WO2019147527A1 - Procédé de fabrication d'un article manufacturé - Google Patents

Procédé de fabrication d'un article manufacturé Download PDF

Info

Publication number
WO2019147527A1
WO2019147527A1 PCT/US2019/014447 US2019014447W WO2019147527A1 WO 2019147527 A1 WO2019147527 A1 WO 2019147527A1 US 2019014447 W US2019014447 W US 2019014447W WO 2019147527 A1 WO2019147527 A1 WO 2019147527A1
Authority
WO
WIPO (PCT)
Prior art keywords
filament
filaments
agents
particles
fibrous structure
Prior art date
Application number
PCT/US2019/014447
Other languages
English (en)
Inventor
Anthoney Edward REED
Michael Sean Pratt
Paul R. Mort, Iii
Stephen Robert Glassmeyer
Dinah Achola Nyangiro
Mark William Hamersky
Richard Allen DIEMAR
Jeffrey Moss Vaughn
Gavin John Broad
Gregory Charles Gordon
Frank William Denome
Mark Robert Sivik
Andreas Josef Dreher
Original Assignee
The Procter & Gamble Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by The Procter & Gamble Company filed Critical The Procter & Gamble Company
Priority to EP19706801.8A priority Critical patent/EP3743547A1/fr
Priority to JP2020539693A priority patent/JP2021512229A/ja
Priority to CN201980006966.7A priority patent/CN111601918A/zh
Publication of WO2019147527A1 publication Critical patent/WO2019147527A1/fr
Priority to JP2023031033A priority patent/JP2023060054A/ja

Abstract

Un procédé, par exemple un procédé continu, pour fabriquer un article manufacturé contenant une structure fibreuse, par exemple une structure composite, et plus particulièrement un procédé de fabrication d'un article manufacturé contenant une structure fibreuse, telle qu'une structure fibreuse soluble, contenant des filaments solubles.
PCT/US2019/014447 2018-01-26 2019-01-22 Procédé de fabrication d'un article manufacturé WO2019147527A1 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
EP19706801.8A EP3743547A1 (fr) 2018-01-26 2019-01-22 Procédé de fabrication d'un article manufacturé
JP2020539693A JP2021512229A (ja) 2018-01-26 2019-01-22 製造物品を作製するためのプロセス
CN201980006966.7A CN111601918A (zh) 2018-01-26 2019-01-22 用于制备制品的方法
JP2023031033A JP2023060054A (ja) 2018-01-26 2023-03-01 製造物品を作製するためのプロセス

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201862622252P 2018-01-26 2018-01-26
US62/622,252 2018-01-26

Publications (1)

Publication Number Publication Date
WO2019147527A1 true WO2019147527A1 (fr) 2019-08-01

Family

ID=65516739

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2019/014447 WO2019147527A1 (fr) 2018-01-26 2019-01-22 Procédé de fabrication d'un article manufacturé

Country Status (5)

Country Link
US (2) US20190233974A1 (fr)
EP (1) EP3743547A1 (fr)
JP (2) JP2021512229A (fr)
CN (1) CN111601918A (fr)
WO (1) WO2019147527A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023200771A1 (fr) * 2022-04-12 2023-10-19 The Procter & Gamble Company Articles en dose unitaire d'entretien de tissus comprenant des capsules

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10683618B2 (en) 2018-01-26 2020-06-16 The Procter & Gamble Company Process of making a multi-ply fibrous water soluble product
US10857756B2 (en) 2018-01-26 2020-12-08 The Procter & Gamble Company Process of making a multi-ply fibrous water soluble product
EP3894528A1 (fr) 2018-12-14 2021-10-20 The Procter & Gamble Company Article produisant de la mousse, se désintégrant dans l'eau
JP7319393B2 (ja) 2019-06-10 2023-08-01 ザ プロクター アンド ギャンブル カンパニー 製品使用結果を向上させるためにユーザフィードバック情報を生成する方法
CN111996606B (zh) * 2020-09-01 2021-12-14 上海邀加科技有限公司 液/固态添加剂在熔喷法非织造工艺中的添加方法和设备
WO2023196214A1 (fr) 2022-04-04 2023-10-12 The Procter & Gamble Company Compositions de soins buccodentaires à dose unitaire comprenant du fluorure

