WO2019175729A1 - Procédés de production couche par couche avec durcissement sélectif - Google Patents

Procédés de production couche par couche avec durcissement sélectif Download PDF

Info

Publication number
WO2019175729A1
WO2019175729A1 PCT/IB2019/051905 IB2019051905W WO2019175729A1 WO 2019175729 A1 WO2019175729 A1 WO 2019175729A1 IB 2019051905 W IB2019051905 W IB 2019051905W WO 2019175729 A1 WO2019175729 A1 WO 2019175729A1
Authority
WO
WIPO (PCT)
Prior art keywords
voxels
layer
enclosed
voxel
cured
Prior art date
Application number
PCT/IB2019/051905
Other languages
English (en)
Inventor
Jeffrey N. BARTOW
Per M. Nelson
Nicholas S. WREN
Alexandra R. CUNLIFFE
Gareth A. Hughes
Original Assignee
3M Innovative Properties Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 3M Innovative Properties Company filed Critical 3M Innovative Properties Company
Publication of WO2019175729A1 publication Critical patent/WO2019175729A1/fr

Abstract

L'invention concerne des procédés de couche par couche pour produire des objets tridimensionnels. Les procédés comprennent des étapes de durcissement sélectif dans lesquelles, pour au moins certaines couches, toutes les limites de l'objet sont durcies et des parties restantes de l'objet sont durcies de manière sélective. Par conséquent, au moins une partie de ces couches reste non durcie avant la formation de la couche suivante. Dans certains modes de réalisation, ces procédés comprennent des étapes pour limiter la quantité de résine non durcie dans l'objet final.
PCT/IB2019/051905 2018-03-13 2019-03-08 Procédés de production couche par couche avec durcissement sélectif WO2019175729A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201862642310P 2018-03-13 2018-03-13
US62/642,310 2018-03-13

Publications (1)

Publication Number Publication Date
WO2019175729A1 true WO2019175729A1 (fr) 2019-09-19

Family

ID=66102148

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/IB2019/051905 WO2019175729A1 (fr) 2018-03-13 2019-03-08 Procédés de production couche par couche avec durcissement sélectif

Country Status (2)

Country Link
TW (1) TW202003206A (fr)
WO (1) WO2019175729A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020018575A1 (fr) * 2018-07-17 2020-01-23 Ajia Global Services Matériaux support et de remplissage et procédés pour la production d'un objet tridimensionnel
US20210354376A1 (en) * 2018-11-13 2021-11-18 Covestro Intellectual Property Gmbh & Co. Kg Method for producing an additively manufactured and treated object

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020253635A1 (fr) * 2019-06-17 2020-12-24 Luxcreo (Beijing) Inc. Systèmes et procédés pour impression en trois dimensions

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1179411A2 (fr) * 2000-08-11 2002-02-13 3D Systems, Inc. Stéréolithographie
EP2241430A1 (fr) * 2009-04-14 2010-10-20 Global Filtration Systems, Inc. Procédé de réduction de la force nécessaire pour séparer un objet solidifié d'un substrat
US20110222081A1 (en) * 2010-03-15 2011-09-15 Chen Yi Printing Three-Dimensional Objects Using Hybrid Format Data
WO2017127561A1 (fr) 2016-01-21 2017-07-27 3M Innovative Properties Company Traitement additif de fluoropolymères

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1179411A2 (fr) * 2000-08-11 2002-02-13 3D Systems, Inc. Stéréolithographie
EP2241430A1 (fr) * 2009-04-14 2010-10-20 Global Filtration Systems, Inc. Procédé de réduction de la force nécessaire pour séparer un objet solidifié d'un substrat
US20110222081A1 (en) * 2010-03-15 2011-09-15 Chen Yi Printing Three-Dimensional Objects Using Hybrid Format Data
WO2017127561A1 (fr) 2016-01-21 2017-07-27 3M Innovative Properties Company Traitement additif de fluoropolymères

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020018575A1 (fr) * 2018-07-17 2020-01-23 Ajia Global Services Matériaux support et de remplissage et procédés pour la production d'un objet tridimensionnel
US20210354376A1 (en) * 2018-11-13 2021-11-18 Covestro Intellectual Property Gmbh & Co. Kg Method for producing an additively manufactured and treated object

Also Published As

Publication number Publication date
TW202003206A (zh) 2020-01-16

Similar Documents

Publication Publication Date Title
WO2019175729A1 (fr) Procédés de production couche par couche avec durcissement sélectif
Zakeri et al. A comprehensive review of the photopolymerization of ceramic resins used in stereolithography
CN108495877B (zh) 含氟聚合物的增材加工
Santoliquido et al. Additive Manufacturing of ceramic components by Digital Light Processing: A comparison between the “bottom-up” and the “top-down” approaches
US10894362B2 (en) Method for specifying and fabricating an object, associated apparatus, and applications
Schwarzer et al. Process development for additive manufacturing of functionally graded alumina toughened zirconia components intended for medical implant application
Dean et al. Continuous digital light processing (cDLP): Highly accurate additive manufacturing of tissue engineered bone scaffolds: This paper highlights the main issues regarding the application of Continuous Digital Light Processing (cDLP) for the production of highly accurate PPF scaffolds with layers as thin as 60 μm for bone tissue engineering
Wu et al. Influence of boundary masks on dimensions and surface roughness using segmented exposure in ceramic 3D printing
EP3925761A1 (fr) Systèmes et procédés pour fabriquer des objets tridimensionnels
Yirmibesoglu et al. Multi-material direct ink writing of photocurable elastomeric foams
CN101063812A (zh) 通过掩膜曝光生成三维对象的设备和方法
WO2009042671A1 (fr) Bioréacteurs tridimensionnels microfabriqués à réseau capillaire incorporé
JP7183352B2 (ja) ３次元物体を形成する方法
CN110997779B (zh) 含氟聚合物的增材加工
US11628618B2 (en) Additive manufacturing method for functionally graded material
Credi et al. Combining stereolithography and replica molding: On the way to superhydrophobic polymeric devices for photovoltaics
Du et al. Study of falling‐down‐type DLP 3D printing technology for high‐resolution hydroxyapatite scaffolds
Huang et al. Visible light 3D printing of high-resolution superelastic microlattices of poly (ethylene glycol) diacrylate/graphene oxide nanocomposites via continuous liquid interface production
Fei et al. Digital halftoning for printer-independent stereolithography of functionally graded materials
RU2783378C2 (ru) Пористый полимерный трехмерный объект сложной формы и способ изготовления пористого полимерного трехмерного объекта сложной формы
Weeks Embedded 3D Printing of Polymeric and Ceramic Lattices
Meem On the Mechanics and Dynamics of Soft UV-cured Materials with Extreme Stretchability for DLP Additive Manufacturing
Scheithaueré et al. CT vol 258 a grid. dxa 2/6/2016 1: 41 PM Page 31–8–
JP2021142739A (ja) セラミックス成形体の製造方法およびセラミックス成形体
KR20240018738A (ko) 고정밀 광경화 3d 프린팅 방법 및 이를 이용한 고정밀 조형물 제조방법

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19716553

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19716553

Country of ref document: EP

Kind code of ref document: A1