 25 wt% to improve the thermal conductivity of the flexible cellular foam, where the metal material is selected from the group consisting of titanium, zinc, nickel, copper, tungsten, platinum, gold, aluminum, tin, chromium, manganese, iron, cobalt, gallium, beryllium, magnesium, strontium, zirconium, molybdenum, derivatives of these metal materials combined with an element selected from the group consisting of oxygen, halogens, carbon, silicon and combinations thereof, and combinations of any of these, and where the metal material particulates have an average particle size range of between about 1 to about 1000 microns.
16. A thermally conductive (TC) foam comprising:
a flexible cellular foam produced by a process comprising polymerizing a polyol with a polyisocyanate, the flexible cellular foam selected from the group consisting of an open cell polyurethane foam, closed cell polyurethane foam, open cell polyester polyurethane foam, closed cell polyester polyurethane foam, and combinations thereof, and
a plurality of metal material particulates dispersed in the flexible cellular foam in an amount ranging from about 0.01 wt% to about 70 wt% to improve the thermal conductivity of the flexible cellular foam, where the metal material is selected from the group consisting of magnesium, titanium, vanadium, chromium, iron, cobalt, nickel, copper, zirconium, silver, platinum, gold, mercury, aluminum, tin, derivatives of these metal materials combined with an element selected from the group consisting of oxygen, halogens, carbon, silicon and combinations thereof, and combinations of any of these, and where the metal material particulates have an average particle size range of between about 0.1 to about 2000 microns.
17. A thermally conductive (TC) latex foam comprising:
a cross-linked latex foam; and
a plurality of metal material particulates dispersed in the cross-linked latex foam in an amount ranging from about 0.01 wt% to about 70 wt% to improve the thermal conductivity of the cross-linked latex foam, where the metal material is selected from the group consisting of beryllium, magnesium, strontium, zinc, molybdenum, cadmium, titanium, vanadium, manganese, iron, cobalt, nickel, copper, zirconium, palladium, silver, tantalum, tungsten, platinum, gold, aluminum, indium, tin, bismuth, germanium, antimony, derivatives of these metal materials combined with an element selected from the group consisting of oxygen, halogens, carbon, silicon and combinations thereof, and combinations of any of these, and where the metal material particulates have an average particle size range between about 0.1 to about 2000 microns.
PCT/US2019/037256 2018-06-15 2019-06-14 Enhanced thermally conductive cushioning foams by addition of metal materials WO2019241675A1 (en)