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8980816B2 (en) * 2012-01-04 2015-03-17 The Procter & Gamble Company Fibrous structures comprising particles and methods for making same
US20150190543A1 (en) * 2014-01-06 2015-07-09 Verdex Technologies Inc. Coform nanofibrous superabsorbent materials
US20160355950A1 (en) * 2015-06-03 2016-12-08 The Procter & Gamble Company Coforming Processes and Forming Boxes Used Therein

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102005008926A1 (de) * 2005-02-24 2006-11-16 Philipps-Universität Marburg Verfahren zur Herstellung von Nano- und Mesofasern durch Elektrospinning von kolloidalen Dispersionen
EP2573215A1 (fr) * 2011-09-20 2013-03-27 Mölnlycke Health Care AB Fibres polymères
CN103958075B (zh) * 2011-12-07 2016-02-24 花王株式会社 粉粒体的散布方法、散布装置和使用其的发热体的制造方法
CA2860650C (fr) * 2012-01-04 2016-08-02 The Procter & Gamble Company Structures fibreuses contenant des principes actifs et presentant de multiples zones
MX2016002480A (es) * 2013-09-06 2016-05-31 Procter & Gamble Bolsitas que comprenden materiales de pared fibrosos solubles en agua y metodos para su fabricacion.
EP3662097A4 (fr) * 2017-07-31 2021-04-07 3M Innovative Properties Company Fibres comprenant une polyoléfine cristalline et une résine tackifiante hydrocarbonée, et leur procédé de fabrication

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8980816B2 (en) * 2012-01-04 2015-03-17 The Procter & Gamble Company Fibrous structures comprising particles and methods for making same
US20150190543A1 (en) * 2014-01-06 2015-07-09 Verdex Technologies Inc. Coform nanofibrous superabsorbent materials
US20160355950A1 (en) * 2015-06-03 2016-12-08 The Procter & Gamble Company Coforming Processes and Forming Boxes Used Therein

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
"CTFA Cosmetic Ingredient Handbook", 1988, THE COSMETIC, TOILETRIES, AND FRAGRANCE ASSOCIATION, INC.
COLLOIDS; SURFACES A, PHYSICO CHEMICAL & ENGINEERING ASPECTS, vol. 162, 2000, pages 107 - 121

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2023200771A1 (fr) * 2022-04-12 2023-10-19 The Procter & Gamble Company Articles en dose unitaire d'entretien de tissus comprenant des capsules

Also Published As

Publication number Publication date
EP3743547A1 (fr) 2020-12-02
US20190233974A1 (en) 2019-08-01
US20240167197A1 (en) 2024-05-23
CN111601918A (zh) 2020-08-28
JP2023060054A (ja) 2023-04-27
JP2021512229A (ja) 2021-05-13

Similar Documents

Publication Publication Date Title
US20240167197A1 (en) Process for making an article of manufacture on a single, continuous manufacturing line
EP3743548B1 (fr) Procédé de fabrication d'un article manufacturé
EP3041921B1 (fr) Sacs comprenant des matériaux de parois fibreux hydrosolubles et leurs procédés de préparation
EP2800831B1 (fr) Structures fibreuses comprenant des particules et leurs procédés de fabrication
US11850293B2 (en) Active agent-containing matrix particles and processes for making same
JP7364677B2 (ja) 粒子を含む起泡性繊維構造体及びその製造方法
US20230086089A1 (en) Fibrous wall material pouch
US20220233416A1 (en) Process For Making An Oral Care Article Of Manufacture

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19706801

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2020539693

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2019706801

Country of ref document: EP

Effective date: 20200826