WO2019237607A1 - 扬声器振膜以及扬声器 - Google Patents
扬声器振膜以及扬声器 Download PDFInfo
- Publication number
- WO2019237607A1 WO2019237607A1 PCT/CN2018/110166 CN2018110166W WO2019237607A1 WO 2019237607 A1 WO2019237607 A1 WO 2019237607A1 CN 2018110166 W CN2018110166 W CN 2018110166W WO 2019237607 A1 WO2019237607 A1 WO 2019237607A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- diaphragm
- speaker diaphragm
- layers
- thermoplastic polyester
- speaker
- Prior art date
Abstract
Description
Claims (13)
- 一种扬声器振膜,其特征在于,包括热塑性聚酯弹性体膜层,其中,热塑性聚酯弹性体为聚酯硬段A与聚醚或脂肪族聚酯软段B组成的共聚物,所述热塑性聚酯弹性体膜层的杨氏模量为1-1000MPa,10%应变后的弹性回复率≥80%。
- 根据权利要求1所述的扬声器振膜,其特征在于,所述热塑性聚酯弹性体膜层的杨氏模量为2-700MPa。
- 根据权利要求1或2所述的扬声器振膜,其特征在于,所述热塑性聚酯弹性膜层的损耗因子≥0.015。
- 根据权利要求1-3任一项所述的扬声器振膜,其特征在于,所述热塑性聚酯弹性体膜层的断裂伸长率≥300%。
- 根据权利要求1-4任一项所述的扬声器振膜,其特征在于,所述热塑性聚酯弹性体膜层的玻璃化转变温度为-90℃-0℃。
- 根据权利要求1-5任一项所述的扬声器振膜,其特征在于,所述聚醚或脂肪族聚酯软段B的材料选自脂肪族聚酯、聚四氢呋喃醚、聚苯醚和聚环氧乙烷中的一种或多种,所述聚酯硬段A的质量百分数为10-95%,所述聚醚或脂肪族聚酯软段B的材料的相对分子质量为600-6000。
- 根据权利要求1-6任一项所述的扬声器振膜,其特征在于,所述聚酯硬段A的材料为二元酸与二元醇的聚合物,其中,二元酸选自对苯二甲酸、间苯二甲酸、萘二甲酸和联苯二甲酸中的一种或多种,二元醇选自乙二醇、丙二醇、丁二醇、戊二醇、己二醇中的一种或多种。
- 根据权利要求1-7任一项所述的扬声器振膜,其特征在于,所述聚酯硬段A能够结晶,并且所述聚酯硬段A材料的平均聚合度≥2,所述聚酯硬段A熔融温度≥150℃。
- 根据权利要求1-8任一项所述的扬声器振膜,其特征在于,包括复合在一起的两个表层和位于两个表层之间的至少一个中间层,至少一个所述表层为热塑性聚酯弹性体膜层,至少一个中间层为胶黏剂层。
- 根据权利要求9所述的扬声器振膜,其特征在于,所述扬声器振膜 呈三层结构,包括一个所述中间层,两个所述表层均为热塑性聚酯弹性体膜层。
- 根据权利要求9或10所述的扬声器振膜,其特征在于,所述扬声器振膜包括两个所述中间层,两个所述表层均为热塑性聚酯弹性体膜层,两个所述中间层为不同材料的胶黏剂层。
- 根据权利要求9-11任一项所述的扬声器振膜,其特征在于,所述扬声器振膜包括三个所述中间层,其中,两个所述中间层为胶黏剂层,另外一个中间层为所述热塑性聚酯弹性体膜层,所述热塑性聚酯弹性体膜层位于两个所述胶黏剂层之间;或者三个所述中间层均为胶黏剂层。
- 一种扬声器,其特征在于,包括振动系统和与所述振动系统相互配合的磁路系统,所述振动系统包括如权利要求1-12中的任意一项所述的扬声器振膜。